CN108236922B - Double-pyrazole functionalized lead imprinting FDU-12 material, and preparation method and application thereof - Google Patents
Double-pyrazole functionalized lead imprinting FDU-12 material, and preparation method and application thereof Download PDFInfo
- Publication number
- CN108236922B CN108236922B CN201611206962.8A CN201611206962A CN108236922B CN 108236922 B CN108236922 B CN 108236922B CN 201611206962 A CN201611206962 A CN 201611206962A CN 108236922 B CN108236922 B CN 108236922B
- Authority
- CN
- China
- Prior art keywords
- lead
- iims
- dpp
- fdu
- mcm
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a double-pyrazole functionalized lead print FDU-12 material, and a preparation method and application thereof. The preparation method comprises the following steps: adding TEPIC into a mixture of DPP lead complex, alkali and tetrahydrofuran, heating and refluxing, vacuumizing to dry a solvent, then adding toluene and a mesoporous material FDU-12, reacting, and washing with acid to remove lead. The double-pyrazole functionalized lead print FDU-12 material has the advantages of high selective adsorption on lead ions, strong anti-interference capability on coexisting ions, strong regeneration capability, high detection sensitivity, good precision and high detection efficiency.
Description
Technical Field
The invention relates to the field of mesoporous materials, in particular to a double-pyrazole functionalized lead print FDU-12 material, and a preparation method and application thereof.
Background
Lead is a heavy metal element which seriously threatens the physiological health of human bodies and has serious harm to the digestive system and the nervous central system of organisms, particularly to the liver and the urinary system. The toxicity of lead to human bodies is cumulative, and lead can be enriched in the food chain through polluted water products and crops, thus causing harm to human bodies. Therefore, the enrichment and separation of trace lead elements in water are indispensable links for treating and analyzing lead-containing wastewater, and are receiving wide attention.
The Ion Imprinting Technology (IIT) is a new technology developed on the basis of the molecular imprinting technology, which integrates the advantages of many subjects in recent years. The Ion Imprinted Polymer (IIP) formed by the IIT has the characteristics of high predetermination, strong identification, wide applicability and the like. The synthesis of IIP typically comprises 3 steps: (1) preparing a monomer-metal complex; (2) carrying out a polymerization reaction on the complex; (3) removing template ions by adopting a proper method to obtain a three-dimensional recognition site. At present, functional monomers such as methacrylic acid, 4-vinylpyridine, chitosan, organosilane, amine and the like are used for preparing the lead ion imprinted polymer. The amino-functionalized lead ion imprinted polymer has very good enrichment and separation effects. However, amine-functionalized lead ion imprinted polymers have the disadvantage of poor chemical stability due to the tendency of amine groups to oxidize. Therefore, the development of a lead ion imprinting system capable of replacing a novel functional monomer is of great significance.
The mesoporous silica material is a research hotspot in recent years, and has the advantages of large specific surface, high orderliness, single pore size distribution, easy surface modification and the like. At present, considerable attention has been paid to the application of mesoporous silica materials as solid extraction materials in the enrichment and separation of heavy metals, and researches show that the functional modification of the mesoporous silica materials can increase the separation efficiency of the heavy metals. He et al reports an amino acid modified lead ion imprinted SBA-15 type mesoporous silica material for selectively removing lead ions. Liu et al reports a chitosan modified lead ion imprinted SBA-15 type mesoporous silica material applied to selective adsorption of lead ions in an aqueous solution. Therefore, selective enrichment and separation of lead ions are realized by optimally designing the ion imprinting point position on the surface of the mesoporous silica material, and the method has important significance for detecting trace lead ions in a complex matrix.
Disclosure of Invention
The invention aims to solve the technical problems of weak adsorption stability of an adsorption material, weak selective adsorption on Pb (II), weak anti-interference capability on coexisting ions and poor material regeneration capability in the prior art, and provides a double-pyrazole functionalized lead imprint FDU-12 material, a preparation method and application thereof. The double-pyrazole functionalized lead print FDU-12 material has the advantages of high selective adsorption on lead ions, strong anti-interference capability on coexisting ions, strong regeneration capability, high detection sensitivity, good precision and high detection efficiency.
The invention solves the technical problems through the following technical scheme:
the invention provides a preparation method of a double-pyrazole functionalized lead print FDU-12 material, which comprises the following steps: adding TEPIC into a mixture of DPP lead complex, alkali and tetrahydrofuran, heating and refluxing, vacuumizing to dry a solvent, then adding toluene and a mesoporous material FDU-12, reacting, and washing with acid to remove lead;
the DPP is 4- (di (1H-pyrazol-1-yl) methyl) phenol and the TEPIC is 3-triethoxysilyl-propyl-isocyanate.
As is clear to one skilled in the art, DPP is 4- (di (1H-pyrazol-1-yl) methyl) phenol having the chemical formula
It will be clear to one skilled in the art that TEPIC is 3-triethoxysilyl-propyl-isocyanate having the chemical formula
It is clear to those skilled in the art that FDU-12 refers to a mesoporous material conventionally used in the art. The mesoporous material FDU-12 is purchased from Nanjing Xiancheng nanometer material science and technology Co.
Wherein the base is preferably K2CO3Triethylamine and Na2CO3One ofOr more, preferably K2CO3. Said K2CO3Preferably dehydration K2CO3。
Wherein, the molar ratio of the DPP lead complex to the alkali is preferably 1: 1-1.2, more preferably 1: 1.
wherein, the molar ratio of the DPP lead complex to the TEPIC is preferably 1: 1-1.2, more preferably 1: 1.
the molar mass ratio of the DPP lead complex to the mesoporous material is preferably 1mmol:0.95 g-1.00 g, more preferably 1mmol:0.97 g-0.98 g.
