CN107825307A - A kind of preparation method of anti-blocking environmentally friendly sand paper - Google Patents
A kind of preparation method of anti-blocking environmentally friendly sand paper Download PDFInfo
- Publication number
- CN107825307A CN107825307A CN201711108974.1A CN201711108974A CN107825307A CN 107825307 A CN107825307 A CN 107825307A CN 201711108974 A CN201711108974 A CN 201711108974A CN 107825307 A CN107825307 A CN 107825307A
- Authority
- CN
- China
- Prior art keywords
- blocking
- dispersant
- preparation
- parts
- weight
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of preparation method of anti-blocking environmentally friendly sand paper, belongs to technology coated abrasive tool technical field.Characterized in that, preparation process is:Primer is applied on pretreated matrix, then plants sand;Grinding tool to be formed is after drying steps, then applies face glue, applies blocking preventing coating, and blocking preventing coating presses 200 g/m2~500g/m2Applied amounts coating;Cut to be molded again and produce;The preparation technology of blocking preventing coating is:Dispersant is added after being sufficiently stirred by water and wetting agent to be sufficiently stirred;Again plus bleeding agent is sufficiently stirred;Then hard hydrochlorate is added while stirring, stirring is abundant;Add adhesive and water is sufficiently stirred and produced.The solvent of the formula of the blocking preventing coating of the environmentally friendly sand paper is water, environmentally safe without any organic solvent, and operator's health is not influenceed.After the completion of coating formula is prepared, viscosity B coefficent is almost unchanged, in stable condition to waste.
Description
Technical field
A kind of preparation method of anti-blocking environmentally friendly sand paper, belongs to technology coated abrasive tool technical field.
Background technology
Existing sand paper coating formula is mostly solvent-borne type, and environmental pollution is serious.Sand paper coating generally uses stearic acid at present
Salt is main material mixture ratio, and stearate is white powder, not soluble in water, ethanol and ether, and is dissolved in toluene, benzene and turpentine oil
Deng organic solvent.But organic solvent environmental pollution is serious, operator's health is also endangered.Make stearic acid not soluble in water
Salt, coating is prepared without using organic solvent, its difficulty is very big.Existing sand paper coating formula organic solvent usage amount is big, easily
Volatilization, formula are unstable.For organic solvent in addition to environmental pollution is serious, its evaporation rate is very fast.Matched somebody with somebody with organic solvent
The sand paper coating formula of system, in coating process, because the volatilization viscosity B coefficent of organic solvent is very fast, formula is extremely unstable
It is fixed, cause largely to waste, preparing the desired stability for solving formula of sand paper coating using organic solvent can not possibly realize substantially.It is existing
There is the change of sand paper coating formula proportioning greatly, coating weight is uncontrollable.The state that stearate is dissolved in organic solvent is different, using having
Its proportioning of solvent preparation sand paper coating can not be completely the same, and the coating formula of same viscosity, the dosage of its organic solvent may
Due to the difference from hard hydrochlorate, difference is very big, so can not accurately control coating weight.Use different formulation ratios
Coating formula, it is unanimously extremely difficult for controlling coating weight.
The content of the invention
The technical problem to be solved in the present invention is:Overcome the deficiencies in the prior art, there is provided a kind of without using organic solvent, painting
The preparation method for the anti-blocking environmentally friendly sand paper that cloth amount is easily controlled.
The technical solution adopted for the present invention to solve the technical problems is:The preparation method of the anti-blocking environmentally friendly sand paper, it is special
Sign is that preparation process is:Primer is applied on pretreated matrix, then plants sand;Grinding tool to be formed after drying steps, then
Painting face glue, applies blocking preventing coating, and blocking preventing coating presses 200 g/m2~500g/m2Applied amounts coating;Cut to be molded again and produce;Described
The preparation technology of blocking preventing coating is:
1)First the wetting agent of the water of 50 ~ 80 parts by weight and 0.5 ~ 5 parts by weight is sufficiently stirred;
2)The dispersant for adding 0.5 ~ 5 parts by weight is sufficiently stirred;
3)The bleeding agent for adding 0.5 ~ 4 parts by weight is sufficiently stirred;
4)The hard hydrochlorate of 20 ~ 45 parts by weight is added while then proceeding to be kept stirring for, stirring is abundant;
5)Add the adhesive of 10 ~ 40 parts by weight and the water of 5 ~ 10 parts by weight is sufficiently stirred and produced;
Step 3)Described in bleeding agent pressed for non-ionic surface active AEO and APES
Mass ratio 10:43 ~ 63 mixing bleeding agent.
