CN108487564A - A kind of fibre web composite zeolite diatom ooze coating - Google Patents
A kind of fibre web composite zeolite diatom ooze coating Download PDFInfo
- Publication number
- CN108487564A CN108487564A CN201810307960.0A CN201810307960A CN108487564A CN 108487564 A CN108487564 A CN 108487564A CN 201810307960 A CN201810307960 A CN 201810307960A CN 108487564 A CN108487564 A CN 108487564A
- Authority
- CN
- China
- Prior art keywords
- zeolite
- fibre web
- diatom ooze
- coating
- ooze coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of fibre web composite zeolite diatom ooze coating, its key points of the technical solution are that：One layer of fibre web is set in the metope base of wall, and fibre web is fixed in metope base, again zeolite diatom ooze coating be sprayed in fibre web mesh and metope base on, while ensureing zeolite diatom ooze coating coating thickness, fibre web protrusion is set to be higher than zeolite diatom ooze coating coating surface again, remove the zeolite diatom ooze coating being adhered on fibre web protrusion part with rag wiping, keep fibre web and metope base and zeolite diatom ooze coating adhesion compound, form wall, metope base, fibre web, zeolite diatom ooze coating lamination layer structure, generate anticollision, stain resistant, anti-crack, reduce difficulty of construction, the technique effect maintained easily, promote the progress and development of zeolite diatom ooze coating technology.
Description
Technical field
The present invention relates to a kind of Environment-friendlyinternal internal wall paint technical field, especially a kind of fibre web composite zeolite diatom ooze
Coating.
Background technology
In internal wall finishing, diatom ooze coating is in its good physical adsorption property and ion exchanging function removal air
The harmful substances such as free formaldehyde, benzene, ammonia and air in the environmental protection concept of peculiar smell be increasingly accepted, applicant also in
A kind of patent application of zeolite diatom ooze coating application No. is 2017108081369, but either diatom are applied within 2017
Slime paint or zeolite diatom ooze coating, all have the following disadvantages and defect：
1, diatom ooze, zeolite diatom ooze coating are that " mud " type coating anti-collision capacity is poor, collide and will damage once meeting object
Diatom ooze, zeolite diatom ooze coating coating surface not only influence beauty, and maintenance cost is high.
2, diatom ooze, zeolite diatom ooze coating are " mud " type coating stain resistant energy force differences, influence practicability, have in family small
The user of child does not select diatom ooze, zeolite diatom ooze coating generally.
3, diatom ooze, zeolite diatom ooze coating " mud " type coating adhesion strength are poor, are not only easy to cause part coatings coating
There is micro-crack, and in order to increase the adhesion strength of diatom ooze, zeolite diatom ooze coating, more or less contains in formula composition
Latex, cellulose and other raw materials for increasing composite layer overall construction intensity, affect diatom ooze, zeolite diatom ooze coating
Adsorption function.
Invention content
Zeolite diatom ooze coating finishing layer is a kind of lamination layer structure in fact, that is, makes Huo Cheongju reason metopes base, make metope
Base's adhesion is compound on wall, then zeolite diatom ooze coating adhesion is compound in metope base and forms a kind of zeolite diatom ooze
Coating lamination layer structure, this zeolite diatom ooze coating lamination layer structure is by wall, metope base, zeolite diatom ooze coating structure
At as long as one layer of fibre web of setting between the metope base and zeolite diatom ooze coating of wall, makes fibre web and metope
Base and zeolite diatom ooze coating adhesion are compound, and fibre web protrusion is made to be higher than zeolite diatom ooze coating coating surface, protrusion
And can be generated higher than the fibre web of zeolite diatom ooze coating coating surface prevents object head-on crash from damaging paint coatings, preventing
Only dirty impression of the hand, dirty footprint and other object Contamination Coatings coatings, improve zeolite diatom ooze coating composite layer overall construction intensity
Technique effect achievees the purpose that overcome insufficient and defect existing for above-mentioned zeolite diatom ooze coating.
The object of the present invention is to provide a kind of fibre web composite zeolite diatom ooze coatings, are set in the metope base of wall
It sets one layer of fibre web and metope base and zeolite diatom ooze coating adhesion is compound, change zeolite diatom ooze coating composite layer knot
Structure overcomes existing for above-mentioned zeolite diatom ooze coating insufficient and defect, promote zeolite diatom ooze interior wall coating technology progress and
Development.
