CN107956044A - A kind of cleaning wiping cloth and preparation method thereof - Google Patents
A kind of cleaning wiping cloth and preparation method thereof Download PDFInfo
- Publication number
- CN107956044A CN107956044A CN201711145043.9A CN201711145043A CN107956044A CN 107956044 A CN107956044 A CN 107956044A CN 201711145043 A CN201711145043 A CN 201711145043A CN 107956044 A CN107956044 A CN 107956044A
- Authority
- CN
- China
- Prior art keywords
- staple fiber
- base fabric
- wiping cloth
- cleaning wiping
- fiber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of cleaning wiping cloth and preparation method thereof, preparation method comprises the following steps：Base fabric permeable formation is made after mixing combs using low melting point staple fiber, three-dimensional hollow polyester staple fiber, two-dimentional hollow pet staple fiber；Base fabric cleaning layer is made after mixing combs using low melting point staple fiber, two-dimentional terylene short fiber peacekeeping polyester staple fiber；By glue spraying after base fabric permeable formation and the superposition of base fabric cleaning layer, and base fabric is made after drying sizing；By the permeable formation side spray glue of two layers of base fabric and corresponding overlapping, cleaning wiping cloth is made after pressing.The adsorption effect lifting of manufactured cleaning wiping cloth, will not bad student's electrostatic, moreover it is possible to reduce the use of detergent, more traditional cleaning wiping cloth is more environmentally-friendly.
Description
Technical field
The present invention relates to nonwoven fabric technology field, and in particular to a kind of cleaning wiping cloth and preparation method thereof.
Background technology
At present, the existing various cleaning wiping cloths for meeting different purposes are used to clean.Such as there is a kind of wiping of sponge material
Cloth, it is soft and can absorb large quantity of moisture, but is not easily cleaned for obstinate stain, and easily leaves washmarking.Again for example
Have a kind of PVA deerskin towels cleaning wiping cloth, although it is with the advantages of compactness good water absorption, soil pick-up ability is strong, it after use,
Clean not in time, spot is detained wherein, just can not thoroughly clean later, so that surface is more and more dirtier, soil pick-up ability declines, and wipes
Washmarking is easily left after wiping or is wiped unclean.
Therefore, the prior art also needs to further improve and develop.
The content of the invention
The purpose of the invention is to provide a kind of cleaning wiping cloth and preparation method thereof, it is intended to solve cleaning wiping cloth and wipe efficiency
Low, wiping process produces the problem of electrostatic can damage precision equipment.
Used technical solution is：
A kind of preparation method of cleaning wiping cloth, wherein, comprise the following steps：
A. using low melting point staple fiber, three-dimensional hollow polyester staple fiber, two-dimentional hollow pet staple fiber after mixing combs
Base fabric permeable formation is made；Base is made after mixing combs using low melting point staple fiber, two-dimentional terylene short fiber peacekeeping polyester staple fiber
Cloth cleaning layer；
B. by glue spraying after base fabric permeable formation and the superposition of base fabric cleaning layer, and base fabric is made after drying sizing；
C. by the permeable formation side spray glue of two layers of base fabric and corresponding overlapping, cleaning wiping cloth is made after pressing.
The cleaning wiping cloth preparation method, wherein, the low melting point staple fiber of preparation base fabric permeable formation, three in the step A
It is 15-25% to tie up hollow pet staple fiber and the percentage by weight ratio shared by two-dimentional hollow short dacron fiber：35-45%：35-
45%.
The cleaning wiping cloth preparation method, wherein, the low melting point staple fiber of preparation base fabric permeable formation, three in the step A
It is 20% to tie up hollow pet staple fiber and the percentage by weight ratio shared by two-dimentional hollow short dacron fiber：40%：40%.
The cleaning wiping cloth preparation method, wherein, the low melting point staple fiber specification for preparing base fabric permeable formation is 15D, three-dimensional
Hollow pet staple fiber specification is 25DX64, and two-dimentional hollow pet staple fiber specification is 25DX51.