The blocking preventing coating that the blocking preventing coating of the present invention is prepared by special process of the present invention, which is coated with, to be formed, the formula of blocking preventing coating
It is the key technical feature that the present invention is achieved with order by merging.1st, it is water that the environmentally friendly blocking preventing coating, which is formulated its solvent, is not had
Any organic solvent, it is environmentally safe, operator's health is not influenceed.Water is used to prepare blocking preventing coating as solvent,
Mainly by step 1), step 2), step 3)To realize.
Step 1)The surface tension of water or interfacial tension are reduced by adding wetting agent, allows the water to be deployed in hard hydrochlorate
On surface, or hard hydrochlorate surface is penetrated, and hard hydrochlorate is soaked.
Step 2)By adding dispersant adsorption in the surface of stearate particle, make the stearate particle surface of cohesion
It is easy to moisten, dispersant can make stearate particle surface form bilayer structure, and outer layer dispersant polar end has with water
Compared with strong affinity, add the degree that stearate particle is spontaneously wet out by water, and make between stearate particle because of electrostatic repulsion and
It is remote, make system uniform, suspendability increase, do not precipitate, make whole system physico-chemical property the same.
Step 3)There is fabulous adhesive force on stearate by adding the specific bleeding agent of the present invention, by effectively oozing
Thoroughly, the effective composition with blocking preventing coating is had an effect, and makes each ingredient stability of recipe more preferable, it is more difficult layering and
Separate out.
2nd, after the completion of the formula of blocking preventing coating used is prepared, viscosity B coefficent is almost unchanged, in stable condition to waste.It is logical
Cross and replace organic solvent with water, non-volatile under normal condition so as to realize, viscosity does not change.
3rd, the formula of blocking preventing coating used is prepared according to identical proportioning and completed, and its viscosity will not differ too many, Ke Yijing
Really control coating formula solids content, so as to reach stable application dose-effect fruit.
Preferably, step 1)Described in wetting agent be anionic surfactant aliphatic acid or/and fatty acid ester sulphur
Hydrochlorate.Preferable wetting agent can preferably allow the water to be deployed on hard hydrochlorate surface compared to other wetting agents, or penetrate
Hard hydrochlorate surface.
More there are choosing, step 1)Described in wetting agent be aliphatic acid and fatty acid ester sulfate in mass ratio 23 ~ 37:8~
12 mixing wetting agent.The wetting agent of optimum ratio form can reach the synergy that the present invention most adapts to, and make hard hydrochlorate
Wetting reaches optimum efficiency.
Preferably, step 2)Described in dispersant disperse for anionic fatty acid dispersant, aliphatic amide type
Agent and/or lipid dispersion agent.Preferable dispersant can preferably be adsorbed in stearate particle compared to other wetting agents
Surface, the stearate particle surface of cohesion is set to be easier to moisten, effect is more preferably faster.
It is furthermore preferred that step 2)Described in dispersant be anionic fatty acid dispersant and aliphatic amide type point
The mixed dispersant of powder.Preferred dispersant can reach the synergy that the present invention adapts to, and make system more uniform,
Suspendability is more preferable.
It is further preferred that step 2)Described in dispersant be anionic fatty acid dispersant and aliphatic amide
Class dispersant in mass ratio 56 ~ 65:5 ~ 11 mixed dispersant.Most preferably dispersant proportioning of the invention, can reach optimal
Synergy, reach the optimal dispersion effect of the present invention.
Preferably, step 3)Described in bleeding agent gather for non-ionic surface active AEO and alkyl phenol
Oxygen ethene rice ether in mass ratio 10:53 ~ 58 mixing bleeding agent.Preferable bleeding agent adhesive force on stearate is best, makes
Each ingredient stability of recipe reaches the best condition of the present invention.