The present invention realizes that the technical solution of above-mentioned purpose is：One layer of fibre web is set in the metope base of wall, and
And fibre web is fixed in metope base, then zeolite diatom ooze coating is sprayed in fibre web mesh and metope base
On, while ensureing zeolite diatom ooze coating coating thickness, and fibre web protrusion is made to be higher than zeolite diatom ooze coating coating
Surface removes the zeolite diatom ooze coating being adhered on fibre web protrusion part with rag wiping, makes fibre web and metope
Base and zeolite diatom ooze coating adhesion are compound, form wall, metope base, fibre web, zeolite diatom ooze coating composite layer
Structure generates anticollision, stain resistant, anti-crack, the technique effect for reducing difficulty of construction, maintaining easily, and improves zeolite
Diatom ooze coating composite layer overall construction intensity can cancel organic adhesive raw material and fiber in zeolite diatom ooze coating formula
Plain raw material, and then science adjusts zeolite diatom ooze coating formula, improves zeolite diatom ooze coating properties of product, promotes zeolite diatom
The progress and development of mud interior wall coating technology.
Zeolite diatom ooze coating of the present invention is by weight percentage, composed of the following components：Zeolite powder 20~40%；
Diatomite 20~40%；Nano-titanium dioxide 1~3%；Titanium dioxide 8~15%；White carbon 5~15%；Kaolin 5~15%；Sierozem power
5~10%.
Zeolite powder of the present invention is clinoptilolite or modenite powder, 200~1250 mesh.
Diatomite of the present invention is the mesh of 120 mesh~325.
Titanium dioxide of the present invention is rutile-type, and content of titanium dioxide is more than 95%.
White carbon of the present invention is white carbon prepared by vapor phase method, or using nonmetallic ore and its extension as silicon source, is adopted
The white carbon prepared with the precipitation method.
Kaolin of the present invention is kaolin powder of 600~800 mesh through calcining, and whiteness is more than 90.
Fibre web of the present invention is that the silk screen that regenerated fiber is made into or regenerated fiber grid cloth, synthetic fibers are made into
The silk screen that the silk screen or inorfil grid cloth, low-melting fiber that silk screen or synthetic fibers grid cloth, inorfil are made into are made into
Or low-melting fiber grid cloth.
Regenerated fiber of the present invention is the regenerated fibers such as viscose fiber, acetate fiber.
Synthetic fibers of the present invention are the synthetic fibers such as polyamide fibre, terylene, acrylic fibers, polyvinyl, nylon.
Inorfil of the present invention is glass fibre, rustless metallic fiber.
Low-melting fiber of the present invention be using low-melting point polyester and normal polyester as raw material, it is micro- from same spinneret after melting
Hole squeezes out, and forms the composite fibre of skin-core structure.
Fibre web mesh area of the present invention is higher than the filament of zeolite diatom ooze coating coating surface to protrude
Net can generate anticollision, the technique effect of stain resistant is standard setting.
The fixed form of the present invention that fibre web is fixed in metope base is：
1, fibre web is fixed in metope base with rustless fastener；
2, when making or clearing up metope base, fibre web is adhered in metope base, with roller in the online Roll of filament
Pressure makes fibre web adhesion composite solid due in metope base.
Compared with prior art, the invention has the advantages that：
1, present invention employs fibre web and metope base and zeolite diatom ooze coating are compound, a kind of fibre web and wall are formed
Face base and zeolite diatom ooze coating lamination layer structure not only increase zeolite diatom ooze coating composite layer overall construction intensity,
And zeolite diatom ooze coating is distributed in fibre web mesh, and adhesion is compound on fibre web and metope base, Ke Yiqu
Organic adhesive raw material and cellulosic material in the zeolite diatom ooze coating that disappears formula adjust zeolite diatom ooze coating for science and match
Side, improve zeolite diatom ooze coating properties of product lay the foundation, further promote zeolite diatom ooze interior wall coating technology into
Step and development.
2, present invention employs fibre web and metope base and zeolite diatom ooze coating are compound, a kind of fibre web is formed
With metope base and zeolite diatom ooze coating lamination layer structure, and fibre web protrusion be higher than zeolite diatom ooze coating coating table
Face, but because fibre web mesh area of the present invention is to protrude the fibre web energy higher than zeolite diatom ooze coating coating surface
The technique effect for generating anticollision is standard setting, can effectively prevent office desk and chair, file cabinet, household desk, bookcase, bed
The furniture such as head, nightstand and other object head-on crash damage zeolite diatom ooze coating coating surface, even if office desk and chair, file
Cabinet, furniture and other object wedge angle damaged in collision zeolite diatom ooze coating coating surfaces, also can because fibre web there are due to subtract
Few zeolite diatom ooze coating coating impaired area, and the zeolite diatom ooze coating damaged in fill fiber silk screen hole is only needed, without
Professional's construction is filled up, and is maintained easily and at low cost.
