CN108283416A - A kind of glass cup body of far-infrared functional cup - Google Patents
A kind of glass cup body of far-infrared functional cup Download PDFInfo
- Publication number
- CN108283416A CN108283416A CN201810160489.7A CN201810160489A CN108283416A CN 108283416 A CN108283416 A CN 108283416A CN 201810160489 A CN201810160489 A CN 201810160489A CN 108283416 A CN108283416 A CN 108283416A
- Authority
- CN
- China
- Prior art keywords
- parts
- glass
- powder
- cup body
- spare
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The present invention discloses a kind of glass cup body of far-infrared functional cup, the material matched by following parts by weight is made, 13 parts of 20 35 parts of high-boron-silicon glass powder, 11 23 parts of quartz sand, 9 19 parts of feldspar, 12 22 parts of energy stone, 8 16 parts of tourmaline, 48 parts of negative ion powder, 5 11 parts of bamboo charcoal powder fiber, 6 17 parts of activated carbon, 5 10 parts of weak base diatom ooze, 37 parts of far-infrared powder, 48 parts of calcium silicates, 13 parts of aluminium oxide, 13 parts of magnesia and cosolvent;Have the advantages that activated water molecule using the far-infrared functional cup of the glass cup body, improve microcirculqtory system, boost metabolism and balancing alkalinity acidity.
Description
The application is original application day on July 28th, 2016, application number 201610612624.8, applicant's stone strategy, invention
Create a kind of divisional application of entitled far-infrared functional cup.
Technical field
Present invention relates particularly to a kind of glass cup bodies of far-infrared functional cup.
Background technology
Water is lifespring, and people needs to be only second to oxygen to water, and modern medicine finds that slight illness 80% and the water of people have
It closes, 30% death is dead because of water.The investigation of the World Health Organization shows:There is 20% people in the whole world because drinking every year at present
The water that is contaminated and suffer from various diseases, 50% cancer is related with unclean water is drunk, 50% death of child be by
Caused by drinking water is contaminated, the number of the global cholera dysentery caused by water pollution and malaria disease is more than 5,000,000, the tissue
Another investigation also indicates that:The people in the countryside of developing country 75%, the drinking water of 1/3 urban population are not achieved safe and healthy
Standard.In China, there is 79% population drinking water that is harmful, being contaminated, wherein there are about 700,000,000 people to drink with big
The exceeded water of enterobacteria, 300,000,000 people, which drink, contains the exceeded water of iron, and 1.1 hundred million people drink high hardness water, and 70,000,000 people drink
High-fluorine water, 50,000,000 people drink high nitric acid brine.For China, there are 532 rivers in the whole nation, wherein 82% is polluted,
Be not subject to pollution is often in exclusion areas such as Xinjiang, Tibet.
Healthy drinking water, various water dispensers, filter or function cup come into being in order to obtain, however these equipment are produced
Raw alkaline water often drinks, some of which function cup, with the increase of cup access times, function highly unwanted to body
It gradually reduces, the purification validity period of some glasss is only 3 months or so, and the service life is shorter, and being not achieved at all makes water form small molecule
The function of change and effect.How to obtain pollution-free, rich in various minerals, and pH value, small-micelle water, negative potential are stablized, symbol
Drink water standard is closed, enables people to trust that the drink water for the health drunk is that current industry is urgently to be resolved hurrily and asks
Topic.
Invention content
The technical problem to be solved in the present invention is to provide a kind of activated water molecule, improve microcirculqtory system, promotion new old generation
Thank to the far-infrared functional cup with balancing alkalinity acidity.
To solve the above problems, the present invention adopts the following technical scheme that:
A kind of glass cup body of far-infrared functional cup, the material matched by following parts by weight are made, high-boron-silicon glass powder
20-35 parts, 11-23 parts of quartz sand, 9-19 parts of feldspar, 12-22 parts of energy stone, 8-16 parts of tourmaline, 4-8 parts of negative ion powder, bamboo
5-11 parts of powdered carbon fiber, 6-17 parts of activated carbon, 5-10 parts of weak base diatom ooze, 3-7 parts of far-infrared powder, 4-8 parts of calcium silicates, aluminium oxide
1-3 parts of 1-3 parts, 1-3 parts of magnesia and cosolvent.
