CN108272557A - 伤口处理用品 - Google Patents
伤口处理用品 Download PDFInfo
- Publication number
- CN108272557A CN108272557A CN201810171067.XA CN201810171067A CN108272557A CN 108272557 A CN108272557 A CN 108272557A CN 201810171067 A CN201810171067 A CN 201810171067A CN 108272557 A CN108272557 A CN 108272557A
- Authority
- CN
- China
- Prior art keywords
- wound
- hole
- care product
- open
- cell material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供伤口处理用品1，其是在包含具有贯通孔的开孔材料的伤口处理用品中，作为能够以不堵塞贯通孔的方式对开孔材料包覆低粘合性树脂、且防止对伤口的粘结的性能也优异的伤口处理用品，包含具有贯通孔111的片状的开孔材料11、和以不堵塞贯通孔111的方式包覆开孔材料11的至少一侧的面的低粘合性树脂12，开孔材料11是由复丝形成的针织布或机织布，贯通孔111的平均开口面积为0.02～1.2mm2，平均个数为40～220/cm2。通过将开孔材料11的贯通孔111的开口面积及个数设定在特定的数值范围，可防止由于肉芽组织侵入贯通孔111引起的粘结，还可确保通过贯通孔111渗出液的充分的透过性。
Description
本申请发明是申请号为201280003313.1、发明名称为伤口处理用品、申请日为2012年3月1日的申请的分案申请。
技术领域
本发明涉及伤口处理用品。更详细地说，涉及用低粘合性树脂包覆开孔材料而成的伤口处理用品。
背景技术
为了保护烫伤、褥疮及其他皮肤损伤部位或皮肤移植部位等患部，一直以来使用用有机硅树脂形成粘合层的伤口处理用品。通过使粘合层为低粘合性的有机硅树脂，可获得不易粘结在患部的伤口处理用品。
例如，在专利文献1中公开了硅胶保留弹性网状增强物的贯通孔，并将网的全部构成要素进行密封而得的伤口处理用品。专利文献1的伤口处理用品在为了处理渗出液而并用吸收体的情况下，吸收体由伤口处理用品的贯通孔的部分露出。因此在贯通孔的部分，存在容易与创伤部的新生组织粘结的危险性。
另外，在专利文献2中提示了将空气不渗透性且体液不渗透性的开孔层材料(载体材料)的一面用硅胶进行覆膜，进而具备吸收体的伤口处理用品。专利文献2的伤口处理用品也与专利文献1的伤口处理用品同样地，由于使用的吸收体在贯通孔的部分为露出的状态，因此不能解决容易与新生组织粘结的危险性。
另一方面，在专利文献3中公开了一种伤口处理用品，其是包含具有贯通孔的开孔材料(网状织物)和在开孔材料一侧的面上配置的吸收体，在用有机硅树脂包覆开孔材料的另一侧的面的同时，对于吸收体将对应于贯通孔的位置用有机硅树脂进行包覆而得的伤口处理用品。专利文献3的伤口处理用品由于成为伤口接触面的开孔材料和吸收体双方都被有机硅树脂包覆，因此即使新生肉芽组织由开孔材料的贯通孔侵入也可防止伤口处理用品强固地附着于创面，从而可以在不对脆弱的新生表皮组织带来损伤的条件下进行伤口处理用品的去除、更换等。
现有技术文献
专利文献
专利文献1：日本特许第2525215号公报
