CN108500080A - A kind of stainless steel bars round-bar pass technique - Google Patents
A kind of stainless steel bars round-bar pass technique Download PDFInfo
- Publication number
- CN108500080A CN108500080A CN201810196193.0A CN201810196193A CN108500080A CN 108500080 A CN108500080 A CN 108500080A CN 201810196193 A CN201810196193 A CN 201810196193A CN 108500080 A CN108500080 A CN 108500080A
- Authority
- CN
- China
- Prior art keywords
- roller
- steel
- stainless steel
- finished product
- workpiece
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of stainless steel bars round-bar pass techniques, include the following steps：A, molding base is packed into heating furnace；B, by hot steel billet dephosphorization；C, roughing；D, it finishes；E, workpiece cools down；F, workpiece aligning and marshalling；G, sawing；H, finished product inspection；I, stacking and bundling；Simple production process of the present invention, production efficiency is high, can reduce stainless steel bars surface defect and internal flaw, improve product qualification rate.
Description
Technical field
The present invention relates to stainless steel round steel technical field, specially a kind of stainless steel bars round-bar pass technique.
Background technology
Stainless steel bars are by stainless steel ingot, made of hot rolling or forging；Can substantially it be divided by shape point:No
Become rusty steel pole, stainless steel square rod, stainless steel hexagonal bar；It can be divided by surface treatment point:The sour white stick of the black stick of stainless steel, stainless steel,
Stainless steel light stick, stainless-steel grinding stick.
Stainless steel bars round-bar pass complex process at present, obtained product defects rate is high, and product qualification rate is low, therefore,
It is further improved.
Invention content
The purpose of the present invention is to provide a kind of stainless steel bars round-bar pass techniques, to solve to carry in above-mentioned background technology
The problem of going out.
To achieve the above object, the present invention provides the following technical solutions：A kind of stainless steel bars round-bar pass technique, including
Following steps：
A, molding base is packed into heating furnace：It is transferred to from die casting machine ejection roller way by lateral machine for moving steel is single during normal production
In heating furnace approach table, steel billet weighed and surveyed in heating furnace approach table it is long after be admitted to walking beam heating furnace into
Row heating；
B, by hot steel billet dephosphorization：After being heated to set temperature by the heating schedule of setting, hot steel billet is put into tapping by extractor
Descaling mill is transported on roller-way carries out dephosphorization；
C, roughing：Steel billet of coming out of the stove removes the iron scale of billet surface by high-pressure water descaler first；The later steel of de-scaling
Base is sent to the 2 thick units of frame two-roller reversible through thick unit approach table and is processed, thick unit maximum roller diameter 1350mm, barrel length
2800mm；
D, it finishes；
E, workpiece cools down：Workpiece carries out cooling treatment by being sent to cold bed through roller-way；
F, workpiece aligning and marshalling：Lower cold bed workpiece is sent by roller-way to being aligned on on-line straightening machine, and straightener is 9 roller gate-types
Pitches straightener；
G, sawing：Workpiece after aligning is subjected to sawing using scale cold saw；
H, finished product inspection：The later rolled piece of sawing is sent to finished product inspection with roller-way, and defective product is routed directly to waste collection
Platform；Qualified products are then sent to finished product piler, and stacking is carried out on size piling bed respectively according to product length；
I, stacking and bundling：The rolled piece that scale is cut by cold saw transports piler to and carries out stacking, and height of embankment is up to 500 millimeters, right
Shaped steel carries out occlusion method stacking, and the good finished product pile of 180 ° of heaps can need to be overturn per alternating floor steel by stacking requirement send through roller-way to beating
At bundle machine；Marking press imprints label, and metal tag is tied up by manually hanging over steel.
Preferably, finished steel bundle is transported to products storage platform after the step I is completed, by workshop electromagnetism lifting
Finished product bundle is hoisted to warehouse for finished product storage to machine by two bundles every time.
Preferably, set temperature is 1200~1250 DEG C in the step B.
