CN107841888A - Improve the pure cotton light black adhesive lining and its production method of clothes quality - Google Patents
Improve the pure cotton light black adhesive lining and its production method of clothes quality Download PDFInfo
- Publication number
- CN107841888A CN107841888A CN201711101666.6A CN201711101666A CN107841888A CN 107841888 A CN107841888 A CN 107841888A CN 201711101666 A CN201711101666 A CN 201711101666A CN 107841888 A CN107841888 A CN 107841888A
- Authority
- CN
- China
- Prior art keywords
- black
- lattice
- adhesive lining
- production method
- powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention discloses a kind of production method for the pure cotton light black adhesive lining for improving clothes quality, and production procedure includes turning over the step such as seam, concise, dyeing, chemical shiinkproof finish, black HDPE powder light coating, machine shrunk.Adhesive lining coating surface black bright, adhesive lining is with that after coloured slim garment material bonding, will not produce the PUR dot problem of white shiny, improve clothes quality.The faults such as leak source, holiday can be easily detected during appearance test, it is ensured that garment enterprise does not occur to produce the loss such as drop because product is made using fault adhesive lining.Free and hydrolysis formaldehyde≤35mg/kg of adhesive lining, is 0.8%~+0.5% through broadwise washing size changing rate.Production method of the present invention is easy to operate, environmentally friendly, excellent product performance.
Description
The application is application number：2016102566056th, the applying date：2016-04-25, title：" pure cotton light black bonds
The divisional application of lining and its production method ".
Technical field
The present invention relates to a kind of pure cotton light black adhesive lining and its production method.
Background technology
, can on the garment material of bonding place after scribbling white PE powder pure cotton adhesive lining and coloured slim garment material bonding
To see the PUR dot of white shiny, clothes quality is had a strong impact on.In addition, conventional production adhesive lining, coating surface is dim,
During appearance test, the fault such as leak source, holiday is not easy one-hundred-percent inspection and gone out sometimes, and garment enterprise, which uses to contain, does not detect fault bonding
After clothes are made in lining, the losses such as quality drop can be produced.
The content of the invention
Present invention aims at a kind of coating surface black bright is provided, adhesive lining bonds with coloured slim garment material
Afterwards, it will not produce the PUR dot problem of white shiny, can easily detect the faults such as leak source, holiday during appearance test,
Ensure that garment enterprise does not occur to produce the loss such as drop, free and hydrolysis formaldehyde≤35mg/ because product is made using fault adhesive lining
Kg, the pure cotton light black adhesive lining and its production method for being -0.8%~+0.5% through broadwise washing size changing rate.
The present invention technical solution be：
A kind of pure cotton light black adhesive lining, it is characterized in that：Coating surface black bright；Free and hydrolysis formaldehyde≤35mg/kg；
It is -0.8%~+0.5% through broadwise washing size changing rate.
The fabric specification of lining cloth is one kind in following two kinds：The first width is 48.5 inches, yarn count 20s
× 20s, density are 60 × 60 pieces/inch, and second width is 48.5 inches, yarn count is 40 s × 40s, density is
58 × 50 pieces/inch.
A kind of production method of pure cotton light black adhesive lining, include turning over seam, concise, dyeing, chemical shrinkproof whole successively
Reason, black HDPE powder light coating, machine shrunk step, it is characterized in that：When contaminating grey, dyed using reducing dye, dye liquor group
Turn into：Vat black BCN 6.5g/L, Threne olive T 4.4g/L, vat red F3B 0.46g/L, remaining is water；Reduction
Liquid forms：26~30g/L of sodium hydroxide, 24~28g/L of sodium hydrosulfite of 85% content, remaining is water；Dyeing flow
It is with condition：Open width cloth feeding → evenness calender pads dye liquor → two row infrared preliminary drying → two group, 70~80 DEG C of hot blast preliminary drying → mono-
12 cylinder drying → cropping → evenness calenders of group pad the lattice 5~30 of reductive steam box decatize 2min at reducing solution → 102 DEG C → two
DEG C cold water is washed, and → oxidation liquid oxidation of the ventilative oxidation → use containing 27.5% 0.5~1g/L of hydrogen peroxide → uses 2~3g/L of concentration soap
Boil agent and carry out the lattice flat wash trough of two lattice soap boilings → six and single-frame flow backwards washing, often lattice temperature be respectively 90~95 DEG C, 80~90 DEG C, 70~
80 DEG C, 70~80 DEG C, 60~70 DEG C, 5~30 DEG C of cold flow water → 5~30 DEG C cold water wash → two rows totally 24 cylinder drying → croppings
；When contaminating black, using Cold Pad-Batch Dyeing with Reactive Dyes, dye liquor composition：Active black LC-G 76.0g/L, active red LC-DB
3.4g/L, reactive orange LC -4RN0.5g/L；Alkali lye forms：Caustic soda 35g/L, low temperature cold dome fixation alkali EW-956 35g/L；Dye
Color technique is：Dye liquor and alkali lye 4：1 ratio mixes, pick-up rate 65%, 55~60m/min of speed, 16~24h of stacking at room temperature；
Dyeing aftertreatment technology is：The lattice flowing cool water of cloth feeding → first, second and third washes 95~98 DEG C of → fourth, fifth lattice, adds releasing soaping agent
2~3g/L of ANT soap boiling → the, six lattice, 70~80 DEG C of washing the → the seven lattice flowing cool water washing → croppings.
