CN108411706A - A kind of electric arc aluminium spraying aluminium-foil paper and its manufacture craft - Google Patents
A kind of electric arc aluminium spraying aluminium-foil paper and its manufacture craft Download PDFInfo
- Publication number
- CN108411706A CN108411706A CN201810180196.5A CN201810180196A CN108411706A CN 108411706 A CN108411706 A CN 108411706A CN 201810180196 A CN201810180196 A CN 201810180196A CN 108411706 A CN108411706 A CN 108411706A
- Authority
- CN
- China
- Prior art keywords
- aluminium
- layer
- foil
- spraying
- original paper
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of electric arc aluminium spraying aluminium-foil paper and its manufacture craft, including original paper layer and aluminium foil layer, the aluminium foil layer is sprayed on by the way of electric arc aluminium spraying on original paper layer, and the surface of the original paper layer and aluminium foil layer is coated with inflaming retarding membrane；The manufacture craft of the electric arc aluminium spraying aluminium-foil paper, is realized by following steps：S1, after being heated, melted by the aluminium wire of electrification using electrothermal way, being atomized, last layer aluminium foil layer is sprayed on low temperature original paper layer by arc-spraying machine, the spray gun of the arc-spraying machine is 45 ° with the gradient of low temperature original paper layer, and spray gun pressure is 17 22KPa；S2, press polish is carried out to the aluminium foil layer being sprayed on original paper layer using calender so that the surfacing of aluminium foil layer is smooth；S3, the aluminium-foil paper after press polish is put into calender, flows into anti-flaming dope in roller both sides, one layer of inflaming retarding membrane is respectively formed in the anti-flaming dope of coating simultaneously on the surface of original paper layer and aluminium foil layer.
Description
Technical field
The invention belongs to aluminium-foil paper technical fields, and in particular to a kind of electric arc aluminium spraying aluminium-foil paper and its manufacture craft.
Background technology
Electric arc spraying is to melt metal using the electric arc between the wire that is continuously fed in two of burning, with high speed gas
Stream is atomized molten metal, and heated material forms the particle of melting or semi-molten state, accelerates to the metallic of atomization
So that it is impacted and is deposited on the technology for forming coating on matrix surface.The aluminium foil layer of electric arc aluminium spraying technique spray has good resistance to
Corrosive power, while aluminium foil layer has excellent coating binding force with matrix, is less prone to skin effect phenomenon.
But electric arc spraying is commonly used in mechanical workpieces or metal surface, for aluminium-foil paper technical field using less, and
It will appear a small amount of pin-hole phenomena after electric arc aluminium spraying, the existing aluminium-foil paper anti-corrosion humidity resistance for cigarette case package is poor, and cigarette exists
It easily goes mouldy under wet environment, in addition existing aluminium-foil paper burning point is low, more easy firing under conditions of summer high temperature is dried, and has one
Fixed danger.
Invention content
The purpose of the present invention is to provide a kind of electric arc aluminium spraying aluminium-foil paper and its manufacture crafts, and it is easy to solve existing aluminium-foil paper
It deliquesces and corrodes the problem low with burning point.
The purpose of the present invention can be achieved through the following technical solutions：
A kind of electric arc aluminium spraying aluminium-foil paper and its manufacture craft, including original paper layer and aluminium foil layer, the aluminium foil layer is using electricity
The aluminium-plated mode of arc is sprayed on original paper layer, and the surface of the original paper layer and aluminium foil layer is coated with inflaming retarding membrane.
A kind of manufacture craft of electric arc aluminium spraying aluminium-foil paper, is realized by following steps：
S1, after the aluminium wire of electrification heated using electrothermal way, is melted, being atomized, by arc-spraying machine in low temperature original
Last layer aluminium foil layer is sprayed on paper layer, the spray gun of the arc-spraying machine is 45 ° with the gradient of low temperature original paper layer, and spray gun pressure is
17-22KPa；
S2, press polish is carried out to the aluminium foil layer being sprayed on original paper layer using calender so that the surfacing light of aluminium foil layer
It is sliding；
S3, the aluminium-foil paper after press polish is put into calender, anti-flaming dope is flowed into roller both sides, in original paper layer and aluminium foil
The anti-flaming dope of coating simultaneously on the surface of layer is respectively formed one layer of inflaming retarding membrane.