专利文献2：日本特许3677283号公报
专利文献3：国际公开第2010/122665号
发明内容
发明要解决的课题
在伤口的治愈过程中，新生肉芽组织慢慢地向上方***，因此使用开孔材料和吸收体处置伤口的情况下，对于从开孔材料的贯通孔侵入的肉芽组织，必须考虑其对吸收体的粘结。作为防止吸收体与肉芽组织的粘结的方法，除了专利文献3所公开的技术以外，可考虑使贯通孔的孔径变小来防止肉芽组织侵入的方法。另一方面，在使开孔材料的贯通孔的孔径变小的情况下，以不堵塞开孔材料的贯通孔的方式对开孔材料包覆低粘合性树脂是困难的，有时会阻碍开孔材料的渗出液通过。
因此，本发明的目的之一是提供一种伤口处理用品，其是包含具有贯通孔的开孔材料的伤口处理用品，该伤口处理用品具有防止对伤口的粘结的性能。另外，本发明的目的之一是提供一种伤口处理用品，其是包含具有孔径小的贯通孔的开孔材料的伤口处理用品，该伤口处理用品是以不堵塞开孔材料的贯通孔的方式对开孔材料包覆低粘合性树脂而得的。
用于解决课题的方法
为了解决上述课题，本发明提供一种伤口处理用品，其包含：
具有贯通孔的开孔材料、和以不堵塞所述贯通孔的方式包覆该开孔材料的至少一侧的面的低粘合性树脂，所述开孔材料是由复丝形成的针织布或机织布，所述贯通孔的平均开口面积为0.02～1.2mm2，平均个数为40～220个/cm2。通过将开孔材料的贯通孔的开口面积及个数设定在特定的数值范围，能够防止由于肉芽组织侵入贯通孔引起的粘结。
在该伤口处理用品中，上述复丝优选由15～100根长丝构成。通过使复丝的长丝根数为特定的数值范围，在对开孔材料包覆低粘合性树脂时，能够防止由于低粘合性树脂而发生贯通孔的堵塞。
在该伤口处理用品中，上述低粘合性树脂优选仅包覆上述开孔材料的一侧的面。另外，上述低粘合性树脂优选为有机硅树脂。
发明的效果
通过本发明，可提供一种伤口处理用品，其是包含具有贯通孔的开孔材料的伤口处理用品，该伤口处理用品能够以不堵塞贯通孔而对开孔材料包覆低粘合性树脂，防止对伤口的粘结的性能也优异。
附图说明
图1是说明本发明的伤口处理用品的构成的图。
图2是说明本发明的伤口处理用品的制造方法的各工序的图。
图3是显示对通过实施例所制作的伤口处理用品处置后的创伤面的整容性进行评价的结果的附图代用照片。
具体实施方式
以下，对于用于实施本发明的优选方式进行说明。另外，以下说明的实施方式，表示本发明的代表性实施方式的一例，并不由此而狭窄地解释本发明的范围。
1.伤口处理用品
(1)开孔材料
图1是说明本发明的伤口处理用品的构成的图。(A)是上面立体图，(B)是下面立体图，(C)是对应于(A)中的P-P剖面的剖面图。
伤口处理用品1包含：具有贯通孔111的片状的开孔材料11(以下也称为“网状织物11”)、和包覆网状织物11的一面的凝胶状的低粘合性树脂12。另外，低粘合性树脂12也可以包覆网状织物11的两面。伤口处理用品1具有叠层于低粘合性树脂12的剥离片(不图示)。
伤口处理用品1优选将吸收体2和覆盖材3组合使用。具体地说，剥离剥离片后，安放伤口处理用品1使得低粘合性树脂12与皮肤损伤部位或皮肤移植部位等患部接触。为了吸收由患部透过伤口处理用品1的贯通孔111渗出的渗出液(含有血液)，将吸收体2配置在伤口处理用品1之上。吸收体2使用现有公知的材料即可。吸收体2例如可以是无纺布、针织布、机织布等纤维状材料、泡沫材料、吸收性树脂材料、吸水性粉末材料等。