The cleaning wiping cloth preparation method, wherein, the low melting point staple fiber of preparation base fabric cleaning layer, two in the step A
The percentage by weight ratio tieed up shared by terylene short fiber peacekeeping polyester staple fiber is 15-25%：35-45%：35-45%.
The cleaning wiping cloth preparation method, wherein, the low melting point staple fiber of preparation base fabric cleaning layer, two in the step A
It is 20% to tie up the percentage by weight ratio shared by terylene short fiber peacekeeping polyester staple fiber：40%：40%.
The cleaning wiping cloth preparation method, wherein, the specification for preparing the low melting point staple fiber of base fabric cleaning layer is 15DX64,
The specification of two-dimentional polyester staple fiber is 40DX64, and polyester staple fiber specification is 25DX51.
The cleaning wiping cloth preparation method, it is characterised in that in the step B used in glue spraying for water-soluble acrylic fourth
Ester, fountain height 20-40g/m2。
The cleaning wiping cloth preparation method, wherein, drying temperature is 150-180 DEG C in the step B, drying time 4-
5 minutes.
The cleaning wiping cloth preparation method, wherein, it is pressure sensitive adhesive that glue spraying is used in the step C, fountain height 15-25g/
m2。
Beneficial effect：The present invention provides a kind of new cleaning wiping cloth and preparation method thereof, which can increase wiping
The efficiency that the adsorption effect lifting of wiping cloth (rags) wipes, avoids bad student's electrostatic, moreover it is possible to reduce the use of detergent, more traditional cleaning wiping cloth
It is more environmentally-friendly.
Brief description of the drawings
Fig. 1 is base cloth production line technological process in the specific embodiment of the invention.
Fig. 2 is cleaning wiping cloth production-line technique flow chart in the specific embodiment of the invention.
Embodiment
To make the objects, technical solutions and advantages of the present invention clearer, clear and definite, develop simultaneously embodiment pair referring to the drawings
The present invention is further described.
A kind of preparation method of cleaning wiping cloth as depicted in figs. 1 and 2, wherein, comprise the following steps：
A. using low melting point staple fiber, three-dimensional hollow polyester staple fiber, two-dimentional hollow pet staple fiber after mixing combs
Base fabric permeable formation is made；Base is made after mixing combs using low melting point staple fiber, two-dimentional terylene short fiber peacekeeping polyester staple fiber
Cloth cleaning layer；
B. by glue spraying after base fabric permeable formation and the superposition of base fabric cleaning layer, and base fabric is made after drying sizing；
C. by the permeable formation side spray glue of two layers of base fabric and corresponding overlapping, cleaning wiping cloth is made after pressing.
The cleaning wiping cloth preparation method, wherein, the low melting point staple fiber of preparation base fabric permeable formation, three in the step A
It is 15-25% to tie up hollow pet staple fiber and the percentage by weight ratio shared by two-dimentional hollow short dacron fiber：35-45%：35-
45%.Wherein, the low melting point staple fiber specification for preparing base fabric permeable formation is 15D, and three-dimensional hollow polyester staple fiber specification is
25DX64 (D represents Denier unit Denier, and X represents the length of fiber), two-dimentional hollow pet staple fiber specification is 25DX51.
The further cleaning wiping cloth preparation method, wherein, the low melting point that base fabric cleaning layer is prepared in the step A is short
Percentage by weight ratio shared by fiber, two-dimentional terylene short fiber peacekeeping polyester staple fiber is 15-25%：35-45%：35-45%.
The cleaning wiping cloth preparation method, wherein, the specification for preparing the low melting point staple fiber of base fabric cleaning layer is 15DX64, two-dimentional terylene
The specification of staple fiber is 40DX64, and polyester staple fiber specification is 25DX51.
Further, in the step B used in glue spraying for water soluble propene's acid butyl ester, fountain height 20-40g/m2, dry
Dry temperature is 150-180 DEG C, and drying time is 4-5 minutes.
Specifically, it is pressure sensitive adhesive that glue spraying is used in the step C, fountain height 15-25g/m2。
Technical solution of the present invention is further elaborated below by embodiment.
