CN107866262B - Catalyst for producing cyclohexylbenzene - Google Patents
Catalyst for producing cyclohexylbenzene Download PDFInfo
- Publication number
- CN107866262B CN107866262B CN201610852215.5A CN201610852215A CN107866262B CN 107866262 B CN107866262 B CN 107866262B CN 201610852215 A CN201610852215 A CN 201610852215A CN 107866262 B CN107866262 B CN 107866262B
- Authority
- CN
- China
- Prior art keywords
- solution
- catalyst
- molecular sieve
- zeolite molecular
- cyclohexylbenzene
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention relates to a catalyst for producing cyclohexylbenzene, a preparation method thereof and a method for synthesizing cyclohexylbenzene by a benzene hydroalkylation one-step method, and mainly solves the technical problems that a catalyst in the prior art causes high yield of cyclohexane serving as a byproduct in a reaction and low yield of cyclohexylbenzene serving as a main product. The catalyst for producing the cyclohexylbenzene comprises a carrier and the following active components: (1) 0.5-20 g/L of Pd; (2)0 to 50g/L of at least one lanthanide; (3) 0-30 g/L of Y element, wherein the carrier is a hydrogen type zeolite molecular sieve, and the technical scheme has a good effect, and can be used for preparing cyclohexylbenzene by a benzene hydroalkylation one-step method.
Description
Technical Field
The invention relates to a catalyst for producing cyclohexylbenzene, a preparation method thereof and a method for synthesizing cyclohexylbenzene by a benzene hydroalkylation one-step method.
Background
The cyclohexylbenzene is an important intermediate and is widely applied to the fields of liquid crystal, plastics, coatings, adhesives and the like. The cyclohexylbenzene liquid crystal has the characteristics of extremely high chemical stability, photochemical stability, low viscosity, excellent physical properties and the like, and is one of ideal materials of display devices. The cyclohexylbenzene is used as an additive of the lithium ion battery electrolyte, has the overcharge prevention performance and can improve the safety performance of the battery. In addition, phenol and cyclohexanone can be prepared through the peroxidation and decomposition reaction processes of cyclohexylbenzene, and the method is used for producing a large amount of chemical raw materials such as phenolic resin, caprolactam, nylon and the like and has a good application prospect. The basic information for cyclohexylbenzene is as follows: colorless liquid with CAS number 827-52-1 and molecular weight of C12H16Density 0.95g/cm3The boiling point is 238-240 ℃, the melting point is 5 ℃, and the flash point is 98 ℃.
The preparation method of the cyclohexylbenzene comprises the following steps: biphenyl selective hydrogenation, benzene and cyclohexene alkylation, and benzene hydrogenation alkylation. Wherein, the reaction principle of preparing the cyclohexylbenzene by benzene hydroalkylation is as follows (formula 1): according to the reaction mechanism of benzene hydrogenation alkylation, benzene is subjected to hydrogenation reaction on a metal center, so that cyclohexene can be selectively generated, and part of cyclohexane and cyclohexadiene are generated at the same time; cyclohexene and cyclohexadiene undergo alkylation with benzene on an acidic center to produce cyclohexylbenzene as a main product. Therefore, the benzene hydroalkylation can be realized to produce the cyclohexylbenzene by adopting the bi-component catalyst with the hydrogenation function and the alkylation function.
The first study on the hydroalkylation of benzene to produce cyclohexylbenzene began in the seventies and eighties of the 20 th century. The catalyst developed in the early stage has the problem of low selectivity of cyclohexylbenzene, for example, a catalyst loaded with hydrogenation metal is developed by ExxonMobil company based on MCM-22 series molecular sieves (U.S. Pat. No. 5,2011/0015457A 1, U.S. Pat. No. 3,2011/0021841A 1) and is used for preparing cyclohexylbenzene by benzene hydroalkylation, and the selectivity of the technology to byproduct cyclohexane is high. U.S. Pat. Nos. US4094918, US4219689 and US4329531 of Phillips oil company, USA, use Ni-rare earth treated zeolite catalyst and Pd as adjuvant, and both the conversion rate of benzene and the yield of CHB are low. The method has the problems of high yield of the cyclohexane as a byproduct and relatively low yield of the cyclohexylbenzene as a product in the process of preparing the cyclohexylbenzene.
