CN107915428A - The manufacture method of afforestation brick - Google Patents
The manufacture method of afforestation brick Download PDFInfo
- Publication number
- CN107915428A CN107915428A CN201711288048.7A CN201711288048A CN107915428A CN 107915428 A CN107915428 A CN 107915428A CN 201711288048 A CN201711288048 A CN 201711288048A CN 107915428 A CN107915428 A CN 107915428A
- Authority
- CN
- China
- Prior art keywords
- adobe
- fixture
- manufacture method
- parts
- afforestation brick
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of manufacture method of afforestation brick, it is related to construction material manufacture technology field, comprises the following steps：It is raw material to choose construction waste, cinder, red mud, pitch, water, and construction waste, cinder, red mud first are mixed to crush by production method obtains particle；Particle is added into water wheels and grinds stirring, is then heated, then put into pitch and be mixed to obtain slurry；Slurry is put into compacting in stock mould and obtains adobe；By being fixed in fixture for adobe, the fixture is in 60~80 degree of angles in horizontal line, is then then rotated between the fixture up time vertically in adobe flank hole using drilling machine, obtains semi-finished product to each flank hole of adobe successively；By semi-finished product be sent into drying chamber 24~36 it is small when up to afforestation brick.The present invention solves the problems, such as that ponding splashing situation occurs in existing afforestation brick.
Description
Technical field
The present invention relates to construction material manufacture technology field, especially a kind of manufacture method of afforestation brick.
Background technology
With social progress and improvement of living standard, people not only need abundant living material, with greater need for air
Pure and fresh, green circular comfortable graceful living environment.Particularly in the life of urbanite, how to afforest valuable and limited
Space, then be the problem of people are concerned about, pay attention to the most the most.In addition to being afforested to dedicated land use for greening, people also cause
Power is afforested in the large area public place such as open parking ground, square.The afforestation brick used at present in gardens is all
Arrangement is laid on green land, is not cohered mutually with cement or other materials between brick and brick, can existed between brick and brick
Gap, gap of the rainy day rainwater between brick and brick enter and hoard between brick body and green land, the situation of ponding occur, and
When pedestrian way is out-of-date, makes clothing dirty by trampling that the ponding of the inside can be sputtered, many puzzlements are brought to pedestrian.
The content of the invention
Problem solved by the invention is to provide a kind of manufacture method of afforestation brick, the garden made of this method
Woods brick for afforesting can solve the problems, such as that ponding splashing situation occurs in existing afforestation brick.
To solve the above-mentioned problems, the technical solution adopted by the present invention is：This afforestation brick, including following weight
The raw material of number：30~40 parts of construction waste, 10~15 parts of cinder, 10~15 parts of red mud, 10~15 parts of pitch, water 50~60
Part；
Above-mentioned afforestation brick, its manufacture method comprise the following steps：
1）Construction waste, cinder, red mud are mixed to crush and obtain particle；
2）By step 1）The particle of gained adds water wheels and grinds stirring, then heats, then put into pitch and be mixed to obtain slurry；
3）By step 2）The slurry of gained is put into compacting in stock mould and obtains adobe；
4）By step 3）The adobe of gained is fixed in fixture, and the fixture is in 60~80 degree of angles in horizontal line, is then made
With drilling machine vertically in adobe flank hole, then rotated between the fixture up time, give adobe each flank hole successively
Obtain semi-finished product；
5）By step 4）Up to afforestation brick when the semi-finished product feeding drying chamber 24~36 of gained is small.
In above-mentioned technical proposal, more specifically technical solution can also be：：The step 2）Middle heating-up temperature for 90~
100℃。
Further：The step 3）The water content of middle adobe is 25~30%, and size is：Long 20cm, wide 20cm are high
8cm。
Further：The step 4）A diameter of 1cm of middle drilling, the depth of drilling is 12cm.
