CN107940914A - It is a kind of to be used for aluminium or the auxiliary heat treatment oven of copper alloy machinery person joint - Google Patents
It is a kind of to be used for aluminium or the auxiliary heat treatment oven of copper alloy machinery person joint Download PDFInfo
- Publication number
- CN107940914A CN107940914A CN201710951321.3A CN201710951321A CN107940914A CN 107940914 A CN107940914 A CN 107940914A CN 201710951321 A CN201710951321 A CN 201710951321A CN 107940914 A CN107940914 A CN 107940914A
- Authority
- CN
- China
- Prior art keywords
- heat treatment
- aluminium
- copper alloy
- air inlet
- auxiliary heat
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
It is used for aluminium or the auxiliary heat treatment oven of copper alloy machinery person joint the invention discloses a kind of, including babinet, air inlet pipe, blast pipe, air blower, the internal layer of the babinet is provided with heating unit, heat insulation wall, the air inlet pipe, blast pipe, it is connected respectively with air inlet and gas outlet, air inlet pipe connects inert gas tank, and flow control valve, blast pipe connection air blower are provided with air inlet pipe;The internal face is equipped with object carrying support, and the internal face also installs temperature control module and safety monitoring module, and the heating unit, safety monitoring module, temperature control module, flow control valve, air blower are electrically connected with peripheral control unit.The present invention takes full advantage of the condition of baking oven, the metal relatively low to internal stress heat treatment temperature(Copper alloy, aluminium alloy)Handled, reduce inter alia the slow Low Temperature Heat Treatment of baking oven influences, and annealing is become more meticulous, and reduces drying course to the possible adverse effect of metal destressing process.
Description
Technical field
The present invention relates to baking oven field, more particularly to a kind of be heat-treated for the auxiliary of aluminium or copper alloy machinery person joint to dry
Case.
Background technology
Baking oven is commonly used equipment in industry, including convection oven, vacuum drying oven etc..Existing baking oven carries mostly
Bleeding point and air inlet babinet, in babinet or on side wall, equipped with heating element.It is divided into several layers by HORIZONTAL PLAID canopy in babinet, holds
The material disc of material is placed on grid, close chamber door, vacuumized with vacuum pump, then start heating element, by heat radiation come
Oven interior is heated, while article in baking oven is heated, achievees the purpose that drying.
For aluminium or copper alloy, due to the property of metal in itself, Low-temperature stress-relief annealing, or even recrystallization annealing exist
Less than 400 DEG C can occur, and the requirement to temperature is relatively low.Since mechanical person joint is to the moment of torsion of metal material, toughness, rigidity
All required with lasting usability, so can generally special thermal treatment be carried out to material.And after forming, to mechanical person joint also
Need grinding, face coat, drying and etc., drying when, have certain temperature, although relatively special annealing process temperature compared with
It is low, but its influence is not negligible, and since baking oven is being run always, certain influence can be produced on metal material,
This influence is difficult to estimate again.Therefore, in order to which effect when accomplishing that baking oven dries mechanical person joint is controllable and predicts its influence degree,
Need to accomplish its heat treatment process it is controllable so that material process is finer, is guaranteed using mechanical property.
The content of the invention
It is used for aluminium or the auxiliary heat treatment oven of copper alloy machinery person joint, the baking it is an object of the invention to provide a kind of
Case carries out it controllable heat treatment process while drying and processing machinery person joint, to overcome existing in the prior art ask
Topic.
In order to realize the above object the technical scheme is that:
It is a kind of to be used for aluminium or the auxiliary heat treatment oven of copper alloy machinery person joint, including babinet, air inlet pipe, blast pipe, air blast
Machine, the internal layer of the babinet are provided with heating unit, heat insulation wall, and the heat insulation wall is distributed in around heating unit and cabinet wall
Face, the air inlet pipe, blast pipe, respectively with being opened in babinet and being connected through the air inlet in cabinet wall face and gas outlet, into
Tracheae connects inert gas tank, and flow control valve, blast pipe connection air blower are provided with air inlet pipe;
The internal face is equipped with object carrying support, and the internal face also installs temperature control module and safety monitoring module, the heating
Device, safety monitoring module, temperature control module, flow control valve, air blower are electrically connected with peripheral control unit.
