CN108166704A - A kind of thin-coat plaster heat insulating decorative board and preparation method thereof - Google Patents
A kind of thin-coat plaster heat insulating decorative board and preparation method thereof Download PDFInfo
- Publication number
- CN108166704A CN108166704A CN201711462455.5A CN201711462455A CN108166704A CN 108166704 A CN108166704 A CN 108166704A CN 201711462455 A CN201711462455 A CN 201711462455A CN 108166704 A CN108166704 A CN 108166704A
- Authority
- CN
- China
- Prior art keywords
- coat
- parts
- thin
- heat insulating
- mortar
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of thin-coat plaster heat insulating decorative boards and preparation method thereof, anchoring piece is embedded in composite plate, its preparation process mainly includes pre-buried anchoring piece, criticizes and scrape bedding mortar, embedment grid cloth, criticize and scrape decorative mortar, batch Puttying, smear priming paint, finishing coat and overlay film etc., ten more steps completed at the construction field (site) by professional is needed largely to simplify to be factory produced tradition, it reduces production cost, shorten construction period, be suitble to large-scale production.
Description
Technical field
The present invention relates to heat insulation decoration integrated plate technical field, more particularly, to a kind of thin-coat plaster heat insulating decorative board and its system
Preparation Method.
Background technology
It is well known that with time, the variation of natural environment, building surface layer can gradual aging, occur blackening, flake,
Therefore phenomena such as cracking, coming off, can install outer on the outer veneer of wall of more and more building surface layer, particularly buildings now
Wall heat insulation decoration integrated board.
Insulation and decoration integrated plate is also energy-saving heat preserving decorative integrated plate, is by adhesive layer, insulation and decoration production board, anchoring
The compositions such as part, sealing material.Arrangement and method for construction is numerous, is applicable not only to the exterior-wall heat insulation and decoration of new building, is also applied for old build
The energy saving and decorative reformation built；All kinds of public buildings are not only suitable for, are also applied for the exterior insulation of residential housing；It is not only suitable for
The building of north cold area is also applied for southern hot area's building.Its heat insulation effect is outstanding, and cold bridge effect is few, energy saving guarantor
Temp effect is good.
But traditional integrated board needs to be assembled by professional at the construction field (site), and production requirement is high, and manufacturing cost is high
It is high, while assembling procedure is numerous and diverse so that construction period greatly prolongs, in the engineering especially to work to tight deadlines in some needs, these
Time is particularly valuable, therefore the preparation of traditional integrated board has been difficult in adapt to the demand of new era.
Invention content
The present invention provides a kind of thin-coat plaster heat insulating decorative boards and preparation method thereof, need to applied with solving existing integrated board
Work scene is assembled, and trivial operations, it is time-consuming and laborious the problem of.
In order to solve the above-mentioned technical problem, the technical solution adopted by the present invention is summarized as follows：
A kind of composite plate, be embedded with anchoring piece in composite plate, and the anchoring piece includes anchor bolt and is flexibly connected with anchor bolt
Holdfast.
The preparation method of above-mentioned composite plate, includes the following steps：
A. pre-buried anchoring piece is squeezed into substrate side, wherein, the substrate is modified EPS plate, low-density EPS sheet, XPS plate
And any one in SEPS plates；
B. the substrate described in step a squeezes into the side of pre-buried anchoring piece and spreads bedding mortar, on the outside of bedding mortar
Grid cloth is applied, and decorative mortar is spread on the outside of grid cloth；
C. putty is spread on the outside of the decorative mortar in stepb, seal coat is painted on the outside of putty；
D. finishing coat, and the overlay film on the outside of finishing coat are painted on the outside of the seal coat described in step c, obtains product.
Further, the bedding mortar, decorative mortar are anticracking grout, and the anticracking grout includes following weight
The component of part：20-40 parts of silicon cement；50-70 parts of washed-out sand；5-10 parts of VAE rubber powders；0.2-0.5 parts of cellulose.
Anticracking grout in this programme is special mortar, and tensile capacity is far superior to ordinary mortar, so that obtained
The integrated board that the more general construction site of integrated board break resistance is assembled is more excellent.
Further, the finishing coat is any one or more in texture paint, lacquer, emulsion paint, multi-color.
Multi-color color polyisocyanate, aesthetic feeling is full, and simulation quality is strong, and the surface constructed has three-dimensional sense and multi-color decorative U.S.
Sense, is suitable for personnalité external wall facing；Building after lacquer finishing has natural true natural colour,
Give elegance, harmonious, serious aesthetic feeling particularly decorates on curved-surface building object, can receive vivid, back to nature
The effect of；Texture paint natural environmental-protective, non-toxic and tasteless, not only waterproof but also with good gas permeability, decoration texture is strong, three-dimensional decoration
It makes random；Emulsion paint is non-toxic and tasteless, colour retention and alkali resistance are strong, waterproof and good permeability, designs and varieties are various, and color is fresh
It is gorgeous, light.Several paints can be selected arbitrarily as needed, then be prepared, so as to can more be bonded the actual demand of user.
