CN107880298A - A kind of BOPET matte releases film - Google Patents
A kind of BOPET matte releases film Download PDFInfo
- Publication number
- CN107880298A CN107880298A CN201711146903.0A CN201711146903A CN107880298A CN 107880298 A CN107880298 A CN 107880298A CN 201711146903 A CN201711146903 A CN 201711146903A CN 107880298 A CN107880298 A CN 107880298A
- Authority
- CN
- China
- Prior art keywords
- parts
- matte
- bopet
- agent
- mixed
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of BOPET matte releases film, including polyester base material and the release layer that is laminated on the side surface of polyester base material one, have the feature that, release layer is formed by curing by release layer coating solution, and release layer coating fluid includes following raw material:2.0 3.3 parts of fluorine resin, 3.0 5.3 parts of polyester polyol resin, 0.5 1.7 parts of aldehyde ketone resin, 1.5 3.0 parts of curing agent, 0.2 0.6 parts of auxiliary agent, 2.1 3.5 parts of delustering agent, 12.0 18.5 parts of mixed solvent, mixed solvent is by benzene, ethylene glycol, 2 heptanone, cyclohexanone by volume 1:0.7:1.5:0.5 is mixed to form, and auxiliary agent is mixed to form by dispersant and antistatic agent;Curing agent is mixed to form by amino resins and closure isocyanates.Matte release film provided by the invention has preferable stripping performance.
Description
Technical field
The present invention relates to a kind of mould release membrance, more particularly to a kind of BOPET matte releases film.
Background technology
Mould release membrance is also known as stripping film, barrier film etc., refers to that surface has the film of separation property, mould release membrance and specific material
Do not have sticky or slight viscosity after contacting under the limited conditions.The product of mould release membrance in the market is usually with PET strip at present
Base is base material, and it is main body that surface, which is coated with parting agent layer, and coating thereafter is shielded, and is torn it during use.
It is extensive with the market application but in the market applies the 95% of material using organosilicon coating at present, it is organic
Silicon does not apply to still in certain fields, such as in the typically inapplicable material containing organosilicon of electronic circuit process industry etc.
Material, because the remaining organosilicon bonded can influence the normal of its electronic circuit what following process or application time connect when peeling off
Use.
So have to use a kind of separated type material of non-organic silicon class in electronics industry.
Chinese patent CN103917347 proposes the mode using ethylene-tetrafluoroethylene copolymer material extrusion drawing and forming
Form fluorine-containing release membrane material so that film has release performance in itself.This membrane material can make directly as separated type material
With without being coated with release layer on film surface, there is the characteristics such as remaining adhesion rate is high, peeling force is low, surface brightness is high.But its table
Face tension force is too low, and peeling force is too small, and its recoatability has very big problem.
Chinese patent CN103923334 propose using silicon dioxide gel, add acrylate monomer, fluorochemical monomer,
Silicon-containing monomer, progress is free-radical polymerized to obtain fluorine silicon mould release, then coordinates with Isocyanates curing agent, is coated on organic substrate
On, obtain fluorine silicon mould release membrance by heat cure.This release product has higher hydrophobic, relatively low peeling force, higher remnants
The advantages that adhesion rate.Its surface is bright smooth, while wherein contains organosilicon material, is unfavorable for making in electronics industry
With.
The content of the invention
For above mentioned problem existing for existing mould release membrance, now provide a kind of combination property preferable BOPET matte releases
Film.
Concrete technical scheme is as follows:
A kind of BOPET matte releases film, including polyester base material and the release layer that is laminated on the side surface of polyester base material one, tool
There is such feature, release layer is formed by curing by release layer coating solution, and release layer coating fluid includes following raw material:
Fluorine resin 2.0-3.3 parts, polyester polyol resin 3.0-5.3 parts, aldehyde ketone resin 0.5-1.7 parts, curing agent 1.5-3.0 parts,
Auxiliary agent 0.2-0.6 parts, delustering agent 2.1-3.5 parts, mixed solvent 12.0-18.5 parts, mixed solvent by benzene, ethylene glycol, 2-HEPTANONE,
Cyclohexanone by volume 1:0.7:1.5:0.5 is mixed to form, and auxiliary agent is mixed to form by dispersant and antistatic agent;Curing agent is by ammonia
Base resin and closure isocyanates are mixed to form.
Above-mentioned BOPET matte release films, also have the feature that, fluorine resin is trifluoro-ethylene-hexafluoropropene
Bipolymer, the hydroxyl value of fluorine resin are 21-35mgKOH/g, acid number 4.5-12.7mgKOH/g, and number-average molecular weight is
13000-27000。
Above-mentioned BOPET matte release films, also have the feature that, polyester polyol resin be chloro phthalic acid-
The bipolymer of trimethylolpropane, the hydroxyl value of polyester polyol resin is 50-150mgKOH/g, acid number 0-50mgKOH/
G, number-average molecular weight 5000-13000.
