CN108516794A - Ceramic tile capable of purifying air and preparation method thereof - Google Patents
Ceramic tile capable of purifying air and preparation method thereof Download PDFInfo
- Publication number
- CN108516794A CN108516794A CN201810438963.8A CN201810438963A CN108516794A CN 108516794 A CN108516794 A CN 108516794A CN 201810438963 A CN201810438963 A CN 201810438963A CN 108516794 A CN108516794 A CN 108516794A
- Authority
- CN
- China
- Prior art keywords
- parts
- ceramic tile
- diopside
- purifying air
- soil
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to building material fields, and in particular to ceramic tile capable of purifying air and preparation method thereof.Ceramic tile is formed by following raw material proportioning：57 parts of highly dense porcelain stone, 11 13 parts of diopside, 79 parts of three-level diopside, 57 parts of base slag, 11 13 parts of Zhucheng soil, 11 13 parts of Laiyang soil, saturating white 9 11 parts of stone, 26 28 parts of green coke, 57 parts of white clay, 0.8 1.3 parts of nano-titanium dioxide.The preparation method of the ceramic tile, includes the following steps：1, weigh each raw material by formula rate, it is ground, except iron, sieving after, mud is made；2, by mud through drying, the aging, green compact of homogenizing be molded and drying after obtain ceramic tile blank；3, ceramic tile blank is put into kiln, is molded through high-temperature firing.For this ceramic tile under natural light and ultraviolet light, the toxic gases such as energy degradation of formaldehyde remove ceramic tile surface greasy dirt and bacterium, beautification household capable of purifying air.
Description
Technical field
The present invention relates to building material fields, and in particular to ceramic tile capable of purifying air and preparation method thereof.
Background technology
As society is constantly progressive and the increasingly raising of people's quality of life, people get over the environmental issue of house fitting-up
More to pay attention to.In household fitment process, common interior decoration and ornament materials, such as artificial floor, paint wall covering fabric and
Adhesive etc., can release the toxic gases such as formaldehyde, stupid, dimethylbenzene, these toxic gases can generate health very big
Harm.
Ceramic tile has extensive and a large amount of application as a kind of domestic finishing material in fitting up indoors.But traditional ceramic tile
It has a single function, cannot effectively degrade the toxic gases such as indoor formaldehyde, stupid, dimethylbenzene.
Invention content
It is an object of the present invention to provide a kind of ceramic tiles capable of purifying air and preparation method thereof, to solve traditional ceramic tile
It has a single function, cannot degrade the toxic gases problem such as indoor formaldehyde, stupid, dimethylbenzene.
To achieve the above object, an embodiment of the present invention provides following technical solutions：
Ceramic tile capable of purifying air is formed by the raw material proportioning of following parts by weight：Highly dense porcelain stone 5-7 parts, diopside 11-13
Part, 7-9 parts of three-level diopside, 5-7 parts of base slag, soil 11-13 parts of Zhucheng, soil 11-13 parts of Laiyang, saturating white 9-11 parts of stone, green coke 26-
28 parts, 5-7 parts of white clay, 0.8-1.3 parts of nano-titanium dioxide.
Preferably, the ceramic tile is formed by the raw material proportioning of following parts by weight：6.4 parts of highly dense porcelain stone, 12.1 parts of diopside,
8.4 parts of three-level diopside, 6.3 parts of base slag, 11.8 parts of Zhucheng soil, 11.8 parts of Laiyang soil, saturating white 9.2 parts of stone, 26.9 parts of green coke, in vain
6.1 parts of mud, 1 part of nano-titanium dioxide.
The preparation method of ceramic tile capable of purifying air, including following preparation process：
Step 1, by formula rate weigh highly dense porcelain stone, diopside, three-level diopside, base slag, Zhucheng soil, Laiyang soil, thoroughly
Bai Shi, green coke, white clay and nano-titanium dioxide, add water to be put into ball mill, after 8-9 hour grinds, remove iron, mistake
Sieve, is prepared into mud；
Step 2, the mud obtained by step 1 is passed through into spray drying tower powder, after gained powder is homogenized aging 24 hours,
Powder green compact after again will be aging is molded to obtain green compact, and green compact obtain ceramic tile blank after twenty minutes by dry kiln drying；
Step 3, step 2 gained ceramic tile blank is put into kiln, 40 is fired by preheating zone, zoneofoxidation and high-temperature region
Minute molding.
Preferably, in step 1, for raw material after grinding, it is 7-8 grams to tail over fineness.
Preferably, in step 2, powder of the mud after spray drying tower, moisture content 6.8-7.2%, green compact
The ceramic tile blank of gained, moisture content 1.5-2.0% after dry kiln drying.
Preferably, in step 2, the temperature of dry kiln is between 290-220 DEG C.
Preferably, in step 3, the temperature of preheating zone is between 360-800 DEG C, and the temperature of zoneofoxidation is at 870-1050 DEG C
Between, the temperature of high-temperature region is between 1060-1070 DEG C.
