CN108505715A - 一种高导热且使用寿命长的电热瓷砖及制作方法 - Google Patents
一种高导热且使用寿命长的电热瓷砖及制作方法 Download PDFInfo
- Publication number
- CN108505715A CN108505715A CN201810339192.7A CN201810339192A CN108505715A CN 108505715 A CN108505715 A CN 108505715A CN 201810339192 A CN201810339192 A CN 201810339192A CN 108505715 A CN108505715 A CN 108505715A
- Authority
- CN
- China
- Prior art keywords
- ceramic
- high heat
- tile
- thin plate
- glue
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
原料 | 台山中温砂 | 莲塘中温砂 | 新丰砂 | 中山石粉 | 北海石粉 |
重量百分比 | 2 | 2 | 12 | 7 | 22 |
原料 | 四会泥 | 新会泥 | 滑石粉 | 铝矾土 | 锂辉石 |
重量百分比 | 9 | 13 | 4 | 19 | 10 |
化学成分 | 氧化硅 | 氧化铝 | 氧化铁 | 氧化钛 | 氧化钙 |
百分比 | 62.44 | 28.61 | 1.2 | 0.84 | 0.3 |
化学成分 | 氧化镁 | 氧化钾 | 氧化钠 | 氧化锂 | 杂质 |
百分比 | 1.29 | 2.24 | 1.85 | 0.6 | 余量 |
原料 | 台山中温砂 | 莲塘中温砂 | 新丰砂 | 中山石粉 | 北海石粉 |
重量百分比 | 2.5 | 2.5 | 11 | 7.5 | 21 |
原料 | 四会泥 | 新会泥 | 滑石粉 | 铝矾土 | 锂辉石 |
重量百分比 | 7.5 | 16 | 2.5 | 20 | 9.5 |
化学成分 | 氧化硅 | 氧化铝 | 氧化铁 | 氧化钛 | 氧化钙 |
百分比 | 62.5 | 29.55 | 1.23 | 0.85 | 0.28 |
化学成分 | 氧化镁 | 氧化钾 | 氧化钠 | 氧化锂 | 杂质 |
百分比 | 0.94 | 2.21 | 1.88 | 0.55 | 余量 |
化学成分 | 氧化硅 | 氧化铝 | 氧化铁 | 氧化钛 | 氧化钙 |
百分比 | 61.99 | 29.9 | 1.25 | 0.87 | 0.29 |
化学成分 | 氧化镁 | 氧化钾 | 氧化钠 | 氧化锂 | 杂质 |
百分比 | 1.06 | 2.27 | 1.86 | 0.5 | 余量 |
原料 | 台山中温砂 | 莲塘中温砂 | 新丰砂 | 中山石粉 | 北海石粉 |
重量百分比 | 3.5 | 3.5 | 9 | 8.5 | 19 |
原料 | 四会泥 | 新会泥 | 滑石粉 | 铝矾土 | 锂辉石 |
重量百分比 | 8.5 | 14 | 3.5 | 22 | 8.5 |
化学成分 | 氧化硅 | 氧化铝 | 氧化铁 | 氧化钛 | 氧化钙 |
百分比 | 61.5 | 3.02 | 1.27 | 0.89 | 0.3 |
化学成分 | 氧化镁 | 氧化钾 | 氧化钠 | 氧化锂 | 杂质 |
百分比 | 1.17 | 2.28 | 1.87 | 0.45 | 余量 |
原料 | 台山中温砂 | 莲塘中温砂 | 新丰砂 | 中山石粉 | 北海石粉 |
重量百分比 | 4 | 4 | 8 | 9 | 18 |
原料 | 四会泥 | 新会泥 | 滑石粉 | 铝矾土 | 锂辉石 |
重量百分比 | 7 | 17 | 2 | 23 | 8 |
化学成分 | 氧化硅 | 氧化铝 | 氧化铁 | 氧化钛 | 氧化钙 |
百分比 | 61.57 | 30.5 | 1.3 | 0.91 | 0.28 |
化学成分 | 氧化镁 | 氧化钾 | 氧化钠 | 氧化锂 | 杂质 |
百分比 | 0.81 | 2.3 | 2.3 | 0.4 | 余量 |
原料 | 石英砂 | 粘土 | 长石 |
重量百分比 | 30 | 40 | 30 |
项目 | 导热系数 | 成品厚度 | 成品强度 | 吸水率 | 烧成周期 | 烧成温度 |
实施方式1 | 3.5W/m·K | 6~7mm | ≥27MPa | 0.01% | 52min | 1185℃ |
实施方式2 | 3W/m·K | 6~7mm | ≥27MPa | 0.01% | 56min | 1185℃ |
实施方式3 | 3W/m·K | 6~7mm | ≥27MPa | 0.01% | 60min | 1185℃ |
实施方式4 | 2.5W/m·K | 6~7mm | ≥27MPa | 0.01% | 64min | 1185℃ |
实施方式5 | 2.5W/m·K | 6~7mm | ≥27MPa | 0.01% | 68min | 1185℃ |
对比例 | 1.3~1.5W/m·K | 12~18mm | ≥27MPa | 0.5% | 90min | 1250℃ |
Claims (10)