CN108385436A - A kind of papermaking paint - Google Patents
A kind of papermaking paint Download PDFInfo
- Publication number
- CN108385436A CN108385436A CN201711354808.XA CN201711354808A CN108385436A CN 108385436 A CN108385436 A CN 108385436A CN 201711354808 A CN201711354808 A CN 201711354808A CN 108385436 A CN108385436 A CN 108385436A
- Authority
- CN
- China
- Prior art keywords
- nano
- papermaking paint
- tiny balloon
- coating
- thickener
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides a kind of papermaking paint, which is characterized in that includes the component of following parts by weight：Waterborne polyurethane resin 25 36, methyl methacrylate 28 43, ethylene vinyl acetate 17 29, disodium ethylene diamine tetraacetate 18 25, polyethylene glycol 12 19, dispersant 11 19, thickener 7 13, antifoaming agent 6 13, pH adjusting agent 8 22, polyimides tiny balloon 45 62, Polyhaxemethylenguanidine Hydrochloride 13 24, distilled water 51 74, nano-graphene particle 22 35, zinc hydride ferrite ceramics powder 21 38, nano-aluminum phosphate molecular sieve 34 55.By regulating and controlling the proportioning of ceramic powder and tiny balloon in the present invention, optimizes Compatibility of Coating Color, assign the functions such as paper anti-microbial property, flame retardant property, salt spray resistance；Improve the printability of coating paper simultaneously.
Description
Technical field
The invention belongs to functional material and pulp technology for making paper, and in particular to a kind of papermaking paint.
Background technology
Coating paper be at least one surface of body paper coating to be dried after pigment coating as main component and
It is formed.Coating paper can be used as the commercial prints objects such as poster, brochure, advertisement poster after polychrome printing or single color printing, or make
For publications such as books, magazines, it is widely used in routine work and life.
The property of coating directly affects ways and methods.A kind of existing common coating be based on starch,
When being produced applied to coating paper, the operability of coating operations is poor, coating weight is relatively low.Lower coating weight can not provide good
The problems such as good surface property, that there are surface roughnesses is larger for gained coating paper, anti-floating poor performance.The coating of coating simultaneously
Can be single, it cannot assign paper new function, be unfavorable for the development of coating paper.
Invention content
In view of this, the present invention provides a kind of papermaking paint, by regulating and controlling matching for ceramic powder and tiny balloon in the present invention
Than optimizing Compatibility of Coating Color, assigning the functions such as paper anti-microbial property, flame retardant property, salt spray resistance；Improve coating paper simultaneously
Printability.
The technical scheme is that：A kind of papermaking paint, which is characterized in that include the component of following parts by weight：Water
Property polyurethane resin 25-36, methyl methacrylate 28-43, ethane-acetic acid ethyenyl ester 17-29, ethylenediamine tetraacetic
Acetic acid disodium 18-25, polyethylene glycol 12-19, dispersant 11-19, thickener 7-13, antifoaming agent 6-13, pH adjusting agent 8-
22, polyimides tiny balloon 45-62, Polyhaxemethylenguanidine Hydrochloride 13-24, distilled water 115-160, nano-graphene
Grain 22-35, zinc hydride ferrite ceramics powder 21-38, nano-aluminum phosphate molecular sieve 34-55.
Further, the grain diameter of the polyimides tiny balloon is 200-400nm.
Further, the grain diameter of the nano-aluminum phosphate molecular sieve is 100-200nm.
Further, the dispersant is lauryl sodium sulfate, methyl anyl alcohol, guar gum, fatty acid polyethylene glycol ester
In one kind.
Further, the thickener is hydroxypropyl methyl cellulose.
Further, the antifoaming agent is dimethyl silicone polymer.
Further, the pH adjusting agent is aminomethyl propanol.
In the present invention, pass through polyimides tiny balloon, Polyhaxemethylenguanidine Hydrochloride, nano-graphene particle, zinc hydride
The synergistic complex role of ferrite ceramics powder, nano-aluminum phosphate molecular sieve, polyimides tiny balloon and nano-aluminum phosphate molecule
Sieve is internal to have unique three-dimensional netted space structure, can adsorb Polyhaxemethylenguanidine Hydrochloride, nano-graphene particle, reach
To the effect of sustained release, the antibacterial ability of coating of the present invention is significantly improved, while the zinc hydride ferrite ceramics powder added assigns this
Invention coating others functional characteristic；The effect of the helper components such as middle disodium ethylene diamine tetraacetate, polyethylene glycol through the invention,
Instant component can be made fully to merge, and there can be good adsorption capacity with paper.
