CN107841215A - A kind of aqueous, environmental protective anticorrosive paint - Google Patents
A kind of aqueous, environmental protective anticorrosive paint Download PDFInfo
- Publication number
- CN107841215A CN107841215A CN201711275389.0A CN201711275389A CN107841215A CN 107841215 A CN107841215 A CN 107841215A CN 201711275389 A CN201711275389 A CN 201711275389A CN 107841215 A CN107841215 A CN 107841215A
- Authority
- CN
- China
- Prior art keywords
- parts
- weight
- aqueous
- anticorrosive paint
- environmental protective
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of aqueous, environmental protective anticorrosive paint, including the aqueous acrylic modified epoxy emulsion of 15 30 parts by weight, 120 200 parts by weight of acrylic acid emulsions, 30 50 parts by weight silicone acrylic emulsions, 0.1 1 parts per weight dispersing agents, 0.1 2 parts by weight wetting agents, 0.5 2 parts by weight defoamers, 50 120 parts by weight antirust agent, 01 parts by weight of thickening agent, 10 20 parts by weight coalescents, 200 500 parts by weight water;The coating, without the release of harmful organic substance, avoids infringement of the organic solvent to health using water as solvent, meets the requirement of environmental protection, and the smooth densification of paint film, antiseptic power and weatherability are strong, for a long time metal surface can be kept not to be corroded.
Description
Technical field
The present invention relates to anticorrosive paint technology field, more particularly to a kind of aqueous, environmental protective anticorrosive paint.
Background technology
Metal product is exposed in natural environment easily by the salt corrosion in moisture in air or seawater, and is damaged,
Shorten its service life;Anticorrosive paint be it is a kind of protect metal surfaces from air, seawater etc. chemistry or electrochemical corrosion
Coating, it is broadly divided into physical and chemically the major class of anticorrosive paint two, physical corrosion resistant coating leans on the appropriate cooperation of pigment and paint vehicle,
Fine and close paint film is formed to prevent the intrusion of corrosive substance;Chemically chemistry suppression rust effect of the corrosion resistant coating by rust resisting pigment.
The content of the invention
In view of in place of above-mentioned the deficiencies in the prior art, it is an object of the invention to provide a kind of aqueous, environmental protective anticorrosive paint,
Aim to solve the problem that metal product is easily corroded in natural environment in the prior art, and influence its service life technical problem.
In order to achieve the above object, this invention takes following technical scheme:
A kind of aqueous, environmental protective anticorrosive paint, include the composition of following parts by weight:
Aqueous acrylic modified epoxy emulsion 15-30 parts,
Acrylic emulsion 120-200 parts,
Silicone acrylic emulsion 30-50 parts,
Dispersant 0.1-1 parts,
Wetting agent 0.1-2 parts,
Defoamer 0.5-2 parts,
Antirust agent 50-120 parts,
Thickener 0-1 parts,
Coalescents 10-20 parts,
Water 200-500 parts.
Described aqueous, environmental protective anticorrosive paint, include the composition of following parts by weight:
Aqueous acrylic modified epoxy emulsion 18-30 parts,
Acrylic emulsion 150-200 parts,
Silicone acrylic emulsion 30-40 parts,
Dispersant 0.5-1 parts,
Wetting agent 0.5-2 parts,
Defoamer 0.5-1.8 parts,
Antirust agent 60-120 parts,
Thickener 0.2-1 parts,
Coalescents 12-20 parts,
Water 200-450 parts.
Described aqueous, environmental protective anticorrosive paint, include the composition of following parts by weight:
Aqueous acrylic modified 26 parts of epoxy emulsion,
180 parts of acrylic emulsion,
35 parts of silicone acrylic emulsion,
1 part of dispersant,
1.8 parts of wetting agent,
1.5 parts of defoamer,
100 parts of antirust agent,
0.6 part of thickener,
20 parts of coalescents,
310 parts of water.