During textile chemistry shiinkproof finish, the composition of shiinkproof finish liquid is：
The g/L of crease-shedding finishing agent RESIN BRT 40
The g/L of Arkofix NDF liqc 80~100
MgCl2·6H2The g/L of O 12~14
Ethylene urea 4.0g/L
The g/L of NON IONIC SOFTNER V-12 4.0
Remaining is water, and adjusts pH to 4.0~4.5 with citric acid；
By open width cloth feeding during chemical shiinkproof finish, shiinkproof finish liquid is rolled in two leachings two, liquid carrying rate 65%~70%, 110~130 DEG C
Loose formula drying, needle plate on overfeeding 2%~4%, eight lattice hot blasts bake, wherein 150 DEG C of the first lattice temperature, the second lattice temperature 160
DEG C, the three~eight 170 DEG C of lattice temperature, two cylinders cool down cropping step, and speed is 30~45m/min.
The processing of black HDPE powder light coating includes open width cloth feeding, No. 1 oily 225-245 DEG C of preheating of hot-rolling, No. 2 oil heat successively
Roller 220~240 DEG C of preheatings, engraved roll black HDPE PURs（Upper sea cowry Lai Te plastic cement Co., Ltd HDPE PURs（Black）
0—200MY）Powder point coating, No. 3 oily 230~250 DEG C of heating of hot-rolling, use power red for 3000~4500W infrared tube progress
It is outer baking melt, mirror roller calendering, tentering setting, temperature≤25 DEG C water cooling, be wrapped step；Engraved roll mesh number：30th, 33 mesh/English
It is very little；23~29g/m of fabric powder point coating amount2, prevent reverse side from permeating；During powder point coating, it is impossible to occur jump powder, leak source,
Half head；Lead to 105-110 DEG C of hot water circuit during black HDPE PUR powder point coatings, in engraved roll；Logical 65 in calender~
85 DEG C of hot water circuit；Cloth feeding speed is 18~22m/min.
Adhesive lining coating surface black bright of the present invention, adhesive lining is with that after coloured slim garment material bonding, will not produce
The PUR dot problem of white shiny, improves clothes quality；The defects such as leak source, holiday can be easily detected during appearance test
Point, it is ensured that garment enterprise does not occur to produce the loss such as drop because product is made using fault adhesive lining；Adhesive lining is through broadwise washing shrinkage
It is small, dissociate low with hydrolysis formaldehyde, environmentally friendly, production method is easy to operate.
With reference to embodiment, the invention will be further described.
Embodiment 1：
The fabric specification of lining cloth is：Door width is 48.5 inches, yarn count is 20s × 20s, density is 60 × 60 pieces/inch.
A kind of production method of pure cotton light black adhesive lining, include turning over seam, concise, dyeing, chemical shrinkproof whole successively
Reason, black HDPE powder light coating, machine shrunk step；When contaminating grey, dyed using reducing dye, dye liquor composition is：Reduction
Black BCN 6.5g/L, Threne olive T 4.4g/L, vat red F3B 0.46g/L, remaining is water；Reducing solution forms：Hydrogen
26~30g/L of sodium oxide molybdena, 24~28g/L of sodium hydrosulfite of 85% content, remaining is water；Dyeing flow is with condition：It is flat
Width cloth feeding → evenness calender pads dye liquor → 70~80 DEG C of two row infrared preliminary drying → two group cylinder of hot blast preliminary drying → mono- group 12
Drying → cropping → evenness calender pad reductive steam box decatize 2min at reducing solution → 102 DEG C → two lattice, 5~30 DEG C of cold water wash →
Ventilative oxidation → with the oxidation liquid oxidation → with 2~3g/L of concentration soap boiling agent containing 27.5% 0.5~1g/L of hydrogen peroxide carries out two
The lattice flat wash trough of lattice soap boiling → six single-frame flows backwards washing, be respectively 90~95 DEG C per lattice temperature, 80~90 DEG C, 70~80 DEG C, 70~
80 DEG C, 60~70 DEG C, 5~30 DEG C of cold flow water → 5~30 DEG C cold water wash → two rows totally 24 cylinder drying → croppings.