3, present invention employs fibre web and metope base and zeolite diatom ooze coating are compound, a kind of fibre web is formed
With metope base and zeolite diatom ooze coating lamination layer structure, and fibre web protrusion be higher than zeolite diatom ooze coating coating table
Face, but because fibre web mesh area of the present invention is to protrude the fibre web energy higher than zeolite diatom ooze coating coating surface
The technique effect for generating stain resistant is standard setting, can effectively prevent dirty impression of the hand, dirty footprint and other object spots, even if production
Other spots are given birth to, the spot on fibre web can be wiped with wet rag remove, in filament mesh on zeolite diatom ooze coating
Spot need not engage professional, house person can fill up cleaning in time, and convenient and efficient, maintenance cost is low.
4, compared with prior art, the present invention not only have generate anticollision, stain resistant, anti-crack, reduce difficulty of construction,
The technique effect maintained easily.And the practicability of zeolite diatom ooze coating technology is increased, more crowds can be made to enjoy environmental protection
New life.
Description of the drawings
Present invention will be further explained below with reference to the attached drawings and examples：
Attached drawing 1 is wall of the present invention, metope base, fibre web, zeolite diatom ooze coating structural schematic diagram.
In attached drawing 1：1, wall；2, metope base；3, fibre web；4, zeolite diatom ooze coating.
Specific implementation mode
In wall（1）Metope base（2）One layer of fibre web of upper setting（3）, and fibre web（3）It is fixed on wall
Face base（2）On, then zeolite diatom ooze coating（4）It is sprayed at fibre web（3）In mesh and metope base（2）On, it is protecting
Demonstrate,prove zeolite diatom ooze coating（4）While coating thickness, and make fibre web（3）Protrusion is higher than zeolite diatom ooze coating（4）It applies
Layer surface is removed with rag wiping and is adhered to fibre web（3）Protrude the zeolite diatom ooze coating on part（4）, make filament
Net（3）With metope base（2）With zeolite diatom ooze coating（4）Adhesion is compound, forms wall, metope base, fibre web, zeolite
Diatom ooze coating lamination layer structure generates anticollision, stain resistant, anti-crack, the technology effect for reducing difficulty of construction, maintaining easily
Fruit, and zeolite diatom ooze coating composite layer overall construction intensity is improved, it can cancel in zeolite diatom ooze coating formula
Organic adhesive raw material and cellulosic material can adjust zeolite diatom ooze coating formula with science, improve the production of zeolite diatom ooze coating
Moral character energy promotes the progress and development of zeolite diatom ooze coating technology.
Embodiment one
Implementation room is meeting room, fibre web（3）Mesh area is higher than zeolite diatom ooze coating to protrude（4）Coating surface
Fibre web（3）The technique effect that anticollision can be generated is standard setting, and mesh area is set as 300 × 300 millimeters；Zeolite silicon
Algal gel coating（4）By weight percentage, composed of the following components：Zeolite powder 30%；Diatomite 25%；Nano-titanium dioxide 2%；
Titanium dioxide 15%；White carbon 10%；Kaolin 10%；Sierozem power 8%.Specific implementation mode is：In meeting room wall（1）Metope base
Layer（2）The fibre web that one layer of nylon fiber of upper setting is made into（3）, and the fibre web that nylon fiber is made into（3）Adherency
In metope base（2）On, the fibre web that is made into nylon fiber with roller（3）Shang Roll pressures, the fiber for making nylon fiber be made into
Silk screen（3）Adhesion composite solid schedules metope base（2）On, then zeolite diatom ooze coating（4）It is sprayed at what nylon fiber was made into
Fibre web（3）In mesh and metope base（2）On, ensureing zeolite diatom ooze coating（4）While coating thickness, and make Buddhist nun
The fibre web that synthetic fibre fiber is made into（3）Protrusion is higher than zeolite diatom ooze coating（4）Coating surface is removed with rag wiping and is adhered to
The fibre web that nylon fiber is made into（3）Protrude the zeolite diatom ooze coating on part（4）, the filament that makes nylon fiber be made into
Net（3）With metope base（2）With zeolite diatom ooze coating（4）Adhesion is compound, and formation wall, metope base, nylon fiber are made into
Fibre web, zeolite diatom ooze coating lamination layer structure, generate anticollision, anti-crack, reduce difficulty of construction, maintain easily
Technique effect,
Embodiment two
Specific implementation mode such as embodiment one is a difference in that it is office to implement room；Fibre web（3）For glass fiber mesh
Ge Bu, fiberglass gridding cloth mesh area are higher than zeolite diatom ooze coating to protrude（4）The fiberglass gridding of coating surface
It is standard setting that cloth, which can generate anticollision and the technique effect of stain resistant, and mesh area is 20 × 20 millimeters, is to use non-corrosive
Fastener fiberglass gridding cloth fibre web（3）It is fixed on metope base（2）On；Zeolite diatom ooze coating（4）By weight
Percentages are measured, it is composed of the following components：Zeolite powder 30%；Diatomite 30%；Nano-titanium dioxide 3%；Titanium dioxide 13%；White carbon
10%；Kaolin 6%；Sierozem power 8% forms wall（1）, metope base（2）, fiberglass gridding cloth fibre web（3）, zeolite
Diatom ooze coating（4）Lamination layer structure generates anticollision, stain resistant, anti-crack, the technology for reducing difficulty of construction, maintaining easily
Effect.
