CN107757220A - A kind of imitation wood carving and its manufacture craft - Google Patents
A kind of imitation wood carving and its manufacture craft Download PDFInfo
- Publication number
- CN107757220A CN107757220A CN201711014274.6A CN201711014274A CN107757220A CN 107757220 A CN107757220 A CN 107757220A CN 201711014274 A CN201711014274 A CN 201711014274A CN 107757220 A CN107757220 A CN 107757220A
- Authority
- CN
- China
- Prior art keywords
- weight
- cement
- sand
- imitation wood
- wood carving
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of imitation wood carving and its manufacture craft, manufacture craft to comprise the following steps：(1) plank undercuts pattern, sands flat and blows off；(2) outer mold is made；(3) mould in silica gel is made with silica gel covering solidification on plank；(4) high-mark cement, fine sand, chopped strand silk, high efficiency water reducing agent, iron oxide pigment and water are mixed and cement fine sand capstock is made；(5) the cement fine sand capstock being stirred is poured at the paramount degree 1/2 of mould in silica gel on vibrated bed, vibration is smooth；(6) high-mark cement, coarse sand, chopped strand silk, high efficiency water reducing agent, iron oxide pigment and water are mixed and cement coarse sand structure material is made；(7) cement coarse sand structure material is poured into mould in silica gel and, to being flushed with mould, vibrates smooth, placement cement setting；(8) maintenance is taken out；(9) cement protective agent is sprayed.A kind of imitation wood carving and its manufacture craft of the present invention, cheap, wide material sources imitation wood carvings can be produced.
Description
Technical field
The present invention relates to a kind of imitation wood carving and its manufacture craft, belong to artificial woodcarving manufacture technology field.
Background technology
Woodcarving is to be carved using various timber and tree root as material, is the important class in traditional artistic carving, is carving
One kind of modeling, " folk art " is commonly referred to as in our countries.Woodcarving is typically from tough and tensile, the on-deformable tree that is of close texture
Kind such as nanmu, red sandalwood, camphorwood, cypress, ginkgo, agalloch eaglewood, redwood, longan.These rare trees are due to needing decades at present
Even upper century-old growth could use, therefore increasingly rare and price more and more higher.Even common trees, with building
A large amount of uses of plank on finishing, available tree resources are fewer and fewer, the price also constantly rise all the way of plank.Meanwhile
The superb woodcarving skill of artificial woodcraft needs, cost are very high.A kind of therefore it provides cheap, imitation wood of wide material sources
Carving and its manufacture craft have become urgent need.
The content of the invention
The technical problem to be solved in the present invention is to provide a kind of imitation wood carving and its manufacture craft, can produce inexpensively, source it is wide
General imitation wood carving, meets the requirement of construction and decoration woodcarving.
In order to solve the above technical problems, a kind of manufacture craft of imitation wood carving of the present invention, the manufacture craft of the imitation wood carving
Comprise the following steps：
(1) one piece of plank is taken, pattern is undercuted with engraving machine, with the careful burr for sanding flat plank of sand paper and the ground of out-of-flatness
Side, then it is clean with air-blowing；
(2) kind of a mould is done with the plank for undercuting picture on surface, being unlikely to deform for the plank that undercuts picture on surface can be accommodated by making
Outer mold；
(3) outer mold is placed on the plane, the plank for undercuting picture on surface is flatted down and is placed among outer mold,
The inner space for filling up outer mold with silica gel covering and silica gel on the plank of picture on surface is undercuted to level, is taken after silica gel solidification
Go out plank, mould in silica gel is made；
(4) high-mark cement, fine sand, chopped strand silk, high efficiency water reducing agent, iron oxide pigment and water are mixed equal
It is even, cement fine sand capstock is made；
(5) outer mold is placed on vibrated bed, the concave surface that flats down of mould in silica gel is placed in outer mold upward,
The cement fine sand capstock being stirred is poured at the paramount degree 1/2 of mould in silica gel, makes cement fine sand capstock with vibrated bed vibration
It is smooth in mould in silica gel；
(6) high-mark cement, coarse sand, chopped strand silk, high efficiency water reducing agent, iron oxide pigment and water are mixed equal
It is even, cement coarse sand structure material is made；
(7) cement coarse sand structure material is poured into mould in silica gel, to being flushed with mould, makes cement coarse sand with vibrated bed vibration
Structure material is smooth in mould in silica gel, then is transported to place and places and smooth make cement setting；
(8) the imitation wood carving semi-finished product in silica gel in mould are taken out to be conserved；
(9) spray the obtained imitation wood of cement protective agent on imitation wood carving semi-finished product after conserving and carve product.
