CN108017162A - Non-Phosphorus composite anti incrustation eorrosion snhibiter and preparation method thereof - Google Patents
Non-Phosphorus composite anti incrustation eorrosion snhibiter and preparation method thereof Download PDFInfo
- Publication number
- CN108017162A CN108017162A CN201711277464.7A CN201711277464A CN108017162A CN 108017162 A CN108017162 A CN 108017162A CN 201711277464 A CN201711277464 A CN 201711277464A CN 108017162 A CN108017162 A CN 108017162A
- Authority
- CN
- China
- Prior art keywords
- parts
- polymer
- acid
- composite anti
- reaction kettle
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of non-phosphorus scale and corrosion inhibitor and preparation method thereof, is made of the raw material of following mass parts:10 20 parts of polycarboxylate, 15 30 parts of polymer-amino-acid, 10 15 parts of zinc salt, 10 15 parts of sodium salt, 12 parts of copper inhibitor, 10 20 parts of sulphonic acids polymer, surplus is water.Its preparation method includes:According to parts by weight by water, zinc salt, addition reaction kettle, 40 55 DEG C are warming up to, sodium salt is added in reaction kettle, is stirred to whole dissolvings;Successively toward polycarboxylate, polymer-amino-acid, copper inhibitor, sulphonic acids polymer is added in reaction kettle, mix.Blowing after sampling, detection are qualified, labelling, storage.The present invention is used in recirculated cooling water, has efficient scale inhibition effect, environmentally safe, and the adsorbed film and precipitation membrane that can be formed in metal surface play corrosion inhibition, prevent all kinds of dirty formation, ensure system normal operation.
Description
Technical field
More particularly to it is a kind of for the without phosphorus multiple of industrial circulating water the present invention relates to the water technology in chemical field
Close anti-incrustation corrosion inhibitor and preparation method thereof.
Background technology
The situation is tense for China's water shortage, and the huge industrial water of consumption, is faced with serious challenge with necessarily standing in the breach.And
In industrial water consumption, cooling water account for very big ratio.Industrial colling accounts for the 80-90% of industrial water, and industry repeats to use
The utilization rate of water only accounts for 20-30%, is the 1/3 of developed country.Therefore, the operation and management gesture for strengthening industrial circulating cooling water exist
It must go.
Measures of Saving Water relatively conventional at present is that recycling, industrial water circulation is made by cooling water after certain processing
It is real reliable Industrial Water Saving measure with instead of original direct current water.
Whole circulation operationally, often produces various problems, such as circulatory mediator to various metallic conduits
And the corrosion of heat exchanger, water are constantly evaporated, concentrated in the process of running, water intermediate ion concentration improves, in heat exchanger surface fouling,
Mattress algae growth etc. in system.These problems influence system operation, can trigger all kinds of security incidents when serious.
General solution is exactly to add chemical agent, such as anti-incrustation corrosion inhibitor, Biocidal algae-killing agent, adhesive mud remover.
Most commonly seen anti-incrustation corrosion inhibitor is phosphorous medicament, has certain effect to preventing incrustation scale and metal erosion, but phosphorus system medicine
Agent long-time service generates the problem of new again, and total phosphorus have received a fixed limit in sewage discharge
System, while a large amount of uses of phosphorous medicament, have aggravated body eutrophication.
The content of the invention
In order to solve the fouling of prior art recirculating cooling water system, etching problem, first technical solution of the invention is to carry
For a kind of non-phosphorus scale and corrosion inhibitor, second technical solution is to provide a kind of preparation method of non-phosphorus scale and corrosion inhibitor.
Realize that above-mentioned purpose uses following technical scheme:
A kind of non-phosphorus scale and corrosion inhibitor, is made of the raw material of following mass parts:10-20 parts of polycarboxylate, polymer-amino-acid
15-30 parts, 10-15 parts of zinc salt, 10-15 parts of sodium salt, 1-2 parts of copper inhibitor, 10-20 parts of sulphonic acids polymer, surplus is water.
The polycarboxylate is one or more of mixing in acrylic acid, maleic acid, polymaleic anhydride.
The polymer-amino-acid is poly-aspartate or polyglutamic acid.
The zinc salt bag is zinc sulfate or zinc chloride.
The sodium salt is sodium gluconate or EDTA-2 sodium.
The copper inhibitor bag is benzotriazole or thin base benzothiazole.
The Sulfonates polymer is acrylic acid -2- acrylamidos -2 '-methyl-propane sulfonic acid copolymer.
