CN108485478A - A kind of anti-corrosion fireproof coating for new energy car battery babinet - Google Patents
A kind of anti-corrosion fireproof coating for new energy car battery babinet Download PDFInfo
- Publication number
- CN108485478A CN108485478A CN201810459244.4A CN201810459244A CN108485478A CN 108485478 A CN108485478 A CN 108485478A CN 201810459244 A CN201810459244 A CN 201810459244A CN 108485478 A CN108485478 A CN 108485478A
- Authority
- CN
- China
- Prior art keywords
- fireproof coating
- corrosion
- corrosion fireproof
- chlorinated rubber
- polyamide
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of anti-corrosion fireproof coatings and preparation method thereof for new energy car battery babinet, raw material include epoxy resin, chlorinated rubber, polyamide, aluminium dihydrogen phosphate, glycerine, tetrabromobisphenol A, silicon oil solution, glass fibre, cyclohexanone, trbasic zinc phosphate, No. 200 industrial napthas and it is anti-settling, thickening, defoaming etc. various auxiliary agents.The present invention not only remains the advantages of existing coating, also has superpower anti-corrosion fire protecting performance.
Description
Technical field
The present invention relates to technical field of paint preparation more particularly to a kind of anti-corrosions for new energy car battery babinet
Fireproof coating and preparation method thereof.
Background technology
The new-energy automobile industry development in China was rapid in recent years, had become the industry that China leads over the world at present
One of.According to the data of the Ministry of Industry and Information Technology, China's new-energy automobile volume of production and marketing in 2017 respectively reach 79.4 ten thousand and
77.7 ten thousand, accumulative ownership reaches 1,800,000, accounts for 50% or more world market ownership, occupies the first in the world within continuous 3 years.
As new industry, the fast development of new-energy automobile industry be unable to do without the support of national policy, and country is quickening new energy vapour
The industrialization process of vehicle has successively promulgated a series of relevant policies files, formulates and implement subsidy policy, double integrator policy
Deng the development generation significant impact to new-energy automobile industry.Since 2014, China's new energy passenger car sales volume persistently increases
Add, sales volume in 2017 grew beyond 3 times with 2015 compared with sales volume, although 2017 year-on-year speedups are declined, but still kept
In 72% high position.In view of the speedup and double integrator policy requirements of fuel oil passenger car, estimate 2018 to the year two thousand twenty I
State's new energy passenger car sales volume will respectively reach 950,000,1,340,000,1,840,000, annual compound growth rate 47%.It is mended
The influence that patch policy weight electricity gently mixes, pure electric vehicle sale gradually become the mainstream of new energy passenger car sale, pure electric vehicle sales volume
Account for the proportion of new energy passenger car total sales volume by 2015 64% rise to 2017 81%.
It is expected that the raising with the progress and market of power battery technology to new-energy automobile degree of recognition, the ratio of pure electric vehicle
Regular meeting is further promoted.The core technology of new-energy automobile is mainly power battery technology, motor technology and electronic control technology, wherein
Power battery is important one of the core component of electric vehicle.Can power battery technology break through, and be the pass of Development of Electric Vehicles
Key.And lithium battery is that technology is more mature, performance is relatively stable in power battery at this stage, one kind for being most widely used.
Good fire protecting performance, which is new energy car battery, to be had, and it is new to ensure that this just needs novel anti-corrosion fireproof coating
Energy automobile battery it is safe to use.
Although new-energy automobile industry is fast-developing, most of manufacturer is to the Battery case as energy carrier
Consciousness of self-protection it is still more weak.Antirust treatment has only done to Battery case in most of manufacturer, and for fire prevention and
In terms of anti-corrosion, all do not account in place.The protective layer used in existing conventional truck, most cost is higher, complex process, and
It is that other demands being directed to are prepared, is not particularly suited for the Battery case of new energy vehicle.Chinese patent CN201510383724
A kind of automobile batteries babinet coating of antiseptic and rustproof, anti-external force damage is disclosed, although the coating in the patent has anticorrosion
Performance, but as with the relevant coating of new energy car battery, but without reference to fire prevention, antistatic property.Chinese patent
CN201510194420 provides a kind of fireproof coating, although the coating involved by the invention has good fire prevention
Property, but cannot be satisfied the etch-proof performance requirement of Battery case.
