CN108338212A - 一种保鲜层合物及其制备方法与应用 - Google Patents
一种保鲜层合物及其制备方法与应用 Download PDFInfo
- Publication number
- CN108338212A CN108338212A CN201810112408.6A CN201810112408A CN108338212A CN 108338212 A CN108338212 A CN 108338212A CN 201810112408 A CN201810112408 A CN 201810112408A CN 108338212 A CN108338212 A CN 108338212A
- Authority
- CN
- China
- Prior art keywords
- layer
- paper
- base material
- keeping
- fresh
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明提供一种保鲜层合物及其制备方法与应用,该层合物至少包括第一基材层、纤维层及第二基材层,纤维层由多根在热和/或压力的作用下能粘接的纤维形成,纤维层位于第一基材层与第二基材层之间,该纤维层中的部分纤维直接附接在第一基材层上或第二基材层上,部分纤维直接粘接在第二基材层或第一基材层上,在附接面和/或粘接面上均留有供气体进出纤维层的透气路;在纤维层的多根的纤维的缝隙中均匀的含有能释放环丙烯类气体的药剂或能释放环丙烷类气体的药剂,第一基材层和第二基材层中的材质至少有一层是透气的材料。本发明在不使用有机溶剂或其他助剂的情形下能层合上药剂,达到了均匀释放气体的目的,解决了本领域长期想解决而没有解决的技术问题。
Description
技术领域
本发明涉及一种保鲜层合物及其制备方法与应用,属于果蔬保鲜领域。
背景技术
近年来,我国的果蔬产业(包括花卉产业)取得了巨大成就,果蔬产量巨大,但在储运过程中由于成熟衰老、腐烂等造成的损失也惊人,目前,果蔬采收后合理有效的贮藏保鲜技术已受到业界的普遍关注。
发明人知晓公开了一种环丙烯化合物的供给***,该***为包括至少一基材、含有至少一种环丙烯化合物的材料和释放剂的环丙烯化合物产生器,其中一个基材的至少一面用含有至少一种环丙烯化合物的材料涂布和其中当含有至少一种环丙烯化合物的材料接触释放剂时,释放出气体环丙烯化合物。该案是将1-MCP/α-环糊精配合物事先采用溶剂(例如聚乙烯基吡咯烷酮)配制成溶液,然后以涂布在基材上,使用时,使该基材与释放剂接触,以释放气体环丙烯化合物。该案提供的环丙烯化合物产生器中含有大量的化学试剂,在应用于果蔬保鲜时存在不安全因素;在制备过程中,所使用的溶剂会污染环境,此外,由于使用时,需要与释放剂接触,因此该产品不方便使用。
此外,发明人作为果蔬保鲜领域的从业者知晓本领域还没有能均匀释放1-MCP的技术,现有产品的1-MCP的含量非常不均匀,单位面积1-MCP含量差异非常大,无法保证实际使用的效果,如果1-MCP含量大,果蔬内部内源乙烯被过度抑制,致使储藏期出现无法后熟影响果蔬品质,如果1-MCP含量少,果蔬内部内源乙烯不能够有效的抑制,致使果蔬在储藏期出现软化后腐烂造成损失。想解决1-MCP均匀释放的技术问题一直是本领域长期想要解决的技术问题,因而,如果能解决该技术问题,那么势必能给果蔬保鲜领域带来显著的进步。
