CN107815773A - Anti-bacterial fibre cloth and preparation method thereof - Google Patents
Anti-bacterial fibre cloth and preparation method thereof Download PDFInfo
- Publication number
- CN107815773A CN107815773A CN201710917940.0A CN201710917940A CN107815773A CN 107815773 A CN107815773 A CN 107815773A CN 201710917940 A CN201710917940 A CN 201710917940A CN 107815773 A CN107815773 A CN 107815773A
- Authority
- CN
- China
- Prior art keywords
- parts
- fiber
- fibre cloth
- bacterial fibre
- reed
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of anti-bacterial fibre cloth, it is made up of each component of following parts by weight：7~10 parts of sisal fiber, 6~9 parts of tossa, 2~5 parts of abaca fibre, 8~12 parts of reed fiber, 3~6 parts of cocoanut fiber, 4~7 parts of viscose rayon, 10~13 parts of carbon fiber, 2~3 parts of polyacrylonitrile, 1~2 part of Rosemary Oil, 5~9 parts of tea tree ethereal oil, 3~7 parts of ice crystal, 4~8 parts of aloe, 11~14 parts of folium artemisiae argyi, 2~3 parts of soda ash, 3~9 parts of polyisobutene, 3~5 parts of glycerine, 2~4 parts of nano zine oxide, 0~6 part of cycloaliphatic epoxy resin, 15~22 parts of dimethylformamide.The invention further relates to the preparation method of the anti-bacterial fibre cloth, anti-bacterial fibre cloth obtained by it, with good antibacterial action, can eliminate because of bacterium and caused by peculiar smell, fabric is set to keep clean and tidy, the breeding of bacterium is avoided simultaneously, and playing reduces the risk propagated again, has wide market prospects.
Description
Technical field
The present invention relates to field of textiles, more particularly, to a kind of anti-bacterial fibre cloth and preparation method thereof.
Background technology
Fiber cloth fibre strength is high, toughness is strong, and the broken wadding of fiber will not be left in body surface substantially during use, and
Various soft flocks can also be adsorbed by the micro- electrostatic interaction of itself, and rely on advanced weaving technology and final finishing technology, make finished product
The fiber of fabric has the chrysanthemum flap section of standard and more layer structures, therefore possesses the features such as moisture absorption, ventilative, can be used for
Clothing, bedding etc. are made, there are wide market prospects.However, clothing etc. is more and human contact, as do not possess it is good
Antibacterial effect, then health can be had an impact, it is therefore desirable to which performance improvement is carried out to traditional cloths.
The content of the invention
It is an object of the invention to provide a kind of anti-bacterial fibre cloth.
It is a further object of the present invention to provide a kind of preparation method of the anti-bacterial fibre cloth.
The object of the invention is achieved by the following technical programs：
A kind of anti-bacterial fibre cloth is provided, is made up of each component of following parts by weight：7~10 parts of sisal fiber, tossa 6~
9 parts, 2~5 parts of abaca fibre, 8~12 parts of reed fiber, 3~6 parts of cocoanut fiber, 4~7 parts of viscose rayon, carbon fiber 10~13
Part, 2~3 parts of polyacrylonitrile, 1~2 part of Rosemary Oil, 5~9 parts of tea tree ethereal oil, 3~7 parts of ice crystal, 4~8 parts of aloe, Chinese mugwort
11~14 parts of leaf, 2~3 parts of soda ash, 3~9 parts of polyisobutene, 3~5 parts of glycerine, 2~4 parts of nano zine oxide, aliphatic ring oxygen tree
0~6 part of fat, 15~22 parts of dimethylformamide.
