CN107840617A - A kind of fire-retardant materials for wall of high-strength insulation - Google Patents
A kind of fire-retardant materials for wall of high-strength insulation Download PDFInfo
- Publication number
- CN107840617A CN107840617A CN201711015994.4A CN201711015994A CN107840617A CN 107840617 A CN107840617 A CN 107840617A CN 201711015994 A CN201711015994 A CN 201711015994A CN 107840617 A CN107840617 A CN 107840617A
- Authority
- CN
- China
- Prior art keywords
- parts
- fire
- wall
- fibre
- materials
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The fire-retardant materials for wall of a kind of high-strength insulation provided by the invention, include the raw material of following parts by weight:6 ~ 10 parts of steel fibre, 3 ~ 5 parts of wood fibre, 3 ~ 5 parts of glass fibre, 3 ~ 5 parts of carbon fiber, 10 ~ 20 parts of crushed crude pearlite, 15 ~ 20 parts of flyash, 20 ~ 25 parts of portland cement, 25 ~ 30 parts of sludge, 4 ~ 6 parts of auxiliary agent, 2 ~ 6 parts of silicone powder, 15 ~ 25 parts of inorganic composite flame retardants, 0.5 ~ 1 part of coupling agent.The fire-retardant materials for wall of a kind of high-strength insulation provided by the invention uses inorganic compounding fire proofing as fire-retardant filler, and adds silicone powder and improve the fire-retardant impact strength of materials for wall, improves the fire resistance of materials for wall.Steel fibre, wood fibre, glass fibre, the intensity of fibre reinforced materials for wall are also added into simultaneously, obtains the high materials for wall of a kind of fire-retardant, high insulating effect, intensity.
Description
Technical field
The present invention relates to building material field, and in particular to a kind of fire-retardant materials for wall of high-strength insulation.
Background technology
With the fast development of industry, economic development is also quite rapid, and the whole world is also increasing to the demand of the energy,
In the total energy consumption increasingly increased, building energy consumption is especially big, accounts for the 11 ~ 25% of total energy consumption, substantial amounts of data and experiment
It is exactly to use heat insulating energy saving material all to show most fast most efficient method.
Now at home and abroad, there is the insulation material of many types.Classify by material, insulation material can be divided into three classes, gold
Belong to insulation material, organic insulation material, inorganic heat insulation material.Metal heat preservation material heat insulation effect is good, and fire resistance is good, but this
Kind material feedstock source is few, expensive, too high as cost for the insulation material of building, it is impossible to extensive use.Organic guarantor
Adiabator heat insulation effect is preferable, cheap, prepares simple, is the insulation material being most widely used at present, but organic heat-insulating
Material is inflammable, and easily produces toxic gas in high temperature, and easy to aging, service life is shorter, when fire occurs, often helps
Long fire spreading, produce more serious consequence.
With the rapid development of science and technology, architectural engineering has a great development, the investment of capital construction rise year by year, it is necessary to
There are the needs that more preferably buildings adapt to architectural engineering development from material, still, in construction material, some old materials
Exist in dead constructions work the amount of labour big, low production efficiency, capital construction cycle be long, building from it is great the shortcomings of, turn into building
The stumbling-block of engineering development.Thus, large panel building particularly light panel frame building system has a great development, novel building material
Expect it is large quantities of emerge in large numbers, effect of raisings one-level sound insulation etc. of the reduction of construction material deadweight, the enhancing of shock resistance, heat-insulating property is wanted
Seek also more and more higher.Its uneven, insufficient strength easy fracture that expands with heat and contract with cold of two existing materials for walls, heat insulating effect is not
It is good, it is therefore necessary to be further improved.
The content of the invention
For prior art, the invention aims to provide a kind of high-strength insulation fire-retardant materials for wall, the wall
Strength of materials height, good heat insulating, heat-proof combustion-resistant performance are superior, and employ sludge as filler, have saved resource, have reduced
Material cost, there is higher practical value and good application prospect.
In order to solve the above technical problems, the present invention provides a kind of fire-retardant materials for wall of high-strength insulation, the material includes
The raw material of following parts by weight:6 ~ 10 parts of steel fibre, 3 ~ 5 parts of wood fibre, 3 ~ 5 parts of glass fibre, 3 ~ 5 parts of carbon fiber, perlite
10 ~ 20 parts of powder, 15 ~ 20 parts of flyash, 20 ~ 25 parts of portland cement, 25 ~ 30 parts of sludge, 4 ~ 6 parts of auxiliary agent, 2 ~ 6 parts of silicone powder,
15 ~ 25 parts of inorganic composite flame retardants, 0.5 ~ 1 part of coupling agent.
