CN107974166A - A kind of aqueous dual-component epoxy iron red shop primer and preparation method thereof - Google Patents
A kind of aqueous dual-component epoxy iron red shop primer and preparation method thereof Download PDFInfo
- Publication number
- CN107974166A CN107974166A CN201711261340.XA CN201711261340A CN107974166A CN 107974166 A CN107974166 A CN 107974166A CN 201711261340 A CN201711261340 A CN 201711261340A CN 107974166 A CN107974166 A CN 107974166A
- Authority
- CN
- China
- Prior art keywords
- water
- aqueous
- component
- epoxy
- shop primer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of aqueous dual-component epoxy iron red shop primer of the present invention and preparation method thereof, is related to a kind of coating composition.The aqueous dual-component epoxy iron red shop primer of the present invention, including first component and second component；First component includes aqueous epoxy resins, iron oxide red pigment, nano aluminium oxide, dispersant, filler material, aqueous defoamer, waterborne preservative, negative ion steam distilled water, water-based amine hardener；Second component includes aqueous epoxy resin emulsion, aqueous defoamer, water-based moistening flatting agent, waterborne preservative, water-soluble active diluent, water.Two component of first, second is aqueous product used by the aqueous dual-component epoxy iron red shop primer of the present invention, easily mixing, can reach and cure sufficient purpose.With stronger anti-impact force, blistering peeling will not be produced, while there is nontoxic, flame-proof explosion-proof effect, be applicable in that the cycle is long, hardness of film is high, toughness is strong, uniform color, can meet the requirement of safety and environmental protection.
Description
Technical field
The present invention relates to chemistry painting industry field, a kind of aqueous dual-component ring provided especially for environment protecting water-based paint
Oxygen iron oxide red primer and preparation method thereof.
Background technology
Currently on the market, many coating products used in traditional machinery, automobile, power equipment coating process, are all
It is formulated by organic solvent, and in practice of construction, since solvent volatilization contained in oil paint causes peripheral ring
The pollution in border, also have impact on the health of construction personnel, and as environmental requirement is higher and higher, oil paint will be phased out,
And water paint not only economizes on resources, but also meet environmental requirement, it has also become substitute the inexorable trend of oil paint, and chemical industry
The development of coating industry industrial upgrading.
Modern industry terrace priming paint requires dust-proof, anti-corrosion, resistance to compression, wear-resisting at the same time, is currently being widely used epoxy iron red shop
Because film has preferable mechanical mass performance and an excellent chemical resistance, and with smooth bright and clean, decoration makes priming paint
It is strong with property, it can meet the requirement of modern industry terrace, therefore be widely used.
Recently as the continuous improvement of environmental requirement, using the oiliness epoxy iron red shop primer of coatings volatile organic compounds, will progressively move back
The arena of history is removed, will be substituted by water-soluble epoxy red ferric oxide primer, water-soluble epoxy red ferric oxide primer has the following advantages in actual use：
1. without using organic solvent, pollution will not be produced to surrounding enviroment；2. coating has unidirectional vapour transmission, avoid because by moisture and
Produce blistering or peeling；3. using water as decentralized medium, flame-proof explosion-proof requirement is reached, has ensured in actual production and construction
Security guard；4. its content is low thus more environmentally-friendly due to volatile organic compounds.Develop what is used on Vehicles Collected from Market
Water-soluble epoxy red ferric oxide primer, particularly bi-component epoxy iron red shop primer, be using a component commonly it is water-based, it is another
A component is oiliness, since in the construction process, aqueous components and oily components are bad there is mixed effect, solidification path
Degree is poor, causes the dried hardness of primer coating not reach requirement, compression strength is inadequate with impact, has seriously affected and has used the longevity
Life.Therefore there is an urgent need to improve product quality by technological innovation, environment-friendly type aqueous bi-component epoxy iron is promoted the use of in quickening
Red priming paint, so as to promote the structural adjustment of coating industry.
