CN108044767A - A kind of production method of the Ceramic Tiles of natural-like stone - Google Patents
A kind of production method of the Ceramic Tiles of natural-like stone Download PDFInfo
- Publication number
- CN108044767A CN108044767A CN201711360305.3A CN201711360305A CN108044767A CN 108044767 A CN108044767 A CN 108044767A CN 201711360305 A CN201711360305 A CN 201711360305A CN 108044767 A CN108044767 A CN 108044767A
- Authority
- CN
- China
- Prior art keywords
- sintering
- mud
- powder
- method described
- ink
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of production method of stone-imitating ceramic brick.The production method of the present invention comprises the following steps:(1)It is prepared by mud, mixture;(2)Spray sodium hydroxide solution;(3)Charity powder;(4)Cutting prepares moulded pottery not yet put in a kiln to bake;(5)Moulded pottery not yet put in a kiln to bake is dry, adobe is made in punching press;(6)Sintering;(7)Rubbing down is processed.The ceramic brick structure that the method for the present invention obtains is more fine and close, adds in powder, improves the density and wear-resisting property of product;Using sintering process three times, and add among different sintering intervals the ink of different efficacies so that pattern lines in the Ceramic Tiles produced is relatively sharp, naturally, and with three-dimensional sense, Integral decoration is better.
Description
Technical field
The present invention relates to ceramic fields, and in particular to a kind of production method of the Ceramic Tiles of natural-like stone.
Background technology
At present, in ceramic wall and floor bricks production process, the ceramic tile of imitating natural stone texture is increasingly becoming mainstream, also increasingly
Obtain the high praise of consumer.There are two types of the common methods that natural stone texture is presented, they are silk-screen printing and grille strip respectively
Line cloth method, wherein method for printing screen are there is larger defect, the texture lines and the texture lines of lithotome formed
Compare, there is lines it is excessively thick, inflexible, simulation quality is poor the defects of, meanwhile, also there are colors to be extremely limited for silk-screen printing, color development
Not bright-coloured enough deficiency.And grid striped distributing method can only also produce some coarse, rough texture lines, such texture
It is limited by cloth grid, dull can only presenting is identical to the grid generally about pattern of formula, and natural stone texture line can not be presented
The fine and smooth sense of item and level effect.
The content of the invention
In view of the above-mentioned problems, the present invention provides a kind of production method of the Ceramic Tiles of natural-like stone.
The present invention is realized using following technical scheme:A kind of production method of the Ceramic Tiles of natural-like stone, including with
Lower step:
(1)By conventional ceramic brick raw material and coloring material for mixing be made moisture content be 15%-20% mud, be then mixed into mud with
Color particulate material devious after pug sintered, and stir and mixture is made;
(2)By mixture distributor in forming mud layer in solid hopper, one layer of sodium hydroxide solution is sprayed;
(3)One layer of powder of charity forms powder layer on mud layer;
(4)Longitudinally cutting, acquisition moulded pottery not yet put in a kiln to bake is carried out to mud pier;
(5)The moulded pottery not yet put in a kiln to bake of well cutting is dried, adobe is made in punching press;
(6)Sintering;
(7)Rubbing down is processed:The product for being sintered postcooling is polished into edging.
The mass concentration of the sodium hydroxide solution is 10-22.5%.
The step(2)Powder is ceramic powder, carborundum, the mixture of silica flour, and grain size is 200-300 mesh;Powder
Dosage is the 20-30% of mud.
The step(6)Sintering temperature be 600-1000 DEG C.
The spot rate is not less than 90%.
Another technical solution of the present invention is to increase following steps in above-mentioned preparation process:In step(6)The sintering
Afterwards, the charity organic solvent type ceramic ink on green body, applies clear frit frit;Then second of sintering is being carried out;At second
Charity can generate the ink for dialling glaze effect on sintered green body;Third time sintering is carried out again, then carries out rubbing down processing.
The temperature of second of sintering is 800-1100 DEG C;The temperature of third time sintering is 1150-1250 DEG C.
The ink that group glaze effect can be generated is prepared into using the technical solution of patent CN 104830156A embodiments 1
It arrives.Preferably, generate organic solvent type ceramic ink or dial the dosage of the ink of glaze effect as 25-45g/ m2。
Preferably, particulate material accounts for the 10-15% of mixture;The ceramic powder, carborundum, the mixed proportion of silica flour are 1:
2:1。
Mud and powder stacking cloth are obtained the mud pier of certain volume by the present invention in solid hopper, by cutter to mud pier
It is longitudinally cutting obtain the adobe of imitating natural stone texture fine, true to nature, finished product is made more to be comparable to some with acinose texture
Lithotome;Polylith adobe is obtained after the cutting of monoblock mud pier, production efficiency is high.Sodium hydroxide solution is added in preparation process pair
Material is handled, and the product structure of acquisition is more fine and close, adds in powder, improves the density and wear-resisting property of product.
Second technical solution of the present invention, using sintering process three times, and adds in not among different sintering intervals
With the ink of effect so that pattern lines in the Ceramic Tiles produced is relatively sharp, naturally, and with three-dimensional sense, it is whole
Excellent decoration effect.
Specific embodiment
The invention will be further described with the following Examples.