覆盖材3包覆吸收体2的上面，用于发挥防止吸收体2的污染、防止由吸收体2渗出的渗出液等污染物质的脱落等功能。另外，可以在覆盖材3的一面上涂布粘合剂之后，将其以由吸收体2的外周缘延伸至外侧的方式粘贴于吸收体2(不图示)。通过将覆盖材3由吸收体2的外周缘延伸至外侧，可简便地将伤口处理用品1和吸收体2固定于患部。覆盖材3使用现有公知的材料即可。覆盖材3例如可以是无纺布、针织布、机织布、网等的纤维状片、合成树脂膜、泡沫等。在覆盖材3使用液体不透过性且水蒸气透过性的塑料膜的情况下，即使渗出液过量时也可防止渗出液由吸收体的外缘漏出，从而可将伤口保持在适度的湿润环境中，因此可实现促进伤口的治愈。
网状织物11是由复丝形成的针织布或机织布。网状织物11具有：具有上面及底面的片状的形态。伤口处理用品1通过成为基材的网状织物11使用纤维材料，由此与基材使用合成树脂膜材料的情况相比，可提高对凹凸的顺应性。通过提高对凹凸的顺应性可提高对患部的密合性，因而伤口处理用品1，即使将低粘合性树脂12的粘合力抑制得较低也不会由患部意外剥落或移动。另外，可以使低粘合性树脂12为低粘合性，由此可降低剥离伤口处理用品1时的患部的损伤。
网状织物11可采用：通过针织布的针眼形成贯通孔111的网状织物或通过针织结构(包含丝的粗细、密度等)的平衡形成贯通孔111的网状织物；或者作为机织布的经丝和纬丝之间的空隙形成贯通孔111的网状织物。该情况下，针织结构或机织结构在具有以下说明的规定的大小和数量的贯通孔111范围内，没有特别限定。另外，针织布或机织布也可以在后加工中进行物理性穿孔而形成贯通孔111。该情况下，对针织结构或机织结构没有特别限定。
网状织物11优选为通过针织布的针眼形成了贯通孔111的针织布或通过针织结构的平衡形成了贯通孔111的针织布。因为这些针织布对患部的凹凸的顺应性特别优异。
构成网状织物11的针织布或机织布的复丝优选由15～100根长丝构成，进一步优选由20～80根长丝构成。通过将构成复丝的长丝根数设定在上述数值范围，从而在将低粘合性树脂12涂布于网状织物11时，贯通孔111可以不被低粘合性树脂12堵塞(详细情况后述)。另外，在使用由上述的长丝根数构成的复丝的情况下，各长丝的直径优选为1～100μm，进一步优选为5～50μm。通过将长丝直径设定在上述数值范围，可以得到能容易地以所需的开口面积及开孔率在网状织物11上形成贯通孔的复丝。
对复丝及构成该复丝的长丝的种类，没有特别限定，可利用聚酯系纤维、丙烯酸系纤维、聚酰胺系纤维、聚氨酯系纤维、纤维素系纤维(棉、人造丝、虎木棉(polynosic)、莱塞尔(Lyocell))、聚烯烃系纤维、聚氯乙烯系纤维、聚偏1,1-二氯乙烯系纤维、玻璃纤维、碳纤维等。
网状织物11的厚度优选为50～1000μm，更优选为100～500μm。如果比50μm薄，则网状织物没有弹力而操作性差，网状织物可保持的低粘合性树脂的量也减少，因此有时产生贯通孔的堵塞。另一方面，如果比500μm厚，则产生对创伤面的顺应性、密合性的问题。
(2)贯通孔
贯通孔111的平均开口面积优选为0.02～1.2mm2，进一步优选为0.08～0.8mm2。如果贯通孔111的开口面积大于1.2mm2，则由患部再生的肉芽组织容易从贯通孔111侵入而粘结于吸收体2。另外，如果贯通孔111的平均开口面积大于1.2mm2，则再生的肉芽组织侵入贯通孔111，从而肉芽组织按照贯通孔的孔壁面的形状而形成凸凹的创面(参照后述的图3(C)(D))。由于在治愈过程中创伤面未变平坦、形成了凸凹，因而可能使伤口完全恢复要花费时间。另一方面，如果贯通孔111的平均开口面积小于0.02mm2，则从患部渗出的渗出液难以通过贯通孔111而向吸收体2移动，从而渗出液的处理功能降低。另外，如果贯通孔111的平均开口面积小于0.02mm2，则将低粘合性树脂12涂布于网状织物11时容易发生贯通孔111的堵塞(详细情况后述)。另外，贯通孔111的开口面积与贯通孔111的孔径在技术上是等价的。
