CN108019028A - A kind of SPC solid wooden compound floors - Google Patents
A kind of SPC solid wooden compound floors Download PDFInfo
- Publication number
- CN108019028A CN108019028A CN201711130861.1A CN201711130861A CN108019028A CN 108019028 A CN108019028 A CN 108019028A CN 201711130861 A CN201711130861 A CN 201711130861A CN 108019028 A CN108019028 A CN 108019028A
- Authority
- CN
- China
- Prior art keywords
- parts
- spc
- pvc board
- wooden compound
- solid wooden
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides a kind of SPC solid wooden compound floors, including PVC board and solid wood slab, the PVC board is closed with solid wood board hide glue and is fixed as one；The PVC board is made of the raw material of following parts by weight：80 130 parts of polyvinyl chloride resin, 260 350 parts of Paris white, PE are 1 1.5 parts cured, 5.5 8 parts of calcium zinc stabilizer, 401 6 12 parts of ACR, 3 4.5 parts of stearic acid；SPC solid wooden compound floors of the present invention, beautiful air, safety and environmental protection, the both natural wood grain with solid wooden floor board, texture, feel, while elasticity is suitable, is unlikely to deform cracking, show excellent in waterproof and dampproof, shock resistance, corrosion-resistant, anti-skid wearable etc..
Description
Technical field
The present invention relates to technical field of floor, and in particular to a kind of SPC solid wooden compound floors.
Background technology
As the progress of industry and the gradual of living standards of the people improve, taste of the people to the environment and finishing of inhabitation
It is being continuously improved, what timber floor was increasingly popularized apply in the live and work of people, now more generally solid wood
Plate and solid wooden compound floor.
Mainly there are solid wooden floor board, solid wooden compound floor and consolidated floor in decoration floor currently on the market.Wherein solid wood
Floor is the floor decorative material that is formed after timber drying, processing.Natural wood grain is the advantage is that, texture, feel are good.Its
Shortcoming be it is protected from environmental big, it is yielding, wear no resistance, easily damaged by worms.Solid wooden floor board disappears using log material at the same time
Substantial amounts of natural resources is consumed, has seriously affected the ecological balance of natural environment, and production cost is higher.
SPC floors are mainly mixed to form compound shakedown material by the certain proportion of calcium powder, polyvinyl chloride, combination of stabilizers.
Hard SPC indoor floors, house ornamentation market is very generally popular abroad, and it is perfectly to present very much for household to adorn.SPC
Plate is 100% Environmental protection floor for being free of formaldehyde, nonpoisonous and tasteless, not afraid of water, not inflammable, be not afraid of tide；Make in scratch resistance performance, resource
With in, non-skid property, SPC floors are superior to consolidated floor.SPC floor surfaces do not have hole, will not seep water；Do not had after splicing
Seam, after being infected with spot, is gently wiped with rag, you can easily cleaning, will not leave behind the marking for being difficult to remove, it is not required that is used special
Different care products maintenance.
In the prior art, also solid wooden floor board is not applied in SPC floors, if therefore by SPC floors and solid wood
The advantages of plate, is combined, and prepares a kind of SPC solid wooden compound floors, will have preferable market prospects.
The content of the invention
It is an object of the invention to provide a kind of SPC solid wooden compound floors, the SPC solid wooden compound floors beauty air,
Safety and environmental protection, the both natural wood grain with solid wooden floor board, texture, feel, while elasticity is suitable, cracking is unlikely to deform, in waterproof
Moisture-proof, shock resistance, corrosion-resistant, anti-skid wearable etc. performance are excellent.
In order to achieve the above object, the present invention is achieved by the following technical programs：
A kind of SPC solid wooden compound floors, including PVC board and solid wood slab, the PVC board are closed with solid wood board hide glue and are fixed as
One；
The PVC board is made of the raw material of following parts by weight：80-130 parts of polyvinyl chloride resin, 260-350 parts of Paris white, PE
1-1.5 parts cured, 5.5-8 parts of calcium zinc stabilizer, 6-12 parts of ACR-401,3-4.5 parts of stearic acid.