Wherein the temperature of the heating reflux is preferably 60-70 ℃, and the time of the heating reflux is preferably 9-13 hours.
Wherein the reaction temperature is preferably 105-115 ℃, and the reaction time is preferably 47-49 hours.
In the present invention, after the completion of the reaction and before washing with an acid to remove lead, it is preferable to further perform a post-treatment. The post-treatment is preferably filtration, and the obtained solid is washed with dichloromethane, distilled water, ethanol and ethyl acetate in sequence and dried.
Wherein the acid is preferably hydrochloric acid and/or nitric acid, more preferably hydrochloric acid; the molar concentration of the acid is preferably 3 mol/L.
Similarly, the invention also provides a preparation method of the double-pyrazole functionalized lead print SBA-15 material, which comprises the following steps: adding TEPIC into a mixture of DPP lead complex, alkali and tetrahydrofuran, heating and refluxing, vacuumizing to dry a solvent, then adding toluene and a mesoporous material SBA-15, reacting, and then washing with acid to remove lead;
the DPP is 4- (di (1H-pyrazol-1-yl) methyl) phenol and the TEPIC is 3-triethoxysilyl-propyl-isocyanate.
The preferable reaction conditions are the same as the preparation method of the double-pyrazole functionalized lead-printed FDU-12 material.
Similarly, the invention also provides a preparation method of the double-pyrazole functionalized lead print MCM-41 material, which comprises the following steps: adding TEPIC into a mixture of DPP lead complex, alkali and tetrahydrofuran, heating and refluxing, vacuumizing to dry a solvent, then adding toluene and a mesoporous material MCM-41, reacting, and washing with acid to remove lead;
the DPP is 4- (di (1H-pyrazol-1-yl) methyl) phenol and the TEPIC is 3-triethoxysilyl-propyl-isocyanate.
The preferable reaction conditions are the same as the preparation method of the double-pyrazole functionalized lead-printed FDU-12 material.
Wherein, the DPP lead complex is prepared by the following preparation method preferably: mixing DPP and lead compound in methanol and/or ethanol for reaction.
Wherein the lead compound is used as an imprinted metal ion template to participate in the reaction, and the lead compound is preferably lead nitrate (Pb (NO)3)2)。
Wherein the reaction temperature is preferably 10-30 ℃, namely the reaction can be completed at room temperature.
Wherein the reaction time is preferably 4 to 6 hours.
Wherein the molar ratio of DPP to lead compound is preferably 1: (0.5-0.6).
The invention also provides a double-pyrazole functionalized lead imprint MCM-41 material, a double-pyrazole functionalized lead imprint SBA-15 material or a double-pyrazole functionalized lead imprint FDU-12 material which are respectively prepared by the preparation method.
The double-pyrazole functionalized lead print MCM-41 material prepared by the method is marked as Pb-IIMS-MCM-41.
The double-pyrazole functionalized lead print SBA-15 material prepared by the invention is marked as Pb-IIMS-SBA-15.
The double-pyrazole functionalized lead printing FDU-12 material prepared by the invention is marked as Pb-IIMS-FDU-12.
The invention also provides application of the double-pyrazole functionalized lead imprint MCM-41 material in adsorption and/or detection of metallic lead.
The invention also provides application of the double-pyrazole functionalized lead print SBA-15 material in adsorption and/or detection of metal lead.
The invention also provides application of the double-pyrazole functionalized lead print FDU-12 material in adsorption and/or detection of metallic lead.
Wherein, the lead is preferably divalent lead.
In the present invention, the divalent lead is Pb (II).
On the basis of the common knowledge in the field, the above preferred conditions can be combined randomly to obtain the preferred embodiments of the invention.
The reagents and starting materials used in the present invention are commercially available.
The positive progress effects of the invention are as follows: the invention successfully prepares three novel adsorbents based on different mesoporous silica SBA-15, MCM-41 and FDU-12, Pb (II) ions serving as templates and DPP (dipeptidyl peptidase) serving as a functional monomer, and all three adsorbent materials are found to have good chemical stability, quite large adsorption capacity and high selectivity. The adsorption behavior of the synthetic adsorbent to Pb (II) accords with a quasi-second-order model, and the adsorption process is chemical adsorption. The sorption isotherm data more closely followed the Langmuir model of single layer coverage of the recommended sorbent material pb (ii). Furthermore, these ion imprinted adsorbents do show improved selectivity compared to the corresponding non-imprinted adsorbent materials. In addition, Pb-IIMS-MCM-41 performed best in terms of adsorption capacity, adsorption equilibrium time, selectivity, and reusability of the three adsorbent materials. The maximum adsorption capacity of Pb-IIMS-MCM-41 obtained from the Langmuir model was 344.8mg g-1Higher than most reported adsorbents. Finally, compared with other two adsorbing materials, the Pb-IIMS-MCM-41 is more successful and more effective in separating and determining Pb (II) in an actual water sample.
Drawings
FIG. 1 is a Fourier infrared spectrum of a product, wherein (a) is a Fourier infrared spectrum of DPP, (b) is a Fourier infrared spectrum of Pb-IIMS-SBA-15, (c) is a Fourier infrared spectrum of Pb-IIMS-MCM-41, and (d) is a Fourier infrared spectrum of Pb-IIMS-FDU-12.
FIG. 2(a) is a drawingSolid-state lead-marking materials Pb-IIMS-SBA-15, Pb-IIMS-MCM-41 and Pb-IIMS-FDU-1229Si NMR spectrogram, FIG. 2(b) is a solid state of three lead imprinted materials Pb-IIMS-SBA-15, Pb-IIMS-MCM-41 and Pb-IIMS-FDU-1213C NMR spectrum chart.
FIG. 3 is an SEM micrograph of three lead imprinted materials Pb-IIMS-SBA-15(a), Pb-IIMS-MCM-41(b), Pb-IIMS-FDU-12 (c).