Above-mentioned BOPET matte release films, also have the feature that, the hydroxyl value of aldehyde ketone resin is 40-140mgKOH/g.
Above-mentioned BOPET matte release films, also have the feature that, amino resins is methyl-etherified melamino-formaldehyde tree
Fat.
Above-mentioned BOPET matte release films, also have the feature that, closure isocyanates is closure three-functionality-degree
Isocyanates.
Above-mentioned BOPET matte release films, also have the feature that, delustering agent is by aerosil and titanium dioxide
In mass ratio 2:1-3:1 is mixed to form.
Above-mentioned BOPET matte release films, also have the feature that, the mass ratio of dispersant and antistatic agent is 1-
3:2-3。
The beneficial effect of such scheme is:
In matte release film provided by the invention, by using the combination of fluorine resin, PEPA and aldehyde ketone resin,
The release layer for making to obtain has preferable stripping performance, the complete transfer of coating after guarantee;Meanwhile dumb light provided by the invention from
Type film tension and hardness are moderate, can meet the needs of actual use.
Embodiment
Below in conjunction with the embodiment of the present invention, the technical scheme in the embodiment of the present invention is clearly and completely described,
Obviously, described embodiment is only part of the embodiment of the present invention, rather than whole embodiments.Based in the present invention
Embodiment, the every other embodiment that those of ordinary skill in the art are obtained on the premise of creative work is not made,
Belong to the scope of protection of the invention.
It should be noted that in the case where not conflicting, the feature in embodiment and embodiment in the present invention can phase
Mutually combination.
With reference to specific embodiment, the invention will be further described, but not as limiting to the invention.
Embodiment 1
A kind of BOPET matte releases film, including polyester base material and the release layer that is laminated on the side surface of polyester base material one, from
Type layer is formed by curing by release layer coating solution, and release layer coating fluid includes following raw material:2.2 parts of fluorine resin,
3.5 parts of PEPA, 0.7 part of aldehyde ketone resin, 2.5 parts of curing agent, 0.4 part of auxiliary agent, 2.7 parts of delustering agent, mixed solvent 15.0
Part, mixed solvent is by benzene, ethylene glycol, 2-HEPTANONE, cyclohexanone by volume 1:0.7:1.5:0.5 is mixed to form, and auxiliary agent is scattered
Agent and the combination of antistatic agent;Curing agent is amino resins and closure isocyanates mixed system;
Wherein, fluorine resin is the bipolymer of trifluoro-ethylene-hexafluoropropene, and the hydroxyl value of fluorine resin is 27mgKOH/
G, acid number 8.4mgKOH/g, number-average molecular weight 17000;Polyester polyol resin is chloro phthalic acid-trihydroxy methyl third
The bipolymer of alkane, the hydroxyl value of polyester polyol resin are 70mgKOH/g, acid number 20mgKOH/g, and number-average molecular weight is
7000;The hydroxyl value of aldehyde ketone resin is 80mgKOH/g;Amino resins is methyl-etherified melamine resin;Closure isocyanic acid
Ester is closure three-functionality-degree isocyanates;Delustering agent is by aerosil and titanium dioxide in mass ratio 2.5:1 compounding shape
Into;Auxiliary agent is by dispersant and antistatic agent in mass ratio 2:1 compounding is formed.
Embodiment 2
A kind of BOPET matte releases film, including polyester base material and the release layer that is laminated on the side surface of polyester base material one, from
Type layer is formed by curing by release layer coating solution, and release layer coating fluid includes following raw material:2.7 parts of fluorine resin,
4.0 parts of PEPA, 1.2 parts of aldehyde ketone resin, 1.9 parts of curing agent, 0.35 part of auxiliary agent, 3.1 parts of delustering agent, mixed solvent 15.0
Part, mixed solvent is by benzene, ethylene glycol, 2-HEPTANONE, cyclohexanone by volume 1:0.7:1.5:0.5 is mixed to form, and auxiliary agent is scattered
Agent and the combination of antistatic agent;Curing agent is amino resins and closure isocyanates mixed system;
Wherein, fluorine resin is the bipolymer of trifluoro-ethylene-hexafluoropropene, and the hydroxyl value of fluorine resin is 33mgKOH/
G, acid number 8.5mgKOH/g, number-average molecular weight 15000;Polyester polyol resin is chloro phthalic acid-trihydroxy methyl third
The bipolymer of alkane, the hydroxyl value of polyester polyol resin are 110mgKOH/g, acid number 40mgKOH/g, and number-average molecular weight is
85000;The hydroxyl value of aldehyde ketone resin is 130mgKOH/g;Amino resins is methyl-etherified melamine resin;Closure isocyanide
Acid esters is closure three-functionality-degree isocyanates;Delustering agent is by aerosil and titanium dioxide in mass ratio 2.5:1 is multiple
With formation;Auxiliary agent is by dispersant and antistatic agent in mass ratio 1.5:2.5 compoundings are formed.