The content of the invention
The object of the invention primarily directed to the deficiencies in the prior art, and provide a kind of aqueous dual-component epoxy iron red shop primer and
Its preparation method.
Two component of first, second provided by the invention, without poisonous solvent, has stronger anti-impact using water as decentralized medium
Power is hit, blistering peeling will not be produced, there is nontoxic, flame-proof explosion-proof effect, terrace, metal primer coating can be used as to use.
The present invention is achieved through the following technical solutions：
A kind of aqueous dual-component epoxy iron red shop primer, it includes first component and second component, in parts by mass：
(1) the first component described in includes：Aqueous epoxy resins 38-45%, iron oxide red pigment 3-15%, nano aluminium oxide
0.5-2%, dispersant 0.1-0.5%, filler material 5-15%, aqueous defoamer 0.5-1.5%, waterborne preservative 0.5-1.5%,
Water 20-30%, water-based amine hardener 5-10%.
(2) the second component described in includes：It is aqueous epoxy resin emulsion 40-50%, aqueous defoamer 0.5-1.5%, water-based
Moistening flatting agent 0.5-1.5%, waterborne preservative 0.5-1%, water-soluble active diluent 5-10%, water 35-50%.
A kind of aqueous dual-component epoxy iron red shop primer, optimization formula are：
First component：Aqueous epoxy resins 40-45%, iron oxide red pigment 5-15%, nano aluminium oxide 0.5-1.5%, dispersant
It is 0.1-0.5%, filler material 5-13%, aqueous defoamer 0.5-1.2%, waterborne preservative 0.5-1.5%, water 20-29%, water-based
Amine hardener 0.5-0.9%.
Second component：Aqueous epoxy resin emulsion 40-49%, aqueous defoamer 0.5-1.3%, water-based moistening flatting agent 0.5-
1.5%th, waterborne preservative 0.5-1%, water-soluble active diluent 5-9%, water 35-45%.
The wherein described water-based amine hardener is non-ionic, transparent, not solvent-laden cosolvent, preferably modified polyamine
Addition product.
The filler material is barium sulfate.
The pigment is 190 iron oxide reds, molecular weight 159.6.
The water-soluble active Diluent Viscosity is 9-10mPa, and boiling range is 260-285 DEG C.
The epoxy resin latex solids content is 45-51% (quality), equivalent 390g/mol.
The nano aluminium oxide ceramics particle diameter is 20-30um.
The aqueous defoamer is German product DF-8206.
The aqueous dispersion is organosiloxane.
The waterborne preservative is benzoic acid.
The aqueous wetting agent is levelling agent.
The water is negative ion steam distilled water.
A kind of aqueous dual-component epoxy iron red shop primer and preparation method thereof, the method is implemented by following steps：
(1) pigment iron oxide red and water and aqueous epoxy resins are added in container first and soaked, while add dispersant and
Even stirring.
(2) after when question response 1 is small, filler material barium sulfate, defoamer, preservative, nano aluminium oxide, simultaneously are added into container
When continuation uniform stirring 0.5 is small.
(3) under stirring well, water-based amine hardener is added into container, while is warming up to 70 DEG C, treats that its is abundant
React 2 it is small when after carry out high speed dispersion mixing 0.5 it is small when.
(4) after being handled by dispersion mixing, temperature is reduced to 40 DEG C, then carries out sand milling process again, is mixed colours
Afterwards by fineness control within 55um.
(5) carried out filtering obtained slurry with 130 mesh stainless steel filtering nets, that is, obtain the first component of water-soluble epoxy red ferric oxide primer.
(6) aqueous epoxy resin emulsion, aqueous defoamer, aqueous wetting agent, waterborne preservative, water-soluble active are diluted
Agent is added separately in container, and open mixer uniform stirring 0.5 it is small when, when then high speed dispersion 0.5 is small.
(7) filtered with 130 mesh stainless steel filtering nets, that is, obtain water-soluble epoxy red ferric oxide primer second component.
