CN107759095A - A kind of high strength glass fiber - Google Patents
A kind of high strength glass fiber Download PDFInfo
- Publication number
- CN107759095A CN107759095A CN201711032991.1A CN201711032991A CN107759095A CN 107759095 A CN107759095 A CN 107759095A CN 201711032991 A CN201711032991 A CN 201711032991A CN 107759095 A CN107759095 A CN 107759095A
- Authority
- CN
- China
- Prior art keywords
- parts
- glass fiber
- high strength
- strength glass
- magnesia
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of high strength glass fiber, is made up of by weight the following raw material:60 66 parts of silica, 20 22 parts of carborundum, 32 33 parts of lime stone, 10 12 parts of aluminum oxide, 10 12 parts of magnesia, 10 12 points of barium monoxide, 10 14 parts of boron oxide, 10 12 parts of quartz sand, 35 parts of light of firefly powder, 34 parts of saltcake, 12 parts of soda ash, 0.5 1 parts of fining agent, 0.8 1.2 parts of sulfate, 0.6 1 parts of halide.Glass fibre flat appearance produced by the invention, color uniformity, various post-processing manufacturing process can be applied to well.And mechanical performance, wearability are good, high mechanical strength, chemical stability and heat endurance are good;Acid resistance is improved;Reduce thermal coefficient of expansion.Resistance to elevated temperatures is excellent, can be applied to less than 1100 DEG C for a long time, have good ablation property, more preferable heat-resisting quantity, chemical resistance and modulus of elasticity, is widely used in manufacturing the fields such as precision instrument heat shield, ablator, heat-insulating material.
Description
Technical field
The present invention relates to inorganic non-metallic material, specifically a kind of high strength glass fiber.
Background technology
Glass fibre belongs to inorganic non-metallic material, has good insulating, heat resistance is strong, corrosion resistance is good, mechanical strength
Many advantages, such as high, therefore as the maximum a kind of matrix material of application amount in enhancing composite.With inorganic non-metallic material
The extensive use of material, the industrially requirement to glass fibre also improve constantly.Prior art is still difficult to make glass fibre simultaneously
With preferable mechanical property and processability.Therefore, we develop one kind by improving glass fibre basic property itself
It can guarantee that the glass fibre new product for meeting low cost again simultaneously compared with higher baseline performance.
The content of the invention
The invention provides a kind of high strength glass fiber, to solve above-mentioned technical problem.
A kind of high strength glass fiber, it is made up of by weight the following raw material:Silica 60-66 parts, carborundum 20-22
Part, lime stone 32-33 parts, aluminum oxide 10-12 parts, magnesia 10-12 parts, 10-12 points of barium monoxide, boron oxide 10-14 parts, quartz
Sand 10-12 parts, light of firefly powder 3-5 parts, saltcake 3-4 parts, soda ash 1-2 parts, fining agent 0.5-1 parts, sulfate 0.8-1.2 parts, halogenation
Thing 0.6-1 parts.
Preferably, described a kind of high strength glass fiber, it is made up of by weight the following raw material:60 parts of silica,
20 parts of carborundum, 32 parts of lime stone, 10 parts of aluminum oxide, 10 parts of magnesia, barium monoxide 10 divide, 10 parts of boron oxide, 10 parts of quartz sand,
3 parts of light of firefly powder, 3 parts of saltcake, 1 part of soda ash, 0.5 part of fining agent, 0.8 part of sulfate, 0.6 part of halide.
Preferably, described a kind of high strength glass fiber, it is made up of by weight the following raw material:63 parts of silica,
21 parts of carborundum, 32.5 parts of lime stone, 11 parts of aluminum oxide, 11 parts of magnesia, barium monoxide 11 divide, 12 parts of boron oxide, quartz sand 11
Part, 4 parts of light of firefly powder, 3.5 parts of saltcake, 1.5 parts of soda ash, 0.8 part of fining agent, 1 part of sulfate, 0.8 part of halide.
Preferably, described a kind of high strength glass fiber, it is made up of by weight the following raw material:66 parts of silica,
22 parts of carborundum, 33 parts of lime stone, 12 parts of aluminum oxide, 12 parts of magnesia, barium monoxide 12 divide, 14 parts of boron oxide, 12 parts of quartz sand,
5 parts of light of firefly powder, 4 parts of saltcake, 2 parts of soda ash, 1 part of fining agent, 1.2 parts of sulfate, 1 part of halide.
