CN108084299B - Composition with polymerization initiating function and method for preparing acrylamide copolymer - Google Patents
Composition with polymerization initiating function and method for preparing acrylamide copolymer Download PDFInfo
- Publication number
- CN108084299B CN108084299B CN201611020630.0A CN201611020630A CN108084299B CN 108084299 B CN108084299 B CN 108084299B CN 201611020630 A CN201611020630 A CN 201611020630A CN 108084299 B CN108084299 B CN 108084299B
- Authority
- CN
- China
- Prior art keywords
- water
- composition
- initiator
- monomer mixture
- acid
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention relates to the field of petrochemical industry, and discloses a composition with a function of initiating polymerization reaction and a method for preparing an acrylamide copolymer. The composition with the function of initiating polymerization reaction contains organic amine and at least one compound shown as a formula I, wherein the weight ratio of the organic amine to the compound is 1: 0.0001-10000. The invention also discloses a method for preparing the acrylamide copolymer, which comprises the following steps: the monomer mixture is polymerized in water in the presence of an initiator, which is provided by the composition of the present invention. By adopting the thioxanthone compound as the initiator, higher polymerization reaction efficiency (higher viscosity average molecular weight of the acrylamide copolymer) can be obtained at lower initiation temperature.
Description
Technical Field
The invention relates to the field of petrochemical industry, in particular to a composition with a function of initiating polymerization reaction and a method for preparing an acrylamide copolymer.
Background
In the conventional oil reservoir oil displacement process, the high molecular weight partially hydrolyzed polyacrylamide can realize the winding state between molecular chains under the condition of lower concentration, has obvious tackifying effect, better chemical stability and high viscosity retention rate, can continuously reduce the water-oil fluidity ratio, improve swept volume and reduce the oil saturation of the swept oil reservoir, thereby improving the recovery ratio, and is a polymer product for oil displacement which is widely used in tertiary oil recovery of an oil field. With the exploitation of recoverable reserves in conventional oil reservoirs, the reservoir conditions for replacing reserves become more severe, and the oil displacing polymer is required to have higher temperature resistance, salt resistance and shear resistance.
Therefore, it is desirable to develop a novel initiation system to obtain a temperature-resistant and salt-tolerant oil-displacing polymer by using a novel polymerization method. The common production processes of the prior polyacrylamide powder products include a hydrolysis process after homopolymerization of an acrylamide monomer and a copolymerization process of the acrylamide monomer and an acrylic acid monomer. In any process, the polymerization process mainly comprises the steps of preparing a mixed aqueous solution with a certain concentration from monomers such as acrylamide, acrylic acid and the like, carrying out thermal initiation or photo-initiation polymerization through an oxidation-reduction system or azo compounds and the like, and carrying out post-treatment to obtain the product. The conventional method has high initial initiation temperature, the polymerization process is not easy to master, the product quality is difficult to control, and particularly, the dissolution time and the viscosity of the product have large fluctuation. In the prior report of preparing polyacrylamide oil displacement agent by related light initiation, for example, CN1590421A adopts the method of using persulfate and NaHSO2·CH2O·2H2O, azo compounds and complexing agentsThe photosensitizer is a copolymerization powder product obtained by an acrylamide monomer and a cationic monomer; CN101353392A utilizes a photosensitizer-co-photosensitizer or common oxidation-reduction initiation system to mix materials, pour the materials on a plane and spread the materials into a sheet shape, and the sheet shape is irradiated by ultraviolet light to obtain high molecular weight instant cationic polyacrylamide; CN102321221A discloses a preparation method of a star polyacrylamide polymer, which adopts an aqueous solution photopolymerization mode to synthesize star polyacrylamide by copolymerization of monomers such as acrylamide and the like initiated by thioxanthone modified polyethyleneimine. The polymer obtained by the method has enhanced mechanical shear resistance, but the process operation is relatively complicated, the molecular weight of the obtained product is small, and the practicability needs to be improved.
Disclosure of Invention
The invention aims to overcome the defects of the prior art and provide a composition with a polymerization initiating function and a method for preparing an acrylamide copolymer, wherein the composition can be used for obtaining high polymerization efficiency at a lower temperature.
In order to achieve the above object, in a first aspect, the present invention provides a composition having a function of initiating polymerization, the composition comprising an organic amine and at least one compound described in the first aspect, wherein the weight ratio of the organic amine to the at least one compound described in the first aspect is 1: 0.0001-10000,
wherein R is1、R2、R3、R1’、R2' and R3' are respectively and independently hydrogen, alkyl, alkoxy, halogen, nitro, amino, alkylamino or a long chain of ethoxyether with the carbon number of 1-255, and n is an integer of 1-255.