During textile chemistry shiinkproof finish, the composition of shiinkproof finish liquid is：
The g/L of crease-shedding finishing agent RESIN BRT 40
The g/L of Arkofix NDF liqc 90~100
MgCl2·6H2The g/L of O 13~14
Ethylene urea 4.0g/L
The g/L of NON IONIC SOFTNER V-12 4.0
Remaining is water, and adjusts pH to 4.0~4.3 with citric acid；
By open width cloth feeding during chemical shiinkproof finish, shiinkproof finish liquid is rolled in two leachings two, liquid carrying rate 65%~70%, 110~130 DEG C
Loose formula drying, needle plate on overfeeding 2%~4%, eight lattice hot blasts bake, wherein 150 DEG C of the first lattice temperature, the second lattice temperature 160
DEG C, the three~eight 170 DEG C of lattice temperature, two cylinders cool down cropping step, and speed is 30~40m/min.
The processing of black HDPE powder light coating includes open width cloth feeding, No. 1 oily 225-245 DEG C of preheating of hot-rolling, No. 2 oil heat successively
Roller 220~240 DEG C of preheatings, engraved roll black HDPE PURs（Upper sea cowry Lai Te plastic cement Co., Ltd HDPE PURs（Black）
0—200MY）Powder point coating, No. 3 oily 230~250 DEG C of heating of hot-rolling, power is used to carry out infrared baking for 4500W infrared tube
Melt, mirror roller calendering, tentering setting, temperature≤25 DEG C water cooling, package step；Engraved roll mesh number：30 mesh/inch；Fabric
27~29g/m of powder point coating amount2, prevent reverse side from permeating；During powder point coating, it is impossible to occur jumping powder, leak source, half head；
Lead to 105-110 DEG C of hot water circuit during black HDPE PUR powder point coatings, in engraved roll；Lead to 65~85 DEG C of heat in calender
Water circulation；Cloth feeding speed is 18~20m/min.
Embodiment 2:
The fabric specification of lining cloth is：Door width is 48.5 inches, yarn count is 40 s × 40s, density is 58 × 50/English
It is very little.
A kind of production method of pure cotton light black adhesive lining, include turning over seam, concise, dyeing, chemical shrinkproof whole successively
Reason, black HDPE powder light coating, machine shrunk step；When contaminating black, using Cold Pad-Batch Dyeing with Reactive Dyes, dye liquor composition：
Active black LC-G 76.0g/L, active red LC-DB 3.4g/L, reactive orange LC -4RN0.5g/L；Alkali lye forms：Caustic soda
35g/L, low temperature cold dome fixation alkali EW-956（Qingdao Chinese mugwort science of culture auxiliary agent Co., Ltd） 35g/L；Dyeing is：Dye liquor with
Alkali lye 4：1 ratio mixes, pick-up rate 65%, 55~60m/min of speed, 16~24h of stacking at room temperature；Dye aftertreatment technology
For：The lattice flowing cool water of cloth feeding → first, second and third washes 95~98 DEG C of → fourth, fifth lattice, adds releasing soaping agent ANT 2~3g/L soaps
Boil 70~80 DEG C of washing the → the seven lattice flowing cool water washing → croppings of the → the six lattice.
During textile chemistry shiinkproof finish, the composition of shiinkproof finish liquid is：
The g/L of crease-shedding finishing agent RESIN BRT 40
The g/L of Arkofix NDF liqc 80~90
MgCl2·6H2The g/L of O 12~13
Ethylene urea 4.0g/L
The g/L of NON IONIC SOFTNER V-12 4.0
Remaining is water, and adjusts pH to 4.2~4.5 with citric acid；
By open width cloth feeding during chemical shiinkproof finish, shiinkproof finish liquid is rolled in two leachings two, liquid carrying rate 65%~70%, 110~130 DEG C
Loose formula drying, needle plate on overfeeding 2%~4%, eight lattice hot blasts bake, wherein 150 DEG C of the first lattice temperature, the second lattice temperature 160
DEG C, the three~eight 170 DEG C of lattice temperature, two cylinders cool down cropping step, and speed is 35~45m/min.