The silicone powder can improve the fire-retardant impact strength of materials for wall, improve the fire resistance of materials for wall, simultaneously
Dispersant is also used as, auxiliary agent, steel fibre, wood fibre, glass fibre, carbon fiber is preferably dispersed in filler.
Further, the inorganic composite flame retardants include red phosphorus, antimony oxide, in magnesium hydroxide it is a kind of with it is ultra-fine
ATH.ATH is nontoxic, environment-friendly, recyclable to be recycled, can suppress smog, cheap, and can be used as filler, strengthens wall
The intensity of material.Ultra-fine ATH can improve the specific surface area of ATH particles, improve the anti-flammability of materials for wall and ATH fillibility,
At the same time it can also have the function that to strengthen materials for wall intensity.When ATH is used alone, its usage amount is larger to be can be only achieved well
Filling effect, be unfavorable for the addition of other functional stuffings.Add a small amount of red phosphorus or antimony oxide or magnesium hydroxide and ATH
Synergy, ATH flame retardant effect, while a large amount of additions for reducing ATH can be greatly increased.
The ultra-fine ATH granularities are less than 200nm.
The coupling agent includes vinyl silanes, titanate esters, alkylketene, acrylic acid isocyanates, phosphorous titanate
In one or more.
The auxiliary agent includes defoamer, stabilizer, water reducer, and its mass ratio is 0.5:3:1.5.
A kind of described fire-retardant materials for wall of high-strength insulation, include the raw material of following parts by weight:It is 8 parts of steel fibre, wooden
4 parts of fiber, 5 parts of glass fibre, 3 parts of carbon fiber, 15 parts of crushed crude pearlite, 20 parts of flyash, 25 parts of portland cement, sludge 25
Part, 0.5 part of defoamer, 3 parts of stabilizer, 1.5 parts of water reducer, 4 parts of silicone powder, ultra-fine ATH18 parts, 2 parts of antimony oxide, coupling
0.8 part of agent.
The preparation method of the fire-retardant materials for wall of high-strength insulation, comprises the following steps:
Step(1):Flyash is added in sludge and stirred, is then heated to 160 ~ 180 DEG C, is handled 6 ~ 7 hours, is dried
Afterwards, pulverize, it is standby to obtain filler for 200 ~ 300 mesh sieves excessively;
Step(2):After adding water to mix stabilizer, defoamer, water reducer, 40 ~ 50 DEG C are heated to, and use 250 ~ 350r/min
Rotating speed stirring make it well mixed after, it is standby to obtain mixed liquor;
Step(3):Coupling agent is heated to 150 ~ 180 DEG C, then stirring adds ultra-fine ATH in the case where rotating speed is 150 ~ 200r/min
Powder, continue to dry after heating stirring reacts 2 ~ 5h, grinding, cross 400 ~ 800 mesh sieves, obtain modified superfine ATH powder;
Step(4):Obtained after modified superfine ATH powder, antimony oxide or red phosphorus or magnesium hydroxide, silicone powder are well mixed
Flame-proof material is standby;
Step(5):Crushed crude pearlite, steel fibre, wood fibre, glass fibre, carbon fiber are added in batch mixer, are in rotating speed
50 ~ 60min is mixed under 100 ~ 200r/min, it is standby to obtain compound;
Step(6):Added in compound by step(1)In obtain filler, step(2)In the mixed liquor arrived, step(4)
In obtained flame-proof material and water, and be uniformly mixed, add portland cement, continue after being uniformly mixed, be sent into mould
In tool, shaping and drying maintenance, high-strength insulation fire proofing is obtained.
The fire-retardant materials for wall of a kind of high-strength insulation provided by the invention, has the advantages that:
(1)The fire-retardant materials for wall of a kind of high-strength insulation provided by the invention is filled out using inorganic compounding fire proofing as fire-retardant
Material, and add silicone powder and improve the fire-retardant impact strength of materials for wall, improve the fire resistance of materials for wall.It is also added into simultaneously
Steel fibre, wood fibre, glass fibre, the intensity of fibre reinforced materials for wall, obtain a kind of fire-retardant, high insulating effect, strong
Spend high materials for wall.
(2)The fire-retardant materials for wall of a kind of high-strength insulation provided by the invention uses ultra-fine ATH and antimony oxide or red
Phosphorus or magnesium hydroxide are modified as composite flame-proof material, and using coupling agent, greatly reduce ultra-fine ATH additions, and
Improve the flame retardant effect of materials for wall, obtain it is a kind of it is environment-friendly, smog can be suppressed, cheap high-strength insulation is fire-retardant
Materials for wall.
