CN107938116A - A kind of processing method of high F numbers spring Asia textile fabric - Google Patents
A kind of processing method of high F numbers spring Asia textile fabric Download PDFInfo
- Publication number
- CN107938116A CN107938116A CN201711227795.XA CN201711227795A CN107938116A CN 107938116 A CN107938116 A CN 107938116A CN 201711227795 A CN201711227795 A CN 201711227795A CN 107938116 A CN107938116 A CN 107938116A
- Authority
- CN
- China
- Prior art keywords
- fibrillation
- agent
- processing method
- textile fabric
- spring asia
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The present invention relates to a kind of processing method of high F numbers spring Asia textile fabric, after the completion of warp thread and weft yarns, then completes processing by fibrillation of decrement, the secondary fibrillation of freshening, dyeing and heat treatment successively.Compared with prior art, the spring Asia textile fabric style that prepared by the present invention is greatly improved with feel closer to cotton fabric, wearing comfort, also tends to the natural stype of current trend；Because of the generation of micro- velvet, fabric texture is more thick and solid close, and feel is more plentiful, substantially increases class sense of fabric etc..
Description
Technical field
The present invention relates to fabric final finishing technical field, more particularly, to a kind of processing method of high F numbers spring Asia textile fabric.
Background technology
With the improvement of living standards, people are also more and more diversified to the demand of various daily necessitiess, for cloth
It is not limited only to hide the function that body is gone to a winter resort, second, having more preferable quality and functional requirement, is particularly embodied in pattern
Selection, comfortable feel.
In the prior art, spring Asia textile fabric passes through three step simple process of fibrillation, dyeing and sizing generally after the completion of braiding
To complete, the fabric that so processing obtains only carries out Alkali reduction to polyester fiber, changes product feel, i.e. flexibility increases,
But there is no " suede " sense, finished surface is more stiff, and chemical fibre sense is still very strong, and sense of worth is relatively low.
The content of the invention
It is an object of the present invention to overcome the above-mentioned drawbacks of the prior art and provide a kind of high F numbers spring Asia spinning face
The processing method of material.
The purpose of the present invention can be achieved through the following technical solutions：
A kind of processing method of high F numbers spring Asia textile fabric, after the completion of warp thread and weft yarns, then successively by decrement one
The secondary fibrillation of secondary fibrillation, freshening, dyeing and heat treatment, that is, complete processing.The institutional framework of fabric braiding in the present invention is pressed
It is 50D/75F*50D/144F 58*48 (amount of twist) through weft yarn order.
Preferably, warp thread uses the high stretch yarn spun polyester thread of 72F, and weft yarn uses the high stretch yarn spun polyester thread using 144F.
Preferably, the process of fibrillation of decrement is specially：
The fabric for weaving completion is placed in a fibrillation including 30% liquid caustic soda, fibrillation agent, bleeding agent and chelated dispersants
Fibrillation handles the 120min wherein addition quality of 30% liquid caustic soda fibrillation agent bleeding agent and chelated dispersants at 105 DEG C in treatment fluid
Accounting is respectively 1.5-2%, 0.1%, 1% and 1%.
It is furthermore preferred that during a fibrillation is reduced, liquid caustic soda adds at the same time with fibrillation agent；
When fabric is placed in a fibrillation treatment fluid, elder generation is heated to 105 DEG C, then constant temperature from 30 DEG C of speed with 1 DEG C/min
120min, is then cooled to 80 DEG C, washing, that is, complete fibrillation of decrement.
Preferably, the process of the secondary fibrillation of freshening is specially：
Fabric is placed in the secondary fibrillation treatment fluid including 30% liquid caustic soda, fibrillation agent, bleeding agent and chelated dispersants,
Fibrillation handles 90min at 130 DEG C, wherein, 30% liquid caustic soda, fibrillation agent, the addition quality accounting point of bleeding agent and chelated dispersants
Wei 0.5%, 0.1%, 1% and 1%.