Beneficial effects of the present invention：1. antibacterial paper paint preparation process of the present invention carries out at normal temperatures and pressures, it is not required to
New equipment is added, simple for process, production cost is low.After 2. coating of the present invention is coated on paper, assisted by each component
Effect acts on, and not only can effectively improve the functions such as anti-microbial property, flame retardant property, the salt spray resistance of paper, but also can assign paper
Good printability.3. being compared to antiseptic mode advantage is added in slurry：Retention rate is preferable, will not cause production process
In antiseptic waste, raw material can be saved；Its dosage added can be according to the requirement of the paper produced in wide range
It changes.
Preferably, preparation method of the invention is：Foundation is formulated aqueous polyurethane resin, metering system above
Sour methyl esters, ethane-acetic acid ethyenyl ester, disodium ethylene diamine tetraacetate, polyethylene glycol, dispersant are added in the water of coating dispersion bucket,
Rate of dispersion is maintained at 5000r/min, and jitter time reduces rotating speed to 2000r/min, antifoaming agent is added and continues to mix after being 15min
10min is closed, polyimides tiny balloon, Polyhaxemethylenguanidine Hydrochloride, nano-graphene particle, hydrogenation Zn ferrite pottery are added
Porcelain powder, nano-aluminum phosphate molecular sieve are gradually increased rotating speed to 8000r/min, after persistently disperseing 25min, then reduce rotating speed extremely
Thickener, pH adjusting agent is added in 2000r/min, disperses 10min, and the papermaking paint that solid content is 30-45% is made.
The present invention application method be：It is placed on body paper is smooth as required on coating machine, pressure tensioning volume, then coating
It collects and is pressed in top of form, put down fixed-wing, take a certain amount of papermaking paint, be evenly distributed on top of form, start button, paper
Coating is completed, and the paper after coating speed 30m/min coatings is put into pattern flash dryer, 105 DEG C of drying temperature, drying time
It is detected according to paper made from the above paint formulation and coating process through shaking flask standard measure for 45s, the results showed that, coating
Coating paper has reached 97% or more to staphylococcus aureus antimicrobial efficiency；Meanwhile after the coating of the above paint formulation, paper
Printability be obviously improved.
Specific implementation mode
Technical scheme of the present invention is clearly and completely described below in conjunction with embodiment, it is clear that described reality
It is only a part of the embodiment of the present invention to apply example, instead of all the embodiments.
Embodiment 1
A kind of papermaking paint, which is characterized in that include the component of following parts by weight：Waterborne polyurethane resin 27, first
Base methyl acrylate 32, ethane-acetic acid ethyenyl ester 21, disodium ethylene diamine tetraacetate 22, polyethylene glycol 15, dispersant 13,
Thickener 10, antifoaming agent 9, pH adjusting agent 14, polyimides tiny balloon 53, Polyhaxemethylenguanidine Hydrochloride 19, distilled water
130, nano-graphene particle 26, zinc hydride ferrite ceramics powder 27, nano-aluminum phosphate molecular sieve 45.
Further, the grain diameter of the polyimides tiny balloon is 300nm.
Further, the grain diameter of the nano-aluminum phosphate molecular sieve is 180nm.
Further, the dispersant is lauryl sodium sulfate.
Further, the thickener is hydroxypropyl methyl cellulose.
Further, the antifoaming agent is dimethyl silicone polymer.
Further, the pH adjusting agent is aminomethyl propanol.
In the present invention, pass through polyimides tiny balloon, Polyhaxemethylenguanidine Hydrochloride, nano-graphene particle, zinc hydride
The synergistic complex role of ferrite ceramics powder, nano-aluminum phosphate molecular sieve, polyimides tiny balloon and nano-aluminum phosphate molecule
Sieve is internal to have unique three-dimensional netted space structure, can adsorb Polyhaxemethylenguanidine Hydrochloride, nano-graphene particle, reach
To the effect of sustained release, the antibacterial ability of coating of the present invention is significantly improved, while the zinc hydride ferrite ceramics powder added assigns this
Invention coating others functional characteristic；The effect of the helper components such as middle disodium ethylene diamine tetraacetate, polyethylene glycol through the invention,
Instant component can be made fully to merge, and there can be good adsorption capacity with paper.