Due to the adoption of the above technical scheme, compared with prior art, ceramic tile capable of purifying air of the invention has following
Advantageous effect：
Nano-titanium dioxide can activate under the action of daylight or ultraviolet light and generate very strong redox ability, energy
It is enough that the damage health such as volatile organic contaminant in air, including formaldehyde, acetaldehyde, stupid and dimethylbenzene is had into poison gas
Body oxidative degradation.Titanium dioxide is added among ceramic tile, under the action of natural light or ultraviolet light, can effectively degrade ground room
The toxic gases such as interior formaldehyde, stupid and dimethylbenzene, to achieve the purpose that purify air.
In addition to this, nano-titanium dioxide is added in ceramic tile, the substance for being adhered to ceramic tile surface includes greasy dirt and bacterium
Deng, can further being aoxidized under the catalytic action of nano-titanium dioxide, become gas or be easy to the substance wiped so that porcelain
Brick has better performance, can beautify household.
Specific implementation mode
The present invention is described in further detail with reference to specific embodiment.Obviously, specific embodiment is only used for retouching
The bright present invention is stated, protection scope of the present invention is not intended to limit.
Specific embodiment 1
Ceramic tile capable of purifying air is formed by the raw material proportioning of following parts by weight：5 parts of highly dense porcelain stone, 11 parts of diopside, three
7 parts of diopside of grade, 5 parts of base slag, 11 parts of Zhucheng soil, 11 parts of Laiyang soil, saturating white 9 parts of stone, 26 parts of green coke, 5 parts of white clay, nano-silica
Change 0.8 part of titanium.
The preparation method of the ceramic tile capable of purifying air, includes the following steps：
Step 1, by formula rate weigh highly dense porcelain stone, diopside, three-level diopside, base slag, Zhucheng soil, Laiyang soil, thoroughly
Bai Shi, green coke, white clay and nano-titanium dioxide are added a certain proportion of water and are put into ball mill, are ground by 8-9 hour
Reach 7-8 grams tail over fineness requirement after, through remove iron, sieving, be prepared into mud；
Step 2, the mud obtained by step 1 is passed through into spray drying tower powder, obtains the powder that moisture content is 6.8-7.2%
Material, after powder is homogenized aging 24 hours, then will be aging after powder green compact be molded to obtain green compact, green compact are 290 DEG C through excess temperature
Drying kiln drying 20 minutes, obtain the ceramic tile blank that moisture content is 1.5-2.0%；
Step 3, step 2 gained ceramic tile blank is put into kiln, by 360 DEG C of preheating zone, 870 DEG C of zoneofoxidation
With 1060 DEG C of high-temperature regions, fires 40 minutes and be molded.
Specific embodiment 2
Ceramic tile capable of purifying air is formed by the raw material proportioning of following parts by weight：7 parts of highly dense porcelain stone, 13 parts of diopside, three
9 parts of diopside of grade, 7 parts of base slag, 13 parts of Zhucheng soil, 13 parts of Laiyang soil, saturating white 11 parts of stone, 28 parts of green coke, 7 parts of white clay, nanometer two
1.3 parts of titanium oxide.
The preparation method of the ceramic tile capable of purifying air, includes the following steps：
Step 1, by formula rate weigh highly dense porcelain stone, diopside, three-level diopside, base slag, Zhucheng soil, Laiyang soil, thoroughly
Bai Shi, green coke, white clay and nano-titanium dioxide are added a certain proportion of water and are put into ball mill, are ground by 8-9 hour
Reach 7-8 grams tail over fineness requirement after, through remove iron, sieving, be prepared into mud；
Step 2, the mud obtained by step 1 is passed through into spray drying tower powder, obtains the powder that moisture content is 6.8-7.2%
Material, after powder is homogenized aging 24 hours, then will be aging after powder green compact be molded to obtain green compact, green compact are 220 DEG C through excess temperature
Drying kiln drying after twenty minutes, obtain moisture content be 1.5-2.0% ceramic tile blank；
Step 3, step 2 gained ceramic tile blank is put into kiln, by 800 DEG C of preheating zone, 1050 DEG C of oxidation
Area and 1070 DEG C of high-temperature regions are fired 40 minutes and are molded.
Specific embodiment 3
Ceramic tile capable of purifying air is formed by the raw material proportioning of following parts by weight：6.4 parts of highly dense porcelain stone, diopside 12.1
Part, 8.4 parts of three-level diopside, 6.3 parts of base slag, 11.8 parts of Zhucheng soil, 11.8 parts of Laiyang soil, saturating white 9.2 parts of stone, green coke 26.9
Part, 6.1 parts of white clay, 1 part of nano-titanium dioxide.