Preferably, the PVC board is made of the raw material of following parts by weight：100 parts of polyvinyl chloride resin, 300 parts of Paris white, PE
Cured 1.2 parts, 7 parts of calcium zinc stabilizer, 8 parts of ACR-401,4 parts of stearic acid.
Preferably, the PVC board is made of the raw material of following parts by weight：115 parts of polyvinyl chloride resin, 320 parts of Paris white, PE
Cured 1.2 parts, 6 parts of calcium zinc stabilizer, 11 parts of ACR-401,3.5 parts of stearic acid.
Preferably, the thickness of the solid wood slab is 0.5-1.5mm.
Preferably, the water content of the solid wood slab is 2.7-3.5%.
The preparation method of the above-mentioned SPC solid wooden compound floors of the present invention comprises the following steps：
(1) preparation of PVC board：
Polyvinyl chloride resin, Paris white, PE cured, calcium zinc stabilizer, ACR-401, stearic acid are weighed by recipe ratio, by above-mentioned original
Material adds in batch mixer be uniformly mixed together, obtains mixture；Feed the mixture into double screw extruder and extruded, obtain PVC
Plate；
(2) preparation of SPC solid wooden compound floors：By the PVC board upper surface roller coating Environment-friendlyglue glue, then it is bonded solid wood board
Skin, is subsequently placed in cold press and suppresses 7-10h, then carries out UV roller coating processing, finally cutting fluting, to obtain the final product.
The beneficial effects of the invention are as follows：
PVC board raw material is simple and easy to get in the present invention, environmentally protective without heavy metal formaldehyde, both PVC board and solid wood slab
Coordinate, size changing rate can be controlled between 0.03-0.08%, obtained SPC solid wooden compound floors is unlikely to deform cracking,
Effectively extend service life.
PVC board is closed and is fixed as one by the present invention with solid wood board hide glue, obtained SPC solid wooden compound floors beauty air,
Both the natural wood grain with solid wooden floor board, texture, feel, while moistureproof and waterproof is good, elasticity is suitable, the termite-proof effect of insect prevention
Good, and SPC solid wooden compound floor anti-skid wearables are excellent, when installation, is simple, and easy for construction, cost of material is few, generation technique letter
It is single.
Embodiment
To make the purpose, technical scheme and advantage of the embodiment of the present invention clearer, below in conjunction with the embodiment of the present invention,
Technical solution in the embodiment of the present invention is clearly and completely described, it is clear that described embodiment is the present invention one
Divide embodiment, instead of all the embodiments.Based on the embodiments of the present invention, those of ordinary skill in the art are not making
All other embodiments obtained under the premise of creative work, belong to the scope of protection of the invention.
Embodiment 1：
A kind of SPC solid wooden compound floors, including PVC board and solid wood slab, the PVC board are closed with solid wood board hide glue and are fixed as
One；
The PVC board is made of the raw material of following parts by weight：100 parts of polyvinyl chloride resin, 300 parts of Paris white, PE be 1.2 parts cured,
7 parts of calcium zinc stabilizer, 8 parts of ACR-401,4 parts of stearic acid.
The thickness of the solid wood slab is 1mm, water content 3%.
The preparation method of above-mentioned SPC solid wooden compound floors comprises the following steps：
(1) preparation of PVC board：
Polyvinyl chloride resin, Paris white, PE cured, calcium zinc stabilizer, ACR-401, stearic acid are weighed by recipe ratio, by above-mentioned original
Material adds in batch mixer be uniformly mixed together, obtains mixture；Feed the mixture into double screw extruder and extruded, obtain PVC
Plate；
(2) preparation of SPC solid wooden compound floors：By the PVC board upper surface roller coating Environment-friendlyglue glue, then it is bonded solid wood board
Skin, is subsequently placed in cold press and suppresses 8h, then carries out UV roller coating processing, finally cutting fluting, to obtain the final product.