As the improvement of the present invention, sand paper is 1000 in the step (1)#Sand paper.
As the improvement of the present invention, mould thinnest part thickness is 1-3 centimetres in silica gel in the step (3).
As the improvement of the present invention, mould thinnest part thickness is 1 centimetre in silica gel in the step (3).
As the improvement of the present invention, high-mark cement is 52.5 rating cements in the step (4), and fine sand is 20 mesh -80
Mesh sand, chopped strand filament length degree are 0.5 centimetre -1 centimetre, and the weight of fine sand is 1.5-2.5 times of cement weight, chopped strand silk
Weight be cement weight 2%-5%, the weight of high efficiency water reducing agent is the 5%-8% of cement weight, the weight of iron oxide pigment
The 0.1-0.3% for cement weight is measured, the weight of water is the 20%-40% of cement weight.
As the improvement of the present invention, step (4) medium-fine sand is the mesh sand of 60 mesh -80, and chopped strand filament length degree is 0.6 li
- 0.8 centimetre of rice, the weight of fine sand are 2 times of cement weight, and the weight of chopped strand silk is the 3.5% of cement weight, is efficiently subtracted
The weight of aqua is the 6.5% of cement weight, and the weight of iron oxide pigment is the 0.2% of cement weight, and the weight of water is cement
The 30% of weight.
As the improvement of the present invention, high-mark cement is 52.5 rating cements in the step (6), and coarse sand is the mesh of 5 mesh -20
Sand, chopped strand filament length degree are 1.5 centimetres -3 centimetres, and the weight of coarse sand is 2.5-3.5 times of cement weight, chopped strand silk
Weight is the 10%-20% of cement weight, and the weight of high efficiency water reducing agent is the 5%-8% of cement weight, the weight of iron oxide pigment
The 0.1-0.3% for cement weight is measured, the weight of water is the 20%-40% of cement weight.
As the improvement of the present invention, step (6) medium coarse sand is the mesh sand of 10 mesh -20, and chopped strand filament length degree is 2 lis
- 2.5 centimetres of rice, the weight of coarse sand are 3 times of cement weight, and the weight of chopped strand silk is the 15% of cement weight, is efficiently subtracted
The weight of aqua is the 6.5% of cement weight, and the weight of iron oxide pigment is the 0.2% of cement weight, and the weight of water is cement
The 30% of weight.
As the improvement of the present invention, the time of cement setting is 48-72 hours in the step (7), in the step (8)
The time that imitation wood carving semi-finished product are conserved is 7-14 days.
In order to solve the above technical problems, a kind of imitation wood carving of the present invention, the imitation wood carving includes the upper and lower, imitation wood carving
The water that is mixed evenly with high-mark cement, fine sand, chopped strand silk, high efficiency water reducing agent, iron oxide pigment and water of upper strata
Mud fine sand capstock is made, and high-mark cement is 52.5 rating cements in cement fine sand capstock, and fine sand is the mesh sand of 20 mesh -80,
Chopped strand filament length degree is 0.5 centimetre -1 centimetre, and the weight of fine sand is 1.5-2.5 times of cement weight, the weight of chopped strand silk
The 2%-5% for cement weight is measured, the weight of high efficiency water reducing agent is the 5%-8% of cement weight, and the weight of iron oxide pigment is
The 0.1-0.3% of cement weight, the weight of water are the 20%-40% of cement weight；It is lower floor's high-mark cement of imitation wood carving, thick
The cement coarse sand structure material that sand, chopped strand silk, high efficiency water reducing agent, iron oxide pigment and water are mixed evenly is made, cement
High-mark cement is 52.5 rating cements in coarse sand structure material, and coarse sand is the mesh sand of 5 mesh -20, and chopped strand filament length degree is 1.5 lis
- 3 centimetres of rice, the weight of coarse sand are 2.5-3.5 times of cement weight, and the weight of chopped strand silk is the 10%- of cement weight
20%, the weight of high efficiency water reducing agent is the 5%-8% of cement weight, and the weight of iron oxide pigment is the 0.1- of cement weight
0.3%, the weight of water is the 20%-40% of cement weight；The outer surface of imitation wood carving is sprayed with cement protective agent, the upper table of imitation wood carving
Face is provided with pattern.
The beneficial effects of the invention are as follows：A kind of imitation wood carving of the present invention has the advantages of cheap, wide material sources, and this hair
A kind of bright imitation wood carving had both kept original characteristic of woodcarving, changed the characteristics of natural timber is easily corrupt again, extending makes
With life-span, also energy-saving and environmental protection, low-carbon.