另外，贯通孔111的平均个数优选为40～220个/cm2，更优选为80～200个/cm2。另外，由贯通孔111的平均开口面积和平均个数算出的网状织物11的开孔率优选为25～90％，进一步优选为30～85％。通过使平均个数及开孔率为上述的优选数值范围，与前述的贯通孔111的优选平均开口面积的范围相结合，形成通过贯通孔111的渗出液的处理能力、由防止肉芽侵入产生的非粘结性、伤口处理用品1的操作性等优异的网状织物。
对贯通孔111的配置没有特别限定，可以规则性地或无规地散布，也可以形成格子状、波状、同心圆状、螺旋状等规定图案来进行配置。贯通孔111优选设置均匀间隔来配置，使得网状织物11整体可均匀地透过渗出液。
(3)低粘合性树脂
低粘合性树脂12只要具有在患部应用并除去本发明的伤口处理用品1时不带给皮肤和/或伤口过度的刺激和/或损伤程度的粘合性即可。低粘合性树脂12包含：天然或合成而得的高分子物质和它们的多种的混合物，以及在这些高分子物质中加入其他物质而得的混合物。本发明使用的低粘合性树脂可以是疏水性、亲水性的任一种，另外，可与适当的液状物质组合，作为有机凝胶或水凝胶的方式使用。另外，还可与亲水性高分子化合物混合，作为所谓的水胶体的形态使用。作为低粘合性树脂，特别优选以疏水性树脂为主成分的低粘合性树脂，特别优选以疏水性凝胶的形态使用。作为疏水性树脂，只要选择由该树脂形成的层的表面与水的接触角为65°以上的树脂即可，可举出例如选自有机硅树脂、丙烯酸树脂、甲基丙烯酸树脂、聚氯乙烯树脂、聚偏1,1-二氯乙烯树脂(即，聚偏二氯乙烯树脂)、氟树脂、烯烃树脂、聚酯树脂、苯乙烯树脂、聚氨酯树脂、聚酰胺树脂及它们的混合物中的1种以上。这些低粘合性树脂中，特别优选操作简便、且不易对患部产生粘结的有机硅树脂。有机硅树脂特别优选通过交联等固化为凝胶状。对有机硅树脂的固化方法，没有特别限定，可通过加热等容易地使其交联。
有机硅树脂，可使用加成反应型、过氧化反应型或缩合反应型的任一种，优选加成反应型的有机硅树脂。有机硅树脂可以单独使用一种，也可以二种以上组合使用。
加成反应型有机硅树脂，是使用氯铂酸等铂化合物催化剂，使具有与硅原子结合的烯基的有机聚硅氧烷(含烯基的有机聚硅氧烷)和具有氢化硅烷基(Si-H)的有机聚硅氧烷(氢化有机聚硅氧烷)进行加成反应(氢化硅烷化反应)而得的。对于加成反应型有机硅树脂，可通过改变其合成中使用的有机氢化聚硅氧烷的量和/或有机氢化聚硅氧烷分子内的氢化硅烷基(Si-H)的量，来调整交联密度。由此，可容易地调整有机硅树脂的硬度和/或粘合力。作为加成反应型有机硅树脂，优选为乙烯基取代聚二甲基硅氧烷与有机氢化聚硅氧烷的加成反应生成物。
另外，在不损害本发明的目的的程度内，可以进一步在有机硅树脂中适当配合药剂、吸水性高分子化合物、pH值调节剂等其他调整剂。
