CN108396983A - Cracking-proof belt and preparation method thereof - Google Patents
Cracking-proof belt and preparation method thereof Download PDFInfo
- Publication number
- CN108396983A CN108396983A CN201810175114.8A CN201810175114A CN108396983A CN 108396983 A CN108396983 A CN 108396983A CN 201810175114 A CN201810175114 A CN 201810175114A CN 108396983 A CN108396983 A CN 108396983A
- Authority
- CN
- China
- Prior art keywords
- fixed
- cracking
- net
- interconnecting piece
- fixed strip
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides a kind of Cracking-proof belts and preparation method thereof, are related to the technical field of building maintenance, including fixed strip and adhesive linkage；Fixed strip includes interconnecting piece and fixed part, it can be fixed along the seam crossing of partition plate or plasterboard by fixed strip, it is connect with partition plate or plasterboard additionally by interconnecting piece, and interconnecting piece is provided with ventilation position, Cracking-proof belt existing in the prior art is alleviated directly to be squeezed or stretch and deform or tear failure, and Cracking-proof belt the phenomenon that heaving or tilting, cause the inaesthetic technical problem of metope；Secondary structure and agent structure are realized, between partition plate and partition plate, the anticracking between the plank of lightgage steel joist is implemented, and increases secondary structure and agent structure, between partition plate and partition plate, service life between the plank of lightgage steel joist is more practical.
Description
Technical field
The present invention relates to building maintenance technical fields, more particularly, to a kind of Cracking-proof belt and preparation method thereof.
Background technology
Secondary structure is difficult to be combined into one with agent structure at present, and anticracking problem is at the most important thing.Have in the market various
Glass fibre anti-cracking net, metal anti-cracking net and various glass fibre Cracking-proof belts.But it is difficult fundamentally to solve agent structure and two
There is miscellaneous partition plate in the market in particular with the development of new material in the anticracking problem of secondary structure, partition plate
It is anti-to be cleaved into problem.
In the prior art, when wall surface generates crack, usually the region of wall surface reflection crack part is profoundly removed,
Concrete is imposed again and fills up or subsidize break-preventing adhesive tape, or subsidizes the practice of Cracking-proof belt.
But when generation is expanded with heat and contract with cold at crack, Cracking-proof belt can be caused directly to be squeezed or stretch and deform or tear
Destruction is split, in addition, since Cracking-proof belt does not have airing function, when expanding or shrinkage phenomenon, is easy due to gas is fled
The phenomenon that causing Cracking-proof belt to heave or tilt, causes metope unsightly.
Invention content
The purpose of the present invention is to provide a kind of Cracking-proof belts and preparation method thereof, to alleviate anticracking existing in the prior art
The phenomenon that band is directly squeezed or stretches and deforms or tear failure and Cracking-proof belt are heaved or tilted, causes metope not beautiful
The technical issues of sight.
A kind of Cracking-proof belt provided by the invention, including：Fixed strip and adhesive linkage；
Fixed strip includes interconnecting piece and fixed part, and there are two interconnecting piece settings, and two interconnecting pieces are symmetrically set along fixed part
It sets, and two interconnecting pieces are connect with fixed part；
Interconnecting piece is connect by adhesive linkage with the structure of both sides at crack, so that fixed part is fixed at crack.
Further, interconnecting piece is integrally formed with fixed part.
Further, interconnecting piece is provided with multiple through-holes, and adhesive linkage can extend to interconnecting piece along the plane of fixed part
In multiple through-holes, by the connection of adhesive linkage and through-hole, fixed part to be fixed at crack.
Further, the through-hole on interconnecting piece is arranged in blossom type.
Further, a kind of Cracking-proof belt provided by the invention further includes fixed net；
Fixed net is set to fixed strip far from the side at crack, and fixed net is connected with fixed strip.
Further, fixed net is fixedly connected with fixed strip.
Further, fixed net uses glass fibre anti-cracking net；
Fixed strip uses PVC material.
Further, the thickness range of fixed strip is：0.5-1.5mm；
Fixed strip width range is：25-60mm；
The width range 8-10mm of fixed part.
A kind of production method of such as above-mentioned Cracking-proof belt provided by the invention, includes the following steps：
Glass fibre anti-cracking net is cut into the fixation net of 80-300mm by step 1；
Step 2 makes fixed strip by composite material, and fixed strip and fixed net is connected.
Further, composite material is mixed using PVC material and calcium carbonate；Wherein, calcium carbonate accounts for composite material
30%-40%.