Preferably, step 4)Described in hard hydrochlorate be calcium stearate, magnesium stearate or zinc stearate.Various stearic acid
Salt can well adapt to present invention process, and environmentally friendly sand paper blocking preventing coating is made.
Preferably, described blocking preventing coating presses 300 g/m2~350g/m2Applied amounts be coated on matrix.It is preferable to apply
Amount can better ensure that the blocking-proof result of sand paper.
Compared with prior art, possessed beneficial effect of the invention is:The coating of the environmentally friendly sand paper of the present invention uses
Environmentally friendly blocking preventing coating prepared by a kind of special process, it is water that the environmentally friendly blocking preventing coating, which is formulated its solvent, without any organic solvent,
It is environmentally safe, operator's health is not influenceed.After the completion of the blocking preventing coating formula is prepared, viscosity B coefficent is almost unchanged,
It is in stable condition to waste.Organic solvent is replaced by using water, non-volatile under normal condition so as to realize, viscosity does not change.Should
Blocking preventing coating formula is prepared according to identical proportioning and completed, and its viscosity will not differ too many, can accurately control coating formula solid
Content, so as to reach stable application dose-effect fruit, so as to ensure the preparation of this sand paper and use that there is good environment protecting.
Embodiment
With reference to specific embodiment, the present invention will be further described, and wherein embodiment 1 is implemented to be optimal.
Embodiment 1
1)First the wetting agent of the water of 65 parts by weight and 2.5 parts by weight is sufficiently stirred;Wetting agent is anionic surfactant
Aliphatic acid and fatty acid ester sulfate in mass ratio 30:10 mixing wetting agent;
2)The dispersant for adding 2.5 parts by weight is sufficiently stirred;Dispersant is anionic fatty acid dispersant and aliphatic
Amide-type dispersant in mass ratio 60:8 mixed dispersant;
3)The bleeding agent for adding 2 parts by weight is sufficiently stirred;Bleeding agent be non-ionic surface active AEO and
APES in mass ratio 10:55 mixing bleeding agent;
4)Then the magnesium stearate of 33 parts by weight is added while stirring, stirring is abundant;
5)Add the adhesive of 25 parts by weight and the water of 8 parts by weight is sufficiently stirred and obtains blocking preventing coating;
6)Primer is applied on pretreated matrix, then plants sand;Grinding tool to be formed is after drying steps, then applies face glue, coats
The blocking preventing coating of step preparation is stated, blocking preventing coating presses 200 g/m2~500g/m2Applied amounts coating;Cut to be molded again and produce.
Embodiment 2
1)First the wetting agent of the water of 60 parts by weight and 3 parts by weight is sufficiently stirred;Wetting agent is anionic surfactant fat
Fat acid and fatty acid ester sulfate in mass ratio 25:11 mixing wetting agent;
2)The dispersant for adding 3 parts by weight is sufficiently stirred;Dispersant is anionic fatty acid dispersant and aliphatic acyl
Amine dispersant in mass ratio 58:6.5 mixed dispersant;
3)The bleeding agent for adding 1.5 parts by weight is sufficiently stirred;Bleeding agent is non-ionic surface active AEO
With APES in mass ratio 10:53 mixing bleeding agent;
4)Then the zinc stearate of 40 parts by weight is added while stirring, stirring is abundant;
5)Add the adhesive of 15 parts by weight and the water of 8 parts by weight is sufficiently stirred and obtains blocking preventing coating;
6)Primer is applied on pretreated matrix, then plants sand;Grinding tool to be formed is after drying steps, then applies face glue, coats
The blocking preventing coating of step preparation is stated, blocking preventing coating presses 200 g/m2~500g/m2Applied amounts coating;Cut to be molded again and produce.
