CN108219311A - 一种高强度环保地板 - Google Patents

一种高强度环保地板 Download PDF

Info

Publication number
CN108219311A
CN108219311A CN201611158311.6A CN201611158311A CN108219311A CN 108219311 A CN108219311 A CN 108219311A CN 201611158311 A CN201611158311 A CN 201611158311A CN 108219311 A CN108219311 A CN 108219311A
Authority
CN
China
Prior art keywords
parts
strength environment
friendly floor
weight
plasticizer
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
CN201611158311.6A
Other languages
English (en)
Inventor
赖群广
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201611158311.6A priority Critical patent/CN108219311A/zh
Publication of CN108219311A publication Critical patent/CN108219311A/zh
Withdrawn legal-status Critical Current

Abstract

本发明公开了一种高强度环保地板，包括一块以上的由胶黏剂粘接拼接基板，所述基板包括以下重量份的原料：聚氯乙烯树脂100‑120份、玻璃纤维8‑10份、羟基吡啶硫酸铜11‑15份、硅藻土10‑20份、硼泥废料45‑50份、热稳定剂2.5‑5份，润滑剂0.5‑1份、碳酸钙40‑50份、增塑剂1.5‑2.5份、促进剂1‑3份、粉煤灰10‑20份和氯化聚乙烯0.2‑0.7份，该高强度环保地板环保性较强、拼接性能较好，可长时间存放，无污染和有害气体。

