CN107905010A - A kind of hawser of deep sea petroleum exploration - Google Patents
A kind of hawser of deep sea petroleum exploration Download PDFInfo
- Publication number
- CN107905010A CN107905010A CN201711201453.0A CN201711201453A CN107905010A CN 107905010 A CN107905010 A CN 107905010A CN 201711201453 A CN201711201453 A CN 201711201453A CN 107905010 A CN107905010 A CN 107905010A
- Authority
- CN
- China
- Prior art keywords
- layer
- deep sea
- wire rope
- hawser
- rope core
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of hawser of deep sea petroleum exploration, it is related to a kind of hawser, waterproof oxidation prevention layer, the sandwich construction such as core fiber layer and external coating is set outside wire rope core to solve the prior art, weight of the deep sea cable in use state itself is increased, is caused inconvenient for use;It includes wire rope core and clad, the wire rope core is formed by multiply rope strand coil buckling, the clad passes sequentially through right-handed screw coiling mode by 96 polyamide multifilament fibrous material tapes and backpitch coiling mode laminated is wrapped on the wire rope core, anti- particulate layer is coated with the outside of the clad, the anti-particulate layer is made of polyvinylidene fluoride layer and modified polypropene layer.By implementing the technical program, to realize the weight for mitigating deep sea cable in use state itself, and there is good corrosion resistance and abrasion resistance properties.
Description
Technical field
The present invention relates to a kind of hawser, more particularly to a kind of hawser of deep sea petroleum exploration.
Background technology
Existing deep sea cable is made of wire rope core and wrap, wherein, wire rope core be by multiply cordage twisting or braiding and
Into wrap is the tube-in-tube structure formed by the braiding of multiply cordage, and wrap is set on wire rope core and wraps wire rope core.
Hole is woven during use, on the coated set of grit in seabed and seawater to enter between wrap and wire rope core, or even into
Enter to inside wire rope core.In this way, when using the deep sea cable, into deep sea cable grit respectively with forming wire rope core and wrap
Cordage phase mutual friction, the cordage for causing to form wire rope core and wrap is worn or even rubs, and then causes wire rope core and bag
Sheathing is damaged, substantially reduces the service life of deep-sea cable.
In the prior art, the patent of Application No. CN201611041861.X discloses a kind of high-strength corrosion-resisting deep-sea cable
Rope, including rope body, external coating and wire rope core, the rope body inside center are equipped with wire rope core, the wire rope core by some rope strand coil bucklings and
Into the wire rope core outside is coated with waterproof oxidation prevention layer, and core fiber layer, the core fiber layer are coated with the outside of the waterproof oxidation prevention layer
Formed for high-strength high-modulus fibre material twisted, external coating is coated with the outside of the core fiber layer, the external coating is in brocade
Synthetic fibre multifilament fiber material, the external coating surface are equipped with coating, and the coating is anti-particulate layer.The technical solution solves biography
The problem of system hawser is caused hawser intensity decreases, is caused security risk using middle abrasion.But the technical solution still have with
Lower shortcoming:The 1st, waterproof oxidation prevention layer is set outside wire rope core, the sandwich construction such as core fiber layer and external coating, increases deep-sea
Hawser causes inconvenient for use in the weight of use state itself.2nd, waterproof oxidation prevention layer, core fiber layer and external coating and sandwich layer bag
Process is covered to consider its corrosion resistance and abrasion resistance properties, manufactures processed complex.
The content of the invention
In view of the above deficiencies of the prior art, it is an object of the invention to provide a kind of cable of deep sea petroleum exploration
Rope, to realize the weight for mitigating deep sea cable in use state itself, and has good corrosion resistance and abrasion resistance properties.
The present invention specifically uses following technical scheme to achieve these goals:
A kind of hawser of deep sea petroleum exploration, including wire rope core and clad, the wire rope core are formed by multiply rope strand coil buckling,
The clad passes sequentially through right-handed screw coiling mode and backpitch coiling mode by 96 polyamide multifilament fibrous material tapes
Laminated is wrapped on the wire rope core, is coated with anti-particulate layer on the outside of the clad, the anti-particulate layer is by polyvinylidene fluoride layer
Formed with modified polypropene layer.