To solve the above problems, the present invention another technical solution to be offered is a kind of preparation method of glass cup body, packet
Include following steps:
1) raw material disposal:Take 8-16 parts of 11-23 parts of quartz sand, 9-19 parts of feldspar, 12-22 parts of energy stone and tourmaline logical
It crosses grinding stone and is ground crushing, mixed-powder is made, it is spare;
2) processing is dried by drying machine in mixed-powder made from step 1), is then carried out handling except iron,
So that the irony in mixed-powder is removed, it is spare;
3) take 20-35 parts of high-boron-silicon glass powder, 5-10 parts of weak base diatom ooze, 3-7 parts of far-infrared powder, 4-8 parts of calcium silicates and
1-3 parts of cosolvent is added in mixed-powder made from step 2), and is stirred uniformly by blender, and glass batch is made
Material, it is spare;
4) it is melted:Glass batch made from step 3) is melted, glass batch is carried out in pot furnace
1500-1600 degrees Celsius of high-temperature heating treatment so that glass batch forms uniform, bubble-free liquid glass, spare;
5) 4-8 parts of negative ion powder, 5-11 parts of bamboo charcoal powder fiber, 6-17 parts of activated carbon, 1-3 parts of aluminium oxide and magnesia 1- are taken
3 parts are added in liquid glass made from step 4), and continuous heating so that above-mentioned material is mixed and stirred for liquid glass
It is even, it is spare;
6) it is molded:Liquid glass made from step 5) is made to the glass shape for requiring processing, system by charging machine
Glass system product are obtained, it is spare;
7) it is heat-treated:By glass system product made from step 6) by annealing, quenching technical, eliminates or generate in glass
Stress, split-phase or the crystallization in portion, and change the configuration state of glass, glass cup body blank is made, it is spare;
8) glass cup body blank made from step 7) is subjected to edging and sealing treatment, the glass cup body is made.
Description of the drawings
Fig. 1 is a kind of overall structure diagram of the far-infrared functional cup of the application glass cup body of the present invention.
Specific implementation mode
Embodiment one:
As shown in fig.1, a kind of far-infrared functional cup of application glass cup body, including glass cup body 1, cup holder 2 and cup
The upper end of lid 3,1 inside of the glass cup body is provided with retainer plate 4, and the retainer plate 4 is fixed with 1 phase of glass cup body, described solid
Surely filtering inner cup 5 is fixed on circle 4, the filtering inner cup 5 is fixed with 4 phase of retainer plate, and the right side of the glass cup body 1 is provided with
Handle 6, the handle 6 are fixed with 1 phase of glass cup body, and the pedestal 2 is located at the bottom of glass cup body 1, the pedestal 2 and glass
1 phase of cup body is fixed, and the cup lid 3 is located at the top of glass cup body 1, and the bottom of the cup lid 3 is provided with sealing ring 7, described close
Seal 7 is fixed with 3 phase of cup lid, and the sealing ring 7 is seamlessly connected with glass cup body 1.
The glass cup body 1 designs for double glazing, is conducive to prevent glass cup body 1 from radiating too fast, influences to keep the temperature.
The upper end of the glass cup body 1 is provided with external screw thread (not shown), is conducive to fix with 3 phase of cup lid.
The filtering inner cup 5 is detachable setting, is conducive to being cleaned inside glass cup body 1.
The bottom of the filtering inner cup 5 is provided with filter opening, is conducive to the tea grounds etc. in drainage.
The bottom of the cup holder 2 is provided with antiskid rubber, is conducive to prevent glass cup body 1 from sliding.
The cup lid 3 is provided with internal thread (not shown), is conducive to fix with 1 phase of glass cup body.
A kind of preparation method of glass cup body, the material matched by following parts by weight is made, including high-boron-silicon glass powder
35 parts, 11 parts of quartz sand, 9 parts of feldspar, 12 parts of energy stone, 8 parts of tourmaline, negative ion powder part, 5 parts of bamboo charcoal powder fiber, activated carbon 6
Part, 5 parts of weak base diatom ooze, 3 parts of far-infrared powder, 4 parts of calcium silicates, 1 part of aluminium oxide, 1 part of magnesia and 1 part of cosolvent, including with
Lower step:
1) raw material disposal:8 parts of 11 parts of quartz sand, 9 parts of feldspar, 12 parts of energy stone and tourmaline is taken to be carried out by grinding stone
It grinds, mixed-powder is made, it is spare;
2) processing is dried by drying machine in mixed-powder made from step 1), is then carried out handling except iron,
So that the irony in mixed-powder is removed, it is spare;
3) 1 part of 35 parts of high-boron-silicon glass powder, 5 parts of weak base diatom ooze, 3 parts of far-infrared powder, 4 parts of calcium silicates and cosolvent is taken to add
It is added in mixed-powder made from step 2), and is stirred uniformly by blender, glass batch is made, it is spare;
4) it is melted:Glass batch made from step 4) is melted, glass batch is carried out in pot furnace
1500-1600 degrees Celsius of high-temperature heating treatment so that glass batch forms uniform, bubble-free liquid glass, spare;
5) 1 part of 4 parts of negative ion powder, 5 parts of bamboo charcoal powder fiber, 6 parts of activated carbon, 1 part of aluminium oxide and magnesia is taken to be added to step
It is rapid 4) made from liquid glass, and continuous heating so that above-mentioned material is mixed and stirred for uniformly with liquid glass, spare;
6) it is molded:Liquid glass made from step 5) is made to the glass cup-shaped for requiring processing by charging machine, is made
Glass product, it is spare;
7) it is heat-treated:By glass product made from step 6) by the techniques such as annealing, quenching, eliminating or generating in glass
Stress, split-phase or the crystallization in portion, and change the configuration state of glass, glass blank is made, it is spare;
8) glass blank made from step 7) is subjected to edging and sealing treatment, the glass is made.