Embodiment 1
The preparation method of cleaning wiping cloth specifically includes following steps：
A cleaning wiping cloth base cloth production line technological processes
1) 15D low melting points staple fiber and 25DX64 three-dimensional hollows polyester staple fiber, 25DX51 two dimension hollow pet staple fibers
After feeding 1# blending boxs fully mix after 1-4# bale openers Weighing feeding 1# is slightly opened and sent machine shredding to mix, feeding 1# essences are opened
Shredding mixes loose machine again, and being sent into the metering of 1-2# hoppers, uniformly feeding 1-2# carding machine coarse denier fibers are combed through 1-2# carding machines
The permeable formation of base fabric is completed in networking.
2) the two-dimentional polyester staple fiber of the low melting point staple fiber of 15DX64 and 40DX64, the polyester staple fiber of 25DX51 are through 5-
8# bale opener Weighings, are sent into after 2# slightly opens and send machine shredding to mix, and are sent into after 2# blending boxs fully mix, feed 2# essence shreddings
Shredding mixes machine again, and being sent into the metering of 3-4# hoppers, uniformly feeding 3-4# carding machine staple fibers comb networking through 3-4# carding machines
Complete the cleaning layer of base fabric.
3) it is sent at needing machine and shapes after 2 layers of cotton net superposition, be sent into 1# glue sprayers, in cotton net front sprinkling water solubility third
Olefin(e) acid butyl ester is sent into bottom baking oven, after drying and shaping, then through 2# glue sprayers glue spraying gives cotton net bottom to spray butyl acrylate, is sending
Enter baking oven middle level after the drying and shaping of upper strata, be sent into press and plate and then baling.
B cleaning wiping cloth finished product production-line technique flows
1) base fabric is put into unreeling machine 1-2, permeable formation is upward.Base fabric 1 sprays pressure sensitive adhesive by glue spraying 1, and base fabric 2 is by spray
Glue 2 sprays pressure sensitive adhesive.Base fabric 1 and 2 is pressed together by pressing machine, it is disconnected that feeding spends machine of cutting to spend, and is fed again into cutting machine
Cutting, coiled, packaging.
Technological requirement：Low melting point staple fiber, the three-dimensional hollow terylene short fiber peacekeeping two dimension of base fabric permeable formation are prepared in step A
Percentage by weight ratio shared by hollow short dacron fiber is 20%：40%：40%.Prepare the short fibre of low melting point of base fabric cleaning layer
Percentage by weight ratio shared by dimension, two-dimentional terylene short fiber peacekeeping polyester staple fiber is 20%：40%：40%.Glue spraying in step B
Water soluble propene's acid butyl ester fountain height used is 40g/m2, drying temperature is 150 DEG C, drying time 5 minutes, is pressed in step C
Quick glue fountain height is 20g/m2。
Cleaning wiping cloth prepared by embodiment 1 is detected, the cleaning wiping cloth of the technological forming has strong adsorption, cleaning effect
The characteristics of rate is high, and wiping process does not produce electrostatic.
Embodiment 2
The preparation method of cleaning wiping cloth specifically includes following steps：
A cleaning wiping cloth base cloth production line technological processes
1) 15D low melting points staple fiber and 25DX64 three-dimensional hollows polyester staple fiber, 25DX51 two dimension hollow pet staple fibers
After feeding 1# blending boxs fully mix after 1-4# bale openers Weighing feeding 1# is slightly opened and sent machine shredding to mix, feeding 1# essences are opened
Shredding mixes loose machine again, and being sent into the metering of 1-2# hoppers, uniformly feeding 1-2# carding machine coarse denier fibers are combed through 1-2# carding machines
The permeable formation of base fabric is completed in networking.
2) the two-dimentional polyester staple fiber of the low melting point staple fiber of 15DX64 and 40DX64, the polyester staple fiber of 25DX51 are through 5-
8# bale opener Weighings, are sent into after 2# slightly opens and send machine shredding to mix, and are sent into after 2# blending boxs fully mix, feed 2# essence shreddings
Shredding mixes machine again, and being sent into the metering of 3-4# hoppers, uniformly feeding 3-4# carding machine staple fibers comb networking through 3-4# carding machines
Complete the cleaning layer of base fabric.