Description

一种高强度环保地板
技术领域
本发明涉及一种高强度环保地板，更具体的说，涉及地板材料领域。
背景技术
在装修领域中，室内地面铺装材料一般为各种木质地板或复合木地板。木质地板的脚感比较舒适，但容易吸水膨胀或干燥变形，在使用过程中常出现收缩、膨胀变形、起翘、开裂等问题，并且需要耗费大量木材，生产周期较长，成本较高，并且大量使用会破坏森林，不可持续。复合木地板主要是利用木屑和粘合剂及其它添加剂经混合挤压而形成的一种地板，其表面色彩丰富，成本低，但存在易吸水变形等问题，并且这种地板的主要问题是释放甲醛，严重危害人体健康、不环保。随着人们对环保意识的加强，对室内环境污染的重视，高强度环保地板必将取代吸水、含甲醛量高的强化地板和不易保养、不耐磨、易变形、安装繁琐的实木地板而成为居家装饰建材的新宠。
胶黏剂在铺设地板中起到至关重要的作用，胶黏剂的质量直接影响到铺设质量。市场上现有的双组分胶黏剂仍存在以下不足 ：配置好的胶黏剂可存放时间短，易固化报废，影响施工效率 ；室温下，所需完全固化时间过长 ；黏性偏大，流动性较差，施工存在一定难度，且环保性不足。综上所述，现有双组分木地板胶黏剂中存在的问题已成为现有地板胶黏剂领域亟待解决的技术难题。
发明内容
有鉴于此，本发明目的是提供一种环保性较强、拼接性能较好，可长时间存放，无污染和有害气体的高强度环保地板。
为了解决上述技术问题，本发明的技术方案是：
一种高强度环保地板，包括一块以上的由胶黏剂粘接拼接基板，所述基板包括以下重量份的原料：聚氯乙烯树脂100-120份、玻璃纤维8-10份、羟基吡啶硫酸铜11-15份、硅藻土10-20份、硼泥废料45-50份、热稳定剂2.5-5份，润滑剂0.5-1份、碳酸钙40-50份、增塑剂1.5-2.5份、促进剂1-3份、粉煤灰10-20份和氯化聚乙烯0.2-0.7份，所述胶黏剂包括以下重量份的原料：聚氨酯树脂0.5-1.7份、四水三氟化铬0.8-1.5份、脱糖缩合木质素磺酸钠2.5-4.2份、鱼胶1.5-3份、牛皮胶3-7份、无定型聚酯多元醇2.3-4.5份、复合淀粉3-7份、乙酸乙酯2-4份、酶解木质素2.3-5份、去离子水20-30份、聚亚烷基二醇1.5-2.8份和纳米蛭石3.2-5.8份。
进一步的，所述基板包括以下重量份的原料：聚氯乙烯树脂100份、玻璃纤维8份、羟基吡啶硫酸铜11份、硅藻土10份、硼泥废料45份、热稳定剂2.5份，润滑剂0.5份、碳酸钙40份、增塑剂1.5份、促进剂1份、粉煤灰10份和氯化聚乙烯0.2份，所述胶黏剂包括以下重量份的原料：聚氨酯树脂0.5份、四水三氟化铬0.8份、脱糖缩合木质素磺酸钠2.5份、鱼胶1.5份、牛皮胶3份、无定型聚酯多元醇2.3份、复合淀粉3份、乙酸乙酯2份、酶解木质素2.3份、去离子水20份、聚亚烷基二醇1.5份和纳米蛭石3.2份。
进一步的，所述基板包括以下重量份的原料：聚氯乙烯树脂120份、玻璃纤维10份、羟基吡啶硫酸铜15份、硅藻土20份、硼泥废料50份、热稳定剂5份，润滑剂1份、碳酸钙50份、增塑剂2.5份、促进剂3份、粉煤灰20份和氯化聚乙烯0.7份，所述胶黏剂包括以下重量份的原料：聚氨酯树脂1.7份、四水三氟化铬1.5份、脱糖缩合木质素磺酸钠4.2份、鱼胶3份、牛皮胶7份、无定型聚酯多元醇4.5份、复合淀粉7份、乙酸乙酯4份、酶解木质素5份、去离子水30份、聚亚烷基二醇2.8份和纳米蛭石5.8份。
进一步的，所述基板包括以下重量份的原料：聚氯乙烯树脂110份、玻璃纤维9份、羟基吡啶硫酸铜13份、硅藻土15份、硼泥废料47.5份、热稳定剂3.5份，润滑剂0.75份、碳酸钙45份、增塑剂2份、促进剂2份、粉煤灰15份和氯化聚乙烯0.45份，所述胶黏剂包括以下重量份的原料：聚氨酯树脂1.1份、四水三氟化铬1.15份、脱糖缩合木质素磺酸钠3.5份、鱼胶2.5份、牛皮胶5份、无定型聚酯多元醇3.4份、复合淀粉5份、乙酸乙酯3份、酶解木质素3.5份、去离子水25份、聚亚烷基二醇2.25份和纳米蛭石4.8份。
进一步的，所述热稳定剂为硬脂酸盐。
进一步的，所述润滑剂为石蜡。
进一步的，所述增塑剂为乙酰基柠檬酸三丁酯、柠檬酸三丁酯和环己烷 -1,2- 羧酸壬酯中的任一种。