Embodiment
A kind of manufacture craft of imitation wood carving, the manufacture craft of the imitation wood carving comprise the following steps：
(1) one piece of plank is taken, pattern is undercuted with engraving machine, with the careful burr for sanding flat plank of sand paper and the ground of out-of-flatness
Side, then it is clean with air-blowing；
(2) kind of a mould is done with the plank for undercuting picture on surface, being unlikely to deform for the plank that undercuts picture on surface can be accommodated by making
Outer mold；
(3) outer mold is placed on the plane, the plank for undercuting picture on surface is flatted down and is placed among outer mold,
The inner space for filling up outer mold with silica gel covering and silica gel on the plank of picture on surface is undercuted to level, is taken after silica gel solidification
Go out plank, mould in silica gel is made；
(4) high-mark cement, fine sand, chopped strand silk, high efficiency water reducing agent, iron oxide pigment and water are mixed equal
It is even, cement fine sand capstock is made；The color that mixing iron oxide pigment in cement material can carve imitation wood connects with wood color
Closely.
(5) outer mold is placed on vibrated bed, the concave surface that flats down of mould in silica gel is placed in outer mold upward,
The cement fine sand capstock being stirred is poured at the paramount degree 1/2 of mould in silica gel, makes cement fine sand capstock with vibrated bed vibration
It is smooth in mould in silica gel；
(6) high-mark cement, coarse sand, chopped strand silk, high efficiency water reducing agent, iron oxide pigment and water are mixed equal
It is even, cement coarse sand structure material is made；The color that mixing iron oxide pigment in cement material can carve imitation wood connects with wood color
Closely.Because woodcarving product has concavo-convex phenomenon, cement coarse sand structure material is taken to strengthen making product not out of shape more firm.
(7) cement coarse sand structure material is poured into mould in silica gel, to being flushed with mould, makes cement coarse sand with vibrated bed vibration
Structure material is smooth in mould in silica gel, then is transported to place and places and smooth make cement setting；
(8) the imitation wood carving semi-finished product in silica gel in mould are taken out to be conserved；
(9) spray the obtained imitation wood of cement protective agent on imitation wood carving semi-finished product after conserving and carve product.
As the improvement of the present invention, sand paper is 1000 in the step (1)#Sand paper.
As the improvement of the present invention, mould thinnest part thickness is 1-3 centimetres in silica gel in the step (3).
As the improvement of the present invention, mould thinnest part thickness is 1 centimetre in silica gel in the step (3).
As the improvement of the present invention, high-mark cement is 52.5 rating cements in the step (4), and fine sand is 20 mesh -80
Mesh sand, chopped strand filament length degree are 0.5 centimetre -1 centimetre, and the weight of fine sand is 1.5-2.5 times of cement weight, chopped strand silk
Weight be cement weight 2%-5%, the weight of high efficiency water reducing agent is the 5%-8% of cement weight, the weight of iron oxide pigment
The 0.1-0.3% for cement weight is measured, the weight of water is the 20%-40% of cement weight.
As the improvement of the present invention, step (4) medium-fine sand is the mesh sand of 60 mesh -80, and chopped strand filament length degree is 0.6 li
- 0.8 centimetre of rice, the weight of fine sand are 2 times of cement weight, and the weight of chopped strand silk is the 3.5% of cement weight, is efficiently subtracted
The weight of aqua is the 6.5% of cement weight, and the weight of iron oxide pigment is the 0.2% of cement weight, and the weight of water is cement
The 30% of weight.
As the improvement of the present invention, high-mark cement is 52.5 rating cements in the step (6), and coarse sand is the mesh of 5 mesh -20
Sand, chopped strand filament length degree are 1.5 centimetres -3 centimetres, and the weight of coarse sand is 2.5-3.5 times of cement weight, chopped strand silk
Weight is the 10%-20% of cement weight, and the weight of high efficiency water reducing agent is the 5%-8% of cement weight, the weight of iron oxide pigment
The 0.1-0.3% for cement weight is measured, the weight of water is the 20%-40% of cement weight.
As the improvement of the present invention, step (6) medium coarse sand is the mesh sand of 10 mesh -20, and chopped strand filament length degree is 2 lis
- 2.5 centimetres of rice, the weight of coarse sand are 3 times of cement weight, and the weight of chopped strand silk is the 15% of cement weight, is efficiently subtracted
The weight of aqua is the 6.5% of cement weight, and the weight of iron oxide pigment is the 0.2% of cement weight, and the weight of water is cement
The 30% of weight.
