CN108339396A - 一种空气净化器的净化组合物及其制备方法 - Google Patents
一种空气净化器的净化组合物及其制备方法 Download PDFInfo
- Publication number
- CN108339396A CN108339396A CN201810280628.XA CN201810280628A CN108339396A CN 108339396 A CN108339396 A CN 108339396A CN 201810280628 A CN201810280628 A CN 201810280628A CN 108339396 A CN108339396 A CN 108339396A
- Authority
- CN
- China
- Prior art keywords
- parts
- weight
- raw materials
- composition
- following raw
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
本发明公开了一种空气净化器的净化组合物及其制备方法，涉及空气净化技术领域，包括以下份计的原料：颗粒组合物35~50份、硅溶胶35~50份、抗菌剂15~25份。本发明能够辅助净化器快速沉淀空气中飞扬的粉尘，并且有效时间长，对甲醛、甲苯、二甲苯及二氧化硫、二氧化氮、一氧化碳等具有很好的选择吸附和光催化降解功能，适用范围更广。
Description
技术领域
本发明涉及空气净化技术领域，具体涉及一种空气净化器的净化组合物及其制备方法。
背景技术
室内空气净化器是实现空气净化的最直接、便捷的仪器，随着室内空气污染性质的不断变化与污染程度的加大，室内空气净化器技术也得到了快速地发展。目前空气净化器产品有：机械过滤式净化器、机械过滤吸附式净化器、静电式净化器、负离子净化器、紫外光空气净化器等。其中机械过滤式净化器和机械过滤吸附式净化器中均需要用到净化剂，由于停留在空气中的有毒有害物质，诸如甲醛、苯、氨、硫化物、碳化物等等，其分子大小和水分子接近，因而它能停留在空气中而不沉降，而要捕捉这些有毒有害物，必须是与之相应大小的孔径。
目前，市场上出现一些用来对空气进行净化的空气净化剂，或者吸附剂，例如活性炭以及一些以植物提取物为基础的甲醛清除剂等。但对于这些空气净化剂而言，其仅适合吸附空气中的部分有害物质，耐用性差，吸附效果也有待于进一步提高。。
发明内容
本发明的目的是提供一种空气净化器的净化组合物及其制备方法，能够辅助净化器快速沉淀空气中飞扬的粉尘，并且有效时间长，对甲醛、甲苯、二甲苯及二氧化硫、二氧化氮、一氧化碳等具有很好的选择吸附和光催化降解功能，适用范围更广。
本发明提供了如下的技术方案：一种空气净化器的净化组合物，包括以下份计的原料：颗粒组合物35~50份、硅溶胶35~50份、抗菌剂15~25份；
所述颗粒组合物包括以下份计的原料：改性沸石15~25份、混合纤维15~25份、膨胀珍珠岩5~10份、粘结剂5~10份、纳米二氧化钛3~6份、鼠尾草精油3~6份、粒状吸水型树脂3~6份、甲基硅油3~6份、氧化铈1~4份、酒石酸1~4份、聚氨酯1~4份、月桂酸单甘油酯1~4份、碳酸氢钠0.8~1.2份和乙二胺四乙酸0.8~1.2份。
