CN108300942A - A kind of hull keel steel pipe - Google Patents
A kind of hull keel steel pipe Download PDFInfo
- Publication number
- CN108300942A CN108300942A CN201810115215.6A CN201810115215A CN108300942A CN 108300942 A CN108300942 A CN 108300942A CN 201810115215 A CN201810115215 A CN 201810115215A CN 108300942 A CN108300942 A CN 108300942A
- Authority
- CN
- China
- Prior art keywords
- steel pipe
- less
- hull keel
- present
- keel steel
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of hull keel steel pipes, belong to ship technical field, the steel pipe is formed with following compositions, described at being grouped as in terms of quality %, contains C:0.04%, Si:0.4%, Mn:1.0%, P:0.3%, S:0.020%, Al:0.10~0.15%, N:0.010% or less, Nb:0.003% less than 0.070%, and surplus is made of Fe and inevitable impurity, and the present invention is corrosion-resistant, and bending strength is maintained at 1400MPa or more.
Description
Technical field
The present invention relates to a kind of hull keel steel pipes, belong to ship technical field.
Background technology
In existing hull keel, (standard size is outer straight to the steel pipe for the use of bending strength being mostly 1400MPa or more
Diameter 50mm, interior diameter 42mm, wall thickness 4mm) it is welded, however these steel pipes are particularly easy to get rusty, and are fully immersed in south
In the seawater pond (100L, tube quality 0.5kg, and steel pipe does not do any safeguard procedures) that sea is fetched, quality mitigates 0.5%
Time is only in 30min, it is difficult to meet the requirements.
Invention content
(1) the technical issues of solving
The present invention provides a kind of corrosion-resistant, and bending strength is maintained at the steel pipe of 1400MPa or more.
(2) technical solution
In order to achieve the above object, the present invention is achieved by the following technical programs:A kind of hull keel steel pipe, it is special
Sign is that the steel pipe is formed with following compositions, described at being grouped as in terms of quality %, contains C:0.04%, Si:0.4%,
Mn:1.0%, P:0.3%, S:0.020%, Al:0.10~0.15%, N:0.010% or less, Nb:0.003% less than
0.070%, surplus is made of Fe and inevitable impurity.
Preferably, the content of the Al is 0.13%.
(3) advantageous effect
The present invention provides a kind of corrosion-resistant, and bending strength is maintained at the steel pipe of 1400MPa or more.
Specific implementation mode
The technical scheme in the embodiments of the invention will be clearly and completely described below.
Embodiment one
The present invention provides a kind of technical solution:A kind of hull keel steel pipe, which is characterized in that the steel pipe has following
It is described at being grouped as in terms of quality % at being grouped as, contain C:0.04%, Si:0.4%, Mn:1.0%, P:0.3%, S:
0.020%, Al:0.10%, N:0.010% or less, Nb:0.003% less than 0.070%, and surplus is by Fe and can not keep away
The impurity exempted from is constituted.
Steel pipe bending strength made from the present embodiment is 1437MPa, and under the experimental situation that background technology proposes, the time is
43min。
Embodiment two
A kind of hull keel steel pipe, which is characterized in that the steel pipe with following compositions form, it is described at be grouped as with
Quality % meters, contain C:0.04%, Si:0.4%, Mn:1.0%, P:0.3%, S:0.020%, Al:0.12%, N:0.010%
Below, Nb:0.003% less than 0.070%, and surplus is made of Fe and inevitable impurity.
Steel pipe bending strength made from the present embodiment is 1477MPa, and under the experimental situation that background technology proposes, the time is
47min。
Embodiment three
A kind of hull keel steel pipe, which is characterized in that the steel pipe with following compositions form, it is described at be grouped as with
Quality % meters, contain C:0.04%, Si:0.4%, Mn:1.0%, P:0.3%, S:0.020%, Al:0.13%, N:0.010%
Below, Nb:0.003% less than 0.070%, and surplus is made of Fe and inevitable impurity.
Steel pipe bending strength made from the present embodiment is 1562MPa, and under the experimental situation that background technology proposes, the time is
54min。
Example IV
A kind of hull keel steel pipe, which is characterized in that the steel pipe with following compositions form, it is described at be grouped as with
Quality % meters, contain C:0.04%, Si:0.4%, Mn:1.0%, P:0.3%, S:0.020%, Al:0.15%, N:0.010%
Below, Nb:0.003% less than 0.070%, and surplus is made of Fe and inevitable impurity.
Steel pipe bending strength made from the present embodiment is 1417MPa, and under the experimental situation that background technology proposes, the time is
41min。
Therefore, when the content of Al is 0.13%, steel pipe bending strength of the invention is higher, and proposed in background technology
Under experimental situation, time 54min is also longer.
Claims (2)
1. a kind of hull keel steel pipe, which is characterized in that the steel pipe is formed with following compositions, described at being grouped as with matter
% meters are measured, C is contained:0.04%, Si:0.4%, Mn:1.0%, P:0.3%, S:0.020%, Al:0.10~0.15%, N:
0.010% or less, Nb:0.003% less than 0.070%, and surplus is made of Fe and inevitable impurity.
2. hull keel steel pipe according to claim 1, which is characterized in that the content of the Al is 0.13%.