The processing of black HDPE powder light coating includes open width cloth feeding, No. 1 oily 225-245 DEG C of preheating of hot-rolling, No. 2 oil heat successively
Roller 220~240 DEG C of preheatings, engraved roll black HDPE PURs（Upper sea cowry Lai Te plastic cement Co., Ltd HDPE PURs（Black）
0—200MY）Powder point coating, No. 3 oily 230~250 DEG C of heating of hot-rolling, power is used to carry out infrared baking for 3000W infrared tube
Melt, mirror roller calendering, tentering setting, temperature≤25 DEG C water cooling, package step；Engraved roll mesh number:33 mesh/inch；Knit
23~25g/m of thing powder point coating amount2, prevent reverse side from permeating；During powder point coating, it is impossible to occur jumping powder, leak source, half head
；Lead to 105-110 DEG C of hot water circuit during black HDPE PUR powder point coatings, in engraved roll；Lead to 65~85 DEG C in calender
Hot water circuit；Cloth feeding speed is 20~22m/min.
Claims (2)
1. a kind of production method for the pure cotton light black adhesive lining for improving clothes quality, it is characterized in that：The fabric specification of lining cloth
For：Door width is 48.5 inches, yarn count is 40 s × 40s, density is 58 × 50 pieces/inch；
Production method, include turning over seam, concise, dyeing, chemical shiinkproof finish, black HDPE powder light coating, machine shrunk successively
Step；When contaminating black, using Cold Pad-Batch Dyeing with Reactive Dyes, dye liquor composition：Active black LC-G 76.0g/L, active red LC-
DB 3.4g/L, reactive orange LC -4RN0.5g/L；Alkali lye forms：Caustic soda 35g/L, low temperature cold dome fixation alkali EW-956（Qingdao
End science of culture auxiliary agent Co., Ltd） 35g/L；Dyeing is：Dye liquor and alkali lye 4：1 ratio mixes, pick-up rate 65%, speed
55~60m/min, 16~24h of stacking at room temperature；Dyeing aftertreatment technology is：The lattice flowing cool water of cloth feeding → first, second and third washes → the
4th, 95~98 DEG C of five lattice, add six lattice of releasing soaping agent 2~3g/L of ANT soap boiling → the, 70~80 DEG C of washing the → the seven lattice flowings cold
Water washing → cropping etc.；
By open width cloth feeding during chemical shiinkproof finish, shiinkproof finish liquid is rolled in two leachings two, liquid carrying rate 65%~70%, 110~130 DEG C
Loose formula drying, needle plate on overfeeding 2%~4%, eight lattice hot blasts bake, wherein 150 DEG C of the first lattice temperature, the second lattice temperature 160
DEG C, the three~eight 170 DEG C of lattice temperature, two cylinders cool down cropping step, and speed is 35~45m/min；
The processing of black HDPE powder light coating includes open width cloth feeding, No. 1 oily hot-rolling 225-245 DEG C of preheating, No. 2 oily hot-rollings successively
220~240 DEG C of preheatings, engraved roll black HDPE PURs powder point coating, No. 3 oily 230~250 DEG C of hot-rollings heat, using power
Carry out infrared baking for 3000W infrared tube and melt, mirror roller calendering, tentering setting, temperature≤25 DEG C water cooling, step be wrapped；
Engraved roll mesh number:33 mesh/inch；23~25g/m of fabric powder point coating amount2, prevent reverse side from permeating；During powder point coating,
Can not occur jumping powder, leak source, half head；Lead to 105-110 DEG C of hot water during black HDPE PUR powder point coatings, in engraved roll
Circulation；Lead to 65~85 DEG C of hot water circuit in calender；Cloth feeding speed is 20~22m/min.
2. the production method of the pure cotton light black adhesive lining according to claim 1 for improving clothes quality, its feature
It is：During textile chemistry shiinkproof finish, the composition of shiinkproof finish liquid is：
The g/L of crease-shedding finishing agent RESIN BRT 40
The g/L of Arkofix NDF liqc 80~90
MgCl2·6H2The g/L of O 12~13
Ethylene urea 4.0g/L
The g/L of NON IONIC SOFTNER V-12 4.0
Remaining is water, and adjusts pH to 4.2~4.5 with citric acid.