CN108294865A - A kind of slight incontinence pad of adult - Google Patents
A kind of slight incontinence pad of adult Download PDFInfo
- Publication number
- CN108294865A CN108294865A CN201711370774.3A CN201711370774A CN108294865A CN 108294865 A CN108294865 A CN 108294865A CN 201711370774 A CN201711370774 A CN 201711370774A CN 108294865 A CN108294865 A CN 108294865A
- Authority
- CN
- China
- Prior art keywords
- woven fabrics
- incontinence pad
- needle punched
- punched non
- fibre
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of slight incontinence pad of adult, both ends are sector structure, which is characterized in that the incontinence pad is combined from top to bottom by guide layer, absorbed layer, bottom;The material of the guide layer uses fragrance terylene woven fabric, surface density 37g/m2;The absorbed layer is combined up and down by two layers of needle punched non-woven fabrics, and the raw material of two layers of needle punched non-woven fabrics is made of viscose glue and polypropylene fibre, and hole is provided on the needle punched non-woven fabrics of upper layer;The bottom is combined by PE ventilated membranes and needle punched non-woven fabrics, and the raw material of needle punched non-woven fabrics is identical as absorbed layer;The guide layer, absorbed layer, bottom are bound off using line to be sutured, and the line that binds off is polypropylene fiber silk.The present invention not only good water absorption repeats washing, and has the function of good antibacterial, deodorization, leakproof, lateral leakage protection etc., good appearance, comfortable and easy to wear, economic and environment-friendly.
Description
Technical field
The present invention relates to a kind of slight incontinence pads of adult, belong to nursing materials technical field.
Background technology
Nowadays, the millions of adult in the whole world suffers from urinary incontinence illness because of various factors, including diabetes, pregnancy, divides
Childbirth, climacteric, prostate problems etc., incontinence not only only occur in the elderly, in working clan also more and more often
See, either such case can may occur in male or women.Incontinence is in addition to that can cause awkward situation, it is also possible to can shadow
Ring health.
Patent CN201085741Y is a kind of reusable usable antimicrobial dirt resistant absorbent pad, is made of trilaminate material, surface layer
For the antibiotic layer of woven fabric or looped fabric making through antibacterial and anti-pollution processing, middle layer is what super-strong moisture absorbing type acupuncture cotton made
Water accepting layer, bottom are the waterproof layer that PVC or PU coating cloth makes.Although having the effect of anti-bacterial and anti-fouling, the bottom after coating
Layer resistance to hydrostatic pressure be not strong, and after carrying certain weight, urine is easy exudation.
Patent CN201263751Y is a kind of incontinence pad being combined by materials at two layers, and surface layer is PVC or PU coating cloth
The waterproof layer of making, internal layer are super-strong moisture absorbing layer made of loop bonding cloth.Although liquid absorption amount is very big, do not have the spy of antibacterial and deodouring
Property,
After through a long time use, it is easy to grow bacterium, influences health.
Patent CN201939593U is a kind of by pressing dust-free paper in absorbed layer upper surface, to increase the bullet of absorbed layer
Property, to solve the problems, such as absorbed layer easy fracture existing for adult incontinent pads.But absorbed layer uses high hydroscopic resin SAP, wood pulp,
Therefore it cannot wash, reuse repeatedly, consumption of raw materials is big, and expense expenditure is more.
In conclusion in order to overcome the existing defect of incontinence pad, research and development to remain to that antibacterial, height is kept to inhale under repeatable washing
The technical solution of the performances such as water, leakproof is still the hot spot studied at present.
Invention content
Problem to be solved by this invention is that existing absorbent incontinence pad is poor, antibiosis and deodorization effects are bad, cannot repeat
Using, be easy to leak hunting the problems such as.