As the improvement of the present invention, the time of cement setting is 48-72 hours in the step (7), in the step (8)
The time that imitation wood carving semi-finished product are conserved is 7-14 days.
A kind of imitation wood made according to above-mentioned manufacture craft is carved, and the imitation wood carving includes the upper and lower, imitation wood carving
The cement that upper strata is mixed evenly with high-mark cement, fine sand, chopped strand silk, high efficiency water reducing agent, iron oxide pigment and water
Fine sand capstock is made, and high-mark cement is 52.5 rating cements in cement fine sand capstock, and fine sand is the mesh sand of 20 mesh -80, short
Filament length is cut as 0.5 centimetre -1 centimetre, the weight of fine sand is 1.5-2.5 times of cement weight, the weight of chopped strand silk
For the 2%-5% of cement weight, the weight of high efficiency water reducing agent is the 5%-8% of cement weight, and the weight of iron oxide pigment is water
The 0.1-0.3% of mud weight, the weight of water are the 20%-40% of cement weight；It is lower floor's high-mark cement of imitation wood carving, thick
The cement coarse sand structure material that sand, chopped strand silk, high efficiency water reducing agent, iron oxide pigment and water are mixed evenly is made, cement
High-mark cement is 52.5 rating cements in coarse sand structure material, and coarse sand is the mesh sand of 5 mesh -20, and chopped strand filament length degree is 1.5 lis
- 3 centimetres of rice, the weight of coarse sand are 2.5-3.5 times of cement weight, and the weight of chopped strand silk is the 10%- of cement weight
20%, the weight of high efficiency water reducing agent is the 5%-8% of cement weight, and the weight of iron oxide pigment is the 0.1- of cement weight
0.3%, the weight of water is the 20%-40% of cement weight；The outer surface of imitation wood carving is sprayed with cement protective agent, the upper table of imitation wood carving
Face is provided with pattern.
A kind of imitation wood carving of the present invention has the advantages of cheap, wide material sources, and a kind of imitation wood carving of the present invention both protected
Original characteristic of woodcarving is held, the characteristics of natural timber is easily corrupt is changed again, extends service life, and also energy-saving and environmental protection,
Low-carbon.
It should be noted that embodiment is only the explanation and illustration to technical solution of the present invention, should not be by it
The restriction to technical solution of the present invention is interpreted as, it is any only to make what is locally changed using the substantive content of the invention of the present invention, should
Fall within the scope of protection of the present invention.
Claims (10)
- A kind of 1. manufacture craft of imitation wood carving, it is characterised in that：The manufacture craft of the imitation wood carving comprises the following steps：(1) one piece of plank is taken, pattern is undercuted with engraving machine, with the careful burr for sanding flat plank of sand paper and the place of out-of-flatness, It is clean with air-blowing again；(2) do kind of a mould with the plank for undercuting picture on surface, make can accommodate the plank that undercuts picture on surface it is on-deformable outside Mould；(3) outer mold is placed on the plane, the plank for undercuting picture on surface is flatted down and is placed among outer mold, undercuted Covered on the plank of picture on surface with silica gel and silica gel fills up the inner space of outer mold to level, wood is taken out after silica gel solidification Plate, mould in silica gel is made；(4) high-mark cement, fine sand, chopped strand silk, high efficiency water reducing agent, iron oxide pigment and water are mixed evenly, made Obtain cement fine sand capstock；(5) outer mold is placed on vibrated bed, the concave surface that flats down of mould in silica gel is placed in outer mold upward, stirring Good cement fine sand capstock is poured at the paramount degree 1/2 of mould in silica gel, makes cement fine sand capstock in silicon with vibrated bed vibration It is smooth in mould in glue；(6) high-mark cement, coarse sand, chopped strand silk, high efficiency water reducing agent, iron oxide pigment and water are mixed evenly, made Obtain cement coarse sand structure material；(7) cement coarse sand structure material is poured into mould in silica gel, to being flushed with mould, makes cement coarse sand structure with vibrated bed vibration Material is smooth in mould in silica gel, then is transported to place and places and smooth make cement setting；(8) the imitation wood carving semi-finished product in silica gel in mould are taken out to be conserved；(9) spray the obtained imitation wood of cement protective agent on imitation wood carving semi-finished product after conserving and carve product.
- A kind of 2. manufacture craft of imitation wood carving according to claim 1, it is characterised in that：Sand paper is in the step (1) 1000#Sand paper.
