CN108559104A - A kind of lignin imines quaternary ammonium salt cation asphalt emulsifier and preparation method thereof - Google Patents
A kind of lignin imines quaternary ammonium salt cation asphalt emulsifier and preparation method thereof Download PDFInfo
- Publication number
- CN108559104A CN108559104A CN201810458406.2A CN201810458406A CN108559104A CN 108559104 A CN108559104 A CN 108559104A CN 201810458406 A CN201810458406 A CN 201810458406A CN 108559104 A CN108559104 A CN 108559104A
- Authority
- CN
- China
- Prior art keywords
- lignin
- preparation
- asphalt
- reaction
- quaternary ammonium
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of lignin imines quaternary ammonium salt cation asphalt emulsifier of present invention proposition and preparation method thereof.A kind of preparation method of lignin imines quaternary ammonium salt cation asphalt emulsifier, general formula of molecular structure are：
Description
Technical field
The invention belongs to field of fine chemical, and in particular to a kind of lignin imines quaternary ammonium salt cationic type asphalt emulsification
Agent.
Background technology
With the continuous development of asphalt applications level, the deficiency of common heated bitumen also begins to show：Pitch rate of set is too
Soon, it needs to heat repeatedly when use, this causes great energy waste and environmental pollution in use.Cold pitch is added
Heat enables pitch with a kind of fine particle in the aqueous solution containing appropriate emulsifier to viscous pasty state is melted by stirring
State is spread in the solution, forms the lotion of (O/W) shape, here it is emulsified asphalts.This asphalt emulsion is at normal temperatures with liquid
Form exists, and is in dark-brown or black, has good mobility under high temperature.Influence emulsified asphalt pavement performance most critical because
Element is exactly asphalt emulsifier, and cationic asphalt emulsifier principal item has organic amine, quaternary ammonium salt, imidazoles both at home and abroad at present
Quinoline class, amides etc., with the application of cationic emulsified bitumen, the kind of asphalt emulsifier is also gradually enriched.
United States Patent (USP) USP4338136 is with C12-18Long carbon chain aliphatic acid reacts preparation with diethylenetriamine under certain condition
Asphalt emulsifier.The disadvantages of this method is that the asphalt emulsifier for preparing is expensive, when for slurry seal construction, is demulsified the time
Long, molding time is slow, and the open to traffic time is long.Chinese patent CN1096714 utilizes oil plant by-product aphthenic acids and alkenyl polyamine
Reaction, prepares asphalt emulsifier.The disadvantages of this method is the raw material supply of emulsifier by severely restricts, is unfavorable for promoting and answer
With.Chinese patent CN1861721A is related to a kind of rosin cation asphalt emulgent.The emulsifier is by rosin and alkenyl polyamine
Reaction, obtain rosin intermediate, then, with different types of quaternary ammonium salt intermediate be condensed, be made function admirable rosin sun from
Sub- asphalt emulsifier.The shortcomings that this method is that reaction step is cumbersome, needs pyroreaction.Chinese patent CN101712625A is related to
And a kind of method for synthesizing amphoteric slow-breaking quick-setting asphalt emulsifier, it is reacted with polyamines using oleic acid and generates polyamide-polyamino, be then added
Halogenating reaction occurs for monoxone, and asphalt emulsifier is made.The disadvantages of this method is to need pyroreaction when preparing.Chinese patent
CN101745340A is related to a kind of cation asphalt emulgent preparation method, and host agent is obtained by the reaction by mixed organic acid and organic amine
Intermediate, then carry out quaternization reaction and be made, adjuvant is nonionic surfactant and modified additive.The disadvantages of this method is system
Standby complex steps, cost is higher, needs pyroreaction.
Invention content
In order to solve the above technical problems, a kind of lignin imines quaternary ammonium salt cationic type asphalt emulsifier of the present invention
And preparation method thereof, asphalt emulsifier raw material sources prepared by the present invention are extensive, and production cost is low, and preparation process is simple, can breast
Change the pitch of a variety of different models, the emulsified asphalt of preparation is fine and smooth uniformly, and storage stability is good.
The present invention provides a kind of lignin imines quaternary ammonium salt cation asphalt emulsifier, and general formula of molecular structure is：
Lignin represents lignin molecule chain.