Further, the environmental condition of the spraying described in step S1 is relative humidity in 70-80%, the item that temperature is 5-10 DEG C
It is sprayed under part.
Further, the low temperature original paper layer described in step S1 is the original paper layer that preservation is lyophilized at -20 DEG C.
Further, the anti-flaming dope includes following components by weight percent raw material：Aluminum hydroxide sol 30-40%, alkali-free glass
Glass powder 10-20%, polyurethane rubber 15-35%, cosolvent 5-10%, antifoaming agent 2-5%, water 5-20%, heated ultrasound breast
Change to obtain the final product.
Further, the cosolvent is tert-pentyl alcohol, and the antifoaming agent is mineral oil.
Beneficial effects of the present invention：
(1) a kind of electric arc aluminium spraying aluminium-foil paper provided by the invention and its manufacture craft, by arc-spraying machine in low temperature original
Last layer aluminium foil layer is sprayed on paper layer, low temperature original paper layer increases the aluminium particle for receiving high temperature semi-molten state, and electric arc spraying
The spray gun of machine is 45 ° with the gradient of low temperature original paper layer, increases the buffering dynamics of semi-molten state aluminium particle so that electric arc spraying
Technology can be applied effectively in aluminium-foil paper technical field, and the aluminium foil layer of electric arc spraying has good corrosion resistance and original paper layer
Binding force, increase the corrosion-resistant deliquescence performance of aluminium-foil paper；
(2) one layer of inflaming retarding membrane, inflaming retarding membrane are respectively formed in the anti-flaming dope of coating simultaneously on the surface of original paper layer and aluminium foil layer
While the flame retardant property for increasing aluminium-foil paper improves burning point, there is sealing of hole effect to aluminium foil layer, improve the sealing of aluminium foil layer
Property and structural strength；
(3) it uses tert-pentyl alcohol as cosolvent, is effectively increased the dissolving energy of aluminum hydroxide sol and polyurethane rubber
Power improves the mobility and stability of anti-flaming dope.
Certainly, it implements any of the products of the present invention and does not necessarily require achieving all the advantages described above at the same time.
Description of the drawings
In order to illustrate the technical solution of the embodiments of the present invention more clearly, will be described below to embodiment required
Attached drawing is briefly described, it should be apparent that, drawings in the following description are only some embodiments of the invention, for ability
For the those of ordinary skill of domain, without creative efforts, it can also be obtained according to these attached drawings other attached
Figure.
Fig. 1 is a kind of structural schematic diagram of electric arc aluminium spraying aluminium-foil paper of the present invention；
In attached drawing, parts list represented by the reference numerals are as follows：
1- original paper layers；2- aluminium foil layers；3- flame-retardant layers.
Specific implementation mode
Following will be combined with the drawings in the embodiments of the present invention, and technical solution in the embodiment of the present invention carries out clear, complete
Site preparation describes, it is clear that described embodiments are only a part of the embodiments of the present invention, instead of all the embodiments.It is based on
Embodiment in the present invention, those of ordinary skill in the art are obtained all other without creative efforts
Embodiment shall fall within the protection scope of the present invention.
