CN108299879A - A kind of diatom ooze, activated carbon composite coating and production technology - Google Patents
A kind of diatom ooze, activated carbon composite coating and production technology Download PDFInfo
- Publication number
- CN108299879A CN108299879A CN201810075567.3A CN201810075567A CN108299879A CN 108299879 A CN108299879 A CN 108299879A CN 201810075567 A CN201810075567 A CN 201810075567A CN 108299879 A CN108299879 A CN 108299879A
- Authority
- CN
- China
- Prior art keywords
- parts
- activated carbon
- diatom ooze
- production technology
- powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of diatom ooze, activated carbon composite coating, the coating is made of the raw material of following mass fraction：0.5 1 parts of dispersant, 0.1 2 parts of surfactant, 0.4 0.8 parts of antifoaming agent, 0.8 3.5 parts of ethylene glycol, grey 10 25 parts of calcium, 25 35 parts of diatomite, 0.8 1.2 parts of rubber powder, 10 20 parts of dry powder, 0.1 0.2 parts of preservative, 0.2 0.7 parts of mould inhibitor, 1 2.5 parts of coalescents, 20 30 parts of water, 10 15 parts of activated carbon, the present invention have the advantages that extensive raw material sources, cheap, safety and environmental protection, sterilization, mould proof, deodorization, purification air.
Description
Technical field
The invention belongs to decoration technology fields, and in particular to a kind of indoor decorative paint more particularly to a kind of diatom ooze, work
Property charcoal composite coating and production technology.
Background technology
Formaldehyde is a kind of clear, colorless, volatilization gas excitatory.It hangs up one's hat in the environment of formaldehyde, can go out
The serious stimulation of existing respiratory tract and oedema, eye shouting pain, headache, can also occur bronchial asthma, direct skin contact formaldehyde can draw
Play dermatitis, color spot, necrosis, it is also possible to cause slow poisoning, mucous hyperemia, skin irritatin disease, allergic dermatitis occur, seriously
Directly cause leukaemia and lymph cancer, cause life greatly to be threatened, formaldehyde, as a kind of to the most harmful gas of the mankind
Body is known as indoor " taking life killer by force ", especially in China, seriously endangers new finishing family, especially children, pregnant woman, old man
Health, existing coatings contain a large amount of formaldehyde components, there is larger harm to human body.
The main raw material(s) of diatom ooze is diatom mineral --- the diatomite formed after 1 years, and diatom is a kind of life
Algae in ocean, lake, the aquatic class biology that swims that diatom ooze is taken before living in millions of years --- diatom deposit and
At natural materials, main component is opal, be rich in multiple beneficial minerals, quality is light and soft, and electron microscope shows its grain
Sublist face has countless small holes, and for porosity up to 90% or more, specific surface area is up to 65 ㎡/g, outstanding point exactly this
Sub- sieve structure determines its unique function --- there is extremely strong physical adsorption property and ion-exchange performance, it is big in metope
Area is sprayed water, and can be absorbed a large amount of water, be illustrated that adsorptivity is extremely strong, and slowly sustained release negative oxygen ion, energy effectively decomposing formaldehyde,
Harmful carcinogen such as benzene, radon gas.
Invention content
There is provided it is an object of the invention to overcome the deficiencies in the prior art a kind of raw material sources it is extensive, it is cheap, peace
Loopful guarantor, sterilization, mould proof, deodorization, diatom ooze, activated carbon composite coating and the production technology for purifying air.
The technical scheme is that：A kind of diatom ooze, activated carbon composite coating, the coating is by following mass fraction
Raw material forms：0.5-1 parts of dispersant, 0.1-2 parts of surfactant, 0.4-0.8 parts of antifoaming agent, 0.8-3.5 parts of ethylene glycol, grey calcium
10-25 parts, 25-35 parts of diatomite, 0.8-1.2 parts of rubber powder, 10-20 parts of dry powder, 0.1-0.2 parts of preservative, mould inhibitor 0.2-
0.7 part, 1-2.5 parts of coalescents, 20-30 parts of water, 10-15 parts of activated carbon.
The dispersant is polycarboxylate sodium.
The antifoaming agent is organosilicon and mineral oil mixture.
The preservative is isothiazolinone.
The mould inhibitor is amino first.
The production technology of a kind of diatom ooze, activated carbon composite coating, the production technology of the coating include the following steps：
Step 1：Activated carbon, diatomite are put into ball mill ball milling 1-1.5 hours, 300-450 mesh sieve is crossed after ball milling, is obtained
It is for use to mixed-powder；
Step 2：Grey calcium is put into ball mill ball milling 1-1.5 hours, 400-500 mesh sieve is crossed after ball milling, obtains sierozem power end
For use；
Step 3：Water is poured into container, and starts to stir, ethylene glycol, sierozem power, rubber powder are sequentially added during stirring
And dry powder, and be sufficiently stirred；
Step 4：The mixed liquor that step 3 obtains is heated and stirred, when being heated to 55-60 DEG C, continues to add into mixed liquor
Add activated carbon and diatomaceous mixed-powder；
Step 5：Will in step 4 be added activated carbon and diatomaceous mixed-powder heating after twenty minutes, continue into mixed liquor according to
Secondary addition surfactant, dispersant and coalescents, and continue to stir；
Step 6：The mixed liquor obtained into step continues to add antifoaming agent, preservative and mould inhibitor successively, and stirs to raw material
It is mixed thoroughly.