In a second aspect, the present invention provides a method for preparing an acrylamide copolymer, the method comprising: polymerizing a monomer mixture in water under photopolymerization conditions in the presence of an initiator, wherein the initiator is provided by the composition of the first aspect and the monomer mixture comprises acrylamide.
By adopting the thioxanthone compound as an initiator, the polyacrylamide oil displacement polymer with viscosity average molecular weight of 2800-3400 ten thousand can be obtained at lower initiation temperature, and the obtained polymer has good temperature resistance, salt resistance and shear resistance.
Additional features and advantages of the invention will be set forth in the detailed description which follows.
Detailed Description
The following describes in detail specific embodiments of the present invention. It should be understood that the detailed description and specific examples, while indicating the present invention, are given by way of illustration and explanation only, not limitation.
The endpoints of the ranges and any values disclosed herein are not limited to the precise range or value, and such ranges or values should be understood to encompass values close to those ranges or values. For ranges of values, between the endpoints of each of the ranges and the individual points, and between the individual points may be combined with each other to give one or more new ranges of values, and these ranges of values should be considered as specifically disclosed herein.
The composition with the function of initiating polymerization reaction provided by the invention contains organic amine and at least one (water-soluble) thioxanthone compound shown in formula I, wherein the weight ratio of the organic amine to the at least one compound shown in formula I is 1: 0.0001 to 10000, preferably 1: 0.002 to 500, more preferably 1: 0.1 to 10, most preferably 1: 0.1-1.
The (water-soluble) thioxanthone compounds used in the invention have a structure represented by the following formula I:
wherein R is1、R2、R3、R1’、R2' and R3' independently of one another, is hydrogen, alkyl, alkoxy, halogen, nitro, amino, alkylamino or a carbon atomLong chain ethoxyether groups of 1 to 255 (preferably 1 to 250, more preferably 5 to 50, most preferably 10 to 20), and n is an integer of 1 to 255 (preferably 1 to 250, more preferably 5 to 50, most preferably 15 to 20).
In the present invention, the alkyl group is preferably a C1-C4 alkyl group such as methyl, ethyl, n-propyl, isopropyl, n-butyl, sec-butyl, isobutyl, tert-butyl, etc.
The alkoxy can be C1-C4 alkoxy, such as methoxy, ethoxy, propoxy, etc.
Halogen may be F, Cl, Br or I.
The alkylamino group can be represented by the general formula-NH-R14Wherein R is14It may be a C1-C4 alkyl group such as methyl, ethyl, n-propyl, isopropyl, n-butyl, sec-butyl, isobutyl, tert-butyl, etc.
The long chain of the ethoxy ether group has a general formula of-O (CH)2CH2O)m-R, wherein m may be from 1 to 125 (preferably from 1 to 120, more preferably from 5 to 50, most preferably from 15 to 20), and R may be a C1-C4 alkyl group (e.g., methyl).
According to a more preferred embodiment of the invention, R1、R2、R3、R1’、R2' and R3' are each independently hydrogen or methyl.
According to the most preferred embodiment of the invention, R1、R2、R3、R1’、R2' and R3' are each independently hydrogen, or, R1And R1' is hydrogen and R2、R3、R2' and R3' are each independently methyl and n is 10 to 20.
In the composition of the present invention, the organic amine may be various amine reduction assistants commonly used in the art, and preferably, the organic amine is at least one of compounds represented by formula II below:
wherein R is11、R12And R13Each independently is hydrogen, straight-chain alkyl (C1-C5), branched-chain alkyl (C1-C5), cycloalkyl (C1-C6), aryl (C1-C6), alkoxy (C1-C6), halogen atom, nitro, sulfydryl, amino, alkylamino (C1-C6), arylamine (C1-C6), alkylhydroxy (C1-C6) or R11、R12And R13Any two of which can be cyclized to a (penta-, hexa-, hepta-or octa-membered) diazacyclo, and R11、R12And R13Not hydrogen at the same time.
More preferably, R11、R12And R13Independently of one another is hydrogen, -CH3、-C2H5、-CH2CH2OH、-CH(OH)CH3、-CH2CH2NH2、-CH(NH2)CH3、-C2H4N(CH3)2、-CON(CH3)2Or R11、R12And R13Any two of which are capable of cyclizing to a geminal diazacyclo, and R11、R12And R13Not hydrogen at the same time.
Further preferably, the organic amine is at least one of N, N ' -tetramethylethylenediamine, N-dimethylethanolamine, N ' -dimethylpiperazine, N ' -tetramethylurea, and triethanolamine.