Embodiment 3
A kind of BOPET matte releases film, including polyester base material and the release layer that is laminated on the side surface of polyester base material one, from
Type layer is formed by curing by release layer coating solution, and release layer coating fluid includes following raw material:3.2 parts of fluorine resin,
4.5 parts of PEPA, 1.6 parts of aldehyde ketone resin, 2.9 parts of curing agent, 0.5 part of auxiliary agent, 3.1 parts of delustering agent, mixed solvent 18.4
Part, mixed solvent is by benzene, ethylene glycol, 2-HEPTANONE, cyclohexanone by volume 1:0.7:1.5:0.5 is mixed to form, and auxiliary agent is scattered
Agent and the combination of antistatic agent;Curing agent is amino resins and closure isocyanates mixed system;
Wherein, fluorine resin is the bipolymer of trifluoro-ethylene-hexafluoropropene, and the hydroxyl value of fluorine resin is 30mgKOH/
G, acid number 12.2mgKOH/g, number-average molecular weight 26000;Polyester polyol resin is chloro phthalic acid-trihydroxy methyl third
The bipolymer of alkane, the hydroxyl value of polyester polyol resin are 130mgKOH/g, acid number 40mgKOH/g, and number-average molecular weight is
11000;The hydroxyl value of aldehyde ketone resin is 90mgKOH/g;Amino resins is methyl-etherified melamine resin;Closure isocyanic acid
Ester is closure three-functionality-degree isocyanates;Delustering agent is by aerosil and titanium dioxide in mass ratio 2.4:1 compounding shape
Into;Auxiliary agent is 3 in mass ratio by dispersant and antistatic agent:2 compoundings are formed.
The matte release film that above-described embodiment 1-3 is prepared carries out performance test, as a result as shown in the table:
In above-mentioned test, surface tension test is tested using a dyne pen;Case hardness test is entered using Mitsubishi's pencil
Row test;Peel test force is tested using national standard GB/T2792-1998 similar approach;Outward appearance is mainly by observing and recording
Its face coat color and state.
In above-mentioned test, comparative example is commercially available matte release film.
As can be seen from the above table, compared with comparative example, peeling force can meet to make the matte release film provided in the present invention
With requiring, and the case hardness of its film is also further lifted.
Preferred embodiments of the present invention are these are only, not thereby limit embodiments of the present invention and protection domain, it is right
For those skilled in the art, all equivalent substitutions with made by present specification should be can appreciate that and shown
And the scheme obtained by the change being clear to, it should be included in protection scope of the present invention.
Claims (8)
1. a kind of BOPET matte releases film, including polyester base material and the release layer that is laminated on the side surface of polyester base material one,
Characterized in that, the release layer is formed by curing by release layer coating solution, the release layer coating fluid includes following weight
Part raw material:Fluorine resin 2.0-3.3 parts, polyester polyol resin 3.0-5.3 parts, aldehyde ketone resin 0.5-1.7 parts, curing agent 1.5-
3.0 parts, auxiliary agent 0.2-0.6 parts, delustering agent 2.1-3.5 parts, mixed solvent 12.0-18.5 parts, the mixed solvent is by benzene, second two
Alcohol, 2-HEPTANONE, cyclohexanone by volume 1:0.7:1.5:0.5 is mixed to form, and the auxiliary agent is mixed by dispersant and antistatic agent
Formed;The curing agent is mixed to form by amino resins and closure isocyanates.
2. BOPET matte releases film according to claim 1, it is characterised in that the fluorine resin is trifluoro-ethylene-six
Fluoropropene bipolymer, and its hydroxyl value is 21-35mgKOH/g, acid number 4.5-12.7mgKOH/g, number-average molecular weight is
13000-27000。
3. BOPET matte releases film according to claim 1, it is characterised in that the polyester polyol resin is chloro
Phthalic acid-trimethylolpropane bipolymer, and its hydroxyl value is 50-150mgKOH/g, acid number 0-50mgKOH/g, is counted
Average molecular weight is 5000-13000.
4. BOPET matte releases film according to claim 1, it is characterised in that the hydroxyl value of the aldehyde ketone resin is 40-
140mgKOH/g。
5. BOPET matte releases film according to claim 1, it is characterised in that the amino resins is methyl-etherified trimerization
Cyanamide formaldehyde resin.
6. BOPET matte releases film according to claim 5, it is characterised in that the closure isocyanates is closing
Property three-functionality-degree isocyanates.
7. the BOPET matte release films according to claim any one of 1-6, it is characterised in that the delustering agent is by gas phase
Silica and titanium dioxide in mass ratio 2:1-3:1 is mixed to form.
8. the BOPET matte release films according to claim any one of 1-6, it is characterised in that the dispersant and described
The mass ratio of antistatic agent is 1-3:2-3.