CN108329527A - A kind of filler promoting plastic strength - Google Patents
A kind of filler promoting plastic strength Download PDFInfo
- Publication number
- CN108329527A CN108329527A CN201711487858.5A CN201711487858A CN108329527A CN 108329527 A CN108329527 A CN 108329527A CN 201711487858 A CN201711487858 A CN 201711487858A CN 108329527 A CN108329527 A CN 108329527A
- Authority
- CN
- China
- Prior art keywords
- parts
- nano
- filler
- plastic strength
- powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of fillers promoting plastic strength, are made of following substance:Attapulgite, pomegranate mountain flour, kaolin powder, nano-titanium dioxide, nano zirconium dioxide, carbon nanotubes.The present invention has arranged in pairs or groups plurality of raw materials ingredient, can effectively improve the overall quality of plastics, the tensile strength of plastics is improved 20% or more, bending strength improves 25% or more, compression strength improves 30% or so, hence it is evident that improves the use quality of plastics, great popularizing value.
Description
Technical field
The invention belongs to technical field of plastic, and in particular to a kind of filler promoting plastic strength.
Background technology
With the transformation of the development and consumption concept of society, people increasingly pay attention to health, thus in city
Constantly increase with all kinds of fitness equipments in household, provides a great convenience and help for people's health improvement.It is common
Fitness equipment have fitness climber, bodybuilder, rowing machine, treadmill, beauty belt massage etc., and a large amount of plastics can be used in above-mentioned equipment
The qualitative effects of shell, plastic casing the use characteristic of fitness equipment, therefore in order to promote quality and the service life of fitness equipment,
It needs constantly to improve the performance of plastic casing.The characteristics such as intensity of most plastic casings are bad currently on the market, comprehensive
It is bad to close performance, needs further to improve.
Invention content
The purpose of the present invention is for existing problem, provide a kind of filler promoting plastic strength.
The present invention is achieved by the following technical solutions:
A kind of filler promoting plastic strength, is made of the substance of following parts by weight:
20 ~ 25 parts of attapulgites, 33 ~ 36 parts of pomegranate mountain flours, 14 ~ 17 parts of kaolin powder, 15 ~ 20 parts of nano-titanium dioxides, 22 ~ 26
Part nano zirconium dioxide, 5 ~ 10 parts of carbon nanotubes.
Preferably, it is made of the substance of following parts by weight:
23 ~ 25 parts of attapulgites, 34 ~ 36 parts of pomegranate mountain flours, 16 ~ 17 parts of kaolin powder, 18 ~ 20 parts of nano-titanium dioxides, 24 ~ 26
Part nano zirconium dioxide, 8 ~ 10 parts of carbon nanotubes.
Preferably, it is made of the substance of following parts by weight:
23 parts of attapulgites, 34 parts of pomegranate mountain flours, 16 parts of kaolin powder, 18 parts of nano-titanium dioxides, 24 parts of nano zirconium dioxides,
8 parts of carbon nanotubes.
Further, the granular size of the attapulgite is 120 ~ 150 mesh.
Further, the granular size of the pomegranate mountain flour and kaolin powder is 300 ~ 400 mesh.
Further, the granular size of the nano-titanium dioxide and nano zirconium dioxide is 20 ~ 70nm.
A kind of preparation method for the filler promoting plastic strength, includes the following steps:
(1)Attapulgite, pomegranate mountain flour, kaolin powder are put into calcining furnace jointly after 1 ~ 2h of calcination processing and taken out, is obtained mixed
It is spare to close powder A;
(2)By step(1)The mixed powder A and nano-titanium dioxide of gained, nano zirconium dioxide, carbon nanotubes are fully puddled uniformly
It takes out afterwards.
Further, step(1)Described in calcination processing when temperature be 800 ~ 860 DEG C.
The present invention has the following advantages compared with prior art:
The present invention has arranged in pairs or groups plurality of raw materials ingredient, can effectively improve the overall quality of plastics, and the tensile strength of plastics is promoted
20% or more, bending strength improves 25% or more, compression strength improves 30% or so, hence it is evident that improve plastics uses product
Matter, great popularizing value.
Specific implementation mode
Embodiment 1
A kind of filler promoting plastic strength, is made of the substance of following parts by weight:
20 parts of attapulgites, 33 parts of pomegranate mountain flours, 14 parts of kaolin powder, 15 parts of nano-titanium dioxides, 22 parts of nano zirconium dioxides,
5 parts of carbon nanotubes.
Further, the granular size of the attapulgite is 120 ~ 150 mesh.
Further, the granular size of the pomegranate mountain flour and kaolin powder is 300 ~ 400 mesh.
Further, the granular size of the nano-titanium dioxide and nano zirconium dioxide is 20 ~ 70nm.
A kind of preparation method for the filler promoting plastic strength, includes the following steps:
(1)Attapulgite, pomegranate mountain flour, kaolin powder are put into calcining furnace jointly after calcination processing 1h and taken out, must be mixed
Powder A is spare;
(2)By step(1)The mixed powder A and nano-titanium dioxide of gained, nano zirconium dioxide, carbon nanotubes are fully puddled uniformly
It takes out afterwards.