It is furthermore preferred that during the secondary fibrillation of freshening, liquid caustic soda adds at the same time with fibrillation agent control
When fabric is placed in secondary fibrillation treatment fluid, elder generation is heated to 130 DEG C from 30 DEG C of speed with 0.6 DEG C/min, then permanent
Warm 90min, is then cooled to 80 DEG C, washing, that is, complete the secondary fibrillation of freshening.
Preferably, dyestuff used in dyeing course includes the scattered dye of disperse dyes red 3B, 0.1wt% of 1.5wt%
Expect the high temperature levelling agent OF and 2v/v% high temperature wetting softener 1227 of orange 4RF, 1v/v%, the pH value control of dyestuff is 4-5, dye
Maximum temperature during color is no more than 130 DEG C.
Preferably, the process of heat treatment is specially：
First using clear water, high temperature pre-setting is handled at 190 DEG C, restores washing, finally, low at 170 DEG C using raising agent
Temperature sizing, that is, complete.
Compared with prior art, the present invention has the following advantages：
(1) present invention employs 72F warp thread and 144F weft yarns, it is much higher than common spring Asia spinning faces of traditional 24F through weft yarn
Material, on the one hand improves the intrinsic feel of spring Asia textile fabric, and feel more flexible silk is slided, while is also established for follow-up double fiber opening process
Raw material basis is determined.
(2) present invention adds decrement+fiber opening process link, decrement arrangement is to improve high F spring Asia relative to traditional handicraft
The soft key of textile fabric, while fibrillation makes fiber fully expand, and further increases feel flexibility, and be rear road cotton sense
Arrangement provides a convenient.
(3) present invention adds the secondary fiber opening process link of freshening, fiber obvolvent is further divided relative to traditional handicraft
Dissipate, fiber is more fluffy, this technique is the critical process of imitative cotton feel.
(4) sub- spinning cotton sense cloth of high F numbers spring, by above-mentioned raw materials proportioning and technique, makes fabric style closer with feel
In cotton fabric, wearing comfort is greatly improved, and also tends to the natural stype of current trend；Because of the generation of micro- velvet,
Fabric texture is more thick and solid close, and feel is more plentiful, substantially increases the class sense of fabric.
Brief description of the drawings
Fig. 1 is the process chart of the secondary fibrillation of freshening of the present invention.
Embodiment
The present invention is described in detail with specific embodiment below in conjunction with the accompanying drawings.
A kind of processing method of high F numbers spring Asia textile fabric, after the completion of warp thread and weft yarns, then successively by decrement one
The secondary fibrillation of secondary fibrillation, freshening, dyeing and heat treatment, that is, complete processing.
As a preferred embodiment of the present invention, warp thread uses the high stretch yarn spun polyester thread of 72F, and weft yarn is adopted
With the high stretch yarn spun polyester thread of 144F.
As a preferred embodiment of the present invention, the process of fibrillation of decrement is specially：
The fabric for weaving completion is placed in a fibrillation including 30% liquid caustic soda, fibrillation agent, bleeding agent and chelated dispersants
In treatment fluid, fibrillation handles 120min at 105 DEG C, wherein, 30% liquid caustic soda, fibrillation agent, bleeding agent and chelated dispersants add
It is respectively 1.5-2%, 0.1%, 1% and 1% to add quality accounting.
It is furthermore preferred that during a fibrillation is reduced, liquid caustic soda adds at the same time with fibrillation agent；
When fabric is placed in a fibrillation treatment fluid, elder generation is heated to 105 DEG C, then constant temperature from 30 DEG C of speed with 1 DEG C/min
120min, is then cooled to 80 DEG C, washing, that is, complete fibrillation of decrement.
