CN108569012A - A kind of easily heat-sealing of mill mist type can in print PE films and preparation method - Google Patents
A kind of easily heat-sealing of mill mist type can in print PE films and preparation method Download PDFInfo
- Publication number
- CN108569012A CN108569012A CN201810227687.0A CN201810227687A CN108569012A CN 108569012 A CN108569012 A CN 108569012A CN 201810227687 A CN201810227687 A CN 201810227687A CN 108569012 A CN108569012 A CN 108569012A
- Authority
- CN
- China
- Prior art keywords
- parts
- layer
- sealing
- films
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention belongs to field of packaging material,Disclose a kind of easily heat-sealing of mill mist type can in print PE films and preparation method,Grind the easily heat-sealing of mist type can in print PE films by corona layer,Sandwich layer and hot sealing layer are constituted,Corona layer is based on mass fraction by 85 95 parts of bimodal PE,5 15 parts of EVA,0 1.5 parts of compositions of 0 1.5 parts of lubrication prescription and opening agent,Sandwich layer is based on mass fraction by 10 30 parts of LLDPE,0 10 parts of HDPE,10 30 parts of LDPE and 30 80 parts of bimodal PE,Hot sealing layer is based on mass fraction by 100 parts of bimodal PE,0 1.5 parts of compositions of 0 1.5 parts of lubrication prescription and opening agent,Each layer formula mixture is set to be plasticized using three-layer co-extruded extruder,It is blow molded into bubble,24~28 DEG C of air-cooling mouldings,Traction,Sided corona treatment,Trimming,Winding film forming.The present invention uses the polyethylene with two peak structure for raw material, has mill fog effect well, heat sealability is good, can be used for high-speed packaging.
Description
Technical field
The invention belongs to the easily heat-sealing of field of packaging material more particularly to a kind of mill mist type can in print PE films and preparation
Method.
Background technology
Currently, the prior art commonly used in the trade is such:Plastic printing packaging film is because of transparent, glossiness is good, product
Have the characteristics that bright, bright-coloured, to substitute sheet package, but there is glass frosted finish effect, the packaged configuration of " mist " shape is presented
Cause the esthetic sentiment that people are new, so the packaging film of exploitation mill mist type, appearance is seemed like ground glass, and sensitive paper packet
Dress, will not be reflective.The existing packaging membrane technology for making mill mist type generally uses the mode of addition masterbatch, but causes after being added following new
The problem of:1, masterbatch component is the CaCO of different-grain diameter3, talcum powder etc., processing fluidity is deteriorated;2, film heat sealability is deteriorated;
3, film material mechanical performance can decline.
In conclusion problem of the existing technology is:
(1) existing mill mist type packaging film processing fluidity is poor;
(2) film heat sealability is poor;
(3) film material mechanical performance declines.
Solve the difficulty and meaning of above-mentioned technical problem:
Difficulty is the prior art generally with the mode of addition masterbatch, and masterbatch component is the CaCO of different-grain diameter3, talcum powder
Deng, to develop again it is a kind of there is the formula of mill mist optical effect, while to keep or improve heat sealability, can in the performances such as to print special
Point;Meaning is that film quality can be improved, increases mechanical performance, improve the speed of heat sealed package.
Invention content
In view of the problems of the existing technology, the present invention provides a kind of easily heat-sealing of mill mist type can in print PE films and preparation
Method.
The invention is realized in this way a kind of mill mist type easily heat-sealing can in print PE films by corona layer, sandwich layer and hot sealing layer
It constitutes;
Corona layer is based on mass fraction by bimodal PE 85-95 parts, 5-15 parts of EVA, 0-1.5 parts of lubrication prescription and opening agent 0-
1.5 parts of compositions;
Sandwich layer is based on mass fraction by 10-30 parts of LLDPE, 10-30 parts of 0-10 parts of HDPE, LDPE and bimodal PE 30-
80 parts;
Hot sealing layer is based on mass fraction by 100 parts of bimodal PE, 0-1.5 parts of compositions of 0-1.5 parts of lubrication prescription and opening agent.
Another object of the present invention is to provide a kind of easily heat-sealing of mill mist type can in print the preparation methods of PE films, including with
Lower step:
1, each layer formula mixture is made to be plasticized using three-layer co-extruded extruder;
2, bubble, 24~28 DEG C of air-cooling mouldings are blow molded into;
3, it draws, sided corona treatment;Plastic film produces general technology;
4, trimming, winding film forming.
Further, 180~210 DEG C of corona layer and hot sealing layer plasticization temperature, 180~220 DEG C of sandwich layer plasticization temperature.
In conclusion advantages of the present invention and good effect are:
The present invention uses the polyethylene with two peak structure for raw material, has mill fog effect well, heat sealability is good, can
For high-speed packaging.Compared with prior art, identical 50 microns of film, there is following obvious advantage and effect:
Description of the drawings
Fig. 1 be mill mist type provided in an embodiment of the present invention easily heat-sealing can in print PE method for manufacturing thin film flow charts.
Specific implementation mode
In order to make the purpose , technical scheme and advantage of the present invention be clearer, with reference to embodiments, to the present invention
It is further elaborated.It should be appreciated that the specific embodiments described herein are merely illustrative of the present invention, it is not used to
Limit the present invention.