By adopting the above-described technical solution, the present invention has the advantages that compared with prior art：
By being punched in four sides of adobe, for the ponding of brick body side when being trampled splashing, ponding is from the hole of brick body side
Into then being discharged from the holes of other sides, play the role of preventing ponding from splashing；Keep adobe have 25%~30% it is aqueous
Amount, in boring procedure, adobe is not in cracking；Fixture tilts 60~80 degree of angles and gives adobe flank hole, the hole drilled out
Groove has certain angle, and the diversion of afforestation brick and drainage effect are more preferable.
Embodiment
With reference to example, the invention will be further described：
Embodiment one：
The raw material of this afforestation brick of this example is as follows：Construction waste 30kg, cinder 10kg, red mud 10kg, pitch
10kg, water 50kg；
Manufacture method is as follows：
1）Construction waste, cinder, red mud are mixed to crush and obtain particle；
2）By step 1）The particle of gained adds water wheels and grinds stirring, then heats, and temperature is 90 DEG C, then puts into pitch mixing
Obtain slurry；
3）By step 2）The slurry of gained is put into compacting in stock mould and obtains adobe, and the water content of adobe is 25%, and size is：It is long
20cm, wide 20cm, high 8cm；
4）By step 3）The adobe of gained is fixed in fixture, and the fixture is in 60 degree of angles in horizontal line, then using brill
Hole machine is vertically in adobe flank hole, and a diameter of 1cm of drilling, the depth of drilling is 12cm, and then the fixture is suitable
Time rotates, and obtains semi-finished product to each flank hole of adobe successively；
5）By step 4）Up to afforestation brick when the semi-finished product feeding drying chamber 24 of gained is small.
Embodiment two：
The raw material of this afforestation brick of this example is as follows：Construction waste 40kg, cinder 15kg, red mud 15kg, pitch
15kg, water 60kg；
Manufacture method is as follows：
1）Construction waste, cinder, red mud are mixed to crush and obtain particle；
2）By step 1）The particle of gained adds water wheels and grinds stirring, then heats, and temperature is 100 DEG C, then puts into pitch mixing and stir
Mix to obtain slurry；
3）By step 2）The slurry of gained is put into compacting in stock mould and obtains adobe, and the water content of adobe is 30%, and size is：It is long
20cm, wide 20cm, high 8cm；
4）By step 3）The adobe of gained is fixed in fixture, and the fixture is in 80 degree of angles in horizontal line, then using brill
Hole machine is vertically in adobe flank hole, and a diameter of 1cm of drilling, the depth of drilling is 12cm, and then the fixture is suitable
Time rotates, and obtains semi-finished product to each flank hole of adobe successively；
5）By step 4）Up to afforestation brick when the semi-finished product feeding drying chamber 36 of gained is small.
Claims (4)
- A kind of 1. manufacture method of afforestation brick, it is characterised in that：Using the raw material of following parts by weight：30~40 parts of construction waste, 10~15 parts of cinder, 10~15 parts of red mud, 10~15 parts of pitch, 50~60 parts of water；Its production method comprises the following steps：1）Construction waste, cinder, red mud are mixed to crush and obtain particle；2）By step 1）The particle of gained adds water wheels and grinds stirring, then heats, then put into pitch and be mixed to obtain slurry；3）By step 2）The slurry of gained is put into compacting in stock mould and obtains adobe；4）By step 3）The adobe of gained is fixed in fixture, and the fixture is in 60~80 degree of angles in horizontal line, is then made With drilling machine vertically in adobe flank hole, then rotated between the fixture up time, give adobe each flank hole successively Obtain semi-finished product；5）By step 4）Up to afforestation brick when the semi-finished product feeding drying chamber 24~36 of gained is small.
- 2. the manufacture method of afforestation brick according to claim 1, it is characterised in that：The step 2）Middle heating temperature Spend for 90~100 DEG C.
- 3. the manufacture method of afforestation brick according to claim 2, it is characterised in that：The step 3）Middle adobe Water content is 25~30%, and size is：Long 20cm, wide 20cm, high 8cm.
- 4. the manufacture method of afforestation brick according to claim 3, it is characterised in that：The step 4）Middle drilling A diameter of 1cm, the depth of drilling is 12cm.