发明内容
有鉴于果蔬保鲜领域长期现实需要,本发明的目的之一在于提供一种保鲜层合物,该层合物采用特殊的结构,不仅能在不使用有机溶剂或其他助剂的情形下,能层合上能释放环丙烯类或环丙烷类气体的药剂,还能使这些药剂能均匀的含在保鲜层合物中,从而达到了均匀释放气体的目的,解决了本领域长期想解决而没有解决的技术问题。
本发明的另一目的在于提供上述保鲜层合物的制备方法。
本发明的再一目的在于提供上述保鲜层合物的应用。
为实现上述目的,本发明提供一种保鲜层合物,其中,其至少包括第一基材层、纤维层及第二基材层,所述纤维层由多根在热和/或压力的作用下能粘接的纤维形成,所述纤维层位于第一基材层与第二基材层之间,并且该纤维层中的部分纤维直接附接在第一基材层上或第二基材层上,部分纤维直接粘接在所述第二基材层或第一基材层上,并且在附接面和/或粘接面上留有供气体进出纤维层的透气路;在所述纤维层的多根的纤维的缝隙中均匀的含有能释放环丙烯类气体的药剂或能释放环丙烷类气体的药剂,且所述第一基材层和第二基材层中的材质至少有一层是透气的材料。
优选地,所述保鲜层合物不含有机溶剂。
本发明特别的结构在不使用有机溶剂或其他助剂的情形下能层合上能释放环丙烯类或环丙烷类气体的药剂,还能使这些药剂能均匀的含在保鲜层合物中,从而达到了均匀释放气体的目的,解决了本领域长期想解决而没有解决的技术问题。当将本发明保鲜层合物置于需要被保鲜的果蔬的环境中时,环境中的湿气或果蔬释放出来的湿气通过第一基材层或第二基材层以及粘结面和/或附接面上供气体进出的透气路到达纤维层,然后与纤维缝隙中的药剂相互作用,产生环丙烯类或环丙烷类气体,这些气体再通过粘结面和/或附接面上供气体进气的通路释放到环境中,从而起到保鲜作用。
在一些实施方式中,所述在热和/或压力的作用下能粘接的纤维包括聚丙烯纤维、聚烯烃纤维、聚乙烯纤维、聚氯乙烯纤维、聚丙烯睛纤维、改性聚丙烯睛纤维、聚乙烯醇系纤维、芳族聚胺纤维、合成纤维、醋酸纤维、胶黏纤维、高湿模量粘胶纤维、聚偏氯乙烯纤维、二烯类弹性纤维和聚氨酯弹性纤维中的一种或多种。特别是聚烯烃纤维类纤维,其粘结性能良好,工艺性能好。这些纤维材料是本领域现有材料。
在一些实施方式中,所述能释放环丙烯类气体的药剂包括能释放环丙烯气体的药剂,或能释放1-甲基-环丙烯气体的药剂;
所述能释放环丙烷类气体的药剂包括能释放二甲基环丙烷的药剂,或能释放亚甲基环丙烷的药剂。
在一些实施方式中,所述能释放环丙烯类气体的药剂为包裹有1-甲基-环丙烯/α-环糊精配合物的粉末。
本发明所用药剂为本领域现有药剂。特别地,1-甲基环丙烯(1-methylcyclopropene,1-MCP)是一种新型的化学保鲜剂。研究表明,果蔬在储运过程中,自身所产生的乙烯或来自外界的乙烯会与果蔬中的乙烯受体结合,从而启动一系列与成熟有关的生理生化反应,加快衰老和死亡。而1-MCP能通过抑制乙烯的产生、阻止乙烯作用的生理过程延缓果蔬的腐败和衰老,从而达到延长果蔬贮藏保鲜期的目的。此外,1-MCP应用后检测不到残留,存在着无毒、高效及低量等优点,其在果蔬贮藏保鲜中具有广泛应用前景。1-MCP因其高化学活性,一般不稳定。为方便1-MCP的应用,现有技术已提供以载体将1-MCP封装的粉末材料,例如包裹有1-MCP/α-环糊精配合物的粉末。