A kind of Ceramic Tiles of 1 natural-like stone of embodiment, are prepared using following steps:
(1)The mud that moisture content is 20% is made in conventional ceramic brick raw material and coloring material for mixing, is then mixed into mud and mud
Color particulate material devious after sintering, and stir and mixture is made;
(2)By mixture distributor in forming mud layer in solid hopper, one layer of sodium hydroxide solution is sprayed;The sodium hydroxide solution
Mass concentration be 18%;
(3)One layer of powder of charity forms powder layer on mud layer;Powder is ceramic powder, carborundum, silica flour in mass ratio 1:
2:1 mixture, grain size are 300 mesh;Powder dosage is the 20% of mud;
(4)Longitudinally cutting, acquisition moulded pottery not yet put in a kiln to bake is carried out to mud pier;
(5)The moulded pottery not yet put in a kiln to bake of well cutting is dried, adobe is made in punching press;
(6)Sintering;It is sintered at 700-8500 DEG C;Then charity organic solvent type ceramic ink, dosage are on green body
35g/ m2, apply clear frit frit;Then carrying out in 800-1100 DEG C of second of sintering;On second of sintered green body
Charity can generate the ink for dialling glaze effect, and the ink for dialling glaze effect that can generate is using patent CN 104830156A embodiments 1
Technical solution be prepared, dosage be 45g/ m2;Again third time sintering is carried out at 1150-1250 DEG C;
(7)Rubbing down is processed:The product for being sintered postcooling is polished into edging.
A kind of Ceramic Tiles of 2 natural-like stone of embodiment, are prepared using following steps:
(1)The mud that moisture content is 20% is made in conventional ceramic brick raw material and coloring material for mixing, is then mixed into mud and mud
Color particulate material devious after sintering, and stir and mixture is made;
(2)By mixture distributor in forming mud layer in solid hopper, one layer of sodium hydroxide solution is sprayed;The sodium hydroxide solution
Mass concentration be 20%;
(3)One layer of powder of charity forms powder layer on mud layer;Powder is ceramic powder, carborundum, silica flour in mass ratio 1:
2:1 mixture, grain size are 200 mesh;Powder dosage is the 30% of mud;
(4)Longitudinally cutting, acquisition moulded pottery not yet put in a kiln to bake is carried out to mud pier;
(5)The moulded pottery not yet put in a kiln to bake of well cutting is dried, adobe is made in punching press;
(6)Sintering;It is sintered at 800-900 DEG C;Then the charity organic solvent type ceramic ink on green body, applies clear frit and melts
Block, dosage are 40g/ m2;Then carrying out in 950-1100 DEG C of second of sintering;The charity on second of sintered green body
The ink for dialling glaze effect can be generated, the ink that glaze effect is dialled in the energy generation uses the skill of patent CN 104830156A embodiments 1
Art scheme is prepared, and dosage is 25g/ m2;Again third time sintering is carried out at 1150-1250 DEG C;
(7)Rubbing down is processed:The product for being sintered postcooling is polished into edging.
Claims (9)
1. a kind of production method of the Ceramic Tiles of natural-like stone, it is characterised in that:Comprise the following steps:
(1)By conventional ceramic brick raw material and coloring material for mixing be made moisture content be 15%-20% mud, be then mixed into mud with
Color particulate material devious after pug sintered, and stir and mixture is made;
(2)By mixture distributor in forming mud layer in solid hopper, one layer of sodium hydroxide solution is sprayed;
(3)One layer of powder of charity forms powder layer on mud layer;
(4)Longitudinally cutting, acquisition moulded pottery not yet put in a kiln to bake is carried out to mud pier;
(5)The moulded pottery not yet put in a kiln to bake of well cutting is dried, adobe is made in punching press;
(6)Sintering;
(7)Rubbing down is processed:The product for being sintered postcooling is polished into edging.
2. according to the method described in claim 1, it is characterized in that, further include following steps:In step(6)After the sintering,
Charity organic solvent type ceramic ink on green body, applies clear frit frit;Then second of sintering is being carried out;After second is sintered
Green body on charity can generate dial glaze effect ink;Third time sintering is carried out again, then carries out rubbing down processing.
3. according to the method described in claim 1, it is characterized in that, the mass concentration of the sodium hydroxide solution is 10-22.5%.
4. according to the method described in claim 1, it is characterized in that, the step(2)Powder be ceramic powder or quartz powder, grain
Footpath is 200-300 mesh;Powder dosage is the 20-30% of mud.
5. according to the method described in claim 1, it is characterized in that, the step(6)Sintering temperature be 600-1000 DEG C.
6. according to the method described in claim 1, it is characterized in that, the spot rate be not less than 90%.
7. according to the method described in claim 2, it is characterized in that, the temperature of second sintering is 800-1100 DEG C;3rd
The temperature of secondary sintering is 1150-1250 DEG C.
8. according to the method described in claim 2, it is characterized in that, it is described can generate dial glaze effect ink use patent CN
The technical solution of 104830156A embodiments 1 is prepared.
9. according to the method described in claim 2, it is characterized in that, the organic solvent type ceramic ink or generate and dial glaze effect
The dosage of ink is 25-45g/ m2。