As shown in Figure 1, in view of the problems of the existing technology, mill mist type provided in an embodiment of the present invention easily heat-sealing can in print
The preparation method of PE films includes:
S101, each layer formula mixture is made to be plasticized using three-layer co-extruded extruder;
S102, bubble, 24~28 DEG C of air-cooling mouldings are blow molded into;
S103, traction, sided corona treatment;
S104, trimming, winding film forming.
The easily heat-sealing of mill mist type can in print PE films be made of corona layer, sandwich layer and hot sealing layer;
Corona layer is based on mass fraction by bimodal PE 85-95 parts, 5-15 parts of EVA, 0-1.5 parts of lubrication prescription and opening agent 0-
1.5 parts of compositions;
Sandwich layer is based on mass fraction by 10-30 parts of LLDPE, 10-30 parts of 0-10 parts of HDPE, LDPE and bimodal PE 30-
80 parts;
Hot sealing layer is based on mass fraction by 100 parts of bimodal PE, 0-1.5 parts of compositions of 0-1.5 parts of lubrication prescription and opening agent.
Embodiment 1:
Corona layer is based on mass fraction by 85 parts of bimodal PE, and EVA15 parts, 1.2 parts of 1.5 parts of lubrication prescription and opening agent are constituted;
Sandwich layer is based on mass fraction by 20 parts of LLDPE, 20 parts of 10 parts of HDPE, LDPE and 50 parts of bimodal PE;
Hot sealing layer is based on mass fraction by 100 parts of bimodal PE, 0.5 part of composition of 1.5 parts of lubrication prescription and opening agent;
Each layer formula mixture is set to be plasticized using three-layer co-extruded extruder, 195 DEG C of corona layer and hot sealing layer plasticization temperature, core
215 DEG C of plasticization temperature of layer is blow molded into bubble, 24 DEG C of air-cooling mouldings, traction, sided corona treatment, trimming, winding film forming.
Embodiment 2:
Corona layer is based on mass fraction by 90 parts of bimodal PE, 10 parts of EVA, 1.0 parts of compositions of 1.2 parts of lubrication prescription and opening agent;
Sandwich layer is based on mass fraction by 24 parts of LLDPE, 20 parts of 6 parts of HDPE, LDPE and PE50 parts bimodal.
Hot sealing layer is based on mass fraction by 100 parts of bimodal PE, 1.2 parts of compositions of 0.8 part of lubrication prescription and opening agent;
Each layer formula mixture is set to be plasticized using three-layer co-extruded extruder, 200 DEG C of corona layer and hot sealing layer plasticization temperature, core
210 DEG C of plasticization temperature of layer is blow molded into bubble, 26 DEG C of air-cooling mouldings, traction, sided corona treatment, trimming, winding film forming.
Embodiment 3:
Corona layer is based on mass fraction by 95 parts of bimodal PE, 5 parts of EVA, 1.0 parts of compositions of 1.0 parts of lubrication prescription and opening agent;
Sandwich layer is based on mass fraction by 20 parts of LLDPE, 17 parts of 3 parts of HDPE, LDPE and 60 parts of bimodal PE.
Hot sealing layer is based on mass fraction by 100 parts of bimodal PE, 0.8 part of composition of 1.2 parts of lubrication prescription and opening agent;
Each layer formula mixture is set to be plasticized using three-layer co-extruded extruder, 200 DEG C of corona layer and hot sealing layer plasticization temperature, core
205 DEG C of plasticization temperature of layer is blow molded into bubble, 28 DEG C of air-cooling mouldings, traction, sided corona treatment, trimming, winding film forming.
The foregoing is merely illustrative of the preferred embodiments of the present invention, is not intended to limit the invention, all essences in the present invention
All any modification, equivalent and improvement etc., should all be included in the protection scope of the present invention made by within refreshing and principle.
Claims (3)
1. a kind of easily heat-sealing of mill mist type can in print PE films, which is characterized in that the easily heat-sealing of mill mist type can in print PE films by corona
Layer, sandwich layer and hot sealing layer are through forming together with three extruder coextrusion coatings;
Corona layer is based on mass fraction by bimodal PE 85-95 parts, 5-15 parts of EVA, 0-1.5 parts of 0-1.5 parts of lubrication prescription and opening agent
It constitutes;
Sandwich layer is based on mass fraction by 10-30 parts of LLDPE, 10-30 parts of 0-10 parts of HDPE, LDPE and PE 30-80 parts bimodal;
Hot sealing layer is based on mass fraction by 100 parts of bimodal PE, 0-1.5 parts of compositions of 0-1.5 parts of lubrication prescription and opening agent.
2. a kind of easily heat-sealing of mill mist type as described in claim 1 can in print the preparation methods of PE films, which is characterized in that including with
Lower step:
(1) each layer formula mixture is made to be plasticized using three-layer co-extruded extruder, through co-extrusion die head so that three layered materials are stacked together;
(2) bubble, 24~28 DEG C of air-cooling mouldings are blow molded into;
(3) it draws, sided corona treatment;
(4) trimming, winding film forming.
3. as claimed in claim 2 the easily heat-sealing of mill mist type can in print the preparation methods of PE films, which is characterized in that corona layer with
180~210 DEG C of hot sealing layer plasticization temperature, 180~220 DEG C of sandwich layer plasticization temperature.