CN107815022A - Stalk fibre laminated film and preparation method thereof - Google Patents
Stalk fibre laminated film and preparation method thereof Download PDFInfo
- Publication number
- CN107815022A CN107815022A CN201711142851.XA CN201711142851A CN107815022A CN 107815022 A CN107815022 A CN 107815022A CN 201711142851 A CN201711142851 A CN 201711142851A CN 107815022 A CN107815022 A CN 107815022A
- Authority
- CN
- China
- Prior art keywords
- stalk
- parts
- preparation
- laminated film
- hypochlorite
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of preparation method of stalk fibre laminated film, the preparation method includes:(1) stalk is crushed, be dispersed in water, oxidation processes are carried out in the presence of TEMPO (the piperidines N epoxides of 2,2,6,6 tetramethyl 1), hypochlorite, dried;(2) dried oxidation stalk, polyacrylate and organic solvent are mixed, is softened afterwards, obtain stalk mixture;(3) stalk mixture, polypropylene, citric acid, sodium dihydrogen phosphate, Tissuemat E, HBB and ethylene glycol are mixed, then precompressed, hot pressing and sanding are carried out, stalk fibre laminated film has been made, the laminated film not only has good tensile strength, also there is good gas permeability, be highly suitable for preparing the packaging material of fruits and vegetables.
Description
Technical field
The present invention relates to the preparation field of stalk material, in particular it relates to a kind of stalk fibre laminated film and its preparation
Method.
Background technology
Any packaging material includes plastic sheeting or edible film, and oxygen, nitrogen, carbon dioxide and water are steamed
The permeability measure of gas is particularly significant, and the packaging material particularly for preserving fruit and vegetable utilizing, its gas permeability is extremely important, because
Film with Suitable breathable, the physiological metabolism after fruits and vegetables could be obtained and play certain regulating and controlling effect, so as to improve fruit
The edible quality of vegetable, the frame goods life-span for extending fruits and vegetables, on the other hand, in order to obtain the material with fine air permeability, people are carried out
Extensive research.
Chinese patent application 201110203184.8 discloses composition and its preparation side of a kind of low Air permenbility ventilated membrane
Method, its component include:Polyolefin resin mixture, Air permenbility conditioning agent, surface be modified micro inorganic particle, antioxidant,
Lubricant and coupling agent.It the advantage is that the mechanical property of ventilated membrane can be improved by receiving micron inorganic filler, while surface is coupled
Modified inorganic particulate adds the compatibility with polyolefin base resin, but is disadvantageous in that high addition (30%-
55%) micron inorganic particulate can not be dispersed in matrix resin well, so as to have impact on the ventilative of thin-film material
Uniformity.
Chinese patent application 201110125458.6 discloses a kind of polyolefin film and preparation method thereof, its component bag
Include:Vistanex, pore former and extractant.It the advantage is that the structure of polypropylene/olefin film prepared by used conventional wet
It is small, quantity is more, but it uses the extraction process of two step high volume percentage concentration, and its extractant is N, N '-dimethyl formyl
Amine, dichloromethane, chloroform etc. belong to high pollution, toxic solvent, can cause huge injury to human body and environment.
Chinese patent application 201710110501.9 discloses a kind of gas permeability laminated film and preparation method thereof, and this is compound
Film is prepared by the component of following percentage by weight:60%-82% vistanex polymer, 2%-8% is micro-nano
Crystalline cellulose particle, 0.4%-1% antioxidant, 15%-30% dispersants, 0.1%-0.5% lubricants, 0.2%-1% couplings
Agent.Its preparation method is as follows:Micro nanocrystalline cellulose aqueous dispersions and coupling agent are uniformly dispersed;It is equal to add dispersant
Even and dry pretreated filler;Resulting pretreated filler, vistanex, antioxidant, lubricant are added to double spiral shells
In bar extruder, by melting extrusion, cooling and gas permeability laminated film constituent is granulated to obtain, hot calender prepares flat film;
Immerse in cleaning agent, ultrasound, dry again;Biaxial tension simultaneously carries out thermal finalization processing, obtains gas permeability laminated film.The laminated film
Permeability is efficient, good mechanical performance.Shortcoming is to need to immerse in cleaning agent, and processing procedure is cumbersome.