FIG. 4 shows three lead imprinting materials Pb-IIMS-SBA-15[ (a)1) And (a)2)]、Pb-IIMS-MCM-41[(b1) And (b)2)]、Pb-IIMS-FDU-12[(c1) And (c)2)]SEM micrograph of (a).
FIG. 5 is an EDX spectrum of three lead imprinting materials Pb-IIMS-SBA-15(a), Pb-IIMS-MCM-41(b) and Pb-IIMS-FDU-12 (c).
FIG. 6 shows N of three lead-printed materials Pb-IIMS-SBA-15(a), Pb-IIMS-MCM-41(b) and Pb-IIMS-FDU-12(c)2Adsorption-desorption isotherms and pore size profiles.
FIG. 7 is a small angle XRD pattern of three lead imprinted materials Pb-IIMS-SBA-15(a), Pb-IIMS-MCM-41(b) and Pb-IIMS-FDU-12 (c).
FIG. 8 is a graph showing the relationship between the extraction efficiency of three lead imprinting materials Pb-IIMS-SBA-15, Pb-IIMS-MCM-41 and Pb-IIMS-FDU-12 for Pb (II) and the pH value of the solution.
FIG. 9(a) is the adsorption isotherms of the three lead imprinting materials Pb-IIMS-SBA-15, Pb-IIMS-MCM-41 and Pb-IIMS-FDU-12 with different initial concentrations of Pb (II); FIG. 9(b) is the adsorption isotherms of three non-lead-printed materials DPP @ SBA-15, DPP @ MCM-41, DPP @ FDU-12 at different initial concentrations of Pb (II); FIG. 9(c) is a graph showing the effect of contact time on three lead print materials, Pb-IIMS-SBA-15, Pb-IIMS-MCM-41, and Pb-IIMS-FDU-12.
FIG. 10 is a selectivity plot of lead trace material Pb-IIMS-SBA-15 and non-imprinted material DPP @ SBA-15(a), lead trace material Pb-IIMS-MCM-41 and non-imprinted material DPP @ MCM-41(b), lead trace material Pb-IIMS-FDU-12 and non-imprinted material DPP @ FDU-12 (c).
FIG. 11 is a diagram of lead imprint material Pb-IIMS-MCM-41 reusability.
Detailed Description
The invention is further illustrated by the following examples, which are not intended to limit the scope of the invention. The experimental methods without specifying specific conditions in the following examples were selected according to the conventional methods and conditions, or according to the commercial instructions.
The detection instrument of the invention comprises the following instruments:
CDCl using Bruker spectrometer3At 400MHz of (1H) And 100MHz of (13C) The procedure was performed to measure the NMR spectrum. Solid state using a Bruker AV-400 spectrometer at 100.6MHz13C and29analysis of Fourier transform Infrared (FT-IR) spectra in KBr on Nicolet AVATAR-360IR Transmission Electron Microscopy (TEM) image testing using Bruker D4 powder X-ray scattering measurement of small angle X-ray scattering (SAXS) using Cu K α radiation (45kV, 650 mA). Transmission Electron Microscopy (TEM) image testing using JEM2010 electron microscope at 200kV Transmission Electron Microscopy (TEM) image testing was performed.
The method synthesizes a double-pyrazole functionalized lead print MCM-41 material (marked as Pb-IIMS-MCM-41), a double-pyrazole functionalized lead print SBA-15 material (marked as Pb-IIMS-SBA-15) and a double-pyrazole functionalized lead print FDU-12 material (marked as Pb-IIMS-FDU-12) respectively according to the following routes. DPP is synthesized by adding pyrazole, 4-hydroxybenzaldehyde and NaH to THF, which is then chelated with Pb (II) to give DPP lead complex. The resulting complex was crosslinked with three mesoporous silicas by using TEPIC. Crosslinking reaction occurs between the phenolic hydroxyl group of DPP and isocyanate of TEPIC, and then the DPP is grafted on the mesoporous silica through mesoporous Si-OH. And then removing the chelated Pb (II) by HCl to obtain the Pb (II) ion imprinted mesoporous silica material adsorbent.
The DPP is synthesized by the following method:
pure pyrazole (2.00g, 29.4mmol) was added to NaH (0.71g, 29.6mmol), stirred in THF for 30 min, then SOCl was added2(1.07mL, 1.75g, 14.7 mmol). After stirring for 5 min, 4-hydroxybenzaldehyde (1.8g, 14.7mmol), pyridine (11.88mL, 11.64g, 147.2mmol) were added and the resulting cloudy reaction mixture was heated (70 ℃ C.) to reflux overnight. Distilled water (50mL) was added and the aqueous phase was extracted to CH2Cl2(3 × 50 mL.) the combined organic extracts were washed with brine, over MgSO4Drying, filtering and then evaporating the filtrate to dryness in vacuo. The crude oily product was dissolved in EtOAc and the solution was evaporated to dryness to remove residual pyridine. The insoluble brown solid was isolated by filtration and dried under a dynamic vacuum. Recrystallization then gives DPP (4- (bis (1H-pyrazol-1-yl) methyl) phenol) as a pale yellow powder. Yield: 1.8g (51%).
The nuclear magnetic data are as follows:1H NMR(400MHz,CD3OD,ppm):6.39-6.40(m,2H),6.80-6.82(d,2H),6.91-6.93(d,2H),7.62-7.63(m,4H),7.78(s,1H)。
the invention adopts the following method to synthesize DPP lead complex:
in a 250mL Erlenmeyer flask, 2mmol of DPP were dissolved in 50mL of methanol. Subsequently, 1mmol of Pb (NO) as the imprinted metal ion (template)3)2Slowly added to the glass flask and the resulting mixture stirred at room temperature for 5 hours. After filtration and drying, a pale yellow powder was obtained, which was the DPP lead complex (654mg, 95%).