To solve the above-mentioned problems, the present invention provides a kind of slight incontinence pad of adult, both ends are sector structure, special
Sign is that the incontinence pad is combined from top to bottom by guide layer, absorbed layer, bottom, and thickness is 6.20~6.40mm, face
Density is 1100~1300g/m2;The material of the guide layer uses fragrance terylene woven fabric, surface density 37g/m2, the machine
Woven fabric is plain weave structure, and warp thread fineness is 75D, and weft yarn fineness is 60D, through it is close be 100/10cm, filling density is 90/10cm;
The absorbed layer is combined up and down by two layers of needle punched non-woven fabrics, and the raw material of two layers of needle punched non-woven fabrics is made of viscose glue and polypropylene fibre,
The surface density of upper layer needle punched non-woven fabrics is 190~220g/m2, the surface density of lower layer's needle punched non-woven fabrics is 210~230g/m2, upper layer
Hole is provided on needle punched non-woven fabrics;The bottom is combined by PE ventilated membranes and needle punched non-woven fabrics, the raw material of needle punched non-woven fabrics with
Absorbed layer is identical, and surface density is 230~250g/m2;The guide layer, absorbed layer, bottom are bound off using line to be sutured, and is copied
Sideline is polypropylene fiber silk.
Preferably, the incontinence pad both sides of the edge are equipped with lateral leakage protection side, and material uses surface density for 500g/m2SMS
The nonwoven polypropylene fabric of structure, the fibre diameter of spun-bonded non-woven fabrics is 40 microns in SMS structures, and the fibre diameter of melt spraying non-woven fabrics is
4 microns.
Preferably, the yarn of the fragrance terylene woven fabric by folium artemisiae argyi plants essential oil by being compounded in washing in fibre core in advance
Synthetic fibre fibre spinning forms, fibre length 40mm, fibre fineness 5D;The fragrance terylene woven fabric is plain weave structure, warp
Yarn fineness is 75D, and weft yarn fineness is 60D, through it is close be 100/10cm, filling density is 90/10cm, surface density 37g/m2。
Preferably, the needle punched non-woven fabrics by by percentage to the quality viscose glue 95% and polypropylene fibre 5% form;The fibre of viscose glue
Dimension length is 40mm, fibre fineness 3D;The fibre length of polypropylene fibre is 40mm, fibre fineness 2D;Hole on needle punched non-woven fabrics
A diameter of 1mm, pitch of holes 5mm.
Preferably, the thickness of the PE ventilated membranes is 0.021mm, surface density 35g/m2。
Preferably, the bottom is added by latter be thermally bonded with feeding hot-rolling mill of PE ventilated membranes and needle punched non-woven fabrics overlapping
Gu.
Preferably, the fineness of the polypropylene fiber silk is 200D.
Preferably, the length of the incontinence pad be 29.3 centimetres, thickness be 6.20~6.40mm, surface density be 1100~
1400g/m2, saturation liquid absorption amount is 100~350mL, and air penetrability is 15.25~15.89mm/s;After washing 50 times, cross-direction shrinkage
Rate is -3.45~-3.35%, and longitudinal contraction rate is -5.25~-5.15%;Smaller sector structure in the sector structure of both ends
Maximum width is 14.3 centimetres, and the maximum width of larger sector structure is 23 centimetres.
The special fibre net structure design of guide layer so that yarn is arranged along longitudinal direction than laterally.Fragrance polyester fiber arranges
It is more, to be conducive to liquid along fibre web longitudinal diffusion, considerably increase the utilization ratio of absorbed layer.In addition, using fragrance yarn
Line makes the incontinence pad have effects that antibacterial, deodorization, even if still keeping the function after washing 30~50 times.
This special structure of absorbed layer makes to generate differential capillary effect between levels, and it is downward by upper layer to be conducive to liquid
Layer transmits, it is possibility to have the prevention liquid of effect is from bottom to guide layer reverse osmosis.
Bottom not only waterproof and breathable, but also can be because soft characteristic avoid people from sending out the sound of " creak " in the process of walking
Sound.In addition, carrying out bonding reinforcing by hot rolling so that film will not fall off damage in washing process, so that retention property is steady
It is fixed.
Compared with prior art, the beneficial effects of the present invention are:
(1) by adding plants essential oil in polyester fiber in-core, to achieve the effect that antibacterial, deodorization;
(2) guide layer uses unique reticular structure, and urine is made quickly to spread, permeate;
(3) viscose rayon is used so that fabric soft comfortable, affine skin is non-stimulated, wears harmless, wholesomeness long
Can be good, and there is good liquid-absorbent, saturation liquid absorption amount is up to 100~350mL;
(4) polypropylene fiber is used, so that the resistance to form of washing repeatedly of fabric is basically unchanged, service life is long, horizontal after washing 50 times
It is -3.45~-3.35% to shrinking percentage, longitudinal contraction rate is -5.25~-5.15%;
(5) PE ventilated membranes are used, not only waterproof and breathable, but also can passed by because the characteristic of PE ventilated membrane softnesses avoids people from being expert at
The sound of " creak " is sent out in journey;
(6) PE ventilated membranes and needle punched non-woven fabrics are bonded together using hot rolling so that film will not take off in washing process
Damage is fallen, to the stabilization of retention property;
(7) use the nonwoven polypropylene fabric of SMS structures as lateral leakage protection side, polypropylene fiber silk is as the line that binds off, because polypropylene fibre is distinctive
Water repellent characteristic, to improve the anti-side leakage effect of incontinence pad.