According to the present invention, the composition may further contain a water-soluble azo initiator in order to further improve the polymerization efficiency. There is no particular requirement on the content of the water-soluble azo initiator, and preferably, the weight ratio of the organic amine to the water-soluble azo initiator is 1: 0.0001 to 10000, more preferably 1: 0.002 to 500, more preferably 1: 0.1 to 10, most preferably 1: 0.1-1.
The water-soluble azo initiator may be a water-soluble azo initiator commonly used in the art, and preferably, the water-soluble azo initiator is at least one selected from the group consisting of 2,2 '-azobis (2-amidinopropane) dihydrochloride, 2' -azobis (2-imidazolinopropane) dihydrochloride, and 4,4 '-azobis (4-cyanovaleric acid), and more preferably, 2' -azobis (2-amidinopropane) dihydrochloride.
According to a preferred embodiment of the invention, the composition further comprises a water-soluble azo initiator, and the weight ratio of the organic amine, the at least one thioxanthone compound as described above and the water-soluble azo initiator is 1: 0.1-10: 0.1-10, wherein the organic amine is N, N, N ', N ' -tetramethyl ethylenediamine, and the water-soluble azo initiator is 2,2' -azobis (2-amidinopropane) dihydrochloride. The polymerization efficiency can be further improved by using the composition of the preferred embodiment as an initiator.
According to a preferred embodiment of the invention, the composition consists of the above-mentioned ingredients. Generally, each component of the composition of the present invention is stored independently and added to the polymerization reaction system at the time of use.
The method for preparing the acrylamide copolymer comprises the following steps: polymerizing a monomer mixture in water under photopolymerization conditions in the presence of an initiator, wherein the initiator is provided by the composition and the monomer mixture contains acrylamide.
In the present invention, the initiator is preferably used in an amount of 0.00001 to 0.5% by weight, more preferably 0.0001 to 0.3% by weight, based on the weight of the monomer mixture.
In the present invention, acrylamide is preferably used in an amount of 30 to 99% by weight based on the total weight of the monomer mixture.
In the present invention, the photopolymerization reaction is carried out in water, and the ratio of the weight of the monomer mixture to the total weight of water and the monomer mixture at the time of initiation of the photopolymerization reaction is not particularly limited and can be varied within a wide range, and preferably, the ratio of the weight of the monomer mixture to the total weight of water and the monomer mixture at the time of initiation of the photopolymerization reaction is from 0.15 to 0.4: 1, more preferably 0.2 to 0.3: 1.
according to the present invention, the conditions of the photopolymerization reaction may be those conventional in the art. For example, the photopolymerization reaction is performed under an inert atmosphere and irradiation of ultraviolet light, and the photopolymerization reaction conditions may include: the polymerization is initiated at a temperature of from 0 ℃ to 50 ℃ (preferably from 10 ℃ to 40 ℃), for a period of from 2 to 12 hours (preferably from 4 to 8 hours), and at a pH of from 4 to 12 (preferably from 5 to 10). The pH may be obtained by adding a pH adjusting agent, which may be various acidic pH adjusting agents and/or alkaline pH adjusting agents conventional in the art, to the polymerization system, and the alkaline pH adjusting agent may be an inorganic alkaline substance, such as at least one of sodium hydroxide, potassium hydroxide, and sodium carbonate, preferably sodium hydroxide; the acidic pH adjusting agent may be one or more of hydrochloric acid, sulfuric acid, and nitric acid.
The inert atmosphere is provided by a gas which does not react with the raw materials and the product, and may be provided by, for example, nitrogen gas or at least one of group zero element gases in the periodic table, preferably nitrogen gas, which is conventional in the art.
In the present invention, the irradiation conditions of ultraviolet light are not particularly limited as long as the polymerization reaction initiated by the photoinitiator can be promoted. Preferably, the power of the ultraviolet irradiation is 10-2000W (more preferably 100-1000W). The power here refers to the power of the uv lamp used and the invention is not limited to use with uv lamps, it being understood by those skilled in the art that other donors capable of producing uv light at the same intensity as 10-2000W uv lamps are equally suitable for use with the invention. In the case of using a 10-2000W ultraviolet lamp to provide ultraviolet light, the light source of the ultraviolet light is preferably 25-150cm from the reaction solution.
In the present invention, the monomer mixture may further contain a monomer a. Wherein the weight ratio of the monomer a to the acrylamide may be 0.001-10:1, preferably 0.05-3: 1. The monomer a can be various monomers capable of improving the temperature resistance and salt resistance effects of the polymer. Preferably, the monomer a is selected from at least one of acrylic acid, 2-acrylamido-2-methylpropanesulfonic acid, N-dimethylacrylamide, N-diethylacrylamide, vinylpyrrolidone, diallyldimethylammonium chloride, styrenesulfonic acid, vinylsulfonic acid, methylvinylsulfonic acid, 2-acrylamido-dodecylsulfonic acid, 2-acrylamido-tetradecanesulfonic acid, 2-acrylamido-hexadecanesulfonic acid, dodecyldimethylallylammonium chloride, tetradecyldimethylallyl ammonium chloride, hexadecyldimethylallylammonium chloride and octadecyldimethylaluminum chloride, more preferably 2-acrylamido-2-methylpropanesulfonic acid.