The nuclear magnetic data are as follows:1H NMR(400MHz,CD3OD,ppm):6.39-6.4(m,2H),6.8-6.82(d,2H),6.91-6.93(d,2H),7.62-7.63(m,4H),7.78(s,1H),13C-NMR(400MHz,CDCl3,ppm):77.11,106.05,115.20,126.44,128.43,130.04,140.30,158.30。
example 1
Synthesis of bispyrazole functionalized lead print MCM-41 material (namely Pb-IIMS-MCM-41)
1mmol of lead complex (0.811g) was dissolved in 80mL of tetrahydrofuran with stirring, and 1mmol of anhydrous K was added to the solution2CO3(0.138 g). After two hours, 1mmol (0.247g) of TEPIC was added dropwise to the solution. The entire mixture was heated at 65 ℃ under reflux for 12 hours and the solvent was dried under vacuum. The resulting solid was dissolved in 20mL of toluene, and 973mg of MCM-41 was added and heated at 110 ℃ under reflux for 48 hours. After filtration and vacuum drying, the obtained solid was repeatedly washed with dichloromethane, distilled water, ethanol and ethyl acetate, and then dried to obtain a white solid substance. 10mL of 3mol L of the imprinted material per 5mg of Pb (II) ion-1The HCl washes to elute the template lead. After drying, obtaining the Pb (II) ion imprinted mesoporous silica material, namely Pb-IIMS-MCM-41.
Will not have water K2CO3Replacing triethylamine, and repeating the steps to obtain Pb-IIMS-MCM-41.
Preparation of Bispyrazole functionalized MCM-41 material (i.e., DPP @ MCM-41 material): 1mmol of DPP are dissolved in tetrahydrofuran and 1mmol of anhydroK is added to the solution2CO3. After 2 hours, 1mmol of TEPIC was added dropwise to the reaction mixture. The whole mixture was refluxed at 65 ℃ for 12 hours, and then MCM-41(590mg) was added. And (3) draining the solvent under vacuum, repeatedly washing the obtained solid with dichloromethane, and drying to obtain a white solid substance, namely DPP @ MCM-41.
Example 2
Synthesis of double-pyrazole functionalized lead-marked SBA-15 material (namely Pb-IIMS-SBA-15)
1mmol of lead complex (0.811g) was dissolved in 80mL of tetrahydrofuran with stirring, and 1mmol of anhydrous K was added to the solution2CO3(0.138 g). After two hours, 1mmol (0.247g) of TEPIC was added dropwise to the solution. The entire mixture was heated at 65 ℃ under reflux for 12 hours and the solvent was dried under vacuum. The resulting solid was dissolved in 20mL of toluene, and 973mg of SBA-15 was added and heated at 110 ℃ under reflux for 48 hours. After filtration and vacuum drying, the obtained solid was repeatedly washed with dichloromethane, distilled water, ethanol and ethyl acetate, and then dried to obtain a white solid substance. 10mL of 3mol L of the imprinted material per 5mg of Pb (II) ion-1The HCl washes to elute the template lead. After drying, a Pb (II) ion print is obtainedTrace mesoporous silica material, namely Pb-IIMS-SBA-15.
Will not have water K2CO3The above procedure was repeated with replacement of triethylamine to obtain Pb-IIMS-SBA-15 in the same manner.
Preparation of DPP @ SBA-15 Material: 1mmol of DPP are dissolved in tetrahydrofuran and 1mmol of anhydroK is added to the solution2CO3. After 2 hours, 1mmol of TEPIC was added dropwise to the reaction mixture. The whole mixture was refluxed at 65 ℃ for 10 hours, then SBA-15(590mg) was added. The solvent is drained under vacuum, and then the obtained solid is repeatedly washed with dichloromethane and dried to obtain a white solid substance, namely DPP @ SBA-15.
Example 3
Synthesis of double-pyrazole functionalized lead-imprinted FDU-12 material (namely Pb-IIMS-FDU-12)
1mmol of lead complex (0.811g) was dissolved in 80mL of tetrahydrofuran with stirring, and 1mmol of anhydrous K was added to the solution2CO3(0.138 g). After two hours, 1mmol (0.247g) of TEPIC was added dropwise to the solution. The entire mixture was heated at 65 ℃ under reflux for 12 hours and the solvent was dried under vacuum. The resulting solid was dissolved in 20mL of toluene, and 973mg of FDU-12 was added and heated at 110 ℃ under reflux for 48 hours. After filtration and vacuum drying, the obtained solid was repeatedly washed with dichloromethane, distilled water, ethanol and ethyl acetate, and then dried to obtain a white solid substance. 10mL of 3mol L of the imprinted material per 5mg of Pb (II) ion-1The HCl washes to elute the template lead. And drying to obtain the Pb (II) ion imprinted mesoporous silica material, namely Pb-IIMS-FDU-12.
Will not have water K2CO3The above procedure was repeated with replacement of triethylamine to obtain Pb-IIMS-FDU-12 in the same manner.
Preparation of DPP @ FDU-12 Material: 1mmol of DPP are dissolved in tetrahydrofuran and 1mmol of anhydroK is added to the solution2CO3. After 2 hours, 1mmol of TEPIC was added dropwise to the reaction mixture. The whole mixture was refluxed at 65 ℃ for 10 hours, and then FDU-12(590mg) was added. The solvent was drained under vacuum, and the resulting solid was washed repeatedly with dichloromethane and driedObtaining a white solid substance, namely DPP @ FDU-12.
In the following effect examples, NIMS refers to the three non-imprinted mesoporous materials DPP @ SBA-15, DPP @ MCM-41 and DPP @ FDU-12.