Described a kind of aqueous dual-component epoxy iron red shop primer and preparation method thereof, wherein being made water-based by step 1-5
Epoxy iron red shop primer first component, is made water-soluble epoxy red ferric oxide primer second component by 6-7 steps, can prepare at the same time, can also
In no particular order prepared by order.
Beneficial effect of the present invention：
Select good pigment iron oxide red, nano aluminium oxide, it can be ensured that pressure-resistant, wear-resisting, anti-impact force requirement, by using water
Insoluble active diluent, avoids harm of the organic volatile release to environment and human body, simultaneously because selecting water-based amine to cure
Agent and the activity of reduction resin reaction are more gentle, and pliability is good, can play preferable complementary coordinative role between each other, make
Primer base has more preferable film coated surface hardness, so as to improve the wearability and durability of primer film.The present invention is used
Two component of first, second be aqueous product, easily mixing, can reach and cure sufficient purpose.Not only it is applicable in cycle length, crosslinking curing
Rear hardness of film is high, toughness is strong, and the aqueous epoxy resin emulsion in second component be it is non-ionic, completely can be with water
For diluent, meet the purpose of uniform color, can reach the primer base effect without organic solvent especially by the present invention
Fruit, has reached the requirement of safety and environmental protection.
Embodiment
The invention will be further described with reference to embodiments.
Embodiment 1
(1) by deionized-distilled water 250kg, aqueous epoxy resins 400kg, iron oxide red pigment 10kg, 2kg points of aqueous dispersion
Be not added in grinding container, and open mixer carry out uniform stirring, 0.5 it is small when after add 10kg defoamers, be further continued for into
Row uniform stirring.
(2) 10kg nano aluminium oxides, 70kg filler materials barium sulfate, 10kg preservative benzene are sequentially added after when question response 1 is small
Formic acid, and continue uniform stirring and react 0.5 minute.
(3) under stirring well, the water-based amine hardeners of 8kg are added into container, while are warming up to 70 DEG C, treat that its is anti-
Answer 2 it is small when after carry out high speed dispersion mixing 0.5 it is small when.
(4) by dispersion mixing processing 0.5 it is small when after, temperature is reduced to 40 DEG C, then carries out sand milling process again,
After toning by fineness control within 55um.
(5) carried out filtering obtained slurry with 130 mesh stainless steel filtering nets, that is, obtain the first component of water-soluble epoxy red ferric oxide primer.
(6) by aqueous epoxy resin emulsion 450kg, deionized-distilled water 350kg, aqueous defoamer 10kg, water-repellent preservation
Agent 9kg, water-soluble active diluent 60kg, after being added separately to when uniform stirring 0.5 is small in container, are carrying out high speed dispersion
0.5 it is small when.
(7) first mix colours, then fineness control is filtered within 55um, then with 130 mesh stainless steel filtering nets, that is, is obtained
The second component of water-soluble epoxy red ferric oxide primer.
Embodiment 2
(1) by deionized-distilled water 260kg, aqueous epoxy resins 430kg, iron oxide red pigment 11kg, 4kg points of aqueous dispersion
Be not added in grinding container, and open mixer carry out uniform stirring, 0.5 it is small when after add 8kg defoamers, be further continued for carrying out
Uniform stirring.
(2) 12kg nano aluminium oxides, 80kg filler materials barium sulfate, 12kg preservative benzene are sequentially added after when question response 1 is small
Formic acid, and continue uniform stirring and react 0.5 minute.
(3) under stirring well, the water-based amine hardeners of 7.5kg are added into container, while are warming up to 70 DEG C, treat it
React 2 it is small when after carry out high speed dispersion mixing 0.5 it is small when.
(4) by dispersion mixing processing 0.5 it is small when after, then carry out sand milling process again, control fineness after toning
Within 55um.
(5) carried out filtering obtained slurry with 130 mesh stainless steel filtering nets, that is, obtain the first component of water-soluble epoxy red ferric oxide primer.