Disclosure of Invention
One of the technical problems to be solved by the invention is the problems of high yield of the byproduct cyclohexane and low yield of the main product cyclohexylbenzene in the prior art, and provides a catalyst for producing the cyclohexylbenzene, which has the advantages of low yield of the cyclohexane and high yield of the cyclohexylbenzene when the catalyst is used for synthesizing the cyclohexylbenzene by reacting benzene and hydrogen.
The second technical problem to be solved by the present invention is a method for preparing the catalyst.
The invention also provides a synthesis method of cyclohexylbenzene by using the catalyst.
One of the technical solutions of the present invention to solve the above technical problems is as follows: the catalyst for producing the cyclohexylbenzene comprises a carrier and the following active components:
(1) 0.5-20 g/L of Pd;
(2)0 to 50g/L of at least one lanthanide;
(3) 0-30 g/L of Y element;
wherein the carrier is a hydrogen type zeolite molecular sieve.
In the technical scheme, the lanthanide is preferably La, Pr or Sm.
In the technical scheme, preferably, the catalyst simultaneously comprises La and Pr, or simultaneously comprises La and Sm, or simultaneously comprises Pr and Sm, and the two elements have synergistic effect on the aspect of improving the CHB yield.
In the technical scheme, La, Pr and Sm are preferably contained at the same time, and the La, Pr and Sm have ternary synergistic effect on the aspect of improving the CHB yield.
In the technical scheme, Y and at least one of La, Pr or Sm have a synergistic effect on the aspect of improving the CHB yield.
In the technical scheme, the preferable Pd content is 1-10 g/L.
In the above technical scheme, the zeolite molecular sieve is preferably selected from BEA, MOR or MWW zeolite molecular sieve; more preferred zeolite molecular sieve supports are BEA zeolite molecular sieves.
In the above technical scheme, the BEA zeolite molecular sieve is preferably a binderless molded BEA zeolite molecular sieve. The mole ratio of silicon dioxide/aluminum oxide of the binderless formed BEA zeolite molecular sieve is preferably 10-100, and more preferably 20-60.
In the technical scheme, the content of the lanthanide in the catalyst is preferably more than 0 and less than or equal to 50g/L, and more preferably 4-30 g/L.
In the technical scheme, the content of the Y element in the catalyst is preferably more than 0 and less than or equal to 30g/L, and more preferably 2-20 g/L.
To solve the second technical problem, the technical solution of the present invention is as follows: the preparation method of the catalyst in the technical scheme of one of the technical problems comprises the following steps:
a) obtaining the hydrogen-form zeolite molecular sieve;
b) preparing a compound with required amount of Pd into a solution I; the optional compound comprises at least one of palladium chloride, palladium nitrate, ammonium chloropalladate and ammonium chloropalladite, the solvent adopted by the solution can be water, and the pH value of the solution is adjusted to be 2.0-6.5 by hydrochloric acid or nitric acid or acetic acid, and in order to facilitate the same proportion, 1mol/L acetic acid aqueous solution is used as the solvent in the examples and the comparative examples in the specific embodiment of the invention;
c) preparing a required amount of lanthanide compound into a solution II;
d) preparing a compound of the element Y into a solution III;
e) loading the solution I prepared in the step b), the solution II prepared in the step c) and the solution III prepared in the step d) on the zeolite molecular sieve carrier prepared in the step a) by adopting an impregnation method, drying, and roasting at 350-550 ℃ for 3-6 hours to prepare the catalyst.
In the above technical scheme, the compound of Pd in the step b) is preferably palladium chloride.
In the above technical scheme, the lanthanide compound in step c) is preferably nitrate.
In the above technical solution, the compound of the Y element in step d) is preferably a nitrate.
In the above technical scheme, the impregnation procedure of step e) adopts mixed impregnation:
and uniformly mixing the solution I, the solution II and the solution III, and then dipping, drying and roasting the mixture together. The impregnation method is mixed impregnation.
The third technical solution of the present invention to solve the above technical problems is as follows: the synthesis method of the cyclohexylbenzene takes benzene and hydrogen as reaction raw materials, and the reaction raw materials are contacted with the catalyst in any technical scheme of the technical problem to carry out benzene hydroalkylation reaction to generate the cyclohexylbenzene.
In the technical scheme, the reaction temperature is preferably 100-200 ℃, and more preferably 120-180 ℃.
