CN108527945A - A kind of flexible honeycomb and manufacturing method of heart cell - Google Patents
A kind of flexible honeycomb and manufacturing method of heart cell Download PDFInfo
- Publication number
- CN108527945A CN108527945A CN201810316808.9A CN201810316808A CN108527945A CN 108527945 A CN108527945 A CN 108527945A CN 201810316808 A CN201810316808 A CN 201810316808A CN 108527945 A CN108527945 A CN 108527945A
- Authority
- CN
- China
- Prior art keywords
- heart
- cell
- honeycomb
- flexible
- shaped
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The present invention relates to a kind of flexible honeycombs and preparation method of heart-shaped cell.This method includes:Core bar glue is applied, core bar glue is coated the surface of flexible thin material is equally spaced using glue spreader;Lamination is bonded, and according to the lamination bonding way of the mutually equally spaced dislocation of neighbouring two layers of core bar glue, flexible thin material's lamination that multilayer is coated with to core bar glue is bonded to form superimposed sheet;Superimposed sheet is carried out hot pressing by hot-press solidifying, makes the core adhesive curing of lamination abutting edge;Drawing and forming, stretch the superimposed sheet after hot pressing, make superimposed sheet that can form the honeycomb of regular hexagon cell in overlapping thickness direction stretching, extension, then heart-shaped mould is stretched into cell, and the surrounding of the honeycomb equipped with heart-shaped mould is fixed using plate washer, honeycomb is made to be deformed into along the end to end heart-shaped cell of draw direction, heart-shaped cell has the flexible edge of arc, wherein, heart-shaped mould is the rod piece that cross section is heart, and the end to end place between heart-shaped cell is adhesive tape abutting edge.
Description
Technical field
The present invention relates to cellular structural material technical field, the flexible honeycomb more particularly to a kind of heart-shaped cell and preparation
Method.
Background technology
Aramid fiber honeycomb core has the characteristics such as high-strength, light, fire-retardant as special sandwich material, it is military, civilian, build
Equal fields are built to be widely used, however in multiple material part manufacturing process, usually with the presence of the larger song of many structures
Rate, traditional regular hexagon honeycomb is because being also easy to produce larger prestressing force and because deforming the excessive structure initial damage brought due to nothing
Method is met the requirements.Flexible honeycomb has extremely excellent all directions flexibility, not will produce structure destruction in process, together
When can also with legacy cellular physical and mechanical properties.But the flexible honeycomb complex forming technology of the prior art, and need
Dedicated equipment is processed, costly.
Therefore, a kind of flexible honeycomb and preparation method of heart-shaped cell are inventor provided.
Invention content
An embodiment of the present invention provides a kind of flexible honeycombs and preparation method of heart-shaped cell, by preparing heart-shaped cell
Flexible honeycomb solves the problems, such as that the honeycomb of the prior art cannot meet greater curvature parts-moulding.
In a first aspect, the embodiment of the present invention proposes a kind of preparation method of the flexible honeycomb of heart-shaped cell, the preparation
Method includes:Core bar glue is applied, core bar glue is coated the surface of flexible thin material is equally spaced using glue spreader;
Lamination is bonded, and according to the lamination bonding way of the mutually equally spaced dislocation of neighbouring two layers of core bar glue, multilayer is applied
There is flexible thin material's lamination of core bar glue to be bonded to form superimposed sheet;
The superimposed sheet is carried out hot pressing, makes the core adhesive curing of lamination abutting edge by hot-press solidifying;
Drawing and forming stretches the superimposed sheet after the hot pressing, makes the superimposed sheet that can be formed just in overlapping thickness direction stretching, extension
Then the honeycomb of hexagon cell stretches into heart-shaped mould in the cell, and utilize plate washer by the honeycomb equipped with heart-shaped mould
The surrounding of structure is fixed, and the honeycomb is made to be deformed into along the end to end heart-shaped cell of draw direction, the heart
Cell has the flexible edge of arc, wherein the heart mould is the rod piece that cross section is heart, the head between the heart cell
Tail joint is at core glue sticking.