Beneficial effects of the present invention:
Glass fibre flat appearance produced by the invention, color uniformity, various post-processing systems can be applied to well
Make technique.And mechanical performance, wearability are good, high mechanical strength, chemical stability and heat endurance are good;Acid resistance is improved;
Reduce thermal coefficient of expansion.Resistance to elevated temperatures is excellent, can be applied to less than 1100 DEG C for a long time, with good ablation property, more
Good heat-resisting quantity, chemical resistance and modulus of elasticity, be widely used in manufacturing precision instrument heat shield, ablator,
The fields such as heat-insulating material.
Embodiment
Embodiments of the invention are described in detail below, but what the present invention can be defined by the claims and cover
Multitude of different ways is implemented.
Below by way of specific embodiment, the present invention will be described in detail.
The technical scheme that the present invention is embodied is:
Embodiment 1
A kind of high strength glass fiber, it is made up of by weight the following raw material:60 parts of silica, 20 parts of carborundum, stone
32 parts of lime stone, 10 parts of aluminum oxide, 10 parts of magnesia, barium monoxide 10 divide, 10 parts of boron oxide, 10 parts of quartz sand, 3 parts of light of firefly powder, awns
3 parts of nitre, 1 part of soda ash, 0.5 part of fining agent, 0.8 part of sulfate, 0.6 part of halide.
Embodiment 2
A kind of high strength glass fiber, it is made up of by weight the following raw material:63 parts of silica, 21 parts of carborundum, stone
32.5 parts of lime stone, 11 parts of aluminum oxide, 11 parts of magnesia, barium monoxide 11 divide, 12 parts of boron oxide, 11 parts of quartz sand, 4 parts of light of firefly powder,
3.5 parts of saltcake, 1.5 parts of soda ash, 0.8 part of fining agent, 1 part of sulfate, 0.8 part of halide.
Embodiment 3
A kind of high strength glass fiber, it is made up of by weight the following raw material:66 parts of silica, 22 parts of carborundum, stone
33 parts of lime stone, 12 parts of aluminum oxide, 12 parts of magnesia, barium monoxide 12 divide, 14 parts of boron oxide, 12 parts of quartz sand, 5 parts of light of firefly powder, awns
4 parts of nitre, 2 parts of soda ash, 1 part of fining agent, 1.2 parts of sulfate, 1 part of halide.
The embodiments of the present invention described above are not intended to limit the scope of the present invention, any in the present invention
Spirit and principle within the modifications, equivalent substitutions and improvements made etc., should be included in the claim protection model of the present invention
Within enclosing.
Claims (4)
1. a kind of high strength glass fiber, it is characterised in that be made up of by weight the following raw material:Silica 60-66 parts, carbon
SiClx 20-22 parts, lime stone 32-33 parts, aluminum oxide 10-12 parts, magnesia 10-12 parts, 10-12 points of barium monoxide, boron oxide 10-
14 parts, quartz sand 10-12 parts, light of firefly powder 3-5 parts, saltcake 3-4 parts, soda ash 1-2 parts, fining agent 0.5-1 parts, sulfate 0.8-
1.2 parts, halide 0.6-1 parts.
2. a kind of high strength glass fiber according to claims 1, it is characterised in that by the following raw material group by weight
Into:60 parts of silica, 20 parts of carborundum, 32 parts of lime stone, 10 parts of aluminum oxide, 10 parts of magnesia, barium monoxide 10 divide, boron oxide
10 parts, 10 parts of quartz sand, 3 parts of light of firefly powder, 3 parts of saltcake, 1 part of soda ash, 0.5 part of fining agent, 0.8 part of sulfate, halide 0.6
Part.
3. a kind of high strength glass fiber according to claims 1, it is characterised in that by the following raw material group by weight
Into:63 parts of silica, 21 parts of carborundum, 32.5 parts of lime stone, 11 parts of aluminum oxide, 11 parts of magnesia, barium monoxide 11 divide, aoxidized
12 parts of boron, 11 parts of quartz sand, 4 parts of light of firefly powder, 3.5 parts of saltcake, 1.5 parts of soda ash, 0.8 part of fining agent, 1 part of sulfate, halide
0.8 part.
4. a kind of high strength glass fiber according to claims 1, it is characterised in that by the following raw material group by weight
Into:66 parts of silica, 22 parts of carborundum, 33 parts of lime stone, 12 parts of aluminum oxide, 12 parts of magnesia, barium monoxide 12 divide, boron oxide
14 parts, 12 parts of quartz sand, 5 parts of light of firefly powder, 4 parts of saltcake, 2 parts of soda ash, 1 part of fining agent, 1.2 parts of sulfate, 1 part of halide.