Embodiment 2：
A kind of SPC solid wooden compound floors, including PVC board and solid wood slab, the PVC board are closed with solid wood board hide glue and are fixed as
One；
The PVC board is made of the raw material of following parts by weight：115 parts of polyvinyl chloride resin, 320 parts of Paris white, PE be 1.2 parts cured,
6 parts of calcium zinc stabilizer, 11 parts of ACR-401,3.5 parts of stearic acid.
The thickness of the solid wood slab is 0.5mm, water content 3.5%.
The preparation method of above-mentioned SPC solid wooden compound floors comprises the following steps：
(1) preparation of PVC board：
Polyvinyl chloride resin, Paris white, PE cured, calcium zinc stabilizer, ACR-401, stearic acid are weighed by recipe ratio, by above-mentioned original
Material adds in batch mixer be uniformly mixed together, obtains mixture；Feed the mixture into double screw extruder and extruded, obtain PVC
Plate；
(2) preparation of SPC solid wooden compound floors：By the PVC board upper surface roller coating Environment-friendlyglue glue, then it is bonded solid wood board
Skin, is subsequently placed in cold press and suppresses 7h, then carries out UV roller coating processing, finally cutting fluting, to obtain the final product.
Embodiment 3：
A kind of SPC solid wooden compound floors, including PVC board and solid wood slab, the PVC board are closed with solid wood board hide glue and are fixed as
One；
The PVC board is made of the raw material of following parts by weight：130 parts of polyvinyl chloride resin, 320 parts of Paris white, PE be 1.5 parts cured,
5.5 parts of calcium zinc stabilizer, 12 parts of ACR-401,4.5 parts of stearic acid.
The thickness of the solid wood slab is 1mm, water content 3%.
The preparation method of above-mentioned SPC solid wooden compound floors comprises the following steps：
(1) preparation of PVC board：
Polyvinyl chloride resin, Paris white, PE cured, calcium zinc stabilizer, ACR-401, stearic acid are weighed by recipe ratio, by above-mentioned original
Material adds in batch mixer be uniformly mixed together, obtains mixture；Feed the mixture into double screw extruder and extruded, obtain PVC
Plate；
(2) preparation of SPC solid wooden compound floors：By the PVC board upper surface roller coating Environment-friendlyglue glue, then it is bonded solid wood board
Skin, is subsequently placed in cold press and suppresses 10h, then carries out UV roller coating processing, finally cutting fluting, to obtain the final product.
Embodiment 4：
A kind of SPC solid wooden compound floors, including PVC board and solid wood slab, the PVC board are closed with solid wood board hide glue and are fixed as
One；
The PVC board is made of the raw material of following parts by weight：80 parts of polyvinyl chloride resin, 260 parts of Paris white, PE are 1 part cured, calcium
6 parts of zinc stabilizer, 8 parts of ACR-401,3 parts of stearic acid.
The thickness of the solid wood slab is 0.8mm, water content 3%.
The preparation method of above-mentioned SPC solid wooden compound floors is the same as embodiment 1.
Embodiment 5：
A kind of SPC solid wooden compound floors, including PVC board and solid wood slab, the PVC board are closed with solid wood board hide glue and are fixed as
One；
The PVC board is made of the raw material of following parts by weight：100 parts of polyvinyl chloride resin, 280 parts of Paris white, PE be 1.2 parts cured,
8 parts of calcium zinc stabilizer, 6 parts of ACR-401,4 parts of stearic acid.
The thickness of the solid wood slab is 1.2mm, water content 3.2%.
The preparation method of above-mentioned SPC solid wooden compound floors is the same as embodiment 1.
Embodiment 6：
A kind of SPC solid wooden compound floors, including PVC board and solid wood slab, the PVC board are closed with solid wood board hide glue and are fixed as
One；
The PVC board is made of the raw material of following parts by weight：90 parts of polyvinyl chloride resin, 300 parts of Paris white, PE be 1.2 parts cured,
8 parts of calcium zinc stabilizer, 8 parts of ACR-401,3.5 parts of stearic acid.
The thickness of the solid wood slab is 1mm, water content 2.8%.