3) it is sent at needing machine and shapes after 2 layers of cotton net superposition, be sent into 1# glue sprayers, in cotton net front sprinkling water solubility third
Olefin(e) acid butyl ester is sent into bottom baking oven, after drying and shaping, then through 2# glue sprayers glue spraying gives cotton net bottom to spray butyl acrylate, is sending
Enter baking oven middle level after the drying and shaping of upper strata, be sent into press and plate and then baling.
B cleaning wiping cloth finished product production-line technique flows
1) base fabric is put into unreeling machine 1-2, permeable formation is upward.Base fabric 1 sprays pressure sensitive adhesive by glue spraying 1, and base fabric 2 is by spray
Glue 2 sprays pressure sensitive adhesive.Base fabric 1 and 2 is pressed together by pressing machine, it is disconnected that feeding spends machine of cutting to spend, and is fed again into cutting machine
Cutting, coiled, packaging.
Technological requirement：Low melting point staple fiber, the three-dimensional hollow terylene short fiber peacekeeping two dimension of base fabric permeable formation are prepared in step A
Percentage by weight ratio shared by hollow short dacron fiber is 15%：45%：40%.Prepare the short fibre of low melting point of base fabric cleaning layer
Percentage by weight ratio shared by dimension, two-dimentional terylene short fiber peacekeeping polyester staple fiber is 15%：45%：40%.Glue spraying in step B
Water soluble propene's acid butyl ester fountain height used is 40/m2, drying temperature is 150 DEG C, drying time 5 minutes, pressure-sensitive in step C
Glue fountain height is 20g/m2。
Cleaning wiping cloth prepared by embodiment 2 is detected, the cleaning wiping cloth of the technological forming has strong adsorption, cleaning effect
The characteristics of rate is high, and wiping process does not produce electrostatic.
Embodiment 3
The preparation method of cleaning wiping cloth specifically includes following steps：
A cleaning wiping cloth base cloth production line technological processes
1) 15D low melting points staple fiber and 25DX64 three-dimensional hollows polyester staple fiber, 25DX51 two dimension hollow pet staple fibers
After feeding 1# blending boxs fully mix after 1-4# bale openers Weighing feeding 1# is slightly opened and sent machine shredding to mix, feeding 1# essences are opened
Shredding mixes loose machine again, and being sent into the metering of 1-2# hoppers, uniformly feeding 1-2# carding machine coarse denier fibers are combed through 1-2# carding machines
The permeable formation of base fabric is completed in networking.
2) the two-dimentional polyester staple fiber of the low melting point staple fiber of 15DX64 and 40DX64, the polyester staple fiber of 25DX51 are through 5-
8# bale opener Weighings, are sent into after 2# slightly opens and send machine shredding to mix, and are sent into after 2# blending boxs fully mix, feed 2# essence shreddings
Shredding mixes machine again, and being sent into the metering of 3-4# hoppers, uniformly feeding 3-4# carding machine staple fibers comb networking through 3-4# carding machines
Complete the cleaning layer of base fabric.
3) it is sent at needing machine and shapes after 2 layers of cotton net superposition, be sent into 1# glue sprayers, in cotton net front sprinkling water solubility third
Olefin(e) acid butyl ester is sent into bottom baking oven, after drying and shaping, then through 2# glue sprayers glue spraying gives cotton net bottom to spray butyl acrylate, is sending
Enter baking oven middle level after the drying and shaping of upper strata, be sent into press and plate and then baling.
B cleaning wiping cloth finished product production-line technique flows
1) base fabric is put into unreeling machine 1-2, permeable formation is upward.Base fabric 1 sprays pressure sensitive adhesive by glue spraying 1, and base fabric 2 is by spray
Glue 2 sprays pressure sensitive adhesive.Base fabric 1 and 2 is pressed together by pressing machine, it is disconnected that feeding spends machine of cutting to spend, and is fed again into cutting machine
Cutting, coiled, packaging.
