CN107740227A - A kind of facial mask and its production technology - Google Patents

A kind of facial mask and its production technology Download PDF

Info

Publication number
CN107740227A
CN107740227A CN201711234981.6A CN201711234981A CN107740227A CN 107740227 A CN107740227 A CN 107740227A CN 201711234981 A CN201711234981 A CN 201711234981A CN 107740227 A CN107740227 A CN 107740227A
Authority
CN
China
Prior art keywords
parts
facial mask
production technology
fiber
hot melt
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201711234981.6A
Other languages
Chinese (zh)
Inventor
王玉梅
孙文强
吴亮亮
马德勋
张志毅
鲍汉鑫
李凡成
蔡源
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shandong Heng Peng Sanitary Ware Co Ltd
Original Assignee
Shandong Heng Peng Sanitary Ware Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shandong Heng Peng Sanitary Ware Co Ltd filed Critical Shandong Heng Peng Sanitary Ware Co Ltd
Priority to CN201711234981.6A priority Critical patent/CN107740227A/en
Publication of CN107740227A publication Critical patent/CN107740227A/en
Pending legal-status Critical Current

Abstract

The invention belongs to cosmetic technical field, and in particular to a kind of facial mask and its production technology, in parts by weight, its raw material composition is described facial mask：65 75 parts of elastomer VM6202,20 25 parts of spunbond material PP3155E3,25 parts of smooth master batch HS560,35 parts of hydrophilic master batch RPSH.Using the present invention, hence it is evident that change the hydrophily and skin-friendly of facial mask, improve the comfortableness of product.

