CN107987404A - A kind of tensile strength is high, the rubber of good corrosion resistance - Google Patents
A kind of tensile strength is high, the rubber of good corrosion resistance Download PDFInfo
- Publication number
- CN107987404A CN107987404A CN201711311141.5A CN201711311141A CN107987404A CN 107987404 A CN107987404 A CN 107987404A CN 201711311141 A CN201711311141 A CN 201711311141A CN 107987404 A CN107987404 A CN 107987404A
- Authority
- CN
- China
- Prior art keywords
- parts
- rubber
- tensile strength
- corrosion resistance
- good corrosion
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of tensile strength height, the rubber of good corrosion resistance, it is formed according to the parts by weight of following raw material:50 100 parts of chlorohydrin rubber, 60 120 parts of ethylene propylene diene rubber, 4 20 parts of stearic acid, 5 15 parts of zinc oxide, 10 20 parts of aluminium hydroxide, 2 10 parts of sulphur, 23 parts of vulcanizing agent, 12 parts of vulcanization accelerator, 6 15 parts of magnesium silicate, 38 parts of rosin, 13 parts of plasticizer, 15 25 parts of linseed oil, 69 parts of aluminum phosphate, 10 15 parts of phenolic resin, 5 10 parts of copper powder, 4 15 parts of palm wax, 69 parts of carbon nano-fiber.The composition of rubber of the present invention substantially increases anti-mold effect, while the rubber also has that tensile strength is high, high temperature resistant, it is corrosion-resistant the advantages that.
Description
Technical field
The present invention relates to a kind of tensile strength height, the rubber of good corrosion resistance.
Background technology
Rubber industry is the important component of chemical industry, tire, sebific duct, adhesive tape, rubber roller, rubber seal, adhesive plaster
The rubbers such as product are widely used in the national warp such as automobile production, aircraft manufacturing, Crude Oil Transportation, telecommunications, hospital
The industry-by-industry of Ji, it has also become one of important basic industry.It is well known that the basic raw material of rubber industry is exactly natural rubber
Glue and synthetic rubber, the natural rubber whether obtained from nature, or the synthesis rubber that the mankind are obtained by industrialization means
Glue, although they have the high resiliency of preciousness and other a series of excellent performances, itself still there is lacking for many in performance
Point, in order to produce the rubber for meeting actual use performance requirement, improves process industrial art performance and reduces rubber
Cost, it is necessary to add various chemical substances, these chemical substances are collectively referred to as compounding agent or processing aid.Compounding agent is according to effect
It is broken generally into vulcanizing agent, accelerating agent, activating agent, antioxidant, antiscorching agent, reinforcing agent, tackifier, plasticizer and other compounding agents.
The content of the invention
The purpose of the present invention is that to solve the above-mentioned problems and provides a kind of tensile strength height, the rubber of good corrosion resistance
Glue.
To achieve these goals, the present invention is achieved by the following technical solutions:A kind of tensile strength is high, corrosion-resistant
Property good rubber, it is formed according to the parts by weight of following raw material:50-100 parts of chlorohydrin rubber, ethylene propylene diene rubber 60-120
Part, 4-20 parts of stearic acid, 5-15 parts of zinc oxide, 10-20 parts of aluminium hydroxide, 2-10 parts of sulphur, 2-3 parts of vulcanizing agent, vulcanization promote
1-2 parts of agent, 6-15 parts of magnesium silicate, 3-8 parts of rosin, 1-3 parts of plasticizer, 15-25 parts of linseed oil, 6-9 parts of aluminum phosphate, phenolic aldehyde tree
10-15 parts of fat, 5-10 parts of copper powder, 4-15 parts of palm wax, 6-9 parts of carbon nano-fiber.
Further, a kind of tensile strength is high, the rubber of good corrosion resistance, its according to following raw material parts by weight array
Into:50-80 parts of chlorohydrin rubber, 60-100 parts of ethylene propylene diene rubber, 4-18 parts of stearic acid, 5-13 parts of zinc oxide, aluminium hydroxide 10-
18 parts, 2-8 parts of sulphur, 2-3 parts of vulcanizing agent, 1-2 parts of vulcanization accelerator, 6-12 parts of magnesium silicate, 3-7 parts of rosin, plasticizer 1-3
Part, 15-20 parts of linseed oil, 6-8 parts of aluminum phosphate, 10-13 parts of phenolic resin, 5-8 parts of copper powder, 4-13 parts of palm wax, nano-sized carbon
6-8 parts of fiber.
Further, a kind of tensile strength is high, the rubber of good corrosion resistance, its according to following raw material parts by weight array
Into:70 parts of chlorohydrin rubber, 80 parts of ethylene propylene diene rubber, 12 parts of stearic acid, 9 parts of zinc oxide, 14 parts of aluminium hydroxide, 5 parts of sulphur, sulphur
2 parts of agent, 1 part of vulcanization accelerator, 10 parts of magnesium silicate, 5 parts of rosin, 2 parts of plasticizer, 18 parts of linseed oil, 7 parts of aluminum phosphate, phenol
12 parts of urea formaldehyde, 6 parts of copper powder, 8 parts of palm wax, 7 parts of carbon nano-fiber.