Rationally, efficiently using agricultural straw resource, turn waste into wealth, production environment friendly materials turn into the world focus
Problem.China is a large agricultural country, and rice, wheat, corn, cotton etc. is main variety of crops.China's crops straw
Stalk annual production arranges No. 1 in the world up to 700,000,000 tons.At present, these agricultural crop straws rich in cellulose mainly have following processing side
Formula, but all Shortcomings:1st, the waste treatment such as landfill, burning, not only without efficent use of resources, and in combustion can
Substantial amounts of carbon dioxide is discharged, pollutes environment;2nd, preparing fuel ethanol, conversion ratio is low, and cost is high;3rd, combustion power generation, added value are low.
Therefore, stalk efficiently also needed to using problem it is widely studied.Using original of the stalk as some laminated films such as density board
Material, can not only turn waste into wealth, and can efficent use of resources, currently with stalk be laminated film made from raw material also deposit
Mechanical strength is relatively low the problem of, but the tensile strength of stalk compound material is often improved, its gas permeability is undesirable, no
It can realize and be used as vegetable and fruit packaging materials'use.
Therefore it provides a kind of mechanical strength is higher, while stalk fibre laminated film of good permeability and preparation method thereof
The problem of being urgent need to resolve of the present invention.
The content of the invention
It is an object of the invention to provide a kind of stalk fibre laminated film and preparation method thereof, solve currently with stalk
The problem of overcoming mechanical strength and incompatible gas permeability for laminated film made from raw material, stalk fibre prepared by the present invention
Laminated film not only has preferable tensile strength, and also with good gas permeability, and preparation method is simple, it is easy to accomplish.
To achieve these goals, the invention provides a kind of preparation method of stalk fibre laminated film, the preparation
Method includes:(1) stalk is crushed, be dispersed in water, in TEMPO (2,2,6,6- tetramethyl -1- piperidines-N- epoxides), secondary chlorine
Oxidation processes are carried out in the presence of hydrochlorate, are dried;(2) by dried oxidation stalk, polyacrylate and organic solvent
Mixed, softened afterwards, obtain stalk mixture;(3) by stalk mixture, polypropylene, citric acid, biphosphate
Sodium, Tissuemat E, HBB and ethylene glycol mixing, then carry out precompressed, hot pressing and sanding.
Present invention also offers a kind of stalk fibre laminated film, the stalk fibre laminated film is by above-mentioned preparation side
Method is made.
Pass through above-mentioned technical proposal, the invention provides a kind of stalk fibre laminated film and preparation method thereof, the system
Preparation Method includes:(1) stalk is crushed, be dispersed in water, in TEMPO (2,2,6,6- tetramethyl -1- piperidines-N- epoxides), secondary
Oxidation processes are carried out in the presence of chlorate, are dried;(2) by dried oxidation stalk, polyacrylate and organic molten
Agent is mixed, and is softened afterwards, obtains stalk mixture;(3) by stalk mixture, polypropylene, citric acid, biphosphate
Sodium, Tissuemat E, HBB and ethylene glycol mixing, then carry out precompressed, hot pressing and sanding.I.e. by aoxidizing, softening by stalk
Mixed with the polypropylene matrix for preparing laminated film, stalk fibre laminated film has been made, the laminated film not only has good
Tensile strength, also with good gas permeability, be highly suitable for preparing the packaging material of fruits and vegetables.
Other features and advantages of the present invention will be described in detail in subsequent specific embodiment part.
Embodiment
The embodiment of the present invention is described in detail below.It is it should be appreciated that described herein specific
Embodiment is merely to illustrate and explain the present invention, and is not intended to limit the invention.
The end points of disclosed scope and any value are not limited to the accurate scope or value herein, these scopes or
Value should be understood to comprising the value close to these scopes or value.For number range, between the endpoint value of each scope, respectively
It can be combined with each other between the endpoint value of individual scope and single point value, and individually between point value and obtain one or more
New number range, these number ranges should be considered as specific open herein.