The preparation method of above-mentioned SPC solid wooden compound floors is the same as embodiment 1.
Performance test：
The size changing rate of SPC solid wooden compound floors in 1-6 of the embodiment of the present invention is tested, test condition is：
6h is placed under conditions of 80 DEG C.It is as shown in table 1 to measure obtained size changing rate：
1 size changing rate of table
| Size changing rate (%) | |
| Embodiment 1 | 0.03 |
| Embodiment 2 | 0.03 |
| Embodiment 3 | 0.05 |
| Embodiment 4 | 0.08 |
| Embodiment 5 | 0.06 |
| Embodiment 6 | 0.05 |
As shown in Table 1, the SPC solid wooden compound floor size changing rates that the present invention is prepared are minimum, only 0.03-
0.08%, much smaller than the size changing rate of general solid wooden compound floor, (size changing rate of general solid wooden compound floor is all higher than
0.25%).SPC composite floor boards of the present invention are indeformable in use, do not crack, and performance is stablized, service life length.
Other performance tests are carried out to the SPC solid wooden compound floors of embodiment 1-6 at the same time, it meets solid wooden compound floor
The requirement of industry performance standard, and the SPC solid wooden compound floors of embodiment 1-6 are in waterproof and dampproof, shock resistance, corrosion-resistant, anti-
It is excellent to slide wear-resisting etc. performance.
The above embodiments are merely illustrative of the technical solutions of the present invention, rather than its limitations；Although with reference to the foregoing embodiments
The present invention is described in detail, it will be understood by those of ordinary skill in the art that：It still can be to foregoing each implementation
Technical solution described in example is modified, or carries out equivalent substitution to which part technical characteristic；And these modification or
Replace, the essence of appropriate technical solution is departed from the spirit and scope of various embodiments of the present invention technical solution.
Claims (6)
- A kind of 1. SPC solid wooden compound floors, it is characterised in that including PVC board and solid wood slab, the PVC board and solid wood slab Gluing is fixed as one；The PVC board is made of the raw material of following parts by weight：80-130 parts of polyvinyl chloride resin, 260-350 parts of Paris white, the cured 1- of PE 1.5 parts, 5.5-8 parts of calcium zinc stabilizer, 6-12 parts of ACR-401,3-4.5 parts of stearic acid.
- 2. SPC solid wooden compound floors according to claim 1, it is characterised in that the PVC board by following parts by weight original Material is made：100 parts of polyvinyl chloride resin, 300 parts of Paris white, PE are 1.2 parts cured, 7 parts of calcium zinc stabilizer, 8 parts of ACR-401, stearic acid 4 Part.
- 3. SPC solid wooden compound floors according to claim 1, it is characterised in that the PVC board by following parts by weight original Material is made：115 parts of polyvinyl chloride resin, 320 parts of Paris white, PE are 1.2 parts cured, 6 parts of calcium zinc stabilizer, 11 parts of ACR-401, stearic acid 3.5 part.
- 4. SPC solid wooden compound floors according to claim 1, it is characterised in that the thickness of the solid wood slab is 0.5- 1.5mm。
- 5. SPC solid wooden compound floors according to claim 1, it is characterised in that the water content of the solid wood slab is 2.7-3.5%.
- 6. according to claim 1-5 any one of them SPC solid wooden compound floors, it is characterised in that：The SPC solid woods are compoundly The preparation method of plate comprises the following steps：(1) preparation of PVC board：Polyvinyl chloride resin, Paris white, PE cured, calcium zinc stabilizer, ACR-401, stearic acid are weighed by recipe ratio, by above-mentioned raw materials one Rise in addition batch mixer and be uniformly mixed, obtain mixture；Feed the mixture into double screw extruder and extruded, obtain PVC board；(2) preparation of SPC solid wooden compound floors：By the PVC board upper surface roller coating Environment-friendlyglue glue, then solid wood slab is bonded, Be subsequently placed in cold press and suppress 7-10h, then carry out UV roller coating processing, finally cutting fluting, to obtain the final product.