- A kind of 3. manufacture craft of imitation wood carving according to claim 1, it is characterised in that：In the step (3) in silica gel Mould thinnest part thickness is 1-3 centimetres.
- A kind of 4. manufacture craft of imitation wood carving according to claim 3, it is characterised in that：In the step (3) in silica gel Mould thinnest part thickness is 1 centimetre.
- A kind of 5. manufacture craft of imitation wood carving according to claim 1, it is characterised in that：High grade in the step (4) Cement is 52.5 rating cements, and fine sand is the mesh sand of 20 mesh -80, and chopped strand filament length degree is 0.5 centimetre -1 centimetre, the weight of fine sand For 1.5-2.5 times of cement weight, the weight of chopped strand silk is the 2%-5% of cement weight, and the weight of high efficiency water reducing agent is The 5%-8% of cement weight, the weight of iron oxide pigment are the 0.1-0.3% of cement weight, and the weight of water is cement weight 20%-40%.
- A kind of 6. manufacture craft of imitation wood carving according to claim 5, it is characterised in that：Step (4) medium-fine sand is The mesh sand of 60 mesh -80, chopped strand filament length degree are 0.6 centimetre -0.8 centimetre, and the weight of fine sand is 2 times of cement weight, and be chopped fibre The weight for tieing up silk is the 3.5% of cement weight, and the weight of high efficiency water reducing agent is the 6.5% of cement weight, the weight of iron oxide pigment Measure as the 0.2% of cement weight, the weight of water is the 30% of cement weight.
- A kind of 7. manufacture craft of imitation wood carving according to claim 1, it is characterised in that：High grade in the step (6) Cement is 52.5 rating cements, and coarse sand is the mesh sand of 5 mesh -20, and chopped strand filament length degree is 1.5 centimetres -3 centimetres, the weight of coarse sand For 2.5-3.5 times of cement weight, the weight of chopped strand silk is the 10%-20% of cement weight, the weight of high efficiency water reducing agent For the 5%-8% of cement weight, the weight of iron oxide pigment is the 0.1-0.3% of cement weight, and the weight of water is cement weight 20%-40%.
- A kind of 8. manufacture craft of imitation wood carving according to claim 7, it is characterised in that：Step (6) medium coarse sand is The mesh sand of 10 mesh -20, chopped strand filament length degree are 2 centimetres -2.5 centimetres, and the weight of coarse sand is 3 times of cement weight, chopped strand The weight of silk is the 15% of cement weight, and the weight of high efficiency water reducing agent is the 6.5% of cement weight, and the weight of iron oxide pigment is The 0.2% of cement weight, the weight of water are the 30% of cement weight.
- A kind of 9. manufacture craft of imitation wood carving according to claim 1, it is characterised in that：Cement coagulates in the step (7) The time of knot is 48-72 hours, and the time that imitation wood carving semi-finished product are conserved in the step (8) is 7-14 days.
- A kind of 10. imitation wood carving that a kind of manufacture craft of imitation wood carving according to claim 1 makes, it is characterised in that：Institute Stating imitation wood carving includes the upper and lower, upper strata high-mark cement, fine sand, chopped strand silk, high efficiency water reducing agent, the oxygen of imitation wood carving Change the cement fine sand capstock that iron pigment and water are mixed evenly to be made, high-mark cement is 52.5 in cement fine sand capstock Rating cement, fine sand are the mesh sand of 20 mesh -80, and chopped strand filament length degree is 0.5 centimetre -1 centimetre, and the weight of fine sand is cement weight 1.5-2.5 times, the weight of chopped strand silk is the 2%-5% of cement weight, and the weight of high efficiency water reducing agent is cement weight 5%-8%, the weight of iron oxide pigment are the 0.1-0.3% of cement weight, and the weight of water is the 20%-40% of cement weight； Lower floor's high-mark cement, coarse sand, chopped strand silk, high efficiency water reducing agent, iron oxide pigment and the water of imitation wood carving mix equal Even cement coarse sand structure material is made, and high-mark cement is 52.5 rating cements in cement coarse sand structure material, and coarse sand is 5 mesh -20 Mesh sand, chopped strand filament length degree are 1.5 centimetres -3 centimetres, and the weight of coarse sand is 2.5-3.5 times of cement weight, chopped strand silk Weight be cement weight 10%-20%, the weight of high efficiency water reducing agent is the 5%-8% of cement weight, iron oxide pigment Weight is the 0.1-0.3% of cement weight, and the weight of water is the 20%-40% of cement weight；The outer surface of imitation wood carving is sprayed with water Mud protective agent, the upper surface of imitation wood carving are provided with pattern.