The invention provides a kind of preparation method of stalk fibre laminated film, the preparation method includes:(1) by stalk
Crush, be dispersed in water, enter in the presence of TEMPO (2,2,6,6- tetramethyl -1- piperidines-N- epoxides), hypochlorite
Row oxidation processes, dry;(2) dried oxidation stalk, polyacrylate and organic solvent are mixed, carried out afterwards soft
Change, obtain stalk mixture;(3) by stalk mixture, polypropylene, citric acid, sodium dihydrogen phosphate, Tissuemat E, HBB and
Ethylene glycol mixes, and then carries out precompressed, hot pressing and sanding.
Pass through above-mentioned technical proposal, the invention provides a kind of stalk fibre laminated film and preparation method thereof, the system
Preparation Method includes:(1) stalk is crushed, be dispersed in water, in TEMPO (2,2,6,6- tetramethyl -1- piperidines-N- epoxides), secondary
Oxidation processes are carried out in the presence of chlorate, are dried;(2) by dried oxidation stalk, polyacrylate and organic molten
Agent is mixed, and is softened afterwards, obtains stalk mixture;(3) by stalk mixture, polypropylene, citric acid, biphosphate
Sodium, Tissuemat E, HBB and ethylene glycol mixing, then carry out precompressed, hot pressing and sanding.I.e. by aoxidizing, softening by stalk
Mixed with the polypropylene matrix for preparing laminated film, stalk fibre laminated film has been made, the laminated film not only has good
Tensile strength, also with good gas permeability, be highly suitable for preparing the packaging material of fruits and vegetables.
In a kind of preferred embodiment of the present invention, in order to further improve obtained stalk fibre laminated film
Tensile strength and gas permeability, the stalk of crushing, water, the mass ratio of TEMPO and hypochlorite are 20:50-100:5-7:3-4.
In a kind of preferred embodiment of the present invention, in order to further improve obtained stalk fibre laminated film
Tensile strength and gas permeability, the stalk of crushing, water, the mass ratio of TEMPO and hypochlorite are 20:50-100:5-7:3-4.
In a kind of preferred embodiment of the present invention, in order to further improve obtained stalk fibre laminated film
Tensile strength and gas permeability, the condition of oxidation processes include:PH is 12-14, and processing time 1-2h, temperature is 40-70 DEG C.
In a kind of preferred embodiment of the present invention, in order to further improve obtained stalk fibre laminated film
Tensile strength and gas permeability, in step (2), the condition of mixing includes:Temperature is 50-70 DEG C, time 20-30min.
In a kind of preferred embodiment of the present invention, in order to further improve obtained stalk fibre laminated film
Tensile strength and gas permeability, the condition of softening include:Temperature is 80-95 DEG C, time 15-25min.
In a kind of preferred embodiment of the present invention, in order to further improve obtained stalk fibre laminated film
Tensile strength and gas permeability, in step (3), the condition of precompressed includes:Pressure is 2.5-3.5MPa, and temperature is 140-160 DEG C.
In a kind of preferred embodiment of the present invention, in order to further improve obtained stalk fibre laminated film
Tensile strength and gas permeability, the condition of hot pressing include:Pressure is 40-60MPa, and temperature is 170-190 DEG C.
In a kind of preferred embodiment of the present invention, in order to further improve obtained stalk fibre laminated film
Tensile strength and gas permeability, the condition of sanding comprise at least:The time of sanding is 20-30min.
In a kind of preferred embodiment of the present invention, in order to further improve obtained stalk fibre laminated film
Tensile strength and gas permeability, in parts by weight, dried oxidation stalk 40-50 parts, polyacrylate 10-20 parts, You Jirong
Agent 15-25 parts, polypropylene 60-80 parts, citric acid 8-10 parts, sodium dihydrogen phosphate 6-8 parts, Tissuemat E 3-5 parts, HBB 8-10
Part and ethylene glycol 3-5 parts.
In a kind of preferred embodiment of the present invention, in order to further improve obtained stalk fibre laminated film
Tensile strength and gas permeability, wherein, the weight average molecular weight of polyacrylate is 5000-7000, the weight average molecular weight of Tissuemat E
For 7000-8000, polyacrylic weight average molecular weight is 10000-30000.