Embodiment two:
As shown in fig.1, a kind of far-infrared functional cup of application glass cup body, including glass cup body 1, cup holder 2 and cup
The upper end of lid 3,1 inside of the glass cup body is provided with retainer plate 4, and the retainer plate 4 is fixed with 1 phase of glass cup body, described solid
Surely filtering inner cup 5 is fixed on circle 4, the filtering inner cup 5 is fixed with 4 phase of retainer plate, and the right side of the glass cup body 1 is provided with
Handle 6, the handle 6 are fixed with 1 phase of glass cup body, and the pedestal 2 is located at the bottom of glass cup body 1, the pedestal 2 and glass
1 phase of cup body is fixed, and the cup lid 3 is located at the top of glass cup body 1, and the bottom of the cup lid 3 is provided with sealing ring 7, described close
Seal 7 is fixed with 3 phase of cup lid, and the sealing ring 7 is seamlessly connected with glass cup body 1.
The glass cup body 1 designs for double glazing, is conducive to prevent glass cup body 1 from radiating too fast, influences to keep the temperature.
The upper end of the glass cup body 1 is provided with external screw thread (not shown), is conducive to fix with 3 phase of cup lid.
The filtering inner cup 5 is detachable setting, is conducive to being cleaned inside glass cup body 1.
The bottom of the filtering inner cup 5 is provided with filter opening, is conducive to the tea grounds etc. in drainage.
The bottom of the cup holder 2 is provided with antiskid rubber, is conducive to prevent glass cup body 1 from sliding.
The cup lid 3 is provided with internal thread (not shown), is conducive to fix with 1 phase of glass cup body.
A kind of preparation method of glass cup body, the material matched by following parts by weight is made, including high-boron-silicon glass powder
20 parts, it is 23 parts of quartz sand, 19 parts of feldspar, 22 parts of energy stone, 16 parts of tourmaline, 8 parts of negative ion powder, 11 parts of bamboo charcoal powder fiber, living
Property 3 parts of 17 parts of charcoal, 10 parts of weak base diatom ooze, 7 parts of far-infrared powder, 8 parts of calcium silicates, 3 parts of aluminium oxide, 3 parts of magnesia and cosolvent,
Include the following steps:
1) raw material disposal:Take 16 parts of 23 parts of quartz sand, 19 parts of feldspar, 22 parts of energy stone and tourmaline by grinding stone into
Row is ground, and mixed-powder is made, spare;
2) processing is dried by drying machine in mixed-powder made from step 1), is then carried out handling except iron,
So that the irony in mixed-powder is removed, it is spare;
3) 3 parts of 20 parts of high-boron-silicon glass powder, 10 parts of weak base diatom ooze, 7 parts of far-infrared powder, 8 parts of calcium silicates and cosolvent are taken
It is added in mixed-powder made from step 2), and is stirred uniformly by blender, glass batch is made, it is spare;
4) it is melted:Glass batch made from step 4) is melted, glass batch is carried out in pot furnace
1500-1600 degrees Celsius of high-temperature heating treatment so that glass batch forms uniform, bubble-free liquid glass, spare;
5) 3 parts of 8 parts of negative ion powder, 11 parts of bamboo charcoal powder fiber, 17 parts of activated carbon, 3 parts of aluminium oxide and magnesia is taken to be added to
In liquid glass made from step 4), and continuous heating so that above-mentioned material is mixed and stirred for uniformly with liquid glass, spare;
6) it is molded:Liquid glass made from step 5) is made to the glass cup-shaped for requiring processing by charging machine, is made
Glass product, it is spare;
7) it is heat-treated:By glass product made from step 6) by the techniques such as annealing, quenching, eliminating or generating in glass
Stress, split-phase or the crystallization in portion, and change the configuration state of glass, glass blank is made, it is spare;
8) glass blank made from step 7) is subjected to edging and sealing treatment, the glass is made.