Embodiment 1
Refering to Figure 1, the present invention is a kind of electric arc aluminium spraying aluminium-foil paper and its manufacture craft, including original paper layer 1 and aluminium
Layers of foil 2, the aluminium foil layer 2 are sprayed on by the way of electric arc aluminium spraying on low temperature original paper layer 1, the original paper layer 1 and aluminium foil
The surface of layer 2 is coated with inflaming retarding membrane 3；
The anti-flaming dope for making inflaming retarding membrane 3 includes following components by weight percent raw material：Aluminum hydroxide sol 30kg, alkali-free glass powder
10kg, polyurethane rubber 30kg, tert-pentyl alcohol 10kg, mineral oil 5kg, water 15kg, heated ultrasonic emulsification to obtain the final product；
A kind of manufacture craft of electric arc aluminium spraying aluminium-foil paper, is realized by following steps：
S1, it is 80% in relative humidity, temperature is after being heated, melted by the aluminium wire of electrification using electrothermal way, being atomized
In the environment of 10 DEG C, the original paper layer 1 that preservation is lyophilized at -20 DEG C is taken out, is sprayed on low temperature original paper layer 1 by arc-spraying machine
One layer of aluminium foil layer 2, the spray gun of the arc-spraying machine are 45 ° with the gradient of original paper layer 1, spray gun pressure 17KPa；
S2, press polish is carried out to the aluminium foil layer 2 being sprayed on original paper layer 1 using calender so that the surfacing of aluminium foil layer 2
It is smooth；
S3, the aluminium-foil paper after press polish is put into calender, anti-flaming dope is flowed into roller both sides, in original paper layer 1 and aluminium
The anti-flaming dope of coating simultaneously on the surface of layers of foil 2 is respectively formed one layer of inflaming retarding membrane 3, to increase the flame retardant property of aluminium-foil paper, system
The burning point of the aluminium-foil paper of work is 446-470 DEG C, while anti-flaming dope has sealing of hole effect to the aluminium foil layer 2 after spraying.
Embodiment 2
Refering to Figure 1, the present invention is a kind of electric arc aluminium spraying aluminium-foil paper and its manufacture craft, including original paper layer 1 and aluminium
Layers of foil 2, the aluminium foil layer 2 are sprayed on by the way of electric arc aluminium spraying on low temperature original paper layer 1, the original paper layer 1 and aluminium foil
The surface of layer 2 is coated with inflaming retarding membrane 3；
The anti-flaming dope for making inflaming retarding membrane 3 includes following components by weight percent raw material：Aluminum hydroxide sol 40kg, alkali-free glass powder
20kg, polyurethane rubber 15kg, tert-pentyl alcohol 5kg, mineral oil 2kg, water 18kg, heated ultrasonic emulsification to obtain the final product；
A kind of manufacture craft of electric arc aluminium spraying aluminium-foil paper, is realized by following steps：
S1, it is 70% in relative humidity, temperature is after being heated, melted by the aluminium wire of electrification using electrothermal way, being atomized
In the environment of 5 DEG C, the original paper layer 1 that preservation is lyophilized at -20 DEG C is taken out, is sprayed on low temperature original paper layer 1 by arc-spraying machine
One layer of aluminium foil layer 2, the spray gun of the arc-spraying machine are 45 ° with the gradient of original paper layer 1, spray gun pressure 22KPa；
S2, press polish is carried out to the aluminium foil layer 2 being sprayed on original paper layer 1 using calender so that the surfacing of aluminium foil layer 2
It is smooth；
S3, the aluminium-foil paper after press polish is put into calender, anti-flaming dope is flowed into roller both sides, in original paper layer 1 and aluminium
The anti-flaming dope of coating simultaneously on the surface of layers of foil 2 is respectively formed one layer of inflaming retarding membrane 3, to increase the flame retardant property of aluminium-foil paper, system
The burning point of the aluminium-foil paper of work is 465-500 DEG C, while anti-flaming dope has sealing of hole effect to the aluminium foil layer 2 after spraying.