The present invention further provides a kind of preparation method of lignin imines quaternary ammonium salt cation asphalt emulsifier, according to
Following steps carry out：
(1) by parahydroxyben-zaldehyde and lignin, thionyl chloride and triethylamine hybrid reaction, reaction intermediate I is obtained, in
Mesosome I is：
(2) by intermediate I, phosphorus oxychloride and pyridine hybrid reaction, intermediate II is obtained, intermediate II is：
(3) by intermediate II, diethanol amine and DMAP hybrid reactions, intermediate III is obtained, intermediate III is：
(4) by intermediate III and hydrobromic acid hybrid reaction, intermediate IV is obtained, intermediate IV is：
(5) ethyl alcohol is closed into trichloroacetaldehyde and iodomethane hybrid reaction, obtains intermediate V, intermediate V is：(CH2CH3)
2CH3N+CH2CH2COOCH2CH3.I-；
(6) by IV hybrid reaction of intermediate V and intermediate, the emulsification of lignin imines quaternary ammonium salt cation asphalt is obtained
Agent；As long as above step does not influence to prepare, replaceable.
Improved as of the invention further, the feed proportioning ratio used for：Parahydroxyben-zaldehyde, thionyl chloride, three second
Amine, lignin, phosphorus oxychloride, pyridine, diethanol amine, DMAP, hydrobromic acid, ethyl alcohol close trichloroacetaldehyde, the molar ratio of iodomethane is
1:(1.2-2):(2-8):(1-1.5):(1-5):(0.5-3):(1-1.8):(0.1-0.5):(1.5-2.5):(1-1.5):(1-
1.7)。
Improved as of the invention further, the feed proportioning ratio used for：：Parahydroxyben-zaldehyde, thionyl chloride, three second
Amine, lignin, phosphorus oxychloride, pyridine, diethanol amine, DMAP, hydrobromic acid, ethyl alcohol close trichloroacetaldehyde, the molar ratio of iodomethane is
1:(1.2-1.5):(2-5):(1-1.2):(1-3):(0.7-2):(1.2-1.5):(0.1-0.4):(1.5-2):(1-1.3):
(1-1.5)。
Improved as of the invention further, the feed proportioning ratio used for：Parahydroxyben-zaldehyde, thionyl chloride, three second
Amine, lignin, phosphorus oxychloride, pyridine, diethanol amine, DMAP, hydrobromic acid, ethyl alcohol close trichloroacetaldehyde, the molar ratio of iodomethane is
1:1.2:4:1.1:2.5:1.2:1.3:0.25:1.7:1.2:1.3。
As further improvement of the invention, specifically comprise the following steps：
(1) parahydroxyben-zaldehyde is added in reaction bulb, sequentially adds thionyl chloride and triethylamine, after reacting at room temperature 2-3h
Lignin is added, 40 DEG C are stirred to react 2h, obtain intermediate I；
(2) intermediate I and phosphorus oxychloride are dissolved in dichloromethane, pyridine is slowly added dropwise, 0 DEG C of reaction 5h obtains intermediate
Ⅱ；
(3) intermediate II and diethanol amine are dissolved in dichloromethane, DMAP is added, 40 DEG C of reaction 2h obtain intermediate III；
(4) intermediate III is dissolved in glacial acetic acid, 30% hydrobromic acid is added dropwise, 40-45 DEG C of reaction 2h obtains intermediate IV；
(5) ethyl alcohol conjunction trichloroacetaldehyde is dissolved in dichloromethane, 0 DEG C is slowly added dropwise iodomethane, reacts 1h, obtains intermediate
Ⅴ；
(6) intermediate IV is dissolved in dichloromethane, 40 DEG C of stirrings are lower to be added dropwise intermediate V, reacts 3h, obtains lignin Asia
Amine quaternary ammonium salt cation asphalt emulsifier.
The present invention further protect above-mentioned lignin imines cation asphalt emulgent prepare split soon type and in split type
Application in cationic emulsified bitumen.