本发明药剂的用量可根据实际需要调节,在一些实施方式中,每平方米的保鲜层合物均匀的含有10mg~2000mg(例如1mg~150mg,20mg~2000mg)所述的包裹有1-甲基-环丙烯/α-环糊精配合物的粉末。特别地,在10mg~2000mg用量范围内,可以有效的抑制果蔬内源乙烯的产生,但又不过分抑制内源乙烯的产生,可以有效控制需要的贮藏时间,可以用于不同水果容量的包装内并达到满意的保鲜效果。
在一些实施方式中,所述第一基材层、第二基材层各自独立地包括透气纸、吸水纸、无酸纸、吸湿纸、胶粘纸、蛋白胶纸、全棉纤维纸、全木浆纸、草浆纸、面包纸、竹浆纸、吸水性纸、塑纸、多孔聚乙烯薄膜、多孔聚酯薄膜、多孔聚丙烯薄膜、多孔聚氯乙烯薄膜、聚苯乙烯薄膜、聚偏二氯乙烯薄膜、乙烯-醋酸乙烯共聚物薄膜、聚碳酸酯薄膜、醋酸纤维素薄膜、无纺聚乙烯或无纺聚丙烯。
在一些实施方式中,所述第一基材层的厚度为1~5000μm(0.001~5mm)。例如0.001~0.5mm。
在一些实施方式中,所述第二基材层的厚度为2~3000μm(0.002~3mm)。例如0.002~1mm。
在一些实施方式中,所述纤维层的厚度为0.5~3000μm(0.0005~3mm)。例如0.0005~0.3mm。
在一些实施方式中,在所述第一基材层或第二基材层上还可层合有能释放SO2和/或ClO2的保鲜剂,在该保鲜剂上还层合有第三基材层。
本发明能释放SO2和/或ClO2的保鲜剂为现有保鲜剂,优选为微胶囊保鲜剂。微胶囊保鲜剂是微胶囊包裹的保鲜剂,其采用部分阻隔水汽通过的材料,将保鲜药剂包裹起来,使其释放变缓,延长释放时间,其为现有技术,被微胶囊包裹的保鲜剂例如为硫酸盐、氯酸盐和缓释剂中的一种或多种,硫酸盐包括但不限于亚硫酸氢钠、亚硫酸钾、焦亚硫酸盐、亚硫酸钠、亚硫酸氢钾中的一种或多种,氯酸盐包括但不限于次氯酸钾、氯酸钠、次氯酸钠、氯酸钾中的一种或多种;缓释剂包括但不限于碳酸钠、柠檬酸、碳酸氢钠、碳酸钾、酒石酸、碳酸氢钾中的一种或多种,保鲜剂例如可组合为焦亚硫酸钠+氯酸钠+柠檬酸。
优选地,所述第三基材层的材质为不透气材料;如为不透气聚氯乙烯薄膜、不透气聚丙烯薄膜或不透气塑纸,当所述第三基材层的材质为不透气材料时,所述第一基材层和第二基材层中处于外侧的基材的材质是透气材料。这样能保障湿气以及产生的气体能顺利进出。
另一方面,本发明提供上述保鲜层合物的制备方法,所述方法包括如下步骤:
准备所述第一基材层或所述第二基材层;
使所述第一基材层或所述第二基材层附接所述在热和/或压力的作用下能粘接的纤维以形成所述纤维层;或准备所述纤维层直接附接在第一基材层或第二基材层上的基材;
在附接在第一基材层或第二基材层上的纤维层上均匀投放所述能释放环丙烯类气体的药剂或能释放环丙烷类气体的药剂;然后将所述第二基材层或第一基材层覆盖在该纤维层上,然后在热和/或压力的作用下粘合,得所述保鲜层合物。
本发明在纤维与基材粘接或附接时,只要附接面或粘接面上非每一个点都被粘接或附接上纤维就可在粘接面或附接面上留有供气体进出纤维层的透气路,这些透气路位于被粘接或附接的纤维之间。
在一些实施方式中,所述纤维层附接在第一基材层或第二基材层上的基材为聚丙烯纤维、聚烯烃纤维、聚乙烯纤维、聚氯乙烯纤维、聚酯纤维、聚丙烯睛纤维、改性聚丙烯睛纤维、聚乙烯醇系纤维、芳族聚胺纤维、合成纤维、醋酯纤维、胶黏纤维、高湿模量粘胶纤维、聚偏氯乙烯纤维、二烯类弹性纤维、聚氨酯弹性纤维、无机纤维或碳纤维中的一种或多种附接在透气纸、吸水纸、无酸纸、吸湿纸、胶粘纸、蛋白胶纸、全棉纤维纸、全木浆纸、草浆纸、面包纸、竹浆纸、吸水性纸、塑纸、多孔聚乙烯薄膜、多孔聚酯薄膜、多孔聚丙烯薄膜、多孔聚氯乙烯薄膜、聚苯乙烯薄膜、聚偏二氯乙烯薄膜、乙烯-醋酸乙烯共聚物薄膜、聚碳酸酯薄膜、醋酸纤维素薄膜、无纺聚乙烯或无纺聚丙烯上的基材。