Description

A kind of facial mask and its production technology
Technical field
The invention belongs to cosmetic technical field, and in particular to a kind of facial mask and its production technology.
Background technology
Facial mask is a kind of carrier of face beautifying health keeping product, powder mediation at present, kaolin, non-woven fabrics, silk mask, tencel face Film, Biofibre facial mask, the facial mask of adhesive-bonded fabric facial mask material use quite varied.Wherein, non-woven fabrics facial mask is that in the market is most normal One of facial mask species seen, make things convenient for customers nursing of being in, and price is human-oriented.Advantage is that it enormously simplify the cumbersome behaviour of mantle Make, it is easier to receive user.Cost is cheap, can largely produce；Quality is light, soft；Stable performance, it is nontoxic non-stimulated.But It is that non-woven fabrics facial mask and skin affinity are bad, skin-friendly is poor；Hydrophily is poor, only the carrier of Essence, Essence infiltration Effect is undesirable, and " back suction " phenomenon occurs in non-woven fabrics facial mask；Comfortableness is poor.
The content of the invention
In view of the above-mentioned problems, the present invention proposes a kind of elastic facial mask and its production technology, using the present invention, hence it is evident that changes The hydrophily and skin-friendly of facial mask, improve the comfortableness of product.
A kind of elastic facial mask of the present invention, in parts by weight, its raw material composition is：Elastomer VM6202 65-75 Part, spunbond material PP3155E3 20-25 parts, smooth master batch HS560 2-5 parts, hydrophilic master batch RPSH 3-5 parts.
In the present invention, elastomer VM6202 is mainly to confer to non-woven fabrics elastic performance, and spunbond material is spun-bonded non-woven fabrics routine Raw materials for production, smooth master batch HS560 assigns the characteristic of non-woven fabrics soft comfortable, and hydrophilic master batch RPSH can assign non-woven fabrics parent The characteristic of water.
Inventor sends out by long-term experiment：Now in parts by weight, when its raw material composition is：70 parts of elastomer VM6202, When 23 parts of spunbond material PP3155E3,3 parts of smooth master batch HS560,4 parts of hydrophilic master batch RPSH, the facial mask effect of acquisition is best.
The production technology of facial mask of the present invention, it is concretely comprised the following steps：
(0) above-mentioned each raw material is weighed in proportion, it is standby；
(1) above-mentioned raw materials are well mixed；
(2) the good raw material of above-mentioned mixing is subjected to extrusion molten by feed system to big screw rod, obtains hot melt；
(3) hot melt is being filtered, measured and distributed；
(4) by the hot melt progress spinning measured and distributed, and spun silk is come into being through side cold front heavy rain Long filament；
(5) the just growing filament is subjected to drawing-off, obtains fiber；
(6) by the fiber sub-wire lapping, fibre web is formed；
(7) two layers of fibre web is passed through into hot rolling, obtains non-woven cloth；
(8) non-woven cloth is wound and cut.
Screw rod melting temperature is 180 DEG C~270 DEG C in step (2).
The operation temperature that hot melt described in step (3) is filtered, measured and distributed is 230~250 DEG C, and pressure exists 5~10MPa, apparatus for production line of the present invention are three die heads, and the product opens S1, S3 die head, and S2 die heads are closed, measuring pump S1/S3 Sendout is identical.
In step (4) by the good hot melt spinning of distribution and computation be by spraying silk in 0.3~0.8mm apertures, through supercooling But bellows cool down, 10~20 DEG C of cool wind box temperature, 0.2~1.5m/s of cooling wind velocity.
By mode of the described first growing filament Jing Guo air-flow sub-wire in step (5), by the horn mouth of slit extension apparatus, First growing filament is subjected to air drawing, air drawing speed is 2000m/min--5000m/min, while by the nascent of drawing-off Long filament strand marshalling, strength is produced, form fiber.
Be taped against into the fiber is mixed and disorderly in step (6) on lace curtaining, into lace curtaining under have air exhauster, carry out downward suction Wind, fiber is fixed on on lace curtaining, precompressed is carried out by pony press, forms fibre web.
80/110 DEG C of hot-rolled temperature, line pressure 30-70MPa in step (7).
The problem of present invention is for skin-friendly difference, optimization is realized by feed change and raw material proportioning；Because using hydrophilic Master batch, in the absence of hydrophilic attenuation problem, also because of infiltration Essence hydrophilic reagent will not be caused to separate out, and absorb Essence times Number is big, and hydrophilic master batch hydrophilic effect is uniform.The problem of for comfortableness difference, the present invention change bullet by adding smooth master batch Property body, spunbond material, smooth master batch ratio realize optimization.
Brief description of the drawings
Fig. 1 is the CD directions elastic curve figure of elastic non-woven cloth prepared by the present invention；
Fig. 2 is the MD directions elastic curve figure of elastic non-woven cloth prepared by the present invention；
Fig. 3 is the technological process of production schematic diagram of elastic facial mask of the present invention；
In figure：1st, feed system；2nd, screw extruder；3rd, filtration system；4th, measuring pump；5th, spinneret；6th, side cold wind is cold But system；7th, extension apparatus；8th, into lace curtaining；9th, hot-rolling mill；10th, winder；
Embodiment
The raw material that the present invention uses is purchase.
Embodiment 1
A kind of facial mask, in parts by weight, its raw material composition is：Elastomer VM6202 65-75 parts, spunbond material PP3155E3 20-25 parts, smooth master batch HS560 2-5 parts, hydrophilic master batch RPSH 3-5 parts.
The production technology of the elastic facial mask, it is concretely comprised the following steps：
(0) above-mentioned each raw material is weighed in proportion, it is standby；
(1) above-mentioned raw materials are well mixed；
(2) the good raw material of above-mentioned mixing is subjected to extrusion molten by feed system to big screw rod, obtains hot melt；
(3) hot melt is being filtered, measured and distributed；
(4) by the hot melt progress spinning measured and distributed, and spun silk is come into being through side cold front heavy rain Long filament；
(5) the just growing filament is subjected to drawing-off, obtains fiber；
(6) by the fiber sub-wire lapping, fibre web is formed；
(7) two layers of fibre web is passed through into hot rolling, obtains non-woven cloth；
(8) non-woven cloth is wound and cut.
Screw rod melting temperature is 180 DEG C in step (2).
The operation temperature that hot melt described in step (3) is filtered, measured and distributed is 250 DEG C, and pressure is in 8MPa.
By the good hot melt spinning of distribution and computation it is by spraying silk in 0.5mm apertures, by cool wind box in step (4) Cooling, 15 DEG C of cool wind box temperature, cooling wind velocity 1m/s.