The present invention further protects a kind of preparation method of emulsified asphalt, which is characterized in that includes the following steps：Right is wanted
It is the 1-3% of the emulsified asphalt gross mass prepared to seek the dosage of the asphalt emulsifier described in 1, adds water to match above-mentioned asphalt emulsifier
Aqueous solution is made, is heated to 60-70 DEG C, soap lye is made；By after heating pitch and emulsifier soap lye emulsified by colloid mill, add
Enter a certain amount of auxiliary agent, prepares cationic emulsified bitumen.
As further improvement of the invention, auxiliary agent includes one or more of aluminum sulfate, ammonium chloride and calcium chloride.
The present invention further protects the emulsified asphalt prepared according to the preparation method of preceding claim.
Beneficial effects of the present invention：
1, raw material sources of the invention are extensive, and production cost is low, and preparation process is simple；
2, the asphalt emulsifier function admirable obtained, the pitch of emulsifiable a variety of different models, the emulsified asphalt of preparation are thin
Greasy uniform, storage stability is good；
3, asphalt emulsifier prepared by the present invention meets national standard, and emulsified asphalt obtained is fine and smooth uniformly, has and splits soon
Type splits the characteristic of type asphalt emulsifier in.
Specific implementation mode
Below in conjunction with the embodiment of the present invention, technical solution in the embodiment of the present invention carries out clear, complete description,
Obviously, the embodiment described is the embodiment of the part of representative of the present invention, rather than whole embodiments, this field are general
Other all embodiments that logical technical staff is obtained without making creative work belong to the protection of the present invention
Range.
Used raw material, reagent are conventional chemical products in the embodiment of the present invention, can be purchased by commercial channel
It can buy.
The preparation of 1 lignin imines quaternary ammonium salt cation asphalt emulsifier of embodiment
It follows the steps below：
(1) 1mol parahydroxyben-zaldehydes are added in reaction bulb, sequentially add 1.2mol thionyl chlorides and 2mol triethylamines,
1mol lignin is added after reacting at room temperature 2-3h, 40 DEG C are stirred to react 2h, obtain intermediate I；
(2) intermediate I and 1mol phosphorus oxychloride are dissolved in dichloromethane, 0.7mol pyridines is slowly added dropwise, 0 DEG C is reacted 5h,
Obtain intermediate II；
(3) intermediate II and 1.2mol diethanol amine are dissolved in dichloromethane, 0.1mol DMAP, 40 DEG C of reaction 2h are added,
Obtain intermediate III；
(4) intermediate III is dissolved in glacial acetic acid, the hydrobromic acid of 1.5mol 30%, 40-45 DEG C of reaction 2h, in obtaining is added dropwise
Mesosome IV；
(5) 1mol ethyl alcohol conjunction trichloroacetaldehyde is dissolved in dichloromethane, 0 DEG C is slowly added dropwise 1mol iodomethane, reacts 1h, obtains
Intermediate V；
(6) intermediate IV is dissolved in dichloromethane, 40 DEG C of stirrings are lower to be added dropwise intermediate V, reacts 3h, obtains lignin Asia
Amine quaternary ammonium salt cation asphalt emulsifier, yield 70%.
The lignin imines quaternary ammonium salt cation asphalt emulsifier of preparation is subjected to FTIR detections after separating-purifying, is tied
Fruit is as follows：3340-3510cm-1 is N-H stretching vibration peaks, and 3238-3540cm-1 is O-H stretching vibration absworption peaks, 2949cm-1
For the asymmetric stretching vibration absworption peak of methylene, 2837cm-1 is methylene symmetrical stretching vibration absorption peak, 1650-1550cm-1
For NH flexural vibrations peaks, 1648cm-1 is C=O stretching vibration absworption peaks, and 1576cm-1 and the skeleton that 1474cm-1 is phenyl ring shake
Dynamic absorption peak, 1400cm-1 and 1306cm-1 are O-H in-plane bending vibration absorption peaks, and 1043cm-1 inhales for Ar-O-C stretching vibrations
Peak is received, 962cm-1,920cm-1 and 864cm-1 are the hydrogen out-of-plane bending vibration absorption peak isolated on phenyl ring, 613cm-1 O-H
Out-of-plane bending vibration absorption peak.