Beneficial effects of the present invention：1. antibacterial paper paint preparation process of the present invention carries out at normal temperatures and pressures, it is not required to
New equipment is added, simple for process, production cost is low.After 2. coating of the present invention is coated on paper, assisted by each component
Effect acts on, and not only can effectively improve the functions such as anti-microbial property, flame retardant property, the salt spray resistance of paper, but also can assign paper
Good printability.3. being compared to antiseptic mode advantage is added in slurry：Retention rate is preferable, will not cause production process
In antiseptic waste, raw material can be saved；Its dosage added can be according to the requirement of the paper produced in wide range
It changes.
Preferably, preparation method of the invention is：Foundation is formulated aqueous polyurethane resin, metering system above
Sour methyl esters, ethane-acetic acid ethyenyl ester, disodium ethylene diamine tetraacetate, polyethylene glycol, dispersant are added in the water of coating dispersion bucket,
Rate of dispersion is maintained at 5000r/min, and jitter time reduces rotating speed to 2000r/min, antifoaming agent is added and continues to mix after being 15min
10min is closed, polyimides tiny balloon, Polyhaxemethylenguanidine Hydrochloride, nano-graphene particle, hydrogenation Zn ferrite pottery are added
Porcelain powder, nano-aluminum phosphate molecular sieve are gradually increased rotating speed to 8000r/min, after persistently disperseing 25min, then reduce rotating speed extremely
Thickener, pH adjusting agent is added in 2000r/min, disperses 10min, and the papermaking paint of the present invention is made.
Embodiment 2
A kind of papermaking paint, which is characterized in that include the component of following parts by weight：Waterborne polyurethane resin 25, first
Base methyl acrylate 28, ethane-acetic acid ethyenyl ester 17, disodium ethylene diamine tetraacetate 18, polyethylene glycol 12, dispersant 11,
Thickener 7, antifoaming agent 6, pH adjusting agent 8, polyimides tiny balloon 45, Polyhaxemethylenguanidine Hydrochloride 13, distilled water
115, nano-graphene particle 22, zinc hydride ferrite ceramics powder 21, nano-aluminum phosphate molecular sieve 34.
Further, the grain diameter of the polyimides tiny balloon is 200nm.
Further, the grain diameter of the nano-aluminum phosphate molecular sieve is 100nm.
Further, the dispersant is methyl anyl alcohol.
Further, the thickener is hydroxypropyl methyl cellulose.
Further, the antifoaming agent is dimethyl silicone polymer.
Further, the pH adjusting agent is aminomethyl propanol.
Embodiment 3
A kind of papermaking paint, which is characterized in that include the component of following parts by weight：Waterborne polyurethane resin 36, first
Base methyl acrylate 43, ethane-acetic acid ethyenyl ester 29, disodium ethylene diamine tetraacetate 25, polyethylene glycol 19, dispersant 19,
Thickener 13, antifoaming agent 13, pH adjusting agent 22, polyimides tiny balloon 62, Polyhaxemethylenguanidine Hydrochloride 24, distillation
Water 160, nano-graphene particle 35, zinc hydride ferrite ceramics powder 38, nano-aluminum phosphate molecular sieve 55.
Further, the grain diameter of the polyimides tiny balloon is 400nm.
Further, the grain diameter of the nano-aluminum phosphate molecular sieve is 200nm.
Further, the dispersant is guar gum.
Further, the thickener is hydroxypropyl methyl cellulose.
Further, the antifoaming agent is dimethyl silicone polymer.
Further, the pH adjusting agent is aminomethyl propanol.
Embodiment 4
A kind of papermaking paint, which is characterized in that include the component of following parts by weight：Waterborne polyurethane resin 28, first
Base methyl acrylate 35, ethane-acetic acid ethyenyl ester 20, disodium ethylene diamine tetraacetate 22, polyethylene glycol 14, dispersant 13,
Thickener 10, antifoaming agent 9, pH adjusting agent 16, polyimides tiny balloon 52, Polyhaxemethylenguanidine Hydrochloride 18, distilled water
138, nano-graphene particle 27, zinc hydride ferrite ceramics powder 26, nano-aluminum phosphate molecular sieve 41.