In the first possible implementation, further include after the drawing and forming step:
The honeycomb equipped with heart-shaped mould is put into shaping baking oven by heat-shaping, and the heart-shaped cell is made to shape;
Form removal impregnation is removed the heart-shaped mould and the plate washer, then by the heart from the honeycomb after sizing
The honeycomb impregnation of shape cell;
Cured sheets are cut, and the honeycomb after impregnation is carried out baking and curing, are then required to carry out sawing according to compact dimensions
Or piece cuts processing, obtains the flexible honeycomb structure of the heart-shaped cell of predetermined dimension.
In conjunction with above-mentioned possible realization method, in second of possible realization method, the sizing and solidifying the step of
In, the honeycomb is placed in 265 DEG C ± 5 DEG C of oven temperature environment, keeps the temperature 20 ± 5min, keeps the heart-shaped cell fixed
Type.
In conjunction with above-mentioned possible realization method, in the third possible realization method, the flexible thin material uses
Aramid paper or metal foil.
In conjunction with above-mentioned possible realization method, in the 4th kind of possible realization method, the heart mould is that cross section is
Heart-shaped hollow stem or solid hopkinson bar.
Second aspect provides a kind of flexible honeycomb of the heart-shaped cell prepared using first aspect, the flexible honeycomb
Cell be end to end heart-shaped cell, it is described heart cell between end to end place be core glue sticking at, described
Both sides at core glue sticking are the flexible edge of arc.
The flexible honeycomb of heart-shaped cell prepared by the present invention at core glue sticking with it is outer be arc flexible edge, have
Preferably respectively to flexibility, while there is physically better and chemical property, preparation method is simple, saves production cost, should
When the flexible honeycomb of heart-shaped cell is as core structure, structural damage not will produce in process, be applicable to use
The more stringent field of condition.
Description of the drawings
In order to illustrate the technical solution of the embodiments of the present invention more clearly, will make below to required in the embodiment of the present invention
Attached drawing is briefly described, it should be apparent that, drawings described below is only some embodiments of the present invention, for
For those of ordinary skill in the art, without creative efforts, other are can also be obtained according to these attached drawings
Attached drawing.
Fig. 1 is the status diagram that heart-shaped mould is inserted into flexible honeycomb cell.
Fig. 2 is a kind of structural schematic diagram of the flexible honeycomb of heart-shaped cell of the embodiment of the present invention.
In figure:
1- heart moulds;2- aramid papers;At 3- core glue stickings;4- heart cells;5- flexible edges.
Specific implementation mode
Embodiments of the present invention are described in further detail with reference to the accompanying drawings and examples.Following embodiment it is detailed
Thin description and attached drawing cannot be used for limiting the scope of the invention for illustratively illustrating the principle of the present invention, i.e., of the invention
It is not limited to described embodiment, covers part, component and connection type under the premise of without departing from the spirit of the present invention
Any modification is replaced and is improved.
It should be noted that in the absence of conflict, the features in the embodiments and the embodiments of the present application can phase
Mutually combination.The application is described in detail below with reference to accompanying drawings and in conjunction with the embodiments.
In a first aspect, the present invention provides a kind of preparation method of the flexible honeycomb of heart-shaped cell, Fig. 2 is in preparation process
Middle heart mould is inserted into the status diagram in flexible honeycomb cell.The preparation method of the flexible honeycomb of heart-shaped cell includes following step
Rapid S110 ~ step S140:
Step S110 is to apply core bar glue, and core bar glue is coated the surface of flexible thin material is equally spaced using glue spreader.
Wherein, flexible thin material can be aramid paper, metal foil either other similar flexible thin plates etc..
In the present embodiment, the flexible thin material in the step uses NOMEX aramid papers, using glue spreader aramid paper side table
Face it is equally spaced coat core bar glue, can also be to be coated all in accordance with equally spaced mode in the both side surface up and down of aramid paper
Core bar glue, core bar glue can be the heat for bonding or generating bonding between the flexible thin material for honeycomb
Thermosetting resin material, the core bar glue specifically applied on the aramid paper of the present embodiment is using J-80B NOMEX paper honeycomb sandwiches
Adhesive.
