CN107930620A - The preparation method of the air purification photocatalyst of titanium dioxide surface load super-small noble metal - Google Patents
The preparation method of the air purification photocatalyst of titanium dioxide surface load super-small noble metal Download PDFInfo
- Publication number
- CN107930620A CN107930620A CN201711230830.3A CN201711230830A CN107930620A CN 107930620 A CN107930620 A CN 107930620A CN 201711230830 A CN201711230830 A CN 201711230830A CN 107930620 A CN107930620 A CN 107930620A
- Authority
- CN
- China
- Prior art keywords
- noble metal
- air purification
- preparation
- titanium dioxide
- photocatalyst
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of preparation method of the air purification photocatalyst of titanium dioxide surface load super-small noble metal, by commercial TiO2(P25, similarly hereinafter) mixed with noble metal precursor liquor, water and ethanol are added into the solid mixture, become a certain concentration suspension, abundant ultrasonic disperse, and dried in spray dryer high temperature quick break, metal precursor crystal growth is avoided, finally obtains powdered solid predecessor.Gained solid precursors are calcined in a reducing atmosphere, up to TiO2M photocatalyst materials.This method preparation process is easy to operate, technique is simple, it is pollution-free, cost is low, for the support type photocatalyst obtained using P25 as substrate, your nano-particle diameter is equably carried on P25 surfaces between 0.3 1nm, have broad application prospects with high effective catalytic active area and excellent air purification ability, thus in air purification field.
Description
Technical field
The present invention relates to a kind of TiO2The air of area load super-small noble metal M (M=Pt, Au, Ag, Pd, Ru, Ir)
Purify the preparation method of photocatalyst, it is more particularly to a kind of P25 apparent heights are dispersed, the minimum particle diameter of load (between
0.3nm-1nm) the preparation method of your nano particle.
Background technology
Room air pollution is to endanger one of 5 overall situation factors of human health, and research shows that there are 500 in room air
A variety of volatile organic matters, such as formaldehyde, benzene carcinogenicity pollutant.Photocatalysis oxidation technique is because its is environmental-friendly, degradation capability
Air purifying process that is strong and becoming most competitiveness.Wherein, TiO2(P25, similarly hereinafter) material is with its cheap, chemical stabilization
The advantages that property is good, catalytic activity is high becomes most popular photocatalyst material.In addition, noble metal nano particles, such as Pt, Au,
Ag, Pd, Ru, Ir etc., have higher surface energy and superficial catalytic activation, there is uniqueness to urge volatile organic matter in air
Change acts on, and its performance is stablized, and is star's catalysis material in catalytic field.
Research confirms to be supported on noble metal nano particles on cheap semiconductor photocatalyst material, can not only improve your gold
The utilization ratio of metal nano-particle, reduces the manufacturing cost of material, moreover it is possible to effectively improves semiconductor-noble metal support type photocatalyst
The photocatalysis performance of material.The catalytic performance of such material depends primarily upon noble metal and the combination of semiconductor photocatalyst material is steady
Qualitative, noble metal is in physical quantitys such as the distributing homogeneity of semiconductor surface, size, composition, structures.Such material is ground at present
The pattern for being directed generally to modified semi-conducting material, structure, crystalline phase etc. are studied carefully, so as to fulfill effectively dividing for its inside photo-generated carrier
From, and then improve its catalytic activity.
But so far, had no in preparation to support type semiconductor-noble metal catalysis material synthesis report on
P25 apparent heights disperse, uniform load size between 0.3 nanometer of -1 nano-noble metal nano particle report.It is right at present at the same time
The preparation of metal nanocrystal is typically all to be carried out using photo-reduction sedimentation or infusion process, these methods are difficult to receive noble metal
The distribution of rice grain, size carry out Effective Regulation, are unfavorable for mass producing, therefore greatly limit it and answered in large-scale production
With.