Effect example 1
The synthesized Pb-IIMS-MCM-41, Pb-IIMS-SBA-15 and Pb-IIMS-FDU-12 were subjected to product analysis, and the results were as follows:
FIG. 1 shows Fourier transform infrared spectra of DPP and Pb-IIMS-MCM-41, Pb-IIMS-SBA-15, Pb-IIMS-FDU-12. All Pb-IIMS can be seen at 1636cm-1And the stretching vibration of the Si-OH on the surfaces of the SBA-15, the MCM-41 and the FDU-12 is avoided. At 1088, 803, 465cm-1The side bands are caused by stretching and bending vibrations of SBA-15, MCM-41, FDU-12, respectively. In addition, 2936cm-1The nearby absorption band is due to C-H stretching vibration of organic group, we can be from 1523cm-1A low intensity band of C ═ N bending vibration in pyrazole was observed in the nearby inset. These spectra preliminarily confirmed that Pb-IIMS-SBA-15, Pb-IIMS-MCM-41, Pb-IIMS-FDU-12 had been prepared.
FIG. 2 shows the solid state of three materials, Pb-IIMS-MCM-41, Pb-IIMS-SBA-15, Pb-IIMS-FDU-1229Si and13c NMR spectrum. As shown in FIG. 2(a), typical peaks at about-100.74, -109.02ppm are caused by Si atoms in the SBA-15, MCM-41, FDU-12(Q) and the DDP (T) silane chain, respectively. A weak signal (D) from the ethyl silane ether was observed at about-17.0 ppm, indicating successful improvement of the functional monomer on SBA-15, MCM-41, FDU-12, respectively. Fig. 2(b) shows the C ═ O characteristic band at 201.4ppm, and the peaks near 59.9, 42.6, 23.6ppm due to carbon atoms in the silica chain; the characteristic carbon peak of benzene appears at 122.0,129.0,118.9,161.7 ppm; the methine carbon is near 77.6 ppm. Solid state13The C NMR spectrum shows that DPP improves the mesoporous silica.
SEM images of Pb-IIMS-SBA-15, Pb-IIMS-MCM-41, Pb-IIMS-FDU-12 show many short rod-like structures and cake-like morphologies, respectively, with relatively ordered morphologies (as shown in FIG. 3). TEM shows that Pb-IIMS-SBA-15 and Pb-IIMS-MCM-41 are original hexagonal pore structures, and the parallel line structure Pb-IIMS-FDU-12 of the longitudinal section of the corresponding channel has spherical mesopores arranged in a cubic structure (as shown in FIG. 4), indicating that SBA-15, MCM-41 and FDU-12 still maintain highly ordered mesopore structures after modification.
The elements on the surface of Pb-IIMS-SBA-15, Pb-IIMS-MCM-41 and Pb-IIMS-FDU-12 were studied by energy dispersive X-ray (EDX). As shown in fig. 5, we can clearly observe the presence of C, N, O, Si. FIG. 6 is a nitrogen adsorption-desorption isotherm of the three materials, with Pb-IIMS-MCM-41 having a higher nitrogen percentage than Pb-IIMS-SBA-15 and Pb-IIMS-FDU-12, indicating that more functional monomers were grafted onto MCM-41. This indicates that Pb-IIMS-MCM-41 has the highest N content, and can enhance the adsorption capacity for Pb (II).
The small angle XRD results are shown in fig. 7, and fig. 7 shows well-documented peaks in the ranges of Pb-IIMS-SBA-15, Pb-IIMS-MCM-41, Pb-IIMS-FDU-12, 2 θ 0.7-2.0 °, 2 θ 2.08 °, and 2 θ 0.6-1.5 °, which can be traced to the (100), (110) and (200) reflections of SBA-15, the (100) reflection of MCM-41, and the (400) reflection of FDU-12, respectively. These details indicate that the structures of SBA-15, MCM-41, FDU-12 are well preserved, which supports SEM and TEM results well. Compared with the original mesopores, the diffraction peaks of Pb-IIMS-SBA-15, Pb-IIMS-MCM-41 and Pb-IIMS-FDU-12 are obviously reduced, and the fact that Pb (II) ion imprinted polymers cover the mesopore channels is proved, and the scattering capacity of the mesoporous silicate walls can be reduced due to the fact that organic functional monomers are adhered to the mesopore channels.
Effect example 2
Adsorption Performance test
(1) Adsorption experiments
To investigate the influence of pH, 5mg of Pb-IIMS-SBA-15, Pb-IIMS-MCM-41 and Pb-IIMS-FDU-12 were added to pH 2-8 containing 5 mg. multidot.L-1In the Pb (II) ion sample solution, the pH value is 1 mol.L-1HNO3And 1 mol. L-1And (5) regulating by NaOH. The mixture was shaken in a continuous water bath at 25 ℃ for 30 minutes, then allowed to stand stably for 30 minutes, centrifuged, filtered, and the concentration of Pb (II) in the upper solution was measured by inductively coupled plasma atomic emission spectrometry (ICP-AES). To select the optimal pH, we investigated the extraction yield.By way of comparison, we also investigated the effect of pH on the non-ionic imprinted polymers. The extraction rate was calculated using the following equation:
Wherein C isoAnd CeIs the concentration of lead ions in the solution in the original and equilibrium states.
For desorption of Pb (II) -functionalized mesoporous silica, a series of selected elution solutions, e.g., different concentrations of HNO, are considered3、HCl。
To study the adsorption capacity of the three Pb (II) -IIMS and the corresponding NIMS, 5mg of each adsorbate was dispersed in 20mL of aqueous solution containing different levels of Pb (II) (5-70ppm) at optimum pH. The mixture was then shaken in a continuous water bath at 25 ℃ for 30 minutes, allowed to stand still for 30 minutes, centrifuged, filtered, and the concentration of Pb (II) in the upper solution was measured by ICP-AES.