Described aqueous, environmental protective anticorrosive paint also includes the pigment of 100-120 parts by weight.
In described aqueous, environmental protective anticorrosive paint, described pigment includes iron oxide red, natural iron oxide red, micaceous iron oxide, aluminium powder
With the one or more in graphite powder.
In described aqueous, environmental protective anticorrosive paint, described antirust agent is inositol hexaphosphate.
Beneficial effect:
The invention provides a kind of aqueous, environmental protective anticorrosive paint, the paint spraying can quickly form one layer of cause at metal surface
Close diaphragm, coating are uniformly dispersed, the smooth densification of paint film, and intensity is high, can reduce the transmission of water, oxygen and ion pair paint film
Degree, using water as solvent, without the release of harmful organic substance, avoids infringement of the organic solvent to health, meets environmental protection
Requirement, and antiseptic power and weatherability are strong, for a long time metal surface can be kept not to be corroded.
Embodiment
The present invention provides a kind of aqueous, environmental protective corrosion resistant coating, for make the purpose of the present invention, technical scheme and effect it is clearer,
Clearly, the present invention is described in more detail by the following examples.It should be appreciated that specific embodiment described herein only to
The present invention is explained, is not intended to limit the present invention.
The present invention provides a kind of aqueous, environmental protective anticorrosive paint, includes the composition of following parts by weight:
Aqueous acrylic modified epoxy emulsion 15-30 parts,
Acrylic emulsion 120-200 parts,
Silicone acrylic emulsion 30-50 parts,
Dispersant 0.1-1 parts,
Wetting agent 0.1-2 parts,
Defoamer 0.5-2 parts,
Antirust agent 50-120 parts,
Thickener 0-1 parts,
Coalescents 10-20 parts,
Water 200-500 parts.
Described aqueous, environmental protective anticorrosive paint, include the composition of following parts by weight:
Aqueous acrylic modified epoxy emulsion 18-30 parts,
Acrylic emulsion 150-200 parts,
Silicone acrylic emulsion 30-40 parts,
Dispersant 0.5-1 parts,
Wetting agent 0.5-2 parts,
Defoamer 0.5-1.8 parts,
Antirust agent 60-120 parts,
Thickener 0.2-1 parts,
Coalescents 12-20 parts,
Water 200-450 parts.
Described aqueous, environmental protective anticorrosive paint, include the composition of following parts by weight:
Aqueous acrylic modified 26 parts of epoxy emulsion,
180 parts of acrylic emulsion,
35 parts of silicone acrylic emulsion,
1 part of dispersant,
1.8 parts of wetting agent,
1.5 parts of defoamer,
100 parts of antirust agent,
0.6 part of thickener,
20 parts of coalescents,
310 parts of water.
Further, described aqueous, environmental protective anticorrosive paint also includes the pigment of 100-120 parts by weight.
Preferably, described pigment include iron oxide red, natural iron oxide red, micaceous iron oxide, aluminium powder and one kind in graphite powder or
It is a variety of.
Preferably, described antirust agent is inositol hexaphosphate.
In summary, the paint spraying can quickly form one layer of fine and close diaphragm at metal surface, and coating disperses
Uniformly, the smooth densification of paint film, intensity is high, can reduce the permeability of water, oxygen and ion pair paint film, using water as solvent, not have
The release of harmful organic substance, avoid infringement of the organic solvent to health, meet environmental protection requirement, and antiseptic power and
Weatherability is strong, for a long time metal surface can be kept not to be corroded.
Embodiment 1
Described aqueous, environmental protective anticorrosive paint, include the composition of following parts by weight:
Aqueous acrylic modified 16 parts of epoxy emulsion,
130 parts of acrylic emulsion,
48 parts of silicone acrylic emulsion,
0.2 part of dispersant,
2 parts of wetting agent,
0.6 part of defoamer,
60 parts of inositol hexaphosphate,
0.1 part of thickener,
20 parts of coalescents,
100 parts of iron oxide red,
400 parts of water.