Further, the grain diameter of the polyimides tiny balloon is 250nm.
Further, the grain diameter of the nano-aluminum phosphate molecular sieve is 150nm.
Further, the dispersant is fatty acid polyethylene glycol ester.
Further, the thickener is hydroxypropyl methyl cellulose.
Further, the antifoaming agent is dimethyl silicone polymer.
Further, the pH adjusting agent is aminomethyl propanol.
Embodiment 5
A kind of papermaking paint, which is characterized in that include the component of following parts by weight：Waterborne polyurethane resin 34, first
Base methyl acrylate 38, ethane-acetic acid ethyenyl ester 25, disodium ethylene diamine tetraacetate 23, polyethylene glycol 17, dispersant 16,
Thickener 11, antifoaming agent 10, pH adjusting agent 19, polyimides tiny balloon 58, Polyhaxemethylenguanidine Hydrochloride 22, distillation
Water 150, nano-graphene particle 32, zinc hydride ferrite ceramics powder 35, nano-aluminum phosphate molecular sieve 53.
Further, the grain diameter of the polyimides tiny balloon is 350nm.
Further, the grain diameter of the nano-aluminum phosphate molecular sieve is 130nm.
Further, the dispersant is lauryl sodium sulfate.
Further, the thickener is hydroxypropyl methyl cellulose.
Further, the antifoaming agent is dimethyl silicone polymer.
Further, the pH adjusting agent is aminomethyl propanol.
Embodiment 6
A kind of papermaking paint, which is characterized in that include the component of following parts by weight：Waterborne polyurethane resin 32, first
Base methyl acrylate 37, ethane-acetic acid ethyenyl ester 24, disodium ethylene diamine tetraacetate 21, polyethylene glycol 16, dispersant 17,
Thickener 9, antifoaming agent 11, pH adjusting agent 18, polyimides tiny balloon 54, Polyhaxemethylenguanidine Hydrochloride 17, distilled water
146, nano-graphene particle 29, zinc hydride ferrite ceramics powder 27, nano-aluminum phosphate molecular sieve 39.
Further, the grain diameter of the polyimides tiny balloon is 250nm.
Further, the grain diameter of the nano-aluminum phosphate molecular sieve is 160nm.
Further, the dispersant is methyl anyl alcohol.
Further, the thickener is hydroxypropyl methyl cellulose.
Further, the antifoaming agent is dimethyl silicone polymer.
Further, the pH adjusting agent is aminomethyl propanol.
Comparative example 1
A kind of papermaking paint, which is characterized in that include the component of following parts by weight：Waterborne polyurethane resin 32, first
Base methyl acrylate 37, ethane-acetic acid ethyenyl ester 24, disodium ethylene diamine tetraacetate 21, polyethylene glycol 16, dispersant 17,
Thickener 9, antifoaming agent 11, pH adjusting agent 18, Polyhaxemethylenguanidine Hydrochloride 17, distilled water 146, hydrogenation Zn ferrite pottery
Porcelain powder 27, nano-aluminum phosphate molecular sieve 39.
Further, the grain diameter of the nano-aluminum phosphate molecular sieve is 160nm.
Further, the dispersant is methyl anyl alcohol.
Further, the thickener is hydroxypropyl methyl cellulose.
Further, the antifoaming agent is dimethyl silicone polymer.
Further, the pH adjusting agent is aminomethyl propanol.
Comparative example 2
A kind of papermaking paint, which is characterized in that include the component of following parts by weight：Waterborne polyurethane resin 32, first
Base methyl acrylate 37, ethane-acetic acid ethyenyl ester 24, dispersant 17, thickener 9, antifoaming agent 11, pH adjusting agent 18,
Polyimides tiny balloon 54, Polyhaxemethylenguanidine Hydrochloride 17, distilled water 146, nano-graphene particle 29, hydrogenation zinc-iron
Ferrite ceramics powder 27, nano-aluminum phosphate molecular sieve 39.
Further, the grain diameter of the polyimides tiny balloon is 250nm.