Invention content
Battery in new-energy automobile dynamical system is arranged in mostly below underbody, there is more cruel mounting ring
Border.Carrier of the Battery case as power battery plays key effect on ensureing the problem of power battery securely and reliably works.
The position of battery installation simultaneously easily touches rainwater, mud etc., is corrosion severely afflicated area, and antiseptic property is more demanding.This hair
Bright purpose is the safe to use of guarantee new energy car battery, provides a kind of anti-corrosion fireproof coating for Battery case.
The present invention provides a kind of anti-corrosion fireproof coating, includes following components according to mass fraction:
Epoxy resin 10~20%, chlorinated rubber 3~11%, polyamide 4~14%, aluminium dihydrogen phosphate 5~15%,
Glycerine 4~14%, tetrabromobisphenol A 5~15%, silicon oil solution 0.5~1%, glass fibre 5~15%, cyclohexanone 3~
13%, 2~12%, No. 200 industrial napthas 6~16%, auxiliary agents 2.5~5% of trbasic zinc phosphate.
Further, the epoxy resin 14~16%, chlorinated rubber 6~7%, polyamide 8~11%, di(2-ethylhexyl)phosphate
Hydrogen aluminium 7~10%, glycerine 7~12%, tetrabromobisphenol A 8~13%, silicon oil solution 0.5~1%, glass fibre 8~12%,
Cyclohexanone 6~10%, trbasic zinc phosphate 5~9%, No. 200 industrial napthas 8~15%, auxiliary agents 2.5~5%.
Further, the auxiliary agent is tricresyl phosphate, G-6 lead manganese drier, the cruel amine of ethyoxyl bay, phenylenediamine.
The preparation method of the anti-corrosion fireproof coating for new energy car battery babinet, including following preparation step
Suddenly:
(1) chlorinated rubber is equipped with glycerine and dissolved by the amount that each component is accurately weighed up by recipe requirements, waits for it completely
It is for use after dissolving;
(2) epoxy resin, polyamide, aluminium dihydrogen phosphate are added chlorinated rubber solution obtained by step (1), and stirred
Uniformly;
(3) step (2) acquired solution is added in the mixed cylinder equipped with remaining various raw material, is stirred evenly with blender, then
It is sent into ball mill and mills, adjust its fineness;
(4) the levigate coating of step (3) is poured into mixed cylinder, its viscosity is adjusted with No. 200 industrial napthas;
(5) impurity is filtered out by filter plant, through being packed after the assay was approved with clean lossless metal bucket, and covers and obturage
It is close.
In the step (3), fineness requirement is less than or equal to 80 μm.
In the step (4), viscosity need to meet《GB12441-2005 finishing fire retardant paints》Index specified in specification.
Compared with existing coating, beneficial effects of the present invention are as follows:
Coating of the present invention also has superpower fire prevention, anti-corrosion, anti-quiet other than the advantages of retaining existing coating
The performance of electricity, and have excellent toughness.First, in the present invention, epoxy resin and chlorinated rubber, polyamide spelling are used as
For the base-material of fireproof coating, the fireproof system fire retardant being made of aluminium dihydrogen phosphate, tetrabromobisphenol A, trbasic zinc phosphate etc. is added, is made
Coating obtains excellent fire protecting performance, while the room of coating is also achieved under the collective effect of polyamide and phenylenediamine
Temperature solidification.Secondly, the film of formation has good corrosion resistance, resistance to acid and alkali, solvent resistance, a weatherability, and adhesive force it is good,
Fast drying, non-discolouring, easy construction, while also there is stable performance and production performance, it is conducive to large-scale production and application.So
Afterwards, coating of the present invention is colourless, can be deployed into other a variety of colors as needed;This product is also added into a certain amount of simultaneously
The toughness of this product is greatly improved in glass fibre;Moreover, after the auxiliary agents such as the cruel amine of ethyoxyl bay are added, significantly
Improve the antistatic property of coating.