In a kind of preferred embodiment of the present invention, in order to further improve obtained stalk fibre laminated film
Tensile strength and gas permeability, stalk in wheat stalk, broomcorn straw, cotton stalk, maize straw and rice straw one
Kind is a variety of.
In a kind of preferred embodiment of the present invention, in order to further improve obtained stalk fibre laminated film
Tensile strength and gas permeability, in step (1), the length of the stalk after crushing is not more than 2cm.
In a kind of preferred embodiment of the present invention, in order to further improve obtained stalk fibre laminated film
Tensile strength and gas permeability, hypochlorite are the one or more in postassium hypochlorite, sodium hypochlorite and calcium hypochlorite.
In a kind of preferred embodiment of the present invention, in order to further improve obtained stalk fibre laminated film
Tensile strength and gas permeability, organic solvent are the one or more in methanol, ethanol, tetrahydrofuran, ethylene glycol, glycerine.
Present invention also offers a kind of stalk fibre laminated film, the stalk fibre laminated film is by above-mentioned preparation side
Method is made.The laminated film not only has good tensile strength, also with good gas permeability, is highly suitable for preparing fruits and vegetables
Packaging material.
The present invention will be described in detail by way of examples below.In following examples, polyacrylate is divided equally again
Son amount is 5000-7000, and the weight average molecular weight of Tissuemat E is 7000-8000;Polyacrylic weight average molecular weight is 10000-
30000。
Following tensile strength parameter is measured by GB1040-2006 method;OTR oxygen transmission rate (unit mL/m2,
My god, standard atmospheric pressure) test is measured using the OTR oxygen transmission rate tester of model 8001, and corresponding standard is GB/
T1038-2000 plastic sheetings and thin slice gas-premeable test method;Moisture-vapor transmission (unit mL/m2) test use
The water vapor permeation rate testers of model Model 3/33 are detected, and corresponding standard is GB/T 30412-2013 plastic sheetings
With the measure of thin slice moisture-vapor transmission.
Preparation example 1
In parts by weight, 20 parts of stalks are crushed into (length of the stalk after crushing is not more than 2cm), is scattered in 50 parts of water
In, add TEMPO 5 parts of (2,2,6,6- tetramethyl -1- piperidines-N- epoxides), 3 parts of hypochlorite carry out oxidation processes (pH 12,
Processing time is 2h, and temperature is 70 DEG C), wherein, it is used as pH adjusting agent by the use of sodium hydroxide, drying after oxidation processes.
Preparation example 2
In parts by weight, 20 parts of stalks are crushed into (length of the stalk after crushing is not more than 2cm), is scattered in 100 parts of water
In, add TEMPO 7 parts of (2,2,6,6- tetramethyl -1- piperidines-N- epoxides), 4 parts of hypochlorite carry out oxidation processes (pH 14,
Processing time is 1h, and temperature is 40 DEG C), wherein, it is used as pH adjusting agent by the use of sodium hydroxide, drying after oxidation processes.
Preparation example 3
In parts by weight, 20 parts of stalks are crushed into (length of the stalk after crushing is not more than 2cm), is scattered in 75 parts of water
In, add TEMPO 6 parts of (2,2,6,6- tetramethyl -1- piperidines-N- epoxides), 3.5 parts of hypochlorite carries out oxidation processes (pH is
13, processing time 1.5h, temperature are 55 DEG C), wherein, pH adjusting agent is used as by the use of sodium hydroxide, drying after oxidation processes.
Preparation example 4
In parts by weight, 20 parts of stalks are crushed into (length of the stalk after crushing is not more than 2cm), is scattered in 75 parts of water
In, add TEMPO 10 parts of (2,2,6,6- tetramethyl -1- piperidines-N- epoxides), 10 parts of hypochlorite carries out oxidation processes (pH is
13, processing time 1.5h, temperature are 55 DEG C), wherein, pH adjusting agent is used as by the use of sodium hydroxide, drying after oxidation processes.