其中，包括以下份计的原料：颗粒组合物38~45份、硅溶胶38~45份、抗菌剂18~22份；
所述颗粒组合物包括以下份计的原料：改性沸石18~22份、混合纤维18~22份、膨胀珍珠岩6~8份、粘结剂6~8份、纳米二氧化钛4~5份、粒状吸水型树脂4~5份、甲基硅油4~5份、氧化铈2~3份、酒石酸2~3份、聚氨酯2~3份、月桂酸单甘油酯2~3份、碳酸氢钠0.9~1.1份和乙二胺四乙酸0.9~1.1份。
其中，所述抗菌剂包括以下份计的原料：柠檬烯5~8份、羧甲基壳聚糖5~8份、三乙醇胺油酸皂5~8份、苯甲酸钠1~4份、丙二醇1~4份、硝酸锌1~4份、纳米银溶液0.8~1.2份、乳酸钠0.8~1.2份、硬脂酸0.8~1.2份、丝氨酸0.3~0.6份、松油醇0.3~0.6份和高锰酸钾0.3~0.6份。
其中，所述改性沸石包括以下份计的原料：沸石25~30份、锆酸钡5~8份、生石灰5~8份、二氨基二苯基甲烷3~5份、液体松香树脂3~5份、邻苯二甲酸二异丁酯1~3份、硬脂酸1~3份和1-羟乙基-2-油基咪唑啉1~3份。
其中，所述改性沸石的制备方法为：按照配比将沸石、生石灰、锆酸钡、邻苯二甲酸二异丁酯混合均匀，加入至5~10倍重量份水中，形成悬浊液，然后加入二氨基二苯基甲烷、液体松香树脂、硬脂酸和1-羟乙基-2-油基咪唑啉，分散均匀，在55~65℃条件下烘干，粉碎，过300~400目筛即得。
其中，所述纳米银溶液为无色透明的水溶性银离子溶液，其浓度为1000～20000ppm。
其中，所述鼠尾草精油的制备方法为：
（1）、将鼠尾草粉碎，放入10~15倍重量份的45～55％乙醇溶液回流提取1～3次，每次2～3h，将提取液过滤合并，回收溶剂，再加入40～50℃水中溶解，得到粗提液；
（2）、向粗提液加入稀土氯化物混合，搅匀，得到混合液；
（3）、将混合液放入大孔树脂柱，先水洗至无色，然后用体积浓度为35～45％乙醇 洗脱，回收乙醇，干燥，得到鼠尾草精油。
其中，所述混合纤维包括以下份计的原料：黄麻纤维4~6份、木棉纤维1~3份、石棉纤维1~3份和粘胶纤维0.8~1.2份。
本发明提供一种空气净化器的净化组合物的制备方法，包括如下步骤：
（1）、制备颗粒组合物
按照配比将改性沸石、混合纤维、膨胀珍珠岩、纳米二氧化钛、鼠尾草精油、粒状吸水型树脂、甲基硅油、酒石酸、聚氨酯、月桂酸单甘油酯、氧化铈、碳酸氢钠和乙二胺四乙酸混合，分散均匀，加入粘结剂，继续搅拌分散，在55~65摄氏度条件下低温干燥20~30min，得到所述颗粒组合物；
（2）、将颗粒组合物、硅溶胶和抗菌剂按照配比混合均匀，低温干燥，直至硅溶胶中的液体蒸发，搅拌分散，得到所述空气净化器的净化组合物。
本发明的有益效果：能够辅助净化器快速沉淀空气中飞扬的粉尘，并且有效时间长，对甲醛、甲苯、二甲苯及二氧化硫、二氧化氮、一氧化碳等具有很好的选择吸附和光催化降解功能，适用范围更广，具体如下：