Further, the grain diameter of the nano-aluminum phosphate molecular sieve is 160nm.
Further, the dispersant is methyl anyl alcohol.
Further, the thickener is hydroxypropyl methyl cellulose.
Further, the antifoaming agent is dimethyl silicone polymer.
Further, the pH adjusting agent is aminomethyl propanol.
Comparative example 3
A kind of papermaking paint, which is characterized in that include the component of following parts by weight：Waterborne polyurethane resin 32, first
Base methyl acrylate 37, ethane-acetic acid ethyenyl ester 24, disodium ethylene diamine tetraacetate 21, polyethylene glycol 16, dispersant 17,
Thickener 9, antifoaming agent 11, pH adjusting agent 18, polyimides tiny balloon 54, Polyhaxemethylenguanidine Hydrochloride 17, distilled water
146, nano-graphene particle 29.
Further, the grain diameter of the polyimides tiny balloon is 250nm.
Further, the dispersant is methyl anyl alcohol.
Further, the thickener is hydroxypropyl methyl cellulose.
Further, the antifoaming agent is dimethyl silicone polymer.
Further, the pH adjusting agent is aminomethyl propanol.
Coating property is tested
Salt spray resistance
By the paint spraying in embodiment and comparative example in wooden test piece.After paint spraying, stands 48 hours and wait for that coating is completely solid
It is tested after chemical conversion film.Adhesive force test, neutral salt spray test carried out to above-mentioned coating, test method according to《GB/T
1720-1979 paint film adhesion measuring methods》、《GB/T 10125-2012 artificial atmosphere corrosion test salt spray tests》It carries out, surveys
Test result such as following table.
Anti-microbial property and flame retardant property
Anti-microbial property test is carried out according to GB/T 21866-2008；According to GB1244-2005 using cell combustion method to above-mentioned
The coating of embodiment carries out flame retardant property test, and the results are shown in table below.
It is obvious to a person skilled in the art that invention is not limited to the details of the above exemplary embodiments, and do not carrying on the back
In the case of spirit or essential attributes from the present invention, the present invention can be realized in other specific forms.Therefore, no matter from which
From the point of view of a bit, the present embodiments are to be considered as illustrative and not restrictive, and the scope of the present invention is wanted by appended right
Ask rather than above description limit, it is intended that by all changes that come within the meaning and range of equivalency of the claims
It is included within the present invention.
In addition, it should be understood that although this specification is described in terms of embodiments, but not each embodiment is only wrapped
Containing an independent technical solution, this description of the specification is merely for the sake of clarity, and those skilled in the art should
It considers the specification as a whole, the technical solutions in the various embodiments may also be suitably combined, forms those skilled in the art
The other embodiment being appreciated that.It is noted that the technical characteristic not being described in detail in the present invention, can pass through this
Field any prior art is realized.
Claims (7)
1. a kind of papermaking paint, which is characterized in that include the component of following parts by weight：Waterborne polyurethane resin 25-
36, methyl methacrylate 28-43, ethane-acetic acid ethyenyl ester 17-29, disodium ethylene diamine tetraacetate 18-25, polyethylene glycol
12-19, dispersant 11-19, thickener 7-13, antifoaming agent 6-13, pH adjusting agent 8-22, polyimides tiny balloon 45-
62, Polyhaxemethylenguanidine Hydrochloride 13-24, distilled water 115-160, nano-graphene particle 22-35, hydrogenation Zn ferrite pottery
Porcelain powder 21-38, nano-aluminum phosphate molecular sieve 34-55.
2. papermaking paint according to claim 1, which is characterized in that the grain diameter of the polyimides tiny balloon is
200-400nm。
3. papermaking paint according to claim 1, which is characterized in that the grain diameter of the nano-aluminum phosphate molecular sieve is
100-200nm。
4. papermaking paint according to claim 1, which is characterized in that the dispersant is lauryl sodium sulfate, methyl
One kind in amylalcohol, guar gum, fatty acid polyethylene glycol ester.
5. papermaking paint according to claim 1, which is characterized in that the thickener is hydroxypropyl methyl cellulose.
6. papermaking paint according to claim 1, which is characterized in that the antifoaming agent is dimethyl silicone polymer.
7. papermaking paint according to claim 1, which is characterized in that the pH adjusting agent is aminomethyl propanol.