Step S120 is bonded for lamination, is bonded according to the lamination of the mutually equally spaced dislocation of neighbouring two layers of core bar glue
Mode, flexible thin material's lamination that multilayer is coated with to core bar glue are bonded to form superimposed sheet.
In this step, in the flexible thin material that multilayer is coated with to core bar glue(Aramid paper 2)Successively carried out lamination
Bonding, needs to ensure the flexible thin material that adjacent upper layer and lower layer is mutually bonded in lamination process(Aramid paper 2)Between glued
The core bar glue connect mutually equally spaced dislocation each other, with ensure the adjacent core bar glue on each layer of flexible thin material respectively with the layer
The upper and lower be bonded.
Step S130 is hot-press solidifying, and the superimposed sheet is carried out hot pressing, makes the core adhesive curing of lamination abutting edge.
In this step, by layer flexible layer material(Aramid paper 2)Lamination is bonded the superimposed sheet to be formed and is placed on and core
It in the comparable temperature environment of glue thermoset condition, pressurizes, makes between each overlapping layers in the thickness direction of superimposed sheet
Core bar glue cures, so that the bonding between every layer of flexible thin layer is more secured.
Step S140 is drawing and forming, and the superimposed sheet after hot pressing is stretched, and superimposed sheet is made to be stretched in overlapping thickness direction
Exhibition can form the honeycomb of regular hexagon cell, then stretch into heart-shaped mould 1 in regular hexagon cell, and will using plate washer
The surrounding of honeycomb equipped with heart-shaped mould 1 is fixed, and honeycomb is made to be deformed into along the end to end heart of draw direction
Cell 4, heart-shaped cell 4 have arc flexible edge 5, wherein heart-shaped mould 1 be cross section be heart rod piece, heart-shaped cell 4 it
Between end to end place be core glue sticking at 3.The state that heart-shaped mould 1 is inserted into flexible honeycomb cell is shown in Figure 1.
In this step, can in the fixed tension belt of the top layer of superimposed sheet and lowest level, by pull tension belt to
It overlaps thickness direction to stretch, when each lamination being made to be stretched over maximum position, the honeycomb of regular hexagon cell can be formed.So
Afterwards by heart-shaped mould 1 be inserted into cell in, as shown in Figure 1, the heart mould 1 is cross section be heart hollow stem or solid hopkinson bar, this reality
Apply heart-shaped mould of the example using hollow rod.
In addition, the preparation method of the flexible honeycomb of the heart-shaped cell 4 of the present invention can also include the following steps S150 ~ step
S170:
Step S150 is heat-shaping, that is, the honeycomb equipped with heart-shaped mould 1 is put into shaping baking oven, makes honeycomb
The unit of heart-shaped cell 4 is shaped.
In this step, honeycomb is placed in 265 DEG C ± 5 DEG C of oven temperature environment, keeps the temperature 20 ± 5min, made each
Heart-shaped cell 4 is shaped.
Step S160 is form removal impregnation, that is, after the above step is finished, by heart-shaped mould 1 and plate washer from the honeycomb after sizing
It is removed in structure.Then the honeycomb of heart-shaped cell 4 is subjected to gum dipping process.
Step S170 cuts for cured sheets, that is, the honeycomb after impregnation is carried out baking and curing, then according to compact dimensions
It is required that progress sawing or piece cut processing, the flexible honeycomb structure of the heart-shaped cell 4 of predetermined dimension is obtained.(Referring to Fig. 2)
In practice, the mode that impregnating resin may be used carries out gum dipping process, then after the completion of impregnation, can use heating or
Air-dried mode has made baking and curing.
Second aspect, as shown in Fig. 2, the present invention provides a kind of heart-shaped cells prepared by the preparation method by first aspect
Flexible honeycomb.The cell of the flexible honeycomb is end to end heart-shaped cell 4, the end to end place between the heart cell 4
It is at core glue sticking 3,3 both sides are the flexible edge 5 of arc at core glue sticking.It is, foramen cordiforme adjacent to each other
The common edge of lattice 4 is the flexible edge 5 of arc.