Embodiment 3
Refering to Figure 1, the present invention is a kind of electric arc aluminium spraying aluminium-foil paper and its manufacture craft, including original paper layer 1 and aluminium
Layers of foil 2, the aluminium foil layer 2 are sprayed on by the way of electric arc aluminium spraying on low temperature original paper layer 1, the original paper layer 1 and aluminium foil
The surface of layer 2 is coated with inflaming retarding membrane 3；
The anti-flaming dope for making inflaming retarding membrane 3 includes following components by weight percent raw material：Aluminum hydroxide sol 35kg, alkali-free glass powder
15kg, polyurethane rubber 33kg, tert-pentyl alcohol 8kg, mineral oil 4kg, water 5kg, heated ultrasonic emulsification to obtain the final product；
A kind of manufacture craft of electric arc aluminium spraying aluminium-foil paper, is realized by following steps：
S1, it is 75% in relative humidity, temperature is after being heated, melted by the aluminium wire of electrification using electrothermal way, being atomized
In the environment of 8 DEG C, the original paper layer 1 that preservation is lyophilized at -20 DEG C is taken out, is sprayed on low temperature original paper layer 1 by arc-spraying machine
One layer of aluminium foil layer 2, the spray gun of the arc-spraying machine are 45 ° with the gradient of original paper layer 1, spray gun pressure 20KPa；
S2, press polish is carried out to the aluminium foil layer 2 being sprayed on original paper layer 1 using calender so that the surfacing of aluminium foil layer 2
It is smooth；
S3, the aluminium-foil paper after press polish is put into calender, anti-flaming dope is flowed into roller both sides, in original paper layer 1 and aluminium
The anti-flaming dope of coating simultaneously on the surface of layers of foil 2 is respectively formed one layer of inflaming retarding membrane 3, to increase the flame retardant property of aluminium-foil paper, system
The burning point of the aluminium-foil paper of work is 455-476 DEG C, while anti-flaming dope has sealing of hole effect to the aluminium foil layer 2 after spraying.
The above content is just an example and description of the concept of the present invention, affiliated those skilled in the art
It makes various modifications or additions to the described embodiments or substitutes by a similar method, without departing from invention
Design or beyond the scope defined by this claim, be within the scope of protection of the invention.
Claims (6)
1. a kind of electric arc aluminium spraying aluminium-foil paper, it is characterised in that：Including original paper layer (1) and aluminium foil layer (2), the aluminium foil layer (2)
It is sprayed on by the way of electric arc aluminium spraying on original paper layer (1), the surface of the original paper layer (1) and aluminium foil layer (2) is coated with
Inflaming retarding membrane (3).
2. a kind of manufacture craft of electric arc aluminium spraying aluminium-foil paper, it is characterised in that：It is realized by following steps：
S1, after the aluminium wire of electrification heated using electrothermal way, is melted, being atomized, by arc-spraying machine in low temperature original paper layer
(1) last layer aluminium foil layer (2) is sprayed on, the spray gun of the arc-spraying machine is 45 ° with the gradient of low temperature original paper layer (1), spray gun
Pressure is 17-22KPa；
S2, press polish is carried out to the aluminium foil layer (2) being sprayed on original paper layer (1) using calender so that the surface of aluminium foil layer (2) is flat
It is whole smooth；
S3, the aluminium-foil paper after press polish is put into calender, anti-flaming dope is flowed into roller both sides, in original paper layer (1) and aluminium foil
The anti-flaming dope of coating simultaneously on the surface of layer (2) is respectively formed one layer of inflaming retarding membrane (3).
3. a kind of manufacture craft of electric arc aluminium spraying aluminium-foil paper according to claim 2, it is characterised in that：Described in step S1
The environmental condition of spraying is relative humidity in 70-80%, and temperature is sprayed under conditions of being 5-10 DEG C.
4. a kind of manufacture craft of electric arc aluminium spraying aluminium-foil paper according to claim 2, it is characterised in that：Described in step S1
Low temperature original paper layer (1) is the original paper layer (1) that preservation is lyophilized at -20 DEG C.
5. a kind of manufacture craft of electric arc aluminium spraying aluminium-foil paper according to claim 2, it is characterised in that：The fire-retardant painting
Material includes following components by weight percent raw material：Aluminum hydroxide sol 30-40%, alkali-free glass powder 10-20%, polyurethane rubber 15-
35%, cosolvent 5-10%, antifoaming agent 2-5%, water 5-20%, heated ultrasonic emulsification to obtain the final product.
6. a kind of manufacture craft of electric arc aluminium spraying aluminium-foil paper according to claim 5, it is characterised in that：The cosolvent
For tert-pentyl alcohol, the antifoaming agent is mineral oil.