Embodiment
The present invention is further described below.
Embodiment 1:
A kind of described fire-retardant materials for wall of high-strength insulation, include the raw material of following parts by weight:6 parts of steel fibre, wood fibre 3
Part, 5 parts of glass fibre, 5 parts of carbon fiber, 10 parts of crushed crude pearlite, 20 parts of flyash, 20 parts of portland cement, 30 parts of sludge, defoaming
0.4 part of agent, 2.4 parts of stabilizer, 1.2 parts of water reducer, 2 parts of silicone powder, 22 parts of super fine magnesium hydroxide, 3 parts of antimony oxide, ethene
0.5 part of base silane.
The preparation method of the fire-retardant materials for wall of high-strength insulation, comprises the following steps:
Step(1):Flyash is added in sludge and stirred, is then heated to 160 ~ 180 DEG C, is handled 6 ~ 7 hours, is dried
Afterwards, pulverize, it is standby to obtain filler for 200 ~ 300 mesh sieves excessively;
Step(2):After adding water to mix stabilizer, defoamer, water reducer, 40 ~ 50 DEG C are heated to, and use 250 ~ 350r/min
Rotating speed stirring make it well mixed after, it is standby to obtain mixed liquor;
Step(3):Vinyl silanes are heated to 150 ~ 180 DEG C, then stirring addition is super in the case where rotating speed is 150 ~ 200r/min
Thin magnesium hydroxide powder, continue to dry after heating stirring reacts 2 ~ 5h, grinding, cross 400 ~ 800 mesh sieves, obtain modified superfine hydrogen-oxygen
Change magnesium dust;
Step(4):It is standby that flame-proof material is obtained after modified superfine magnesium hydroxide, antimony oxide, silicone powder are well mixed;
Step(5):Crushed crude pearlite, steel fibre, wood fibre, glass fibre, carbon fiber are added in batch mixer, are in rotating speed
50 ~ 60min is mixed under 100 ~ 200r/min, it is standby to obtain compound;
Step(6):Added in compound by step(1)In obtain filler, step(2)In the mixed liquor arrived, step(4)
In obtained flame-proof material and water, and be uniformly mixed, add portland cement, continue after being uniformly mixed, be sent into mould
In tool, shaping and drying maintenance, high-strength insulation fire proofing is obtained.
Embodiment 2:
A kind of described fire-retardant materials for wall of high-strength insulation, include the raw material of following parts by weight:10 parts of steel fibre, wood fibre
5 parts, 3 parts of glass fibre, 3 parts of carbon fiber, 20 parts of crushed crude pearlite, 15 parts of flyash, 25 parts of portland cement, 25 parts of sludge, disappear
0.6 part of infusion, 3.6 parts of stabilizer, 1.8 parts of water reducer, 6 parts of silicone powder, ultra-fine ATH14 parts, 1 part of red phosphorus, alkylketene 1
Part.
The preparation method of the fire-retardant materials for wall of high-strength insulation, comprises the following steps:
Step(1):Flyash is added in sludge and stirred, is then heated to 160 ~ 180 DEG C, is handled 6 ~ 7 hours, is dried
Afterwards, pulverize, it is standby to obtain filler for 200 ~ 300 mesh sieves excessively;
Step(2):After adding water to mix stabilizer, defoamer, water reducer, 40 ~ 50 DEG C are heated to, and use 250 ~ 350r/min
Rotating speed stirring make it well mixed after, it is standby to obtain mixed liquor;
Step(3):Alkylketene is heated to 150 ~ 180 DEG C, then stirring addition is super in the case where rotating speed is 150 ~ 200r/min
Thin ATH powder, continue to dry after heating stirring reacts 2 ~ 5h, grinding, cross 400 ~ 800 mesh sieves, obtain modified superfine ATH powder;
Step(4):It is standby that flame-proof material is obtained after modified superfine ATH powder, red phosphorus, silicone powder are well mixed;
Step(5):Crushed crude pearlite, steel fibre, wood fibre, glass fibre, carbon fiber are added in batch mixer, are in rotating speed
50 ~ 60min is mixed under 100 ~ 200r/min, it is standby to obtain compound;
Step(6):Added in compound by step(1)In obtain filler, step(2)In the mixed liquor arrived, step(4)
In obtained flame-proof material and water, and be uniformly mixed, add portland cement, continue after being uniformly mixed, be sent into mould
In tool, shaping and drying maintenance, high-strength insulation fire proofing is obtained.