Further, the substrate is modified A grades of fire-proof plates.
Further, the modified A grades of fire-proof plates are made by any one in following two methods：
1) technique permeated by negative-pressure adsorption pours into inorganic fire slurry in low-density EPS sheet, and conserved；
2) EPS expanded beads and inorganic fire slurry in proportion are stirred evenly, finished product is cut in injection molding maintenance；
Wherein, the inorganic fire slurry includes the component of following parts by weight：40-60 parts of portland cement；Coarse whiting 10-20
Part；1-5 parts of Si modification auxiliary agent；10-20 parts of water.
A grades of fire-proof plates of the modification being obtained by this method overcome the shortcomings that traditional polystyrene foam plate is inflammable, reach completely
To A as defined in the Ministry of Public Security2Grade fire-protection standard, and waste material, waste water, exhaust gas will not be generated in process of production, when big fire is burnt
Smoke-free and tasteless, the leftover pieces generated in production process can also reuse, and practitioner will not cause silicosis, and to surrounding
Environment is safe from harm, and is a kind of reliable refractory material of environmental protection.The use of modified A grades of fire-proof plates so that this programme can be with simple
Efficiently the excellent integrated board of fire protecting performance is made in technique.
In conclusion by adopting the above-described technical solution, the beneficial effects of the invention are as follows：
When needing compared to tradition using heat insulation decoration integrated plate, it can only be assembled at the construction field (site) by professional,
Production requirement is high, and manufacturing cost is high, while assembling procedure is numerous and diverse, long construction period, the program that the present invention will prepare composite plate
Most of batch production only needs a small amount of work that can complete the installation of composite plate, greatly shortens and apply in construction site
Work period, while simple production process can be produced in batches, and the composite plate produced has good energy-saving heat preserving effect；
In addition, anchoring piece is divided into anchor bolt and holdfast, by anchor bolt preburied in substrate, later stage composite plate only need to be by anchor bolt and holdfast when installing
Connection, and in the hole that holdfast insertion wall is reserved, finishing coat is made when simplifying installation process, while being also avoided that installation
Into damage.
In short, the input of the present invention is relatively fewer, price is relatively low, easy to use, is without complicated construction technology
It can quickly produce, there is great promotional value.
Description of the drawings
Fig. 1 is anchoring piece position view in composite plate；
Fig. 2 is thin-coat plaster insulation and decoration plate structure schematic diagram produced by the present invention；
In figure label for：1- base course walls, 2- binding sand pulp layer, 3- thin-coat plaster heat insulating decorative boards, 4- anchor bolts, 5- holdfasts,
6- binding sand pulp layer, 7- substrates, 8- bedding mortars, 9- grid cloths, 10- decorative mortars, 11- putty, 12- seal coats, 13-
Finishing coat.
Specific embodiment
The present invention is described in further detail With reference to embodiment.Embodiments of the present invention are included but not
It is limited to the following example.
Embodiment 1
Prepare raw material：Anchoring piece, mortar, grid cloth, putty, paint, XPS plate, film.
Prepared by composite plate, include the following steps：
A. XPS plate is taken as substrate 7, the anchor bolt 4 in the pre-buried anchoring piece in 7 side of substrate；
B. bedding mortar 8 is spread in the side of 7 cast-in fixing bolt 4 of substrate described in step a, is applied in 8 outside of bedding mortar
Upper grid cloth 9, and spread decorative mortar 10 in 9 outside of grid cloth；
C. putty 11 is spread in 10 outside of the decorative mortar in stepb, and seal coat 12 is painted in 11 outside of putty；
D. the outside of seal coat 12 described in step c paints finishing coat 13, and in 13 side overlay film of finishing coat, obtains product.
Anchor bolt 4 wherein in anchoring piece is flexibly connected with holdfast 5 by screw thread, when making thin-coat plaster heat insulating decorative board 3
It is anchor bolt 4 is pre-buried in a substrate, and the screw socket of anchor bolt 4 is exposed to outside thin-coat plaster heat insulating decorative board 3, when mounted by anchor bolt 4 with
Holdfast 5 is threadably secured connection, then holdfast 5 is inserted into the hole that wall is reserved, without individually being protected again from thin-coat plaster
Punching is anchored in warm decorative panel 3, has both avoided the destruction of veneer coating layer, is also avoided that in punching and thin-coat plaster is kept the temperature
Structure inside decorative panel 3 damages, and reduces its service life, while simplify installation process, shortens construction period, protects
The integrality of 3 internal structure of thin-coat plaster heat insulating decorative board is demonstrate,proved.