Various raw materials in anti-corrosion fireproof coating of the present invention on the market all can by name or model is bought.
Specific implementation mode
Embodiment is combined to technical solution of the present invention below to be described in detail.
Embodiment 1
Epoxy resin 10%, chlorinated rubber 10%, polyamide 10%, aluminium dihydrogen phosphate 10%, glycerine 10%, four
Bromine bisphenol-A 10%, silicon oil solution 1%, glass fibre 10%, cyclohexanone 10%, 5%, No. 200 industrial naptha 10% of trbasic zinc phosphate,
Auxiliary agent 4%.
The preparation method of the anti-corrosion fireproof coating for new energy car battery babinet, including following preparation step
Suddenly:
(1) chlorinated rubber is equipped with glycerine and dissolved by the amount that each component is accurately weighed up by recipe requirements, waits for it completely
It is for use after dissolving;
(2) epoxy resin, polyamide, aluminium dihydrogen phosphate are added chlorinated rubber solution obtained by step (1), and stirred
Uniformly;
(3) step (2) acquired solution is added in the mixed cylinder equipped with remaining various raw material, is stirred evenly with blender, then
It is sent into ball mill and mills, adjust its fineness;
(4) the levigate coating of step (3) is poured into mixed cylinder, its viscosity is adjusted with No. 200 industrial napthas;
(5) impurity is filtered out by filter plant, through being packed after the assay was approved with clean lossless metal bucket, and covers and obturage
It is close.
Embodiment 2
Epoxy resin 20%, chlorinated rubber 5%, polyamide 10%, aluminium dihydrogen phosphate 10%, glycerine 10%, four
Bromine bisphenol-A 5%, silicon oil solution 0.5%, glass fibre 10%, cyclohexanone 10%, 5%, No. 200 industrial naptha 10% of trbasic zinc phosphate,
Auxiliary agent 4.5%.
The preparation method of the anti-corrosion fireproof coating for new energy car battery babinet, including following preparation step
Suddenly:
(1) chlorinated rubber is equipped with glycerine and dissolved by the amount that each component is accurately weighed up by recipe requirements, waits for it completely
It is for use after dissolving;
(2) epoxy resin, polyamide, aluminium dihydrogen phosphate are added chlorinated rubber solution obtained by step (1), and stirred
Uniformly;
(3) step (2) acquired solution is added in the mixed cylinder equipped with remaining various raw material, is stirred evenly with blender, then
It is sent into ball mill and mills, adjust its fineness;
(4) the levigate coating of step (3) is poured into mixed cylinder, its viscosity is adjusted with No. 200 industrial napthas;
(5) impurity is filtered out by filter plant, through being packed after the assay was approved with clean lossless metal bucket, and covers and obturage
It is close.
Embodiment 3
Epoxy resin 14%, chlorinated rubber 6%, polyamide 9%, aluminium dihydrogen phosphate 10%, glycerine 9%, tetrabromo
Bisphenol-A 10%, silicon oil solution 0.5%, glass fibre 10%, cyclohexanone 8%, 7%, No. 200 industrial naptha 11.5% of trbasic zinc phosphate,
Auxiliary agent 5%.
The preparation method of the anti-corrosion fireproof coating for new energy car battery babinet, including following preparation step
Suddenly:
(1) chlorinated rubber is equipped with glycerine and dissolved by the amount that each component is accurately weighed up by recipe requirements, waits for it completely
It is for use after dissolving;
(2) epoxy resin, polyamide, aluminium dihydrogen phosphate are added chlorinated rubber solution obtained by step (1), and stirred
Uniformly;
(3) step (2) acquired solution is added in the mixed cylinder equipped with remaining various raw material, is stirred evenly with blender, then
It is sent into ball mill and mills, adjust its fineness;
(4) the levigate coating of step (3) is poured into mixed cylinder, its viscosity is adjusted with No. 200 industrial napthas;
(5) impurity is filtered out by filter plant, through being packed after the assay was approved with clean lossless metal bucket, and covers and obturage
It is close.
