CN108185597A - Ceramic applications are in the production technology of jewelry - Google Patents
Ceramic applications are in the production technology of jewelry Download PDFInfo
- Publication number
- CN108185597A CN108185597A CN201810007866.3A CN201810007866A CN108185597A CN 108185597 A CN108185597 A CN 108185597A CN 201810007866 A CN201810007866 A CN 201810007866A CN 108185597 A CN108185597 A CN 108185597A
- Authority
- CN
- China
- Prior art keywords
- ceramics
- ceramic
- paste
- jewellery
- slot
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides a kind of ceramic applications in the production technology of jewelry, groove milling processing is carried out to the side wall of the ceramic accommodating cavity of jewellery matrix;In the fill area injection paste ceramics of slot, ceramic accommodating cavity then is filled up with paste ceramics, the jewellery matrix for having been injected into paste ceramics is soaked in style keeping liquid and carries out the curing process of high temperature and pressure;It is polished molding ceramics and polishing treatment.The beneficial effects of the present invention are:Provide a kind of technique, the technique processes slot in the side wall of the ceramic accommodating cavity of jewellery, a small amount of paste ceramics are injected in slot for enhancing the connection of ceramics and jewellery, again ceramic accommodating cavity is filled up with paste ceramics, ceramic paste is cured as by ceramics by continuous high temperature high pressure, finally sanding and polishing is carried out to ceramics to handle to obtain jewellery, it is easily broken to solve the problems, such as that ceramic paste causes because of being interference fitted in curing process with jewellery ontology, considerably increases product qualification rate.
Description
Technical field
The present invention relates to bullion manufacturing fields, refer in particular to a kind of ceramic applications in the production technology of jewelry.
Background technology
Ceramics are a kind of general name of pottery and porcelain in fact, and the mankind are early in the about B.C. 8000-2000 (Neolithic Ages
Epoch) just invent pottery.Traditional ceramic material has clay, aluminium oxide, kaolin etc..Clay room temperature chance water is plastic, micro- dry
It can carve, it is absolutely dry to grind;Water can be filled into pottery by burning to 700 degree;It burns to 1100 degree of then porcelain, does not absorb water and high temperature resistant corrosion resistant
Erosion.The deep porcelain of history culture inside information with jewellery is combined as porcelain big country, can be that jewellery increase cultural bottom by China
Accumulate, have the heavy feeling of history.
But traditional ceramics due to material, technique the problem of, it is difficult to the unique and exquisite product of moulding be obtained, with ceramics
The continuous development of production technology and perfect, the appearance of high technology ceramics makes it possible ceramic applications in jewellery.High technology ceramics are to adopt
It is made of the stringent control dispensing of the inorganic material such as zirconium oxide, silica, silicon nitride process and special process smooth flat with surface
Whole ceramics.
In the existing manufacture craft for inlaying high technology ceramics jewellery, it is maximum the problem of be cured in the jewellery process of ceramics
In, it easily bursts, jewelry manufacture is caused to fail, it is therefore desirable to be improved to prior art.
Invention content
The technical problems to be solved by the invention are:A kind of making work that ceramics is avoided to burst during curing in jewellery is provided
Skill.
In order to solve the above-mentioned technical problem, the technical solution adopted by the present invention is:A kind of ceramic applications are in the production of jewelry
Technique, including:
S1, the jewellery matrix with ceramic accommodating cavity is prepared;
S2, slot treatment is carried out to the side wall of ceramic accommodating cavity;
S3, plastering agent and binder are smeared successively in ceramic accommodating cavity and slot;
S4, paste ceramics are injected in slot, then fills up ceramic accommodating cavity with paste ceramics;
S5, the jewellery matrix for having been injected into paste ceramics is soaked in style keeping liquid and carries out the curing process of high temperature and pressure;
S6, it is polished molding ceramics and polishing treatment.
Further, in step S2, the section of slot is at an acute angle, one kind in C fonts or V-shaped.
Further, in step S2, slot includes fill area and non-filling area.
Further, in step S4, by the fill area of paste ceramics injection slot, the non-filling area of slot is not injected into paste pottery
Porcelain.
Further, in step S4, the paste ceramics of the fill area of slot and the paste ceramics of ceramic accommodating cavity have contact surface.
Further, in step S5, the atmospheric pressure of curing process is 110-130 kPas, and temperature is 80-140 degrees Celsius,
Duration is 50-70 minutes.
Further, it in step S6, further includes:
S61, thick grinding process is carried out to ceramics with the cotton piece buff for being coated with Chinese wax;
S62, thin grinding process is carried out to ceramics with the cotton piece buff for being coated with blue wax;
S63, finishing polish processing is carried out to ceramics with the cotton piece buff for being coated with yellow wax.
Further, in step S1, making jewellery matrix is dried including expecting by casting, system, holding mould, coating, ultraviolet light
The step of.