In the present invention, the method may further comprise hydrolyzing and drying the polymer obtained after the polymerization reaction, the hydrolysis allowing the degree of hydrolysis of the polymer obtained after the polymerization reaction to be 10 to 40%. As will be appreciated by those skilled in the art, the process of hydrolysis involves reacting a hydrolyzing agent with the polymer. By hydrolysis, part of the acrylamide structural units is converted into acrylate structural units.
In the present invention, the conditions of the hydrolysis are not particularly limited, and preferably, the conditions of the hydrolysis include: the temperature is 50-110 ℃, and the optimal temperature is 70-90 ℃; the time is 0.5 to 6 hours, preferably 1 to 4 hours.
In the present invention, the degree of hydrolysis means the percentage of the number of moles of the acrylate structural unit to the total number of moles of the structural units of the acrylamide copolymer of the present invention. The degree of hydrolysis is determined by the amount of the hydrolytic agent of the invention.
In the present invention, the hydrolytic agent is various inorganic alkaline substances commonly used in the art to achieve the above purpose, and may be selected from one or more of sodium hydroxide, potassium hydroxide and sodium carbonate. The amount of the hydrolyzing agent may be appropriately selected depending on the degree of hydrolysis of the acrylamide copolymer so that the degree of hydrolysis of the acrylamide copolymer satisfies the use requirements, and the inorganic basic substance is preferably used so that the degree of hydrolysis of the acrylamide copolymer is 10 to 40%.
As will be appreciated by those skilled in the art, acrylamide copolymers of varying degrees of hydrolysis can be obtained by adjusting the amount of inorganic basic material used.
In the present invention, the number of moles of the inorganic basic substance is equal to the number of moles of the acrylate structural unit.
According to the invention, the invention has no special requirements on the drying conditions, the drying method can adopt a hot air drying method, and the hot air drying temperature can be 40-120 ℃, preferably 70-90 ℃; the time is 0.2 to 4 hours, preferably 0.5 to 2 hours.
In addition, the method of the present invention may further include crushing and screening the dried product, and the crushing and screening conditions may be reasonably selected according to the prior art, and are not described herein again.
In a preferred embodiment of the present invention, the preparation method of the acrylamide copolymer comprises the steps of:
(1) mixing an acrylamide monomer, a monomer a and water to form a comonomer aqueous solution, adjusting the pH to 5-10 by using an inorganic alkaline substance, and controlling the initial temperature of solution polymerization to be 0-50 ℃;
(2) introducing nitrogen into the comonomer aqueous solution to remove oxygen, and controlling the oxygen content in the solution to be less than 1 mg/L;
(3) adding an initiator system into the monomer aqueous solution under the conditions of introducing nitrogen and irradiating by ultraviolet light, and carrying out photopolymerization reaction to obtain polymer gel;
(4) and (3) carrying out primary granulation, hydrolysis, secondary granulation, drying, crushing and screening on the polymer gel to obtain the temperature-resistant and salt-resistant acrylamide copolymer product.
The present invention will be described in detail below by way of examples.
