CN108342070A - 一种建筑专用保温隔热板材及其制备方法 - Google Patents
一种建筑专用保温隔热板材及其制备方法 Download PDFInfo
- Publication number
- CN108342070A CN108342070A CN201810418227.6A CN201810418227A CN108342070A CN 108342070 A CN108342070 A CN 108342070A CN 201810418227 A CN201810418227 A CN 201810418227A CN 108342070 A CN108342070 A CN 108342070A
- Authority
- CN
- China
- Prior art keywords
- parts
- thermal insulation
- mud
- waterproofing agent
- building special
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
本发明公开了一种建筑专用保温隔热板材，包括以下重量份的原料：聚氨酯20～30份、可发泡性聚苯乙烯10～20份、粉煤灰15～30份、改性膨润土8～19份、膨胀玻化微珠12～27份、可分散乳胶粉6～11份、聚丙烯纤维2～4份、布纤维1～3份、羧甲基纤维素钠2～3份、防水剂1～2份、阻燃剂1～3份。所述建筑专用保温隔热板材通过控制原料的种类及原料之间的配比，制备出的产品吸水率低，耐久性好，具有很好的隔热保温效果，并且防火性能好，不会对对人类的生命、安全造成威胁。
Description
技术领域
本发明属于节能产品技术领域，具体涉及一种建筑专用保温隔热板材及其制备方法。
背景技术
保温隔热是建筑节能中最主要的节能措施，目前我国的保温材料品种很多，但普遍存在吸水率高、耐久性差或易燃、防火性能差的问题，前者使得保温材料的保温性能大大降低，影响了保温隔热的效果，增加空调***的能量消耗，后者会对人类的生命、安全造成威胁。
发明内容
本发明提供了一种建筑专用保温隔热板材及其制备方法，解决了背景技术中的问题，所述建筑专用保温隔热板材通过控制原料的种类及原料之间的配比，制备出的产品吸水率低，耐久性好，具有很好的隔热保温效果，并且防火性能好，不会对对人类的生命、安全造成威胁。
为了解决现有技术存在的问题，采用如下技术方案：
一种建筑专用保温隔热板材，包括以下重量份的原料：聚氨酯20～30份、可发泡性聚苯乙烯10～20份、粉煤灰15～30份、改性膨润土8～19份、膨胀玻化微珠12～27份、可分散乳胶粉6～11份、聚丙烯纤维2～4份、布纤维1～3份、羧甲基纤维素钠2～3份、防水剂1～2份、阻燃剂1～3份。
优选的，所述建筑专用保温隔热板材，包括以下重量份的原料：聚氨酯24～28份、可发泡性聚苯乙烯11～17份、粉煤灰20～25份、改性膨润土10～17份、膨胀玻化微珠15～24份、可分散乳胶粉8～10份、聚丙烯纤维2.5～3.2份、布纤维1.7～2.1份、羧甲基纤维素钠2.3～2.9份、防水剂1.1～1.6份、阻燃剂1.5～1.9份。
优选的，所述建筑专用保温隔热板材，包括以下重量份的原料：聚氨酯25份、可发泡性聚苯乙烯16份、粉煤灰23份、改性膨润土14份、膨胀玻化微珠20份、可分散乳胶粉9份、聚丙烯纤维2.7份、布纤维2份、羧甲基纤维素钠2.4份、防水剂1.1份、阻燃剂1.8份。