By mode of the described first growing filament Jing Guo air-flow sub-wire in step (5), by the horn mouth of slit extension apparatus, First growing filament is subjected to air drawing, air drawing speed is 4000m/min, while the first growing filament strand row Jing Guo drawing-off Row are neat, produce strength, form fiber.
Be taped against into the fiber is mixed and disorderly in step (6) on lace curtaining, into lace curtaining under have air exhauster, carry out downward suction Wind, fiber is fixed on on lace curtaining, precompressed is carried out by pony press, forms fibre web.
110/123 DEG C of hot-rolled temperature, line pressure 50MPa in step (7).
Embodiment 2
A kind of facial mask, in parts by weight, its raw material composition is：65 parts of elastomer VM6202, spunbond material PP3155E3 20 Part, 5 parts of smooth master batch HS560,3 parts of hydrophilic master batch RPSH.
The production technology of the elastic facial mask, it is concretely comprised the following steps：
(0) above-mentioned each raw material is weighed in proportion, it is standby；
(1) above-mentioned raw materials are well mixed；
(2) the good raw material of above-mentioned mixing is subjected to extrusion molten by feed system to big screw rod, obtains hot melt；
(3) hot melt is being filtered, measured and distributed；
(4) by the hot melt progress spinning measured and distributed, and spun silk is come into being through side cold front heavy rain Long filament；
(5) the just growing filament is subjected to drawing-off, obtains fiber；
(6) by the fiber sub-wire lapping, fibre web is formed；
(7) two layers of fibre web is passed through into hot rolling, obtains non-woven cloth；
(8) non-woven cloth is wound and cut.
Screw rod melting temperature is 180 DEG C in step (2).
The operation temperature that hot melt described in step (3) is filtered, measured and distributed is 230 DEG C, and pressure is in 8MPa.
By the good hot melt spinning of distribution and computation it is by spraying silk in 0.3mm apertures, by cool wind box in step (4) Cooling, 20 DEG C of cool wind box temperature, cooling wind velocity 1.5m/s.
By mode of the described first growing filament Jing Guo air-flow sub-wire in step (5), by the horn mouth of slit extension apparatus, First growing filament is subjected to air drawing, air drawing speed is 2000m/min, while the first growing filament strand row Jing Guo drawing-off Row are neat, produce strength, form fiber.
Be taped against into the fiber is mixed and disorderly in step (6) on lace curtaining, into lace curtaining under have air exhauster, carry out downward suction Wind, fiber is fixed on on lace curtaining, precompressed is carried out by pony press, forms fibre web.
110/123 DEG C of hot-rolled temperature, line pressure 30MPa in step (7).
Embodiment 3
A kind of facial mask, in parts by weight, its raw material composition is：75 parts of elastomer VM6202, spunbond material PP3155E3 22 Part, 2 parts of smooth master batch HS560,4 parts of hydrophilic master batch RPSH.
The production technology of the elastic facial mask, it is concretely comprised the following steps：
(0) above-mentioned each raw material is weighed in proportion, it is standby；
(1) above-mentioned raw materials are well mixed；
(2) the good raw material of above-mentioned mixing is subjected to extrusion molten by feed system to big screw rod, obtains hot melt；
(3) hot melt is being filtered, measured and distributed；
(4) by the hot melt progress spinning measured and distributed, and spun silk is come into being through side cold front heavy rain Long filament；
(5) the just growing filament is subjected to drawing-off, obtains fiber；
(6) by the fiber sub-wire lapping, fibre web is formed；
(7) two layers of fibre web is passed through into hot rolling, obtains non-woven cloth；
(8) non-woven cloth is wound and cut.
Screw rod melting temperature is 220 DEG C in step (2).
The operation temperature that hot melt described in step (3) is filtered, measured and distributed is 240 DEG C, and pressure is in 8MPa.
By the good hot melt spinning of distribution and computation it is by spraying silk in 0.5mm apertures, by cool wind box in step (4) Cooling, 10 DEG C of cool wind box temperature, cooling wind velocity 0.2m/s.
By mode of the described first growing filament Jing Guo air-flow sub-wire in step (5), by the horn mouth of slit extension apparatus, First growing filament is subjected to air drawing, air drawing speed is 4000m/min, while the first growing filament strand row Jing Guo drawing-off Row are neat, produce strength, form fiber.
Be taped against into the fiber is mixed and disorderly in step (6) on lace curtaining, into lace curtaining under have air exhauster, carry out downward suction Wind, fiber is fixed on on lace curtaining, precompressed is carried out by pony press, forms fibre web.
110/123 DEG C of hot-rolled temperature, line pressure 50MPa in step (7).
Embodiment 4
A kind of facial mask, in parts by weight, its raw material composition is：70 parts of elastomer VM6202, spunbond material PP3155E3 25 Part, 4 parts of smooth master batch HS560,5 parts of hydrophilic master batch RPSH.
The production technology of the elastic facial mask, it is concretely comprised the following steps：
(0) above-mentioned each raw material is weighed in proportion, it is standby；
(1) above-mentioned raw materials are well mixed；
(2) the good raw material of above-mentioned mixing is subjected to extrusion molten by feed system to big screw rod, obtains hot melt；
(3) hot melt is being filtered, measured and distributed；
(4) by the hot melt progress spinning measured and distributed, and spun silk is come into being through side cold front heavy rain Long filament；
(5) the just growing filament is subjected to drawing-off, obtains fiber；
(6) by the fiber sub-wire lapping, fibre web is formed；
(7) two layers of fibre web is passed through into hot rolling, obtains non-woven cloth；
(8) non-woven cloth is wound and cut.
Screw rod melting temperature is 270 DEG C in step (2).
The operation temperature that hot melt described in step (3) is filtered, measured and distributed is 250 DEG C, and pressure exists 10MPa。
By the good hot melt spinning of distribution and computation it is by spraying silk in 0.8mm apertures, by cool wind box in step (4) Cooling, 15 DEG C of cool wind box temperature, cooling wind velocity 1m/s.
By mode of the described first growing filament Jing Guo air-flow sub-wire in step (5), by the horn mouth of slit extension apparatus, First growing filament is subjected to air drawing, air drawing speed is 5000m/min, while the first growing filament strand row Jing Guo drawing-off Row are neat, produce strength, form fiber.
Be taped against into the fiber is mixed and disorderly in step (6) on lace curtaining, into lace curtaining under have air exhauster, carry out downward suction Wind, fiber is fixed on on lace curtaining, precompressed is carried out by pony press, forms fibre web.
110/123 DEG C of hot-rolled temperature, line pressure 70MPa in step (7).
The elastic facial mask obtained to the present invention is accordingly tested, and concrete outcome is as follows：
Table 1
Project Maximum Minimum value Average value Remarks
Grammes per square metre g/m2 29.9 25.9 27.9
Strength CDN/5cm 13.2 10.5 11.4
Strength MDN/5cm 20.1 18.1 19.3
Elongation CD% 260.0 210.0 234.0
Elongation MD% 231.0 194.5 206.5
Fibre diameter μm 19.46 16.7 17.87 3.5D
Pliability CDg 1.8 1.3 1.6
Pliability MDg 2.0 1.8 1.9
Essence absorbs multiple 7.9 7.4 7.7
The elastic curve of table 2 is tested