The operation principle of base case of the present invention is:When using the deep sea cable, gravel in seabed or seawater because
The wire rope core and clad of braiding are externally provided with anti-particulate layer and directly can not directly be contacted with wire rope core, can avoid wire rope core because with gravel phase
Mutual friction produces damage because of the immersion corrosion of inorganic salts in seawater, extends the service life of deep sea cable;And anti-particulate layer
It is made of polyvinylidene fluoride layer and modified polypropene layer, polyvinylidene fluoride layer and modified polypropene layer have good chemically-resistant corruption
Corrosion, excellent impact resistance intensity, oxidative resistance and hydrophobicity, therefore play a big part to the permeability resistance of film,
It is adapted to use on the more severe hawser of deep-sea etching condition, avoids biology, bacterium or inorganic salts in deep-sea to deep sea cable
Corrosion, and sandwich construction safeguard structure need not be set to can reach waterproof effect, mitigate deep sea cable in use state itself
Weight and the overall weight in use state deep sea cable, it is easy to use;Further, the clad on the outside of wire rope core is by nine
16 polyamide multifilament fibrous material tapes pass sequentially through right-handed screw coiling mode and backpitch coiling mode laminated is wrapped in wire rope core
On, the tight ness rating that polyamide multifilament fibrous material tapes are wrapped on wire rope core can be increased, the polyamide multifilament fibrous material used is from whole
The abrasion resistance properties of hawser are improved on body, increase the stress intensity of deep sea cable, extend the service life of deep sea cable.
Further, the wire rope core is formed by 3 strands, 6 strands, 12 strands or 24 strand stock coil bucklings.The program is set on the outside of wire rope core
The anti-particulate layer put reduces the seawater amount of deep sea cable of being immersed in from source, and set on the outside of wire rope core by 96
The clad of polyamide multifilament fibrous material tapes winding has preferable structural strength, therefore wire rope core is without the rope of much complex
Stock is twisted into, and reduces manufacture cost.
Further, the wire rope core is made of superhigh molecular weight polyethylene fibers weaving.Superhigh molecular weight polyethylene fibers
Strength of materials high tenacity is good, and light weight, therefore can mitigate the weight of deep sea cable itself.
Further, the cable diameter is X, and as 80mm≤X≤100mm, the thickness of the anti-particulate layer is 2mm-
3mm;As 100 < X≤120mm, the thickness of the anti-particulate layer is 3.2mm-4.2mm.This programme avoids setting outside wire rope core
Put waterproof oxidation prevention layer, the sandwich construction such as core fiber layer and external coating, and the structure of wire rope core and clad is increasing hawser
Structural strength and wearability, therefore hawser is small and has preferable mechanical strength, is coated with by polyvinylidene fluoride layer and changes
Property polypropylene layer composition anti-particulate layer also compared with the prior art in the thinner thickness of anti-particulate layer can reach waterproof anti-corrosion
Effect, so as to mitigate the weight of deep sea cable itself on the whole.
Further, the width of polyamide multifilament fibrous material tapes is A in the clad, and 23cm≤A≤32cm.It is easy to
The clad of polyamide multifilament fibrous material tapes is wrapped on wire rope core, and 96 polyamide multifilament fibrous material tapes pass sequentially through
Right-handed screw coiling mode and backpitch coiling mode laminated are wrapped on wire rope core, have stronger wearability and tight ness rating, are extended
The service life of deep sea cable.
Further, the thickness of polyamide multifilament fibrous material tapes is B in the clad, and 3mm≤B≤5mm.Through application
People's many experiments can obtain, and the thickness of polyamide multifilament fibrous material tapes is arranged to 3mm-5mm, can effectively ensure that wearability and tight ness rating
While reduce deep sea cable manufacture cost.
Further, the anti-particulate layer is two layers of insulation system, and internal layer is polyvinylidene fluoride layer, and outer layer is modified poly- third
Alkene layer.Generation is avoided to be coated with blind spot so that deep sea cable has good corrosion resistance.
As described above, beneficial effects of the present invention are as follows:
1st, the present invention is externally provided with anti-particulate layer in the wire rope core and clad of braiding, can avoid wire rope core because with gravel phase mutual friction
Or damage is produced because of the immersion corrosion of inorganic salts in seawater, extend the service life of deep sea cable;And anti-particulate layer is by poly- inclined
Vinyl fluoride layer and modified polypropene layer composition, polyvinylidene fluoride layer and modified polypropene layer have good chemical resistance,
Excellent impact resistance intensity, oxidative resistance and hydrophobicity, therefore play a big part to the permeability resistance of film, it is adapted to deep
Used on the more severe hawser of extra large etching condition, avoid the corrosion of biology, bacterium or inorganic salts to deep sea cable in deep-sea, and
Sandwich construction safeguard structure need not be set to can reach waterproof effect, mitigate deep sea cable in the weight of use state itself and
Overall weight in use state deep sea cable.
2nd, the clad in the present invention on the outside of wire rope core passes sequentially through right-handed screw by 96 polyamide multifilament fibrous material tapes
Coiling mode and backpitch coiling mode laminated are wrapped on wire rope core, can be increased polyamide multifilament fibrous material tapes and are wrapped in wire rope core
On tight ness rating, the polyamide multifilament fibrous material used improves the abrasion resistance properties of hawser, increases deep sea cable on the whole
Stress intensity, extend the service life of deep sea cable.
