CN107760084A - Automobile coating - Google Patents
Automobile coating Download PDFInfo
- Publication number
- CN107760084A CN107760084A CN201711099480.1A CN201711099480A CN107760084A CN 107760084 A CN107760084 A CN 107760084A CN 201711099480 A CN201711099480 A CN 201711099480A CN 107760084 A CN107760084 A CN 107760084A
- Authority
- CN
- China
- Prior art keywords
- parts
- levelling agent
- automobile coating
- paint
- dimethylbenzene
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Automobile coating, it is prepared from the following raw materials in parts by weight：2% 5~9 parts of the rheological agent aqueous solution, 1~5 part of clay, 5~7 parts of wax additives, 0.1~0.3 part of organosilicon levelling agent, 0.5~1 part of non-organic silicon levelling agent, 20~29 parts of dispersions of polyurethanes, 15~22 parts of dimethylbenzene, 18~27 parts of polyester varnish, 8~14 parts of paint naphtha, 5~10 parts of titanium dioxide；It is an advantage of the invention that：Practicality and good endurance.
Description
Technical field
The present invention relates to automobile coating, belongs to paint technology field.
Background technology
Paint is seen everywhere in schedule life, and it mainly plays a part of to protect and decorated, and according to different uses
Environment, the species of paint is also varied, traditional paint generally existing smell weight, easily comes off, be perishable, not enough environmental protection etc.
Problem, requirement of the consumer to paint can not be met, therefore, it is necessary to improve the formula of original paint, increase is painted
Practicality and durability, reduce its harm to environment and human body, and various use environment conditions can be adapted to.
The content of the invention
It is an object of the invention to provide automobile coating.
The problem to be solved in the present invention is traditional paint generally existing smell weight, easily comes off, be perishable, not environmentally friendly enough
The problems such as.
To realize the purpose of the present invention, the technical solution adopted by the present invention is：
Automobile coating, it is prepared from the following raw materials in parts by weight：
2% 5~9 parts of the rheological agent aqueous solution, 1~5 part of clay, 5~7 parts of wax additives, organosilicon levelling agent 0.1~0.3
Part, 0.5~1 part of non-organic silicon levelling agent, 20~29 parts of dispersions of polyurethanes, 15~22 parts of dimethylbenzene, polyester varnish 18~27
Part, 8~14 parts of paint naphtha, 5~10 parts of titanium dioxide, 9~13 parts of styrene, 15~19 parts of aramid fiber short fibre, polystyrene
6~11 parts of thermoplastic elastomer (TPE), 21~35 parts of rosin modified phenolic resin, 1~100 part of deionized water.
Above-mentioned anti-corrosion automobile coating, is prepared from the following raw materials in parts by weight：2% 6 parts of the rheological agent aqueous solution, 3 parts of clay,
6 parts of wax additives, 0.2 part of organosilicon levelling agent, 0.8 part of non-organic silicon levelling agent, 25 parts of dispersions of polyurethanes, dimethylbenzene 19
Part, 22 parts of polyester varnish, 11 parts of paint naphtha, 8 parts of titanium dioxide, 11 parts of styrene, 17 parts of aramid fiber short fibre, polystyrene heat
9 parts of thermoplastic elastic, 31 parts of rosin modified phenolic resin, 55 parts of deionized water.
Anti-corrosion automobile coating advantage of the present invention is：Crosslink density is good, and coating late hardness is high, mechanical performance, and ageing properties are excellent
It is different, and be not easy peeling after drying and do not break；Add aramid fiber short fibre so that paint has certain pressure resistance after drying
Degree；Add epoxy resin so that paint sticky moderate performance；Due to the distinctive architectural characteristic of rosin, make resin and pigment
Moistening dispersiveness is greatly improved, thus rosin modified phenolic resin has softening point is high, viscosity is big and good stability,
The advantages that compatibility and oil-soluble, manufactured paint film film forming is fast, drying property is good, and brightness and hardness are high.
Embodiment
With reference to embodiment, the present invention is further illustrated.
Embodiment 1, automobile coating of the present invention, is prepared from the following raw materials in parts by weight：2% 6 parts of the rheological agent aqueous solution, clay
3 parts, 6 parts of wax additives, 0.2 part of organosilicon levelling agent, 0.8 part of non-organic silicon levelling agent, 25 parts of dispersions of polyurethanes, dimethylbenzene
19 parts, 22 parts of polyester varnish, 11 parts of paint naphtha, 8 parts of titanium dioxide, 11 parts of styrene, 17 parts of aramid fiber short fibre, polystyrene
9 parts of thermoplastic elastomer (TPE), 31 parts of rosin modified phenolic resin, 55 parts of deionized water.
Claims (2)
1. automobile coating, it is characterized in that：It is prepared from the following raw materials in parts by weight：2% 5~9 parts of the rheological agent aqueous solution, clay 1~5
Part, 5~7 parts of wax additives, 0.1~0.3 part of organosilicon levelling agent, 0.5~1 part of non-organic silicon levelling agent, dispersions of polyurethanes
20~29 parts, 15~22 parts of dimethylbenzene, 18~27 parts of polyester varnish, 8~14 parts of paint naphtha, 5~10 parts of titanium dioxide, benzene second
9~13 parts of alkene, 15~19 parts of aramid fiber short fibre, 6~11 parts of styrene series thermoplastic elastomer, rosin modified phenolic resin 21~
35 parts, 1~100 part of deionized water.
2. automobile coating according to claim 1, it is characterized in that：It is prepared from the following raw materials in parts by weight：2% rheological agent water
6 parts of solution, 3 parts of clay, 6 parts of wax additives, 0.2 part of organosilicon levelling agent, 0.8 part of non-organic silicon levelling agent, they
25 parts of body, 19 parts of dimethylbenzene, 22 parts of polyester varnish, 11 parts of paint naphtha, 8 parts of titanium dioxide, 11 parts of styrene, aramid fiber short fibre
17 parts, 9 parts of styrene series thermoplastic elastomer, 31 parts of rosin modified phenolic resin, 55 parts of deionized water.