In the following examples and comparative examples, acrylamide was purchased from Baumo Biochemical industries, Inc.; 2-acrylamido-2-methylpropanesulfonic acid was purchased from xiamen changtian corporation; 2,2 '-azobis (2-amidinopropane) dihydrochloride (2,2' -azobisisobutylamidine dihydrochloride) was purchased from Aldrich; thioxanthone was purchased from Aldrich; the structure of the water-soluble thioxanthone compound 1 is shown as a formula I, and R1、R2、R3、R1’、R2' and R3' is hydrogen, n is 16, and the synthesis method is as follows: dissolving 10g of polyethylene glycol (number average molecular weight 750) in 50ml of toluene, adding 1ml of pyridine and 6ml of thionyl chloride, refluxing at 120 ℃ for 2h, cooling the reaction solution to room temperature, filtering, evaporating the filtrate under reduced pressure to remove the toluene, cooling to room temperature, adding 40ml of dichloromethane and 25g of Al into the obtained viscous liquid2O3Stirring for 2h, filtering, evaporating dichloromethane from the filtrate under reduced pressure, dripping the residue into 300ml of cold anhydrous ether to separate out white precipitate, performing suction filtration, and drying the filter cake under reduced pressure to obtain the dichloroopolymerEthylene glycol, 0.5g sodium hydride, 50.0mL toluene, 4 g 2-hydroxythioxanthone in a three-necked flaskStirring and heating to 85 ℃, adding 7 g of dichloropolyethylene glycol, reacting for 24h, dropwise adding 2mol/L hydrochloric acid isopropanol solution to adjust the pH value to 4, removing most of solvent by spinning, separating out solid, pouring out upper layer toluene solution, repeatedly washing with diethyl ether, evaporating to remove diethyl ether, and drying in vacuum to obtain a product, wherein the product is characterized by infrared spectrum, and in the infrared spectrum, 1625cm-1The position is a carbonyl absorption peak in thioxanthone, 1600cm-1、1590cm-1Is the absorption peak of the carbon-carbon double bond of the benzene ring at 1110cm-1The broad peak of (A) is a characteristic absorption peak of a C-O-C group in polyethylene glycol, and a target product is obtained by matching nuclear magnetism and mass spectrum results;
the structure of the water-soluble thioxanthone compound 2 is shown as the formula I, and R1And R1' is hydrogen, R2、R3、R2' and R3' is methyl, n is 16, and the synthesis method is as follows: dissolving 10g of polyethylene glycol (number average molecular weight 750) in 50ml of toluene, adding 1ml of pyridine and 6ml of thionyl chloride, refluxing at 120 ℃ for 2h, cooling the reaction solution to room temperature, filtering, evaporating the filtrate under reduced pressure to remove the toluene, cooling to room temperature, adding 40ml of dichloromethane and 25g of Al into the obtained viscous liquid2O3Stirring for 2h, filtering, evaporating dichloromethane from the filtrate under reduced pressure, dropping the residue into 300mL of cold anhydrous ether to separate out white precipitate, performing suction filtration, drying the filter cake under reduced pressure to obtain the dichloropolyethylene glycol, adding 0.5g of sodium hydride and 50.0mL of toluene into a three-necked flask, adding 4.5 g of 2-hydroxy-3, 4-dimethyl-thioxanthoneStirring and heating to 85 ℃, adding 7 g of dichloropolyethylene glycol, reacting for 24h, dropwise adding 2mol/L hydrochloric acid isopropanol solution to adjust the pH value to 4, removing most of solvent by spinning, separating out solid, pouring out upper layer toluene solution, repeatedly washing with diethyl ether, evaporating to remove diethyl ether, and drying in vacuum to obtain a product, wherein the product is characterized by infrared spectrum, and in the infrared spectrum, 1625cm-1The position is a carbonyl absorption peak in thioxanthone, 1600cm-1、1590cm-11440cm is the absorption peak of the carbon-carbon double bond of the benzene ring-1、1398cm-1And 1358cm-11110cm for bending vibration of methyl and methylene-1The broad peak of (A) is a characteristic absorption peak of a C-O-C group in polyethylene glycol, and a target product is obtained by matching nuclear magnetism and mass spectrum results;
commercially available products are high molecular weight polyacrylamides (type: Japanese MO4000) with a molecular weight of 2200 ten thousand; the polymer properties in the examples were tested as follows:
1. the dissolution time was measured according to the method described in GB 12005.8-89;
2. intrinsic viscosity [ eta ]]Viscous phase relative molecular mass MηAccording to the oil and gas industry standard of the people's republic of China (SY/T5862-2008), the intrinsic viscosity [ eta ] is measured by a dilution method]=H/C0Calculating the molecular weight M by the formulaη=([η]/0.000373)1.515;
3. The apparent viscosity of the aqueous polymer solution was determined at a temperature of 95 ℃ using a Brookfield viscometer, the polymer solution concentration was 1500mg/L, the salinity of the brine was 30000mg/L, the divalent calcium and magnesium ions were 1000mg/L, and the shear rate was 7.34s-1;
4. And (3) measuring the filtration ratio, the shear viscosity retention rate and the AM residual monomer content of the aqueous solution of the polymer according to the enterprise standard Q/SH 10201572-2006 of China petrochemical group Shengli Petroleum administration.
Example 1
This example illustrates the preparation of acrylamide copolymers using thioxanthone-based compounds of the present invention as initiators.