（1）、本发明采用颗粒组合物、硅溶胶和抗菌剂为原料，采用合理的配比和制备方法，得到的空气净化器的净化组合物，对空气中污染物具有较强吸附能力，可以作为滤网材料、也可以作为滤芯材料等用于空气净化器中，能够辅助净化器快速沉淀空气中飞扬的粉尘，并且有效时间长，对甲醛、甲苯、二甲苯及二氧化硫、二氧化氮、一氧化碳等具有很好的选择吸附和光催化降解功能，适用范围更广，还能够有效杀菌、吸附微小粉尘、除异味，提高了室内的空气质量，改善环境；颗粒组合物具有吸附和光催化降解双重作用，能够持久抗菌杀毒、净化空气并释放负氧离子；抗菌剂可以有效抗菌和除去异味，有效杀灭空气中的金色葡萄球菌、大肠杆菌等细菌，净化空气，抗菌抑菌，两者形成复合结构，性能稳定，相互协作，使得颗粒组合物作用时间长，缓释效果好；
（2）、本发明采用改性沸石、混合纤维、膨胀珍珠岩、粘结剂、纳米二氧化钛为主要原料，以鼠尾草精油、粒状吸水型树脂、甲基硅油、酒石酸、聚氨酯、月桂酸单甘油酯、碳酸氢钠份和乙二胺四乙酸为辅助原料，得到的颗粒组合物，通过混合纤维和粘结剂形成改性沸石和膨胀珍珠岩的复合结构，其余原料吸附或者粘结在结构的孔隙中，复合形成具有复杂孔隙的结构，该复合结构具有吸附和光催化净化两种功能，且其耐用性较好，性能稳定；鼠尾草精油除了具有去异味的功能外，还可以润滑混合纤维，使其将其他原料进行有效搭接，增强体系强度和促进结构生成；另外，该颗粒组合物，不易达到饱和状态，吸附性能好，效率高。
具体实施方式
下面结合具体实施例，进一步阐述本发明。这些实施例仅用于说明本发明而不用于限制本发明的范围。
实施例1
一种空气净化器的净化组合物，包括以下份计的原料：颗粒组合物35份、硅溶胶35份、抗菌剂15份；
所述颗粒组合物包括以下份计的原料：改性沸石15份、混合纤维15份、膨胀珍珠岩5份、粘结剂5份、纳米二氧化钛3份、鼠尾草精油3份、粒状吸水型树脂3份、甲基硅油3份、氧化铈1份、酒石酸1份、聚氨酯1份、月桂酸单甘油酯1份、碳酸氢钠0.8份和乙二胺四乙酸0.8份。
其中，
所述抗菌剂包括以下份计的原料：柠檬烯5份、羧甲基壳聚糖5份、三乙醇胺油酸皂5份、苯甲酸钠1份、丙二醇1份、硝酸锌1份、纳米银溶液0.8份、乳酸钠0.8份、硬脂酸0.8份、丝氨酸0.3份、松油醇0.3份和高锰酸钾0.3份。
其中，
所述改性沸石包括以下份计的原料：沸石25份、锆酸钡5份、生石灰5份、二氨基二苯基甲烷3份、液体松香树脂3份、邻苯二甲酸二异丁酯1份、硬脂酸1份和1-羟乙基-2-油基咪唑啉1份。
所述改性沸石的制备方法为：按照配比将沸石、生石灰、锆酸钡、邻苯二甲酸二异丁酯混合均匀，加入至5倍重量份水中，形成悬浊液，然后加入二氨基二苯基甲烷、液体松香树脂、硬脂酸和1-羟乙基-2-油基咪唑啉，分散均匀，在55℃条件下烘干，粉碎，过300目筛即得。
其中，
所述纳米银溶液为无色透明的水溶性银离子溶液，其浓度为1000ppm。
其中，
所述鼠尾草精油的制备方法为：
（1）、将鼠尾草粉碎，放入10倍重量份的45％乙醇溶液回流提取1次，每次2h，将提取液过滤合并，回收溶剂，再加入40℃水中溶解，得到粗提液；
（2）、向粗提液加入稀土氯化物混合，搅匀，得到混合液；
（3）、将混合液放入大孔树脂柱，先水洗至无色，然后用体积浓度为35％乙醇 洗脱，回收乙醇，干燥，得到鼠尾草精油。
其中，
所述混合纤维包括以下份计的原料：黄麻纤维4份、木棉纤维1份、石棉纤维1份和粘胶纤维0.8份。
本实施例中提供一种空气净化器的净化组合物的制备方法，包括如下步骤：
（1）、制备颗粒组合物