Preferably, the anti-bacterial fibre cloth is made up of each component of following parts by weight：8 parts of sisal fiber, tossa 8
Part, 4 parts of abaca fibre, 10 parts of reed fiber, 5 parts of cocoanut fiber, 6 parts of viscose rayon, 12 parts of carbon fiber, 2.5 parts of polyacrylonitrile,
1.5 parts of Rosemary Oil, 8 parts of tea tree ethereal oil, 6 parts of ice crystal, 7 parts of aloe, 12 parts of folium artemisiae argyi, 2.5 parts of soda ash, 5 parts of polyisobutene,
4 parts of glycerine, 3 parts of nano zine oxide, 4 parts of cycloaliphatic epoxy resin, 18 parts of dimethylformamide.
Present invention also offers the preparation method of the anti-bacterial fibre cloth, comprise the following steps：
S1. by aloe, the moisture content of folium artemisiae argyi cleaning, drying to 9~12%, sisal fiber, tossa, abaca fibre, reed are added
Reed fiber, cocoanut fiber, viscose rayon, carbon fiber, polyacrylonitrile and ice crystal, it is 120~250 kPa in pressure, temperature is
Mechanical Crushing, and grind into powder are carried out at 120~150 DEG C；
S2. 80~90 DEG C of 1~2 part of 25~32 parts of water and weak acid is added in powder obtained by step S1, stirs 5~8min, drop
Rosemary Oil and tea tree ethereal oil are added after to room temperature, stirs 20~30min, then heats to 95~100 DEG C, is added remaining former
Material, 130~150min is stirred, obtains spinning solution；
S3. after spinning solution filtering step S2 obtained, vacuum standing and defoaming 20~30min, Ran Houyong at 30~60 DEG C
Conventional wet spinning carries out spinning and post processing, obtains chemical fibre silk；
S4. chemical fibre silk weaving obtained by step S3 is made into cloth, obtains anti-bacterial fibre cloth.
Further, the weak acid described in step S2 is carbonic acid or hypochlorous acid.
Compared with prior art, the invention has the advantages that：
The invention provides a kind of anti-bacterial fibre cloth, has good antibacterial action, can eliminate because of bacterium and caused by peculiar smell,
Fabric is kept clean and tidy, while avoid the breeding of bacterium, playing reduces the risk propagated again, has wide market prospects.
Embodiment
With reference to specific embodiment, the present invention is further illustrated.
Embodiment 1
Present embodiment discloses a kind of anti-bacterial fibre cloth, it is made up of each component of following parts by weight：7 parts of sisal fiber, jute
9 parts of fiber, 2 parts of abaca fibre, 12 parts of reed fiber, 3 parts of cocoanut fiber, 7 parts of viscose rayon, 10 parts of carbon fiber, polyacrylonitrile 3
Part, 1 part of Rosemary Oil, 5 parts of tea tree ethereal oil, 7 parts of ice crystal, 4 parts of aloe, 11 parts of folium artemisiae argyi, 3 parts of soda ash, 3 parts of polyisobutene,
3 parts of glycerine, 2 parts of nano zine oxide, 22 parts of dimethylformamide.
Embodiment 2
Present embodiment discloses a kind of anti-bacterial fibre cloth, it is made up of each component of following parts by weight：10 parts of sisal fiber, jute
6 parts of fiber, 5 parts of abaca fibre, 8 parts of reed fiber, 6 parts of cocoanut fiber, 4 parts of viscose rayon, 13 parts of carbon fiber, polyacrylonitrile 2
Part, 2 parts of Rosemary Oil, 9 parts of tea tree ethereal oil, 3 parts of ice crystal, 8 parts of aloe, 14 parts of folium artemisiae argyi, 2 parts of soda ash, 9 parts of polyisobutene,
5 parts of glycerine, 4 parts of nano zine oxide, 6 parts of cycloaliphatic epoxy resin, 15 parts of dimethylformamide.