To sum up, the flexible honeycomb for the heart-shaped cell that prepared by the present invention at core glue sticking with it is outer be arc flexibility
Side has preferably respectively to flexibility, while having physically better and chemical property, and preparation method is simple, saves production
Cost when the flexible honeycomb of the heart cell is as core structure, not will produce structural damage in process, the present invention
The flexible honeycomb of heart-shaped cell be applicable to the more stringent field of use condition.
It should be clear that each embodiment in this specification is described in a progressive manner, each embodiment it
Between just to refer each other for same or analogous part, the highlights of each of the examples are it is different from other embodiment it
Place.For the embodiment of product, related place can be found in the part explanation of embodiment of the method.The invention is not limited in upper
Literary particular step described and shown in figure and structure.Also, it for brevity, omits here to known method technology
Detailed description.
Above is only an example of the present application, it is not restricted to the application.The scope of the present invention is not being departed from
In the case of to those skilled in the art, the application can have various modifications and variations.It is all in spirit herein and
Any modification, equivalent replacement, improvement and so within principle, should be included within the scope of claims hereof.
Claims (6)
1. a kind of preparation method of the flexible honeycomb of heart cell, which is characterized in that the preparation method includes:
Core bar glue is applied, core bar glue is coated the surface of flexible thin material is equally spaced using glue spreader;
Lamination is bonded, and according to the lamination bonding way of the mutually equally spaced dislocation of neighbouring two layers of core bar glue, multilayer is applied
There is flexible thin material's lamination of core bar glue to be bonded to form superimposed sheet;
The superimposed sheet is carried out hot pressing, makes the core adhesive curing of lamination abutting edge by hot-press solidifying;
Drawing and forming stretches the superimposed sheet after the hot pressing, makes the superimposed sheet that can be formed just in overlapping thickness direction stretching, extension
Then the honeycomb of hexagon cell stretches into heart-shaped mould in the cell, and utilize plate washer by the honeycomb equipped with heart-shaped mould
The surrounding of structure is fixed, and the honeycomb is made to be deformed into along the end to end heart-shaped cell of draw direction, the heart
Cell has the flexible edge of arc, wherein the heart mould is the rod piece that cross section is heart, the head between the heart cell
Tail joint is at core glue sticking.
2. the preparation method of the flexible honeycomb of heart cell according to claim 1, which is characterized in that be drawn into described
Further include after type step:
The honeycomb equipped with heart-shaped mould is put into shaping baking oven by heat-shaping, and the heart-shaped cell is made to shape;
Form removal impregnation is removed the heart-shaped mould and the plate washer, then by the heart from the honeycomb after sizing
The honeycomb impregnation of shape cell;
Cured sheets are cut, and the honeycomb after impregnation is carried out baking and curing, are then required to carry out sawing according to compact dimensions
Or piece cuts processing, obtains the flexible honeycomb structure of the heart-shaped cell of predetermined dimension.
3. the preparation method of the flexible honeycomb of heart cell according to claim 2, which is characterized in that solid in the sizing
In the step of change, the honeycomb is placed in 265 DEG C ± 5 DEG C of oven temperature environment, keeps the temperature 20 ± 5min, make the heart
Shape cell is shaped.
4. the preparation method of the flexible honeycomb of heart cell according to claim 1, which is characterized in that the flexible thin layer
Material uses aramid paper or metal foil.
5. it is according to claim 1 heart cell flexible honeycomb preparation method, which is characterized in that it is described heart mould be
Cross section is the hollow stem or solid hopkinson bar of heart.
6. a kind of flexible honeycomb of heart cell, which is characterized in that the flexible honeycomb of the heart cell uses claim 1 institute
The method stated prepares molding, and the cell of the flexible honeycomb is end to end heart-shaped cell, the head between the heart cell
Tail joint is at core glue sticking, and the both sides at the core glue sticking are the flexible edge of arc.