Claims (9)

  1. A kind of 1. facial mask, it is characterised in that：In parts by weight, its raw material composition is：Elastomer VM6202 65-75 parts, spunbond material PP3155E3 20-25 parts, smooth master batch HS560 2-5 parts, hydrophilic master batch RPSH 3-5 parts.
  2. A kind of 2. elastic facial mask according to claim 1, it is characterised in that：In parts by weight, its raw material composition is：Elasticity 70 parts of body VM6202,23 parts of spunbond material PP3155E3,3 parts of smooth master batch HS560,4 parts of hydrophilic master batch RPSH.
  3. A kind of 3. production technology for producing the facial mask described in claim 1, it is characterised in that：It is concretely comprised the following steps：
    (0) above-mentioned each raw material is weighed in proportion, it is standby；
    (1) above-mentioned raw materials are well mixed；
    (2) the good raw material of above-mentioned mixing is subjected to extrusion molten by feed system to big screw rod, obtains hot melt；
    (3) hot melt is being filtered, measured and distributed；
    (4) by the hot melt progress spinning measured and distributed, and spun silk is obtained and just grown through side cold front heavy rain Silk；
    (5) the just growing filament is subjected to drawing-off, obtains fiber；
    (6) by the fiber sub-wire lapping, fibre web is formed；
    (7) two layers of fibre web is passed through into hot rolling, obtains non-woven cloth；
    (8) non-woven cloth is wound and cut.
  4. 4. the production technology of elastic facial mask according to claim 3, it is characterised in that：Screw rod melting temperature in step (2) For 180 DEG C~270 DEG C.
  5. 5. the production technology of elastic facial mask according to claim 3, it is characterised in that：Hot melt described in step (3) The operation temperature for being filtered, being measured and being distributed is 230~250 DEG C, and pressure is in 5~10MPa.
  6. 6. the production technology of elastic facial mask according to claim 3, it is characterised in that：It is in step (4) that distribution and computation is good Hot melt spinning be the cool wind box temperature 10~20 by spraying silk in 0.3~0.8mm apertures, being cooled down by cool wind box DEG C, 0.2~1.5m/s of cooling wind velocity.
  7. 7. the production technology of elastic facial mask according to claim 3, it is characterised in that：Described is come into being in step (5) Mode of the long filament Jing Guo air-flow sub-wire, by the horn mouth of slit extension apparatus, first growing filament is subjected to air drawing, air-flow is led It is 2000m/min-5000m/min to stretch speed, while the first growing filament strand marshalling Jing Guo drawing-off, produces strength, shape Into fiber.
  8. 8. the production technology of elastic facial mask according to claim 3, it is characterised in that：It is in step (6) that the fiber is miscellaneous Random is taped against on lace curtaining, into lace curtaining under have air exhauster, carry out downward suction air, fiber be fixed on on lace curtaining, pass through Pony press carries out precompressed, forms fibre web.
  9. 9. the production technology of elastic facial mask according to claim 3, it is characterised in that：Hot-rolled temperature 80/ in step (7) 110 DEG C, line pressure 30-70MPa.
CN201711234981.6A 2017-11-30 2017-11-30 A kind of facial mask and its production technology Pending CN107740227A (en)