Embodiment 4
Epoxy resin 16%, chlorinated rubber 10%, polyamide 6%, aluminium dihydrogen phosphate 12%, glycerine 8%, tetrabromo
2.5%, No. 200 bisphenol-A 9%, silicon oil solution 1%, glass fibre 9.5%, cyclohexanone 6%, trbasic zinc phosphate 5%, auxiliary agent solvent vapour
Oil 15%.
The preparation method of the anti-corrosion fireproof coating for new energy car battery babinet, including following preparation step
Suddenly:
(1) chlorinated rubber is equipped with glycerine and dissolved by the amount that each component is accurately weighed up by recipe requirements, waits for it completely
It is for use after dissolving;
(2) epoxy resin, polyamide, aluminium dihydrogen phosphate are added chlorinated rubber solution obtained by step (1), and stirred
Uniformly;
(3) step (2) acquired solution is added in the mixed cylinder equipped with remaining various raw material, is stirred evenly with blender, then
It is sent into ball mill and mills, adjust its fineness;
(4) the levigate coating of step (3) is poured into mixed cylinder, its viscosity is adjusted with No. 200 industrial napthas;
(5) impurity is filtered out by filter plant, through being packed after the assay was approved with clean lossless metal bucket, and covers and obturage
It is close.
Fireproof coating described in any of the above-described embodiment, the model G-6 lead manganese driers of drier used, press-type
Number and title be commercially available on the market.
The present invention is not limited to above-mentioned preferred forms, it should be understood that design of the invention can be by other various shapes
Formula is implemented to use, they also fall in protection scope of the present invention.
By experiment test, every constituent mass ratio and preparation method according to provided in the content of present invention is with obtained
The coating arrived can reach technical indicator below:
Claims (5)
1. a kind of anti-corrosion fireproof coating, which is characterized in that the anti-corrosion fireproof coating includes following components according to mass ratio:Ring
Oxygen resin 10~20%, chlorinated rubber 3~11%, polyamide 4~14%, aluminium dihydrogen phosphate 5~15%, glycerine 4~
14%, tetrabromobisphenol A 5~15%, silicon oil solution 0.5~1%, glass fibre 5~15%, cyclohexanone 3~13%, trbasic zinc phosphate 2
~12%, No. 200 industrial naptha 6~16%, auxiliary agent 2.5~5%.
2. anti-corrosion fireproof coating as described in claim 1, which is characterized in that the auxiliary agent is tricresyl phosphate, G-6 lead manganese
It is one or more in drier, the cruel amine of ethyoxyl bay or phenylenediamine.
3. anti-corrosion fireproof coating as described in claim 1, which is characterized in that the anti-corrosion fireproof coating is according to mass ratio packet
Include following components:Epoxy resin 14~16%, chlorinated rubber 6~7%, polyamide 8~11%, aluminium dihydrogen phosphate 7~
10%, glycerine 7~12%, tetrabromobisphenol A 8~13%, silicon oil solution 0.5~1%, glass fibre 8~12%, cyclohexanone 6
~10%, 5~9%, No. 200 industrial napthas 8~15%, auxiliary agents 2.5~5% of trbasic zinc phosphate.
4. a kind of preparation method of anti-corrosion fireproof coating as described in claims 1 to 3, which is characterized in that the preparation method
Include the following steps:
(1) chlorinated rubber is equipped with glycerine and dissolved, waits for that it is completely dissolved by the amount that each component is accurately weighed up by recipe requirements
It is for use afterwards;
(2) chlorinated rubber solution obtained by step (1) is added in epoxy resin, polyamide, aluminium dihydrogen phosphate, and stirred equal
It is even;
(3) step (2) acquired solution is added in the mixed cylinder equipped with remaining various raw material, is stirred evenly, is then fed into blender
It mills in ball mill, adjusts its fineness;
(4) the levigate coating of step (3) is poured into mixed cylinder, its viscosity is adjusted with No. 200 industrial napthas;
(5) impurity is filtered out by filter plant, through pack after the assay was approved with clean lossless metal bucket, and lid obturage it is close.
5. a kind of application of anti-corrosion fireproof coating as described in claims 1 to 3, which is characterized in that the anti-corrosion fireproof coating
Applied to new energy car battery babinet.