A kind of Cracking-proof belt provided by the invention, including：Fixed strip and adhesive linkage；Fixed strip includes interconnecting piece and fixed part,
There are two interconnecting piece settings, and two interconnecting pieces are symmetrical arranged along fixed part, and two interconnecting pieces are connect with fixed part；Interconnecting piece
It is connect with the structure of both sides at crack by adhesive linkage, so that fixed part is fixed at crack；By fixed strip can along every
Either the seam crossing of plasterboard is fixed and is connect with partition plate or plasterboard additionally by interconnecting piece wallboard, and connects
Portion is provided with ventilation position, alleviates Cracking-proof belt existing in the prior art and is directly squeezed or stretches and deform or tear and is broken
The phenomenon that bad and Cracking-proof belt is heaved or tilted causes the inaesthetic technical problem of metope；Realize secondary structure and main body knot
Structure, between partition plate and partition plate, the anticracking between the plank of lightgage steel joist is implemented, and secondary structure and agent structure are increased,
Between partition plate and partition plate, service life between the plank of lightgage steel joist is more practical.
A kind of production method of such as above-mentioned Cracking-proof belt provided by the invention, includes the following steps：Step 1, by glass fibers
Dimension anti-cracking net is cut into the fixation net of 80-300mm.Step 2 makes fixed strip by composite material, and by fixed strip and fixes net
Connection；It can be fixed along the seam crossing of partition plate or plasterboard by fixed strip, it can be additionally by fixed net
Ensure gas permeability under the premise of, more ensure fixed strip stability, alleviate Cracking-proof belt existing in the prior art directly by
To the phenomenon that squeeze or stretching and deform or tear failure and Cracking-proof belt are heaved or tilted, the inaesthetic technology of metope is caused
Problem；Secondary structure and agent structure are realized, between partition plate and partition plate, the anticracking between the plank of lightgage steel joist is real
It applies, increases secondary structure and agent structure, between partition plate and partition plate, service life between the plank of lightgage steel joist, more
Add practicality.
Description of the drawings
It, below will be to specific in order to illustrate more clearly of the specific embodiment of the invention or technical solution in the prior art
Embodiment or attached drawing needed to be used in the description of the prior art are briefly described, it should be apparent that, in being described below
Attached drawing is some embodiments of the present invention, for those of ordinary skill in the art, before not making the creative labor
It puts, other drawings may also be obtained based on these drawings.
Fig. 1 is the overall structure diagram of Cracking-proof belt provided in an embodiment of the present invention；
Fig. 2 is the overall structure diagram under the first visual angle of Cracking-proof belt provided in an embodiment of the present invention；
Fig. 3 is the structural schematic diagram of the fixed strip of Cracking-proof belt provided in an embodiment of the present invention.
Icon：100- fixed strips；101- interconnecting pieces；111- through-holes；102- fixed parts；200- fixes net.
Specific implementation mode
Technical scheme of the present invention is clearly and completely described below in conjunction with attached drawing, it is clear that described implementation
Example is a part of the embodiment of the present invention, instead of all the embodiments.Based on the embodiments of the present invention, ordinary skill
The every other embodiment that personnel are obtained without making creative work, shall fall within the protection scope of the present invention.
In the description of the present invention, it should be noted that such as occur term "center", "upper", "lower", "left", "right",
"vertical", "horizontal", "inner", "outside" etc., indicated by orientation or positional relationship be orientation based on ... shown in the drawings or position
Relationship is merely for convenience of description of the present invention and simplification of the description, and not indicating or implying the indicated device or element must have
There is specific orientation, with specific azimuth configuration and operation, therefore is not considered as limiting the invention.In addition, as occurred
Term " first ", " second ", " third " are used for description purposes only, and are not understood to indicate or imply relative importance.
In the description of the present invention, it should be noted that unless otherwise clearly defined and limited, term " peace such as occur
Dress ", " connected ", " connection " shall be understood in a broad sense, for example, it may be being fixedly connected, may be a detachable connection, or integrally
Connection；It can be mechanical connection, can also be electrical connection；Can be directly connected, can also indirectly connected through an intermediary,
It can be the connection inside two elements.For the ordinary skill in the art, it can understand above-mentioned art with concrete condition
The concrete meaning of language in the present invention.
Fig. 1 is the overall structure diagram of Cracking-proof belt provided in this embodiment；Wherein, fixed net 200 and fixed strip 100 connect
It connects.
Fig. 2 is the overall structure diagram under the first visual angle of Cracking-proof belt provided in this embodiment；In fact, the first visual angle is
Along the direction of the side view of fixed band.