1500 g of acrylamide, 75 g of 2-acrylamido-2-methylpropanesulfonic acid and 6300 g of deionized water are added into a polymerization bottle, the temperature of the solution is controlled at 0 ℃ under the stirring state, and sodium hydroxide is added to adjust the pH value to 7. 1.575 mg of water-soluble thioxanthone compound 1, 1.575 mg of N, N, N ', N ' -tetramethylethylenediamine and 1.575 mg of water-soluble azo initiator 2,2' -azobis (2-amidinopropane) dihydrochloride are added, high-purity nitrogen is introduced for deoxygenation for 0.5h, and the oxygen content in the solution is controlled to be less than 1 mg/L. Carrying out photopolymerization reaction (100W ultraviolet irradiation) for 5h to obtain the polymer block. And granulating the rubber block into 4-6 mm small rubber particles by a granulator. Kneading and contacting the obtained small colloidal particles with 171.69 g of sodium hydroxide granular alkali, hydrolyzing at 90 ℃ for 4h, drying, crushing and screening to obtain a product with 20-80 meshes, wherein the performance test results are shown in Table 1.
Example 2
This example illustrates the preparation of acrylamide copolymers using thioxanthone-based compounds of the present invention as initiators.
250 g of acrylamide, 750 g of 2-acrylamido-2-methylpropanesulfonic acid and 2333.33 g of deionized water are added into a polymerization bottle, the solution temperature is controlled at 40 ℃ under the stirring state, and sodium hydroxide is added to adjust the pH value to 5. 1000mg of water-soluble thioxanthone compound 1, 1000mg of N, N, N ', N ' -tetramethylethylenediamine and 1000mg of water-soluble azo initiator 2,2' -azobis (2-amidinopropane) dihydrochloride are added, oxygen is removed for 0.5h by introducing high-purity nitrogen, and the oxygen content in the solution is controlled to be less than 1 mg/L. Carrying out photopolymerization reaction (1000W ultraviolet irradiation) for 6h to obtain the polymer block. And granulating the rubber block into 4-6 mm small rubber particles by a granulator. Kneading and contacting the obtained small colloidal particles with 57.08 g of sodium hydroxide granular alkali, hydrolyzing for 1h at the temperature of 70 ℃, drying, crushing and screening to obtain a product with the granularity of 20-80 meshes, wherein the performance test results are shown in Table 1.
Example 3
This example illustrates the preparation of acrylamide copolymers using thioxanthone-based compounds of the present invention as initiators.
1000 g of acrylamide, 500 g of 2-acrylamido-2-methylpropanesulfonic acid and 4500 g of deionized water are added into a polymerization bottle, the solution temperature is controlled at 0 ℃ under the stirring state, and sodium hydroxide is added to adjust the pH value to 10. 150 mg of water-soluble thioxanthone compound 1, 150 mg of N, N, N ', N ' -tetramethylethylenediamine and 150 mg of water-soluble azo initiator 2,2' -azobis (2-amidinopropane) dihydrochloride are added, oxygen is removed for 0.5h by introducing high-purity nitrogen, and the oxygen content in the solution is controlled to be less than 1 mg/L. Carrying out photopolymerization reaction (500W ultraviolet irradiation) for 8h to obtain the polymer block. And granulating the rubber block into 4-6 mm small rubber particles by a granulator. Kneading and contacting the obtained small colloidal particles with 74.16 g of sodium hydroxide granular alkali, hydrolyzing at the temperature of 85 ℃ for 2h, drying, crushing and screening to obtain a product with the granularity of 20-80 meshes, wherein the performance test results are shown in Table 1.
Example 4
This example illustrates the preparation of acrylamide copolymers using thioxanthone-based compounds of the present invention as initiators.
869.56 g of acrylamide, 60.43 g of 2-acrylamido-2-methylpropanesulfonic acid, 70 g of vinylpyrrolidone and 4000 g of deionized water are added into a polymerization flask, the solution temperature is controlled at 0 ℃ under stirring, and sodium hydroxide is added to adjust the pH to 10. 50 mg of water-soluble thioxanthone compound 1, 50 mg of N, N, N ', N ' -tetramethylethylenediamine and 50 mg of water-soluble azo initiator 2,2' -azobis (2-amidinopropane) dihydrochloride are added, oxygen is removed for 0.5h by introducing high-purity nitrogen, and the oxygen content in the solution is controlled to be less than 1 mg/L. Carrying out photopolymerization reaction (100W ultraviolet irradiation) for 8h to obtain the polymer block. And granulating the rubber block into 4-6 mm small rubber particles by a granulator. Kneading and contacting the obtained small colloidal particles with 74.16 g of sodium hydroxide granular alkali, hydrolyzing at 90 ℃ for 4h, drying, crushing and screening to obtain a product with 20-80 meshes, wherein the performance test results are shown in Table 1.
Example 5
This example illustrates the preparation of acrylamide copolymers using thioxanthone-based compounds of the present invention as initiators.