Further, step(1)Described in calcination processing when temperature be 800 DEG C.
Embodiment 2
A kind of filler promoting plastic strength, is made of the substance of following parts by weight:
23 parts of attapulgites, 34 parts of pomegranate mountain flours, 16 parts of kaolin powder, 18 parts of nano-titanium dioxides, 24 parts of nano zirconium dioxides,
8 parts of carbon nanotubes.
Further, the granular size of the attapulgite is 120 ~ 150 mesh.
Further, the granular size of the pomegranate mountain flour and kaolin powder is 300 ~ 400 mesh.
Further, the granular size of the nano-titanium dioxide and nano zirconium dioxide is 20 ~ 70nm.
A kind of preparation method for the filler promoting plastic strength, includes the following steps:
(1)Attapulgite, pomegranate mountain flour, kaolin powder are put into calcining furnace jointly after calcination processing 1.6h and taken out, is obtained mixed
It is spare to close powder A;
(2)By step(1)The mixed powder A and nano-titanium dioxide of gained, nano zirconium dioxide, carbon nanotubes are fully puddled uniformly
It takes out afterwards.
Further, step(1)Described in calcination processing when temperature be 830 DEG C.
Embodiment 3
A kind of filler promoting plastic strength, is made of the substance of following parts by weight:
25 parts of attapulgites, 36 parts of pomegranate mountain flours, 17 parts of kaolin powder, 20 parts of nano-titanium dioxides, 26 parts of nano zirconium dioxides,
10 parts of carbon nanotubes.
Further, the granular size of the attapulgite is 120 ~ 150 mesh.
Further, the granular size of the pomegranate mountain flour and kaolin powder is 300 ~ 400 mesh.
Further, the granular size of the nano-titanium dioxide and nano zirconium dioxide is 20 ~ 70nm.
A kind of preparation method for the filler promoting plastic strength, includes the following steps:
(1)Attapulgite, pomegranate mountain flour, kaolin powder are put into calcining furnace jointly after calcination processing 2h and taken out, must be mixed
Powder A is spare;
(2)By step(1)The mixed powder A and nano-titanium dioxide of gained, nano zirconium dioxide, carbon nanotubes are fully puddled uniformly
It takes out afterwards.
Further, step(1)Described in calcination processing when temperature be 860 DEG C.
Claims (8)
1. a kind of filler promoting plastic strength, which is characterized in that be made of the substance of following parts by weight:
20 ~ 25 parts of attapulgites, 33 ~ 36 parts of pomegranate mountain flours, 14 ~ 17 parts of kaolin powder, 15 ~ 20 parts of nano-titanium dioxides, 22 ~ 26
Part nano zirconium dioxide, 5 ~ 10 parts of carbon nanotubes.
2. a kind of filler promoting plastic strength according to claim 1, which is characterized in that by the substance of following parts by weight
It is made:
23 ~ 25 parts of attapulgites, 34 ~ 36 parts of pomegranate mountain flours, 16 ~ 17 parts of kaolin powder, 18 ~ 20 parts of nano-titanium dioxides, 24 ~ 26
Part nano zirconium dioxide, 8 ~ 10 parts of carbon nanotubes.
3. a kind of filler promoting plastic strength according to claim 1, which is characterized in that by the substance of following parts by weight
It is made:
23 parts of attapulgites, 34 parts of pomegranate mountain flours, 16 parts of kaolin powder, 18 parts of nano-titanium dioxides, 24 parts of nano zirconium dioxides,
8 parts of carbon nanotubes.
4. a kind of filler of promotion plastic strength according to any one of claim 1 ~ 3, which is characterized in that described recessed
The granular size of convex stick soil is 120 ~ 150 mesh.
5. a kind of filler of promotion plastic strength according to any one of claim 1 ~ 3, which is characterized in that the stone
The granular size of garnet powder and kaolin powder is 300 ~ 400 mesh.
6. a kind of filler of promotion plastic strength according to any one of claim 1 ~ 3, which is characterized in that described to receive
The granular size of rice titanium dioxide and nano zirconium dioxide is 20 ~ 70nm.
7. a kind of preparation method of the filler of promotion plastic strength as described in any one of claim 1 ~ 3, feature exist
In including the following steps:
(1)Attapulgite, pomegranate mountain flour, kaolin powder are put into calcining furnace jointly after 1 ~ 2h of calcination processing and taken out, is obtained mixed
It is spare to close powder A;
(2)By step(1)The mixed powder A and nano-titanium dioxide of gained, nano zirconium dioxide, carbon nanotubes are fully puddled uniformly
It takes out afterwards.
8. a kind of preparation method of filler promoting plastic strength according to claim 7, which is characterized in that step(1)
Described in calcination processing when temperature be 800 ~ 860 DEG C.