进一步的，所述促进剂为硬脂酸锌。
本发明技术效果主要体现在以下方面：在传统的聚氯乙烯地板组分中还添加了玻璃纤维，使得其防水性能方面极大提升，同时本发明还增加了防霉剂羟基吡啶硫酸铜使得其不容易产生霉斑，同时也增加了其他耐候性，室温下，本发明胶黏剂所需完全固化时间短；且胶黏剂所用原料均安全无污染，可以释放对人体有益的负氧离子，既环保又可净化空气，提高空气质量，由于胶黏剂含有牛皮胶和酶解木质素成分，因此，还具有防火、透气、调节温度、湿度的特性，通过采用特定用量的聚亚烷基二醇、四水三氟化铬和复合淀粉，使得该地板之间的粘接具有良好的弹性和强粘接力，并具有很好的耐水性能和低温弹性，也具有很好的抗压能力。
具体实施方式
以下结合实施例，对本发明的具体实施方式作进一步详述，以使本发明技术方案更易于理解和掌握。
实施例1：
一种高强度环保地板，包括一块以上的由胶黏剂粘接拼接基板，所述基板包括以下重量份的原料：聚氯乙烯树脂100份、玻璃纤维8份、羟基吡啶硫酸铜11份、硅藻土10份、硼泥废料45份、热稳定剂2.5份，润滑剂0.5份、碳酸钙40份、增塑剂1.5份、促进剂1份、粉煤灰10份和氯化聚乙烯0.2份，所述胶黏剂包括以下重量份的原料：聚氨酯树脂0.5份、四水三氟化铬0.8份、脱糖缩合木质素磺酸钠2.5份、鱼胶1.5份、牛皮胶3份、无定型聚酯多元醇2.3份、复合淀粉3份、乙酸乙酯2份、酶解木质素2.3份、去离子水20份、聚亚烷基二醇1.5份和纳米蛭石3.2份，所述热稳定剂为硬脂酸盐，所述润滑剂为石蜡，所述增塑剂为柠檬酸三丁酯，所述促进剂为硬脂酸锌。
一种高强度环保地板的制备方法，包括以下步骤：
1）硅藻土10份经干燥、粉碎、风选后粒度在200目；硼泥废料45份经干燥、粉碎、风选后粒度在150目；
2）将聚氯乙烯树脂100份、碳酸钙40份、粉煤灰10份、粉粹的硅藻土10份和硼泥废料45份混合并充分搅拌；
3）加入混料机，高速升温至110度，去掉水分及挥发杂质，并加入玻璃纤维8份、羟基吡啶硫酸铜11份、热稳定剂2.5份、润滑剂0.5份、增塑剂1.5份、促进剂1份和氯化聚乙烯0.2份，混料转速为130转/分钟，混合总时间为10分钟，再在常温下冷却后得到混合粉；
4）经双螺杆挤出机高温挤出，温度为170℃，再经过水冷却定型、切割程序后制成基板；
5）将聚氨酯树脂0.5份、四水三氟化铬0.8份、脱糖缩合木质素磺酸钠2.5份、鱼胶1.5份缓慢加入到去离子水20份中，于60℃条件下边搅拌边加入，搅拌20min；
6）继续加入牛皮胶3份、无定型聚酯多元醇2.3份、复合淀粉3份、乙酸乙酯2份、酶解木质素2.3份、聚亚烷基二醇1.5份和纳米蛭石3.2份，于70℃条件下边搅拌边加入，搅拌至各组分充分混合成乳状液；
7）将温度升高到80℃，保持10min，然后停止加热，自然搅拌降温至室温，得到胶黏剂；
8）将各个基板通过胶黏剂进行粘接拼接。
实施例2：
一种高强度环保地板，包括一块以上的由胶黏剂粘接拼接基板，所述基板包括以下重量份的原料：聚氯乙烯树脂120份、玻璃纤维10份、羟基吡啶硫酸铜15份、硅藻土20份、硼泥废料50份、热稳定剂5份，润滑剂1份、碳酸钙50份、增塑剂2.5份、促进剂3份、粉煤灰20份和氯化聚乙烯0.7份，所述胶黏剂包括以下重量份的原料：聚氨酯树脂1.7份、四水三氟化铬1.5份、脱糖缩合木质素磺酸钠4.2份、鱼胶3份、牛皮胶7份、无定型聚酯多元醇4.5份、复合淀粉7份、乙酸乙酯4份、酶解木质素5份、去离子水30份、聚亚烷基二醇2.8份和纳米蛭石5.8份，所述热稳定剂为硬脂酸盐，所述润滑剂为石蜡，所述增塑剂为乙酰基柠檬酸三丁酯，所述促进剂为硬脂酸锌。
一种高强度环保地板的制备方法，包括以下步骤：
1）硅藻土20份经干燥、粉碎、风选后粒度在200目；硼泥废料50份经干燥、粉碎、风选后粒度在150目；
2）将聚氯乙烯树脂120份、碳酸钙50份、粉煤灰20份、粉粹的硅藻土20份和硼泥废料50份混合并充分搅拌；
3）加入混料机，高速升温至110度，去掉水分及挥发杂质，并加入玻璃纤维10份、羟基吡啶硫酸铜15份、热稳定剂5份、润滑剂1份、增塑剂2.5份、促进剂3份和氯化聚乙烯0.7份，混料转速为130转/分钟，混合总时间为10分钟，再在常温下冷却后得到混合粉；