再一方面,本发明提供上述保鲜层合物在果蔬保鲜中的应用。
在一些实施方式中,可将上述保鲜层合物应用于对包括葡萄、樱桃、香蕉、西梅、桃子、李子、西兰花、西红柿、芦笋、西葫芦中的一种或多种保鲜。
具体使用时,可根据实际需被保鲜果蔬的重量裁切一定面积的保鲜层合物,作为果蔬包装盒的内衬,直接放置在包装盒内,保鲜层合物的非印刷面朝向包装盒内的果蔬,密封包装盒,保持果蔬在一个密闭的环境中贮藏,包装盒外界环境贮藏条件可根据实际果蔬选择。实验表明本发明保鲜层合物对果蔬具有优异的保鲜作用。
综上可知,本发明提供了一种保鲜层合物及其制备方法与应用,该保鲜层合物中不含任何有机溶剂,其能均匀的释放,在实际应用过程中对果蔬具有优异的保鲜作用。
附图说明
图1为本发明具体实施例制备的保鲜层合物1~保鲜层合物4的结构示意图;
图2为本发明图1纤维层的放大图;图1及图2中的标号具有如下意义:
1:第一基材层;2:第二基材层;3:纤维层;31:纤维;32:药剂。
具体实施方式
为了对本发明的技术特征、目的和有益效果有更加清楚的理解,现结合具体实施例及对本发明的技术方案进行以下详细说明,应理解这些实例仅用于说明本发明而不用于限制本发明的范围。实施例中,各原始试剂材料均可商购获得,未注明具体条件的实验方法为所属领域熟知的常规方法和常规条件,或按照仪器制造商所建议的条件。
本发明的一些实施方案通过以下实施例来说明:
制备实施例
保鲜层合物1
本实施例提供保鲜层合物1及其制备方法,所述方法包括:
准备所述纤维层直接附接在第一基材层的基材;
其中,所述第一基材层的材质为全棉纤维纸,其厚度为0.10mm;
所述纤维层的材质为聚乙烯纤维,其厚度为0.05mm;
该第一基材层是透气的材料。
在60m2附接在第一基材层上的纤维层上均匀投放101.28g包裹有1-MCP/α-环糊精配合物的粉末;然后将60m2所述第二基材层覆盖在该纤维层上,然后在热的作用下粘合,得所述保鲜层合物1,所述第二基材层的材质为无纺聚乙烯,其厚度为0.10mm。
本实施例所得保鲜层合物的结构示意图如图1所示,图1纤维层的放大图如图2所示,其包括第一基材层1、纤维层3及第二基材层2,所述纤维层3由多根在热的作用下能粘接的纤维31形成,所述纤维层3位于第一基材层1与第二基材层2之间,并且该纤维层3中的部分纤维31直接附接在第一基材层1上,部分纤维直接粘接在所述第二基材层2上,并且在附接面上均留有供气体进出纤维层的透气路;在所述纤维层3的多根的纤维31的缝隙中均匀的含有能释放1-MCP包裹有1-MCP/α-环糊精配合物的粉末,且所述第一基材层1是透气的材料。
保鲜层合物2
本实施例提供保鲜层合物2及其制备方法,所述方法包括:
准备所述纤维层直接附接在第一基材层的基材;
其中,所述第一基材层的材质为全木浆纸,其厚度为0.20mm;
所述纤维层的材质为聚丙烯纤维,其厚度为0.05mm;
该第一基材层是透气的材料。
在34m2附接在第一基材层上的纤维层上均匀投放57.39g包裹有1-MCP/α-环糊精配合物的粉末;然后将34m2所述第二基材层覆盖在该纤维层上,然后在热的作用下粘合,得所述保鲜层合物2,所述第二基材层的材质为多孔聚乙烯薄膜层,其厚度为0.03mm。其结构示意图如图1所示。