(6) by aqueous epoxy resin emulsion 480kg, deionized-distilled water 400kg, aqueous defoamer 11kg, water-repellent preservation
Agent 8kg, water-soluble active diluent 65kg, after being added separately to when uniform stirring 0.5 is small in container, are carrying out high speed dispersion
0.5 it is small when.
(7) first mix colours, then fineness control is filtered within 55um, then with 130 mesh stainless steel filtering nets, that is, is obtained
The second component of water-soluble epoxy red ferric oxide primer.
Embodiment 3
(1) by deionized-distilled water 280kg, aqueous epoxy resins 450kg, iron oxide red pigment 14kg, 5kg points of aqueous dispersion
Be not added in grinding container, and open mixer carry out uniform stirring, 0.5 it is small when after add 11kg defoamers, be further continued for into
Row uniform stirring.
(2) 13kg nano aluminium oxides, 100kg filler materials barium sulfate, 12kg preservative benzene are sequentially added after when question response 1 is small
Formic acid, and continue uniform stirring and react 0.5 minute.
(3) under stirring well, the water-based amine hardeners of 9kg are added into container, while are warming up to 70 DEG C, treat that its is anti-
Answer 2 it is small when after carry out high speed dispersion mixing 0.5 it is small when.
(4) by dispersion mixing processing 0.5 it is small when after, temperature is reduced to 40 DEG C, then carries out sand milling process again,
After toning by fineness control within 55um.
(5) carried out filtering obtained slurry with 130 mesh stainless steel filtering nets, that is, obtain the first component of water-soluble epoxy red ferric oxide primer.
(6) by aqueous epoxy resin emulsion 480kg, deionized-distilled water 380kg, aqueous defoamer 12kg, water-repellent preservation
Agent 10kg, water-soluble active diluent 80kg, after being added separately to when uniform stirring 0.5 is small in container, are carrying out high speed dispersion
0.5 it is small when.
(7) first mix colours, then fineness control is filtered within 55um, then with 130 mesh stainless steel filtering nets, that is, is obtained
The second component of water-soluble epoxy red ferric oxide primer.
Such as in actual construction, only first component and second component need to be used to press 1:1 ratio carries out mixing preparation and stirs equal
It is even, it can be used after ten minutes.
Equipment according to the present invention is coatings industry commonly used equipment, and above example only expresses the implementation of the present invention
Mode.
It is as a result as follows by embodiment 1-3 film property test performances.
The performance of product in embodiment 1-3
Although the foregoing describing the embodiment of the present invention, it will be appreciated by those of skill in the art that these
It is merely illustrative of, protection scope of the present invention is defined by the appended claims.Those skilled in the art is not carrying on the back
On the premise of from the principle of the present invention and essence, various changes or modifications can be made to these embodiments, but these are changed
Protection scope of the present invention is each fallen within modification.
Claims (15)
1. a kind of aqueous dual-component epoxy iron red shop primer, it is characterised in that it includes first component and second component, in parts by mass：
First component includes：Aqueous epoxy resins 38-45%, iron oxide red pigment 3-15%, nano aluminium oxide 0.5-2%, dispersant
It is 0.1-0.5%, filler material 5-15%, aqueous defoamer 0.5-1.5%, waterborne preservative 0.5-1.5%, water 20-30%, water-based
Amine hardener 5-10%.
Second component includes：Aqueous epoxy resin emulsion 40-50%, aqueous defoamer 0.5-1.5%, water-based moistening flatting agent 0.5-
1.5%th, waterborne preservative 0.5-1%, water-soluble active diluent 5-10%, water 35-50%.
2. a kind of aqueous dual-component epoxy iron red shop primer according to claim 1, it is characterised in that optimization formula is：
First component：Aqueous epoxy resins 40-45%, iron oxide red pigment 5-15%, nano aluminium oxide 0.5-1.5%, dispersant 0.1-
0.5%th, filler material 5-13%, aqueous defoamer 0.5-1.2%, waterborne preservative 0.5-1.5%, water 20-29%, water-based amine are consolidated
Agent 0.5-0.9%.