3rd, wire rope core of the present invention only needs to be formed by 3 strands, 6 strands, 12 strands or 24 strand stock coil bucklings, can reach preferable structure
Intensity, reduces manufacture cost.
4th, cable diameter is X in the present invention, and as 80mm≤X≤100mm, the thickness of the anti-particulate layer is 2mm-3mm;
As 100 < X≤120mm, the thickness of the anti-particulate layer is 3.2mm-4.2mm;Polyamide multifilament fibrous material tapes in clad
Width be A, and 23cm≤A≤32cm;The thickness of polyamide multifilament fibrous material tapes is B in clad, and 3mm≤B≤5mm;
Hawser is small and has preferable mechanical strength, is coated with the anti-particulate layer being made of polyvinylidene fluoride layer and modified polypropene layer
Also compared with the prior art in the thinner thickness of anti-particulate layer can reach waterproof anti-corrosion effect, so as to mitigate deep-sea on the whole
The weight of hawser itself.
Brief description of the drawings
Fig. 1 is a kind of schematic diagram of the cable embodiments 1 of deep sea petroleum exploration of the present invention;
Fig. 2 is a kind of cross-sectional view of the cable embodiments 1 of deep sea petroleum exploration of the present invention;
Fig. 3 is a kind of schematic diagram of the cable embodiments 2 of deep sea petroleum exploration of the present invention.
Reference numeral:01- wire rope cores, 02- clads, 03- rope strands, 04- polyamide multifilaments fibrous material tapes, the anti-particulate layers of 05-,
06- polyvinylidene fluoride layers, 07- modified polypropene layers.
Embodiment
In order to which those skilled in the art are better understood from the present invention, below in conjunction with the accompanying drawings with following embodiments to the present invention
It is described in further detail.
Please refer to Fig.1 with shown in Fig. 2, the present embodiment provides a kind of hawser of deep sea petroleum exploration, a kind of deep-sea oil
The hawser of exploration, including wire rope core 01 and clad 02, wire rope core 01 are formed by 12 strand stock, 03 coil buckling, and clad 02 is by 90
Six polyamide multifilament fibrous material tapes 04 pass sequentially through right-handed screw coiling mode and backpitch coiling mode laminated is wrapped in wire rope core
On 01, the tight ness rating that polyamide multifilament fibrous material tapes 04 are wrapped on wire rope core 01 can be increased, the polyamide multifilament undulation degree used
Material improves the abrasion resistance properties of hawser on the whole, increases the stress intensity of deep sea cable, and extend deep sea cable uses the longevity
Life.
Further, the outside of clad 02 is coated with anti-particulate layer 05, and anti-particulate layer 05 is by polyvinylidene fluoride layer 06 and changes
Property polypropylene layer 07 form, when using the deep sea cable, gravel in seabed or seawater because braiding wire rope core 01 and coat
Layer 02 is externally provided with anti-particulate layer 05 and directly can not directly be contacted with wire rope core 01, can avoid wire rope core 01 because with the mutual friction of gravel phase or
Damage is produced because of the immersion corrosion of inorganic salts in seawater, extends the service life of deep sea cable;And anti-particulate layer 05 is by poly- inclined
Vinyl fluoride layer 06 and modified polypropene layer 07 form, and polyvinylidene fluoride layer 06 and modified polypropene layer 07 have good chemically-resistant
Corrosivity, excellent impact resistance intensity, oxidative resistance and hydrophobicity, therefore very big work is risen to the permeability resistance of film
With being adapted to use on the more severe hawser of deep-sea etching condition, avoid biology, bacterium or inorganic salts in deep-sea to deep sea cable
Corrosion, and sandwich construction safeguard structure need not be set to can reach waterproof effect, mitigate deep sea cable in use state itself
Weight and overall weight in use state deep sea cable;In addition, anti-particulate layer 05 is two layers of insulation system, internal layer is
Polyvinylidene fluoride layer 06, outer layer are modified polypropene layer 07, avoid generation from being coated with blind spot so that deep sea cable has well resistance to
Corrosivity.
Specifically, wire rope core 01 is made of superhigh molecular weight polyethylene fibers weaving, superhigh molecular weight polyethylene fibers material
Strength high toughness is good, and light weight, therefore can mitigate the weight of deep sea cable itself.