按照配比将改性沸石、混合纤维、膨胀珍珠岩、纳米二氧化钛、鼠尾草精油、粒状吸水型树脂、甲基硅油、酒石酸、聚氨酯、月桂酸单甘油酯、氧化铈、碳酸氢钠和乙二胺四乙酸混合，分散均匀，加入粘结剂，继续搅拌分散，在55摄氏度条件下低温干燥20min，得到所述颗粒组合物；
（2）、将颗粒组合物、硅溶胶和抗菌剂按照配比混合均匀，低温干燥，直至硅溶胶中的液体蒸发，搅拌分散，得到所述空气净化器的净化组合物。
实施例2
一种空气净化器的净化组合物，包括以下份计的原料：颗粒组合物50份、硅溶胶50份、抗菌剂25份；
所述颗粒组合物包括以下份计的原料：改性沸石25份、混合纤维25份、膨胀珍珠岩10份、粘结剂10份、纳米二氧化钛6份、鼠尾草精油6份、粒状吸水型树脂6份、甲基硅油6份、氧化铈4份、酒石酸4份、聚氨酯4份、月桂酸单甘油酯4份、碳酸氢钠1.2份和乙二胺四乙酸1.2份。
其中，
所述抗菌剂包括以下份计的原料：柠檬烯8份、羧甲基壳聚糖8份、三乙醇胺油酸皂8份、苯甲酸钠4份、丙二醇4份、硝酸锌4份、纳米银溶液1.2份、乳酸钠1.2份、硬脂酸1.2份、丝氨酸0.6份、松油醇0.6份和高锰酸钾0.6份。
其中，
所述改性沸石包括以下份计的原料：沸石30份、锆酸钡8份、生石灰8份、二氨基二苯基甲烷5份、液体松香树脂5份、邻苯二甲酸二异丁酯3份、硬脂酸3份和1-羟乙基-2-油基咪唑啉3份。
所述改性沸石的制备方法为：按照配比将沸石、生石灰、锆酸钡、邻苯二甲酸二异丁酯混合均匀，加入至10倍重量份水中，形成悬浊液，然后加入二氨基二苯基甲烷、液体松香树脂、硬脂酸和1-羟乙基-2-油基咪唑啉，分散均匀，在65℃条件下烘干，粉碎，过400目筛即得。
其中，
所述纳米银溶液为无色透明的水溶性银离子溶液，其浓度为20000ppm。
其中，
所述鼠尾草精油的制备方法为：
（1）、将鼠尾草粉碎，放入15倍重量份的55％乙醇溶液回流提取3次，每次3h，将提取液过滤合并，回收溶剂，再加入50℃水中溶解，得到粗提液；
（2）、向粗提液加入稀土氯化物混合，搅匀，得到混合液；
（3）、将混合液放入大孔树脂柱，先水洗至无色，然后用体积浓度为45％乙醇 洗脱，回收乙醇，干燥，得到鼠尾草精油。
其中，
所述混合纤维包括以下份计的原料：黄麻纤维6份、木棉纤维3份、石棉纤维3份和粘胶纤维1.2份。
本实施例中提供一种空气净化器的净化组合物的制备方法，包括如下步骤：
（1）、制备颗粒组合物
按照配比将改性沸石、混合纤维、膨胀珍珠岩、纳米二氧化钛、鼠尾草精油、粒状吸水型树脂、甲基硅油、氧化铈、酒石酸、聚氨酯、月桂酸单甘油酯、碳酸氢钠和乙二胺四乙酸混合，分散均匀，加入粘结剂，继续搅拌分散，在65摄氏度条件下低温干燥30min，得到所述颗粒组合物；
（2）、将颗粒组合物、硅溶胶和抗菌剂按照配比混合均匀，低温干燥，直至硅溶胶中的液体蒸发，搅拌分散，得到所述空气净化器的净化组合物。
实施例3
一种空气净化器的净化组合物，包括以下份计的原料：颗粒组合物40份、硅溶胶40份、抗菌剂20份；
所述颗粒组合物包括以下份计的原料：改性沸石20份、混合纤维20份、膨胀珍珠岩7.5份、粘结剂7.5份、纳米二氧化钛4.5份、粒状吸水型树脂4.5份、甲基硅油4.5份、氧化铈2.5份、酒石酸2.5份、聚氨酯2.5份、月桂酸单甘油酯2.5份、碳酸氢钠1份和乙二胺四乙酸1份。