A kind of preparation method of non-phosphorus scale and corrosion inhibitor, includes the following steps:
Preparing raw material is by weight
Step 1:
Check whether reaction kettle is clean, close each valve, added water to according to parts by weight in reaction kettle;
Step 2:
According to parts by weight by 10-15 parts of addition reaction kettles of zinc salt, 40-55 DEG C is warming up to, is stirred to whole dissolvings;
Step 3:
According to parts by weight by 10-15 parts of sodium salt, add in reaction kettle, stir to whole dissolvings;
Step 4:
According to parts by weight successively toward adding 10-20 parts of polycarboxylate, 15-30 parts of polymer-amino-acid, copper inhibition in reaction kettle
1-2 parts of agent, 10-20 parts of sulphonic acids polymer;
Step 5:
Blowing after sampling, detection are qualified, labelling, storage.
It is compared with prior art, efficient present invention is mainly used in recirculated cooling water, having using above-mentioned technical proposal
Scale inhibition effect, usage amount is few, environmentally safe, and the adsorbed film and precipitation membrane that can be formed in metal surface play corrosion inhibition,
At the same time have to the calcium carbonate in water, calcium phosphate, calcium sulfate etc. good chelating disperse and distortion of lattice effect, prevent all kinds of dirts
Formation, ensure that system normal operation.In addition the manufacture of the without phosphorus medicament of environment-friendly type and using process, to health and
Environmental security influence is smaller, will not cause body eutrophication, meet the requirement of sustainable development and advocating for Green Chemistry,
New Environmentally-friephosphorus-free phosphorus-free water treatment agent is researched and developed to have important practical significance.
Embodiment
In order to make the purpose , technical scheme and advantage of the present invention be clearer, with reference to embodiments, to the present invention
It is described in further details.It should be appreciated that the specific embodiments described herein are merely illustrative of the present invention, it is not used to limit
The fixed present invention.
Non-phosphorus scale and corrosion inhibitor of the present invention is made of the raw material of following parts by weight:10-20 parts of polycarboxylate, amino acid is birdsed of the same feather flock together
15-30 parts of compound, 10-15 parts of zinc salt, 10-15 parts of sodium salt, 1-2 parts of copper inhibitor, 10-20 parts of sulphonic acids polymer, surplus are
Water.
The polycarboxylate is one or more of mixing in acrylic acid, maleic acid, polymaleic anhydride.
The polymer-amino-acid is poly-aspartate or polyglutamic acid.
The zinc salt bag is zinc sulfate or zinc chloride.
The sodium salt is sodium gluconate or EDTA-2 sodium.
The copper inhibitor bag is benzotriazole or thin base benzothiazole.
The Sulfonates polymer is acrylic acid -2- acrylamidos -2 '-methyl-propane sulfonic acid copolymer.
Embodiment 1:
Raw material calculates by weight
Step 1:
Check whether reaction kettle is clean, close each valve, by 24 parts of addition reaction kettles of water.
Step 2:
By in 12 parts of addition reaction kettles of zinc sulfate, 50 DEG C are warming up to, is stirred to whole dissolvings.
Step 3:
By 13 parts of sodium gluconate, reaction kettle is added, is stirred to whole dissolvings.
Step 4:
Successively toward 15 parts of acrylic acid is added in reaction kettle, 20 parts of poly-aspartate, dredges 1 part of base benzothiazole, acrylic acid -2- propylene
Amide groups -2 ' 5 parts of-methyl-propane sulfonic acid copolymer 1 is mixed.
Step 5:
Blowing after sampling, detection are qualified, labelling, storage.
Embodiment 2:
Raw material is by weight
Step 1:
Check whether reaction kettle is clean, close each valve, by 29 parts of addition reaction kettles of water.
Step 2:
By in 12 parts of addition reaction kettles of zinc chloride, 50 DEG C are warming up to, is stirred to whole dissolvings.
Step 3:
By 15 parts of sodium gluconate, reaction kettle is added, is stirred to whole dissolvings.
Step 4:
13 parts of polymaleic anhydride is added in reaction kettle successively, 15 parts of poly-aspartate, dredges 1 part of base benzothiazole, acrylic acid -2-
Acrylamido -2 ' 5 parts of-methyl-propane sulfonic acid copolymer 1 is mixed.
Step 5:
Blowing after sampling, detection are qualified, labelling, storage.
Embodiment 3:
Raw material is by weight
Step 1:
Check whether reaction kettle is clean, close each valve, by 32 parts of addition reaction kettles of water.
Step 2:
By in 12 parts of addition reaction kettles of zinc chloride, 55 DEG C are warming up to, is stirred to whole dissolvings.
Step 3:
By 10 parts of sodium gluconate, reaction kettle is added, is stirred to whole dissolvings.
Step 4:
15 parts of poly is added in reaction kettle successively, 15 parts of poly-aspartate, dredges 1 part of base benzothiazole, acrylic acid -2- third
Acrylamide base -2 ' 5 parts of-methyl-propane sulfonic acid copolymer 1 is mixed.