Further, in the step of ultraviolet light is dried, the time that ultraviolet light is dried is 35-45 seconds.
Further, after step S6, the step of processing of electricity gold and cleaning are carried out to jewellery matrix is further included.
The beneficial effects of the present invention are:A kind of technique is provided, which adds in the side wall of the ceramic accommodating cavity of jewellery
Work goes out slot, a small amount of paste ceramics is injected in slot for enhancing the connection of ceramics and jewellery, then fill up ceramics with paste ceramics
Ceramic paste is cured as ceramics by accommodating cavity by continuous high temperature high pressure, and finally carrying out sanding and polishing to ceramics handles to obtain jewellery,
It is easily broken to solve the problems, such as that ceramic paste causes because of being interference fitted in curing process with jewellery ontology, considerably increases
Product qualification rate.
Description of the drawings
The concrete structure of the present invention is described in detail below in conjunction with the accompanying drawings:
Fig. 1 is the flow diagram of the present invention;
Fig. 2 is the cross-sectional view of one embodiment of the invention;
Fig. 3 is that one embodiment of the invention fills the cross-sectional view after paste ceramics.
1- jewellery matrixes;2- ceramics accommodating cavities;3- slots;The non-filling area of 31- slots;The paste ceramics of 4- fill areas;5- cream
Shape ceramics.
Specific embodiment
In order to describe the technical content, the structural feature, the achieved object and the effect of this invention in detail, below in conjunction with embodiment
And attached drawing is coordinated to be explained in detail.
Embodiment
Referring to Fig. 1, a kind of ceramic applications are in the production technology of jewelry, including:
S1, the jewellery matrix with ceramic accommodating cavity is prepared;
By casting, system material, hold the step of mould, coating, ultraviolet light are dried and produce the jewellery base with ceramic accommodating cavity
Body,
Casting:Using hollow glued membrane, by the way of casting cooling, style wax-pattern is obtained.
Hold mould:Preliminary surface processing, the flaw that finishing is left in making are carried out to jewellery matrix.
Coating:It is armor coated in jewellery matrix surface.
Ultraviolet light is dried:Cure the protective layer of jewellery matrix surface, the time that ultraviolet light is dried is 35-45 seconds.
S2, slot treatment is carried out to the side wall of ceramic accommodating cavity;
Slot is made in the side wall of ceramic accommodating cavity, the section of slot is at an acute angle, one kind in C fonts or V-shaped, on the one hand may be used
Stress area is provided for jewellery matrix and facilitates fixing ceramics, is increased the reliability that ceramics are connect with jewellery matrix, is on the other hand
Expansion of the paste ceramics in forming process provides buffer area, will not squeeze and generate on ceramics because space is excessively narrow
Crackle.
S3, plastering agent and binder are smeared successively in ceramic accommodating cavity and slot;
The plastering agent of HyCeram Link is first smeared, then smears the binder of VP-206BondII, smear plastering agent and sticks
Mixture can further increase the reliability that ceramics are connect with jewellery matrix.
S4, paste ceramics are injected in slot, then fills up ceramic accommodating cavity with paste ceramics;
Fig. 2 and Fig. 3 is please referred to, the slot made is divided into fill area and non-filling area, in the fill area injection paste pottery of slot
Porcelain facilitates fixing ceramics for providing stress area for jewellery matrix;The non-filling area of slot expands reserved space for providing.
Specifically, injecting a small amount of paste ceramics close to ceramic accommodating cavity bottom side in slot, the remaining space of slot is not injected into
Paste ceramics, then fill up ceramic accommodating cavity with paste ceramics, until accent.
It fills up after paste ceramics and further includes the step of smooth accent paste ceramics.
S5, the jewellery matrix for having been injected into paste ceramics is soaked in style keeping liquid and carries out the curing process of high temperature and pressure;
Jewellery are put into the reaction chamber of air compressor machine, style keeping liquid is poured into reaction chamber, not cross the ceramics of jewellery matrix
Subject to accommodating cavity, start air compressor machine, to reaction chamber pressurized, heated, the ceramic paste in the ceramic accommodating cavity of jewellery matrix is consolidated
Change is handled.
S6, it is polished molding ceramics and polishing treatment.
The jewellery completed will be cured by being taken out in air compressor machine, sanding and polishing is carried out to the ceramics of jewellery, makes ceramic surface shape
Into even surface, luster effect is generated.
As can be seen from the above description, the beneficial effects of the present invention are:A kind of technique is provided, the technique is in the ceramics of jewellery
The side wall of accommodating cavity processes slot, and a small amount of paste ceramics are injected in slot for enhancing the connection of ceramics and jewellery, then use cream
Shape ceramics fill up ceramic accommodating cavity, and ceramic paste is cured as ceramics by continuous high temperature high pressure, finally carries out polishing throwing to ceramics
Light processing obtains jewellery, and solve ceramic paste causes easily broken because of being interference fitted in curing process with jewellery ontology
Problem considerably increases product qualification rate.