869.56 g of acrylamide, 110.43 g of 2-acrylamido-2-methylpropanesulfonic acid, 20 g of hexadecyldimethylallylammonium chloride and 4000 g of deionized water are added into a polymerization bottle, the solution temperature is controlled at 0 ℃ under the stirring state, and sodium hydroxide is added to adjust the pH to 7. 5 mg of water-soluble thioxanthone compound 1, 5 mg of N, N, N ', N ' -tetramethylethylenediamine and 5 mg of water-soluble azo initiator 2,2' -azobis (2-amidinopropane) dihydrochloride are added, oxygen is removed for 0.5h by introducing high-purity nitrogen, and the oxygen content in the solution is controlled to be less than 1 mg/L. Carrying out photopolymerization reaction (100W ultraviolet irradiation) for 8h to obtain the polymer block. And granulating the rubber block into 4-6 mm small rubber particles by a granulator. Kneading and contacting the obtained small colloidal particles with 130.43 g of sodium hydroxide granular alkali, hydrolyzing at 90 ℃ for 4h, drying, crushing and screening to obtain a product with 20-80 meshes, wherein the performance test results are shown in Table 1.
Example 6
This example illustrates the preparation of acrylamide copolymers using thioxanthone-based compounds of the present invention as initiators.
1000 g of acrylamide, 500 g of 2-acrylamido-2-methylpropanesulfonic acid and 4500 g of deionized water are added into a polymerization bottle, the solution temperature is controlled at 0 ℃ under the stirring state, and sodium hydroxide is added to adjust the pH value to 10. 1.5 mg of water-soluble thioxanthone compound 1, 1.5 mg of N, N, N ', N ' -tetramethylethylenediamine and 1.5 mg of water-soluble azo initiator 2,2' -azobis (2-amidinopropane) dihydrochloride are added, and oxygen is removed for 0.5h by introducing high-purity nitrogen, so that the oxygen content in the solution is controlled to be less than 1 mg/L. Carrying out photopolymerization reaction (100W ultraviolet irradiation) for 8h to obtain the polymer block. And granulating the rubber block into 4-6 mm small rubber particles by a granulator. Kneading and contacting the obtained small colloidal particles with 74.16 g of sodium hydroxide granular alkali, hydrolyzing at the temperature of 85 ℃ for 1.5h, drying, crushing and screening to obtain a product with the granularity of 20-80 meshes, wherein the performance test results are shown in Table 1.
Example 7
An acrylamide copolymer was prepared in the same manner as in example 1, except that a water-soluble azo initiator, 2' -azobis (2-amidinopropane) dihydrochloride, was not used, and the results of the property test of the obtained product are shown in Table 1.
Example 8
An acrylamide copolymer was prepared in the same manner as in example 1, except that "triethanolamine" was used instead of "N, N, N ', N' -tetramethylethylenediamine", and the results of the performance test of the obtained product were as shown in Table 1.
Example 9
An acrylamide copolymer was prepared in the same manner as in example 1 except that 0.315 mg of water-soluble thioxanthone-type compound 1, 1.575 mg of N, N, N ', N ' -tetramethylethylenediamine and 0.158 mg of water-soluble azo initiator 2,2' -azobis (2-amidinopropane) dihydrochloride were added as an initiator, and after drying, pulverization and sieving, 20 to 80 mesh products were obtained, and the results of the performance test thereof are shown in Table 1.
Example 10
An acrylamide copolymer was prepared in the same manner as in example 2 except that 100 mg of water-soluble thioxanthone-based compound 1, 1000mg of N, N, N ', N ' -tetramethylethylenediamine and 500mg of water-soluble azo initiator 2,2' -azobis (2-amidinopropane) dihydrochloride were added as an initiator, and after drying, pulverization and sieving, 20 to 80 mesh products were obtained, and the results of the performance test thereof are shown in Table 1.
Example 11
An acrylamide copolymer was prepared in the same manner as in example 1, except that "water-soluble thioxanthone-based compound 2" was used instead of "water-soluble thioxanthone-based compound 1", and the results of the performance test of the obtained product are shown in Table 1.
Comparative example 1
An acrylamide copolymer was prepared in the same manner as in example 1, except that "thioxanthone" was used instead of the water-soluble thioxanthone-based compound 1, and the results of the performance test of the obtained product are shown in Table 1.
TABLE 1
As can be seen from the results shown in Table 1, the use of thioxanthone compounds as initiator components enables acrylamide copolymers having a high molecular weight to be obtained at a relatively low temperature, and the polymerization efficiency is high. Moreover, the molecular weight of the temperature-resistant and salt-resistant polymer can be adjusted between 2850-3330 ten thousand by adjusting the type and the dosage of the initiation system and the polymerization monomer. Compared with commercially available high molecular weight polyacrylamide, the temperature-resistant salt-resistant polyacrylamide obtained by the method has a larger viscosity advantage.