As a preferred embodiment of the present invention, the process of the secondary fibrillation of freshening is specially：
Fabric is placed in the secondary fibrillation treatment fluid including 30% liquid caustic soda, fibrillation agent, bleeding agent and chelated dispersants,
Fibrillation handles 90min at 130 DEG C, wherein, 30% liquid caustic soda, fibrillation agent, the addition quality accounting point of bleeding agent and chelated dispersants
Wei 0.5%, 0.1%, 1% and 1%.
It is furthermore preferred that during the secondary fibrillation of freshening, liquid caustic soda adds at the same time with fibrillation agent control
When fabric is placed in secondary fibrillation treatment fluid, elder generation is heated to 130 DEG C from 30 DEG C of speed with 0.6 DEG C/min, then permanent
Warm 90min, is then cooled to 80 DEG C, washing, that is, complete the secondary fibrillation of freshening.
As a preferred embodiment of the present invention, dyestuff used in dyeing course includes the scattered of 1.5wt%
High temperature levelling agent OF and 2v/v% the high temperature wetting softener of disperse dyes orange 4RF, 1v/v% of dyestuff red 3B, 0.1wt%
1227, the control of the pH value of dyestuff be 4-5, and the maximum temperature in dyeing course is no more than 130 DEG C.
As a preferred embodiment of the present invention, the process of heat treatment is specially：
First using clear water, high temperature pre-setting is handled at 190 DEG C, restores washing, finally, low at 170 DEG C using raising agent
Temperature sizing, that is, complete.
Embodiment 1
A kind of processing method of high F numbers spring Asia textile fabric, after the completion of warp thread and weft yarns, then successively by decrement one
The secondary fibrillation of secondary fibrillation, freshening, dyeing and heat treatment, that is, complete processing.
In the present embodiment, warp thread uses the high stretch yarn spun polyester thread of 72F, and weft yarn uses the high stretch yarn Polyester Yarns using 144F
Line.
The process of fibrillation of decrement is specially in the present embodiment：
The fabric for weaving completion is placed in a fibrillation including 30% liquid caustic soda, fibrillation agent, bleeding agent and chelated dispersants
In treatment fluid, fibrillation handles 120min at 105 DEG C, wherein, 30% liquid caustic soda, fibrillation agent, bleeding agent and chelated dispersants add
It is respectively 1.5-2%, 0.1%, 1% and 1% to add quality accounting.During a fibrillation is reduced, liquid caustic soda and fibrillation agent are at the same time
Add；When fabric is placed in a fibrillation treatment fluid, elder generation is heated to 105 DEG C, then constant temperature from 30 DEG C of speed with 1 DEG C/min
120min, is then cooled to 80 DEG C, washing, that is, complete fibrillation of decrement.
The process of the secondary fibrillation of freshening is as shown in Figure 1, be specially in the present embodiment：By fabric be placed in including 30% liquid caustic soda,
In the secondary fibrillation treatment fluid of fibrillation agent, bleeding agent and chelated dispersants, fibrillation handles 90min at 130 DEG C, wherein, 30%
Liquid caustic soda, fibrillation agent, the addition quality accounting of bleeding agent and chelated dispersants are respectively 0.5%, 0.1%, 1% and 1%.In freshening
During secondary fibrillation, liquid caustic soda adds at the same time with fibrillation agent control；When fabric is placed in secondary fibrillation treatment fluid, first from 30 DEG C with
The speed of 0.6 DEG C/min is heated to 130 DEG C, then constant temperature 90min, is then cooled to 80 DEG C, washing, that is, completes that freshening is secondary to be opened
It is fine.
In the present embodiment, dyestuff used includes point of disperse dyes red 3B, 0.1wt% of 1.5wt% in dyeing course
The high temperature levelling agent OF and 2v/v% high temperature wetting softener 1227 of dyestuff orange 4RF, 1v/v% are dissipated, the pH value control of dyestuff is 4-
5, the maximum temperature in dyeing course is no more than 130 DEG C.