Specific implementation mode
In order to make the present invention more obvious and understandable, it is hereby described in detail below with preferred embodiment.
Raw material used in embodiment 1-3 is fragrance polyester fiber commercially available, viscose rayon, polypropylene fiber, third
Synthetic fibre silk, PE ventilated membranes.Wherein, fragrance polyester fiber is provided by foreign thousand material application technology Co., Ltd of Shenzhen;Viscose glue
Fiber is provided by Sanyou Group Co., Ltd., Tangshan;Polypropylene fiber is provided by Taizhou City Hai Lun chemical fibres Co., Ltd;PE ventilated membranes
It is provided by Yi Chang plastic cement Industrial Co., Ltd. of Foshan City;Polypropylene fiber silk is provided by sun,moon and star gloves auxiliary material firm.
The performance test methods of the slight incontinence pad of adult obtained by embodiment 1-3 are specific as follows:
1, the measurement of mass area ratio presses GB/T 24218.1-2009 " textile non-woven cloth test methods the 1st
Point:The measurement of mass area ratio ";
2, thickness measurement presses GB/T 24218.2-2009 " textile non-woven cloth test method part 2s:The survey of thickness
It is fixed ";
3, permeability test presses GB/T 5453-1997 " textile fabric permeability test ";
4, liquid absorption amount, which measures, presses " the 6th parts of textile non-woven cloth test method GB/T 24218.8-2010:Absorbability
Measurement ";
5, GB/T 20944.3-2008 " the evaluation third portions of antibacterial textile performance are pressed in antibiotic property test:Succusion ";
6, shrinkage determination presses GB/T 8629-2001 " Textile Test home washings and drying program ".
Embodiment 1
Woven fabric, eedle-punched non-wovens, film are constituted to the slight incontinence pad of adult after overseam, concrete technology flow process is:
(1) preparation of guide layer:Use spinning technique by specification for the polyester fiber spun yarn of 40mm 5D, using machine
Knit technology by the weft yarn that warp thread and fineness that fineness is 75D are 60D be made through it is close be 100/10cm, filling density is 90/10cm
Woven fabric, constitute guide layer, surface density 37g/m2;
(2) preparation of absorbed layer:Use specification for the viscose rayon of 40mm 3D and polypropylene fiber that specification is 40mm 2D
With viscose glue 95%:The ratio of polypropylene fibre 5% mixes, and needle punched non-woven fabrics, structure is made through combing networking, pinprick reinforcement, mechanical punching
At absorbed layer, which is made of upper and lower two sheets, is through road drilling process, opening diameter later after upper layer of sheet material needle thorn
1mm, two pitchs of holes are 5mm, and perforated area is entire top area, surface density 190g/m2;Lower layer's fibre web is without punching work
Sequence, surface density 210g/m2;
(3) preparation of bottom:Use surface density for 35g/m2, air penetrability is the PE ventilated membrane knead doughs of 5000g/m2/24/h
Density is 210g/m2Needle punched non-woven fabrics it is hot rolled after constitute bottom, the needle punched non-woven fabrics are the same as layer of sheet material under absorbed layer;
(4) preparation on lateral leakage protection side:The non-woven fabrics that SMS structures are made of polypropylene fibre constitutes lateral leakage protection side, surface density
500g/m2, fibre diameter used by spun-bonded non-woven fabrics is 40 microns, and fibre diameter used by melt spraying non-woven fabrics is 4 microns,
The line that binds off uses polypropylene fiber silk, and fineness 200D, lateral leakage protection side and the whole surface density for line composition of binding off are 500g/m2。
Through the slight incontinence pad, after tested, thickness 6.23mm, grammes per square metre 1182g/m of being grown up made from above-mentioned operation2,
Saturation liquid absorption amount is 185mL, air penetrability 15.89mm/s, and after washing 50 times, lateral shrinkage is -3.35%, longitudinal contraction rate
It is -5.15%, the bacteriostasis rate to Escherichia coli is 98%, and the bacteriostasis rate to staphylococcus aureus is 70%.