Embodiment 3
1)First the wetting agent of the water of 70 parts by weight and 1.5 parts by weight is sufficiently stirred;Wetting agent is anionic surfactant
Aliphatic acid and fatty acid ester sulfate in mass ratio 33:9 mixing wetting agent;
2)The dispersant for adding 1.5 parts by weight is sufficiently stirred;Dispersant is anionic fatty acid dispersant and aliphatic
Amide-type dispersant in mass ratio 62:9.5 mixed dispersant;
3)The bleeding agent for adding 3 parts by weight is sufficiently stirred;Bleeding agent be non-ionic surface active AEO and
APES in mass ratio 10:58 mixing bleeding agent;;
4)Then the calcium stearate of 25 parts by weight is added while stirring, stirring is abundant;
5)Add the adhesive of 25 parts by weight and the water of 6 parts by weight is sufficiently stirred and obtains blocking preventing coating;
6)Primer is applied on pretreated matrix, then plants sand;Grinding tool to be formed is after drying steps, then applies face glue, coats
The blocking preventing coating of step preparation is stated, blocking preventing coating presses 200 g/m2~500g/m2Applied amounts coating;Cut to be molded again and produce.
Embodiment 4
1)First the wetting agent of the water of 50 parts by weight and 5 parts by weight is sufficiently stirred;Wetting agent is anionic surfactant fat
Fat acid and fatty acid ester sulfate in mass ratio 23:12 mixing wetting agent;
2)The dispersant for adding 0.5 parts by weight is sufficiently stirred;Dispersant is anionic fatty acid dispersant and aliphatic
Amide-type dispersant in mass ratio 56:11 mixed dispersant;
3)The bleeding agent for adding 4 parts by weight is sufficiently stirred;Bleeding agent be non-ionic surface active AEO and
APES in mass ratio 10:43 mixing bleeding agent;
4)Then the zinc stearate of 20 parts by weight is added while stirring, stirring is abundant;
5)Add the adhesive of 40 parts by weight and the water of 5 parts by weight is sufficiently stirred and obtains blocking preventing coating;
6)Primer is applied on pretreated matrix, then plants sand;Grinding tool to be formed is after drying steps, then applies face glue, coats
The blocking preventing coating of step preparation is stated, blocking preventing coating presses 350g/m2Applied amounts coating;Cut to be molded again and produce.
Embodiment 5
1)First the wetting agent of the water of 80 parts by weight and 0.5 parts by weight is sufficiently stirred;Wetting agent is anionic surfactant
Aliphatic acid and fatty acid ester sulfate;In mass ratio 37:8 mixing wetting agent;
2)The dispersant for adding 5 parts by weight is sufficiently stirred;Dispersant is anionic fatty acid dispersant and aliphatic acyl
Amine dispersant in mass ratio 65:11 mixed dispersant;
3)The bleeding agent for adding 0.5 parts by weight is sufficiently stirred;Bleeding agent is non-ionic surface active AEO
With APES in mass ratio 10:63 mixing bleeding agent;
4)Then the zinc stearate of 45 parts by weight is added while stirring, stirring is abundant;
5)Add the adhesive of 10 parts by weight and the water of 10 parts by weight is sufficiently stirred and obtains blocking preventing coating;
6)Primer is applied on pretreated matrix, then plants sand;Grinding tool to be formed is after drying steps, then applies face glue, coats
The blocking preventing coating of step preparation is stated, blocking preventing coating presses 400g/m2Applied amounts coating;Cut to be molded again and produce.
Embodiment 6
1)First the wetting agent of the water of 65 parts by weight and 2.5 parts by weight is sufficiently stirred;Wetting agent is anionic surfactant
Aliphatic acid;
2)The dispersant for adding 2.5 parts by weight is sufficiently stirred;Dispersant is anionic fatty acid dispersant and aliphatic
Amide-type dispersant in mass ratio 60:8 mixed dispersant;
3)The bleeding agent for adding 2 parts by weight is sufficiently stirred;Bleeding agent be non-ionic surface active AEO and
APES in mass ratio 10:55 mixing bleeding agent;
4)Then the magnesium stearate of 33 parts by weight is added while stirring, stirring is abundant;
5)Add the adhesive of 25 parts by weight and the water of 8 parts by weight is sufficiently stirred and obtains blocking preventing coating;
6)Primer is applied on pretreated matrix, then plants sand;Grinding tool to be formed is after drying steps, then applies face glue, coats
The blocking preventing coating of step preparation is stated, blocking preventing coating presses 300g/m2Applied amounts coating;Cut to be molded again and produce.