Reaction equation is as follows：
The preparation of 2 lignin imines quaternary ammonium salt cation asphalt emulsifier of embodiment
It follows the steps below：
(1) 1mol parahydroxyben-zaldehydes are added in reaction bulb, sequentially add 2mol thionyl chlorides and 8mol triethylamines, room
1.5mol lignin is added after temperature reaction 2-3h, 40 DEG C are stirred to react 2h, obtain intermediate I；
(2) intermediate I and 5mol phosphorus oxychloride are dissolved in dichloromethane, 3mol pyridines is slowly added dropwise, 0 DEG C of reaction 5h is obtained
To intermediate II；
(3) intermediate II and 1.8mol diethanol amine are dissolved in dichloromethane, 0.4mol DMAP, 40 DEG C of reaction 2h are added,
Obtain intermediate III；
(4) intermediate III is dissolved in glacial acetic acid, the hydrobromic acid of 2mol 30% is added dropwise, 40-45 DEG C of reaction 2h obtains centre
Body IV；
(5) 1.3mol ethyl alcohol conjunction trichloroacetaldehyde is dissolved in dichloromethane, 0 DEG C is slowly added dropwise 1.5mol iodomethane, reacts 1h,
Obtain intermediate V；
(6) intermediate IV is dissolved in dichloromethane, 40 DEG C of stirrings are lower to be added dropwise intermediate V, reacts 3h, obtains lignin Asia
Amine quaternary ammonium salt cation asphalt emulsifier, yield 81%.
The lignin imines quaternary ammonium salt cation asphalt emulsifier of preparation is subjected to FTIR detections after separating-purifying, is tied
Fruit proves lignin imines quaternary ammonium salt cation asphalt emulsifier.
The preparation of 3 lignin imines quaternary ammonium salt cation asphalt emulsifier of embodiment
It follows the steps below：
(1) 1mol parahydroxyben-zaldehydes are added in reaction bulb, sequentially add 1.5mol thionyl chlorides and 5mol triethylamines,
1.2mol lignin is added after reacting at room temperature 2-3h, 40 DEG C are stirred to react 2h, obtain intermediate I；
(2) intermediate I and 3mol phosphorus oxychloride are dissolved in dichloromethane, 2mol pyridines is slowly added dropwise, 0 DEG C of reaction 5h is obtained
To intermediate II；
(3) intermediate II and 1.5mol diethanol amine are dissolved in dichloromethane, 0.4mol DMAP, 40 DEG C of reaction 2h are added,
Obtain intermediate III；
(4) intermediate III is dissolved in glacial acetic acid, the hydrobromic acid of 2mol 30% is added dropwise, 40-45 DEG C of reaction 2h obtains centre
Body IV；
(5) 1.3mol ethyl alcohol conjunction trichloroacetaldehyde is dissolved in dichloromethane, 0 DEG C is slowly added dropwise 1.5mol iodomethane, reacts 1h,
Obtain intermediate V；
(6) intermediate IV is dissolved in dichloromethane, 40 DEG C of stirrings are lower to be added dropwise intermediate V, reacts 3h, obtains lignin Asia
Amine quaternary ammonium salt cation asphalt emulsifier, yield 85%.
The lignin imines quaternary ammonium salt cation asphalt emulsifier of preparation is subjected to FTIR detections after separating-purifying, is tied
Fruit proves lignin imines quaternary ammonium salt cation asphalt emulsifier.
The preparation of 4 lignin imines quaternary ammonium salt cation asphalt emulsifier of embodiment
It follows the steps below：
(1) 1mol parahydroxyben-zaldehydes are added in reaction bulb, sequentially add 1.2mol thionyl chlorides and 4mol triethylamines,
1.1mol lignin is added after reacting at room temperature 2-3h, 40 DEG C are stirred to react 2h, obtain intermediate I；
(2) intermediate I and 2.5mol phosphorus oxychloride are dissolved in dichloromethane, 1.2mol pyridines, 0 DEG C of reaction is slowly added dropwise
5h obtains intermediate II；
(3) intermediate II and 1.3mol diethanol amine are dissolved in dichloromethane, 0.25mol DMAP, 40 DEG C of reactions is added
2h obtains intermediate III；
(4) intermediate III is dissolved in glacial acetic acid, the hydrobromic acid of 1.7mol 30%, 40-45 DEG C of reaction 2h, in obtaining is added dropwise
Mesosome IV；
(5) 1.2mol ethyl alcohol conjunction trichloroacetaldehyde is dissolved in dichloromethane, 0 DEG C is slowly added dropwise 1.3mol iodomethane, reacts 1h,
Obtain intermediate V；
(6) intermediate IV is dissolved in dichloromethane, 40 DEG C of stirrings are lower to be added dropwise intermediate V, reacts 3h, obtains lignin Asia
Amine quaternary ammonium salt cation asphalt emulsifier, yield 93%.