Embodiment 3
Present embodiment discloses a kind of anti-bacterial fibre cloth, it is made up of each component of following parts by weight：9 parts of sisal fiber, jute
7 parts of fiber, 3 parts of abaca fibre, 11 parts of reed fiber, 4 parts of cocoanut fiber, 5 parts of viscose rayon, 11 parts of carbon fiber, polyacrylonitrile
2.2 parts, 1.8 parts of Rosemary Oil, 7 parts of tea tree ethereal oil, 4 parts of ice crystal, 5 parts of aloe, 13 parts of folium artemisiae argyi, 2.2 parts of soda ash, poly- isobutyl
8 parts of alkene, 3.5 parts of glycerine, 2.8 parts of nano zine oxide, 2 parts of cycloaliphatic epoxy resin, 20 parts of dimethylformamide.
Embodiment 4
Present embodiment discloses a kind of anti-bacterial fibre cloth, it is made up of each component of following parts by weight：8 parts of sisal fiber, jute
8 parts of fiber, 4 parts of abaca fibre, 10 parts of reed fiber, 5 parts of cocoanut fiber, 6 parts of viscose rayon, 12 parts of carbon fiber, polyacrylonitrile
2.5 parts, 1.5 parts of Rosemary Oil, 8 parts of tea tree ethereal oil, 6 parts of ice crystal, 7 parts of aloe, 12 parts of folium artemisiae argyi, 2.5 parts of soda ash, poly- isobutyl
5 parts of alkene, 4 parts of glycerine, 3 parts of nano zine oxide, 4 parts of cycloaliphatic epoxy resin, 18 parts of dimethylformamide.
Embodiment 5
The components by weight percent of any embodiment of Example 1~4 prepares anti-bacterial fibre cloth, and preparation process is as follows：
S1. by aloe, the moisture content of folium artemisiae argyi cleaning, drying to 9%, it is fine that sisal fiber, tossa, abaca fibre, reed are added
Dimension, cocoanut fiber, viscose rayon, carbon fiber, polyacrylonitrile and ice crystal, it is 120 kPa in pressure, temperature is to enter at 150 DEG C
Row Mechanical Crushing, and grind into powder；
S2. 90 DEG C of 2 parts of 32 parts of water and weak acid is added in powder obtained by step S1, stirs 8min, fan is added after being down to room temperature
Repeatedly essential oil and tea tree ethereal oil, 20min is stirred, then heats to 100 DEG C, add remaining raw material, stirred 130min, spun
Silk stock solution；
S3. after spinning solution filtering step S2 obtained, the vacuum standing and defoaming 30min at 30 DEG C, the wet of routine is then used
Method spinning carries out spinning and post processing, obtains chemical fibre silk；
S4. chemical fibre silk weaving obtained by step S3 is made into cloth, obtains anti-bacterial fibre cloth.
Embodiment 6
The components by weight percent of any embodiment of Example 1~4 prepares anti-bacterial fibre cloth, and preparation process is as follows：
S1. by aloe, the moisture content of folium artemisiae argyi cleaning, drying to 12%, sisal fiber, tossa, abaca fibre, reed are added
Fiber, cocoanut fiber, viscose rayon, carbon fiber, polyacrylonitrile and ice crystal, it is 250 kPa in pressure, temperature is at 120 DEG C
Carry out Mechanical Crushing, and grind into powder；
S2. 80 DEG C of 1 part of 25 parts of water and weak acid is added in powder obtained by step S1, stirs 5min, fan is added after being down to room temperature
Repeatedly essential oil and tea tree ethereal oil, 30min is stirred, then heats to 95 DEG C, add remaining raw material, stirred 150min, spun
Silk stock solution；
S3. after spinning solution filtering step S2 obtained, the vacuum standing and defoaming 20min at 60 DEG C, the wet of routine is then used
Method spinning carries out spinning and post processing, obtains chemical fibre silk；
S4. chemical fibre silk weaving obtained by step S3 is made into cloth, obtains anti-bacterial fibre cloth.