Embodiment 2
Described aqueous, environmental protective anticorrosive paint, include the composition of following parts by weight:
Aqueous acrylic modified 20 parts of epoxy emulsion,
156 parts of acrylic emulsion,
42 parts of silicone acrylic emulsion,
0.4 part of dispersant,
1.5 parts of wetting agent,
1.2 parts of defoamer,
80 parts of inositol hexaphosphate,
0.3 part of thickener,
16 parts of coalescents,
120 parts of aluminium powder,
500 parts of water.
Embodiment 3
Described aqueous, environmental protective anticorrosive paint, include the composition of following parts by weight:
Aqueous acrylic modified 24 parts of epoxy emulsion,
180 parts of acrylic emulsion,
36 parts of silicone acrylic emulsion,
0.7 part of dispersant,
1.1 parts of wetting agent,
1.6 parts of defoamer,
100 parts of inositol hexaphosphate,
0.6 part of thickener,
14 parts of coalescents,
Natural iron oxide red 117 parts,
300 parts of water.
Embodiment 4
Described aqueous, environmental protective anticorrosive paint, include the composition of following parts by weight:
Aqueous acrylic modified 30 parts of epoxy emulsion,
198 parts of acrylic emulsion,
30 parts of silicone acrylic emulsion,
1 part of dispersant,
0.3 part of wetting agent,
1.9 parts of defoamer,
120 parts of inositol hexaphosphate,
0.9 part of thickener,
11 parts of coalescents,
113 parts of graphite,
200 parts of water.
It is understood that for those of ordinary skills, can be with technique according to the invention scheme and its hair
Bright design is subject to equivalent substitution or change, and all these changes or replacement should all belong to the guarantor of appended claims of the invention
Protect scope.
Claims (6)
1. a kind of aqueous, environmental protective anticorrosive paint, it is characterised in that include the composition of following parts by weight:
Aqueous acrylic modified epoxy emulsion 15-30 parts,
Acrylic emulsion 120-200 parts,
Silicone acrylic emulsion 30-50 parts,
Dispersant 0.1-1 parts,
Wetting agent 0.1-2 parts,
Defoamer 0.5-2 parts,
Antirust agent 50-120 parts,
Thickener 0-1 parts,
Coalescents 10-20 parts,
Water 200-500 parts.
2. aqueous, environmental protective anticorrosive paint according to claim 1, it is characterised in that include the composition of following parts by weight:
Aqueous acrylic modified epoxy emulsion 18-30 parts,
Acrylic emulsion 150-200 parts,
Silicone acrylic emulsion 30-40 parts,
Dispersant 0.5-1 parts,
Wetting agent 0.5-2 parts,
Defoamer 0.5-1.8 parts,
Antirust agent 60-120 parts,
Thickener 0.2-1 parts,
Coalescents 12-20 parts,
Water 200-450 parts.
3. aqueous, environmental protective anticorrosive paint according to claim 2, it is characterised in that include the composition of following parts by weight:
Aqueous acrylic modified 26 parts of epoxy emulsion,
180 parts of acrylic emulsion,
35 parts of silicone acrylic emulsion,
1 part of dispersant,
1.8 parts of wetting agent,
1.5 parts of defoamer,
100 parts of antirust agent,
0.6 part of thickener,
20 parts of coalescents,
310 parts of water.
4. according to the aqueous, environmental protective anticorrosive paint described in claim any one of 1-3, it is characterised in that described corrosion resistant coating also wraps
Include the pigment of 100-120 parts by weight.
5. aqueous, environmental protective anticorrosive paint according to claim 4, it is characterised in that described pigment includes iron oxide red, natural
One or more in iron oxide red, micaceous iron oxide, aluminium powder and graphite powder.
6. according to the aqueous, environmental protective anticorrosive paint described in claim any one of 1-3, it is characterised in that described antirust agent is flesh
The phosphate of alcohol six.