Embodiment three
Specific implementation mode such as embodiment one is a difference in that it is the household room for having child to implement room；Fibre web（3）It is
Acetate fiber grid cloth, acetate fiber grid cloth mesh area are higher than zeolite diatom ooze coating to protrude（4）The vinegar of coating surface
It is standard setting that ester fiber grid cloth, which can generate anticollision and the technique effect of stain resistant, and acetate fiber grid cloth mesh area is
10 × 10 millimeters；Zeolite diatom ooze coating（4）By weight percentage, composed of the following components：Zeolite powder 35%；Diatomite
35%；Nano-titanium dioxide 1%；Titanium dioxide 8%；White carbon 10%；Kaolin 6%；Sierozem power 5% forms wall（1）, metope base
（2）, acetate fiber grid cloth fibre web（3）, zeolite diatom ooze coating（4）Lamination layer structure, generate anticollision, stain resistant,
Anti-crack, the technique effect for reducing difficulty of construction, maintaining easily.
This reality invention the embodiment described is the description carried out to the preferred embodiment of the present invention, not to the present invention
Conception and scope is defined, and under the premise of not departing from design philosophy of the present invention, engineers and technicians are to this hair in this field
The all variations and modifications that bright technical solution is made should all fall into protection scope of the present invention, the claimed skill of the present invention
Art content has all been recorded in detail in the claims.
Claims (5)
1. a kind of fibre web composite zeolite diatom ooze coating, including wall, metope base, zeolite diatom ooze coating, feature
It is that one layer of fibre web is arranged in the metope base of wall, fibre web is fixed in metope base, then zeolite silicon
Algal gel coating is sprayed in fibre web mesh and in metope base, while ensureing zeolite diatom ooze coating coating thickness,
So that fibre web protrusion is higher than zeolite diatom ooze coating coating surface again, makes fibre web and metope base and zeolite diatom mash
Expect that adhesion is compound, forms wall, metope base, fibre web, zeolite diatom ooze coating lamination layer structure.
2. a kind of fibre web composite zeolite diatom ooze coating as described in claim 1, it is characterised in that the zeolite diatom
Slime paint is by weight percentage, composed of the following components：Zeolite powder 20~40%；Diatomite 20~40%；Nano-titanium dioxide 1
~3%；Titanium dioxide 8~15%；White carbon 5~15%；Kaolin 5~15%；Sierozem power 5~10%.
3. a kind of fibre web composite zeolite diatom ooze coating as described in claim 1, it is characterised in that the fibre web
It is silk screen or synthetic fibers grid cloth that the silk screen or regenerated fiber grid cloth, synthetic fibers being made into for regenerated fiber are made into, inorganic
The silk screen or low-melting fiber grid cloth that the silk screen or inorfil grid cloth, low-melting fiber that fiber is made into are made into.
4. by a kind of fibre web composite zeolite diatom ooze coating described in claim 1 or 3, it is characterised in that the fiber
Screen mesh area with protrude be higher than zeolite diatom ooze coating coating surface fibre web can generate anticollision, stain resistant skill
Art effect is standard setting.
5. by a kind of fibre web composite zeolite diatom ooze coating described in claim 1 or 3, it is characterised in that described fiber
The fixed form that silk screen is fixed in metope base is：
（1）Fibre web is fixed in metope base with rustless fastener；
（2）When making or clearing up metope base, fibre web is adhered in metope base, with roller in the online Roll of filament
Pressure makes fibre web adhesion composite solid due in metope base.