Preferably, finishing machine by 1 frame, two roller unit and the omnipotent unit of 1 frame and forms in the step D, and processing is I-shaped
Product is processed using omnipotent roller system；Processing angle steel, round steel and channel steel are processed with two roller roller systems；It can be opened on the body of roll of two roller roller systems more
A groove makes hole slot be directed at machining center line with the method for traversing rack.
Compared with prior art, the beneficial effects of the invention are as follows：Simple production process of the present invention, production efficiency is high, can
Stainless steel bars surface defect and internal flaw are reduced, product qualification rate is improved；Wherein, the present invention is direct using molding steel billet
Hot delivery and hot charging technology reduces ton steel cost；And enter stove blank and weigh automatically, it may be implemented to optimize steel rolling, improve lumber recovery.
Description of the drawings
Fig. 1 is flow chart of the present invention.
Specific implementation mode
Following will be combined with the drawings in the embodiments of the present invention, and technical solution in the embodiment of the present invention carries out clear, complete
Site preparation describes, it is clear that described embodiments are only a part of the embodiments of the present invention, instead of all the embodiments.It is based on
Embodiment in the present invention, it is obtained by those of ordinary skill in the art without making creative efforts every other
Embodiment shall fall within the protection scope of the present invention.
Referring to Fig. 1, the present invention provides a kind of technical solution：A kind of stainless steel bars round-bar pass technique, including it is following
Step：
A, molding base is packed into heating furnace：It is transferred to from die casting machine ejection roller way by lateral machine for moving steel is single during normal production
In heating furnace approach table, steel billet weighed and surveyed in heating furnace approach table it is long after be admitted to walking beam heating furnace into
Row heating；
B, by hot steel billet dephosphorization：After being heated to set temperature by the heating schedule of setting, set temperature is 1200~1250 DEG C,
Hot steel billet is put on tapping roller-way and transports to descaling mill progress dephosphorization by extractor；
C, roughing：Steel billet of coming out of the stove removes the iron scale of billet surface by high-pressure water descaler first；The later steel of de-scaling
Base is sent to the 2 thick units of frame two-roller reversible through thick unit approach table and is processed, thick unit maximum roller diameter 1350mm, barrel length
2800mm, according to the difference of product variety and specification, workpiece processes 7~13 passages on thick unit, is furnished with before and after thick unit and pushes away
Bed tilting gear, the guide beam of unit are mounted on working roll bearing block, and when replacement is replaced with working roll；
D, it finishes；
E, workpiece cools down：Workpiece carries out cooling treatment by being sent to cold bed through roller-way, and the maximum length of rolled piece that cold bed can accommodate does not surpass
76 meters are crossed, sets 1 cropping sampling hot saw in cold-bed run-in table, hot saw undertakes the cutting sample of the task simultaneously, is cut
Sample by below roller-way sample conveyer export, segmentation with sampling saw a diameter of 1600~1800 millimeters of saw blade；Cold bed has
There are pre-bending function, round steel to be then collected by the collecting frame at cold-bed run-in table rear portion directly by hot saw scale；
F, workpiece aligning and marshalling：Lower cold bed workpiece is sent by roller-way to being aligned on on-line straightening machine, and straightener is 9 roller gate-types
Pitches straightener, first, nine rollers are driven by hydraulic motor, remaining seven roller by seven frequency controls alternating current generator, maximum rectify
1~3 meter per second of straight speed；
G, sawing：Workpiece after aligning is subjected to sawing, wherein running saw 1, fixed saw 1 using scale cold saw, in fixation
Shear gauge one, 6~18 meters of sawing steel cut lengths are set after saw；
H, finished product inspection：The later rolled piece of sawing is sent to finished product inspection with roller-way, by three finished product inspection platforms, width 2*12
Rice, 18 meters, defective product, by manually carrying out, is routed directly to waste collection platform by the shape of product with surface quality inspection；It closes
Lattice product is then sent to finished product piler, and stacking is carried out on size piling bed respectively according to product length；
I, stacking and bundling：The rolled piece that scale is cut by cold saw transports piler to and carries out stacking, and height of embankment is up to 500 millimeters, right
Shaped steel carries out occlusion method stacking, and the good finished product pile of 180 ° of heaps can need to be overturn per alternating floor steel by stacking requirement send through roller-way to beating
At bundle machine；Marking press imprints label, and metal tag is tied up by manually hanging over steel.