In the above technical scheme, the molar ratio of benzene to hydrogen in the reaction raw material is preferably 0.5 to 2.0, and more preferably 0.5 to 1.3.
In the above-mentioned technical means, the pressure of the reaction is preferably 0.5 to 3.0MPa (gauge pressure), and more preferably 0.5 to 2.0MPa (gauge pressure).
In the technical scheme, the liquid volume space velocity of the reaction raw material benzene is preferably 0.2-2 h-1More preferably 0.2 to 1.5 hours-1。
The catalyst of the invention simultaneously adopts Pd, lanthanide and Y as active components, thereby reducing the yield of the cyclohexane and increasing the yield of the p-cyclohexylbenzene. At the reaction temperature of 150 ℃, the molar ratio of benzene to hydrogen of 0.8, the pressure of 2.0MPa and the liquid volume space velocity of benzene of 0.5h-1Under the conditions, the yield of the cyclohexane can reach below 5.0 percent, the yield of the cyclohexylbenzene can reach up to 32 percent, and a better technical effect is achieved.
Detailed Description
[ example 1 ]
1. Catalyst preparation
Weighing PdCl containing 1.9g Pd2Dissolving in 1mol/L hydrochloric acid water solution to prepare 80g of solution I; measuring 0.1L of binderless cylindrical hydrogen type BEA zeolite molecular sieve with diameter of 1mm and length of 5mm (the mole ratio of silicon dioxide/aluminum oxide is 40); loading the solution I on a hydrogen type BEA zeolite molecular sieve, soaking for 12h at room temperature, drying for 12h at 100 ℃, and roasting for 4h at 450 ℃ to obtain the required catalyst.
2. Catalyst evaluation
10ml of the catalyst was charged into a fixed bed reactor, and activity evaluation was performed after reduction activation under the following conditions: the reaction temperature is 150 ℃, the molar ratio of benzene to hydrogen in the reaction raw material is 0.8, the reaction pressure is 2.0MPa (gauge pressure), and the liquid volume space velocity of the reaction raw material benzene is 0.5h-1。
The composition of the catalyst and the evaluation results are shown in Table 1 for convenience of comparison.
Comparative example 1
1. Catalyst preparation
PdCl containing Pd 0.3g is weighed2Dissolving in 1mol/L hydrochloric acid water solution to prepare 40g of solution I; la (NO) 1.6g of La was weighed out3)3·6H2Dissolving O in water40g of solution II; weighing 0.1L of binderless cylindrical hydrogen type BEA zeolite molecular sieve (the molar ratio of silicon dioxide to aluminum oxide is 40) with the diameter of 1mm and the length of 5mm, uniformly mixing the solution I and the solution II, loading the mixture on the hydrogen type BEA zeolite molecular sieve, soaking the mixture at room temperature for 12 hours, drying the mixture at 100 ℃ for 12 hours, and roasting the mixture at 450 ℃ for 4 hours to obtain the required catalyst.
2. Catalyst evaluation
The catalyst evaluation method is shown in example 1.
The composition of the catalyst and the evaluation results are shown in Table 1 for convenience of comparison.
Comparative example 2
1. Catalyst preparation
PdCl containing Pd 0.3g is weighed2Dissolving in 1mol/L hydrochloric acid water solution to prepare 40g of solution I; weighing Pr (NO) containing Pr 1.6g3)3·6H2Dissolving O in water to prepare 40g of solution II; weighing 0.1L of binderless cylindrical hydrogen type BEA zeolite molecular sieve (the molar ratio of silicon dioxide to aluminum oxide is 40) with the diameter of 1mm and the length of 5mm, uniformly mixing the solution I and the solution II, loading the mixture on the hydrogen type BEA zeolite molecular sieve, soaking the mixture at room temperature for 12 hours, drying the mixture at 100 ℃ for 12 hours, and roasting the mixture at 450 ℃ for 4 hours to obtain the required catalyst.
2. Catalyst evaluation
The catalyst evaluation method is shown in example 1.
The composition of the catalyst and the evaluation results are shown in Table 1 for convenience of comparison.