其中，
所述抗菌剂包括以下份计的原料：柠檬烯6.5份、羧甲基壳聚糖6.5份、三乙醇胺油酸皂6.5份、苯甲酸钠2.5份、丙二醇2.5份、硝酸锌2.5份、纳米银溶液1份、乳酸钠1份、硬脂酸1份、丝氨酸0.45份、松油醇0.45份和高锰酸钾0.45份。
其中，
所述改性沸石包括以下份计的原料：沸石27.5份、锆酸钡6.5份、生石灰6.5份、二氨基二苯基甲烷4份、液体松香树脂4份、邻苯二甲酸二异丁酯2份、硬脂酸2份和1-羟乙基-2-油基咪唑啉2份。
所述改性沸石的制备方法为：按照配比将沸石、生石灰、锆酸钡、邻苯二甲酸二异丁酯混合均匀，加入至8倍重量份水中，形成悬浊液，然后加入二氨基二苯基甲烷、液体松香树脂、硬脂酸和1-羟乙基-2-油基咪唑啉，分散均匀，在60℃条件下烘干，粉碎，过350目筛即得。
其中，
所述纳米银溶液为无色透明的水溶性银离子溶液，其浓度为1000ppm。
其中，
所述鼠尾草精油的制备方法为：
（1）、将鼠尾草粉碎，放入13倍重量份的50％乙醇溶液回流提取2次，每次2.5h，将提取液过滤合并，回收溶剂，再加入45℃水中溶解，得到粗提液；
（2）、向粗提液加入稀土氯化物混合，搅匀，得到混合液；
（3）、将混合液放入大孔树脂柱，先水洗至无色，然后用体积浓度为40％乙醇 洗脱，回收乙醇，干燥，得到鼠尾草精油。
其中，
所述混合纤维包括以下份计的原料：黄麻纤维5份、木棉纤维2份、石棉纤维2份和粘胶纤维1份。
本实施例中提供一种空气净化器的净化组合物的制备方法，包括如下步骤：
（1）、制备颗粒组合物
按照配比将改性沸石、混合纤维、膨胀珍珠岩、纳米二氧化钛、鼠尾草精油、粒状吸水型树脂、甲基硅油、氧化铈、酒石酸、聚氨酯、月桂酸单甘油酯、碳酸氢钠和乙二胺四乙酸混合，分散均匀，加入粘结剂，继续搅拌分散，在60摄氏度条件下低温干燥25min，得到所述颗粒组合物；
（2）、将颗粒组合物、硅溶胶和抗菌剂按照配比混合均匀，低温干燥，直至硅溶胶中的液体蒸发，搅拌分散，得到所述空气净化器的净化组合物。
参照前述实施例对本发明进行了详细的说明，对于本领域的技术人员来说，其依然可以对前述各实施例所记载的技术方案进行修改，或者对其中部分技术特征进行等同替换。凡在本发明的精神和原则之内，所作的任何修改、等同替换、改进等，均应包含在本发明的保护范围之内。
Claims (10)
1.一种空气净化器的净化组合物，其特征在于，包括以下份计的原料：颗粒组合物35~50份、硅溶胶35~50份、抗菌剂15~25份；
所述颗粒组合物包括以下份计的原料：改性沸石15~25份、混合纤维15~25份、膨胀珍珠岩5~10份、粘结剂5~10份、纳米二氧化钛3~6份、鼠尾草精油3~6份、粒状吸水型树脂3~6份、甲基硅油3~6份、氧化铈1~4份、酒石酸1~4份、聚氨酯1~4份、月桂酸单甘油酯1~4份、碳酸氢钠0.8~1.2份和乙二胺四乙酸0.8~1.2份。
2.根据权利要求1所述的空气净化器的净化组合物，其特征在于，包括以下份计的原料：颗粒组合物38~45份、硅溶胶38~45份、抗菌剂18~22份；
所述颗粒组合物包括以下份计的原料：改性沸石18~22份、混合纤维18~22份、膨胀珍珠岩6~8份、粘结剂6~8份、纳米二氧化钛4~5份、粒状吸水型树脂4~5份、甲基硅油4~5份、氧化铈2~3份、酒石酸2~3份、聚氨酯2~3份、月桂酸单甘油酯2~3份、碳酸氢钠0.9~1.1份和乙二胺四乙酸0.9~1.1份。