Embodiment 7
The components by weight percent of any embodiment of Example 1~4 prepares anti-bacterial fibre cloth, and preparation process is as follows：
S1. by aloe, the moisture content of folium artemisiae argyi cleaning, drying to 10%, sisal fiber, tossa, abaca fibre, reed are added
Fiber, cocoanut fiber, viscose rayon, carbon fiber, polyacrylonitrile and ice crystal, it is 200 kPa in pressure, temperature is at 140 DEG C
Carry out Mechanical Crushing, and grind into powder；
S2. 88 DEG C of 1.5 parts of 30 parts of water and weak acid is added in powder obtained by step S1,6min is stirred, is added after being down to room temperature
Rosemary Oil and tea tree ethereal oil, 25min is stirred, then heats to 98 DEG C, add remaining raw material, stirred 140min, obtain
Spinning solution；
S3. after spinning solution filtering step S2 obtained, the vacuum standing and defoaming 25min at 50 DEG C, the wet of routine is then used
Method spinning carries out spinning and post processing, obtains chemical fibre silk；
S4. chemical fibre silk weaving obtained by step S3 is made into cloth, obtains anti-bacterial fibre cloth.
Claims (4)
1. a kind of anti-bacterial fibre cloth, it is characterised in that be made up of each component of following percentage by weight：7~10 parts of sisal fiber,
6~9 parts of tossa, 2~5 parts of abaca fibre, 8~12 parts of reed fiber, 3~6 parts of cocoanut fiber, 4~7 parts of viscose rayon,
10~13 parts of carbon fiber, 2~3 parts of polyacrylonitrile, 1~2 part of Rosemary Oil, 5~9 parts of tea tree ethereal oil, 3~7 parts of ice crystal, reed
4~8 parts of luxuriant growth, 11~14 parts of folium artemisiae argyi, 2~3 parts of soda ash, 3~9 parts of polyisobutene, 3~5 parts of glycerine, 2~4 parts of nano zine oxide,
0~6 part of cycloaliphatic epoxy resin, 15~22 parts of dimethylformamide.
2. anti-bacterial fibre cloth according to claim 1, it is characterised in that be made up of each component of following parts by weight：Sword
8 parts of flaxen fiber, 8 parts of tossa, 4 parts of abaca fibre, 10 parts of reed fiber, 5 parts of cocoanut fiber, 6 parts of viscose rayon, carbon fiber
12 parts, 2.5 parts of polyacrylonitrile, 1.5 parts of Rosemary Oil, 8 parts of tea tree ethereal oil, 6 parts of ice crystal, 7 parts of aloe, 12 parts of folium artemisiae argyi is pure
2.5 parts of alkali, 5 parts of polyisobutene, 4 parts of glycerine, 3 parts of nano zine oxide, 4 parts of cycloaliphatic epoxy resin, 18 parts of dimethylformamide.
3. the preparation method of anti-bacterial fibre cloth according to claim 1 or claim 2, it is characterised in that comprise the following steps：
S1. by aloe, the moisture content of folium artemisiae argyi cleaning, drying to 9~12%, sisal fiber, tossa, abaca fibre, reed are added
Reed fiber, cocoanut fiber, viscose rayon, carbon fiber, polyacrylonitrile and ice crystal, it is 120~250 kPa in pressure, temperature is
Mechanical Crushing, and grind into powder are carried out at 120~150 DEG C；
S2. 80~90 DEG C of 1~2 part of 25~32 parts of water and weak acid is added in powder obtained by step S1, stirs 5~8min, drop
Rosemary Oil and tea tree ethereal oil are added after to room temperature, stirs 20~30min, then heats to 95~100 DEG C, is added remaining former
Material, 130~150min is stirred, obtains spinning solution；
S3. after spinning solution filtering step S2 obtained, vacuum standing and defoaming 20~30min, Ran Houyong at 30~60 DEG C
Conventional wet spinning carries out spinning and post processing, obtains chemical fibre silk；
S4. chemical fibre silk weaving obtained by step S3 is made into cloth, obtains anti-bacterial fibre cloth.
4. according to the preparation method of the anti-bacterial fibre cloth of claim 1 or 3, it is characterised in that the weak acid described in step S2
For carbonic acid or hypochlorous acid.