Embodiment three:
As shown in fig.1, a kind of far-infrared functional cup of application glass cup body, including glass cup body 1, cup holder 2 and cup
The upper end of lid 3,1 inside of the glass cup body is provided with retainer plate 4, and the retainer plate 4 is fixed with 1 phase of glass cup body, described solid
Surely filtering inner cup 5 is fixed on circle 4, the filtering inner cup 5 is fixed with 4 phase of retainer plate, and the right side of the glass cup body 1 is provided with
Handle 6, the handle 6 are fixed with 1 phase of glass cup body, and the pedestal 2 is located at the bottom of glass cup body 1, the pedestal 2 and glass
1 phase of cup body is fixed, and the cup lid 3 is located at the top of glass cup body 1, and the bottom of the cup lid 3 is provided with sealing ring 7, described close
Seal 7 is fixed with 3 phase of cup lid, and the sealing ring 7 is seamlessly connected with glass cup body 1.
The glass cup body 1 designs for double glazing, is conducive to prevent glass cup body 1 from radiating too fast, influences to keep the temperature.
The upper end of the glass cup body 1 is provided with external screw thread (not shown), is conducive to fix with 3 phase of cup lid.
The filtering inner cup 5 is detachable setting, is conducive to being cleaned inside glass cup body 1.
The bottom of the filtering inner cup 5 is provided with filter opening, is conducive to the tea grounds etc. in drainage.
The bottom of the cup holder 2 is provided with antiskid rubber, is conducive to prevent glass cup body 1 from sliding.
The cup lid 3 is provided with internal thread (not shown), is conducive to fix with 1 phase of glass cup body.
A kind of preparation method of glass cup body, the material matched by following parts by weight is made, including high-boron-silicon glass powder
27.5 parts, it is 17 parts of quartz sand, 14 parts of feldspar, 17 parts of energy stone, 12 parts of tourmaline, 6 parts of negative ion powder, 8 parts of bamboo charcoal powder fiber, living
Property 11.5 parts of charcoal, 7.5 parts of weak base diatom ooze, 5 parts of far-infrared powder, 6 parts of calcium silicates, 2 parts of aluminium oxide, 2 parts of magnesia and cosolvent 2
Part, include the following steps:
1) raw material disposal:Take 12 parts of 17 parts of quartz sand, 14 parts of feldspar, 17 parts of energy stone and tourmaline by grinding stone into
Row is ground, and mixed-powder is made, spare;
2) processing is dried by drying machine in mixed-powder made from step 1), is then carried out handling except iron,
So that the irony in mixed-powder is removed, it is spare;
3) 27.5 parts of high-boron-silicon glass powder, 7.5 parts of weak base diatom ooze, 5 parts of far-infrared powder, 6 parts of calcium silicates and cosolvent are taken
1-3 parts are added in mixed-powder made from step 2), and are stirred uniformly by blender, and glass batch is made, standby
With;
4) it is melted:Glass batch made from step 4) is melted, glass batch is carried out in pot furnace
1500-1600 degrees Celsius of high-temperature heating treatment so that glass batch forms uniform, bubble-free liquid glass, spare;
5) 2 parts of 6 parts of negative ion powder, 8 parts of bamboo charcoal powder fiber, 11.5 parts of activated carbon, 2 parts of aluminium oxide and magnesia is taken to be added to
In liquid glass made from step 4), and continuous heating so that above-mentioned material is mixed and stirred for uniformly with liquid glass, spare;
6) it is molded:Liquid glass made from step 5) is made to the glass cup-shaped for requiring processing by charging machine, is made
Glass product, it is spare;
7) it is heat-treated:By glass product made from step 6) by the techniques such as annealing, quenching, eliminating or generating in glass
Stress, split-phase or the crystallization in portion, and change the configuration state of glass, glass blank is made, it is spare;
8) glass blank made from step 7) is subjected to edging and sealing treatment, the glass is made.
Experimental example:
Experimental subjects:150 clinic trial persons are divided into 3 groups, every group of 50 people according to experimental method.
Experimental method and time:Control group 1 uses common glass drinking cup, control group 2 real by special glass drinking cup
Group far-infrared functional cup for using the present invention is tested, experimental period is 3 months, and record number is 3 times, record floor situation.
Criterion:
It is effective:Improve microcirculqtory system, boost metabolism it is with obvious effects with balancing alkalinity acidity;
Effectively:Stronger improvement microcirculqtory system boosts metabolism and balancing alkalinity acidity;
In vain:Improve microcirculqtory system, boost metabolism it is invalid with balancing alkalinity acidity;
Three groups of luggages carry out first month effect and compare, and as a result see chart 1.