Step 5:
Blowing after sampling, detection are qualified, labelling, storage.
Embodiment 4:
Raw material is by weight
Step 1:
Check whether reaction kettle is clean, close each valve, by 31 parts of addition reaction kettles of water.
Step 2:
By in 13 parts of addition reaction kettles of zinc chloride, 40 DEG C are warming up to, is stirred to whole dissolvings.
Step 3:
By 10 parts of EDTA-2 sodium, reaction kettle is added, is stirred to whole dissolvings.
Step 4:
Successively toward 10 parts of poly is added in reaction kettle, 15 parts of poly-aspartate, dredges 1 part of base benzothiazole, acrylic acid -2-
Acrylamido -2 ' 20 parts of-methyl-propane sulfonic acid copolymer, is mixed.
Step 5:
Blowing after sampling, detection are qualified, labelling, storage.
Contrast on effect is analyzed:
Measure tosca method of the evaluation of antisludging performance according to GB/T 16632-2008 water treatment agent scale-inhibiting properties
The measure rotary hanging plate method of the Appreciation gist GB/T 18175-2000 water treatment agent corrosion inhibitions of corrosion inhibition
Evaluation method:
The scale-inhibiting properties of the non-phosphorus scale and corrosion inhibitor of above-mentioned 3 kinds of different ratios of raw materials synthesis, corrosion inhibition contrast.
The foregoing is merely illustrative of the preferred embodiments of the present invention, is not intended to limit the invention, it is all the present invention spirit and
All any modification, equivalent and improvement made within principle etc., should all be included in the protection scope of the present invention.
Claims (9)
1. a kind of non-Phosphorus composite anti incrustation eorrosion snhibiter, it is characterised in that non-phosphorus scale and corrosion inhibitor is made of the raw material of following parts by weight:
10-20 parts of polycarboxylate, 15-30 parts of polymer-amino-acid, 10-15 parts of zinc salt, 10-15 parts of sodium salt, 1-2 parts of copper inhibitor,
10-20 parts of sulphonic acids polymer, surplus is water.
2. according to the non-Phosphorus composite anti incrustation eorrosion snhibiter described in right 1, it is characterised in that polycarboxylate is acrylic acid, maleic acid, gathers
One or more of mixing in maleic anhydride.
3. according to the non-Phosphorus composite anti incrustation eorrosion snhibiter described in right 1, it is characterised in that amino acid polymer be poly-aspartate or
Polyglutamic acid.
4. according to the non-Phosphorus composite anti incrustation eorrosion snhibiter described in right 1, it is characterised in that zinc salt is zinc sulfate or zinc chloride.
5. according to the non-Phosphorus composite anti incrustation eorrosion snhibiter described in right 1, it is characterised in that sodium salt is sodium gluconate or EDTA-2
Sodium.
6. according to the non-Phosphorus composite anti incrustation eorrosion snhibiter described in right 1, it is characterised in that copper inhibitor is benzotriazole or thin base
Benzothiazole.
7. according to the non-Phosphorus composite anti incrustation eorrosion snhibiter described in right 1, it is characterised in that sulfonate polymer is acrylic acid -2- third
Acrylamide base -2 '-methyl-propane sulfonic acid copolymer.
8. non-Phosphorus composite anti incrustation eorrosion snhibiter according to claim 1, it is characterised in that the non-phosphorus scale and corrosion inhibitor by with
The raw material of lower parts by weight is made:10-20 parts of polycarboxylate, 15-30 parts of polymer-amino-acid, 10-15 parts of zinc salt, sodium salt 10-
15 parts, 1-2 parts of copper inhibitor, 10-20 parts of sulphonic acids polymer, water is 20-40 parts.
9. a kind of preparation method of non-Phosphorus composite anti incrustation eorrosion snhibiter as claimed in claim 1, it is characterised in that including following step
Suddenly:
Step 1:
Check whether reaction kettle is clean, close each valve, be added to water in reaction kettle for 20-40 parts according to parts by weight;
Step 2:
According to parts by weight by 10-15 parts of addition reaction kettles of zinc salt, 40-55 DEG C is warming up to, is stirred to whole dissolvings;
Step 3:
According to parts by weight by 10-15 parts of sodium salt, add in reaction kettle, stir to whole dissolvings;
Step 4:
According to parts by weight successively toward adding 10-20 parts of polycarboxylate, 15-30 parts of polymer-amino-acid, copper inhibition in reaction kettle
1-2 parts of agent, 10-20 parts of sulphonic acids polymer;
Step 5:
Blowing after sampling, detection are qualified, labelling, storage.