The adsorption capacity is calculated by the following equation:
wherein q ise(adsorption Capacity, mg. g)-1) Is the amount of Pb (II) adsorbed by IIMS, CoAnd CeIs the initial and equilibrium concentration of Pb (II) in the solution, m (g) is the weight of Pb-IIMS, and V (L) is the volume of the metal ion solution.
Meanwhile, kinetic studies were performed on pb (ii) to determine the adsorption rate of pb (ii) in water samples as follows: 5mg of each adsorbent was dispersed in 20mL of a solution containing 90ppm of the same initial Pb (II) concentration. Each mixture was shaken in a continuous water bath at 25 ℃ for 10, 20, 30, 40 or 50 minutes. After each time period, the solution was filtered and analyzed by ICP-AES to determine the concentration of pb (ii) in the final solution.
The pH volume of the solution is the most important parameter affecting the adsorption function of the adsorbent, since pH affects the protonation of the coordination sites of heavy metal ions grafted on mesoporous silica. Of Pb (II)The relationship between extraction efficiency and various pH values of the solution is shown in fig. 8. Obviously, the pH value of the solution has obvious influence on the adsorption capacity. The graph shows the maximum extraction efficiency of Pb-IIMS-SBA-15, Pb-IIMS-MCM-41, Pb-IIMS-FDU-12 at pH 6.0, 6.0 and 5.5, respectively. The extraction efficiency remains increased from pH 2 to its ideal pH, after which the pH change has no significant effect on the extraction efficiency of the adsorbent. Therefore, the optimum pH values of Pb-IIMS-SBA-15, Pb-IIMS-MCM-41 and Pb-IIMS-FDU-12 were determined to be 6.0, 6.0 and 5.5, respectively. This phenomenon may be due to the progressive reduction in protonation of Pb-IIMS, resulting in the bispyrazole group being more readily chelated to Pb (ii) in solution as pH is increased. In addition, since Pb (II) forms Pb (OH)2The precipitate, further increasing the solution pH, slightly reduced the extraction efficiency.
Using HNO at different concentrations3HCl, etc. series of acidic elution solutions and their mixtures with thiourea to investigate the elution efficiency of pb (ii) ions in the ion imprinted material. As shown in Table 1, 10mL of HCl (3 mol. L) was used-1) The best quantitative recovery of Pb (II) can be obtained. To a certain extent, the recovery rates of Pb-IIMS-SBA-15, Pb-IIMS-MCM-41 and Pb-IIMS-FDU-12 were 95.9%, 96.7% and 93.9%, respectively.
Table 1 effect of different types and concentrations of stripping agent.a
aThe volume of the stripping agent was 10 mL.
As shown in FIG. 9, the adsorption isotherms of Pb (II) ions by Pb-IIMS and NIMS at 25 ℃ were observed to rapidly increase the adsorption capacity of Pb (II) with the increase in the initial concentration of Pb (II) until the Pb-IIMS-SBA-15, Pb-IIMS-MCM-41 and Pb-IIMS-FDU-12 reached the saturated adsorption capacities (193.2, 283.7 and 155.2 mg. g. at Pb (II) concentrations of approximately 50, 70 and 40ppm, respectively-1). The higher adsorption capacity of Pb-IIMS compared to its corresponding NIMS indicates that the recognition site for Pb (ii) is improved on IIMS with higher adsorption capacity. Furthermore, Pb-IIMS-MCM-41 has a ratio of Pb-IIMS-SBA-15, Pb-IIThe better binding properties of MS-FDU-12 are probably due to the larger specific surface area of MCM-41 which modifies more functional monomers.
Adsorption isotherm experiments can help to understand the adsorption characteristics of Pb-IIMS. Langmuir and Freundlich models were used to study adsorbate-adsorbent interactions. Langmuir model, assuming that the adsorption sites on the adsorbent surface are homogenous, results in monolayer adsorption of the adsorbate. The Langmuir equation is expressed as:
wherein q ise(mg·g-1) And Ce(mg·L-1) Is the adsorption capacity and concentration of Pb (II) in the solution, qm (mg. g)-1) Is the maximum adsorption capacity of the adsorbent, b (L. mg)-1) Is the Langmuir constant.
The Freundlich model describes a multi-layer adsorption and heterogeneous system. The Freundlich equation is defined as:
qe=KfCe 1/n(7)
wherein Kf((mg·g-1)(L·mol-1)1/n) And n is a constant of Freundlich, which correlates with adsorption capacity and adsorption strength, respectively.
Table 2 summarizes the constants of the Langmuir and Freundlich models. For Pb-IIMS-SBA-15, Pb-IIMS-MCM-41 and Pb-IIMS-FDU-12, Langmuir model (R)20.9919, 0.9845, 0.9045) is higher than the Freundlich model R2=(R20.9657, 0.9312, 0.8428), indicating that the Langmuir model is more suitable for adsorption, and that adsorption of IIMS of pb (ii) occurs with monolayer coverage of the adsorbent surface. The maximum adsorption capacity of Pb-IIMS-MCM-41 obtained from the Langmuir model was 344.8mg g-1Higher than the previously reported Pb (II) ion imprinted adsorbents (listed in Table 3).
The influence of the contact time between the adsorbent and pb (ii) was used to judge the adsorption kinetics, and the result is shown in fig. 9 (c). It can be seen that the adsorption capacity of the adsorbent greatly increased in the initial stage. The adsorption of Pb-IIMS-SBA-15, Pb-IIMS-MCM-41 and Pb-IIMS-FDU-12 reaches equilibrium within 20, 40 and 40 minutes respectively. It is exciting that Pb-IIMS-MCM-41 not only shows a faster adsorption rate for Pb (II) than the other two adsorbents, but also shows a higher equilibrium adsorption capacity within 20 minutes.
