CN107805849A - Silk cocoon reels off raw silk from cocoons method - Google Patents
Silk cocoon reels off raw silk from cocoons method Download PDFInfo
- Publication number
- CN107805849A CN107805849A CN201711206237.5A CN201711206237A CN107805849A CN 107805849 A CN107805849 A CN 107805849A CN 201711206237 A CN201711206237 A CN 201711206237A CN 107805849 A CN107805849 A CN 107805849A
- Authority
- CN
- China
- Prior art keywords
- silk
- silk cocoon
- cocoons
- cocoon
- steaming
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
Reeled off raw silk from cocoons method the invention discloses a kind of silk cocoon, be related to textile technology field, this silk cocoon method of reeling off raw silk from cocoons comprises the following steps：Silk cocoon is put into stirring pool first, first pours into white wine, is then stirred while being put into sodium bicarbonate and alum, stirring is cleaned after 10~15 minutes with clear water；Then silk cocoon is put into steaming room and carries out steaming, steaming temperature is 60~70 DEG C, a length of 50~60 minutes during steaming；Then silk cocoon is put into dryer and dried, drying temperature is 55~65 DEG C, and drying time period is 15~20 minutes；Finally silk cocoon is put into hot water storgae, reeled off raw silk from cocoons with silk cocoon is carried out in reeling machine.Solving the problems, such as existing silk cocoon to reel off raw silk from cocoons, the small speed of dynamics is slow, the excessive easy fracture of wire of dynamics.
Description
Technical field
The present invention relates to textile technology field, especially a kind of silk cocoon reels off raw silk from cocoons method.
Background technology
The technique that silk cocoon is extracted out to silk is referred to as filature, and filature silk technology originates from ancient china earliest, has long
History.Silk has the advantages that light and elongated, fabric sheen is good, comfortable and easy to wear, and sub- sense is smooth plentiful, poor heat conductivity, and moisture absorption is breathed freely.
Silk reeling technology process include the beating of cooked cocoon, shaking, silk collection thread, pick up sheath, reel silk from cocoons solution, the silk reel silk from cocoons of part silkworm cocoon it is complete or in
Add thread and end feeding, the winding of raw silk and drying when way is breaked end.At present, silk cocoon is carried out high temperature boiling by the method that silk cocoon reels off raw silk from cocoons
Afterwards, silk is drawn with crosisure, then hands over device to be reeled off raw silk from cocoons on bobbin by network, still, such method of reeling off raw silk from cocoons has dynamics too
The problem of small spinning speeds are slow, dynamics excessive easy fracture of wire.
The content of the invention
The present invention provides a kind of silk cocoon and reeled off raw silk from cocoons method, can solve existing silk cocoon and reel off raw silk from cocoons that the small speed of dynamics is slow, dynamics is excessive
The problem of easy fracture of wire.
In order to solve the above-mentioned technical problem, the technical solution adopted in the present invention is：This silk cocoon reel off raw silk from cocoons method include with
Lower step：
1）Silk cocoon is put into stirring pool first, first pours into white wine, is then stirred while be put into sodium bicarbonate and alum, stirring 10
Cleaned after~15 minutes with clear water；
2）Then silk cocoon is put into steaming room and carries out steaming, steaming temperature is 60~70 DEG C, a length of 50~60 minutes during steaming；
3）Then silk cocoon is put into dryer and dried, drying temperature is 55~65 DEG C, and drying time period is 15~20 minutes；
4）Finally silk cocoon is put into hot water storgae, reeled off raw silk from cocoons with silk cocoon is carried out in reeling machine.
In above-mentioned technical proposal, more specifically technical scheme can also be：The white wine number of degrees are 28~33 degree.
Further：The hot water temperature is 50~60 DEG C.
By adopting the above-described technical solution, the present invention has the advantages that compared with prior art：Sodium bicarbonate and
Alum mixing adds white wine catalysis, can remove the impurity of silk cocoon, also act as the effect of increase silk toughness；By sodium bicarbonate,
Alum and white spirit mixed processing, then steaming processing is carried out, good unwinding effect is played to silk cocoon, it is easier to reel off raw silk from cocoons, increasing is taken out
Silk great efforts can accelerate spinning speeds without breaking silk.
Embodiment
With reference to instantiation, the invention will be further described：
Embodiment one
This silk cocoon method of reeling off raw silk from cocoons of this example comprises the following steps：
1）Silk cocoon is put into stirring pool first, first pours into 28 degree of white wine, then stirs while be put into sodium bicarbonate and alum, stirs
Cleaned after mixing 10 minutes with clear water；
2）Then silk cocoon is put into steaming room and carries out steaming, steaming temperature is 60 DEG C, a length of 50 minutes during steaming；
3）Then silk cocoon is put into dryer and dried, drying temperature is 55 DEG C, and drying time period is 15 minutes；
4）Finally silk cocoon is put into hot water storgae, hot water temperature is 50 DEG C, is reeled off raw silk from cocoons with silk cocoon is carried out in reeling machine.
Embodiment two
This silk cocoon method of reeling off raw silk from cocoons of this example comprises the following steps：
1）Silk cocoon is put into stirring pool first, first pours into 33 degree of white wine, then stirs while be put into sodium bicarbonate and alum, stirs
Cleaned after mixing 15 minutes with clear water；
2）Then silk cocoon is put into steaming room and carries out steaming, steaming temperature is 70 DEG C, a length of 60 minutes during steaming；
3）Then silk cocoon is put into dryer and dried, drying temperature is 65 DEG C, and drying time period is 20 minutes；
4）Finally silk cocoon is put into hot water storgae, hot water temperature is 60 DEG C, is reeled off raw silk from cocoons with silk cocoon is carried out in reeling machine.
Claims (3)
- A kind of method 1. silk cocoon reels off raw silk from cocoons, it is characterised in that：Comprise the following steps：1）Silk cocoon is put into stirring pool first, first pours into white wine, is then stirred while be put into sodium bicarbonate and alum, stirring 10 Cleaned after~15 minutes with clear water；2）Then silk cocoon is put into steaming room and carries out steaming, steaming temperature is 60~70 DEG C, a length of 50~60 minutes during steaming；3）Then silk cocoon is put into dryer and dried, drying temperature is 55~65 DEG C, and drying time period is 15~20 minutes；4）Finally silk cocoon is put into hot water storgae, reeled off raw silk from cocoons with silk cocoon is carried out in reeling machine.
- The method 2. silk cocoon according to claim 1 reels off raw silk from cocoons, it is characterised in that：The white wine number of degrees are 28~33 degree.
- The method 3. silk cocoon according to claim 2 reels off raw silk from cocoons, it is characterised in that：The hot water temperature is 50~60 DEG C.