Embodiment 7
1)First the wetting agent of the water of 65 parts by weight and 2.5 parts by weight is sufficiently stirred;Wetting agent is anionic surfactant
Aliphatic acid and fatty acid ester sulfate in mass ratio 30:10 mixing wetting agent;
2)The dispersant for adding 2.5 parts by weight is sufficiently stirred;Dispersant is anionic fatty acid dispersant and aliphatic
Amide-type dispersant in mass ratio 30:30 mixed dispersant;
3)The bleeding agent for adding 2 parts by weight is sufficiently stirred;Bleeding agent be non-ionic surface active AEO and
APES in mass ratio 10:55 mixing bleeding agent;
4)Then the calcium stearate of 33 parts by weight is added while stirring, stirring is abundant;
5)Add the adhesive of 25 parts by weight and the water of 8 parts by weight is sufficiently stirred and obtains blocking preventing coating;
6)Primer is applied on pretreated matrix, then plants sand;Grinding tool to be formed is after drying steps, then applies face glue, coats
The blocking preventing coating of step preparation is stated, blocking preventing coating presses 500g/m2Applied amounts coating;Cut to be molded again and produce.
Embodiment 8
1)First the wetting agent of the water of 65 parts by weight and 2.5 parts by weight is sufficiently stirred;Wetting agent is anionic surfactant
Aliphatic acid and fatty acid ester sulfate in mass ratio 30:10 mixing wetting agent;
2)The dispersant for adding 2.5 parts by weight is sufficiently stirred;Dispersant is anionic fatty acid dispersant;
3)The bleeding agent for adding 2 parts by weight is sufficiently stirred;Bleeding agent be non-ionic surface active AEO and
APES in mass ratio 10:55 mixing bleeding agent;
4)Then the calcium stearate of 33 parts by weight is added while stirring, stirring is abundant;
5)Add the adhesive of 25 parts by weight and the water of 8 parts by weight is sufficiently stirred and obtains blocking preventing coating;
6)Primer is applied on pretreated matrix, then plants sand;Grinding tool to be formed is after drying steps, then applies face glue, coats
The blocking preventing coating of step preparation is stated, blocking preventing coating presses 200 g/m2Applied amounts coating;Cut to be molded again and produce.
Comparative example 1
Material proportion with embodiment 1, unlike, step 1)、2)、3)Order be changed to according to 3)、2)、1)Order perform behaviour
Make.
Blocking preventing coating performance test
1st, detection method is illustrated:
1)Dispersiveness test:30 parts of stearate is distributed to 70 parts of organic solvent, water, environmentally friendly blocking preventing coating formula respectively
In, stirring observes and records deployment conditions in 30 minutes.Decentralized standard is as follows:It is completely dispersed no bulky grain, is without stearate powder
One-level;It is two level that part, which is dispersed with stearic acid powder,;Small part is dispersed with stearate bulky grain and powder is three-level;Completely not
Scattered stearate and solution are separated into level Four.
2)Viscosity B coefficent is tested:30 parts of stearate is distributed to respectively in 70 parts of toluene and environmental protection formulae, be made into
Coating solution.Measure its temperature and viscosity.Ventilation is placed into, tests its viscosity B coefficent within every 30 minutes.
3)Identical proportioning viscosity test:30 parts of stearate is distributed to 70 parts of organic solvent and environmental protection formulae respectively
In, coating solution is made into, repeats to prepare ten parts of record viscosity.
2nd, test result:
The dispersion results of table 1 are with reference to detection method.
The dispersive property test result of table 1
。
The viscosity B coefficent of table 2 dispersion viscosity of the present invention does not change substantially, hence it is evident that better than organic solvent system, and contrasts
Example 1 can not normal use, can not measuring stability.
The viscosity B coefficent test result of table 2
。
Initial viscosity dispersion viscosity of the present invention is more or less the same under 3 identical proportioning of table, and organic solvent system difference is very big,
The present invention is substantially better than organic solvent dispersion system.
The identical proportioning initial viscosity test result of table 3
。
The grinding performance test of sand paper made from embodiment and comparative example:
A. reciprocating automatic grinding testing machine grinding:
Test equipment:Reciprocating automatic grinding testing machine
Method of testing:The aluminium bar that material is diameter 12mm is ground, grinding force 1kg, is ground time 15min, what record was ground every time
Removal amount;
B. sander free hand grinding is vibrated:
Test equipment:Shake sander
Method of testing:Sander free hand grinding is vibrated, grinding material is white oak plate, is ground time 5min*2.