作为药剂的例子，可显示为了保湿、抗老化、美白等而调整皮肤的生理功能的物质、促进伤口的治愈的物质、具有抗菌性的物质等。作为其具体例，可举出鞘脂、尿素、乙醇酸、氨基酸及其衍生物(精氨酸、半胱氨酸、甘氨酸、赖氨酸、脯氨酸、丝氨酸等)、蛋白质水解产物(胶原、弹性蛋白、角蛋白等)、粘多糖及其衍生物(透明质酸、硫酸软骨素、肝素等)、B族维生素(硫胺素、核黄素、烟酸、吡哆素、吡哆醛、吡哆胺、生物素、叶酸、氰钴胺素等)、抗坏血酸(维生素C及其衍生物)、视黄醇类(维生素A、视黄醛、视黄酸等)、维生素D(D2、D3等)、维生素E及其衍生物、类胡萝卜素(胡萝卜素、番茄红素、叶黄素等)、酶、辅酶、γ-谷维素等，特别优选鞘脂。作为鞘脂，优选鞘氨醇与脂肪酸结合而成的神经酰胺、神经酰胺与糖结合而成的鞘糖脂。神经酰胺可使用天然、合成的任一种，可举出1～7型的神经酰胺，特别优选2、5、7型的神经酰胺。作为鞘糖脂，优选脑苷脂、半乳糖神经酰胺、葡萄糖神经酰胺等。作为吸水性高分子化合物、pH值调节剂可使用公知的物质。
低粘合性树脂12优选仅包覆网状织物11的伤口接触面。即，在具有上面及底面的网状织物11中，优选仅将其一面用低粘合性树脂12包覆。如果用低粘合性树脂12包覆网状织物11的两面，则把持伤口处理用品1时粘住手指、和/或粘合面彼此粘住，对患部粘贴时及更换时的操作变得繁杂。
如以上那样，伤口处理用品1，通过将网状织物11的贯通孔111的开口面积、个数及开孔率设定在特定的数值范围，从而在防止由于肉芽组织侵入贯通孔111而引起的粘结、使创面彻底恢复(提高整容性)的同时，也充分确保通过贯通孔111的渗出液的处理能力。因此，利用伤口处理用品1，剥离时不发生患部的损伤和/或疼痛、出血，还可防止由渗出液引起的患部及其浸软的浸软，从而促进患部的良好的治愈。
进而，伤口处理用品1，通过将构成网状织物11的针织布或机织布的复丝的长丝根数及网状织物11的贯通孔111的开口面积设定在特定的数值范围，可以利用下面说明的简便的制造方法在不发生贯通孔111的堵塞的条件下进行制造。
2.伤口处理用品的制造方法
本发明的伤口处理用品的制造方法，包括利用转印涂布将低粘合性树脂12涂布于上述的网状织物11的工序。更具体地说，该制造方法包括以下工序：将规定量的低粘合性树脂的涂布液涂布于剥离转印用基材的第一工序；将网状织物11叠放于转印用基材并使网状织物11吸收涂布液的第二工序；和使低粘合性树脂固化的第三工序。进而，可以在第三工序之后，包括以下工序：由网状织物11剥离转印用基材的第四工序；用剥离片包覆固化的低粘合性树脂12表面的第五工序。参照图2对于各工序依次进行说明。
[第一工序]
首先，将规定量的低粘合性树脂的涂布液121涂布于转印用基材4(参照图2(A))。转印用基材4可使用经硅氧烷系或氟系的剥离剂处理的剥离纸、剥离膜、或聚碳酸酯、聚乙烯醇、塞璐玢、聚氨酯等的膜。
[第二工序]
接着，将涂布了涂布液121的转印用基材4与网状织物11叠合。由此，使作为由复丝所形成的针织布或机织布的网状织物11吸收涂布液121(参照图2(B))。此时，通过使构成网状织物11的复丝的长丝根数为上述数值范围，可将网状织物11中的涂布液121的吸收量设定为适当的量。即，可以在涂布液121被构成网状织物11的复丝吸收的同时，以不堵塞贯通孔111的方式包覆网状织物11的一面侧。
[第三工序]
使网状织物11吸收涂布液121后，在将网状织物11和转印用基材4叠合的状态下加热并使低粘合性树脂固化。
[第四工序]
低粘合性树脂固化后，通过由网状织物11剥离转印用基材4，得到网状织物11被低粘合性树脂12包覆的伤口处理用品1(参照图2(C))。另外，第二工序中即使涂布液121残留在转印用基材4上，也会在对应于转印用基材4的贯通孔111的位置固化而直接与转印用基材4一同被去除(不图示)。因此，得到的伤口处理用品1被低粘合性树脂12堵塞贯通孔111的情况少，大部分的贯通孔111维持开口状态。