When carrying out composite plate installation using anchoring piece, mainly include the following steps that：
A. hanging wire, snap the line on base course wall 1 exist according to the position of 4 screw socket of anchor bolt on thin-coat plaster heat insulating decorative board plate 3
Corresponding 1 surface of base course wall punching, hole depth are adapted with diameter with anchoring piece；
Before hanging wire, snap the line, ensure that base course wall 1 reaches quality standards by the acceptance of work, the residue of metope and de-
Mould agent is cleaned out, and chisel or repairing have been picked in the overproof part of degree of plainness for wall surface, and external scaffolding or hanging basket are installed by job requirements,
And through Security Officer's acceptance(check), adapted operation ensures safe and punctual, and distance must be more than 20cm to scaffold from the ground.
According to the size of the anchor bolt 4 at 3 back side of thin-coat plaster heat insulating decorative board, bore dia 1.5-2cm, depth 3-4.5cm,
Having beaten hole needs to clear up dust, and tamp hole using adhesive mortar,.
B. holdfast 5 is tightened into 4 screw socket of anchor bolt at 3 back side of thin-coat plaster heat insulating decorative board first, then is protected toward thin-coat plaster
The backside surface of warm decorative panel 3 smears binding sand pulp layer 6；
The method that the backside surface of thin-coat plaster heat insulating decorative board 3 smears adhesive mortar can be：Using trowel in every block of plate
The back side uniformly scratches the bonding point of 6-8 blocks diameter about 10cm, thickness 8-10mm, this bonding point must be arranged uniformly；
C., holdfast 5 on thin-coat plaster heat insulating decorative board 3 is aligned to the hole tamped on base course wall 1 through adhesive mortar so that
Holdfast 5 on thin-coat plaster heat insulating decorative board 3 is caught in hole, 3 paving of thin-coat plaster heat insulating decorative board to 1 surface of base course wall, is completed
The installation of thin-coat plaster heat insulating decorative board 3.
Thin-coat plaster heat insulating decorative board 3 should pressing board length, should when plate is attached on metope to paving in the horizontal direction from the bottom up
It is carried out gently flattening operation with 2m guiding rulers, is sure not to tap in order to avoid destroying the veneer coating in 3 front face surface of thin-coat plaster heat insulating decorative board
Layer ensures its flatness and pastes securely.
In addition, when the holdfast 5 in composite plate 3 is caught in the hole tamped through adhesive mortar, the adhesive mortar in hole is in still
Unhardened state.
The preparation scheme process of the present embodiment is simple, and above-mentioned steps can be completed in factory, built so as to be greatly shortened
The construction period in place is built, and cost is relatively low, it is applied widely, it is appropriate for large-scale promotion.
Embodiment 2
It is prepared by modified A grades of fire-proof plates：
1) 50 parts of portland cement is taken；10 parts of coarse whiting；4 parts of Si modification auxiliary agent；15 parts of water；
2) more than raw material is mixed and stirred evenly, to inorganic fire slurry；
3) technique permeated by negative-pressure adsorption pours into inorganic fire slurry in low-density EPS sheet, after being conserved
To modified A grades of fire-proof plates.
It is prepared by anticracking grout：Take 35 parts of silicon cement；60 parts of washed-out sand；8 parts of VAE rubber powders；0.4 part of cellulose.Routinely sand
Prepared by slurry preparation method, details are not described herein.
Prepare raw material：Anchoring piece, anticracking grout, grid cloth, putty, paint, modified A grades of fire-proof plates, films.
Prepared by composite plate, include the following steps：
A. modified A grades of fire-proof plates obtained are taken as substrate 7, the anchor bolt 4 in the pre-buried anchoring piece in 7 side of substrate；
B. bedding mortar 8 is spread in the side of 7 cast-in fixing bolt 4 of substrate described in step a, is applied in 8 outside of bedding mortar
Upper grid cloth 9, and spread decorative mortar 10 in 9 outside of grid cloth；
C. putty 11 is spread in 10 outside of the decorative mortar in stepb, and seal coat 12 is painted in 11 outside of putty；
D. the outside of seal coat 12 described in step c paints finishing coat 13, and in 13 side overlay film of finishing coat, obtains product.
Wherein, the decorative mortar 10, bedding mortar 8 are anticracking grout obtained.
Relative to the product of embodiment 1, the product fire protecting performance and break resistance of embodiment 2 have obtained greatly carrying
It rises, can more meet building demand.