Step 1, by formula rate weigh highly dense porcelain stone, diopside, three-level diopside, base slag, Zhucheng soil, Laiyang soil, thoroughly
Bai Shi, green coke, white clay and nano-titanium dioxide are added a certain proportion of water and are put into ball mill, are ground by 8-9 hour
Reach 7-8 grams tail over fineness requirement after, through remove iron, sieving, be prepared into mud；
Step 2, the mud obtained by step 1 is passed through into spray drying tower powder, obtains the powder that moisture content is 6.8-7.2%
Material, after powder is homogenized aging 24 hours, then will be aging after powder green compact be molded to obtain green compact, green compact are 250 DEG C through excess temperature
Drying kiln drying after twenty minutes, obtain moisture content be 1.5-2.0% ceramic tile blank；
Step 3, step 2 gained ceramic tile blank is put into kiln, by 600 DEG C of preheating zone, 950 DEG C of zoneofoxidation
With 1060 DEG C of high-temperature regions, fires 40 minutes and be molded.
In above three embodiments, it refers to every 100 grams of mud after 250 mesh analysis sieve that 7-8 grams, which tails over fineness, is tailed over
7-8 grams.
Under the action of natural light or ultraviolet light, the titanium dioxide in ceramic tile of the present invention has very strong oxidability,
The formaldehyde in air, stupid, dimethylbenzene etc. of can effectively degrading damage the toxic gas of health, will be adhered to the oil of ceramic tile surface
Dirty and bacterial decomposition and harmless treatment are played the role of purifying air beautification household.And in this process, two in ceramic tile
As a kind of photochemical catalyst, itself will not change and be lost titanium oxide, can under natural light and ultraviolet irradiation
With the toxic gas in continual purification air, and titanium dioxide is nontoxic, safe to the human body reliable, so this hair
It is bright environmentally protective, it is nontoxic and low energy consumption.
The above is all the preferred embodiment of the present invention, and protection scope of the present invention is not limited to above-described embodiment,
All other technologies schemes belonged under thinking of the present invention all belong to the scope of protection of the present invention.It should be pointed out that in no disengaging sheet
Under the premise of inventive principle, several improvements and modifications that those of ordinary skill in the art are made, these improvements and modifications should also regard
For protection scope of the present invention.
Claims (7)
1. ceramic tile capable of purifying air, which is characterized in that ceramic tile is formed by the raw material proportioning of following parts by weight：Highly dense porcelain stone 5-7
Part, 11-13 parts of diopside, 7-9 parts of three-level diopside, 5-7 parts of base slag, soil 11-13 parts of Zhucheng, soil 11-13 parts of Laiyang, saturating white stone
9-11 parts, 26-28 parts of green coke, 5-7 parts of white clay, 0.8-1.3 parts of nano-titanium dioxide.
2. ceramic tile capable of purifying air according to claim 1, which is characterized in that the ceramic tile by following parts by weight original
Material matches：6.4 parts of highly dense porcelain stone, 12.1 parts of diopside, 8.4 parts of three-level diopside, 6.3 parts of base slag, 11.8 parts of Zhucheng soil,
11.8 parts of Laiyang soil, saturating white 9.2 parts of stone, 26.9 parts of green coke, 6.1 parts of white clay, 1 part of nano-titanium dioxide.
3. the preparation method of ceramic tile capable of purifying air according to claim 1, which is characterized in that including preparing step as follows
Suddenly：
Step 1, by formula rate weigh highly dense porcelain stone, diopside, three-level diopside, base slag, Zhucheng soil, Laiyang it is native, thoroughly white stone,
Green coke, white clay and nano-titanium dioxide are added a certain proportion of water and are put into ball mill, after 8-9 hour grinds, remove
Iron, sieving, is prepared into mud；
Step 2, the mud obtained by step 1 is passed through into spray drying tower powder, after gained powder is homogenized aging 24 hours, then will
Powder green compact after aging is molded to obtain green compact, and green compact obtain ceramic tile blank after twenty minutes by dry kiln drying；
Step 3, step 2 gained ceramic tile blank is put into kiln, is fired 40 minutes by preheating zone, zoneofoxidation and high-temperature region
Molding.
4. the preparation method of ceramic tile capable of purifying air according to claim 3, which is characterized in that in step 1, raw material warp
After crossing grinding, it is 7-8 grams to tail over fineness.
5. the preparation method of ceramic tile capable of purifying air according to claim 3, which is characterized in that in step 2, mud warp
Cross the powder after spray drying tower, moisture content 6.8-7.2%, the ceramic tile blank of green compact gained after dry kiln drying,
Its moisture content 1.5-2.0%.
6. the preparation method of ceramic tile capable of purifying air according to claim 3, which is characterized in that in step 2, dry kiln
Temperature at 290-220 DEG C.
7. the preparation method of ceramic tile capable of purifying air according to claim 3, which is characterized in that in step 3, preheating zone
Temperature is between 360-800 DEG C, and zoneofoxidation temperature is between 870-1050 DEG C, and high-temperature region temperature is between 1060-1070 DEG C.