In summary the invention has the advantages that:The composition of rubber of the present invention substantially increases anti-mold effect,
The rubber also has that tensile strength is high at the same time, high temperature resistant, it is corrosion-resistant the advantages that.
Embodiment
Specific embodiment 1:A kind of tensile strength is high, the rubber of good corrosion resistance, its according to following raw material parts by weight
Composition:50 parts of chlorohydrin rubber, 60 parts of ethylene propylene diene rubber, 4 parts of stearic acid, 5 parts of zinc oxide, 10 parts of aluminium hydroxide, 2 parts of sulphur,
2 parts of vulcanizing agent, 1 part of vulcanization accelerator, 6 parts of magnesium silicate, 3 parts of rosin, 1 part of plasticizer, 15 parts of linseed oil, 6 parts of aluminum phosphate, phenol
10 parts of urea formaldehyde, 5 parts of copper powder, 4 parts of palm wax, 6 parts of carbon nano-fiber.
Specific embodiment 2:A kind of tensile strength is high, the rubber of good corrosion resistance, its according to following raw material parts by weight
Composition:70 parts of chlorohydrin rubber, 80 parts of ethylene propylene diene rubber, 12 parts of stearic acid, 9 parts of zinc oxide, 14 parts of aluminium hydroxide, 5 parts of sulphur,
2 parts of vulcanizing agent, 1 part of vulcanization accelerator, 10 parts of magnesium silicate, 5 parts of rosin, 2 parts of plasticizer, 18 parts of linseed oil, 7 parts of aluminum phosphate,
12 parts of phenolic resin, 6 parts of copper powder, 8 parts of palm wax, 7 parts of carbon nano-fiber.
Specific embodiment 3:A kind of tensile strength is high, the rubber of good corrosion resistance, its according to following raw material parts by weight
Composition:100 parts of chlorohydrin rubber, 120 parts of ethylene propylene diene rubber, 20 parts of stearic acid, 15 parts of zinc oxide, 20 parts of aluminium hydroxide, sulphur
10 parts, 3 parts of vulcanizing agent, 2 parts of vulcanization accelerator, 15 parts of magnesium silicate, 8 parts of rosin, 3 parts of plasticizer, 25 parts of linseed oil, aluminum phosphate
9 parts, 15 parts of phenolic resin, 10 parts of copper powder, 15 parts of palm wax, 9 parts of carbon nano-fiber.
Embodiment provided above is the better embodiment of the present invention, is only used for the convenient explanation present invention, not to this hair
The limitation of bright work in any form, any those of ordinary skill in the art, if putting forward skill not departing from the present invention
In the range of art feature, using the equivalent embodiment for locally changing or modifying made by disclosed technology contents, and
Without departing from the technical feature content of the present invention, in the range of still falling within the technology of the present invention feature.
Claims (3)
1. a kind of tensile strength is high, the rubber of good corrosion resistance, it is characterised in that is formed according to the parts by weight of following raw material:
50-100 parts of chlorohydrin rubber, 60-120 parts of ethylene propylene diene rubber, 4-20 parts of stearic acid, 5-15 parts of zinc oxide, aluminium hydroxide 10-20
Part, 2-10 parts of sulphur, 2-3 parts of vulcanizing agent, 1-2 parts of vulcanization accelerator, 6-15 parts of magnesium silicate, 3-8 parts of rosin, 1-3 parts of plasticizer,
15-25 parts of linseed oil, 6-9 parts of aluminum phosphate, 10-15 parts of phenolic resin, 5-10 parts of copper powder, 4-15 parts of palm wax, Nano carbon fibers
6-9 parts of dimension.
2. a kind of tensile strength according to claim 1 is high, the rubber of good corrosion resistance, it is characterised in that according to following
The parts by weight composition of raw material:50-80 parts of chlorohydrin rubber, 60-100 parts of ethylene propylene diene rubber, 4-18 parts of stearic acid, zinc oxide 5-
13 parts, 10-18 parts of aluminium hydroxide, 2-8 parts of sulphur, 2-3 parts of vulcanizing agent, 1-2 parts of vulcanization accelerator, 6-12 parts of magnesium silicate, rosin
3-7 parts, 1-3 parts of plasticizer, 15-20 parts of linseed oil, 6-8 parts of aluminum phosphate, 10-13 parts of phenolic resin, 5-8 parts of copper powder, palm
4-13 parts of wax, 6-8 parts of carbon nano-fiber.
3. a kind of tensile strength according to claim 1 is high, the rubber of good corrosion resistance, it is characterised in that according to following
The parts by weight composition of raw material:70 parts of chlorohydrin rubber, 80 parts of ethylene propylene diene rubber, 12 parts of stearic acid, 9 parts of zinc oxide, hydroxide
14 parts of aluminium, 5 parts of sulphur, 2 parts of vulcanizing agent, 1 part of vulcanization accelerator, 10 parts of magnesium silicate, 5 parts of rosin, 2 parts of plasticizer, linseed oil
18 parts, 7 parts of aluminum phosphate, 12 parts of phenolic resin, 6 parts of copper powder, 8 parts of palm wax, 7 parts of carbon nano-fiber.