保鲜层合物3
本实施例提供保鲜层合物3及其制备方法,所述方法包括:
准备所述纤维层直接附接在第一基材层的基材;
其中,所述第一基材层的材质为面包纸,其厚度为0.25mm;
所述纤维层的材质为聚乙烯纤维,其厚度为0.05mm;
该第一基材层是透气的材料。
在68m2附接在第一基材层上的纤维层上均匀投放114.78gg包裹有1-MCP/α-环糊精配合物的粉末;然后将68m2所述第二基材层覆盖在该纤维层上,然后在热的作用下粘合,得所述保鲜层合物3,所述第二基材层的材质为多孔聚乙烯薄膜层,其厚度为0.01mm。其结构示意图如图1所示。
保鲜层合物4
本实施例提供保鲜层合物4及其制备方法,所述方法包括:
准备所述纤维层直接附接在第一基材层的基材;
其中,所述第一基材层的材质为乙烯-醋酸乙烯共聚物薄膜,其厚度为0.02mm;
所述纤维层的材质为聚丙烯纤维,其厚度为0.05mm;
该第一基材层与第二基材层都是透气的材料。
在34m2附接在第一基材层上的纤维层上均匀投放57.392gg包裹有1-MCP/α-环糊精配合物的粉末;然后将34m2所述第二基材层覆盖在该纤维层上,然后在热的作用下粘合,得所述保鲜层合物4,所述第二基材层的材质为无纺聚乙烯,其厚度为0.1mm。其结构示意图如图1所示。
应用实施例
在5Kg红提葡萄保鲜上,使用截取3张长36.5cm,宽25cm长方形保鲜层合物1。作为葡萄包装盒的内衬,保鲜层合物的非印刷面朝向包装盒内的葡萄,密封包装盒,保持葡萄在一个密闭的环境中贮藏(包装盒外界环境贮藏条件:0℃、相对湿度在90%)。葡萄释放的水气透过上下两层基材进入药剂层,释放出1-MCP气体。通过贮藏实验可知,此实验中本实施例的保鲜层合物中1-MCP的释放期在12-48小时,在储藏30天葡萄果柄翠绿,无掉粒现象,无腐烂葡萄粒。
按1Kg樱桃裁取0.03m2面积的上述制备得到的保鲜层合物1,作为樱桃包装盒的内衬,保鲜层合物的非印刷面朝向包装盒内的樱桃,密封包装盒,保持樱桃在一个密闭的环境中贮藏(包装盒外界环境贮藏条件:2℃、相对湿度在80%)。经过试验可知,此试验中本实施例的保鲜层合物中1-MCP的释放期在12-48小时,在贮藏20天后樱桃果实润泽,保持较好硬度,无腐烂现象。
在1Kg西梅保鲜上,裁取0.05m2的保鲜层合物2,作为西梅包装盒的内衬,保鲜层合物的非印刷面朝向包装盒内的西梅,密封包装盒,保持西梅在一个密闭的环境中贮藏(包装盒外界环境贮藏条件:2℃、相对湿度在80%)。西梅经过包装后产生的呼吸热水气透过上下两层基材进入药剂层,释放出1-MCP气体。经过试验可知,此试验中本实施例的保鲜层合物中1-MCP的释放期在12-48小时,在贮藏30天后西梅果实色泽鲜美,可溶性固形物含量不变,较好的保持了果实硬度,未见霉变腐烂等现象。
在7Kg樱桃保鲜上,截取长36.5cm,宽25cm的长方形保鲜层合物3。作为樱桃包装箱的内衬,保鲜层合物的非印刷面朝向包装箱内的樱桃,密封包装箱,保持樱桃在一个密闭的环境中贮藏(包装箱外界环境贮藏条件:2℃、相对湿度在60%)。经过实验可知,此试验中本实施例的保鲜层合物,可使樱桃储藏周期由5天延长至30天,樱桃果实润泽,保持较好硬度,无腐烂现象。