Second component：Aqueous epoxy resin emulsion 40-49%, aqueous defoamer 0.5-1.3%, water-based moistening flatting agent 0.5-
1.5%th, waterborne preservative 0.5-1%, water-soluble active diluent 5-9%, water 35-45%.
3. a kind of aqueous dual-component epoxy iron red shop primer according to claim 1, it is characterised in that the water-based amine is consolidated
Agent is non-ionic, transparent, not solvent-laden cosolvent, preferably modified polyamine addition product.
4. a kind of aqueous dual-component epoxy iron red shop primer according to claim 1, it is characterised in that the filler material is
Barium sulfate.
5. a kind of aqueous dual-component epoxy iron red shop primer according to claim 1, it is characterised in that the pigment is
190 iron oxide reds, molecular weight 159.6.
6. a kind of aqueous dual-component epoxy iron red shop primer according to claim 1, it is characterised in that the water solubility is living
Property Diluent Viscosity be 9-10mPa, boiling range be 260-285 DEG C.
A kind of 7. aqueous dual-component epoxy iron red shop primer according to claim 1, it is characterised in that the epoxy resin
Latex solids content is 45-51% (quality), equivalent 390g/mol.
8. a kind of aqueous dual-component epoxy iron red shop primer according to claim 1, it is characterised in that described is nano oxidized
Aluminium ceramics particle diameter is 20-30um.
A kind of 9. aqueous dual-component epoxy iron red shop primer according to claim 1, it is characterised in that the water-based defoaming
Agent is German product DF-8206.
A kind of 10. aqueous dual-component epoxy iron red shop primer according to claim 1, it is characterised in that described water-based point
Powder is organosiloxane.
11. a kind of aqueous dual-component epoxy iron red shop primer according to claim 1, it is characterised in that described is water-based anti-
Rotten agent is benzoic acid.
A kind of 12. aqueous dual-component epoxy iron red shop primer according to claim 1, it is characterised in that the water-based profit
Humectant is levelling agent.
13. a kind of aqueous dual-component epoxy iron red shop primer according to claim 1, it is characterised in that the water is negative
Ion distilled water.
14. a kind of aqueous dual-component epoxy iron red shop primer according to claim 1, it is characterised in that a kind of water-based double groups
Divide the preparation method of epoxy iron red shop primer, the method is implemented by following steps：
(1) pigment iron oxide red and water and aqueous epoxy resins are added in container first and soaked, while added dispersant and uniformly stir
Mix.
(2) after when question response 1 is small, filler material barium sulfate, defoamer, preservative, nano aluminium oxide is added into container and is continued
When uniform stirring 0.5 is small.
(3) under stirring well, water-based amine hardener is added into container, while is warming up to 70 DEG C, treats that it fully reacts 2
When progress high speed dispersion mixing 0.5 is small after hour.
(4) after being handled by dispersion mixing, temperature is reduced to 40 DEG C, then carries out sand milling process again, will after toning
Fineness is controlled within 55um.
(5) carried out filtering obtained slurry with 130 mesh stainless steel filtering nets, that is, obtain the first component of water-soluble epoxy red ferric oxide primer.
(6) by aqueous epoxy resin emulsion, aqueous defoamer, aqueous wetting agent, waterborne preservative, water-soluble active diluent point
Be not added in container, and open mixer uniform stirring 0.5 it is small when, when then high speed dispersion 0.5 is small.
(7) filtered with 130 mesh stainless steel filtering nets, that is, obtain water-soluble epoxy red ferric oxide primer second component.
A kind of a kind of 15. aqueous dual-component epoxy iron red shop primer according to claim 1, it is characterised in that water
Property bi-component epoxy iron oxide red primer and preparation method thereof, wherein water-soluble epoxy red ferric oxide primer first component is made by step 1-5, lead to
Cross 6-7 steps and water-soluble epoxy red ferric oxide primer second component is made, can prepare at the same time, successively can not also sequentially prepare.