It is tested by first month, three groups of situations have notable difference.
Three groups of luggages carry out second month effect and compare, and as a result see chart 2.
It is tested by second month, three groups of situations have highly significant sex differernce.
Three groups of luggages carry out a third month effect and compare, and as a result see chart 3.
It was tested by three months, three groups of situations have highly significant sex differernce.
By the above experimental result it is found that the effect of the far-infrared functional cup of the present invention is best.
Typical case:Zhang is a construction worker, needs a large amount of moisturizings, but due to common water can not supplement Zhang because
The labour of high intensity and the nutrient being lost in, therefore Zhang has selected the far-infrared functional cup of the present invention, is drinking this hair for a long time
After the water of bright far-infrared functional cup, Zhang has found the physical recovery of oneself faster, while feeling that body is become better and better,
Muscle acid is swollen caused by labour can be in second day fast quick-recovery, and alleviates fatigue.
The beneficial effects of the invention are as follows:Be conducive to improve hydrone activation, improve oxygen content, can reforming water molecules,
Activating cell increases skin elastic and changes water clusters by far infrared so that cell activation reaches pore and normally arranges
Go out toxin, in addition, being conducive to improve microcirculqtory system, enables to independent hydrone to enter cell, then pass through resonance
Forming thermal response promotes subcutaneous deep temperature rise, fine vascular expansion to promote blood circulation, and extravasated blood etc. is harmed metabolism
Obstacle all remove clean, so that tissue is brought back to life again, promote ferment growth, furthermore, additionally it is possible to boost metabolism, balance body
The acid-base value of body can be played obviously and alleviate aging, solution cigarette poison, solution alcohol, and can prevented calculi in vivo, neutralize internal acid
The effects that malicious.
The above description is merely a specific embodiment, but scope of protection of the present invention is not limited thereto, any
The change or replacement expected without creative work should all be covered subject to the new protection domain of this practicality.
Claims (2)
1. a kind of glass cup body of far-infrared functional cup, it is characterised in that:The material matched by following parts by weight is made, high boron
20-35 parts of silica glass powder, 11-23 parts of quartz sand, 9-19 parts of feldspar, 12-22 parts of energy stone, 8-16 parts of tourmaline, negative ion powder
4-8 parts, 5-11 parts of bamboo charcoal powder fiber, 6-17 parts of activated carbon, 5-10 parts of weak base diatom ooze, 3-7 parts of far-infrared powder, calcium silicates 4-8
Part, 1-3 parts of aluminium oxide, 1-3 parts of magnesia and 1-3 parts of cosolvent.
2. the preparation method of glass cup body as described in claim 1, it is characterised in that:Include the following steps:
1) raw material disposal:Take 8-16 parts of 11-23 parts of quartz sand, 9-19 parts of feldspar, 12-22 parts of energy stone and tourmaline by grinding
Grinding stone is ground crushing, and mixed-powder is made, spare;
2) processing is dried by drying machine in mixed-powder made from step 1), is then carried out handling except iron so that
Irony in mixed-powder is removed, spare;
3) 20-35 parts of high-boron-silicon glass powder, 5-10 parts of weak base diatom ooze, 3-7 parts of far-infrared powder, 4-8 parts of calcium silicates and hydrotropy are taken
1-3 parts of agent is added in mixed-powder made from step 2), and is stirred uniformly by blender, and glass batch is made,
It is spare;
4) it is melted:Glass batch made from step 3) is melted, glass batch is subjected to 1500- in pot furnace
1600 degrees Celsius of high-temperature heating treatment so that glass batch forms uniform, bubble-free liquid glass, spare;
5) 1-3 parts of 4-8 parts of negative ion powder, 5-11 parts of bamboo charcoal powder fiber, 6-17 parts of activated carbon, 1-3 parts of aluminium oxide and magnesia are taken
It is added in liquid glass made from step 4), and continuous heating so that above-mentioned material is mixed and stirred for uniformly with liquid glass,
It is spare;
6) it is molded:Liquid glass made from step 5) is made to the glass shape for requiring processing by charging machine, glass is made
Glass cup body product, it is spare;
7) it is heat-treated:By glass system product made from step 6) by annealing, quenching technical, inside glass is eliminated or generated
Stress, split-phase or crystallization, and change the configuration state of glass, glass cup body blank is made, it is spare;
8) glass cup body blank made from step 7) is subjected to edging and sealing treatment, the glass cup body is made.