Finished steel bundle is finally transported to products storage platform, two bundles hang finished product bundle every time by workshop electromagnetic lifter
It is transported to warehouse for finished product storage.
In the present invention, finishing machine by 1 frame, two roller unit and the omnipotent unit of 1 frame and forms in step D, processes I-shaped production
Product are processed using omnipotent roller system；Processing angle steel, round steel and channel steel are processed with two roller roller systems；It can be opened on the body of roll of two roller roller systems multiple
Groove makes hole slot be directed at machining center line with the method for traversing rack.
In conclusion simple production process of the present invention, production efficiency is high, can reduce stainless steel bars surface defect and interior
Portion's defect, improves product qualification rate；Wherein, the present invention reduces ton steel cost using the molding direct hot delivery and hot charging technology of steel billet；
And enter stove blank and weigh automatically, it may be implemented to optimize steel rolling, improve lumber recovery.
It although an embodiment of the present invention has been shown and described, for the ordinary skill in the art, can be with
Understanding without departing from the principles and spirit of the present invention can carry out these embodiments a variety of variations, modification, replace
And modification, the scope of the present invention is defined by the appended.
Claims (4)
1. a kind of stainless steel bars round-bar pass technique, it is characterised in that：Include the following steps：
A, molding base is packed into heating furnace：It is transferred to from die casting machine ejection roller way by lateral machine for moving steel is single during normal production
In heating furnace approach table, steel billet weighed and surveyed in heating furnace approach table it is long after be admitted to walking beam heating furnace into
Row heating；
B, by hot steel billet dephosphorization：After being heated to set temperature by the heating schedule of setting, hot steel billet is put into tapping by extractor
Descaling mill is transported on roller-way carries out dephosphorization；
C, roughing：Steel billet of coming out of the stove removes the iron scale of billet surface by high-pressure water descaler first；The later steel of de-scaling
Base is sent to the 2 thick units of frame two-roller reversible through thick unit approach table and is processed, thick unit maximum roller diameter 1350mm, barrel length
2800mm；
D, it finishes；
E, workpiece cools down：Workpiece carries out cooling treatment by being sent to cold bed through roller-way；
F, workpiece aligning and marshalling：Lower cold bed workpiece is sent by roller-way to being aligned on on-line straightening machine, and straightener is 9 roller gate-types
Pitches straightener；
G, sawing：Workpiece after aligning is subjected to sawing using scale cold saw；
H, finished product inspection：The later rolled piece of sawing is sent to finished product inspection with roller-way, and defective product is routed directly to waste collection
Platform；Qualified products are then sent to finished product piler, and stacking is carried out on size piling bed respectively according to product length；
I, stacking and bundling：The rolled piece that scale is cut by cold saw transports piler to and carries out stacking, and height of embankment is up to 500 millimeters, right
Shaped steel carries out occlusion method stacking, and the good finished product pile of 180 ° of heaps can need to be overturn per alternating floor steel by stacking requirement send through roller-way to beating
At bundle machine；Marking press imprints label, and metal tag is tied up by manually hanging over steel.
2. a kind of stainless steel bars round-bar pass technique according to claim 1, it is characterised in that：The step I is completed
Finished steel bundle is transported to products storage platform later, finished product bundle is hoisted to finished product by two bundles every time by workshop electromagnetic lifter
Inventory is put.
3. a kind of stainless steel bars round-bar pass technique according to claim 1, it is characterised in that：It is set in the step B
Constant temperature degree is 1200~1250 DEG C.
4. a kind of stainless steel bars round-bar pass technique according to claim 1, it is characterised in that:It is smart in the step D
Processing machine is by 1 frame, two roller unit and the omnipotent unit of 1 frame and forms, and processes I-shaped product and is processed using omnipotent roller system；Process angle
Steel, round steel and channel steel are processed with two roller roller systems；Multiple grooves can be opened on the body of roll of two roller roller systems, make hole with the method for traversing rack
Slot is directed at machining center line.