使用在15Kg香蕉(金蕉、弓蕉)保鲜上,需裁取长46cm,宽28cm长方形保鲜层合物4。作为香蕉(金蕉、弓蕉)包装箱的内衬,保鲜层合物的印刷面朝向包装箱内的香蕉(金蕉、弓蕉),密封包装箱,保持香蕉(金蕉、弓蕉)在一个密闭的环境中贮藏(包装箱外界环境贮藏条件:24℃、相对湿度在78.5%)。香蕉呼吸后产生的水气透过上下两层基材进入药剂层,释放出1-MCP气体。通过贮藏实验可知,此实验中本实施例的保鲜层合物中1-MCP的释放期在4-8天左右,保证香蕉储藏货架期延长5天以上,且后熟过程中果实的色泽转变、软化和淀粉水解均正常,从而保证其食用和商品价值。
效果测试例
保鲜层合物1
取0.1平方米的保鲜层合物1,平均分成10等份,0.01平方米的面积层合物。称取重量每张为:1.25g、1.30g、1.24g、1.25g、1.25g、1.25g、1.30g、1.25g、1.25g、1.25g;
测试方法为:将等份的层合物放入带有胶皮塞的平底烧瓶中,用注射器快速加入1mol/LNaOH溶液约15ml,立即以胶皮塞密封,摇晃烧瓶使样品全部溶解,静置10min后用微量进样器抽取烧瓶顶部气体注入气质联用仪中,由GC-MS分析结果定性确定样品中1-MCP组分的存在。
经过测试1-MCP的气体含量为:
0.055mg、0.055mg、0.050mg、0.051mg、0.050mg、0.053mg、0.055mg、0.052mg、0.050mg、0.050mg、0.050mg。
经过测试1-MCP的气体含量均能够达到0.050mg,经实验可知,经过本发明保鲜层合物均匀度可达到99.9%。
保鲜层合物2
取0.1平方米的保鲜层合物1,平均分成10等份,0.01平方米的面积层合物。称取重量每张为:3.25g、3.33g、3.30g、3.30g、3.29g、3.32g、3.30g、3.33g、3.30g、3.30g;
测试方法为:将等份的层合物放入带有胶皮塞的平底烧瓶中,用注射器快速加入1mol/LNaOH溶液约15ml,立即以胶皮塞密封,摇晃烧瓶使样品全部溶解,静置10min后用微量进样器抽取烧瓶顶部气体注入气质联用仪中,由GC-MS分析结果定性确定样品中1-MCP组分的存在。
经过测试1-MCP的气体含量为:
0.050mg、0.050mg、0.050mg、0.051mg、0.050mg、0.053mg、0.055mg、0.052mg、0.050mg、0.050mg、0.050mg。
经过测试1-MCP的气体含量均能够达到0.050mg,经实验可知,经过本发明保鲜层合物均匀度可达到99.9%。
保鲜层合物3
取0.1平方米的保鲜层合物1,平均分成10等份,0.01平方米的面积层合物。称取重量每张为:1.59g、1.60g、1.57g、1.60g、1.65g、1.52g、1.65g、1.63g、1.62g、1.60g;
测试方法为:将等份的层合物放入带有胶皮塞的平底烧瓶中,用注射器快速加入1mol/LNaOH溶液约15ml,立即以胶皮塞密封,摇晃烧瓶使样品全部溶解,静置10min后用微量进样器抽取烧瓶顶部气体注入气质联用仪中,由GC-MS分析结果定性确定样品中1-MCP组分的存在。
经过测试1-MCP的气体含量为:
0.049mg、0.050mg、0.049mg、0.050mg、0.050mg、0.050mg、0.050mg、0.049mg、0.048mg、0.050mg、0.050mg。
经过测试1-MCP的气体含量均能够达到0.050mg,经实验可知,经过本发明保鲜层合物均匀度可达到99.9%。
保鲜层合物4