3.根据权利要求1所述的空气净化器的净化组合物，其特征在于，包括以下份计的原料：颗粒组合物40份、硅溶胶40份、抗菌剂20份；
所述颗粒组合物包括以下份计的原料：改性沸石20份、混合纤维20份、膨胀珍珠岩7.5份、粘结剂7.5份、纳米二氧化钛4.5份、粒状吸水型树脂4.5份、甲基硅油4.5份、氧化铈2.5份、酒石酸2.5份、聚氨酯2.5份、月桂酸单甘油酯2.5份、碳酸氢钠1份和乙二胺四乙酸1份。
4.根据权利要求1所述的空气净化器的净化组合物，其特征在于，所述抗菌剂包括以下份计的原料：柠檬烯5~8份、羧甲基壳聚糖5~8份、三乙醇胺油酸皂5~8份、苯甲酸钠1~4份、丙二醇1~4份、硝酸锌1~4份、纳米银溶液0.8~1.2份、乳酸钠0.8~1.2份、硬脂酸0.8~1.2份、丝氨酸0.3~0.6份、松油醇0.3~0.6份和高锰酸钾0.3~0.6份。
5.根据权利要求1所述的空气净化器的净化组合物，其特征在于，所述改性沸石包括以下份计的原料：沸石25~30份、锆酸钡5~8份、生石灰5~8份、二氨基二苯基甲烷3~5份、液体松香树脂3~5份、邻苯二甲酸二异丁酯1~3份、硬脂酸1~3份和1-羟乙基-2-油基咪唑啉1~3份。
6.根据权利要求5所述的空气净化器的净化组合物，其特征在于，所述改性沸石的制备方法为：按照配比将沸石、生石灰、锆酸钡、邻苯二甲酸二异丁酯混合均匀，加入至5~10倍重量份水中，形成悬浊液，然后加入二氨基二苯基甲烷、液体松香树脂、硬脂酸和1-羟乙基-2-油基咪唑啉，分散均匀，在55~65℃条件下烘干，粉碎，过300~400目筛即得。
7.根据权利要求1所述的空气净化器的净化组合物，其特征在于，所述纳米银溶液为无色透明的水溶性银离子溶液，其浓度为1000～20000ppm。
8.根据权利要求1所述的空气净化器的净化组合物，其特征在于，所述鼠尾草精油的制备方法为：
（1）、将鼠尾草粉碎，放入10~15倍重量份的45～55％乙醇溶液回流提取1～3次，每次2～3h，将提取液过滤合并，回收溶剂，再加入40～50℃水中溶解，得到粗提液；
（2）、向粗提液加入稀土氯化物混合，搅匀，得到混合液；
（3）、将混合液放入大孔树脂柱，先水洗至无色，然后用体积浓度为35～45％乙醇 洗脱，回收乙醇，干燥，得到鼠尾草精油。
9.根据权利要求1所述的可以净化空气的环保颗粒组合物，其特征在于，所述混合纤维包括以下份计的原料：黄麻纤维4~6份、木棉纤维1~3份、石棉纤维1~3份和粘胶纤维0.8~1.2份。
10.一种根据权利要求1~9任一项所述的空气净化器的净化组合物的制备方法，其特征在于，包括如下步骤：
（1）、制备颗粒组合物
按照配比将改性沸石、混合纤维、膨胀珍珠岩、纳米二氧化钛、鼠尾草精油、粒状吸水型树脂、甲基硅油、氧化铈、酒石酸、聚氨酯、月桂酸单甘油酯、碳酸氢钠和乙二胺四乙酸混合，分散均匀，加入粘结剂，继续搅拌分散，在55~65摄氏度条件下低温干燥20~30min，得到所述颗粒组合物；
（2）、将颗粒组合物、硅溶胶和抗菌剂按照配比混合均匀，低温干燥，直至硅溶胶中的液体蒸发，搅拌分散，得到所述空气净化器的净化组合物。