Fig. 3 is the structural schematic diagram of the fixed strip of Cracking-proof belt provided in this embodiment；Wherein, two interconnecting pieces 101 along
Fixed part 102 is symmetrical arranged, and interconnecting piece 101 is provided with multiple through-holes 111.
As shown in Figs. 1-3, a kind of Cracking-proof belt provided in this embodiment, including：Fixed strip 100 and adhesive linkage；Fixed strip 100
Including interconnecting piece 101 and fixed part 102, there are two the settings of interconnecting piece 101, and two interconnecting pieces 101 are symmetrically set along fixed part 102
It sets, and two interconnecting pieces 101 are connect with fixed part 102；Interconnecting piece 101 is connect by adhesive linkage with the structure of both sides at crack,
So that fixed part 102 is fixed at crack.
Wherein, the material of fixed strip 100 can be a variety of, such as：PVC material, PU materials, PP materials etc., due to P VC
Material has preferable stability and ductility, it is preferable that the material of fixed strip 100 is PVC material.
PVC material, polyvinyl chloride, English abbreviation PVC (Polyvinyl chloride), is vinyl chloride monomer (vinyl
Chloride monomer, abbreviation VCM) in initiators such as peroxide, azo-compounds；Or by freely under light, heat effect
The polymer that base polymerization reaction mechanism is polymerized.
PU materials, polyurethane material are the abbreviations of polyurethanes, and English name is polyurethane, it is a kind of
High molecular material.Polyurethane is a kind of emerging high-molecular organic material, is known as " the fifth-largest plastics ".
Prepared by PP materials, polypropylene is by propylene polymerization a kind of thermoplastic resin.It is divided by methyl arrangement position
Isotactic polypropylene (isotactic polypropylene), random polypropylene (atactic polypropylene) and rule poly- third
Three kinds of alkene (syndiotactic polypropylene).
The connection type of interconnecting piece 101 and fixed part 102 can be a variety of, such as：Bonding, by suture connection or
Connected by connected nail etc., it is preferable that the connection type of interconnecting piece 101 and fixed part 102 is bonding.
Further, interconnecting piece 101 and fixed part 102 are integrally formed, by interconnecting piece 101 and 102 one of fixed part at
Type can more preferably ensure that fixed part 102 is fixed on secondary structure and agent structure, partition plate and partition wall by interconnecting piece 101
Between plate, at the crack between the plank of lightgage steel joist, the stability of fixed part 102 ensure that.
Further, the thickness range of fixed strip 100 is：0.5-1.5mm；100 width range of fixed strip is：25-60mm；
The width range 8-10mm of fixed part 102.
Preferably, the width of fixed part 102 is 8mm, due to secondary structure and agent structure, partition plate and partition plate it
Between, the width in the crack between the plank of lightgage steel joist is generally 5-8mm, so, it, can be with when the width of fixed part 102 is 8mm
Meet the width for being more than crack under normal circumstances, so as to which preferably crack is covered and fixed.
In addition, working as secondary structure and agent structure, between partition plate and partition plate, the crack between the plank of lightgage steel joist
Width it is wide when, can by select bigger width fixed strip 100, so as to actual conditions select it is various sizes of solid
Determine item 100, in order to which fixed strip 100 is fixed on secondary structure and agent structure, between partition plate and partition plate, lightgage steel joist
At crack between plank, the stability of fixed part 102 ensure that.
Preferably, fixed strip 100 is be bonded by cementing agent with the connection type at crack.
In addition, the length of fixed strip 100 can carry out selection according to the length in different cracks, it is preferable that fixed strip 100
Select continuable banded structure.
A kind of Cracking-proof belt provided in this embodiment, including：Fixed strip 100 and adhesive linkage；Fixed strip 100 includes interconnecting piece
101 and fixed part 102, there are two the settings of interconnecting piece 101, and two interconnecting pieces 101 are symmetrical arranged along fixed part 102, and two
Interconnecting piece 101 is connect with fixed part 102；Interconnecting piece 101 is connect by adhesive linkage with the structure of both sides at crack, so that fixed part
102 are fixed at crack；It can be fixed along the seam crossing of partition plate or plasterboard by fixed strip 100, in addition led to
It crosses interconnecting piece 101 to connect with partition plate or plasterboard, and interconnecting piece 101 is provided with ventilation position, alleviates the prior art
Present in Cracking-proof belt be directly squeezed or stretch and deform or the phenomenon that tear failure and Cracking-proof belt are heaved or tilted,
Cause the inaesthetic technical problem of metope；Secondary structure and agent structure are realized, between partition plate and partition plate, lightgage steel joist
Plank between anticracking implement, increase secondary structure and agent structure, between partition plate and partition plate, the plate of lightgage steel joist
Service life between material, it is more practical.