优选的，所述改性膨润土的制备方法如下：
（1）按重量份计，称取膨润土粉末100份、纳米氧化钙40份、纳米碳酸钙25份、环氧树脂7份、酚醛树脂15份；
（2）将膨润土粉末、纳米氧化钙和纳米碳酸钙进行混合，得到混合物；
（3）向步骤（2）所得的混合物中加入环氧树脂和酚醛树脂，得到所述改性膨润土。
优选的，所述防水剂为三乙醇胺、甲基硅醇钠防水剂或硫酸铝防水剂中的一种。
优选的，所述阻燃剂为三氧化二锑。
一种制备所述建筑专用保温隔热板材的方法，包括以下步骤：
（1）按上述配方称取聚氨酯、可发泡性聚苯乙烯、粉煤灰、改性膨润土、膨胀玻化微珠、可分散乳胶粉、聚丙烯纤维、布纤维、羧甲基纤维素钠、防水剂、阻燃剂，备用；
（2）将聚氨酯、可发泡性聚苯乙烯、可分散乳胶粉置于反应釜中搅拌混合均匀，然后升温至50～70℃，保温搅拌混合20～30分钟，得混合物料A；
（3）将粉煤灰、改性膨润土、膨胀玻化微珠混合均匀，然后加水至物料中含水量为22%～28%，搅拌混合均匀，然后加入聚丙烯纤维、布纤维、羧甲基纤维素钠，搅拌混合均匀，得混合物料B；
（4）将混合物料A和混合物料B混合，然后加入防水剂、阻燃剂，搅拌混合，得混合物料C；
（5）将混合物料C送至模具中，进行加压成型，然后经过5～24h水化后，混合物料C终凝后进行脱模，脱模后在自然条件下养护，即得所述建筑专用保温隔热板材。
优选的，所述养护时间为7～12天。
本发明与现有技术相比，其具有以下有益效果：
本发明所述建筑专用保温隔热板材通过控制原料的种类及原料之间的配比，制备出的产品吸水率低，耐久性好，具有很好的隔热保温效果，并且防火性能好，不会对对人类的生命、安全造成威胁，具体如下：
（1）本发明原料中添加了聚氨酯、可发泡性聚苯乙烯、粉煤灰、改性膨润土及膨胀玻化微珠，聚氨酯、可发泡性聚苯乙烯、粉煤灰、改性膨润土及膨胀玻化微珠之间相互协同作用，制备出的产品为多孔结构，具有很好的隔热保温效果，并且加入防水剂，可以降低产品的吸水率，提高产品的保温性能；
（2）本发明原料中添加了粉煤灰、改性膨润土及膨胀玻化微珠、阻燃剂等，在提高产品的保温性能的同时，还可以提高产品的防火性能。
具体实施方式
下面结合具体实施例，进一步阐述本发明。这些实施例仅用于说明本发明而不用于限制本发明的范围。
实施例1
本实施例涉及一种建筑专用保温隔热板材，包括以下重量份的原料：聚氨酯20份、可发泡性聚苯乙烯10份、粉煤灰15份、改性膨润土8份、膨胀玻化微珠12份、可分散乳胶粉6份、聚丙烯纤维2份、布纤维1份、羧甲基纤维素钠2份、防水剂1份、阻燃剂1份。
其中，所述改性膨润土的制备方法如下：
（1）按重量份计，称取膨润土粉末100份、纳米氧化钙40份、纳米碳酸钙25份、环氧树脂7份、酚醛树脂15份；
（2）将膨润土粉末、纳米氧化钙和纳米碳酸钙进行混合，得到混合物；
（3）向步骤（2）所得的混合物中加入环氧树脂和酚醛树脂，得到所述改性膨润土。
其中，所述防水剂为三乙醇胺。
其中，所述阻燃剂为三氧化二锑。
一种制备所述建筑专用保温隔热板材的方法，包括以下步骤：
（1）按上述配方称取聚氨酯、可发泡性聚苯乙烯、粉煤灰、改性膨润土、膨胀玻化微珠、可分散乳胶粉、聚丙烯纤维、布纤维、羧甲基纤维素钠、防水剂、阻燃剂，备用；