The content of the invention
To solve drawbacks described above existing in the prior art, it is an object of the invention to provide one kind effectively to suppress expensive
Metal makes it with superfine small size uniform, firm is supported on titanium dioxide (P25, similarly hereinafter) table in the reunion of semiconductor surface
Face, and technique is simple, and pollution-free, cost is low, can realize method prepared by batch.The supported titanium obtained2- M (M=
Pt, Au, Ag, Pd, Ru, Ir) photocatalyst is using P25 as substrate, noble metal nano particles (diameter is between 0.3-1nm) are equably born
P25 surfaces are loaded in, there is high effective catalytic active area and excellent air purification ability, thus are had in air purification field
Have broad application prospects.
The present invention is realized by following technical proposals.
The preparation method of the air purification photocatalyst of titanium dioxide surface load super-small noble metal provided by the invention,
Comprise the following steps：
1) first will be according to TiO2Mass ratio with noble metal is 1：10-1:1000, by TiO2Powder and noble metal precursor body
Solution mixes, then into the mixed liquor according to solid content (TiO2With noble metal gross mass) and water and ethanol 10：600：400
Mass ratio adds water and ethanol, and it is 10% to make formed suspension ratio containing solid quality, then carries out abundant ultrasound to it
After scattered, it is passed through quick break in spray dryer and dries, metal precursor crystal growth is avoided, before collecting powdered solid content
Drive thing；
2) the solid predecessor is placed in Muffle furnace, 400 DEG C is warming up to 5 DEG C/min, in the hydrogen argon gas of hydrogen 5%
Calcined in gaseous mixture, the product after calcining is TiO2- M photocatalyst materials.
Further, contained noble metal is one kind in Pt, Au, Ag, Pd, Ru or Ir in the noble metal precursor liquid.
Further, the noble metal precursor liquid is the salting liquid of soluble correspondence noble metal, corresponding your gold of solubility
It is respectively chloroplatinic acid, gold chloride, silver nitrate, chlorine palladium acid, ruthenium hydrochloride ammonium or chloro-iridic acid to belong to salt.
Further, the concentration of salt solution of the noble metal is 50-100mM.
Further, in the step 1), the suspension that is formed contains 10% solid content, after abundant ultrasonic disperse, is passed through spray
In mist drier, the flow velocity for keeping suspension is 10-1000ml/h.
Further, in the step 1), drier drying temperature setting range is 100-180 DEG C.
Further, in the step 2), reducing atmosphere is the hydrogen argon gas gaseous mixture of hydrogen 5%.
Further, in the step 2), solid predecessor is warming up to 400 DEG C in Muffle furnace with 5 DEG C/min, calcination time
2h。
Whole preparation process of the present invention is easy to operate, and technique is simple, available for supported titanium2- M (M=Pt, Au, Ag,
Pd, Ru, Ir) photocatalyst material batch prepare.This method is pollution-free, and cost is low, the supported titanium obtained2- M (M=Pt,
Au, Ag, Pd, Ru, Ir) photocatalyst is using P25 as substrate, your nano particle (diameter is between 0.3nm-1nm) is equably carried on
P25 surfaces, have high effective catalytic active area and excellent air purification ability, thus have extensively in air purification field
Wealthy application prospect.
Sprayed by spray dryer high temperature, dry suspension quick break, can effectively suppress noble metal precursor body
The forming core of salt is grown up, and is made precious metal ion uniform adsorption and is highly dispersed in P25 particle surfaces, further forges in a reducing atmosphere
Burn, promote the precious metal ion original position forming core of these high degree of dispersion and form size to receive between 0.3 nanometer -1 nanometer of noble metal
Rice corpuscles is carried on P25 surfaces.
Brief description of the drawings
The transmission electron microscope picture that it is commercial P25 that Fig. 1, which is,；
Fig. 2 is TiO prepared by embodiment 12The transmission electron microscope picture of-Au photocatalysts；
Fig. 3 is TiO prepared by embodiment 22The transmission electron microscope picture of-Ir photocatalysts；
Fig. 4 is TiO prepared by embodiment 32The transmission electron microscope picture of-Pd photocatalysts；
Fig. 5 is TiO prepared by embodiment 42The transmission electron microscope picture of-Pt photocatalysts；
Fig. 6 is TiO prepared by embodiment 52The transmission electron microscope picture of-Ru photocatalysts；
Fig. 7 is TiO prepared by embodiment 62The transmission electron microscope picture of-Pt-Au photocatalysts.