Embodiment 3:
A kind of described fire-retardant materials for wall of high-strength insulation, include the raw material of following parts by weight:8 parts of steel fibre, wood fibre 4
Part, 5 parts of glass fibre, 3 parts of carbon fiber, 15 parts of crushed crude pearlite, 20 parts of flyash, 25 parts of portland cement, 25 parts of sludge, defoaming
0.5 part of agent, 3 parts of stabilizer, 1.5 parts of water reducer, 4 parts of silicone powder, ultra-fine ATH18 parts, 2 parts of antimony oxide, titanate esters 0.8
Part.
The preparation method of the fire-retardant materials for wall of high-strength insulation, comprises the following steps:
Step(1):Flyash is added in sludge and stirred, is then heated to 160 ~ 180 DEG C, is handled 6 ~ 7 hours, is dried
Afterwards, pulverize, it is standby to obtain filler for 200 ~ 300 mesh sieves excessively;
Step(2):After adding water to mix stabilizer, defoamer, water reducer, 40 ~ 50 DEG C are heated to, and use 250 ~ 350r/min
Rotating speed stirring make it well mixed after, it is standby to obtain mixed liquor;
Step(3):Titanate esters are heated to 150 ~ 180 DEG C, then stirring adds ultra-fine ATH in the case where rotating speed is 150 ~ 200r/min
Powder, continue to dry after heating stirring reacts 2 ~ 5h, grinding, cross 400 ~ 800 mesh sieves, obtain modified superfine ATH powder;
Step(4):It is standby that flame-proof material is obtained after modified superfine ATH powder, antimony oxide, silicone powder are well mixed;
Step(5):Crushed crude pearlite, steel fibre, wood fibre, glass fibre, carbon fiber are added in batch mixer, are in rotating speed
50 ~ 60min is mixed under 100 ~ 200r/min, it is standby to obtain compound;
Step(6):Added in compound by step(1)In obtain filler, step(2)In the mixed liquor arrived, step(4)
In obtained flame-proof material and water, and be uniformly mixed, add portland cement, continue after being uniformly mixed, be sent into mould
In tool, shaping and drying maintenance, high-strength insulation fire proofing is obtained.
The present invention is not limited to above-mentioned preferred forms, and anyone can show that other are various under the enlightenment of the present invention
The product of form, however, make any change in its shape or structure, it is every that there is skill identical or similar to the present application
Art scheme, is within the scope of the present invention.
Claims (6)
- A kind of 1. fire-retardant materials for wall of high-strength insulation, it is characterised in that:Include the raw material of following parts by weight:Steel fibre 6 ~ 10 Part, 3 ~ 5 parts of wood fibre, 3 ~ 5 parts of glass fibre, 3 ~ 5 parts of carbon fiber, 10 ~ 20 parts of crushed crude pearlite, 15 ~ 20 parts of flyash, silicic acid 20 ~ 25 parts of salt cement, 25 ~ 30 parts of sludge, 4 ~ 6 parts of auxiliary agent, 2 ~ 6 parts of silicone powder, 15 ~ 25 parts of inorganic composite flame retardants, coupling agent 0.5 ~ 1 part.
- A kind of 2. fire-retardant materials for wall of high-strength insulation according to claim 1, it is characterised in that:The inorganic compounding resistance Firing agent includes a kind of and ultra-fine ATH in red phosphorus, antimony oxide, magnesium hydroxide.
- A kind of 3. fire-retardant materials for wall of high-strength insulation according to claim 2, it is characterised in that:The ultra-fine ATH grains Degree is less than 200nm.
- A kind of 4. fire-retardant materials for wall of high-strength insulation according to claim 1, it is characterised in that:The coupling agent includes One or more in vinyl silanes, titanate esters, alkylketene, acrylic acid isocyanates, phosphorous titanate.
- A kind of 5. fire-retardant materials for wall of high-strength insulation according to claim 1, it is characterised in that:The auxiliary agent includes disappearing Infusion, stabilizer, water reducer, its mass ratio are 0.5:3:1.5.
- A kind of 6. fire-retardant materials for wall of high-strength insulation according to claim 5, it is characterised in that:Including following parts by weight Raw material:8 parts of steel fibre, 4 parts of wood fibre, 5 parts of glass fibre, 3 parts of carbon fiber, 15 parts of crushed crude pearlite, 20 parts of flyash, silicon 25 parts of acid salt cement, 25 parts of sludge, 0.5 part of defoamer, 3 parts of stabilizer, 1.5 parts of water reducer, 4 parts of silicone powder, ultra-fine ATH18 Part, 2 parts of antimony oxide, 0.8 part of coupling agent.