Embodiment 3
It is prepared by modified A grades of fire-proof plates：
1) 60 parts of portland cement is taken；20 parts of coarse whiting；5 parts of Si modification auxiliary agent；20 parts of water；
2) more than raw material is mixed and stirred evenly, to inorganic fire slurry；
3) EPS expanded beads and inorganic fire slurry in proportion are stirred evenly, injection molding maintenance, cutting obtains A grades modified
Fire-proof plate；
Prepare raw material：Anchoring piece, mortar, grid cloth, putty, paint, modified A grades of fire-proof plates, films.
Prepared by composite plate, include the following steps：
A. modified A grades of fire-proof plates obtained are taken as substrate 7, the anchor bolt 4 in the pre-buried anchoring piece in 7 side of substrate；
B. bedding mortar 8 is spread in the side of 7 cast-in fixing bolt 4 of substrate described in step a, is applied in 8 outside of bedding mortar
Upper grid cloth 9, and spread decorative mortar 10 in 9 outside of grid cloth；
C. putty 11 is spread in 10 outside of the decorative mortar in stepb, and seal coat 12 is painted in 11 outside of putty；
D. the outside of seal coat 12 described in step c paints finishing coat 13, and in 13 side overlay film of finishing coat, obtains product.
Comparative example
A kind of heat insulation decoration integrated plate preparation method mainly includes the following steps：
1) inorganic board is chosen；2) fixed thick sand milling, at least twice；3) dedusting；4) resin imports；5) UV putty is applied；6) sand
Levigate sand；7) dedusting；8) (washed ore) is sanded；9) dedusting, until detection dust content is qualified；10) priming paint is applied；11) it toasts
Until priming paint condenses；12) second time priming paint is brushed；13) baking is until priming paint condenses；14) dedusting；15) finishing coat is brushed one times；16) it dries
It bakes to finishing coat and condenses；17) cover；18) it toasts；19) overlay film；20) it is compound；21) cutting obtains product.
Compared with the embodiment of the present invention, long construction period, trivial operations are with high costs, consume a large amount of manpower
Material resources are not suitable for carrying out large batch of production, and need to punch on integrated board when mounted, can be to veneer coating layer and one
Intralamellar part structure causes to damage, and reduces the performance of integrated board.
It is the embodiment of the present invention as described above.The present invention is not limited to the above-described embodiments, anyone should learn that
The structure change made under the enlightenment of the present invention, the technical schemes that are same or similar to the present invention each fall within this
Within the protection domain of invention.
Claims (6)
1. a kind of thin-coat plaster heat insulating decorative board, which is characterized in that anchoring piece is embedded in composite plate, the anchoring piece includes anchor bolt
And the holdfast being flexibly connected with anchor bolt.
2. a kind of preparation method of thin-coat plaster heat insulating decorative board as described in claim 1, includes the following steps：
A. squeeze into pre-buried anchoring piece in substrate side, wherein, the substrate for modified EPS plate, low-density EPS sheet, XPS plate and
Any one in SEPS plates；
B. the substrate described in step a squeezes into the side of pre-buried anchoring piece and spreads bedding mortar, is applied on the outside of bedding mortar
Grid cloth, and decorative mortar is spread on the outside of grid cloth；
C. putty is spread on the outside of the decorative mortar in stepb, seal coat is painted on the outside of putty；
D. finishing coat, and the overlay film on the outside of finishing coat are painted on the outside of the seal coat described in step c, obtains product.
3. a kind of preparation method of thin-coat plaster heat insulating decorative board as claimed in claim 2, the bedding mortar, decorative mortar
It is anticracking grout, the anticracking grout includes the component of following parts by weight：20-40 parts of silicon cement；50-70 parts of washed-out sand；VAE
5-10 parts of rubber powder；0.2-0.5 parts of cellulose.
4. as claim 2 a kind of thin-coat plaster heat insulating decorative board and preparation method thereof, which is characterized in that the finishing coat is
Any one or more in texture paint, lacquer, emulsion paint, multi-color.
5. a kind of preparation method of thin-coat plaster heat insulating decorative board as claimed in claim 2, which is characterized in that the substrate is
Modified A grades of fire-proof plates.
A kind of 6. preparation method of thin-coat plaster heat insulating decorative board as claimed in claim 5, which is characterized in that the modified A
Grade fire-proof plate is made by any one in following two methods：
1) technique permeated by negative-pressure adsorption pours into inorganic fire slurry in low-density EPS sheet, is obtained into after being conserved
Product；
2) EPS expanded beads and inorganic fire slurry in proportion are stirred evenly, injection molding maintenance obtains finished product after cutting；
Wherein, the inorganic fire slurry includes the component of following parts by weight：40-60 parts of portland cement；10-20 parts of coarse whiting；
1-5 parts of Si modification auxiliary agent；10-20 parts of water.