TABLE 2 Langmuir and Freundlich isotherm constants for Pb (II) adsorption, IIMS
Table 3 compares the maximum adsorption capacities of Pb-IIMS-MCM-41 and the reported Pb (II) adsorbents
To investigate the adsorption principle of pb (ii), the adsorption kinetics were further analyzed by using different kinetic models comprising quasi-primary (eq.) and quasi-secondary (eq.).
ln(qe-qt)=lnqe-K1(9)
Wherein q iseAnd q ist(mg·g-1) Respectively the amount of pb (ii) adsorbed per mass of adsorbent under equilibrium conditions and at time t. k is a radical of1(min-1) And k2(g·mg-1·min-1) Are the first-order and second-order-like rate constants, respectively. Kinetic constants and correlation coefficients were calculated and summarized in table 4. From pseudo-second order (R)20.9691, 0.9992 and 0.9735) obtained from Pb-IIMS-SBA-15, Pb-IIMThe correlation coefficient of S-MCM-41 and Pb-IIMS-FDU-12 is larger than the quasi-first order (R)20.9567, 0.7090, and 0.7829). Therefore, the adsorption process of pb (ii) -IIMS is more amenable to a quasi-secondary model, mainly due to the chemical reaction between the adsorbent and the pb (ii) ions. The adsorption rate can be controlled by chemisorption of selective exchange between the adsorbent and pb (ii).
From the above analysis, the reason for the considerable adsorption performance results can be explained from several points below. First, conventional adsorbents exhibit poor site accessibility, possibly due to adsorption sites being embedded with a high density of cross-linked polymer matrix. Secondly, the metal ion imprinted mesoporous silica solves the defects of the traditional adsorbent, and the mesoporous silica with rich Si-OH on the surface can provide more improved sites for grafting more functional monomers. Third, the N-containing bidentate functionality we have obtained is readily reactive with pb (ii). Therefore, a large number of adsorption sites grafted on the surface of Pb-IIMS can have high adsorption capacity and rapid adsorption rate.
Table 4 pseudo-primary and pseudo-secondary kinetic parameters of the adsorbents.
(2) Selectivity test
To investigate the specific and selective adsorption of Pb (II), three ion imprinted materials and their corresponding non-imprinted materials were tested for their adsorption performance in a mixed solution containing Cd (II), Co (II), Cr (III), Pb (II), Hg (II), Cu (II), Zn (II), Mn (II) as competing ions, with Pb-IIMS and NIMS both in amounts of 5mg and with original concentrations of these ions of 20 ppm. The mixture was then shaken in a continuous water bath at 25 ℃ for 30 minutes, allowed to stand for 30 minutes, centrifuged, and filtered. ICP-AES is used for measuring Cd (II), Co (II), Cr (III), Pb (II), Hg (II), Cu (II), Zn (II) and Mn (II) before and after adsorption. The distribution coefficient K is calculated based on the following equationd(mL·g-1) Selectivity coefficient (α), relative selectivity coefficient (β):
wherein C iso(mL·g-1) And Ce(mL·g-1) Represents the initial and equilibrium concentrations of Pb (II); m (g) is the weight of IIMS, V (L) is the volume of the metal ion solution; kd1And Kd2Distribution coefficients of Pb (II) and competitive ions, α1And α2The selectivity coefficients of the ionic imprinting material and the non-ionic imprinting material are respectively expressed.
To investigate the inference of various cations in natural samples, the tests were performed by using the same amounts of li (i), na (i), k (i), mg (II), mn (II), co (II), cd (II), ba (II), hg (II), cr (iii), cu (II) as co-existing ions added to 20mL of a solution containing 0.5ppm Pb (II). An aqueous mixture of X/Pb (II) mixed with 5mg of Pb-IIMS-SBA-15, Pb-IIMS-MCM-41, Pb-IIMS-FDU-12 and their corresponding NIMSs, respectively, was shaken in a continuous water bath at 25 ℃ for 30 minutes, then allowed to stand stably for 30 minutes, centrifuged, filtered, and the concentration of Pb (II) in the final solution was determined by ICP-AES. We use the extraction of pb (ii) by the adsorbent to illustrate the interference resistance of our adsorbent in the presence of interfering ions.
Adsorption selectivity and adverse effects were studied, since selectivity is the essence in evaluating the adsorption performance of Pb-IIMS for Pb (ii). The adsorption selectivity check for Pb (II) was carried out in the presence of Cd (II), Co (II), Cr (III), Cu (II), Hg (II), Mn (II) and Zn (II). Optimum conditions for the three adsorbents, their concentrations and Pb (II) (20 mg. L)-1) The same selectivities (α) and relative selectivities (β) are summarized in Table 5 from FIG. 10 it can be seen that Pb-IIMS-SBA-15, Pb-IIMS-MCM-41 and Pb-IIMS-FDU-12 give a recommendable adsorption selectivity for competitive metal ions containing Pb (II). More specifically, Table 5 clearly shows that the selectivity coefficient for Pb-IIMS-MCM-41 for Pb (II) contained in competitive metal ions is higher than that for the other two adsorbents and DPP @ MCM-41. For Pb-IIMS-MCM-41, the selectivity coefficients for Pb (II) to Cr (III) and Pb (II) to Cu (II) were 266 and 377, respectively, if and only if the selectivity coefficient for DPP @ MCM-41 was 0.12 and 0.28. These details lead to the conclusion that the synthesized Pb-IIMS has a more excellent selectivity for Pb (ii).