Embodiment 2
Woven fabric, eedle-punched non-wovens, film are constituted to the slight incontinence pad of adult after overseam, concrete technology flow process is:
(1) preparation of guide layer:Use spinning technique by specification for the polyester fiber spun yarn of 40mm 5D, using machine
Knit technology by the weft yarn that warp thread and fineness that fineness is 75D are 60D be made through it is close be 100/10cm, filling density is 90/10cm
Woven fabric, constitute guide layer, surface density 37g/m2;
(2) preparation of absorbed layer:Use specification for the viscose rayon of 40mm 3D and polypropylene fiber that specification is 40mm 2D
With viscose glue 95%:The ratio of polypropylene fibre 5% mixes, and needle punched non-woven fabrics, structure is made through combing networking, pinprick reinforcement, mechanical punching
At absorbed layer, which is made of upper and lower two sheets, is through road drilling process, opening diameter later after upper layer of sheet material needle thorn
1mm, two pitchs of holes are 5mm, and perforated area is entire top area, surface density 210g/m2;Lower layer's fibre web is without punching work
Sequence, surface density 230g/m2;
(3) preparation of bottom:Use surface density for 35g/m2, air penetrability 5000g/m2The PE ventilated membrane knead doughs of/24/h
Density is 230g/m2Needle punched non-woven fabrics it is hot rolled after constitute bottom, the needle punched non-woven fabrics are the same as layer of sheet material under absorbed layer;
(4) preparation on lateral leakage protection side:The non-woven fabrics that SMS structures are made of polypropylene fibre constitutes lateral leakage protection side, surface density
500g/m2, fibre diameter used by spun-bonded non-woven fabrics is 40 microns, and fibre diameter used by melt spraying non-woven fabrics is 4 microns,
The line that binds off uses polypropylene fiber silk, and fineness 200D, lateral leakage protection side and the whole surface density for line composition of binding off are 500g/m2。
Through slight incontinence pad of being grown up made from above-mentioned operation, after tested, the adult is slight, and incontinence pad thickness is 6.36mm, gram
Weight is 1242g/m2, saturation liquid absorption amount be 247mL, air penetrability 15.63mm/s, washing 50 times after, lateral shrinkage be-
3.42%, longitudinal contraction rate is -5.29%, and longitudinal contraction rate is -5.15%, and the bacteriostasis rate to Escherichia coli is 98%, to gold
The bacteriostasis rate of staphylococcus aureus is 70%.
Embodiment 3
Woven fabric, eedle-punched non-wovens, film are constituted to the slight incontinence pad of adult after overseam, concrete technology flow process is:
(1) preparation of guide layer:Use spinning technique by specification for the polyester fiber spun yarn of 40mm 5D, using machine
Knit technology by the weft yarn that warp thread and fineness that fineness is 75D are 60D be made through it is close be 100/10cm, filling density is 90/10cm
Woven fabric, constitute guide layer, surface density 37g/m2;
(2) preparation of absorbed layer:Use specification for the viscose rayon of 40mm 3D and polypropylene fiber that specification is 40mm 2D
With viscose glue 95%:The ratio of polypropylene fibre 5% mixes, and needle punched non-woven fabrics, structure is made through combing networking, pinprick reinforcement, mechanical punching
At absorbed layer, which is made of upper and lower two sheets, is through road drilling process, opening diameter later after upper layer of sheet material needle thorn
1mm, two pitchs of holes are 5mm, and perforated area is entire top area, surface density 230g/m2;Lower layer's fibre web is without punching work
Sequence, surface density 250g/m2;
(3) preparation of bottom:Use surface density for 35g/m2, air penetrability 5000g/m2The PE ventilated membrane knead doughs of/24/h
Density is 250g/m2Needle punched non-woven fabrics it is hot rolled after constitute bottom, the needle punched non-woven fabrics are the same as layer of sheet material under absorbed layer;
(4) preparation on lateral leakage protection side:The non-woven fabrics that SMS structures are made of polypropylene fibre constitutes lateral leakage protection side, surface density
500g/m2, fibre diameter used by spun-bonded non-woven fabrics is 40 microns, and fibre diameter used by melt spraying non-woven fabrics is 4 microns,
The line that binds off uses polypropylene fiber silk, and fineness 200D, lateral leakage protection side and the whole surface density for line composition of binding off are 500g/m2。
Through the slight incontinence pad, after tested, thickness 6.40mm, grammes per square metre 1302g/m of being grown up made from above-mentioned operation2,
Saturation liquid absorption amount is 262mL, air penetrability 15.29mm/s, and after washing 50 times, lateral shrinkage is -3.51%, longitudinal contraction rate
It is -5.46%, the bacteriostasis rate to Escherichia coli is 98%, and the bacteriostasis rate to staphylococcus aureus is 70%.