Embodiment
The invention will be described in further detail with reference to the accompanying drawings and examples, but is not intended as doing any limit to invention
The foundation of system.
The preparation method of the air purification photocatalyst of the titanium dioxide surface load super-small noble metal of the present invention, including
Following step：
1) first will be according to TiO2Mass ratio with noble metal is 1：10-1:1000, by TiO2Powder and noble metal precursor body
Solution mixes, and the Concentration of precursor solution of noble metal be 50-100mM, in noble metal precursor liquid contained noble metal be Pt, Au, Ag, Pd,
One kind in Ru or Ir；Noble metal precursor liquid corresponds to the salting liquid of noble metal, corresponding soluble precious-metal salinity for solubility
Wei not chloroplatinic acid, gold chloride, silver nitrate, chlorine palladium acid, ruthenium hydrochloride ammonium or chloro-iridic acid；According to solid content (TiO2With mixing for noble metal
Compound) and water and ethanol 10：600：400 mass ratio adds water and ethanol, forms the suspension containing 10% solid content, fully super
After sound disperses, it is passed through in spray dryer, the flow velocity for keeping suspension is 10-1000ml/h, and drier drying temperature sets model
Enclose for 100-180 DEG C, avoid metal precursor crystal growth, collection obtains powdered solid predecessor.
2) powdered solid predecessor is placed in Muffle furnace, 400 DEG C is warming up to 5 DEG C/min, in the hydrogen of hydrogen 5%
2h is calcined in argon gas gaseous mixture,.Calcining promotes the precious metal ion original position forming core of these high degree of dispersion and to form super-small expensive
Metal nanoparticle is carried on oxide surface, you can obtains the new TiO that high uniformity disperses, particle diameter is minimum2- M (M=Pt,
Au, Ag, Pd, Ru, Ir) photocatalyst material, the product after calcining is TiO2- M photocatalyst materials.
Specific embodiment is given below to further illustrate the present invention.
Embodiment 1：
First, the TiO of 200g is weighed2Insert in beaker, then add HAuCl thereto4Solution, the noble metal added
Contained noble metal (Au) and TiO in precursor liquid2Mass ratio be 1：100.According to solid content (TiO2With the mixture of noble metal) with
Water and ethanol 10：600：400 mass ratio adds water and ethanol, forms the suspension containing 10% solid content, abundant ultrasonic disperse
Afterwards, it is passed through in spray dryer, the flow velocity for keeping suspension is 100ml/h, and drier drying temperature setting range is 120 DEG C,
Quick break drying is carried out, collects powdered solid content predecessor.Then, gained solid predecessor is inserted in Muffle furnace, with 5
DEG C/min be warming up to 400 DEG C calcining 2h, in the hydrogen-argon-mixed middle calcining 2h of hydrogen 5%, the product after calcining is TiO2-
Au photocatalyst materials.
Fig. 1 is business TiO2(P25) transmission electron microscope picture, it can be seen that the particle diameter of its single nanoparticle is about left in 25nm
The right side, the smooth non-loaded particle in surface.Fig. 2 is the transmission electron microscope picture using the P25 after present invention load 1%Au, it can be seen that Au
Nano particle (average grain diameter about 0.9nm) is equably carried on P25 surfaces.
Embodiment 2：
First, the TiO of 200g is weighed2Insert in beaker, then add H thereto2IrCl6Solution, the noble metal added
Contained noble metal (Ir) and TiO in precursor liquid2Mass ratio be 1：500.According to solid content (TiO2With the mixture of noble metal) with
Water and ethanol 10：600：400 mass ratio adds water and ethanol, forms the suspension containing 10% solid content, abundant ultrasonic disperse
Afterwards, it is passed through in spray dryer, the flow velocity for keeping suspension is 200ml/h, and drier drying temperature setting range is 140 DEG C,
Quick break drying is carried out, collects powdered solid content predecessor.Then, gained solid predecessor is inserted in Muffle furnace, with 5
DEG C/min be warming up to 400 DEG C calcining 2h, in the hydrogen-argon-mixed middle calcining 2h of hydrogen 5%, the product after calcining is TiO2-
Ir photocatalyst materials.