Comparative example 3
1. Catalyst preparation
PdCl containing Pd 0.3g is weighed2Dissolving in 1mol/L hydrochloric acid water solution to prepare 40g of solution I; sm (NO) 1.6g is weighed3)3·6H2Dissolving O in water to prepare 40g of solution II; weighing 0.1L of binderless cylindrical hydrogen type BEA zeolite molecular sieve (the molar ratio of silicon dioxide to aluminum oxide is 40) with the diameter of 1mm and the length of 5mm, uniformly mixing the solution I and the solution II, loading the mixture on the hydrogen type BEA zeolite molecular sieve, soaking the mixture at room temperature for 12 hours, drying the mixture at 100 ℃ for 12 hours, and roasting the mixture at 450 ℃ for 4 hours to obtain the required catalyst.
2. Catalyst evaluation
The catalyst evaluation method is shown in example 1.
The composition of the catalyst and the evaluation results are shown in Table 1 for convenience of comparison.
Comparative example 4
1. Catalyst preparation
PdCl containing Pd 0.3g is weighed2Dissolving in 1mol/L hydrochloric acid water solution to prepare 40g of solution I; weighing Y (NO) containing 1.6g of Y3)3·6H2Dissolving O in water to prepare 40g of solution II; weighing 0.1L of binderless cylindrical hydrogen type BEA zeolite molecular sieve (the molar ratio of silicon dioxide to aluminum oxide is 40) with the diameter of 1mm and the length of 5mm, mixing the solution I and the solution II, loading the mixture on the hydrogen type BEA zeolite molecular sieve, soaking the mixture at room temperature for 12 hours, drying the mixture at 100 ℃ for 12 hours, and roasting the mixture at 450 ℃ for 4 hours to obtain the required catalyst.
2. Catalyst evaluation
The catalyst evaluation method is shown in example 1.
The composition of the catalyst and the evaluation results are shown in Table 1 for convenience of comparison.
[ example 2 ]
1. Catalyst preparation
PdCl containing Pd 0.3g is weighed2Dissolving in 1mol/L hydrochloric acid water solution to prepare 40g of solution I; la (NO) containing 1.2g of La was weighed out3)3·6H2Dissolving O in water to prepare 20g of solution II; weighing Y (NO) containing 0.4g of Y3)3·6H2Dissolving O in water to prepare 20g of solution III; weighing 0.1L of binderless cylindrical hydrogen type BEA zeolite molecular sieve (the molar ratio of silicon dioxide to aluminum oxide is 40) with the diameter of 1mm and the length of 5mm, mixing the solution I, the solution II and the solution III, loading the mixture on the hydrogen type BEA zeolite molecular sieve, soaking the mixture at room temperature for 12 hours, drying the mixture at 100 ℃ for 12 hours, and roasting the mixture at 450 ℃ for 4 hours to obtain the required catalyst.
2. Catalyst evaluation
The catalyst evaluation method is shown in example 1.
The compositions of the catalysts are shown in Table 1 for comparison, and the evaluation results are shown in Table 2.
[ example 3 ]
1. Catalyst preparation
PdCl containing Pd 0.3g is weighed2Dissolving in 1mol/L hydrochloric acid water solution to prepare 40g of solution I; weighing Pr (NO) containing Pr 1.2g3)3·6H2Dissolving O in water to prepare 20g of solution II; weighing Y (NO) containing 0.4g of Y3)3·6H2Dissolving O in water to prepare 20g of solution III; weighing 0.1L of binderless cylindrical hydrogen type BEA zeolite molecular sieve (the molar ratio of silicon dioxide to aluminum oxide is 40) with the diameter of 1mm and the length of 5mm, mixing the solution I, the solution II and the solution III, loading the mixture on the hydrogen type BEA zeolite molecular sieve, soaking the mixture at room temperature for 12 hours, drying the mixture at 100 ℃ for 12 hours, and roasting the mixture at 450 ℃ for 4 hours to obtain the required catalyst.
2. Catalyst evaluation
The catalyst evaluation method is shown in example 1.
The composition of the catalyst and the evaluation results are shown in Table 1 for convenience of comparison.
[ example 4 ]
1. Catalyst preparation
PdCl containing Pd 0.3g is weighed2Dissolving in 1mol/L hydrochloric acid water solution to prepare 40g of solution I; weighing Sm (NO) 1.2g3)3·6H2Dissolving O in water to prepare 20g of solution II; weighing Y (NO) containing 0.4g of Y3)3·6H2Dissolving O in water to prepare 20g of solution III; weighing 0.1L of binderless cylindrical hydrogen type BEA zeolite molecular sieve (the molar ratio of silicon dioxide to aluminum oxide is 40) with the diameter of 1mm and the length of 5mm, mixing the solution I, the solution II and the solution III, loading the mixture on the hydrogen type BEA zeolite molecular sieve, soaking the mixture at room temperature for 12 hours, drying the mixture at 100 ℃ for 12 hours, and roasting the mixture at 450 ℃ for 4 hours to obtain the required catalyst.