The present invention has the following advantages：The present invention use primary raw material of the diatom ooze as coating, diatom ooze it is main at
Divide diatomaceous pyroconductivity very low, be ideal heat preserving and insulating material in itself, there is extraordinary thermal and insulating performance, every
Thermal effect is 6 times of condition of equivalent thickness cement mortar, unique " molecular sieve " structure of diatom ooze, after the moisture in touching air
" water fall effect " is will produce, to constantly release the negative oxygen ion beneficial to human body, any heavy metal is free of, does not generate quiet
Electricity, floating dust are not easy to adhere to, and metope is permanently pure and fresh, and diatom ooze is not likely to produce electrostatic, and metope surface is not easy dust fall, and active carbon purifying is empty
The principle of gas is can significantly to touch surrounding air by the pore structure and surface area by its charcoal itself prosperity,
In passive adsorption some pollutants to the hole of oneself, effectively play the role of sterilization, deodorization, purification air, present invention tool
There is the advantages of extensive raw material sources, cheap, safety and environmental protection, sterilization, mould proof, deodorization, purification air.
Specific implementation mode
With reference to embodiment, the present invention is further illustrated.
Embodiment 1
A kind of diatom ooze, activated carbon composite coating, the coating are made of the raw material of following mass fraction：Dispersant 0.5kg,
Surfactant 0.1kg, antifoaming agent 0.4kg, ethylene glycol 3.5kg, grey calcium 10kg, diatomite 25kg, rubber powder 1.2kg, dry powder
20kg, preservative 0.2kg, mould inhibitor 0.7kg, coalescents 1kg, water 22.4kg, activated carbon 15kg.
The production technology of a kind of diatom ooze, activated carbon composite coating, the production technology of the coating include the following steps：
Step 1：Activated carbon, diatomite are put into ball mill ball milling 1-1.5 hours, 300-450 mesh sieve is crossed after ball milling, is obtained
It is for use to mixed-powder；
Step 2：Grey calcium is put into ball mill ball milling 1-1.5 hours, 400-500 mesh sieve is crossed after ball milling, obtains sierozem power end
For use；
Step 3：Water is poured into container, and starts to stir, ethylene glycol, sierozem power, rubber powder are sequentially added during stirring
And dry powder, and be sufficiently stirred；
Step 4：The mixed liquor that step 3 obtains is heated and stirred, when being heated to 55-60 DEG C, continues to add into mixed liquor
Add activated carbon and diatomaceous mixed-powder；
Step 5：Will in step 4 be added activated carbon and diatomaceous mixed-powder heating after twenty minutes, continue into mixed liquor according to
Secondary addition surfactant, dispersant and coalescents, and continue to stir；
Step 6：The mixed liquor obtained into step continues to add antifoaming agent, preservative and mould inhibitor successively, and stirs to raw material
It is mixed thoroughly.
The present invention uses primary raw material of the diatom ooze as coating, and the diatomaceous pyroconductivity of main component of diatom ooze is very
It is low, it is ideal heat preserving and insulating material in itself, there is extraordinary thermal and insulating performance, heat insulation is condition of equivalent thickness cement
6 times of mortar, unique " molecular sieve " structure of diatom ooze, will produce " water fall effect " after the moisture in touching air, from
And the negative oxygen ion beneficial to human body is constantly released, any heavy metal is free of, does not generate electrostatic, floating dust is not easy to adhere to, wall
Face is permanently pure and fresh, and diatom ooze is not likely to produce electrostatic, and metope surface is not easy dust fall, and the principle of active carbon purifying air is by relying on it
The pore structure and surface area of charcoal itself prosperity can significantly touch surrounding air, some pollutants of passive adsorption
Into the hole of oneself, effectively play the role of sterilization, deodorization, purification air, the present invention extensive, price with raw material sources
The advantages of cheap, safety and environmental protection, sterilization, mould proof, deodorization, purification air.
Embodiment 2
A kind of diatom ooze, activated carbon composite coating, the coating are made of the raw material of following mass fraction：Dispersant 1kg, table
Face activating agent 2kg, antifoaming agent 0.8kg, ethylene glycol 3.5kg, grey calcium 15kg, diatomite 30kg, rubber powder 0.8kg, dry powder 11kg,
Preservative 0.1kg, mould inhibitor 0.2kg, coalescents 1kg, water 24.6kg, activated carbon 10kg.
