CN107760811A - 一种80吨转炉的开新炉冶炼方法 - Google Patents
一种80吨转炉的开新炉冶炼方法 Download PDFInfo
- Publication number
- CN107760811A CN107760811A CN201610678719.XA CN201610678719A CN107760811A CN 107760811 A CN107760811 A CN 107760811A CN 201610678719 A CN201610678719 A CN 201610678719A CN 107760811 A CN107760811 A CN 107760811A
- Authority
- CN
- China
- Prior art keywords
- adds
- batches
- rifle
- blow
- stove
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
本发明公开了一种80吨转炉的开新炉冶炼方法,下枪至基本枪位,并以0.7Mpa氧压点火,点火后立即加入第一批造渣材料,吹2‑3min后提枪到化渣枪位在1.4‑1.8m处,正常氧压0.8Mpa,焦碳加入总量为1.5‑2.0t,点火后立即加入第一批0.5t,此后每隔2‑3min加入0.3‑0.4t,在开吹10min内加完,焦碳加完后,采用正常氧压0.8Mpa吹炼;炉渣碱度按3.0~3.5控制,开吹加入活性石灰2.5t,轻烧白云石1.5t或镁球,吹炼4‑7min内,视炉内化渣情况分两批或多批加入余量石灰,后期可用轻烧白云石或镁球调温,萤石每批量不大于100kg/批,总量不大于300kg/炉。该方法主要是针对新炉进行使用,使得转炉的效率高,满足使用。
Description
技术领域
本发明涉及一种方法,尤其是涉及一种80吨转炉的开新炉冶炼方法。
背景技术
冶炼是一种提炼技术,是指用焙烧、熔炼、电解以及使用化学药剂等方法把矿石中的金属提取出来;减少金属中所含的杂质或增加金属中某种成分,炼成所需要的金属。2012年8月我国精炼锌产量39.7万吨,同比下降2.2%,环比增长8.5%。1-8月累计精炼锌产量313.4万吨,同比下降5.1%。8月国内锌冶炼企业开工率仅为72.41%,同比下降2.68个百分点,创年内最低。开工率下降的主要原因是受限电以及原料紧缺影响。8月锌价继续下滑,国内加工费、进口加工费均走低,且矿山惜售情绪较浓,冶炼企业原料压力加重。进入9月份,限电有所缓解,企业检修也基本完成,并且下游生产旺季将至,预计冶炼厂生产情况会有所好转。2012年1-9月,黑色金属冶炼及压延加工业累计完成固定资产投资3696亿元,同比增长3.90%,增速较1-8月下滑了3.76个百分点。中投调查,2012年9月有色金属冶炼及压延加工业累计完成固定资产投资3279.33亿元,同比增长18.62%,增速较1-8月上升了0.25个百分点。钢铁行业投资9月同比增速明显下滑,且1-9月累计同比增速处于近2年来的低位。
现在转炉的新炉冶炼时效率低,不能满足使用。
发明内容
本发明的目的在于克服上述现有转炉的新炉冶炼时效率低,不能满足使用的问题,设计了一种80吨转炉的开新炉冶炼方法,该方法主要是针对新炉进行使用,使得转炉的效率高,满足使用。
本发明的目的通过下述技术方案实现:一种80吨转炉的开新炉冶炼方法,包括以下步骤:
(1)下枪至基本枪位,并以0.7Mpa氧压点火,点火后立即加入第一批造渣材料,吹2-3min后提枪到化渣枪位在1.4-1.8m处,正常氧压0.8Mpa,焦碳加入总量为1.5-2.0t,点火后立即加入第一批0.5t, 此后每隔2-3min加入0.3-0.4t,在开吹10min内加完,焦碳加完后,采用正常氧压0.8Mpa吹炼;
(2)炉渣碱度按3.0~3.5控制,开吹加入活性石灰2.5t,轻烧白云石1.5t或镁球,吹炼4-7min内,视炉内化渣情况分两批或多批加入余量石灰,后期可用轻烧白云石或镁球调温,萤石每批量不大于100kg/批,总量不大于300kg/炉;
(3)为保证炉衬烧结质量,开新炉确保连续冶炼5炉以上,两炉之间间隔时间不大于12min。
综上所述,本发明的有益效果是:该方法主要是针对新炉进行使用,使得转炉的效率高,满足使用。
具体实施方式
下面结合实施例,对本发明作进一步的详细说明,但本发明的实施方式不仅限于此。
实施例:
一种80吨转炉的开新炉冶炼方法,包括以下步骤:
(1)下枪至基本枪位,并以0.7Mpa氧压点火,点火后立即加入第一批造渣材料,吹2-3min后提枪到化渣枪位在1.4-1.8m处,正常氧压0.8Mpa,焦碳加入总量为1.5-2.0t,点火后立即加入第一批0.5t, 此后每隔2-3min加入0.3-0.4t,在开吹10min内加完,焦碳加完后,采用正常氧压0.8Mpa吹炼;
(2)炉渣碱度按3.0~3.5控制,开吹加入活性石灰2.5t,轻烧白云石1.5t或镁球,吹炼4-7min内,视炉内化渣情况分两批或多批加入余量石灰,后期可用轻烧白云石或镁球调温,萤石每批量不大于100kg/批,总量不大于300kg/炉;
(3)为保证炉衬烧结质量,开新炉确保连续冶炼5炉以上,两炉之间间隔时间不大于12min。
该方法主要是针对新炉进行使用,使得转炉的效率高,满足使用。
以上所述,仅是本发明的较佳实施例,并非对本发明做任何形式上的限制,凡是依据本发明的技术、方法实质上对以上实施例所作的任何简单修改、等同变化,均落入本发明的保护范围之内。
Claims (1)
1.一种80吨转炉的开新炉冶炼方法,其特征在于,包括以下步骤:
(1)下枪至基本枪位,并以0.7Mpa氧压点火,点火后立即加入第一批造渣材料,吹2-3min后提枪到化渣枪位在1.4-1.8m处,正常氧压0.8Mpa,焦碳加入总量为1.5-2.0t,点火后立即加入第一批0.5t, 此后每隔2-3min加入0.3-0.4t,在开吹10min内加完,焦碳加完后,采用正常氧压0.8Mpa吹炼;
(2)炉渣碱度按3.0~3.5控制,开吹加入活性石灰2.5t,轻烧白云石1.5t或镁球,吹炼4-7min内,视炉内化渣情况分两批或多批加入余量石灰,后期可用轻烧白云石或镁球调温,萤石每批量不大于100kg/批,总量不大于300kg/炉;
(3)为保证炉衬烧结质量,开新炉确保连续冶炼5炉以上,两炉之间间隔时间不大于12min。