2. Catalyst evaluation
The catalyst evaluation method is shown in example 1.
The composition of the catalyst and the evaluation results are shown in Table 1 for convenience of comparison.
[ example 5 ]
1. Catalyst preparation
PdCl containing 0.3g Pd was weighed2Dissolving in 1mol/L hydrochloric acid water solution to prepare 40g of solution I; weighing the mixture containing La 0.6g of La (NO)3)3·6H2O and Pr (NO) containing Pr 0.6g3)3·6H2Dissolving O in water to prepare 20g of solution II; weighing Y (NO) containing 0.4g of Y3)3·6H2Dissolving O in water to prepare 20g of solution III; then uniformly mixing the solution I, the solution II and the solution III; weighing 0.1L of binderless cylindrical hydrogen type BEA zeolite molecular sieve (the molar ratio of silicon dioxide to aluminum oxide is 40) with the diameter of 1mm and the length of 5mm, loading the mixed solution on the hydrogen type BEA zeolite molecular sieve, soaking at room temperature for 12h, drying at 100 ℃ for 12h, and roasting at 450 ℃ for 4h to obtain the required catalyst.
2. Catalyst evaluation
The catalyst evaluation method is shown in example 1.
The composition of the catalyst and the evaluation results are shown in Table 1 for convenience of comparison.
[ example 6 ]
1. Catalyst preparation
PdCl containing 0.3g Pd was weighed2Dissolving in 1mol/L hydrochloric acid water solution to prepare 40g of solution I; la (NO) 0.6g of La was weighed out3)3·6H2O and Sm (NO) in an amount of 0.6g of Sm3)3·6H2Dissolving O in water to prepare 20g of solution II; weighing Y (NO) containing 0.4g of Y3)3·6H2Dissolving O in water to prepare 20g of solution III; then uniformly mixing the solution I, the solution II and the solution III; weighing 0.1L of binderless cylindrical hydrogen type BEA zeolite molecular sieve (the molar ratio of silicon dioxide to aluminum oxide is 40) with the diameter of 1mm and the length of 5mm, loading the mixed solution on the hydrogen type BEA zeolite molecular sieve, soaking at room temperature for 12h, drying at 100 ℃ for 12h, and roasting at 450 ℃ for 4h to obtain the required catalyst.
2. Catalyst evaluation
The catalyst evaluation method is shown in example 1.
The composition of the catalyst and the evaluation results are shown in Table 1 for convenience of comparison.
[ example 7 ]
1. Catalyst preparation
PdCl containing 0.3g Pd was weighed2Dissolving in 1mol/L hydrochloric acid water solution to prepare40g of solution I; weighing Pr (NO) containing 0.6g Pr3)3·6H2O and Sm (NO) in an amount of 0.6g of Sm3)3·6H2Dissolving O in water to prepare 20g of solution II; weighing Y (NO) containing 0.4g of Y3)3·6H2Dissolving O in water to prepare 20g of solution III; then uniformly mixing the solution I, the solution II and the solution III; weighing 0.1L of binderless cylindrical hydrogen type BEA zeolite molecular sieve (the molar ratio of silicon dioxide to aluminum oxide is 40) with the diameter of 1mm and the length of 5mm, loading the mixed solution on the hydrogen type BEA zeolite molecular sieve, soaking at room temperature for 12h, drying at 100 ℃ for 12h, and roasting at 450 ℃ for 4h to obtain the required catalyst.
2. Catalyst evaluation
The catalyst evaluation method is shown in example 1.
The composition of the catalyst and the evaluation results are shown in Table 1 for convenience of comparison.