Further, cable diameter X, and X=120, the thickness of anti-particulate layer 05 is 4.2mm;This programme avoids restricting
The outside of core 01 setting waterproof oxidation prevention layer, core fiber layer and the grade sandwich construction of external coating 02, and the knot of wire rope core 01 and clad 02
Structure is increasing the structural strength of hawser and wearability;Therefore, the weight of deep sea cable itself is small and mechanical strength high abrasion
Property is good;The width of polyamide multifilament fibrous material tapes 04 is A in clad 02, and A=32cm;Easy to by polyamide multifilament fibrous material
It is wrapped in 04 clad 02 on wire rope core 01, and 96 polyamide multifilament fibrous material tapes 04 pass sequentially through right-handed screw coiling
Mode and backpitch coiling mode laminated are wrapped on wire rope core 01, are had stronger wearability and tight ness rating, are extended deep-sea cable
The service life of rope;The thickness of polyamide multifilament fibrous material tapes 04 is B in clad 02, and B=5mm.It is repeatedly real through applicant
Testing to obtain, and the thickness of polyamide multifilament fibrous material tapes 04 is arranged to 5mm, reduced while can effectively ensure that wearability and tight ness rating
The manufacture cost of deep sea cable.
In this example, when using the deep sea cable, the gravel in seabed or seawater is because of the wire rope core 01 and clad in braiding
02 is externally provided with anti-particulate layer 05 and directly can not directly be contacted with wire rope core 01, can avoid wire rope core 01 because with the mutual friction of gravel phase or because
The immersion of inorganic salts corrodes and produces damage in seawater, extends the service life of deep sea cable;And anti-particulate layer 05 is by gathering inclined fluorine
Pvdf layer 06 and modified polypropene layer 07 form, and avoid the corrosion of biology, bacterium or inorganic salts to deep sea cable in deep-sea, and
Sandwich construction safeguard structure need not be set to can reach waterproof effect, mitigate deep sea cable in the weight of use state itself and
Overall weight in use state deep sea cable, and the structure of wire rope core 01 and clad 02 is strong to increase the structure of hawser
Degree and wearability so that deep sea cable mechanical strength high-wearing feature is good, can extend the service life of deep sea cable.
Embodiment 2
Embodiment 2 is substantially the same manner as Example 1, its difference is:As shown in figure 3, cable diameter is X, and X=
80, the thickness of anti-particulate layer 05 is 2mm;Therefore hawser is small and has preferable mechanical strength, is coated with by Kynoar
Layer 06 and modified polypropene layer 07 form anti-particulate layer 05 also compared with the prior art in anti-particulate layer 05 thinner thickness
Reach waterproof anti-corrosion effect;And the width of polyamide multifilament fibrous material tapes 04 is A in clad 02, and A=23cm;Clad
The thickness of polyamide multifilament fibrous material tapes 04 is B in 02, and B=3mm, can be obtained through applicant's many experiments, polyamide multifilament fiber
The thickness of material strips 04 is arranged to 3mm, and the manufacture cost of deep sea cable is reduced while can effectively ensure that wearability and tight ness rating,
Practicality is good.
The above, is only presently preferred embodiments of the present invention, is not intended to limit the invention, patent protection model of the invention
Enclose and be subject to claims, the equivalent structure change that every specification and accompanying drawing content with the present invention is made, similarly
It should include within the scope of the present invention.
Claims (7)
1. a kind of hawser of deep sea petroleum exploration, including wire rope core and clad, it is characterised in that:The wire rope core is by multiply rope strand
Coil buckling forms, and the clad passes sequentially through right-handed screw coiling mode and backpitch by 96 polyamide multifilament fibrous material tapes
Coiling mode laminated is wrapped on the wire rope core, anti-particulate layer is coated with the outside of the clad, the anti-particulate layer is by poly- inclined
Vinyl fluoride layer and modified polypropene layer composition.
A kind of 2. hawser of deep sea petroleum exploration according to claim 1, it is characterised in that:The wire rope core by 3 strands, 6
Stock, 12 strands or 24 strand stock coil bucklings form.
A kind of 3. hawser of deep sea petroleum exploration according to claim 1, it is characterised in that:The wire rope core is by superelevation point
Sub- weight polyethylene fiber weaving is made.
A kind of 4. hawser of deep sea petroleum exploration according to claim 1, it is characterised in that:The cable diameter is X,
As 80mm≤X≤100mm, the thickness of the anti-particulate layer is 2mm-3mm;As 100 < X≤120mm, the anti-particulate layer
Thickness be 3.2mm-4.2mm.
A kind of 5. hawser of deep sea petroleum exploration according to claim 1, it is characterised in that:Polyamide fibre in the clad
The width of multifilament fiber material strips is A, and 23cm≤A≤32cm.
A kind of 6. hawser of deep sea petroleum exploration according to claim 1, it is characterised in that:Polyamide fibre in the clad
The thickness of multifilament fiber material strips is B, and 3mm≤B≤5mm.
A kind of 7. hawser of deep sea petroleum exploration according to claim 1-6 any one, it is characterised in that:It is described anti-
Particulate layer is two layers of insulation system, and internal layer is polyvinylidene fluoride layer, and outer layer is modified polypropene layer.