Fig. 3 is the transmission electron microscope picture using the P25 after load factor 0.2%Ir of the present invention, it can be seen that Ir nano particles
(average grain diameter about 0.5nm) is equably carried on P25 surfaces.
Embodiment 3：
First, the TiO of 200g is weighed2Insert in ball grinder, chlorine palladium acid solution, your gold added then added thereto
Belong to contained noble metal (Pd) and TiO in precursor liquid2Mass ratio be 1：10.According to solid content (TiO2With the mixture of noble metal)
With water and ethanol 10：600：400 mass ratio adds water and ethanol, forms the suspension containing 10% solid content, fully ultrasound point
After dissipating, it is passed through in spray dryer, the flow velocity for keeping suspension is 500ml/h, and drier drying temperature setting range is 150
DEG C, quick break drying is carried out, collects powdered solid content predecessor.Then, gained solid predecessor is inserted in Muffle furnace,
400 DEG C of calcining 2h are warming up to 5 DEG C/min, in the hydrogen-argon-mixed middle calcining 2h of hydrogen 5%, the product after calcining is
TiO2- Pd photocatalyst materials.
Fig. 4 is the transmission electron microscope picture using the P25 after present invention load 5%Pd, it can be seen that Pd nano particles (average grain
Footpath about 1nm) equably it is carried on P25 surfaces.
Embodiment 4：
First, the TiO of 200g is weighed2Insert in ball grinder, then add H thereto2PtCl6Solution, your gold added
Belong to contained noble metal (Pt) and TiO in precursor liquid2Mass ratio be 1：200.According to solid content (TiO2With the mixture of noble metal)
With water and ethanol 10：600：400 mass ratio adds water and ethanol, forms the suspension containing 10% solid content, fully ultrasound point
After dissipating, it is passed through in spray dryer, the flow velocity for keeping suspension is 800ml/h, and drier drying temperature setting range is 180
DEG C, quick break drying is carried out, collects powdered solid content predecessor.Then, gained solid predecessor is inserted in Muffle furnace,
400 DEG C of calcining 2h are warming up to 5 DEG C/min, in the hydrogen-argon-mixed middle calcining 2h of hydrogen 5%, the product after calcining is
TiO2- Pt photocatalyst materials.
Fig. 5 is the transmission electron microscope picture using the P25 after present invention load 0.5%Pt, it can be seen that Pt nano particles are (average
Particle diameter about 0.3nm) equably it is carried on P25 surfaces.
Embodiment 5：
First, the TiO of 200g is weighed2Insert in ball grinder, then add ruthenium hydrochloride ammonia solution thereto, what is added is expensive
Contained noble metal (Ru) and TiO in metal front liquid2Mass ratio be 1：1000, according to solid content (TiO2With the mixing of noble metal
Thing) and water and ethanol 10：600：400 mass ratio adds water and ethanol, forms the suspension containing 10% solid content, fully ultrasound
After scattered, it is passed through in spray dryer, the flow velocity for keeping suspension is 400ml/h, and drier drying temperature setting range is 140
DEG C, quick break drying is carried out, collects powdered solid content predecessor.Then, gained solid predecessor is inserted in Muffle furnace,
400 DEG C of calcining 2h are warming up to 5 DEG C/min, 2h is calcined in the hydrogen argon gas gaseous mixture of hydrogen 5%.Then, by gained solid-state
Predecessor is inserted in Muffle furnace, 400 DEG C of calcining 2h is warming up to 5 DEG C/min, in the hydrogen-argon-mixed middle calcining 2h of hydrogen 5%
Product after calcining is TiO2- Ru photocatalyst materials.
Fig. 6 is the transmission electron microscope picture using the P25 after present invention load 0.1%Ru, it can be seen that Ru nano particles are (average
Particle diameter 0.9nm) equably it is carried on P25 surfaces.