取0.1平方米的保鲜层合物1,平均分成10等份,0.01平方米的面积层合物。称取重量每张为:4.00g、4.03g、4.00g、4.02g、4.05g、4.03g、4.00g、4.00g、4.00g、4.05g;
测试方法为:将等份的层合物放入带有胶皮塞的平底烧瓶中,用注射器快速加入1mol/LNaOH溶液约15ml,立即以胶皮塞密封,摇晃烧瓶使样品全部溶解,静置10min后用微量进样器抽取烧瓶顶部气体注入气质联用仪中,由GC-MS分析结果定性确定样品中1-MCP组分的存在。
经过测试1-MCP的气体含量为:
0.052mg、0.052mg、0.054mg、0.055mg、0.051mg、0.055mg、0.057mg、0.052mg、0.051mg、0.055mg、0.055mg。
经过测试1-MCP的气体含量均能够达到0.050mg,经实验可知,经过本发明保鲜层合物均匀度可达到99.9%。
市售保鲜垫
购买市面利统果蔬保鲜垫,其有效1-MCP的含量为3.3%,其面积为0.01平方米,将其平均分成10等份,0.001平方米的面积产品,称取重量每张为:1.47g、1.50g、1.02g、1.00g、2.01g、2.03g、1.50g、0.89g、0.90g、2.02g。
测试方法为:将等份的层合物放入带有胶皮塞的平底烧瓶中,用注射器快速加入1mol/LNaOH溶液约15ml,立即以胶皮塞密封,摇晃烧瓶使样品全部溶解,静置10min后用微量进样器抽取烧瓶顶部气体注入气质联用仪中,有GC-MS分析结果定性确定样品中1-mcp组分的存在。
经过测试1-MCP的气体含量为:
0.0010mg、0.0024mg、0.0000mg、0.0030mg、0.0000mg、0.0000mg、0.0000mg、0.0000mg、0.0000mg、0.0007mg。
经过测试1-MCP的气体含量平均值为0.0007mg,但经过等份的样品数据不一致,差距大。经实验可知,该市面某品牌果蔬保鲜垫,其1-MCP的均匀度较差,甚至可以说无均匀度。
最后说明的是:以上实施例仅用于说明本发明的实施过程和特点,而非限制本发明的技术方案,尽管参照上述实施例对本发明进行了详细说明,本领域的普通技术人员应当理解:依然可以对本发明进行修改或者等同替换,而不脱离本发明的精神和范围的任何修改或局部替换,均应涵盖在本发明的保护范围当中。
Claims (10)
1.一种保鲜层合物,其中,其至少包括第一基材层(1)、纤维层(3)及第二基材层(2),所述纤维层(3)由多根在热和/或压力的作用下能粘接的纤维(31)形成,所述纤维层(3)位于第一基材层(1)与第二基材层(2)之间,并且该纤维层(3)中的部分纤维(31)直接附接在第一基材层(1)上或第二基材层(2)上,部分纤维直接粘接在所述第二基材层(2)或第一基材层(1)上,并且在附接面和/或粘接面上均留有供气体进出纤维层的透气路;在所述纤维层(3)的多根的纤维(31)的缝隙中均匀的含有能释放环丙烯类气体的药剂(32)或能释放环丙烷类气体的药剂(32),且所述第一基材层(1)和第二基材层(2)中的材质至少有一层是透气的材料;
优选地,所述保鲜层合物不含有机溶剂;
优选地,所述第一基材层(1)的厚度为1~5000μm;
优选地,所述第二基材层(2)的厚度为2~3000μm;
优选地,所述纤维层(3)的厚度为0.5~3000μm。