[第五工序]
使低粘合性树脂固化，由网状织物11剥离转印用基材4后，为了保护固化的低粘合性树脂12的表面，用剥离片5来包覆(参照图2(D))。
第二工序中的网状织物11中的涂布液121的吸收量，可通过构成网状织物11复丝的长丝根数来控制。在长丝根数过多的情况下，网状织物11的涂布液121的吸收量变得过多，涂布液121被吸收到网状织物11的内部而不残留于表面，因此不能用低粘合性树脂12来包覆网状织物11。网状织物11的表面未被低粘合性树脂12包覆的情况下，伤口处理用品1容易粘结于创伤面。
另一方面，在长丝根数过少的情况下，网状织物11的涂布液121的吸收量变得过小，涂布液121在对应于转印用基材4上的贯通孔111的位置大量残留。如果残留的大量的涂布液121在第三工序中固化，则会堵塞贯通孔111。如果贯通孔111被低粘合性树脂12堵塞，则通过贯通孔111的渗出液的透过性降低。
另外，在网状织物11的贯通孔111的开口面积过小的情况下，也容易发生由残留于转印用基材4上的涂布液121而引起的贯通孔111的堵塞。在伤口处理用品1中，通过将贯通孔111的开口面积设定在上述的数值范围，也可抑制该堵塞的发生。
在本发明的制造方法中，将复丝的长丝根数设定在特定的数值范围，从而将网状织物11中的涂布液121的吸收量设定为适当的量。因此，在本发明的制造方法中，即使不在第一工序中严密地调整涂布于转印用基材4的涂布液121的量，也可在第三工序及第四工序中以不堵塞贯通孔111的方式通过低粘合性树脂12来包覆网状织物11的表面。另外，对于网状织物11的贯通孔111的开口面积，也设定成即使不严密地调整第一工序中的涂布液121的量，在第三工序及第四工序中也不发生贯通孔111的堵塞那样的大小。因此，本发明的制造方法可得到对渗出液具有高透过性、且不易粘结于患部的伤口处理用品1。
进而，在本发明的制造方法中，通过湿法复合(wet lamination)来进行低粘合性树脂12的包覆，从而与浸渍(浸渍涂布)不同，可仅在网状织物11的一面进行低粘合性树脂12的包覆。另外，在本发明的制造方法中，像直接涂布那样不发生涂布液121的透墨，因此使粘合性树脂12仅包覆网状织物11的一面是容易的。
实施例
以下，基于实施例更详细地说明本发明，但本发明并不限定于这些实施例。关于本发明的伤口处理用品的特性，通过以下的方法来测定。
[开孔材料的贯通孔平均开口面积(单位：mm2)]
用显微镜由垂直方向(与开孔材料的平面正交的方向)来观察开孔材料的平面，测定5个贯通孔的面积，求其平均值。
[开孔材料的贯通孔的平均个数(单位：个/cm2)]
用显微镜由垂直方向观察开孔材料的平面，数出在一定面积内有多少个孔存在，将其值换算为每1cm2的个数来求出。
[开孔材料的开孔率(单位：％)]
用显微镜由垂直方向观察开孔材料的平面，数出在一定面积内有多少个孔存在，并基于上述算出的开口面积的平均值来求出。
[开孔材料的厚度(单位：mm)]
依据JIS L 1096“一般织物试验方法”，测定包覆低粘合性树脂之前的厚度。
[构成复丝的长丝直径(单位：μm)]
由复丝中取出构成该复丝的长丝，以显微镜来观察，测定5根长丝的直径，求其平均值。
〈实施例1〉
根据上述的制造方法制作伤口处理用品。具体如下。