Claims (8)
1. a kind of slight incontinence pad of adult, both ends are sector structure, which is characterized in that the incontinence pad is by guide layer, absorption
Layer, bottom are combined from top to bottom, and thickness is 6.20~6.40mm, and surface density is 1100~1300g/m2;The water conservancy diversion
The material of layer uses fragrance terylene woven fabric, surface density 37g/m2, which is plain weave structure, and warp thread fineness is 75D,
Weft yarn fineness is 60D, through it is close be 100/10cm, filling density is 90/10cm;The absorbed layer by two layers of needle punched non-woven fabrics above and below
It being combined, the raw material of two layers of needle punched non-woven fabrics is made of viscose glue and polypropylene fibre, and the surface densities of upper layer needle punched non-woven fabrics is 190~
220g/m2, the surface density of lower layer's needle punched non-woven fabrics is 210~230g/m2, hole is provided on the needle punched non-woven fabrics of upper layer;The bottom by
PE ventilated membranes and needle punched non-woven fabrics are combined, and the raw material of needle punched non-woven fabrics is identical as absorbed layer, surface density be 230~
250g/m2;The guide layer, absorbed layer, bottom are bound off using line to be sutured, and the line that binds off is polypropylene fiber silk.
2. slight incontinence pad of being grown up as described in claim 1, which is characterized in that the incontinence pad both sides of the edge are equipped with lateral leakage protection
Side, material use surface density for 500g/m2SMS structures nonwoven polypropylene fabric, the fiber of spun-bonded non-woven fabrics is straight in SMS structures
Diameter is 40 microns, and the fibre diameter of melt spraying non-woven fabrics is 4 microns.
3. slight incontinence pad of being grown up as described in claim 1, which is characterized in that the yarn of the fragrance terylene woven fabric is by thing
Folium artemisiae argyi plants essential oil is first compounded in the polyester fiber in fibre core to spin, fibre length 40mm, fibre fineness is
5D;The fragrance terylene woven fabric be plain weave structure, warp thread fineness be 75D, weft yarn fineness be 60D, through it is close be 100/10cm,
Filling density is 90/10cm, surface density 37g/m2。
4. slight incontinence pad of being grown up as described in claim 1, which is characterized in that the needle punched non-woven fabrics are by with mass percent
The viscose glue 95% and polypropylene fibre 5% of meter form;The fibre length of viscose glue is 40mm, fibre fineness 3D;The fibre length of polypropylene fibre is
40mm, fibre fineness 2D;A diameter of 1mm in hole, pitch of holes 5mm on needle punched non-woven fabrics.
5. slight incontinence pad of being grown up as described in claim 1, which is characterized in that the thickness of the PE ventilated membranes is 0.021mm,
Surface density is 35g/m2。
6. slight incontinence pad of being grown up as described in claim 1, which is characterized in that the bottom is by PE ventilated membranes and acupuncture nonwoven
Cloth overlapping is latter to be thermally bonded reinforcing with feeding hot-rolling mill.
7. slight incontinence pad of being grown up as described in claim 1, which is characterized in that the fineness of the polypropylene fiber silk is 200D.
8. slight incontinence pad of being grown up as described in claim 1, which is characterized in that the length of the incontinence pad is 29.3 centimetres,
Thickness is 6.20~6.40mm, and surface density is 1100~1400g/m2, saturation liquid absorption amount is 100~350mL, and air penetrability is
15.25~15.89mm/s;Washing 50 times after, lateral shrinkage be -3.45~-3.35%, longitudinal contraction rate be -5.25~-
5.15%;The maximum width of smaller sector structure is 14.3 centimetres in the sector structure of both ends, the maximum of larger sector structure
Width is 23 centimetres.