（2）将聚氨酯、可发泡性聚苯乙烯、可分散乳胶粉置于反应釜中搅拌混合均匀，然后升温至50℃，保温搅拌混合20分钟，得混合物料A；
（3）将粉煤灰、改性膨润土、膨胀玻化微珠混合均匀，然后加水至物料中含水量为22%，搅拌混合均匀，然后加入聚丙烯纤维、布纤维、羧甲基纤维素钠，搅拌混合均匀，得混合物料B；
（4）将混合物料A和混合物料B混合，然后加入防水剂、阻燃剂，搅拌混合，得混合物料C；
（5）将混合物料C送至模具中，进行加压成型，然后经过5h水化后，混合物料C终凝后进行脱模，脱模后在自然条件下养护，即得所述建筑专用保温隔热板材。
其中，所述养护时间为7天。
实施例2
本实施例涉及一种建筑专用保温隔热板材，包括以下重量份的原料：聚氨酯30份、可发泡性聚苯乙烯20份、粉煤灰30份、改性膨润土19份、膨胀玻化微珠27份、可分散乳胶粉11份、聚丙烯纤维4份、布纤维3份、羧甲基纤维素钠3份、防水剂2份、阻燃剂3份。
其中，所述改性膨润土的制备方法如下：
（1）按重量份计，称取膨润土粉末100份、纳米氧化钙40份、纳米碳酸钙25份、环氧树脂7份、酚醛树脂15份；
（2）将膨润土粉末、纳米氧化钙和纳米碳酸钙进行混合，得到混合物；
（3）向步骤（2）所得的混合物中加入环氧树脂和酚醛树脂，得到所述改性膨润土。
其中，所述防水剂为甲基硅醇钠防水剂。
其中，所述阻燃剂为三氧化二锑。
一种制备所述建筑专用保温隔热板材的方法，包括以下步骤：
（1）按上述配方称取聚氨酯、可发泡性聚苯乙烯、粉煤灰、改性膨润土、膨胀玻化微珠、可分散乳胶粉、聚丙烯纤维、布纤维、羧甲基纤维素钠、防水剂、阻燃剂，备用；
（2）将聚氨酯、可发泡性聚苯乙烯、可分散乳胶粉置于反应釜中搅拌混合均匀，然后升温至70℃，保温搅拌混合30分钟，得混合物料A；
（3）将粉煤灰、改性膨润土、膨胀玻化微珠混合均匀，然后加水至物料中含水量为28%，搅拌混合均匀，然后加入聚丙烯纤维、布纤维、羧甲基纤维素钠，搅拌混合均匀，得混合物料B；
（4）将混合物料A和混合物料B混合，然后加入防水剂、阻燃剂，搅拌混合，得混合物料C；
（5）将混合物料C送至模具中，进行加压成型，然后经过24h水化后，混合物料C终凝后进行脱模，脱模后在自然条件下养护，即得所述建筑专用保温隔热板材。
其中，所述养护时间为12天。
实施例3
本实施例涉及一种建筑专用保温隔热板材，包括以下重量份的原料：聚氨酯24份、可发泡性聚苯乙烯11份、粉煤灰20份、改性膨润土10份、膨胀玻化微珠15份、可分散乳胶粉8份、聚丙烯纤维2.5份、布纤维1.7份、羧甲基纤维素钠2.3份、防水剂1.1份、阻燃剂1.5份。
其中，所述改性膨润土的制备方法如下：
（1）按重量份计，称取膨润土粉末100份、纳米氧化钙40份、纳米碳酸钙25份、环氧树脂7份、酚醛树脂15份；
（2）将膨润土粉末、纳米氧化钙和纳米碳酸钙进行混合，得到混合物；
（3）向步骤（2）所得的混合物中加入环氧树脂和酚醛树脂，得到所述改性膨润土。
其中，所述防水剂为硫酸铝防水剂。
其中，所述阻燃剂为三氧化二锑。
一种制备所述建筑专用保温隔热板材的方法，包括以下步骤：
（1）按上述配方称取聚氨酯、可发泡性聚苯乙烯、粉煤灰、改性膨润土、膨胀玻化微珠、可分散乳胶粉、聚丙烯纤维、布纤维、羧甲基纤维素钠、防水剂、阻燃剂，备用；
（2）将聚氨酯、可发泡性聚苯乙烯、可分散乳胶粉置于反应釜中搅拌混合均匀，然后升温至55℃，保温搅拌混合23分钟，得混合物料A；