Technological requirement：Low melting point staple fiber, the three-dimensional hollow terylene short fiber peacekeeping two dimension of base fabric permeable formation are prepared in step A
Percentage by weight ratio shared by hollow short dacron fiber is 15%：40%：45%.Prepare the short fibre of low melting point of base fabric cleaning layer
Percentage by weight ratio shared by dimension, two-dimentional terylene short fiber peacekeeping polyester staple fiber is 15%：40%：45%.Glue spraying in step B
Water soluble propene's acid butyl ester fountain height used is 40/m2, drying temperature is 150 DEG C, drying time 5 minutes, pressure-sensitive in step C
Glue fountain height is 20g/m2。
Cleaning wiping cloth prepared by embodiment 3 is detected, the cleaning wiping cloth of the technological forming has strong adsorption, cleaning effect
The characteristics of rate is high, and wiping process does not produce electrostatic.
It should be appreciated that the application of the present invention is not limited to above-mentioned citing, for those of ordinary skills, can
To be improved or converted according to the above description, all these modifications and variations should all belong to the guarantor of appended claims of the present invention
Protect scope.
Claims (10)
1. a kind of preparation method of cleaning wiping cloth, it is characterised in that comprise the following steps：
A. it is made using low melting point staple fiber, three-dimensional hollow polyester staple fiber, two-dimentional hollow pet staple fiber after mixing combs
Base fabric permeable formation；Base fabric is made after mixing combs and wipes using low melting point staple fiber, two-dimentional terylene short fiber peacekeeping polyester staple fiber
Wipe layer；
B. by glue spraying after base fabric permeable formation and the superposition of base fabric cleaning layer, and base fabric is made after drying sizing；
C. by the permeable formation side spray glue of two layers of base fabric and corresponding overlapping, cleaning wiping cloth is made after pressing.
2. cleaning wiping cloth preparation method according to claim 1, it is characterised in that base fabric permeable formation is prepared in the step A
Low melting point staple fiber, the percentage by weight ratio shared by three-dimensional hollow terylene short fiber peacekeeping two dimension hollow short dacron fiber be 15-
25%：35-45%：35-45%.
3. cleaning wiping cloth preparation method according to claim 2, it is characterised in that base fabric permeable formation is prepared in the step A
Low melting point staple fiber, the percentage by weight ratio shared by three-dimensional hollow terylene short fiber peacekeeping two dimension hollow short dacron fiber be
20%：40%：40%.
4. cleaning wiping cloth preparation method according to claim 1, it is characterised in that prepare the short fibre of low melting point of base fabric permeable formation
Dimension specification is 15D, and three-dimensional hollow polyester staple fiber specification is 25DX64, and two-dimentional hollow pet staple fiber specification is 25DX51.
5. cleaning wiping cloth preparation method according to claim 1, it is characterised in that base fabric cleaning layer is prepared in the step A
Low melting point staple fiber, the percentage by weight ratio shared by two-dimentional terylene short fiber peacekeeping polyester staple fiber be 15-25%：35-
45%：35-45%.
6. cleaning wiping cloth preparation method according to claim 5, it is characterised in that base fabric cleaning layer is prepared in the step A
Low melting point staple fiber, the percentage by weight ratio shared by two-dimentional terylene short fiber peacekeeping polyester staple fiber be 20%：40%：
40%.
7. cleaning wiping cloth preparation method according to claim 1, it is characterised in that prepare the short fibre of low melting point of base fabric cleaning layer
The specification of dimension is 15DX64, and the specification of two-dimentional polyester staple fiber is 40DX64, and polyester staple fiber specification is 25DX51.
8. cleaning wiping cloth preparation method according to claim 1, it is characterised in that in the step B used in glue spraying for water
Soluble acrylic butyl ester, fountain height 20-40g/m2。
9. cleaning wiping cloth preparation method according to claim 1, it is characterised in that drying temperature is 150- in the step B
180 DEG C, drying time is 4-5 minutes.
10. cleaning wiping cloth preparation method according to claim 1, it is characterised in that glue spraying is used to be pressure-sensitive in the step C
Glue, fountain height 15-25g/m2。