The lignin imines quaternary ammonium salt cation asphalt emulsifier of preparation is subjected to FTIR detections after separating-purifying, is tied
Fruit proves lignin imines quaternary ammonium salt cation asphalt emulsifier.
The preparation of 5 emulsified asphalt of embodiment
AH-90# pitch 300g are taken, are heated to 125 DEG C, 9g asphalt emulsifiers manufactured in the present embodiment are added to 200g water
In, it is configured to aqueous solution, is heated to 60-70 DEG C, soap lye is made；By after heating pitch and emulsifier soap lye pass through colloid mill breast
Change, a certain amount of auxiliary agent ammonium chloride is added, prepares cationic emulsified bitumen.
The preparation of 6 emulsified asphalt of embodiment
AH-90# pitch 300g are taken, are heated to 125 DEG C, 9g asphalt emulsifiers manufactured in the present embodiment are added to 200g water
In, it is configured to aqueous solution, is heated to 60-70 DEG C, soap lye is made；By after heating pitch and emulsifier soap lye pass through colloid mill breast
Change, a certain amount of auxiliary agent aluminum sulfate is added, prepares cationic emulsified bitumen.
The preparation of 7 emulsified asphalt of embodiment
AH-90# pitch 300g are taken, are heated to 125 DEG C, 9g asphalt emulsifiers manufactured in the present embodiment are added to 200g water
In, it is configured to aqueous solution, is heated to 60-70 DEG C, soap lye is made；By after heating pitch and emulsifier soap lye pass through colloid mill breast
Change, a certain amount of auxiliary agent calcium chloride is added, prepares cationic emulsified bitumen.
1 each emulsified asphalt of test example breaks performance
Emulsified asphalt made from embodiment 5-7 is pressed into the cationic emulsified bitumen standard (JTJ052- that Chinese transportation portion works out
2000) it is detected, the results are shown in Table 1-3.
1 normal temperature storage stability of table
The general technology performance of 2 each emulsified asphalt of table
The de-emulsification speed of 3 each emulsified asphalt of table
| Emulsified asphalt | Mix and stir stability |
| Embodiment 5 | It splits soon |
| Embodiment 6 | In split |
| Embodiment 7 | In split |
It can be seen from the above result that lignin imines quaternary ammonium salt cation asphalt emulsifier prepared by the present invention is emulsifiable more
The emulsified asphalt of the pitch of kind different model, preparation is fine and smooth uniform, and storage stability is good, suitable for being used to spray, making surface
Road surface and penetration type road surface are punished, has and splits the characteristic that type splits type asphalt emulsifier in soon.Emulsified asphalt items obtained
It can meet the cationic emulsified bitumen standard (JTJ052-2000) of Chinese transportation portion formulation.
Although an embodiment of the present invention has been shown and described, it will be understood by those skilled in the art that：Not
In the case of being detached from the principle of the present invention and objective a variety of change, modification, replacement and modification can be carried out to these embodiments, this
The range of invention is limited by claim and its equivalent.
Claims (10)
1. a kind of lignin imines quaternary ammonium salt cation asphalt emulsifier, which is characterized in that its general formula of molecular structure is：
Lignin represents lignin molecule chain.
2. a kind of preparation method of lignin imines quaternary ammonium salt cation asphalt emulsifier, which is characterized in that according to following step
It is rapid to carry out：
(1) by parahydroxyben-zaldehyde and lignin, thionyl chloride and triethylamine hybrid reaction, reaction intermediate I, intermediate are obtained
I is：
(2) by intermediate I, phosphorus oxychloride and pyridine hybrid reaction, intermediate II is obtained, intermediate II is：
(3) by intermediate II, diethanol amine and DMAP hybrid reactions, intermediate III is obtained, intermediate III is：
(4) by intermediate III and hydrobromic acid hybrid reaction, intermediate IV is obtained, intermediate IV is：
(5) ethyl alcohol is closed into trichloroacetaldehyde and iodomethane hybrid reaction, obtains intermediate V, intermediate V is：(CH2CH3)2CH3N+
CH2CH2COOCH2CH3.I-；
(6) by IV hybrid reaction of intermediate V and intermediate, lignin imines quaternary ammonium salt cation asphalt emulsifier is obtained；
As long as above step does not influence to prepare, replaceable.