Embodiment 6：
First, the TiO of 200g is weighed2Insert in ball grinder, then add H thereto2PtCl6Solution and HAuCl4Solution,
Contained noble metal (Pt, Au) and TiO in the noble metal precursor liquid added2Mass ratio be 1：100.According to solid content (TiO2With
The mixture of noble metal) and water and ethanol 10：600：400 mass ratio adds water and ethanol, is formed outstanding containing 10% solid content
Turbid, after abundant ultrasonic disperse, is passed through in spray dryer, and the flow velocity for keeping suspension is 1000ml/h, drier drying temperature
It is 170 DEG C to spend setting range, carries out quick break drying, collects powdered solid content predecessor.Then, by gained solid forerunner
Thing is inserted in Muffle furnace, is warming up to 400 DEG C of calcining 2h with 5 DEG C/min, in the hydrogen-argon-mixed middle calcining 2h of hydrogen 5%, is forged
Product after burning is TiO2- Pt-Au photocatalyst materials.
Fig. 7 is the transmission electron microscope picture using the P25 after present invention load 0.5%Pt and 0.5%Au, it can be seen that Pt-Au
Nano particle (average grain diameter 0.6nm) is equably carried on P25 surfaces.
The invention is not limited in above-described embodiment, on the basis of technical solution disclosed by the invention, the skill of this area
Art personnel are according to disclosed technology contents, it is not necessary to which performing creative labour can make one to some of which technical characteristic
A little to replace and deform, these are replaced and deformation is within the scope of the present invention.
Claims (9)
1. the preparation method of the air purification photocatalyst of titanium dioxide surface load super-small noble metal, it is characterised in that bag
Include following step：
1) first will be according to TiO2Mass ratio with noble metal is 1：10-1:1000, by TiO2Powder is mixed with noble metal precursor liquid
Close, then into the mixed liquor according to solid content TiO2With noble metal gross mass and water and ethanol 10：600：400 mass ratio adds
Enter water and ethanol, form suspension；Subsequent abundant ultrasonic disperse, and high temperature quick break is dried, collection obtains powdered solid
Predecessor；
2) the solid predecessor is placed in Muffle furnace, is heated up with certain speed, calcined in gaseous mixture reducing atmosphere, calcined
Product afterwards is TiO2- M photocatalyst materials.
2. the preparation of the air purification photocatalyst of titanium dioxide surface load super-small noble metal according to claim 1
Method, it is characterised in that contained noble metal is one kind in Pt, Au, Ag, Pd, Ru or Ir in the noble metal precursor liquid.
3. the preparation of the air purification photocatalyst of titanium dioxide surface load super-small noble metal according to claim 2
Method, it is characterised in that the noble metal precursor liquid is the salting liquid of soluble correspondence noble metal, corresponding your gold of solubility
It is respectively chloroplatinic acid, gold chloride, silver nitrate, chlorine palladium acid, ruthenium hydrochloride ammonium or chloro-iridic acid to belong to salt.
4. the preparation of the air purification photocatalyst of titanium dioxide surface load super-small noble metal according to claim 3
Method, it is characterised in that the concentration of salt solution of the noble metal is 50-100mM.
5. the preparation of the air purification photocatalyst of titanium dioxide surface load super-small noble metal according to claim 1
Method, it is characterised in that in the step 1), the suspension formed contains solid content for 10%.
6. the preparation of the air purification photocatalyst of titanium dioxide surface load super-small noble metal according to claim 1
Method, it is characterised in that in the step 1), the flow velocity for being passed through suspension in spray dryer is 10-1000ml/h.
7. the preparation of the air purification photocatalyst of titanium dioxide surface load super-small noble metal according to claim 1
Method, it is characterised in that in the step 1), dryer temperature setting range is 100 DEG C -180 DEG C.
8. the preparation of the air purification photocatalyst of titanium dioxide surface load super-small noble metal according to claim 1
Method, it is characterised in that in the step 2), reducing atmosphere is the hydrogen argon gas gaseous mixture of hydrogen 5%.
9. the preparation of the air purification photocatalyst of titanium dioxide surface load super-small noble metal according to claim 1
Method, it is characterised in that in the step 2), solid precursors are warming up to 400 DEG C in Muffle furnace with 5 DEG C/min, during calcining
Between 2h.