Preparation example 5
In parts by weight, 20 parts of stalks are crushed into (length of the stalk after crushing is not more than 2cm), is scattered in 75 parts of water
In, add TEMPO 3 parts of (2,2,6,6- tetramethyl -1- piperidines-N- epoxides), 2 parts of hypochlorite carry out oxidation processes (pH 13,
Processing time is 1.5h, and temperature is 55 DEG C), wherein, it is used as pH adjusting agent by the use of sodium hydroxide, drying after oxidation processes.
Embodiment 1
In parts by weight, 40 parts of the dried oxidation stalk that will be prepared in preparation example 1,10 parts of polyacrylate and ethanol
15 parts carry out mixing 30min in 70 DEG C, carry out softening 25min after 95 DEG C, obtain stalk mixture;Then polypropylene is added
60 parts, 8 parts of citric acid, 6 parts of sodium dihydrogen phosphate, 3 parts of Tissuemat E, the 3 parts of mixing of 8 parts of HBB and ethylene glycol, then carry out pre-
Pressure, preload pressure 3.5MPa, temperature are 160 DEG C, are then 60MPa in pressure, temperature carries out heat under conditions of being 190 DEG C
Pressure, last sanding 30min.
The tensile strength of obtained stalk fibre laminated film is 17.4MPa, OTR oxygen transmission rate 1775mL/m2, water steaming
Vapor permeability is 6.4mL/m2。
Embodiment 2
In parts by weight, 50 parts of the dried oxidation stalk that will be prepared in preparation example 2,20 parts of polyacrylate and ethanol
25 parts carry out mixing 20min in 50 DEG C, carry out softening 15min after 80 DEG C, obtain stalk mixture;Then polypropylene is added
80 parts, 10 parts of citric acid, 8 parts of sodium dihydrogen phosphate, 5 parts of Tissuemat E, the 5 parts of mixing of 10 parts of HBB and ethylene glycol, then carry out
Precompressed, preload pressure 2.5MPa, temperature are 140 DEG C, are then 40MPa in pressure, temperature carries out heat under conditions of being 170 DEG C
Pressure, last sanding 20min.
The tensile strength of obtained stalk fibre laminated film is 17.9MPa, OTR oxygen transmission rate 1820mL/m2, water steaming
Vapor permeability is 6.7mL/m2。
Embodiment 3
In parts by weight, 45 parts of the dried oxidation stalk that will be prepared in preparation example 3,15 parts of polyacrylate and ethanol
20 parts carry out mixing 25min in 60 DEG C, carry out softening 20min after 88 DEG C, obtain stalk mixture;Then polypropylene is added
70 parts, 9 parts of citric acid, 7 parts of sodium dihydrogen phosphate, 4 parts of Tissuemat E, the 4 parts of mixing of 9 parts of HBB and ethylene glycol, then carry out pre-
Pressure, preload pressure 3MPa, temperature are 150 DEG C, are then 50MPa in pressure, and temperature carries out hot pressing under conditions of being 180 DEG C,
Last sanding 25min.The tensile strength of obtained stalk fibre laminated film is 18.5MPa, OTR oxygen transmission rate 1844mL/
m2, moisture-vapor transmission 6.8mL/m2。
Embodiment 4
Stalk fibre laminated film is prepared according to the preparation method in embodiment 3, unlike, it will be prepared in preparation example 3
Dried oxidation stalk be changed to " the dried oxidation stalk prepared in preparation example 4 ".Obtained stalk fibre is compound
The tensile strength of film is 18.1MPa, OTR oxygen transmission rate 1615mL/m2, moisture-vapor transmission 5.8mL/m2。
Embodiment 5
Stalk fibre laminated film is prepared according to the preparation method in embodiment 3, unlike, it will be prepared in preparation example 3
Dried oxidation stalk be changed to " the dried oxidation stalk prepared in preparation example 5 ".Obtained stalk fibre is compound
The tensile strength of film is 16.8MPa, OTR oxygen transmission rate 1726mL/m2, moisture-vapor transmission 5.4mL/m2。
Embodiment 6
Stalk fibre laminated film is prepared according to the preparation method in embodiment 3, unlike, precompressed, hot pressing and sanding
Condition be:Preload pressure is 2MPa, and temperature is 160 DEG C, and then pressure is 30MPa, and temperature carries out heat under conditions of being 190 DEG C
Pressure and sanding 30min.The tensile strength of obtained stalk fibre laminated film is 17.1MPa, OTR oxygen transmission rate 1745mL/
m2, moisture-vapor transmission 8.2mL/m2。
Embodiment 7
Stalk fibre laminated film is prepared according to the preparation method in embodiment 3, unlike, soft condition is:Temperature
Softening 30min is carried out for 100 DEG C.The tensile strength of obtained stalk fibre laminated film is 17.6MPa, and OTR oxygen transmission rate is
1723mL/m2, moisture-vapor transmission 8.3mL/m2。
The preferred embodiment of the present invention described in detail above, still, the present invention are not limited in above-mentioned embodiment
Detail, in the range of the technology design of the present invention, a variety of simple variants can be carried out to technical scheme, this
A little simple variants belong to protection scope of the present invention.