The preferred embodiments of the present invention have been described in detail, however, the present invention is not limited to the specific details of the above embodiments, and various simple modifications may be made to the technical solution of the present invention within the technical idea of the present invention, and these simple modifications are within the protective scope of the present invention.
It should be noted that the various technical features described in the above embodiments can be combined in any suitable manner without contradiction, and the invention is not described in any way for the possible combinations in order to avoid unnecessary repetition.
In addition, any combination of the various embodiments of the present invention is also possible, and the same should be considered as the disclosure of the present invention as long as it does not depart from the spirit of the present invention.
Claims (15)
1. The composition with the function of initiating polymerization reaction is characterized by comprising organic amine and at least one water-soluble compound shown as a formula I, wherein the weight ratio of the organic amine to the at least one compound shown as the formula I is 1: 0.1-10,
Wherein R is1、R2、R3、R1’、R2' and R3' are respectively and independently hydrogen, alkyl, alkoxy, halogen, nitro, amino, alkylamino or an ethoxyether long chain with 10-20 carbon atoms, and n is an integer of 10-20;
the organic amine is at least one of N, N, N ', N ' -tetramethyl ethylenediamine, N, N-dimethylethanolamine, N, N ' -dimethylpiperazine, N, N, N ', N ' -tetramethylurea and triethanolamine.
2. The composition of claim 1, wherein R1、R2、R3、R1’、R2' and R3' are each independently hydrogen or methyl.
3. The composition of claim 1, wherein R1、R2、R3、R1’、R2' and R3' are each independently hydrogen.
4. The composition of claim 1, wherein R1And R1' is hydrogen and R2、R3、R2' and R3' are each independently methyl.
5. The composition according to claim 1, further comprising a water-soluble azo initiator.
6. The composition of claim 5, wherein the weight ratio of the organic amine to the water-soluble azo-based initiator is 1: 0.1-10.
7. The composition of claim 5 or 6, wherein the water-soluble azo-based initiator is selected from at least one of 2,2' -azobis (2-amidinopropane) dihydrochloride, 2' -azobis (2-imidazolinopropane) dihydrochloride, and 4,4 ' -azobis (4-cyanovaleric acid).
8. The composition of claim 1, wherein the composition further comprises a water-soluble azo initiator, and the weight ratio of the organic amine, the at least one compound of formula I, and the water-soluble azo initiator is 1: 0.1-10: 0.1-10, wherein the organic amine is N, N, N ', N ' -tetramethyl ethylenediamine, and the water-soluble azo initiator is 2,2' -azobis (2-amidinopropane) dihydrochloride.
9. A method of preparing an acrylamide copolymer, the method comprising: polymerizing a monomer mixture in water under photopolymerization conditions in the presence of an initiator, wherein the initiator is provided by the composition of any one of claims 1-8, and the monomer mixture comprises acrylamide.
10. The method of claim 9, wherein the initiator is used in an amount of 0.00001 to 0.5 wt% based on the weight of the monomer mixture.
11. The method of claim 10, wherein the initiator is used in an amount of 0.0001 to 0.3 wt% based on the weight of the monomer mixture.
12. The method of claim 9, wherein the ratio of the weight of the monomer mixture to the total weight of water and monomer mixture at the start of the photopolymerization reaction is from 0.15 to 0.4: 1.
13. the method of claim 12, wherein the ratio of the weight of the monomer mixture to the total weight of water and monomer mixture at the start of the photopolymerization reaction is from 0.2 to 0.3: 1.
14. the method of claim 9, wherein the photopolymerization is carried out under an inert atmosphere and under irradiation of ultraviolet light, and the photopolymerization conditions include: the initial temperature of the polymerization reaction is 0 ℃ to 50 ℃, the time is 2 to 12 hours, and the pH value is 4 to 12.
15. The method of any one of claims 9-14, wherein the monomer mixture further comprises monomer a, the weight ratio of monomer a to acrylamide is 0.001-10: 1; the monomer a is at least one selected from the group consisting of acrylic acid, 2-acrylamido-2-methylpropanesulfonic acid, N-dimethylacrylamide, N-diethylacrylamide, vinylpyrrolidone, diallyldimethylammonium chloride, styrenesulfonic acid, vinylsulfonic acid, methylvinylsulfonic acid, 2-acrylamido-dodecanesulfonic acid, 2-acrylamido-tetradecanesulfonic acid, 2-acrylamido-hexadecanesulfonic acid, dodecyldimethylallylammonium chloride, tetradecyldimethylammonium chloride, hexadecyldimethylallylammonium chloride and octadecyldimethylammonium chloride.