4）经双螺杆挤出机高温挤出，温度为170℃，再经过水冷却定型、切割程序后制成基板；
5）将聚氨酯树脂1.7份、四水三氟化铬1.5份、脱糖缩合木质素磺酸钠4.2份、鱼胶3份缓慢加入到去离子水30份中，于60℃条件下边搅拌边加入，搅拌20min；
6）继续加入牛皮胶7份、无定型聚酯多元醇4.5份、复合淀粉7份、乙酸乙酯4份、酶解木质素5份、去离子水30份、聚亚烷基二醇2.8份和纳米蛭石5.8份，于70℃条件下边搅拌边加入，搅拌至各组分充分混合成乳状液；
7）将温度升高到80℃，保持10min，然后停止加热，自然搅拌降温至室温，得到胶黏剂；
8）将各个基板通过胶黏剂进行粘接拼接。
实施例3：
一种高强度环保地板，包括一块以上的由胶黏剂粘接拼接基板，所述基板包括以下重量份的原料：聚氯乙烯树脂110份、玻璃纤维9份、羟基吡啶硫酸铜13份、硅藻土15份、硼泥废料47.5份、热稳定剂3.5份，润滑剂0.75份、碳酸钙45份、增塑剂2份、促进剂2份、粉煤灰15份和氯化聚乙烯0.45份，所述胶黏剂包括以下重量份的原料：聚氨酯树脂1.1份、四水三氟化铬1.15份、脱糖缩合木质素磺酸钠3.5份、鱼胶2.5份、牛皮胶5份、无定型聚酯多元醇3.4份、复合淀粉5份、乙酸乙酯3份、酶解木质素3.5份、去离子水25份、聚亚烷基二醇2.25份和纳米蛭石4.8份，所述热稳定剂为硬脂酸盐，所述润滑剂为石蜡，所述增塑剂为环己烷 -1,2- 羧酸壬酯，所述促进剂为硬脂酸锌。
一种高强度环保地板的制备方法，包括以下步骤：
1）硅藻土15份经干燥、粉碎、风选后粒度在200目；硼泥废料47.5份经干燥、粉碎、风选后粒度在150目；
2）将聚氯乙烯树脂110份、碳酸钙45份、粉煤灰15份、粉粹的硅藻土15份和硼泥废料47.5份混合并充分搅拌；
3）加入混料机，高速升温至110度，去掉水分及挥发杂质，并加入玻璃纤维9份、羟基吡啶硫酸铜13份、热稳定剂3.5份、润滑剂0.75份、增塑剂2份、促进剂2份和氯化聚乙烯0.45份，混料转速为130转/分钟，混合总时间为10分钟，再在常温下冷却后得到混合粉；
4）经双螺杆挤出机高温挤出，温度为170℃，再经过水冷却定型、切割程序后制成基板；
5）将聚氨酯树脂1.1份、四水三氟化铬1.15份、脱糖缩合木质素磺酸钠3.5份、鱼胶2.5份缓慢加入到去离子水25份中，于60℃条件下边搅拌边加入，搅拌20min；
6）继续加入牛皮胶5份、无定型聚酯多元醇3.4份、复合淀粉5份、乙酸乙酯3份、酶解木质素3.5份、聚亚烷基二醇2.25份和纳米蛭石4.8份，于70℃条件下边搅拌边加入，搅拌至各组分充分混合成乳状液；
7）将温度升高到80℃，保持10min，然后停止加热，自然搅拌降温至室温，得到胶黏剂；
8）将各个基板通过胶黏剂进行粘接拼接。
实验例：
将上述实施例制得基板和胶黏剂与市售地板分别进行粘接强度、机械稳定性、冻融稳定性、甲醛释放量和吸水厚度膨胀率的对比测试，结果显示，样品各项性能均优于市售地板。具体实验结果见下表
如下表所示：
由上表可见，本发明的高强度环保地板的甲醛释放量明显低于现有的地板，且剥离强度、粘接强度、聚合物稳定性和机械稳定性明显高于现有地板，同时在后续3个月的跟踪测试中，也未有出现霉斑等情况。
本发明技术效果主要体现在以下方面：在传统的聚氯乙烯地板组分中还添加了玻璃纤维，使得其防水性能方面极大提升，同时本发明还增加了防霉剂羟基吡啶硫酸铜使得其不容易产生霉斑，同时也增加了其他耐候性，室温下，本发明胶黏剂所需完全固化时间短；且胶黏剂所用原料均安全无污染，可以释放对人体有益的负氧离子，既环保又可净化空气，提高空气质量，由于胶黏剂含有牛皮胶和酶解木质素成分，因此，还具有防火、透气、调节温度、湿度的特性，通过采用特定用量的聚亚烷基二醇、四水三氟化铬和复合淀粉，使得该地板之间的粘接具有良好的弹性和强粘接力，并具有很好的耐水性能和低温弹性，也具有很好的抗压能力。
当然，以上只是本发明的典型实例，除此之外，本发明还可以有其它多种具体实施方式，凡采用等同替换或等效变换形成的技术方案，均落在本发明要求保护的范围之内。