It is further to note that each particular technique feature described in above-mentioned embodiment, in not lance
In the case of shield, can be combined by any suitable means, in order to avoid unnecessary repetition, the present invention to it is various can
The combination of energy no longer separately illustrates.
In addition, various embodiments of the present invention can be combined randomly, as long as it is without prejudice to originally
The thought of invention, it should equally be considered as content disclosed in this invention.
Claims (10)
1. a kind of preparation method of stalk fibre laminated film, it is characterised in that the preparation method includes:
(1) stalk is crushed, be dispersed in water, deposited in TEMPO (2,2,6,6- tetramethyl -1- piperidines-N- epoxides), hypochlorite
Oxidation processes are carried out in case, are dried;
(2) dried oxidation stalk, polyacrylate and organic solvent are mixed, is softened afterwards, obtain stalk
Mixture;
(3) stalk mixture, polypropylene, citric acid, sodium dihydrogen phosphate, Tissuemat E, HBB and ethylene glycol are mixed, then
Carry out precompressed, hot pressing and sanding.
2. preparation method according to claim 1, wherein, the stalk of crushing, water, TEMPO and hypochlorite quality it
Than for 20:50-100:5-7:3-4.
3. preparation method according to claim 2, wherein, the condition of oxidation processes includes:PH is 12-14, processing time
For 1-2h, temperature is 40-70 DEG C.
4. preparation method according to claim 1, wherein, in step (2), the condition of mixing includes:Temperature is 50-70
DEG C, time 20-30min;And/or
The condition of softening includes:Temperature is 80-95 DEG C, time 15-25min.
5. preparation method according to claim 1, wherein, in step (3), the condition of precompressed includes:Pressure is 2.5-
3.5MPa, temperature are 140-160 DEG C.
6. preparation method according to claim 1, wherein, the condition of hot pressing includes:Pressure is 40-60MPa, and temperature is
170-190℃;
And/or the condition of sanding comprises at least:The time of sanding is 20-30min.
7. preparation method according to claim 1, wherein, in parts by weight, dried oxidation stalk 40-50 parts, gather
Acrylate 10-20 parts, organic solvent 15-25 parts, polypropylene 60-80 parts, citric acid 8-10 parts, sodium dihydrogen phosphate 6-8 parts, gather
Ethylene waxes 3-5 parts, HBB 8-10 parts and ethylene glycol 3-5 parts.
8. preparation method according to claim 7, wherein, the weight average molecular weight of polyacrylate is 5000-7000, poly- second
The weight average molecular weight of alkene wax is 7000-8000, and polyacrylic weight average molecular weight is 10000-30000.
9. preparation method according to claim 1, wherein, stalk is selected from wheat stalk, broomcorn straw, cotton stalk, jade
One or more in rice stalk and rice straw;
And/or in step (1), the length of the stalk after crushing is not more than 2cm;
And/or hypochlorite is the one or more in postassium hypochlorite, sodium hypochlorite and calcium hypochlorite;
And/or organic solvent is the one or more in methanol, ethanol, tetrahydrofuran, ethylene glycol, glycerine.
10. the stalk fibre laminated film that the preparation method in a kind of 1-9 according to claim described in any one is prepared.