The production technology of a kind of diatom ooze, activated carbon composite coating, the production technology of the coating include the following steps：
Step 1：Activated carbon, diatomite are put into ball mill ball milling 1-1.5 hours, 300-450 mesh sieve is crossed after ball milling, is obtained
It is for use to mixed-powder；
Step 2：Grey calcium is put into ball mill ball milling 1-1.5 hours, 400-500 mesh sieve is crossed after ball milling, obtains sierozem power end
For use；
Step 3：Water is poured into container, and starts to stir, ethylene glycol, sierozem power, rubber powder are sequentially added during stirring
And dry powder, and be sufficiently stirred；
Step 4：The mixed liquor that step 3 obtains is heated and stirred, when being heated to 55-60 DEG C, continues to add into mixed liquor
Add activated carbon and diatomaceous mixed-powder；
Step 5：Will in step 4 be added activated carbon and diatomaceous mixed-powder heating after twenty minutes, continue into mixed liquor according to
Secondary addition surfactant, dispersant and coalescents, and continue to stir；
Step 6：The mixed liquor obtained into step continues to add antifoaming agent, preservative and mould inhibitor successively, and stirs to raw material
It is mixed thoroughly.
The present invention uses primary raw material of the diatom ooze as coating, and the diatomaceous pyroconductivity of main component of diatom ooze is very
It is low, it is ideal heat preserving and insulating material in itself, there is extraordinary thermal and insulating performance, heat insulation is condition of equivalent thickness cement
6 times of mortar, unique " molecular sieve " structure of diatom ooze, will produce " water fall effect " after the moisture in touching air, from
And the negative oxygen ion beneficial to human body is constantly released, any heavy metal is free of, does not generate electrostatic, floating dust is not easy to adhere to, wall
Face is permanently pure and fresh, and diatom ooze is not likely to produce electrostatic, and metope surface is not easy dust fall, and the principle of active carbon purifying air is by relying on it
The pore structure and surface area of charcoal itself prosperity can significantly touch surrounding air, some pollutants of passive adsorption
Into the hole of oneself, effectively play the role of sterilization, deodorization, purification air, the present invention extensive, price with raw material sources
The advantages of cheap, safety and environmental protection, sterilization, mould proof, deodorization, purification air.
Claims (6)
1. a kind of diatom ooze, activated carbon composite coating, it is characterised in that：The coating is the raw material group by following mass fraction
At：0.5-1 parts of dispersant, 0.1-2 parts of surfactant, 0.4-0.8 parts of antifoaming agent, 0.8-3.5 parts of ethylene glycol, grey calcium 10-25
Part, 25-35 parts of diatomite, 0.8-1.2 parts of rubber powder, 10-20 parts of dry powder, 0.1-0.2 parts of preservative, 0.2-0.7 parts of mould inhibitor,
1-2.5 parts of coalescents, 20-30 parts of water, 10-15 parts of activated carbon.
2. the production technology of a kind of diatom ooze as described in claim 1, the compound indoor decorative paint of activated carbon, feature exist
In：The dispersant is polycarboxylate sodium.
3. the production technology of a kind of diatom ooze as described in claim 1, the compound indoor decorative paint of activated carbon, feature exist
In：The antifoaming agent is organosilicon and mineral oil mixture.
4. the production technology of a kind of diatom ooze as described in claim 1, the compound indoor decorative paint of activated carbon, feature exist
In：The preservative is isothiazolinone.
5. the production technology of a kind of diatom ooze as described in claim 1, the compound indoor decorative paint of activated carbon, feature exist
In：The mould inhibitor is amino first.
6. the production technology of a kind of diatom ooze, activated carbon composite coating, it is characterised in that：The production technology of the coating includes
Following steps：
Step 1：Activated carbon, diatomite are put into ball mill ball milling 1-1.5 hours, 300-450 mesh sieve is crossed after ball milling, is obtained
It is for use to mixed-powder；
Step 2：Grey calcium is put into ball mill ball milling 1-1.5 hours, 400-500 mesh sieve is crossed after ball milling, obtains sierozem power end
For use；
Step 3：Water is poured into container, and starts to stir, ethylene glycol, sierozem power, rubber powder are sequentially added during stirring
And dry powder, and be sufficiently stirred；
Step 4：The mixed liquor that step 3 obtains is heated and stirred, when being heated to 55-60 DEG C, continues to add into mixed liquor
Add activated carbon and diatomaceous mixed-powder；
Step 5：Will in step 4 be added activated carbon and diatomaceous mixed-powder heating after twenty minutes, continue into mixed liquor according to
Secondary addition surfactant, dispersant and coalescents, and continue to stir；
Step 6：The mixed liquor obtained into step continues to add antifoaming agent, preservative and mould inhibitor successively, and stirs to raw material
It is mixed thoroughly.