（3）将粉煤灰、改性膨润土、膨胀玻化微珠混合均匀，然后加水至物料中含水量为24%，搅拌混合均匀，然后加入聚丙烯纤维、布纤维、羧甲基纤维素钠，搅拌混合均匀，得混合物料B；
（4）将混合物料A和混合物料B混合，然后加入防水剂、阻燃剂，搅拌混合，得混合物料C；
（5）将混合物料C送至模具中，进行加压成型，然后经过8h水化后，混合物料C终凝后进行脱模，脱模后在自然条件下养护，即得所述建筑专用保温隔热板材。
其中，所述养护时间为8天。
实施例4
本实施例涉及一种建筑专用保温隔热板材，包括以下重量份的原料：聚氨酯28份、可发泡性聚苯乙烯17份、粉煤灰25份、改性膨润土17份、膨胀玻化微珠24份、可分散乳胶粉10份、聚丙烯纤维3.2份、布纤维2.1份、羧甲基纤维素钠2.9份、防水剂1.6份、阻燃剂1.9份。
其中，所述改性膨润土的制备方法如下：
（1）按重量份计，称取膨润土粉末100份、纳米氧化钙40份、纳米碳酸钙25份、环氧树脂7份、酚醛树脂15份；
（2）将膨润土粉末、纳米氧化钙和纳米碳酸钙进行混合，得到混合物；
（3）向步骤（2）所得的混合物中加入环氧树脂和酚醛树脂，得到所述改性膨润土。
其中，所述防水剂为三乙醇胺。
其中，所述阻燃剂为三氧化二锑。
一种制备所述建筑专用保温隔热板材的方法，包括以下步骤：
（1）按上述配方称取聚氨酯、可发泡性聚苯乙烯、粉煤灰、改性膨润土、膨胀玻化微珠、可分散乳胶粉、聚丙烯纤维、布纤维、羧甲基纤维素钠、防水剂、阻燃剂，备用；
（2）将聚氨酯、可发泡性聚苯乙烯、可分散乳胶粉置于反应釜中搅拌混合均匀，然后升温至60℃，保温搅拌混合25分钟，得混合物料A；
（3）将粉煤灰、改性膨润土、膨胀玻化微珠混合均匀，然后加水至物料中含水量为25%，搅拌混合均匀，然后加入聚丙烯纤维、布纤维、羧甲基纤维素钠，搅拌混合均匀，得混合物料B；
（4）将混合物料A和混合物料B混合，然后加入防水剂、阻燃剂，搅拌混合，得混合物料C；
（5）将混合物料C送至模具中，进行加压成型，然后经过12h水化后，混合物料C终凝后进行脱模，脱模后在自然条件下养护，即得所述建筑专用保温隔热板材。
其中，所述养护时间为9天。
实施例5
本实施例涉及一种建筑专用保温隔热板材，包括以下重量份的原料：聚氨酯25份、可发泡性聚苯乙烯16份、粉煤灰23份、改性膨润土14份、膨胀玻化微珠20份、可分散乳胶粉9份、聚丙烯纤维2.7份、布纤维2份、羧甲基纤维素钠2.4份、防水剂1.1份、阻燃剂1.8份。
其中，所述改性膨润土的制备方法如下：
（1）按重量份计，称取膨润土粉末100份、纳米氧化钙40份、纳米碳酸钙25份、环氧树脂7份、酚醛树脂15份；
（2）将膨润土粉末、纳米氧化钙和纳米碳酸钙进行混合，得到混合物；
（3）向步骤（2）所得的混合物中加入环氧树脂和酚醛树脂，得到所述改性膨润土。
其中，所述防水剂为硫酸铝防水剂。
其中，所述阻燃剂为三氧化二锑。
一种制备所述建筑专用保温隔热板材的方法，包括以下步骤：
（1）按上述配方称取聚氨酯、可发泡性聚苯乙烯、粉煤灰、改性膨润土、膨胀玻化微珠、可分散乳胶粉、聚丙烯纤维、布纤维、羧甲基纤维素钠、防水剂、阻燃剂，备用；
（2）将聚氨酯、可发泡性聚苯乙烯、可分散乳胶粉置于反应釜中搅拌混合均匀，然后升温至65℃，保温搅拌混合28分钟，得混合物料A；
（3）将粉煤灰、改性膨润土、膨胀玻化微珠混合均匀，然后加水至物料中含水量为27%，搅拌混合均匀，然后加入聚丙烯纤维、布纤维、羧甲基纤维素钠，搅拌混合均匀，得混合物料B；