3. preparation method according to claim 2, which is characterized in that the feed proportioning ratio used for：Parahydroxyben-zaldehyde, two
Chlorine sulfoxide, triethylamine, lignin, phosphorus oxychloride, pyridine, diethanol amine, DMAP, hydrobromic acid, ethyl alcohol close trichloroacetaldehyde, iodomethane
Molar ratio be 1:(1.2-2):(2-8):(1-1.5):(1-5):(0.5-3):(1-1.8):(0.1-0.5):(1.5-2.5):
(1-1.5):(1-1.7)。
4. preparation method according to claim 2, which is characterized in that the feed proportioning ratio used for：Parahydroxyben-zaldehyde, two
Chlorine sulfoxide, triethylamine, lignin, phosphorus oxychloride, pyridine, diethanol amine, DMAP, hydrobromic acid, ethyl alcohol close trichloroacetaldehyde, iodomethane
Molar ratio be 1:(1.2-1.5):(2-5):(1-1.2):(1-3):(0.7-2):(1.2-1.5):(0.1-0.4):(1.5-
2):(1-1.3):(1-1.5)。
5. preparation method according to claim 2, which is characterized in that the feed proportioning ratio used for：Parahydroxyben-zaldehyde, two
Chlorine sulfoxide, triethylamine, lignin, phosphorus oxychloride, pyridine, diethanol amine, DMAP, hydrobromic acid, ethyl alcohol close trichloroacetaldehyde, iodomethane
Molar ratio be 1:1.2:4:1.1:2.5:1.2:1.3:0.25:1.7:1.2:1.3.
6. preparation method according to claim 2, which is characterized in that specifically comprise the following steps：
(1) parahydroxyben-zaldehyde is added in reaction bulb, sequentially adds thionyl chloride and triethylamine, be added after reacting at room temperature 2-3h
Lignin, 40 DEG C are stirred to react 2h, obtain intermediate I；
(2) intermediate I and phosphorus oxychloride are dissolved in dichloromethane, pyridine is slowly added dropwise, 0 DEG C of reaction 5h obtains intermediate II；
(3) intermediate II and diethanol amine are dissolved in dichloromethane, DMAP is added, 40 DEG C of reaction 2h obtain intermediate III；
(4) intermediate III is dissolved in glacial acetic acid, 30% hydrobromic acid is added dropwise, 40-45 DEG C of reaction 2h obtains intermediate IV；
(5) ethyl alcohol conjunction trichloroacetaldehyde is dissolved in dichloromethane, 0 DEG C is slowly added dropwise iodomethane, reacts 1h, obtains intermediate V；
(6) intermediate IV is dissolved in dichloromethane, 40 DEG C of stirrings are lower to be added dropwise intermediate V, reacts 3h, obtains lignin imines
Quaternary ammonium salt cation asphalt emulsifier.
7. lignin imines cation asphalt emulgent splits type in preparation and splits type cation in soon according to claim 1
Application in emulsified asphalt.
8. a kind of preparation method of emulsified asphalt, which is characterized in that include the following steps：Asphalt emulsification described in claim 1
The dosage of agent is the 1-3% of the emulsified asphalt gross mass prepared, adds water to be configured to aqueous solution above-mentioned asphalt emulsifier, is heated to
60-70 DEG C, soap lye is made；By after heating pitch and emulsifier soap lye emulsified by colloid mill, a certain amount of auxiliary agent is added, make
It is standby go out cationic emulsified bitumen.
9. preparation method according to claim 8, which is characterized in that the auxiliary agent includes aluminum sulfate, ammonium chloride and calcium chloride
One or more of.
10. emulsified asphalt prepared by preparation method according to claim 8.