On the basis of the above embodiments, further, the interconnecting piece 101 of Cracking-proof belt provided in this embodiment is provided with more
A through-hole 111, adhesive linkage can be extended to along the plane of fixed part 102 in multiple through-holes 111 of interconnecting piece 101, with by viscous
The connection for connecing layer and through-hole 111, fixed part 102 is fixed at crack.
The cross sectional shape of through-hole 111 can be a variety of, such as：Rectangle, circle, ellipse etc., preferably, through-hole 111
Cross sectional shape is circle.
Further, the through-hole 111 on interconnecting piece 101 is arranged in blossom type.
Wherein, when drilling through plum blossom type hole, it is first determined the first exhausting hole 111 passes through phase per two adjacent through-holes 111
Same spacing is drilled through；After having drilled through through-hole 111 of first row, determine the second exhausting hole 111, the second exhausting hole 111 with
111 spacing of through-hole of first row is identical as the adjacent spacing of two through-holes 111, in addition, the through-hole 111 of second row be respectively provided with
Near the center line of the two neighboring through-hole of first row 111, in the same manner, the spacing of the through-hole 111 and the through-hole 111 of second row of third row
Identical as the adjacent spacing of two through-holes 111, two through-holes adjacent with second row are arranged in the through-hole 111 of same third row
It near 111 center line, is repeated in and drills through, until completing whole through-holes 111, form blossom type through-hole 111.
Specifically, by the secondary structure and agent structure of the both sides at crack, between partition plate and partition plate, lightgage steel joist
Plank between spread cementing agent, at the alignment crack of the centre position of fixed part 102 so that fixed part 102 can be straight
It connects and is bonded at crack, extra cementing agent can be overflowed by through-hole 111 at interconnecting piece 101, and the cement that will be overflowed is passed through
Cementing agent can lead to along the surface rubbing of interconnecting piece 101 after the 111 cementing agent of through-hole of blossom type cooling is fixed
It crosses interconnecting piece 101 fixed part 102 is fixed at crack.
Further, a kind of Cracking-proof belt provided in this embodiment further includes fixed net 200；Fixed net 200 is set to fixation
Item 100 is connected far from the side at crack, fixed net 200 and fixed strip 100.
Further, fixed net 200 uses glass fibre anti-cracking net.
Fiberglass gridding cloth is to impregnate coating through the anti-lotion of macromolecule using fiberglass woven fabric as base material.To have
There are good alkali resistance, flexibility and through broadwise high resistance pulling force, the heat preservation of building external and internal wall can be widely used in, prevented
Water, cracking resistance etc..
Further, fixed net 200 is fixedly connected with fixed strip 100.
Wherein, the connection type of fixed net 200 and fixed strip 100 can be a variety of, such as：Fixed strip 100 passes through bonding
Mode and fixed net 200 it is compound, which cost is relatively low, thereby may be ensured that the stabilization of fixed strip 100 and fixed net 200
Property,
For another example：Fixed strip 100 is compound with fixed net 200 in a manner of suturing sewing machine, due to which cost compared with
Height is suitable for the smaller situation of the size of fixed strip 100.
Cracking-proof belt provided in this embodiment is provided with multiple through-holes 111 by interconnecting piece 101, and multiple through-holes 111 are in plum
Flower pattern is arranged, and being overflowed when fixed strip 100 is applied at crack, in each through-hole 111 has cementing agent, when each through-hole
After cementing agent in 111 is fixed, each through-hole 111 is exactly a fixing end, and fixed by multiple through-holes 111 is made
With can be fixed on fixed part 102 is very firm at crack；In addition, passing through the common work of fixed net 200 and fixed band
With the stability of guarantee fixed strip 100 alleviates Cracking-proof belt existing in the prior art and is directly squeezed or stretches and deform
Or tear failure and Cracking-proof belt the phenomenon that heaving or tilting, cause the inaesthetic technical problem of metope.
A kind of production method of such as above-mentioned Cracking-proof belt provided in this embodiment, includes the following steps：Step 1, by glass
Fiber anti-cracking net is cut into the fixation net 200 of 80-300mm；Step 2 makes fixed strip 100 by composite material, and by fixed strip
100 connect with fixed net 200.
Wherein, glass fibre anti-cracking net selects the self-adhesive tape of the glass fibre anti-cracking net of 80g, and specifically, glass fibre is anti-
Split every square of grammes per square metre of net be 80 grams, have excellent alkali resistance, durable, high-tensile and deformation resistance, Anti-cracking, no
Rotten, not blistering foam, outstanding tack need not go up primary coat, use quick, easy construction in advance.