C. automatic disc grinding test machine is ground:
Test equipment:Automatic disc grinding test machine
Method of testing:6 cun of 7 hole disk grinding, grinding material are plank, and grinding force 5.1kg is ground time 5min*3, and record is every
The removal amount of secondary grinding.
The grinding performance test result of sand paper made from embodiment and comparative example
A. reciprocating automatic grinding testing machine grinding:
。
B. sander free hand grinding is vibrated:
。
C. automatic disc grinding test machine is ground:
。
The above described is only a preferred embodiment of the present invention, being not the limitation for making other forms to the present invention, appoint
What those skilled in the art changed or be modified as possibly also with the technology contents of the disclosure above equivalent variations etc.
Imitate embodiment.But it is every without departing from technical solution of the present invention content, the technical spirit according to the present invention is to above example institute
Any simple modification, equivalent variations and the remodeling made, still fall within the protection domain of technical solution of the present invention.
Claims (9)
1. a kind of preparation method of anti-blocking environmentally friendly sand paper, it is characterised in that preparation process is:The linging on pretreated matrix
Glue, then plant sand;Grinding tool to be formed is after drying steps, then applies face glue, applies blocking preventing coating, and blocking preventing coating presses 200 g/m2~
500g/m2Applied amounts coating;Cut to be molded again and produce;The preparation technology of described blocking preventing coating is:
1)First the wetting agent of the water of 50 ~ 80 parts by weight and 0.5 ~ 5 parts by weight is sufficiently stirred;
2)The dispersant for adding 0.5 ~ 5 parts by weight is sufficiently stirred;
3)The bleeding agent for adding 0.5 ~ 4 parts by weight is sufficiently stirred;
4)The hard hydrochlorate of 20 ~ 45 parts by weight is added while then proceeding to be kept stirring for, stirring is abundant;
5)Add the adhesive of 10 ~ 40 parts by weight and the water of 5 ~ 10 parts by weight is sufficiently stirred and produced;
Step 3)Described in bleeding agent pressed for non-ionic surface active AEO and APES
Mass ratio 10:43 ~ 63 mixing bleeding agent.
A kind of 2. preparation method of anti-blocking environmentally friendly sand paper according to claim 1, it is characterised in that:Step 1)Described in
Wetting agent is anionic surfactant aliphatic acid or/and fatty acid ester sulfate.
A kind of 3. preparation method of anti-blocking environmentally friendly sand paper according to claim 1, it is characterised in that:Step 1)Described in
Wetting agent is aliphatic acid and fatty acid ester sulfate in mass ratio 23 ~ 37:8 ~ 12 mixing wetting agent.
A kind of 4. preparation method of anti-blocking environmentally friendly sand paper according to claim 1, it is characterised in that:Step 2)Described in
Dispersant is anionic fatty acid dispersant, aliphatic amide type dispersant and/or lipid dispersion agent.
A kind of 5. preparation method of anti-blocking environmentally friendly sand paper according to claim 1, it is characterised in that:Step 2)Described in
Dispersant is the mixed dispersant of anionic fatty acid dispersant and aliphatic amide type dispersant.
A kind of 6. preparation method of anti-blocking environmentally friendly sand paper according to claim 1, it is characterised in that:Step 2)Described in
Dispersant is anionic fatty acid dispersant and aliphatic amide type dispersant in mass ratio 56 ~ 65:5 ~ 11 mixing point
Powder.
A kind of 7. preparation method of anti-blocking environmentally friendly sand paper according to claim 1, it is characterised in that:Step 3)Described in
Bleeding agent is non-ionic surface active AEO and alkylphenol-polyethenoxy rice ether in mass ratio 10:53 ~ 58
Mix bleeding agent.
A kind of 8. preparation method of anti-blocking environmentally friendly sand paper according to claim 1, it is characterised in that:Step 4)Described in
Hard hydrochlorate is calcium stearate, magnesium stearate or zinc stearate.
A kind of 9. preparation method of anti-blocking environmentally friendly sand paper according to claim 1, it is characterised in that:Described blocking preventing coating
By 300 g/m2~350g/m2Applied amounts be coated on matrix.