TABLE 5 Selective adsorption Performance of Pb-IIMS and NIMS
To assess the potential for sorbent applications, the effect of various ions in water was investigated, such as Li (I), Na (I), K (I), Mg (II), Mn (II), Co (II), Cd (II), Cr (III), Cu (II), Cl-、SO42-、CH3COO-. We define the maximum concentration of foreign ions that can result in an error of less than 5% by tolerance, using X/pb (ii) to represent the tolerable concentration ratio. The results are shown in Table 6. As can be seen from the table, the extraneous ions had no significant effect on the detection of Pb (II) ions by NIMS under optimal conditions.
TABLE 6 tolerance ratio of various ions to Pb (II) ion measurement
(3) Experiment of reusability
To evaluate the reusability of Pb-IIMS-MCM-41, we performed depositionExperiment, desorption of pb (ii) from the adsorbent. 10mL of 3 mol. L was used-1Hydrochloric acid was used as a stripping agent, and the solution was shaken in a continuous water bath at 25 ℃ for 30 minutes. After Pb (II) ions were removed from the solution and washed with deionized water, the solution was measured by ICP-AES. The following adsorption experiments were performed. The same adsorbent was then used to compete in five cycles of adsorption-deposition experiments before obtaining an assessment of the reusability of Pb-IIMS-MCM-41.
By using 3 mol. L-1The stability and reusability of HCl as the desorption medium for Pb-IIMS-MCM-41 was again used for twelve adsorption-desorption cycles, and the results are shown in FIG. 11. In addition to a slight decrease in extraction efficiency over twelve cycles, the ion-imprinted mesoporous silica still maintained over 95% pb (ii) extraction efficiency. Therefore, it was confirmed that the obtained IIMS having high extraction efficiency can be reused.
Effect example 3
Application of Pb-IIMS-MCM-41 in determination of Pb (II)
Tap water and river water samples were collected from the laboratory, Huangpu river (Shanghai, China), respectively, and then centrifuged and filtered. 20mL of the preparation water sample and three concentrations of Pb (II) standards (0.01 mg. multidot.L) spiked with 5mg of Pb-IIMS-MCM-41-1、0.05mg·L-1And 0.1 mg. L-1) Using 1 mol. L-1HNO3And 1 mol. L-1The resulting mixture was adjusted to pH 6.0 with NaOH and the mixture solution was stirred continuously at 25 ℃ for 30 minutes. After filtration, 10mL of 3 mol. L was used-1The adsorbed Pb (II) ions were eluted by hydrochloric acid of (1) and measured by ICP-AES. Three replicates were performed for each concentration.
Due to outstanding selectivity and reusability, Pb-IIMS-MCM-41 was used to measure Pb (II) in tap water and river water to evaluate the suitability for developing adsorbents. The adsorbed pb (ii) concentration was analyzed by standard addition methods. As shown in Table 7, the recovery rate was changed from 95.0% to 106.0%, and the RSD was in the range of 0.36% to 2.26%. It can be concluded that Pb-IIMS-MCM-41 is an ideal candidate for separating and detecting Pb (II) in water.
TABLE 7 recovery (%) and relative standard deviation (RSD,%) of Pb-IIMS-MCM-41 of Pb (II) obtained from water sample
Claims (13)
1. A preparation method of a double-pyrazole functionalized lead printing FDU-12 material comprises the following steps: adding TEPIC into a mixture of DPP lead complex, alkali and tetrahydrofuran, heating and refluxing, vacuumizing to dry a solvent, then adding toluene and a mesoporous material FDU-12, reacting, and washing with acid to remove lead;
the DPP is 4- (di (1H-pyrazol-1-yl) methyl) phenol, the TEPIC is 3-triethoxysilyl-propyl-isocyanate, and the lead is divalent lead.
2. The method of claim 1, wherein the base is K2CO3Triethylamine and Na2CO3One or more of (a).
3. The method of claim 2, wherein K is2CO3For dehydration of K2CO3。
4. The preparation method according to claim 1, wherein the molar ratio of the DPP lead complex to the base is 1: 1-1.2;
and/or the molar ratio of the DPP lead complex to the TEPIC is 1: 1-1.2;
and/or the molar mass ratio of the DPP lead complex to the mesoporous material is 1mmol:0.95 g-1.00 g.
5. The process according to claim 1, wherein the molar ratio of DPP lead complex to base is 1: 1;
and/or the molar ratio of the DPP lead complex to the TEPIC is 1: 1;
and/or the molar mass ratio of the DPP lead complex to the mesoporous material is 1mmol:0.97 g-0.98 g.
6. The preparation method according to claim 1, wherein the temperature of the heating reflux is 60 to 70 ℃, and the time of the heating reflux is 9 to 13 hours;
and/or the reaction temperature is 105-115 ℃, and the reaction time is 47-49 hours.
7. The process according to claim 1, wherein after the completion of the reaction and before the removal of lead by acid washing, a post-treatment is further carried out; and the post-treatment is filtration, and the obtained solid is washed by dichloromethane, distilled water, ethanol and ethyl acetate in sequence and dried.
8. The method according to claim 7, wherein the acid is hydrochloric acid and/or nitric acid; the molar concentration of the acid is 3 mol/L.
9. The method of claim 8, wherein the acid is hydrochloric acid.
10. The process according to claim 1, wherein the DPP lead complex is prepared by the following steps: mixing DPP and lead compound in methanol and/or ethanol for reaction.
11. The method according to claim 10, wherein the lead compound is lead nitrate;
wherein, in the preparation reaction of the DPP lead complex, the reaction temperature is 10-30 ℃; the reaction time is 4-6 hours;
wherein the molar ratio of the DPP to the lead compound is 1: (0.5-0.6).
12. The double-pyrazole functionalized lead-printed FDU-12 material prepared by the preparation method of any one of claims 1 to 11.
13. The use of the double pyrazole functionalized lead-print FDU-12 material as defined in claim 12 for adsorbing and/or detecting metallic lead; wherein the lead is divalent lead.