将以乙烯基取代聚二甲基硅氧烷、有机氢化聚硅氧烷及铂催化剂作为主体的双组分型的加成反应型有机硅树脂(ダゥコ一ニング社(Dow CorningCorporation)制，商品名“D〇W CORNING 7-9800”)混合，将得到的混合液以一定的厚度涂布于氟硅氧烷处理的转印用基材。接着，在涂布的有机硅树脂上，供给包含由聚酯制的复丝形成的针织布的开孔材料，将有机硅树脂涂布面与开孔材料叠合。该开孔材料的贯通孔的平均开口面积为0.22mm2，贯通孔的平均个数为155个/cm2，开孔率为35％，厚度为330μm。另外，构成针织布的复丝的长丝根数为36根，各个长丝直径为12μm。其后，在110℃加热2分钟，使有机硅树脂固化后，剥离转印用基材，以硅氧烷剥离片包覆固化的有机硅树脂表面，得到伤口处理用品。
〈实施例2〉
除了将贯通孔的平均开口面积、平均个数、开孔率、开孔材料的厚度及复丝的长丝根数变更为“表1”所示那样以外，通过与实施例1同样的方法得到伤口处理用品。
〈实施例3〉
除了将贯通孔的平均开口面积、平均个数、开孔率、厚度及复丝的长丝根数及长丝直径变更为“表1”所示那样以外，通过与实施例1同样的方法得到伤口处理用品。
〈比较例1〉
使用贯通孔的平均开口面积和平均个数与本发明不同的开孔材料来得到伤口处理用品。构成开孔材料的针织布，使用由尼龙制的复丝形成的针织布。
〈比较例2〉
使用贯通孔的平均个数和复丝的长丝根数与本发明不同的开孔材料来得到伤口处理用品。
〈比较例3〉
使用贯通孔的平均开口面积、平均个数、开孔率、厚度与本发明不同的开孔材料来得到伤口处理用品。开孔材料使用聚氨酯开孔膜。
对于通过上述的实施例和比较例得到的伤口处理用品，评价以下的项目。
[贯通孔的堵塞]
评价开孔材料的贯通孔是否被涂布的有机硅树脂堵塞。
[创伤面的肉芽的整容性]
在6周龄的雄性SD大鼠的左侧腹部制作直径3cm的全层皮肤缺损层。在制作的伤部包覆已灭菌的伤口处理用品，从其上缠绕弹性绷带并进行固定。从制作伤口起9天后，从伤口部剥离伤口处理用品，观察其创伤面的状况，评价整容性(凸凹的有无)。
将评价结果示于“表1”及图3。另外，图3(A)～(D)是用实施例1、实施例2、比较例1及比较例3的伤口处理用品处置后的创伤面的照片。
表1
对于比较例1、3的伤口处理用品，在创伤面沿着开孔材料的形状产生凹凸，与实施例1、2的伤口处理用品相比整容性差。另外，对于比较例2的伤口处理用品，开孔材料的贯通孔的一部分被有机硅树脂塞住而堵塞，不满足作为伤口处理用品的基本功能。
另一方面，对于实施例中得到的伤口处理用品，不发生开孔材料的堵塞，没有创伤与伤口处理用品的粘结，进而创伤面也不产生凹凸而平坦地治愈。
产业可利用性
本发明的伤口处理用品，不发生剥离时的患部的损伤和/或疼痛、出血，还可防止由于渗出液而浸软患部及其周围，从而可以促进患部的良好的治愈。因此，本发明的伤口处理用品，适合用于保护、治疗烫伤、褥疮及其他的皮肤损伤部位或皮肤移植部位等患部。
Claims (3)
1.一种伤口处理用品，其包含：
具有贯通孔的开孔材料、和
以不堵塞所述贯通孔的方式仅包覆该开孔材料的伤口接触面的低粘合性树脂，
并且，该伤口处理用品不包含吸收体，
所述开孔材料是由复丝形成的针织布或机织布，
所述贯通孔的平均开口面积为0.02～1.2mm2，平均个数为40～220个/cm2，
所述复丝由15～100根长丝构成，
构成所述复丝的长丝的直径为1～100μm。
2.根据权利要求1所述的伤口处理用品，其中，所述复丝从聚酯系纤维、丙烯酸系纤维、聚酰胺系纤维、聚氨酯系纤维、纤维素系纤维、聚烯烃系纤维、聚氯乙烯系纤维、聚偏1,1-二氯乙烯系纤维、玻璃纤维、碳纤维和它们的组合中选择。
3.根据权利要求1或2所述的伤口处理用品，其中，所述低粘合性树脂为有机硅树脂。