Embodiment 1
In above-mentioned, in step S5, the atmospheric pressure of curing process is 110-130 kPas, and temperature is 80-140 degrees Celsius, is held
The continuous time is 50-70 minutes.
When for atmospheric pressure less than 110 kPas, temperature less than 80 degrees Celsius, the duration is less than 50 points in the parameter of curing process
Zhong Shi, ceramic solidification failure, ceramic hardness is excessively soft, and durability is inadequate;
When for atmospheric pressure higher than 130 kPas, temperature higher than 140 degrees Celsius, the duration is more than 70 in the parameter of curing process
During minute, ceramic hardness is excessively high, easily broken.
Embodiment 2
In above-mentioned, in step S6, further include:
S61, thick grinding process is carried out to ceramics with the cotton piece buff for being coated with Chinese wax;
Thick grinding process is carried out to ceramics, the rough place of ceramic surface is polished flat.
S62, thin grinding process is carried out to ceramics with the cotton piece buff for being coated with blue wax;
Thin grinding process is carried out to ceramics, ceramic surface is polishing to concordant with jewellery matrix surface.
S63, finishing polish processing is carried out to ceramics with the cotton piece buff for being coated with yellow wax.
Finishing polish processing finally is carried out to ceramics, ceramic surface is finished to smooth smooth surface, generates luster effect.
Embodiment 3
After step S6, the step of processing of electricity gold and cleaning are carried out to jewellery matrix is further included.
Sanding and polishing is disposed, and electricity gold processing is carried out to jewellery matrix, electro-cladding is formed in jewellery matrix surface,
It then starts the cleaning processing, finally obtains jewellery finished product.
The foregoing is merely the embodiment of the present invention, are not intended to limit the scope of the invention, every to utilize this hair
The equivalent structure or equivalent flow shift that bright specification and accompanying drawing content are made directly or indirectly is used in other relevant skills
Art field, is included within the scope of the present invention.
Claims (10)
1. a kind of ceramic applications are in the production technology of jewelry, which is characterized in that including:
S1, the jewellery matrix with ceramic accommodating cavity is prepared;
S2, slot treatment is carried out to the side wall of ceramic accommodating cavity;
S3, plastering agent and binder are smeared successively in ceramic accommodating cavity and slot;
S4, paste ceramics are injected in slot, then fills up ceramic accommodating cavity with paste ceramics;
S5, the jewellery matrix for having been injected into paste ceramics is soaked in style keeping liquid and carries out the curing process of high temperature and pressure;
S6, it is polished molding ceramics and polishing treatment.
2. ceramic applications as described in claim 1 are in the production technology of jewelry, it is characterised in that:In step S2, the section of slot
One kind at an acute angle, C fonts or V-shaped.
3. ceramic applications as claimed in claim 2 are in the production technology of jewelry, it is characterised in that:In step S2, slot includes filling out
Fill area and non-filling area.
4. ceramic applications as claimed in claim 3 are in the production technology of jewelry, it is characterised in that:In step S4, paste is made pottery
Porcelain injects the fill area of slot, and the non-filling area of slot is not injected into paste ceramics.
5. ceramic applications as claimed in claim 4 are in the production technology of jewelry, it is characterised in that:In step S4, the filling of slot
The paste ceramics in area and the paste ceramics of ceramic accommodating cavity have contact surface.
6. ceramic applications as claimed in claim 5 are in the production technology of jewelry, it is characterised in that:In step S5, curing process
Atmospheric pressure for 110-130 kPas, temperature is 80-140 degrees Celsius, and the duration is 50-70 minutes.
7. ceramic applications as claimed in claim 6 are in the production technology of jewelry, it is characterised in that:In step S6, further include:
S61, thick grinding process is carried out to ceramics with the cotton piece buff for being coated with Chinese wax;
S62, thin grinding process is carried out to ceramics with the cotton piece buff for being coated with blue wax;
S63, finishing polish processing is carried out to ceramics with the cotton piece buff for being coated with yellow wax.
8. ceramic applications as claimed in claim 7 are in the production technology of jewelry, it is characterised in that:In step S1, including passing through
Casting, holds the step of mould, coating, ultraviolet light dry making jewellery matrix at system material.
9. ceramic applications as claimed in claim 8 are in the production technology of jewelry, it is characterised in that:Ultraviolet light is dried the step of
In, the time that ultraviolet light is dried is 35-45 seconds.
10. ceramic applications as claimed in claim 9 are in the production technology of jewelry, it is characterised in that:After step S6, further include
The step of processing of electricity gold and cleaning are carried out to jewellery matrix.