[ example 8 ]
1. Catalyst preparation
PdCl containing 0.3g Pd was weighed2Dissolving in 1mol/L hydrochloric acid water solution to prepare 40g of solution I; la (NO) 0.6g of La was weighed out3)3·6H2O and Pr (NO) containing Pr 0.3g3)3·6H2O and Sm (NO) in an amount of 0.3g of Sm3)3·6H2Dissolving O in water to prepare 20g of solution II; weighing Y (NO) containing 0.4g of Y3)3·6H2Dissolving O in water to prepare 20g of solution III; then uniformly mixing the solution I, the solution II and the solution III; weighing 0.1L of binderless cylindrical hydrogen type BEA zeolite molecular sieve (the molar ratio of silicon dioxide to aluminum oxide is 40) with the diameter of 1mm and the length of 5mm, loading the mixed solution on the hydrogen type BEA zeolite molecular sieve, soaking at room temperature for 12h, drying at 100 ℃ for 12h, and roasting at 450 ℃ for 4h to obtain the required catalyst.
2. Catalyst evaluation
The catalyst evaluation method is shown in example 1.
The composition of the catalyst and the evaluation results are shown in Table 1 for convenience of comparison.
[ example 9 ]
1. Catalyst preparation
PdCl containing 0.3g Pd was weighed2Dissolving in 1mol/L hydrochloric acid water solution to prepare 40g of solution I; la (NO) 0.3g of La was weighed out3)3·6H2O and Pr (NO) containing Pr 0.6g3)3·6H2O and Sm (NO) in an amount of 0.3g of Sm3)3·6H2Dissolving O in water to prepare 20g of solution II; weighing Y (NO) containing 0.4g of Y3)3·6H2Dissolving O in water to prepare 20g of solution III; then uniformly mixing the solution I, the solution II and the solution III; weighing 0.1L of binderless cylindrical hydrogen type BEA zeolite molecular sieve (the molar ratio of silicon dioxide to aluminum oxide is 40) with the diameter of 1mm and the length of 5mm, loading the mixed solution on the hydrogen type BEA zeolite molecular sieve, soaking at room temperature for 12h, drying at 100 ℃ for 12h, and roasting at 450 ℃ for 4h to obtain the required catalyst.
2. Catalyst evaluation
The catalyst evaluation method is shown in example 1.
The composition of the catalyst and the evaluation results are shown in Table 1 for convenience of comparison.
[ example 10 ]
1. Catalyst preparation
PdCl containing 0.3g Pd was weighed2Dissolving in 1mol/L hydrochloric acid water solution to prepare 40g of solution I; la (NO) 0.3g of La was weighed out3)3·6H2O and Pr (NO) containing Pr 0.3g3)3·6H2O and Sm (NO) in an amount of 0.6g of Sm3)3·6H2Dissolving O in water to prepare 20g of solution II; weighing Y (NO) containing 0.4g of Y3)3·6H2Dissolving O in water to prepare 20g of solution III; then uniformly mixing the solution I, the solution II and the solution III; weighing 0.1L of binderless cylindrical hydrogen type BEA zeolite molecular sieve (the molar ratio of silicon dioxide to aluminum oxide is 40) with the diameter of 1mm and the length of 5mm, loading the mixed solution on the hydrogen type BEA zeolite molecular sieve, soaking at room temperature for 12h, drying at 100 ℃ for 12h, and roasting at 450 ℃ for 4h to obtain the required catalyst.
2. Catalyst evaluation
The catalyst evaluation method is shown in example 1.
The composition of the catalyst and the evaluation results are shown in Table 1 for convenience of comparison.
[ example 11 ]
1. Catalyst preparation
PdCl containing 0.3g Pd was weighed2Dissolving in 1mol/L hydrochloric acid water solution to prepare 40g of solution I; la (NO) 0.4g of La was weighed out3)3·6H2O and Pr (NO) containing Pr 0.4g3)3·6H2O and Sm (NO) in an amount of 0.4g of Sm3)3·6H2Dissolving O in water to prepare 20g of solution II; weighing Y (NO) containing 0.4g of Y3)3·6H2Dissolving O in water to prepare 20g of solution III; then uniformly mixing the solution I, the solution II and the solution III; weighing 0.1L of binderless cylindrical hydrogen type BEA zeolite molecular sieve (the molar ratio of silicon dioxide to aluminum oxide is 40) with the diameter of 1mm and the length of 5mm, loading the mixed solution on the hydrogen type BEA zeolite molecular sieve, soaking at room temperature for 12h, drying at 100 ℃ for 12h, and roasting at 450 ℃ for 4h to obtain the required catalyst.
2. Catalyst evaluation
The catalyst evaluation method is shown in example 1.