When fixed strip 100 to be fixed at crack, since fixation net 200 selects oneself of the glass fibre anti-cracking net of 80g
Adhesive tape, fixed net 200 can and secondary structure and agent structure, between partition plate and partition plate or the tool of the plank of lightgage steel joist
Body structural bond can give fixed strip 100 certain extruding force, make while can preferably ensure firm at crack
Obtaining fixed strip 100 can preferably be fixed at crack, ensure the stability of fixed strip 100.
Further, composite material is mixed using PVC material and calcium carbonate；Wherein, calcium carbonate accounts for composite material
30%-40%.
Since the material is soft for PVC material, by the calcium carbonate material for adding 30%-40%, it is ensured that composite material
On the basis of ductility, the intensity of composite material is improved so that fixed strip 100 can be preferably fixed at crack so that be set
Meter is more perfect, more practical.
A kind of production method of such as above-mentioned Cracking-proof belt provided in this embodiment, includes the following steps：Step 1, by glass
Fiber anti-cracking net is cut into the fixation net 200 of 80-300mm.Step 2 makes fixed strip 100 by composite material, and by fixed strip
100 connect with fixed net 200；It can be fixed along the seam crossing of partition plate or plasterboard by fixed strip 100, in addition
It can more be ensured the stability of fixed strip 100 under the premise of ensureing gas permeability, alleviate existing skill by fixed net 200
Cracking-proof belt present in art is directly squeezed or stretches and deforms or tear failure and Cracking-proof belt is heaved or what is tilted shows
As causing the inaesthetic technical problem of metope；Secondary structure and agent structure are realized, between partition plate and partition plate, light steel
Anticracking between the plank of keel is implemented, and secondary structure and agent structure are increased, between partition plate and partition plate, lightgage steel joist
Plank between service life, it is more practical.
Finally it should be noted that：The above embodiments are only used to illustrate the technical solution of the present invention., rather than its limitations；To the greatest extent
Present invention has been described in detail with reference to the aforementioned embodiments for pipe, it will be understood by those of ordinary skill in the art that：Its according to
So can with technical scheme described in the above embodiments is modified, either to which part or all technical features into
Row equivalent replacement；And these modifications or replacements, various embodiments of the present invention technology that it does not separate the essence of the corresponding technical solution
The range of scheme.
Claims (10)
1. a kind of Cracking-proof belt, which is characterized in that including：Fixed strip and adhesive linkage；
The fixed strip includes interconnecting piece and fixed part, and there are two the interconnecting piece settings, and two interconnecting pieces are along described
Fixed part is symmetrical arranged, and two interconnecting pieces are connect with the fixed part；
The interconnecting piece is connect by the adhesive linkage with the structure of both sides at crack, so that the fixed part is fixed on crack
Place.
2. Cracking-proof belt according to claim 1, which is characterized in that the interconnecting piece is integrally formed with the fixed part.
3. Cracking-proof belt according to claim 1, which is characterized in that the interconnecting piece is provided with multiple through-holes, the bonding
Layer can be extended to along the plane of the fixed part in multiple through-holes of the interconnecting piece, to pass through the adhesive linkage and described logical
The connection in hole, the fixed part is fixed at crack.
4. Cracking-proof belt according to claim 3, which is characterized in that the through-hole on the interconnecting piece is arranged in blossom type.
5. according to claim 1-3 any one of them Cracking-proof belts, which is characterized in that further include fixed net；
The fixed net is set to the fixed strip far from the side at crack, and the fixed net is connected with the fixed strip.
6. Cracking-proof belt according to claim 5, which is characterized in that the fixed net is fixedly connected with the fixed strip.
7. Cracking-proof belt according to claim 6, which is characterized in that the fixed net uses glass fibre anti-cracking net；
The fixed strip uses PVC material.
8. Cracking-proof belt according to claim 1, which is characterized in that the thickness range of the fixed strip is：0.5-1.5mm；
The fixed strip width range is：25-60mm；
The width range 8-10mm of the fixed part.
9. a kind of production method of Cracking-proof belt as described in claim 1, which is characterized in that include the following steps：
Glass fibre anti-cracking net is cut into the fixation net of 80-300mm by step 1；
Step 2 makes fixed strip by composite material, and fixed strip and fixed net is connected.
10. the production method of Cracking-proof belt according to claim 9, which is characterized in that the composite material uses PVC material
It is mixed with calcium carbonate；Wherein, calcium carbonate accounts for the 30%-40% of the composite material.