Preferably, the temperature control module realizes that the temperature range that temperature control is adjusted is room temperature ~ 350 DEG C.Aluminium alloy
Stress relief annealing temperature is at 280-350 DEG C, and the stress relief annealing temperature of copper alloy is at 260-300 DEG C, and actual use temperature is than it
Low 20 ~ 30 DEG C, this temperature range can meet requirement.
Preferably, the safety monitoring module includes temperature monitoring, pressure monitor, emergency stop device.Safety monitoring
The change of module main monitoring temperature, pressure, when there is a situation where excessive, emergency stop.
Preferably, the thickness of the heat insulation wall is 12-27mm.The thickness of heat insulation wall ensures heat insulation effect.
Preferably, the temperature adjustment speed excursion of the temperature control module is 3 ~ 20 DEG C/min.Temperature control module temperature adjustment speed
Change makes its controllability very strong.
It is connected to preferably, the blast pipe stretches out a branch pipe in babinet.Branch pipe circulates in occurring, and supervisor makes air blast
Dry outer circulation.
Preferably, the heat insulation wall is made of thermal insulation material, the thermal insulation material includes the component of following parts by weight:
15-20 parts of hydrophobic calcium silicates
20-25 parts of mineral wool
20-30 parts of alumina silicate
20-40 parts of inorganic salts coagulating agent.
Above component heat resistance is good, can long-time service at 300 ~ 400 DEG C.
Preferably, the thermal insulation material is pressed into 60kg/m when heat insulation wall is made3With upper density, and component is layered
Arrangement, hydrophobic calcium silicates is as outer layer, and alumina silicate is as internal layer.Make heat insulation effect more notable with upper density and level setting.
The beneficial effects of the present invention are:The present invention's is used for aluminium or the auxiliary heat treatment baking of copper alloy machinery person joint
Case, well arranged, heat treatment condition is controllable.The ratio of inner-outer circulation is adjusted into inert gas air blast and blast pipe and branch pipe,
It is stable reliable;Temperature control module controls heating rate, the process of heat treatment and baking is become controllable;Object carrying support reduces robot
Joint and contact area, are at vacant state, heat treatment is evenly;Safety monitoring module makes security performance reliable and stable.
The baking oven of the present invention takes full advantage of the heat condition of baking oven, the metal relatively low to internal stress heat treatment temperature(Copper alloy, aluminium close
Gold)Handled, reduce special heat treatment process step, while the slow Low Temperature Heat Treatment for reducing baking oven influences, and makes
Annealing becomes more meticulous, and reduces drying course to the possible adverse effect of metal destressing process.
Brief description of the drawings
Fig. 1 is the structure diagram of the embodiment of the present invention.
In figure:1- babinets, 11- internal faces, 2- air inlet pipe, 20- flow control valves, 21- air inlets, 3- blast pipes, 31- go out
Gas port, 32- branch pipes, 4- air blowers, 5- heating units, 6- heat insulation walls, 7- object carrying supports, 81- temperature control modules, 82- safety monitorings
Module.
Embodiment
In order to illustrate the technical solutions in the embodiments of the present application or in the prior art more clearly, letter will be made to embodiment below
Singly introduce.