The composition of the catalyst and the evaluation results are shown in Table 1 for convenience of comparison.
[ example 12 ]
PdCl containing 0.5g Pd was weighed2Dissolving in 1mol/L hydrochloric acid water solution to prepare 40g of solution I; la (NO) 1.8g was weighed out3)3·6H2O and Pr 1.2g of Pr (NO)3)3·6H2O and Sm (NO) containing Sm 1.2g3)3·6H2Dissolving O in water to prepare 20g of solution II; weighing Y (NO) containing Y2 g3)3·6H2Dissolving O in water to prepare 20g of solution III; then uniformly mixing the solution I, the solution II and the solution III; weighing 0.1L of binderless cylindrical hydrogen type BEA zeolite molecular sieve (the molar ratio of silicon dioxide to aluminum oxide is 40) with the diameter of 1mm and the length of 5mm, loading the mixed solution on the hydrogen type BEA zeolite molecular sieve, soaking at room temperature for 12h, drying at 100 ℃ for 12h, and roasting at 450 ℃ for 4h to obtain the required catalyst.
2. Catalyst evaluation
The catalyst evaluation method is shown in example 1.
The composition of the catalyst and the evaluation results are shown in Table 1 for convenience of comparison.
[ example 13 ]
1. Catalyst preparation
PdCl containing 0.1g Pd was weighed2Dissolving in 1mol/L hydrochloric acid water solution to prepare 40g of solution I; la (NO) 0.2g of La was weighed out3)3·6H2O and Pr 0.1g of Pr (NO)3)3·6H2O and Sm (NO) in an amount of 0.1g of Sm3)3·6H2Dissolving O in water to prepare 20g of solution II; weighing Y (NO) containing 0.2g of Y3)3·6H2Dissolving O in water to prepare 20g of solution III; then uniformly mixing the solution I, the solution II and the solution III; weighing 0.1L of binderless cylindrical hydrogen type BEA zeolite molecular sieve (the molar ratio of silicon dioxide to aluminum oxide is 40) with the diameter of 1mm and the length of 5mm, loading the mixed solution on the hydrogen type BEA zeolite molecular sieve, soaking at room temperature for 12h, drying at 100 ℃ for 12h, and roasting at 450 ℃ for 4h to obtain the required catalyst.
2. Catalyst evaluation
The catalyst evaluation method is shown in example 1.
The composition of the catalyst and the evaluation results are shown in Table 1 for convenience of comparison.
TABLE 1 catalyst composition and evaluation results
Note: in table 1, CH represents cyclohexane, and CHB represents cyclohexylbenzene.
Claims (5)
1. The catalyst for producing the cyclohexylbenzene comprises a carrier and the following active components:
(1) 0.5-20 g/L of Pd;
(2) 4-30 g/L of lanthanide;
(3) 2-20 g/L of Y element;
wherein the carrier is a hydrogen type zeolite molecular sieve; the hydrogen type zeolite molecular sieve is a BEA zeolite molecular sieve, and the selected BEA zeolite molecular sieve is a binderless formed BEA zeolite molecular sieve; the mole ratio of silicon dioxide/aluminum oxide of the binderless formed BEA zeolite molecular sieve is 10-100;
the lanthanide element comprises both La and Pr, or both La and Sm, or both Pr and Sm.
2. The catalyst according to claim 1, wherein the Pd content is 1 to 10 g/L.
3. A process for preparing the catalyst of claim 1, comprising the steps of:
a) obtaining the hydrogen-form zeolite molecular sieve;
b) preparing a compound with required amount of Pd into a solution I;
c) preparing a required amount of lanthanide compound into a solution II;
d) preparing a compound of the element Y into a solution III;
e) loading the solution I prepared in the step b), the solution II prepared in the step c) and the solution III prepared in the step d) on the zeolite molecular sieve carrier prepared in the step a) by adopting an impregnation method, drying, and roasting at 350-550 ℃ for 3-6 hours to prepare the catalyst.
4. A synthesis method of cyclohexylbenzene, which takes benzene and hydrogen as reaction raw materials, and makes the reaction raw materials contact with the catalyst of any one of claims 1 to 2 to carry out benzene hydroalkylation reaction to generate the cyclohexylbenzene.
5. The method as set forth in claim 4, characterized in that the liquid volume space velocity of the reaction raw material benzene is 0.2-3 h-1。