2.根据权利要求1所述的保鲜层合物,其中,所述在热和/或压力的作用下能粘接的纤维(31)包括聚丙烯纤维、聚烯烃纤维、聚乙烯纤维、聚氯乙烯纤维、聚丙烯睛纤维、改性聚丙烯睛纤维、聚乙烯醇系纤维、芳族聚胺纤维、合成纤维、醋酸纤维、胶黏纤维、高湿模量粘胶纤维、聚偏氯乙烯纤维、二烯类弹性纤维和聚氨酯弹性纤维中的一种或多种。
3.根据权利要求1所述的保鲜层合物,其中,所述能释放环丙烯类气体的药剂(32)包括能释放环丙烯气体的药剂,或能释放1-甲基-环丙烯气体的药剂;
所述能释放环丙烷类气体的药剂(32)包括能释放二甲基环丙烷的药剂,或能释放亚甲基环丙烷的药剂。
4.根据权利要求3所述的保鲜层合物,其中,所述能释放环丙烯类气体的药剂(32)为包裹有1-甲基-环丙烯/α-环糊精配合物的粉末;
优选地,每平方米的保鲜层合物均匀的含有10mg~2000mg所述的包裹有1-甲基-环丙烯/α-环糊精配合物的粉末。
5.根据权利要求1所述的保鲜层合物,其中,所述第一基材层(1)、第二基材层(2)的材质各自独立地包括透气纸、吸水纸、无酸纸、吸湿纸、胶粘纸、蛋白胶纸、全棉纤维纸、全木浆纸、草浆纸、面包纸、竹浆纸、吸水性纸、塑纸、多孔聚乙烯薄膜、多孔聚酯薄膜、多孔聚丙烯薄膜、多孔聚氯乙烯薄膜、聚苯乙烯薄膜、聚偏二氯乙烯薄膜、乙烯-醋酸乙烯共聚物薄膜、聚碳酸酯薄膜、醋酸纤维素薄膜、无纺聚乙烯或无纺聚丙烯。
6.根据权利要求1~5中任一项所述的保鲜层合物,其中,在所述第一基材层(1)或第二基材层(2)上层合有能释放SO2和/或ClO2的保鲜剂,在该保鲜剂上还层合有第三基材层;
优选地,所述能释放SO2和/或ClO2的保鲜剂为微胶囊保鲜剂;
优选地,所述第三基材层的材质为不透气材料;如为不透气聚氯乙烯薄膜、不透气聚丙烯薄膜或不透气塑纸,当所述第三基材层的材质为不透气材料时,所述第一基材层和第二基材层中处于外侧的基材的材质是透气材料。
7.权利要求1~6中任一项所述的保鲜层合物的制备方法,所述方法包括如下步骤:
准备所述第一基材层(1)或所述第二基材层(2);
使所述第一基材层(1)或所述第二基材层(2)附接所述在热或/和压力的作用下能粘接的纤维(31)以形成所述纤维层(3);或直接准备所述纤维层(3)附接在第一基材层(1)或第二基材层(2)上的基材;
在附接在第一基材层(1)或第二基材层(2)上的纤维层上均匀投放所述能释放环丙烯类气体的药剂(32)或能释放环丙烷类气体的药剂(32);然后将所述第二基材层(2)或第一基材层(1)覆盖在该纤维层上,然后在热或/和压力的作用下粘合,得所述保鲜层合物。
8.根据权利要求7所述的制备方法,其中,所述纤维层(3)附接在第一基材层(1)或第二基材层(2)上的基材为聚丙烯纤维、聚烯烃纤维、聚乙烯纤维、聚氯乙烯纤维、聚酯纤维、聚丙烯睛纤维、改性聚丙烯睛纤维、聚乙烯醇系纤维、芳族聚胺纤维、合成纤维、醋酯纤维、胶黏纤维、高湿模量粘胶纤维、聚偏氯乙烯纤维、二烯类弹性纤维、聚氨酯弹性纤维中的一种或多种附接在透气纸、吸水纸、无酸纸、吸湿纸、胶粘纸、蛋白胶纸、全棉纤维纸、全木浆纸、草浆纸、面包纸、竹浆纸、吸水性纸、塑纸、多孔聚乙烯薄膜、多孔聚酯薄膜、多孔聚丙烯薄膜、多孔聚氯乙烯薄膜、聚苯乙烯薄膜、聚偏二氯乙烯薄膜、乙烯-醋酸乙烯共聚物薄膜、聚碳酸酯薄膜、醋酸纤维素薄膜、无纺聚乙烯或无纺聚丙烯上的基材。
9.权利要求1~6中任一项所述的保鲜层合物在果蔬保鲜中的应用。
10.根据权利要求9所述的应用,其中,所述果蔬包括葡萄、樱桃、香蕉、西梅、桃子、李子、西兰花、西红柿、芦笋、西葫芦中的一种或多种。