Claims (8)

1.一种高强度环保地板，包括一块以上的由胶黏剂粘接拼接基板，其特征在于，所述基板包括以下重量份的原料：聚氯乙烯树脂100-120份、玻璃纤维8-10份、羟基吡啶硫酸铜11-15份、硅藻土10-20份、硼泥废料45-50份、热稳定剂2.5-5份，润滑剂0.5-1份、碳酸钙40-50份、增塑剂1.5-2.5份、促进剂1-3份、粉煤灰10-20份和氯化聚乙烯0.2-0.7份，所述胶黏剂包括以下重量份的原料：聚氨酯树脂0.5-1.7份、四水三氟化铬0.8-1.5份、脱糖缩合木质素磺酸钠2.5-4.2份、鱼胶1.5-3份、牛皮胶3-7份、无定型聚酯多元醇2.3-4.5份、复合淀粉3-7份、乙酸乙酯2-4份、酶解木质素2.3-5份、去离子水20-30份、聚亚烷基二醇1.5-2.8份和纳米蛭石3.2-5.8份。
2.根据权利要求1所述的高强度环保地板，其特征在于：所述基板包括以下重量份的原料：聚氯乙烯树脂100份、玻璃纤维8份、羟基吡啶硫酸铜11份、硅藻土10份、硼泥废料45份、热稳定剂2.5份，润滑剂0.5份、碳酸钙40份、增塑剂1.5份、促进剂1份、粉煤灰10份和氯化聚乙烯0.2份，所述胶黏剂包括以下重量份的原料：聚氨酯树脂0.5份、四水三氟化铬0.8份、脱糖缩合木质素磺酸钠2.5份、鱼胶1.5份、牛皮胶3份、无定型聚酯多元醇2.3份、复合淀粉3份、乙酸乙酯2份、酶解木质素2.3份、去离子水20份、聚亚烷基二醇1.5份和纳米蛭石3.2份。
3.根据权利要求1所述的高强度环保地板，其特征在于：所述基板包括以下重量份的原料：聚氯乙烯树脂120份、玻璃纤维10份、羟基吡啶硫酸铜15份、硅藻土20份、硼泥废料50份、热稳定剂5份，润滑剂1份、碳酸钙50份、增塑剂2.5份、促进剂3份、粉煤灰20份和氯化聚乙烯0.7份，所述胶黏剂包括以下重量份的原料：聚氨酯树脂1.7份、四水三氟化铬1.5份、脱糖缩合木质素磺酸钠4.2份、鱼胶3份、牛皮胶7份、无定型聚酯多元醇4.5份、复合淀粉7份、乙酸乙酯4份、酶解木质素5份、去离子水30份、聚亚烷基二醇2.8份和纳米蛭石5.8份。
4.根据权利要求3所述的高强度环保地板，其特征在于：所述基板包括以下重量份的原料：聚氯乙烯树脂110份、玻璃纤维9份、羟基吡啶硫酸铜13份、硅藻土15份、硼泥废料47.5份、热稳定剂3.5份，润滑剂0.75份、碳酸钙45份、增塑剂2份、促进剂2份、粉煤灰15份和氯化聚乙烯0.45份，所述胶黏剂包括以下重量份的原料：聚氨酯树脂1.1份、四水三氟化铬1.15份、脱糖缩合木质素磺酸钠3.5份、鱼胶2.5份、牛皮胶5份、无定型聚酯多元醇3.4份、复合淀粉5份、乙酸乙酯3份、酶解木质素3.5份、去离子水25份、聚亚烷基二醇2.25份和纳米蛭石4.8份。
5.根据权利要求1-4中任一项所述的高强度环保地板，其特征在于：所述热稳定剂为硬脂酸盐。
6.根据权利要求5所述的高强度环保地板，其特征在于：所述润滑剂为石蜡。
7.根据权利要求6所述的高强度环保地板，其特征在于：所述增塑剂为乙酰基柠檬酸三丁酯、柠檬酸三丁酯和环己烷 -1,2- 羧酸壬酯中的任一种。
8.根据权利要求7所述的高强度环保地板，其特征在于：所述促进剂为硬脂酸锌。
CN201611158311.6A 2016-12-15 2016-12-15 一种高强度环保地板 Withdrawn CN108219311A (zh)