In the present embodiment, the process of heat treatment is specially：
First using clear water, high temperature pre-setting is handled at 190 DEG C, restores washing, finally, low at 170 DEG C using raising agent
Temperature sizing, that is, complete.
The above-mentioned description to embodiment is understood that for ease of those skilled in the art and using invention.
Person skilled in the art obviously easily can make these embodiments various modifications, and described herein general
Principle is applied in other embodiment without by performing creative labour.Therefore, the invention is not restricted to above-described embodiment, ability
Field technique personnel disclose according to the present invention, do not depart from improvement that scope made and modification all should be the present invention's
Within protection domain.
Claims (8)
1. a kind of processing method of high F numbers spring Asia textile fabric, it is characterised in that after the completion of warp thread and weft yarns, then successively
By being reduced a fibrillation, the secondary fibrillation of freshening, dyeing and heat treatment, that is, complete processing.
2. the processing method of a kind of high F numbers spring Asia textile fabric according to claim 1, it is characterised in that warp thread uses 72F
High stretch yarn spun polyester thread, weft yarn use using 144F high stretch yarn spun polyester thread.
3. the processing method of a kind of high F numbers spring Asia textile fabric according to claim 1, it is characterised in that decrement is once opened
Fine process is specially：
The fabric for weaving completion is placed in a fibrillation including 30% liquid caustic soda, fibrillation agent, bleeding agent and chelated dispersants to handle
In liquid, fibrillation handles 120min at 105 DEG C, wherein, 30% liquid caustic soda, fibrillation agent, the addition matter of bleeding agent and chelated dispersants
It is respectively 1.5-2%, 0.1%, 1% and 1% to measure accounting.
4. the processing method of a kind of high F numbers spring Asia textile fabric according to claim 3, it is characterised in that in decrement once
During fibrillation, liquid caustic soda adds at the same time with fibrillation agent；
When fabric is placed in a fibrillation treatment fluid, elder generation is heated to 105 DEG C, then constant temperature from 30 DEG C of speed with 0.6 DEG C/min
120min, is then cooled to 80 DEG C, washing, that is, complete fibrillation of decrement.
5. the processing method of a kind of high F numbers spring Asia textile fabric according to claim 1, it is characterised in that freshening is secondary to be opened
Fine process is specially：
Fabric is placed in the secondary fibrillation treatment fluid including 30% liquid caustic soda, fibrillation agent, bleeding agent and chelated dispersants, 130
Fibrillation handles 90min at DEG C, wherein, 30% liquid caustic soda, fibrillation agent, the addition quality accounting of bleeding agent and chelated dispersants are respectively
0.5%th, 0.1%, 1% and 1%.
6. the processing method of a kind of high F numbers spring Asia textile fabric according to claim 5, it is characterised in that secondary in freshening
During fibrillation, liquid caustic soda adds at the same time with fibrillation agent control
When fabric is placed in secondary fibrillation treatment fluid, elder generation is heated to 130 DEG C, then constant temperature from 30 DEG C of speed with 0.6 DEG C/min
90min, is then cooled to 80 DEG C, washing, that is, complete the secondary fibrillation of freshening.
A kind of 7. processing method of high F numbers spring Asia textile fabric according to claim 1 or 6, it is characterised in that dyeing course
In used dyestuff include 1.5wt% disperse dyes red 3B, 0.1wt% disperse dyes orange 4RF, 1v/v% high temperature level dyeing
Agent OF and 2v/v% high temperature wetting softener 1227, the pH value control of dyestuff is 4-5, and the maximum temperature in dyeing course is no more than
130℃。
8. the processing method of a kind of high F numbers spring Asia textile fabric according to claim 1, it is characterised in that heat treatment
Process is specially：
First using clear water, high temperature pre-setting is handled at 190 DEG C, is restored washing, finally, is determined using raising agent in 170 DEG C of low temperature
Type, that is, complete.