It is a kind of for aluminium or the auxiliary heat treatment oven of copper alloy machinery person joint such as Fig. 1, including babinet 1, air inlet pipe 2,
Blast pipe 3, air blower 4, the internal layer of the babinet 1 are provided with heating unit 5, heat insulation wall 6, and the heat insulation wall 6 is distributed in heating
With 1 internal face 11 of babinet around device 5, the thickness of the heat insulation wall 6 is 12-27mm;
The air inlet pipe 2, blast pipe 3, respectively with being opened in babinet 1 and the air inlet 21 through 1 internal face of babinet and gas outlet
31 connections, air inlet pipe 2 connect inert gas tank(Not shown in figure), flow control valve 20, blast pipe 3 are provided with air inlet pipe 2
Air blower 4 is connected, the blast pipe 3 stretches out a branch pipe 32 and is connected in babinet 1, and valve is also provided with blast pipe 3 and branch pipe 32
Door;
The internal face 11 is equipped with object carrying support 7, and the internal face 11 also installs temperature control module 81 and safety monitoring module 82,
The temperature control module 81 realizes that the temperature range that temperature control is adjusted is room temperature ~ 350 DEG C, the temperature adjustment speed of the temperature control module 81
Excursion is 3 ~ 20 DEG C/min, and the safety monitoring module 82 includes temperature monitoring, pressure monitor, emergency stop device, institute
State heating unit 5, safety monitoring module 82, temperature control module 81, flow control valve 20, air blower 4 and peripheral control unit(In figure
It is not shown)It is electrically connected;
The heat insulation wall 6 is made of thermal insulation material, and the thermal insulation material includes the component of following parts by weight:
15-20 parts of hydrophobic calcium silicates
20-25 parts of mineral wool
20-30 parts of alumina silicate
20-40 parts of inorganic salts coagulating agent,
Wherein, 60kg/m is pressed into when heat insulation wall is made in the thermal insulation material3With upper density, and component carries out layered arrangement, hates
Water calcium silicates is as outer layer, and alumina silicate is as internal layer;
During the oven aluminum alloy machinery person joint, treatment temperature is 250-320 DEG C, 8 ~ 15 DEG C/min of heating rate, place
Manage 1.5 ~ 4h of the time;During the oven copper alloy machinery person joint, treatment temperature is 230-280 DEG C, heating rate 5 ~ 10
DEG C/min, 3 ~ 6h of processing time.
Above example is only illustrating the preferred technical solution of the present invention, it is noted that for the general of the art
For logical technical staff, without departing from the principle of the present invention, some improvement made or equivalent substitution, are accordingly to be regarded as this
The protection domain of invention, should cover in scope of the presently claimed invention.
Claims (8)
1. a kind of be used for aluminium or the auxiliary heat treatment oven of copper alloy machinery person joint, it is characterised in that including babinet, air inlet
Pipe, blast pipe, air blower, the internal layer of the babinet are provided with heating unit, heat insulation wall, and the heat insulation wall is distributed in heating unit
Around and cabinet wall face, the air inlet pipe, blast pipe, respectively be opened in babinet and through cabinet wall face air inlet and
Gas outlet connects, air inlet pipe connection inert gas tank, and flow control valve, blast pipe connection air blower are provided with air inlet pipe;
The internal face is equipped with object carrying support, and the internal face also installs temperature control module and safety monitoring module, the heating
Device, safety monitoring module, temperature control module, flow control valve, air blower are electrically connected with peripheral control unit.
2. a kind of auxiliary heat treatment oven for aluminium or copper alloy machinery person joint according to claim 1, its feature
It is, the temperature control module realizes that the temperature range that temperature control is adjusted is room temperature ~ 350 DEG C.
3. a kind of auxiliary heat treatment oven for aluminium or copper alloy machinery person joint according to claim 1, its feature
It is, the safety monitoring module includes temperature monitoring, pressure monitor, emergency stop device.
4. a kind of auxiliary heat treatment oven for aluminium or copper alloy machinery person joint according to claim 1, its feature
It is, the thickness of the heat insulation wall is 12-27mm.
5. a kind of auxiliary heat treatment oven for aluminium or copper alloy machinery person joint according to claim 2, its feature
It is, the temperature adjustment speed excursion of the temperature control module is 3 ~ 20 DEG C/min.
6. a kind of auxiliary heat treatment oven for aluminium or copper alloy machinery person joint according to claim 1, its feature
It is, the blast pipe stretches out a branch pipe and is connected in babinet.
7. a kind of auxiliary heat treatment oven for aluminium or copper alloy machinery person joint according to claim 1, its feature
It is, the heat insulation wall is made of thermal insulation material, and the thermal insulation material includes the component of following parts by weight:
15-20 parts of hydrophobic calcium silicates
20-25 parts of mineral wool
20-30 parts of alumina silicate
20-40 parts of inorganic salts coagulating agent.
8. a kind of auxiliary heat treatment oven for aluminium or copper alloy machinery person joint according to claim 7, its feature
It is, the thermal insulation material is pressed into 60kg/m when heat insulation wall is made3With upper density, and component carries out layered arrangement, hydrophobic silicon
Sour calcium is as outer layer, and alumina silicate is as internal layer.