（4）将混合物料A和混合物料B混合，然后加入防水剂、阻燃剂，搅拌混合，得混合物料C；
（5）将混合物料C送至模具中，进行加压成型，然后经过20h水化后，混合物料C终凝后进行脱模，脱模后在自然条件下养护，即得所述建筑专用保温隔热板材。
其中，所述养护时间为11天。
以上对本发明的具体实施例进行了描述。需要理解的是，本发明并不局限于上述特定实施方式，本领域技术人员可以在权利要求的范围内做出各种变形或修改，这并不影响本发明的实质内容。
Claims (8)
1.一种建筑专用保温隔热板材，其特征在于，包括以下重量份的原料：聚氨酯20～30份、可发泡性聚苯乙烯10～20份、粉煤灰15～30份、改性膨润土8～19份、膨胀玻化微珠12～27份、可分散乳胶粉6～11份、聚丙烯纤维2～4份、布纤维1～3份、羧甲基纤维素钠2～3份、防水剂1～2份、阻燃剂1～3份。
2.根据权利要求1所述的建筑专用保温隔热板材，其特征在于，包括以下重量份的原料：聚氨酯24～28份、可发泡性聚苯乙烯11～17份、粉煤灰20～25份、改性膨润土10～17份、膨胀玻化微珠15～24份、可分散乳胶粉8～10份、聚丙烯纤维2.5～3.2份、布纤维1.7～2.1份、羧甲基纤维素钠2.3～2.9份、防水剂1.1～1.6份、阻燃剂1.5～1.9份。
3.根据权利要求1所述的建筑专用保温隔热板材，其特征在于，包括以下重量份的原料：聚氨酯25份、可发泡性聚苯乙烯16份、粉煤灰23份、改性膨润土14份、膨胀玻化微珠20份、可分散乳胶粉9份、聚丙烯纤维2.7份、布纤维2份、羧甲基纤维素钠2.4份、防水剂1.1份、阻燃剂1.8份。
4.根据权利要求1所述的建筑专用保温隔热板材，其特征在于，所述改性膨润土的制备方法如下：
（1）按重量份计，称取膨润土粉末100份、纳米氧化钙40份、纳米碳酸钙25份、环氧树脂7份、酚醛树脂15份；
（2）将膨润土粉末、纳米氧化钙和纳米碳酸钙进行混合，得到混合物；
（3）向步骤（2）所得的混合物中加入环氧树脂和酚醛树脂，得到所述改性膨润土。
5.根据权利要求1所述的建筑专用保温隔热板材，其特征在于，所述防水剂为三乙醇胺、甲基硅醇钠防水剂或硫酸铝防水剂中的一种。
6.根据权利要求1所述的建筑专用保温隔热板材，其特征在于，所述阻燃剂为三氧化二锑。
7.一种制备权利要求1～6任一项所述建筑专用保温隔热板材的方法，其特征在于，包括以下步骤：
（1）按上述配方称取聚氨酯、可发泡性聚苯乙烯、粉煤灰、改性膨润土、膨胀玻化微珠、可分散乳胶粉、聚丙烯纤维、布纤维、羧甲基纤维素钠、防水剂、阻燃剂，备用；
（2）将聚氨酯、可发泡性聚苯乙烯、可分散乳胶粉置于反应釜中搅拌混合均匀，然后升温至50～70℃，保温搅拌混合20～30分钟，得混合物料A；
（3）将粉煤灰、改性膨润土、膨胀玻化微珠混合均匀，然后加水至物料中含水量为22%～28%，搅拌混合均匀，然后加入聚丙烯纤维、布纤维、羧甲基纤维素钠，搅拌混合均匀，得混合物料B；
（4）将混合物料A和混合物料B混合，然后加入防水剂、阻燃剂，搅拌混合，得混合物料C；
（5）将混合物料C送至模具中，进行加压成型，然后经过5～24h水化后，混合物料C终凝后进行脱模，脱模后在自然条件下养护，即得所述建筑专用保温隔热板材。
8.根据权利要求7所述的制备方法，其特征在于，所述养护时间为7～12天。